阅读说明：本技术 固废骨料用调节剂及其调节方法和混凝土 (Solid waste aggregate regulator and regulating method thereof and concrete ) 是由 陈志杰 杨文俊 刘衍行 黄沛文 于 2020-05-30 设计创作，主要内容包括：本申请涉及建筑材料技术领域,公开一种固废骨料用调节剂,包括A组分和B组分；该A组分包括聚羧酸母液、二乙醇单异丙醇胺、三异丙醇胺、甘油和硫酸钠；溶剂为水；该B组分包括无机复合填料和表面活性剂。本公开实施例中,A组分和B组分分开存储,独立包装。在对固废骨料进行调节时,先加入B组分,对固废骨料中的孔隙进行填充,排出固废骨料的孔隙中的气体,并可减少固废骨料的吸水量；再加入A组分,对固废骨料的表面进行包覆修饰提高获得的混凝土的性能。有效利用了固废骨料,环境友好。本申请还公开一种采用前述的固废骨料用调节剂调节固废骨料的方法和混凝土。(The application relates to the technical field of building materials, and discloses a regulator for solid waste aggregate, which comprises a component A and a component B; the component A comprises polycarboxylic acid mother liquor, diethanol monoisopropanolamine, triisopropanolamine, glycerol and sodium sulfate; the solvent is water; the component B comprises inorganic composite filler and surfactant. In the disclosed embodiment, the A component and the B component are stored separately and packaged independently. When the solid waste aggregate is regulated, the component B is added firstly to fill the pores in the solid waste aggregate, discharge the gas in the pores of the solid waste aggregate and reduce the water absorption of the solid waste aggregate; and adding the component A, and coating and modifying the surface of the solid waste aggregate to improve the performance of the obtained concrete. Effectively utilizes the solid waste aggregate and is environment-friendly. The application also discloses a method for regulating the solid waste aggregate by adopting the regulator for the solid waste aggregate and concrete.)

1. The regulator for the solid waste aggregate is characterized by comprising a component A and a component B;

the component A comprises the following components in percentage by weight: 2 to 5 percent of polycarboxylic acid mother liquor, 1 to 4 percent of diethanolisopropanolamine, 0.1 to 0.4 percent of triisopropanolamine, 1 to 4 percent of glycerol and 0.1 to 0.4 percent of sodium sulfate; the solvent is water;

the component B comprises the following components in parts by weight: 95-99 parts of inorganic composite filler and 1-5 parts of surfactant; the inorganic composite filler comprises ground limestone, micro-nano titanium dioxide, calcium silicate hydrate gel seed crystals and bentonite, and the weight ratio of the ground limestone to the micro-nano titanium dioxide to the calcium silicate hydrate gel seed crystals to the bentonite is 5-10: 2-4: 1-2: 1 in sequence.

2. The conditioner for solid waste aggregate according to claim 1, wherein the component A comprises the following components in percentage by weight: 4% of polycarboxylic acid mother liquor, 2% of diethanolisopropanolamine, 0.2% of triisopropanolamine, 2% of glycerol and 0.2% of sodium sulfate; the solvent is water.

3. The conditioner for solid waste aggregate according to claim 1, wherein the component B comprises the following components in parts by weight: 98 parts of inorganic composite filler and 2 parts of surfactant.

4. The conditioner for solid waste aggregates according to claim 1, wherein the weight ratio of the ground limestone, the micro-nano titanium dioxide, the calcium silicate hydrate gel seed crystals and the bentonite in the inorganic composite filler is 8: 2.5: 1.5: 1 in sequence.

5. The method for conditioning solid waste aggregate using the conditioning agent for solid waste aggregate according to any one of claims 1 to 4, comprising:

adding the component B into solid waste aggregate, and performing ball milling and uniform mixing to obtain a mixed material; wherein the mass ratio of the solid waste aggregate to the component B is 1: 0.1-0.2;

adding the component A into the mixed material, and performing ball milling and uniform mixing to finish the method for adjusting the solid waste aggregate; the dosage of the component A is 0.5-1% of the solid waste aggregate.

6. The method for conditioning solid waste aggregate by using the conditioning agent for solid waste aggregate according to claim 5, wherein the solid waste aggregate is reinforced solid waste aggregate;

the strengthening method for strengthening the solid waste aggregate comprises the following steps: carrying out strengthening treatment on the solid waste aggregate by adopting a wood wax oil modified component to obtain strengthened solid waste aggregate; the wood wax oil modified component comprises, by weight, 50 parts of tung oil, 10 parts of orange oil, 10 parts of moringa seed oil, 5 parts of pine oil and 5 parts of nano-filler.

7. The method for conditioning solid waste aggregate with the conditioning agent for solid waste aggregate according to claim 6, wherein the method for strengthening the solid waste aggregate comprises the following steps:

heating the solid waste aggregate to 50-60 ℃, preserving heat for 1-2 hours, and removing water in the solid waste aggregate to obtain dry solid waste aggregate;

adding a wood wax oil modified component into the dry solid waste aggregate, and performing ball milling for 2-3 h; then discharging the modified components of the wood wax oil, and then oscillating to remove impurities to obtain oil-impregnated solid waste aggregate; wherein the volume ratio of the wood wax oil modified component to the dry solid waste aggregate is 0.3-0.5: 1;

and airing the oil-impregnated solid waste aggregate to obtain the reinforced solid waste aggregate.

8. The method for conditioning solid waste aggregate with the conditioning agent for solid waste aggregate according to claim 6 or 7, wherein in the wood wax oil modification component, the nano filler comprises nano high-hardness shell powder.

9. The concrete comprises a cementing material, a coarse aggregate, a fine aggregate and a water reducing agent; the method is characterized in that the coarse aggregate and/or the fine aggregate are/is solid waste aggregate which is adjusted by the method of claim 6, 7 or 8; the amount of the water reducing agent is 3-4% of the weight of the cementing material.

10. The concrete according to claim 9, further comprising an admixture in a weight ratio of 0.5 to 1: 1; the admixture comprises fly ash, pumice powder and zeolite powder; wherein the weight ratio of the fly ash to the pumice powder is 1: 0.5-0.8; the weight ratio of the fly ash to the zeolite powder is 1: 0.5-0.8.

Technical Field

The application relates to the technical field of building materials, for example to a solid waste aggregate regulator, a regulating method thereof and concrete.

Background

Concrete, referred to as "concrete" for short: the concrete is a general term for engineering composite materials formed by cementing aggregate into a whole by cementing materials, and the term of concrete generally refers to that cement is used as the cementing materials, and sand and stone are used as the aggregate; the cement concrete, also called as common concrete, is obtained by mixing with water (which may contain additives and admixtures) according to a certain proportion and stirring, and is widely applied to civil engineering. Therefore, sand and stone as aggregates are main materials of concrete composition.

At present, with the increasing number of stones used in the building market, natural stone resources are less and less, so that the construction solid waste recycled aggregate, referred to as solid waste aggregate for short, appears, and the natural aggregate can be partially or completely replaced.

In the process of implementing the embodiments of the present disclosure, it is found that at least the following problems exist in the related art: the solid waste aggregate has large internal porosity and high water absorption rate, and has great influence on the performance of the prepared concrete.

Disclosure of Invention

The following presents a simplified summary in order to provide a basic understanding of some aspects of the disclosed embodiments. This summary is not an extensive overview nor is intended to identify key/critical elements or to delineate the scope of such embodiments but rather as a prelude to the more detailed description that is presented later.

The embodiment of the disclosure provides a regulator for solid waste aggregate, a regulating method thereof and concrete, and aims to solve the problems that the solid waste aggregate has high internal porosity and high water absorption rate and has great influence on the performance of the prepared concrete.

In some embodiments, the conditioning agent for solid waste aggregate comprises an A component and a B component;

the component A comprises the following components in percentage by weight: 2 to 5 percent of polycarboxylic acid mother liquor, 1 to 4 percent of diethanolisopropanolamine, 0.1 to 0.4 percent of triisopropanolamine, 1 to 4 percent of glycerol and 0.1 to 0.4 percent of sodium sulfate; the solvent is water;

the component B comprises the following components in parts by weight: 95-99 parts of inorganic composite filler and 1-5 parts of surfactant; the inorganic composite filler comprises ground limestone, micro-nano titanium dioxide, calcium silicate hydrate gel seed crystals and bentonite, and the weight ratio of the ground limestone to the micro-nano titanium dioxide to the calcium silicate hydrate gel seed crystals to the bentonite is 5-10: 2-4: 1-2: 1 in sequence. :

in some embodiments, the method for conditioning solid waste aggregate by using the conditioning agent for solid waste aggregate comprises the following steps:

adding the component B into solid waste aggregate, and performing ball milling and uniform mixing to obtain a mixed material; wherein the mass ratio of the solid waste aggregate to the component B is 1: 0.1-0.2;

Adding the component A into the mixture, and performing ball milling and uniform mixing to finish the method for adjusting the solid waste aggregate; the dosage of the component A is 0.5 to 1 percent of the solid waste aggregate.

In some embodiments, the concrete comprises cementitious material, coarse aggregate, fine aggregate, and water reducer; wherein, the coarse aggregate and/or the fine aggregate adopt the solid waste aggregate regulated by the method; the dosage of the water reducing agent is 3-4% of the weight of the cementing material.

The solid waste aggregate regulator, the regulating method thereof and the concrete provided by the embodiment of the disclosure can realize the following technical effects:

in the regulator for solid waste aggregate of the embodiment of the disclosure, the component A and the component B are separately stored and independently packaged, when the solid waste aggregate is regulated, the component B is added firstly to fill the pores in the solid waste aggregate, discharge the gas in the pores of the solid waste aggregate, and reduce the water absorption capacity of the solid waste aggregate; and adding the component A, coating and modifying the surface of the solid waste aggregate, and enabling the components in the component A to act with the cementing material when subsequently mixing with the fine aggregate and the cementing material, so that the performance of the obtained concrete is improved. Effectively utilizes the solid waste aggregate and is environment-friendly.

In the solid waste aggregate regulator disclosed by the embodiment of the disclosure, water is mainly used as raw material and auxiliary material mixed water, no waste liquid is generated, no cleaning is needed after stirring, and no production wastewater is generated. And no waste gas is generated in the stirring process.

The foregoing general description and the following description are exemplary and explanatory only and are not restrictive of the application.

Detailed Description

So that the manner in which the features and technical contents of the embodiments of the present disclosure can be understood in detail, the embodiments of the present disclosure are described in detail below for illustrative purposes only and are not intended to limit the embodiments of the present disclosure. In the following description of the technology, for purposes of explanation, numerous details are set forth in order to provide a thorough understanding of the disclosed embodiments. However, one or more embodiments may be practiced without these details.

The terms "first," "second," and the like in the description and in the claims of the embodiments of the present disclosure are used for distinguishing between similar elements and not necessarily for describing a particular sequential or chronological order. It should be understood that the data so used may be interchanged under appropriate circumstances such that embodiments of the present disclosure described herein may be made. Furthermore, the terms "comprising" and "having," as well as any variations thereof, are intended to cover non-exclusive inclusions.

The terms "upper", "lower", "inner", "middle", "outer", "front", "rear", and the like in the embodiments of the present disclosure are mainly used for better describing the embodiments of the present disclosure and the embodiments thereof, and are not used to limit the indicated devices, elements or components to have a specific orientation or to be constructed and operated in a specific orientation. Moreover, some of the above terms may be used to indicate other meanings besides the orientation or positional relationship, for example, the term "on" may also be used to indicate some kind of attachment or connection relationship in some cases. The specific meanings of these terms in the embodiments of the present disclosure can be understood by those of ordinary skill in the art as appropriate.

In addition, the terms "disposed," "connected," and "secured" are to be construed broadly. For example, "connected" may be a fixed connection, a detachable connection, or a unitary construction; can be a mechanical connection, or an electrical connection; may be directly connected, or indirectly connected through intervening media, or may be in internal communication between two devices, elements or components. Specific meanings of the above terms in the embodiments of the present disclosure can be understood by those of ordinary skill in the art according to specific situations.

The term "plurality" means two or more unless otherwise specified.

In the embodiment of the present disclosure, the character "/" indicates that the preceding and following objects are in an or relationship. For example, A/B represents: a or B.

The term "and/or" is an associative relationship that describes objects, meaning that three relationships may exist. For example, a and/or B, represents: a or B, or A and B.

It should be noted that, in the case of no conflict, the embodiments and features in the embodiments of the present disclosure may be combined with each other.

The embodiment of the disclosure provides a conditioning agent for solid waste aggregate, which comprises a component A and a component B. Wherein, the component A comprises the following components in percentage by weight: 2 to 5 percent of polycarboxylic acid mother liquor, 1 to 4 percent of diethanolisopropanolamine, 0.1 to 0.4 percent of triisopropanolamine, 1 to 4 percent of glycerol and 0.1 to 0.4 percent of sodium sulfate; the solvent is water. The component B comprises the following components in parts by weight: 95-99 parts of inorganic composite filler and 1-5 parts of surfactant; the inorganic composite filler comprises ground limestone, micro-nano titanium dioxide, hydrated calcium silicate gel seed crystals and bentonite, wherein the weight ratio of the ground limestone to the micro-nano titanium dioxide to the hydrated calcium silicate gel seed crystals to the bentonite is 5-10: 2-4: 1-2: 1 in sequence.

In the regulator for solid waste aggregate of the embodiment of the disclosure, the component A and the component B are separately stored and independently packaged, when the solid waste aggregate is regulated, the component B is added firstly to fill the pores in the solid waste aggregate, discharge the gas in the pores of the solid waste aggregate, and reduce the water absorption capacity of the solid waste aggregate; and adding the component A, coating and modifying the surface of the solid waste aggregate, and enabling the components in the component A to act with the cementing material when subsequently mixing with the fine aggregate and the cementing material, so that the performance of the obtained concrete is improved. When the solid waste aggregate is adjusted, the mass ratio of the component A to the component B is 1: 2.

In the conditioning agent for solid waste aggregate of the embodiment of the disclosure, in the component B, the inorganic composite filler mainly takes heavy calcium carbonate and nano titanium dioxide as main materials, so that the density of the solid waste aggregate is improved; the bentonite is filled in the pores of the solid waste aggregate, and when the concrete is prepared, the bentonite expands when meeting water to effectively discharge air in the pores, so that the porosity is reduced; the hydrated calcium silicate gel crystal seeds are pre-filled into the pores of the solid waste aggregate, so that the crystal seeds grow in situ in the pores in the process of preparing the concrete, gas in the pores of the solid waste aggregate is discharged in an auxiliary mode, the pores of the solid waste aggregate can be occupied in a hydrogel mode, water consumption is reduced, and the water bleeding phenomenon of the concrete can be reduced.

In the regulator for solid waste aggregates in the embodiment of the disclosure, the component A has rich hydroxyl groups, is alkalescent, does not contain chloride ions, is nontoxic and noncorrosive, and is a high-performance green environment-friendly material. The component A is simple in component, and excellent performance is achieved by regulating and controlling the reasonable proportion of 5 components. Meets the GB8076-2008 concrete additive specification, and can be widely used for various concrete projects. In the component A, the polycarboxylic acid mother liquor is transparent or light yellow viscous liquid, has no pungent smell, has the boiling point of 100 ℃, the density of 1.080 +/-0.02 g/mL, the viscosity of 10-50 Pa.s and the water reduction rate of more than or equal to 25 percent. The polycarboxylic acid mother liquor is a weakly alkaline material, is soluble in water, is non-toxic and non-corrosive, and has no explosion and flammability dangers, thereby being a relatively green and environment-friendly product. Diethanol monoisopropanolamine, a clear, colorless, slightly odorous liquid with a boiling point of 145 ℃ and a density of 1.03g/cm³As water reducing agent and surfactant. Triisopropanolamine: transparent colorless liquid with density of 1.02g/cm³The pH value is 5-7, the critical temperature is 200 ℃ (1013hPa), triisopropanolamine is used as a cement grinding aid and an early strength agent, and the early strength effect is achieved by promoting the early coagulation characteristic. Glycerol: colorless, odorless, sweet in flavor, clear, viscous liquid in appearance, and relative density 1.26362. Melting point 17.8 deg.C, boiling point 290.0 deg.C (in minutes) Solution), refractive index 1.4746, flash point (open cup) 176 ℃, as a moisture absorbent, to achieve a certain drying effect. Sodium sulfate: sodium sulfate (Na)₂SO₄) Is salt formed by combining sulfate radical and sodium ion, is neutral salt of sulfuric acid, and is very stable salt. Is easily soluble in water, and the water solution is weakly alkaline, and is soluble in glycerol but insoluble in ethanol. The high purity, finely divided anhydrate is called glauber's salt. The anhydrous sodium sulphate is white, odorless and bitter crystal or powder, has hygroscopicity, and is colorless, transparent, large crystal or granular small crystal. The sodium sulfate can make the hydrated product calcium sulphoaluminate generate more quickly, thereby accelerating the hydration hardening speed of the cement and improving the early strength of the concrete by 50 to 100 percent. Therefore, in the component A of the embodiment of the disclosure, water is mainly used as raw material and auxiliary material mixed water, no waste liquid is generated, no cleaning is needed after stirring, and no production wastewater is generated. And no waste gas is generated in the stirring process.

Therefore, the component A in the conditioning agent for solid waste aggregate in the embodiment of the disclosure has the following action principle when preparing concrete:

1. the high-polarity molecular groups in the component A can generate stronger chemical reaction with a cement matrix, and can easily form covalent bonds with metal ions by a pair of functional groups containing N atoms in molecules to generate complex reaction, so that the dissolution rates of C3S and C4AF in the cement are improved, the volume of cement paste is increased, the wrapping property of a cementing material is improved, the compactness of the cement is improved, and the strength of the cement is improved;

2. The component A can allow Ca (OH) in a cement liquid phase₂The supersaturation degree is improved, so that the saturation point doping amount of the water reducing agent is effectively improved, segregation and bleeding are not easy to generate, and meanwhile, the C3A is effectively prevented from being hydrated in early stage to generate a loose crystalline phase structure, so that the compactness of the cement during hardening is further improved;

3. the component A can promote the dissolution of iron ions and improve the hydration rate of ferrite, so that the later strength of the cement is improved;

4. the component A can go deep into the fine gaps in the sandstone aggregate in a microscopic way to form covalent bonds, so that the transition area of the cement matrix and the section of the sandstone is improved, and the adhesive force of cement stone is improved.

In the disclosed embodiment, a polycarboxylic acid mother liquor, diethanol monoisopropanolamine, triisopropanolamine, glycerol, sodium sulfate and water are prepared according to the weight percentage of the component A. Adding sodium sulfate into partial water to dissolve to obtain a sodium sulfate solution; and then mixing the polycarboxylic acid mother liquor, diethanolisopropanolamine, triisopropanolamine, glycerol and a sodium sulfate solution, and uniformly stirring to obtain the component A in the regulator disclosed by the embodiment of the disclosure.

In some embodiments, the component a comprises, by weight: 3 to 5 percent of polycarboxylic acid mother liquor, 1 to 3 percent of diethanolisopropanolamine, 0.1 to 0.3 percent of triisopropanolamine, 1 to 3 percent of glycerol and 0.1 to 0.3 percent of sodium sulfate; the solvent is water. The proportion of each component is more finely regulated and controlled, so that the mutual synergistic effect among the raw materials is better, and the synergistic effect is better played.

In some embodiments, the component a comprises, by weight: 4% of polycarboxylic acid mother liquor, 2% of diethanolisopropanolamine, 0.2% of triisopropanolamine, 2% of glycerol and 0.2% of sodium sulfate; the solvent is water. The proportion of each component is accurately regulated and controlled, so that the mutual synergistic action among the raw materials is optimal, and the synergistic action is better played.

In the embodiment of the disclosure, the component B can be obtained by mixing and ball-milling the components.

In some embodiments, the component B comprises, by weight: 97 to 99 parts of inorganic composite filler and 1 to 3 parts of surfactant.

Optionally, the component B comprises the following components in parts by weight: 98 parts of inorganic composite filler and 2 parts of surfactant.

In some embodiments, the weight ratio of the ground limestone, the micro-nano titanium dioxide, the calcium silicate hydrate gel seed crystals and the bentonite in the inorganic composite filler in the component B is 6-9: 2-3: 1.5: 1 in sequence.

Optionally, in the inorganic composite filler in the component B, the weight ratio of the ground limestone, the micro-nano titanium dioxide, the calcium silicate hydrate gel seed crystal and the bentonite is 8: 2.5: 1.5: 1 in sequence.

In the embodiment of the disclosure, the surfactant in the component B can prevent the inorganic composite filler from agglomerating, so that the inorganic composite filler is uniformly mixed. The surfactant is not particularly limited, and may be one or a mixture of two of a cationic surfactant and a zwitterionic surfactant.

In some embodiments, the surfactant is a cationic surfactant. Optionally, the cationic surfactant comprises C₁₅～C₁₈An alkyl quaternary ammonium salt type cationic surfactant.

In some embodiments, the surfactant is a zwitterionic surfactant. Optionally, the zwitterionic surfactant comprises C₁₅～C₁₈Alkyl dimethyl betaines.

In some embodiments, the surfactant is a mixture of a cationic surfactant and a zwitterionic surfactant. Optionally, the surfactant comprises C₁₅～C₁₈Alkyl quaternary ammonium salt type cationic surfactant and C₁₅～C₁₈Alkyl dimethyl betaine, and the two can be mixed in any proportion.

The embodiment of the disclosure discloses a method for adjusting solid waste aggregate by adopting the conditioning agent for solid waste aggregate, which comprises the following steps:

s10, adding the component B into the solid waste aggregate, and performing ball milling and uniform mixing to obtain a mixed material; wherein the mass ratio of the solid waste aggregate to the component B is 1: 0.1-0.2;

s20, adding the component A into the mixture obtained in the step S10, and performing ball milling and uniform mixing to finish the method for adjusting the solid waste aggregate; the dosage of the component A is 0.5 to 1 percent of the mass of the solid waste aggregate.

In the method of the embodiment of the disclosure, the component B is added firstly to fill the pores in the solid waste aggregate, discharge the gas in the pores of the solid waste aggregate, and reduce the water absorption of the solid waste aggregate; and adding the component A, coating and modifying the surface of the solid waste aggregate, and enabling the components in the component A to act with the cementing material when subsequently mixing with the fine aggregate and the cementing material, so that the performance of the obtained concrete is improved.

In the method of the disclosed embodiment, the preparation of the component B adopts the following method: respectively preparing inorganic composite filler and surfactant according to the component B, mixing the inorganic composite filler and the surfactant, and performing ball milling to obtain the component B.

Alternatively, in step S10, the mass ratio of the solid waste aggregate to the component B is 1: 0.15.

Alternatively, in step S20, the amount of the component a is 0.8% by mass of the solid waste aggregate.

In some embodiments, in step S10, the solid waste aggregate is reinforced solid waste aggregate; the strengthening method for strengthening the solid waste aggregate comprises the following steps: carrying out strengthening treatment on the solid waste aggregate by adopting a wood wax oil modified component to obtain strengthened solid waste aggregate; the wood wax oil modified component comprises, by weight, 50 parts of tung oil, 10 parts of orange oil, 10 parts of moringa seed oil, 5 parts of pine oil and 5 parts of nano-filler. The solid waste aggregate treated by the wood wax oil modification component at least forms an oil immersion layer on the surface of the solid waste aggregate, and the nano filler can be immersed into the surface layer of the solid waste aggregate along with the wood wax oil, so that the surface layer strength is enhanced. The solid waste aggregate with small particle size can be completely soaked by the wood wax oil, and the strength is further improved.

In some embodiments, when the solid waste aggregate is reinforced solid waste aggregate, the surfactant in the component B is preferably a mixture of a cationic surfactant and a zwitterionic surfactant. Optionally, the surfactant comprises C ₁₅～C₁₈Alkyl quaternary ammonium salt type cationic surfactant and C₁₅～C₁₈Alkyl dimethyl betaine, and the two can be mixed in any proportion. The hydrophobic group of the surfactant is connected to the surface of the reinforced solid waste aggregate, so that the inorganic composite filler can be ensured to be filled into the pores of the reinforced solid waste aggregate.

In the embodiment of the disclosure, in the process of infiltrating and ball-milling the solid waste aggregate by the wood wax oil, the edges and corners on the surface of the solid waste aggregate particles are rubbed to become smooth, the surface becomes smooth, and some cement mortar on the surface of the solid waste aggregate can also fall off. Moreover, the nano filler in the wood wax oil modified component can invade into microcracks on the surfaces of the solid waste aggregate particles, so that the hardness of the solid waste particles can be enhanced while the microcracks are filled.

In the embodiment of the disclosure, the wood wax oil modification component is easy to obtain all components, low in cost and simple and effective in modification method. And the modified components of the wood wax oil can be recycled, so that the cost is further reduced. The wood wax oil modified component is prepared by uniformly mixing all the components. Of course, it is also possible to perform a heat treatment to polymerize each vegetable oil and enhance the wetting effect, for example, a method for preparing the wood wax oil modified component includes: heating mixed vegetable oil of tung oil, orange oil, moringa seed oil and pine oil for pretreatment and impurity removal; preserving the heat of the vegetable oil after impurity removal for 16 hours at the temperature of 200 ℃ in the nitrogen protective atmosphere to obtain polymerized vegetable oil; and mixing the polymerized vegetable oil and the nano filler, heating and ultrasonically dispersing to obtain the wood wax oil modified component in a dispersion system.

In some embodiments, a method of strengthening solid waste aggregate, comprising:

s31, heating the solid waste aggregate to 50-60 ℃, preserving heat for 1-2 hours, and removing water in the solid waste aggregate to obtain dry solid waste aggregate;

s32, adding wood wax oil modified components into the dry solid waste aggregate obtained in the step S31, and carrying out ball milling for 2-3 h; then discharging the modified components of the wood wax oil, and then oscillating to remove impurities to obtain oil-impregnated solid waste aggregate; wherein the volume ratio of the wood wax oil modified component to the dry solid waste aggregate is 0.3-0.5: 1;

s33, airing the oil-impregnated solid waste aggregate obtained in the step S32 to obtain the reinforced solid waste aggregate.

In step S33, the film may be dried naturally or air-dried.

In some embodiments, the wood wax oil modifying component includes a nanofiller comprising nano high-hard husk powder. The high-hardness shell includes, but is not limited to, walnut shell and date pit, and other shells capable of reaching the hardness of the walnut shell or date pit can be used. The nano high-hardness shell powder is used as the nano filler, so that the nano high-hardness shell powder is favorably and uniformly mixed with the wood wax oil and is more favorably infiltrated into the solid waste aggregate along with the vegetable oil.

The embodiment of the disclosure discloses concrete, which comprises a cementing material, a coarse aggregate, a fine aggregate and a water reducing agent; wherein, the coarse aggregate and/or the fine aggregate adopt the solid waste aggregate regulated by the method; the dosage of the water reducing agent is 3-4% of the weight of the cementing material.

In the concrete of the embodiments of the present disclosure, the cementitious material is cement.

In the concrete of the embodiments of the present disclosure, the water reducing agent includes a polycarboxylic acid water reducing agent. The polycarboxylic acid water reducing agent adopted in the component A in the regulator for solid waste aggregates can be adopted.

Optionally, the amount of the water reducing agent is 3.3-3.8% of the weight of the cementing material.

Optionally, the water reducing agent is used in an amount of 3.6% by weight of the cementitious material.

The embodiment of the disclosure discloses that in concrete, aggregate can be replaced by solid waste aggregate adjusted by the method.

In some embodiments, both coarse and fine aggregates are solid waste aggregates conditioned by the methods described above. The particle size of the coarse aggregate and the fine aggregate is the conventional particle size. The aggregate is the concrete obtained by adopting the solid waste aggregate regulated by the regulation method, and the performance of the concrete is equivalent to that of the concrete adopting natural sandstone.

In some embodiments, the coarse aggregate is solid waste aggregate conditioned by the method described above; the fine aggregate is natural sand and/or machine-made sand.

In the embodiment of the disclosure, when the fine aggregate is the machine-made sand, the component A in the regulator for solid waste aggregate can be used for modifying the fine aggregate. The surface of the machine-made sand adsorbs the regulator, and particularly, the regulator is coated on the surface of stone powder in the machine-made sand, so that the viscosity brought by the stone powder is reduced, and the fluidity of concrete is favorably improved.

In some embodiments, the mechanical sand modification treatment comprises:

step 41, adding water to dilute the component A to obtain a diluted component A; wherein the mixing ratio of the component A to water is 1: 2-5;

step 42, heating the machine-made sand to 45-55 ℃, then mixing and uniformly stirring the diluted component A and the machine-made sand, preserving heat for 1-2 hours, and cooling to obtain modified machine-made sand; wherein the volume ratio of the diluted component A to the machine-made sand is 1: 90-120.

In the embodiment, the component A can be bonded with the machine-made sand on the surface of the machine-made sand, so that the compound is grafted on the surface of the machine-made sand in situ, the viscosity caused by stone powder in the machine-made sand can be better reduced, the subsequent fusion connection with other materials such as cement is facilitated, the fluidity of the concrete is improved, and the physical properties such as the compressive strength of the concrete are improved.

Optionally, the A component is diluted, and the mixing ratio of the A component to water is 1: 3-5. Optionally, the mixing ratio of the A component and water is 1: 4.

Optionally, heating the machine-made sand to 50 ℃, mixing and stirring the diluted component A and the machine-made sand uniformly, preserving heat for 1.5 hours, and cooling to obtain modified machine-made sand; wherein, the volume ratio of the diluted component A to the machine-made sand is 1: 100.

In some embodiments, the concrete further comprises an admixture, wherein the weight ratio of the admixture to the cementitious material is 0.5-1: 1; the admixture comprises fly ash, pumice powder and zeolite powder; wherein the weight ratio of the fly ash to the pumice powder is 1: 0.5-0.8; the weight ratio of the fly ash to the zeolite powder is 1: 0.5-0.8. In the embodiment of the disclosure, the admixture is a mixture of fly ash, pumice powder and zeolite powder. Pumice powder is a volcano-ejected lightweight porous rock with a developed pore structure. The main chemical components of the pumice powder are ferric oxide and aluminum oxide. The zeolite powder is prepared by grinding natural zeolite rock. Zeolite is a naturally calcined pozzolanic aluminosilicate mineral. The aluminosilicate in the zeolite powder can react with carbonate in stone powder of the machine-made sand to generate the aluminosilicate to offset the influence of the stone powder amount on the cement strength, so that the machine-made sand can completely replace natural river sand, and the strength of concrete can be further improved.

Optionally, the weight ratio of the fly ash to the pumice powder is 1: 0.6; the weight ratio of the fly ash to the zeolite powder is 1: 0.6.

in some embodiments, the pumice powder has a particle size of 1-5 μm and the zeolite powder has a particle size of 10-200 nm. The zeolite powder can be filled into the pore structure of the pumice powder, so that the specific gravity of the pumice powder is increased, the dispersibility of the pumice powder in concrete is improved, the pumice powder is in contact reaction with cement fully, and the performance of the concrete is improved.

In some embodiments, a method of making an admixture comprises: ball-milling the zeolite powder for 30 min-1 h, adding pumice powder, and ball-milling for 1-2 h; finally adding the fly ash, and ball-milling and mixing for 30-45 min. And obtaining the admixture. Zeolite powder can be filled in the air holes of the pumice powder, so that the specific gravity of the pumice powder is improved, the dispersibility of the pumice powder in concrete is improved, the pumice powder is in contact reaction with cement fully, and the performance of the concrete is improved.

In some embodiments, the admixture is present at a weight ratio of 0.5 to 0.8: 1. The cement consumption is reduced.

Optionally, the weight ratio of admixture to cementitious material is 0.65: 1.

In the embodiment of the present disclosure, the ratio of each component in the concrete may be based on the ratio of the conventional concrete, or may be specifically blended according to the actual situation, which is not limited.

In some embodiments, the concrete comprises, in parts by weight: 150 to 200 parts of cementing material, 800 to 1000 parts of coarse aggregate, 800 to 1200 parts of fine aggregate, 4.5 to 8 parts of water reducing agent, 100 to 150 parts of admixture and 100 to 200 parts of water. The amount of each component may be any amount within the range, and will not be described herein.

Optionally, the concrete comprises, by weight: 160-190 parts of cementing material, 800-900 parts of coarse aggregate, 1000-1100 parts of fine aggregate, 5.2-7.2 parts of water reducing agent, 100-130 parts of admixture and 130-180 parts of water.

Optionally, the concrete comprises, by weight: 180 parts of cementing material, 850 parts of coarse aggregate, 1050 parts of fine aggregate, 6.5 parts of water reducing agent, 120 parts of admixture and 160 parts of water.

Specific examples of the embodiments of the present disclosure are given below.