阅读说明：本技术 高遮光度的防霉窗帘制造方法 (Method for manufacturing mould-proof curtain with high shading degree ) 是由 叶海军 于 2020-04-07 设计创作，主要内容包括：本发明公开了高遮光度的防霉窗帘制造方法,包括以下步骤：将普通丝线与抗菌丝线按3:1的比例混合成纺线；纺线通过经纬编织的方式编织成内衬布；内衬布和遮光布用亚克力乳液粘接,得到成品布匹。本发明的优点是：通过普通丝线与抗菌丝线的组合,让内衬布料具有一定的防霉特性,同时内衬布料再与遮光布复合,形成窗帘布,在朝向室内的部分看见内衬布,朝向室外部分为遮光布,提高了室内部分的美观度,同时可以在内衬布上印染各种图案,保证遮光性的同时丰富了窗帘的样式。(The invention discloses a method for manufacturing a mould-proof curtain with high shading degree, which comprises the following steps: mixing common silk threads and antibacterial silk threads in a ratio of 3:1 to form spinning threads; the textile yarns are woven into lining cloth in a warp and weft weaving mode; and (4) bonding the lining cloth and the shading cloth by using acrylic emulsion to obtain the finished cloth. The invention has the advantages that: through the combination of common silk thread and antibiotic silk thread, let inside lining cloth have certain mould proof characteristic, inside lining cloth is compound with shading cloth again simultaneously, forms the casement, sees inside lining cloth at the indoor part of orientation, and the outdoor part of orientation is shading cloth, has improved indoor part's pleasing to the eye degree, can dye on inside lining cloth simultaneously various patterns, has richened the style of (window) curtain when guaranteeing the light-proofness.)

1. The manufacturing method of the mould-proof curtain with high shading degree is characterized in that: the method comprises the following steps:

A. mixing common silk threads and antibacterial silk threads in a ratio of 3:1 to form spinning threads;

B. b, weaving the yarns obtained in the step A into lining cloth in a warp and weft weaving mode;

C. and D, bonding the lining cloth and the shading cloth obtained in the step B by using acrylic emulsion to obtain the finished cloth.

2. The method for manufacturing a mildewproof window curtain with high light-shielding degree according to claim 1, wherein the steps of: and B, in the step B, 100-140D of warp yarns and 70-90D of weft yarns.

3. The method for manufacturing a mildewproof window curtain with high light-shielding degree according to claim 1, wherein the steps of: and B, dyeing the common silk thread in the step A through a dye vat, and winding the common silk thread on an anti-hypha thread.

4. The method for manufacturing a mildewproof window curtain with high light-shielding degree according to claim 1, wherein the steps of: the pH value of the dyeing liquid in the dye vat is 5.2-6.

5. The method for manufacturing a mildewproof window curtain with high light-shielding degree according to claim 1, wherein the steps of: the common silk thread is cotton silk thread or cotton-covered polyester silk thread.

6. The method for manufacturing a mildewproof window curtain with high light-shielding degree according to claim 1, wherein the steps of: further comprising the step of D: and D, spraying a composite photocatalyst solution containing silver ions on the lining cloth after the finished cloth obtained in the step C is finished, then naturally shading and airing the lining cloth in a ventilated and dry place, and repeating the spraying and airing operation twice.

7. The method for manufacturing a mildewproof curtain with high light-shielding degree according to claim 6, wherein the molar concentration of the silver ions in the composite photocatalyst solution containing the silver ions is 0.6 to 0.8 mol/L.

Technical Field

The invention relates to a method for manufacturing a mould-proof curtain with high shading degree.

Background

People generally need to use curtains at home, but for curtains, the most important is the light-shading property, especially, projectors are installed in some families at present, the light-shading property is higher in use, the traditional curtains are made of cotton or chemical fiber materials, the light-shading property is not good, the attractiveness of the traditional curtains is affected by adopting light-shading cloth with an inner coating, and the common curtains can also face the problem of mildewing after being used for a long time.

Disclosure of Invention

The invention aims to provide a method for manufacturing a mildewproof curtain with high shading degree, which can effectively solve the problems that the existing curtain is easy to mildew and the shading degree is not enough.

In order to solve the technical problems, the invention is realized by the following technical scheme:

the manufacturing method of the mould-proof curtain with high shading degree comprises the following steps:

A. mixing common silk threads and antibacterial silk threads in a ratio of 3:1 to form spinning threads;

B. b, weaving the yarns obtained in the step A into lining cloth in a warp and weft weaving mode;

C. and D, bonding the lining cloth and the shading cloth obtained in the step B by using acrylic emulsion to obtain the finished cloth.

Preferably, the warp yarns in the step B are 100-140D, and the weft yarns in the step B are 70-90D. The warp yarns are thicker than the weft yarns, so that dust falls easily, and the dust attached to the curtain is reduced.

Preferably, the common silk thread in the step A is dyed in a dye vat and then wound on an antibacterial silk thread, so that the characteristics of the antibacterial silk thread are fully exerted, the common silk thread wound on the common silk thread can also play an antibacterial role, the antibacterial silk thread is not dyed, and the antibacterial characteristics of the antibacterial silk thread are not influenced.

Preferably, the pH value of the dyeing liquid in the dye vat is 5.2-6. The dyeing liquid with the pH value has soft hand feeling, is not easy to produce crease, is dark in color and is not easy to fade.

Preferably, the common silk thread is cotton silk thread or cotton-covered polyester silk thread. Effectively reducing the cost of the lining cloth.

Preferably, the method further comprises the step D: and D, spraying a composite photocatalyst solution containing silver ions on the lining cloth after the finished cloth obtained in the step C is finished, then naturally shading and airing the lining cloth in a ventilated and dry place, and repeating the spraying and airing operation twice. Further, the inner lining cloth is subjected to mildew-proof treatment, so that the mildew resistance of the inner lining cloth is improved.

Preferably, in the composite photocatalyst solution containing silver ions, the molar concentration of the silver ions is 0.6-0.8 mol/L, and sufficient silver ion solubility is ensured to play a role in sterilization and mildew prevention.

Compared with the prior art, the invention has the advantages that: through the combination of common silk thread and antibiotic silk thread, let inside lining cloth have certain mould proof characteristic, inside lining cloth is compound with shading cloth again simultaneously, forms the casement, sees inside lining cloth at the indoor part of orientation, and the outdoor part of orientation is shading cloth, has improved indoor part's pleasing to the eye degree, can dye on inside lining cloth simultaneously various patterns, has richened the style of (window) curtain when guaranteeing the light-proofness.

Detailed Description

The following detailed description of the embodiments of the present invention is intended to be illustrative, and not to be construed as limiting the invention.

The manufacturing method of the mould-proof curtain with high shading degree comprises the following steps:

A. mixing common silk threads and antibacterial silk threads in a ratio of 3:1 to form spinning threads;

B. b, weaving the yarns obtained in the step A into lining cloth in a warp and weft weaving mode;

C. b, bonding the lining cloth and the shading cloth obtained in the step B by using acrylic emulsion to obtain finished cloth;

D. and D, after the finished cloth obtained in the step C is finished, spraying a composite photocatalyst solution containing silver ions on the lining cloth, then placing the lining cloth in a ventilated and dry place for natural sun shading and airing, and repeating the spraying and airing operation twice to obtain the final curtain.

The common silk threads in the step A are dyed in the dye vat and then wound on the anti-silk thread, so that the anti-bacterial silk threads are less affected by dye and keep the anti-bacterial property, the pH value of the dyeing liquid in the dye vat is kept at 5.2-6, the dye is easier to color, and the common silk threads are cotton silk threads or cotton-covered polyester silk threads, so that the common silk threads are easier to dye and are convenient to weave patterns at the later stage.

And in the step B, 100-140D of the warp yarns and 70-90D of the weft yarns are adopted, so that dust falling on the curtain is easier to fall.

The antibacterial silk thread and the acrylic latex used in the scheme are both products directly purchased from the market. By adopting the scheme, through the combination of the common silk thread and the antibacterial silk thread, the lining cloth material has certain mildew-proof property, and is compounded with the shading cloth to form the curtain cloth, the lining cloth material is seen from the part facing indoors, and the shading cloth is arranged from the part facing outdoors, so that the attractiveness of the indoor part is improved, various patterns can be printed on the lining cloth, and the style of the curtain is enriched while the shading property is ensured.

The above description is only an embodiment of the present invention, but the technical features of the present invention are not limited thereto, and any changes or modifications within the technical field of the present invention by those skilled in the art are covered by the claims of the present invention.