阅读说明：本技术 耐刮擦低烟无卤阻燃聚烯烃电缆料 (Scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material ) 是由 董建东 何亚丽 于 2020-07-04 设计创作，主要内容包括：本发明涉及电缆的技术领域,具体涉及一种耐刮擦低烟无卤阻燃聚烯烃电缆料,包括如下重量份数的组分：EVA 30-50份、HDPE 50-70份、LDPE 15-25份、阻燃剂90-120份、相容剂8-12份、偶联剂1-2份、抗氧剂0.5-0.8份及润滑剂0.5-1.0份；其中,润滑剂至少由改性硅酮母粒、硬脂酸及芥酸酰胺混配而成。本发明提供的耐刮擦低烟无卤阻燃聚烯烃电缆料具有耐刮擦性能好的效果。(The invention relates to the technical field of cables, in particular to a scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material which comprises the following components in parts by weight: 30-50 parts of EVA, 50-70 parts of HDPE, 15-25 parts of LDPE, 90-120 parts of flame retardant, 8-12 parts of compatilizer, 1-2 parts of coupling agent, 0.5-0.8 part of antioxidant and 0.5-1.0 part of lubricant; wherein, the lubricant is prepared by mixing modified silicone master batch, stearic acid and erucamide. The scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material provided by the invention has a good scratch-resistant effect.)

1. The scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material is characterized by comprising the following components in parts by weight:

30-50 parts of EVA, 50-70 parts of HDPE, 15-25 parts of LDPE, 90-120 parts of flame retardant, 8-12 parts of compatilizer, 1-2 parts of coupling agent, 0.5-0.8 part of antioxidant and 0.5-1.0 part of lubricant; wherein, the lubricant is prepared by mixing modified silicone master batch, stearic acid and erucamide.

2. The scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material according to claim 1, characterized in that: the preparation method of the modified silicone master batch comprises the following steps: 1) uniformly mixing PVC resin, silicone powder, a foaming agent and modified ramie fibers, and preheating; 2) melting and extruding the mixture to obtain a modified silicone strip; 3) and cooling, drying and cutting the modified silicone strip to obtain the modified silicone master batch.

3. The scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material according to claim 2, characterized in that: the preparation method of the modified ramie fiber comprises the following steps: 1) soaking the ramie fibers in a sodium hydroxide solution for 12-14 h; 2) cleaning and drying the soaked ramie fibers; 3) and crushing the dried ramie fibers to obtain the modified ramie fibers.

4. The scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material according to claim 1, characterized in that: the modified silicone master batch comprises the following components: stearic acid: the weight portion ratio of the erucamide is 15: 3: 7.

5. the scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material according to claim 1, characterized in that: the flame retardant is at least formed by mixing aluminum hydroxide and magnesium hydroxide.

6. The scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material according to claim 5, characterized in that: the flame retardant needs to be pretreated, and the treatment method comprises the following steps: 1) adding the flame retardant into a high-speed mixer, uniformly mixing, and preheating; 2) slowly spraying the coupling agent into the high-speed mixer in a mist form to uniformly mix the flame retardant and the coupling agent; 3) and drying the flame retardant to obtain the treated flame retardant.

7. The scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material according to claim 1, characterized in that: the antioxidant comprises one or more of antioxidant 2246, antioxidant CA and antioxidant 1010.

8. The scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material according to any one of claims 1 to 7, characterized in that: the preparation method of the scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material comprises the following steps: 1) uniformly mixing EVA, HDPE and LDPE in parts by weight, and then banburying to obtain a mixture; 2) adding a flame retardant, a compatilizer, a coupling agent, an antioxidant and a lubricant into the mixture, uniformly mixing, and then banburying again to obtain a banburying mixture; 3) and extruding, granulating, finishing, cooling and screening the banburying mixture to obtain the scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material.

Technical Field

The invention relates to the technical field of cables, in particular to a scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material.

Background

With the rapid development of global economy and the enhancement of environmental awareness of human beings, the requirements of various fields on the quality and the performance of electric wires and cables are higher and higher. Fire caused by aging of wires and cables is increasing, so that low smoke, halogen-free, flame retardant and environmental protection are also development directions of the wire and cable industry. The demand of the halogen-free low-smoke flame-retardant cable material is increasing, and most of the halogen-free low-smoke flame-retardant cable materials are produced by adding a large amount of flame retardant into a polyolefin base material to achieve a flame-retardant effect.

In the production, transportation and use processes of the electric wire and the cable, the phenomena of friction, scraping and the like caused by the inevitable friction between the electric wire and the cable or the friction of hard objects are generated, and the appearance of the electric wire and the cable is greatly influenced. Therefore, how to improve the scratch resistance of the cable material, thereby improving the scratch resistance of the electric wire and the electric cable, is a very important and urgent problem to be solved.

Disclosure of Invention

Aiming at the defects in the prior art, the invention aims to provide a scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material which has a good scratch-resistant effect.

In order to achieve the purpose, the invention provides the following technical scheme:

a scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material comprises the following components in parts by weight:

30-50 parts of EVA, 50-70 parts of HDPE, 15-25 parts of LDPE, 90-120 parts of flame retardant, 8-12 parts of compatilizer, 1-2 parts of coupling agent, 0.5-0.8 part of antioxidant and 0.5-1.0 part of lubricant; wherein, the lubricant is prepared by mixing modified silicone master batch, stearic acid and erucamide.

By adopting the technical scheme, the surface energy of the modified silicone master batch is low and the modified silicone master batch is easy to migrate to the surface of the cable material, so that a compact silicone lubricating layer is formed on the surface of the cable material, the friction coefficient of the surface of the cable material is reduced, and the scratch resistance of the surface of the cable material is improved; stearic acid is an internal lubricant, has good compatibility with each component of the raw material, and can be uniformly dispersed among molecular chains, so that the interaction among the molecular chains is weakened, the external lubricant erucamide is more easily transferred to the surface of the cable material, a lubricant molecular layer is formed on the surface of the cable material, the friction coefficient of the surface of the cable material is further reduced, and the scratch resistance of the cable material is improved; the EVA, the HDPE and the LDPE are used as basic resin, so that the cable material has the corrosion resistance, low temperature resistance and flexibility of the EVA, the wear resistance, electrical insulation and chemical stability of the HDPE, and the extensibility and easy processing performance of the LDPE; the flame retardant can improve the flame retardant property of the cable and ensure the use safety of the cable; the compatibility of the resin in the raw materials and other additives is poor, and the addition of the compatilizer can improve the surface activity of the resin and other additives, so that the resin and other additives can be uniformly mixed, and the uniformity of the quality of the cable material is ensured; the coupling agent generally comprises two active groups, namely an inorganic group and an organic group, so that the coupling agent can play a role in binding resin and inorganic auxiliary agent, so that the connection between the components of the raw materials is more stable, and the stability of the cable material is ensured; the antioxidant can delay or inhibit the oxidation process of the raw materials, so that the aging speed of the raw materials is slowed down, and the service life of the cable material is prolonged.

The invention is further provided with: the preparation method of the modified silicone master batch comprises the following steps: 1) uniformly mixing PVC resin, silicone powder, a foaming agent and modified ramie fibers, and preheating; 2) melting and extruding the mixture to obtain a modified silicone strip; 3) and cooling, drying and cutting the modified silicone strip to obtain the modified silicone master batch.

The modified silicone master batch has a small addition amount and is difficult to uniformly disperse in the raw materials, and by adopting the technical scheme, the foaming agent is uniformly mixed with the PVC resin, the silicone powder and the modified ramie fibers, and can change the PVC resin, the silicone powder and the modified ramie fibers to form pores in the molecular structure, so that the modified silicone master batch with the same weight part has larger volume, a small amount of modified silicone master batch can be uniformly dispersed in the raw materials, and the uniformity of the performance of the raw materials is ensured; meanwhile, various materials are filled with each other, and PVC resin is filled in the silicone powder, so that the mechanical property of the silicone powder can be ensured; the modified ramie fiber is very tough, has high strength and low extensibility, and has good wear resistance, so that the wear resistance of the modified silicone master batch can be improved, and the wear resistance of the cable material is further improved.

The invention is further provided with: the preparation method of the modified ramie fiber comprises the following steps: 1) soaking the ramie fibers in a sodium hydroxide solution for 12-14 h; 2) cleaning and drying the soaked ramie fibers; 3) and crushing the dried ramie fibers to obtain the modified ramie fibers.

By adopting the technical scheme, the ramie fibers are relatively stiff due to high modulus, and after being soaked in alkali liquor, the ramie fibers shrink in length, swell in diameter and form curls on the surface, so that the modified ramie fibers are obtained; the modified ramie fiber is more flexible, so that the flexibility of the cable material is improved, and meanwhile, the change of the internal structure of the modified ramie fiber enables PVC resin and silicone powder to be more easily interwoven with the modified ramie fiber into a whole, so that the quality of the modified silicone master batch is more uniform.

The invention is further provided with: the modified silicone master batch comprises the following components: stearic acid: the weight portion ratio of the erucamide is 15: 3: 7.

the invention is further provided with: the flame retardant is at least formed by mixing aluminum hydroxide and magnesium hydroxide.

By adopting the technical scheme, the aluminum hydroxide and the magnesium hydroxide release crystal water when being heated and decomposed, and a large amount of heat needs to be absorbed in the process, so that the cooling effect can be achieved, meanwhile, the water vapor generated by the reaction can dilute combustible gas, the spread of combustion is inhibited, and the purpose of flame retardance is achieved.

The invention is further provided with: the flame retardant needs to be pretreated, and the treatment method comprises the following steps: 1) adding the flame retardant into a high-speed mixer, uniformly mixing, and preheating; 2) slowly spraying the coupling agent into the high-speed mixer in a mist form to uniformly mix the flame retardant and the coupling agent; 3) and drying the flame retardant to obtain the treated flame retardant.

The aluminum hydroxide and the magnesium hydroxide are both inorganic materials, the compatibility with polymers is poor, in order to meet the specified flame retardant requirement, the addition amount of the combustion improver is large, and the flame retardant is easy to agglomerate.

The invention is further provided with: the antioxidant comprises one or more of antioxidant 2246, antioxidant CA and antioxidant 1010.

By adopting the technical scheme, the antioxidant 2246, the antioxidant CA and the antioxidant 1010 are all nontoxic pollution-free flame retardants, have good compatibility with resin, are easier to uniformly disperse in each component of the raw materials, and can effectively limit the aging of the cable, thereby prolonging the service life of the cable.

The invention is further provided with: the preparation method of the scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material comprises the following steps: 1) uniformly mixing EVA, HDPE and LDPE in parts by weight, and then banburying to obtain a mixture; 2) adding a flame retardant, a compatilizer, a coupling agent, an antioxidant and a lubricant into the mixture, uniformly mixing, and then banburying again to obtain a banburying mixture; 3) and extruding, granulating, finishing, cooling and screening the banburying mixture to obtain the scratch-resistant low-smoke halogen-free flame-retardant polyolefin cable material.

By adopting the technical scheme, the EVA, the HDPE and the LDPE are melted and mixed uniformly, so that the base resins are crosslinked and mixed more uniformly; then adding the flame retardant, the compatilizer, the coupling agent, the antioxidant, the lubricant and the like into the molten base resin, so that the various additives and the base resin are mixed more uniformly, and the uniformity of the performance of the cable material is ensured; the whole preparation process is simple, easy to operate and suitable for mass production of a large amount of cable materials.

In conclusion, the beneficial technical effects of the invention are as follows:

1. the surface energy of the modified silicone master batch is low and the modified silicone master batch is easy to migrate to the surface of the cable material, so that a compact silicone lubricating layer is formed on the surface of the cable material, the friction coefficient of the surface of the cable material is reduced, and the scratch resistance of the surface of the cable material is improved; stearic acid is an internal lubricant, has good compatibility with each component of the raw material, and can be uniformly dispersed among molecular chains, so that the interaction among the molecular chains is weakened, the external lubricant erucamide is more easily transferred to the surface of the cable material, a lubricant molecular layer is formed on the surface of the cable material, the friction coefficient of the surface of the cable material is further reduced, and the scratch resistance of the cable material is improved;

2. the foaming agent is uniformly mixed with the PVC resin, the silicone powder and the modified ramie fibers, and can change the PVC resin, the silicone powder and the modified ramie fibers to form pores in the molecular structure, so that the modified silicone master batches with the same weight part have larger volume, a small amount of modified silicone master batches can be uniformly dispersed in the raw materials, and the uniformity of the performance of the raw materials is ensured;

3. the ramie fibers are relatively stiff due to high modulus, and after being soaked in alkali liquor, the ramie fibers shrink in length, swell in diameter and form curls on the surface to obtain modified ramie fibers; the modified ramie fiber is more flexible, so that the flexibility of the cable material is improved, and meanwhile, the change of the internal structure of the modified ramie fiber enables PVC resin and silicone powder to be more easily interwoven with the modified ramie fiber into a whole, so that the quality of the modified silicone master batch is more uniform.

Detailed Description

The present invention will be described in further detail with reference to examples.

The silicone masterbatch is MB20-002 silicone masterbatch produced by Dow Corning company.