阅读说明：本技术 一种大漆镀金银玻璃器皿的生产工艺 (Production process of lacquer gold-silver-plated glassware ) 是由 江扬 江欣洁 于 2020-05-21 设计创作，主要内容包括：本发明公开了一种大漆镀金银玻璃器皿的生产工艺,包括步骤：备料,除尘,刷漆,上漆打磨,髹涂打捻,髹涂色漆和二次打磨,通过分步的大漆和彩漆以及打磨的配合,并且通过不同的上漆工艺,再配合打磨等工艺,生产出一种表面呈多种层次颜色的金胎杯,杯体表面带有多层色彩层次,使杯体外观美观大方,且杯体与漆层之间不容易出现脱胎的效果。(The invention discloses a production process of lacquer gold-silver plated glassware, which comprises the following steps: the method comprises the steps of preparing materials, removing dust, painting, polishing, painting and twisting, painting and coating colored paint and polishing for the second time, and producing the gold child cup with the surface in multiple levels of colors by matching the step-by-step lacquering and colored paint and polishing, and matching different painting processes, polishing and other processes.)

1. A production process of lacquer gold-silver-plated glassware comprises the following steps:

s1, preparing materials, namely preparing materials used for production, including raw lacquer, first polishing lacquer, second polishing lacquer, third polishing lacquer, gold foil, hairbrush, abrasive paper, a paint mixing disc, turpentine, sticky rice glue and a glass gold body cup with a gold (silver) plated layer;

s2, dust removal: dedusting the surface of the glass gold matrix cup to ensure that no foreign matters exist on the surface of the glass gold matrix cup, and simultaneously placing the glass gold matrix cup after dedusting into a dust-free processing station;

s3, painting: uniformly coating the raw lacquer on a gold (silver) plating layer on the outer surface of the glass gold tire cup, repeatedly coating a second layer of raw lacquer and a third layer of raw lacquer after the raw lacquer is solidified, coating a fourth layer of raw lacquer on the outer surface of the third layer of raw lacquer after the third layer of raw lacquer is dried, and drying the fourth layer of raw lacquer on the surface of the cup body in the shade;

s4, painting and polishing: after the fourth layer of raw lacquer is dried in the shade, coating the fifth layer of raw lacquer, and after the fifth layer of raw lacquer is dried in the shade, polishing the lacquer layer on the surface of the cup body by using dry abrasive paper to ensure that the lacquer surface on the surface of the cup body is smooth and flat;

s5, coating and twisting with lacquer: brushing the first polishing paint on the surface of the paint layer of the cup body by using a hairbrush, performing secondary brushing of the first polishing paint by using a twisting process after the first polishing paint is dried and solidified, and drying the cup body after the secondary brushing of the first polishing paint in the shade;

s6, coating a color paint with a coat of lacquer: after the second first polishing paint on the surface of the cup body is dried in the shade, the first polishing paint is coated on the surface of the paint layer of the cup body for the third time, the gold foil is used for inlaying and inlaying the mother-of-pear on the surface of the cup body, then the twisting process is used for coating the first polishing paint for the fourth time, after the first polishing paint coated for the fourth time is dried in the shade, the paint layer on the surface of the cup body is uniformly coated with the second polishing paint, after the second polishing paint is dried in the shade, the third polishing paint is uniformly coated on the surface of the second polishing paint, after the third polishing paint is dried in the shade, the first polishing paint is uniformly coated, the coating and the painting of the polishing paint are repeatedly carried out, the painting is repeatedly carried out until 30-35 layers of polishing paint are obtained, and the polishing paint is dried in the shade;

s7, secondary polishing, after the polishing paint on the surface of the cup body is dried in the shade, polishing the paint layer on the surface of the cup body by using water sand paper until the paint layer on the surface of the cup body has multiple levels of paint color textures, namely finishing the processing of the paint layer of the cup body, cleaning, dedusting and packaging the cup body, and finishing the processing.

2. The process according to claim 1, wherein the process comprises the following steps: the drying in the shade is to put the product into an environment which is dustless and can not contact with the sunlight, the air temperature is 20-28 ℃, and the air humidity is 78-82 percent for natural drying.

3. The process according to claim 2, wherein the step of manufacturing the lacquer gold-silver-plated glassware comprises the following steps: the twisting process comprises the steps of uniformly mixing the polishing paint mixed with the egg white, dipping the mixed polishing paint by using a tool, and uniformly spot-coating the surface of the paint layer on the surface of the cup body.

4. The process according to claim 1, wherein the process comprises the following steps: in the steps S3-S6, each time the upper layer of paint is completely dried, the next step of paint can be carried out.

5. The process according to claim 1, wherein the process comprises the following steps: the thickness of the paint layer connected with the glass-gold tire cup in the S3 is no more than 1/5 of the thickness of other paint layers.

Technical Field

The invention relates to the field of container processing, in particular to a production process of a lacquer gold-silver-plated glass vessel.

Background

Along with the economic basis of people is better and better, the quality of life pursued by people is higher and higher, for tea tasting, the tea drinker is elegant and comfortable artistic enjoyment, the tea drinker is not only an indispensable container when drinking tea, and has practicability, but also is favorable for improving the color, fragrance and taste of tea, meanwhile, a elegant and exquisite tea set also has appreciation value and is rich in artistry, if the appearance of the tea drinker is common, the experience of tea tasting can be greatly reduced, in addition, the outer surface of the glass cup of the cup body used by the invention is plated with a metal layer, and the phenomenon that a paint layer is stripped in the painting process or the using process can occur, and the quality of the product is influenced.

Disclosure of Invention

The invention provides a production process of lacquer gold-silver-plated glassware, which comprises the following steps:

s1, preparing materials, namely preparing materials used for production, including raw lacquer, first polishing lacquer and second polishing lacquer,

third polishing paint, gold foil, hairbrush, abrasive paper, paint mixing disc, turpentine, sticky rice glue and glass gold body cup with gold (silver) plating layer;

s2, dust removal: the surface of the glass gold matrix cup is dedusted, so that no foreign matters exist on the surface of the glass gold matrix cup,

simultaneously placing the glass gold matrix cup after dust removal into a dust-free processing station;

s3, painting: the raw lacquer is evenly coated on the gold (silver) plating layer on the outer surface of the glass gold tire cup,

repeatedly brushing a second layer of raw lacquer and a third layer of raw lacquer after the raw lacquer is solidified, after the third layer of raw lacquer is dried and solidified,

coating a fourth layer of raw lacquer on the outer surface of the third layer of raw lacquer, and drying the fourth layer of raw lacquer on the surface of the cup body in the shade;

s4, painting and polishing: after the fourth layer of raw lacquer is dried in the shade, coating the fifth layer of raw lacquer, and after the fifth layer of raw lacquer is dried in the shade, polishing the lacquer layer on the surface of the cup body by using dry abrasive paper to ensure that the lacquer surface on the surface of the cup body is smooth and flat;

s5, coating and twisting with lacquer: brushing the first polishing paint on the surface of the paint layer of the cup body by using a hairbrush, performing secondary brushing of the first polishing paint by using a twisting process after the first polishing paint is dried and solidified, and drying the cup body after the secondary brushing of the first polishing paint in the shade;

s6, coating a color paint with a coat of lacquer: after the second first polishing paint on the surface of the cup body is dried in the shade, the first polishing paint is coated on the surface of the paint layer of the cup body for the third time, the gold foil is used for inlaying and inlaying the mother-of-pear on the surface of the cup body, then the twisting process is used for coating the first polishing paint for the fourth time, after the first polishing paint coated for the fourth time is dried in the shade, the paint layer on the surface of the cup body is uniformly coated with the second polishing paint, after the second polishing paint is dried in the shade, the third polishing paint is uniformly coated on the surface of the second polishing paint, after the third polishing paint is dried in the shade, the first polishing paint is uniformly coated, the coating and the painting of the polishing paint are repeatedly carried out, the painting is repeatedly carried out until 30-35 layers of polishing paint are obtained, and the polishing paint is dried in the shade;

s7, secondary polishing, after the polishing paint on the surface of the cup body is dried in the shade, polishing the paint layer on the surface of the cup body by using water sand paper until the paint layer on the surface of the cup body has multiple levels of paint color textures, namely finishing the processing of the paint layer of the cup body, cleaning, dedusting and packaging the cup body, and finishing the processing.

Further, the drying in the shade is to put the product into an environment which is dustless and can not contact with sunlight, the air temperature is 20-28 ℃, and the air humidity is 78-82% for natural drying.

Further, the twisting process comprises the steps of uniformly mixing the polishing paint mixed with the egg white, dipping the mixed polishing paint by using a tool, and uniformly spot-coating the surface of the paint layer on the surface of the cup body.

Furthermore, in each of the steps S3-S6, the next step of painting can be performed after the paint on the upper layer is completely dried.

Furthermore, the thickness of the paint layer of the first layer connected with the glass-gold tire cup in the S3 is no more than 1/5 of the thickness of other paint layers.

The invention provides a production process of a lacquer gold-silver plating glassware, which has the following beneficial effects:

the paint layer outside the cup body is the multi-layer paint, the paint presents different levels of color textures, the color textures are more layered, the appearance of the cup body is more exquisite, the ornamental value is high, the use good feeling of a user is improved, the cup body can be used as an artwork ornament, the thickness of the first layer of lacquer is reduced, the adsorbability between the first layer of lacquer and the cup body is greatly increased, and the phenomenon that the paint layer of a product is stripped is prevented.

Detailed Description

The technical solutions of the present invention will be described clearly and completely with reference to the following embodiments of the present invention, and it should be understood that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.