阅读说明：本技术 一种具有防水防火特性的瓦楞纸浆 (Corrugated paper pulp with waterproof and fireproof characteristics ) 是由 鲍双铭 金乌兰 于 2019-11-13 设计创作，主要内容包括：一种具有防水防火特性的瓦楞纸浆属于造纸技术领域,其包括植物纤维、陶瓷纤维、氢氧化铝、氯化铵、松香胶、淀粉、氯化石蜡、三氧化二钛、硅油、阻燃剂、钛白粉、聚乙烯醇、乳胶、疏水剂、石蜡、软化剂和水以及植物油；其制作方法：先将植物纤维和陶瓷纤维搅拌均匀,再将松香胶、淀粉添加其内搅拌均匀；再添加氢氧化铝和氯化铵的水溶液搅拌均匀；再添加硅油、氯化石蜡和三氧化二钛溶液搅拌均匀；再添加阻燃剂、钛白粉和水搅拌均匀；先将聚乙烯醇溶液、乳胶和疏水剂溶液搅拌均匀,再添加石蜡和软化剂以及适量的水形成的溶液添加其内搅拌均匀,形成瓦楞纸浆,由瓦楞纸浆制成的瓦楞纸板,具有防火、阻燃、耐高温、防水、防潮的特性。(A corrugated paper pulp with waterproof and fireproof characteristics belongs to the technical field of paper making, and comprises vegetable fibers, ceramic fibers, aluminum hydroxide, ammonium chloride, rosin size, starch, chlorinated paraffin, titanium sesquioxide, silicone oil, a flame retardant, titanium dioxide, polyvinyl alcohol, latex, a hydrophobic agent, paraffin, a softener, water and vegetable oil; the manufacturing method comprises the following steps: firstly, uniformly stirring the plant fiber and the ceramic fiber, and then adding the rosin size and the starch into the mixture and uniformly stirring the mixture; then adding aqueous solution of aluminum hydroxide and ammonium chloride and stirring uniformly; then adding silicone oil, chlorinated paraffin and titanium sesquioxide solution and stirring uniformly; then adding the flame retardant, the titanium dioxide and the water and stirring uniformly; the corrugated paper board made of corrugated paper pulp has the characteristics of fire resistance, flame retardance, high temperature resistance, water resistance and moisture resistance.)

1. A corrugated paper pulp having waterproof and fireproof properties, characterized in that: the paper pulp comprises the following components in parts by weight: 45-60 parts of plant fiber, 40-50 parts of ceramic fiber, 20-30 parts of aluminum hydroxide, 20-30 parts of ammonium chloride, 10-20 parts of rosin size, 20-30 parts of starch, 10-20 parts of chlorinated paraffin, 10-20 parts of titanium trioxide, 10-20 parts of silicone oil, 20-30 parts of flame retardant, 20-30 parts of titanium dioxide, 30-40 parts of polyvinyl alcohol, 20-30 parts of latex, 20-30 parts of hydrophobic agent, 1-10 parts of paraffin, 10-20 parts of softener, a proper amount of water and a proper amount of plant oil.

2. The corrugated pulp having waterproof and fireproof properties according to claim 1, wherein: the manufacturing method of the corrugated paper pulp comprises the following steps:

step 1: firstly, plant fibers and ceramic fibers are put into a container and stirred uniformly;

step 2: adding rosin size and starch into the container, and uniformly stirring the rosin size and the starch with the uniformly stirred materials in the container in the step 1;

and step 3: dissolving aluminum hydroxide and ammonium chloride by using water, adding the solution into the container, and uniformly stirring the solution and the materials uniformly stirred in the step (2) in the container;

and 4, step 4: dissolving silicone oil, chlorinated paraffin and titanium sesquioxide by using vegetable oil, adding into the container, and uniformly stirring with the uniformly stirred material in the container in the step 3;

and 5: adding a flame retardant, titanium dioxide and a proper amount of water into the container, and uniformly stirring the mixture and the materials uniformly stirred in the container in the step (4);

step 6: uniformly stirring the polyvinyl alcohol solution, the latex and the hydrophobing agent solution, adding a solution formed by adding paraffin, a softening agent and a proper amount of water into the container, and uniformly stirring the solution and the materials uniformly stirred in the container in the step 5 to form paper pulp.

3. The corrugated pulp having waterproof and fireproof properties according to claim 2, wherein: the water in the step 3 is water with the temperature of 25-35 ℃.

4. The corrugated pulp having waterproof and fireproof properties according to claim 3, wherein: the water in the step 3 is water with the temperature of 30 ℃.

Technical Field

The invention belongs to the technical field of papermaking, and particularly relates to corrugated paper pulp with flame-retardant, waterproof, fireproof and high-temperature-resistant characteristics and a manufacturing method thereof.

Background

The corrugated case is a packaging product with the widest application, and the use amount is always the first of various packaging products. For more than half a century, corrugated cartons gradually replace transport packaging containers such as wooden boxes and the like with excellent service performance and good processing performance, and become the leading force of transport packaging. The corrugated case has the defects of poor fire resistance, water resistance, moisture resistance, high temperature resistance and flame retardance, and always suffers from the following defects of market fouling.

Disclosure of Invention

The invention aims to overcome the defects in the prior art and provides a formula of corrugated paper pulp with waterproof and fireproof characteristics and a manufacturing method of the corrugated paper pulp.

To achieve the object of the present invention, we will use the following technical solutions.

A corrugated paper pulp having waterproof and fireproof properties, characterized in that: the corrugated paper pulp comprises the following components in parts by weight: 45-60 parts of plant fiber, 40-50 parts of ceramic fiber, 20-30 parts of aluminum hydroxide, 20-30 parts of ammonium chloride, 10-20 parts of rosin size, 20-30 parts of starch, 10-20 parts of chlorinated paraffin, 10-20 parts of titanium trioxide, 10-20 parts of silicone oil, 20-30 parts of flame retardant, 20-30 parts of titanium dioxide, 30-40 parts of polyvinyl alcohol, 20-30 parts of latex, 20-30 parts of hydrophobic agent, 1-10 parts of paraffin, 10-20 parts of softener, a proper amount of water and a proper amount of plant oil.

The manufacturing method of the corrugated paper pulp comprises the following steps:

step 1: firstly, plant fibers and ceramic fibers are put into a container and stirred uniformly;

step 2: adding rosin size and starch into the container, and uniformly stirring the rosin size and the starch with the uniformly stirred materials in the container in the step 1;

and step 3: dissolving aluminum hydroxide and ammonium chloride by using water, adding the solution into the container, and uniformly stirring the solution and the materials uniformly stirred in the step (2) in the container;

and 4, step 4: dissolving silicone oil, chlorinated paraffin and titanium sesquioxide by using vegetable oil, adding into the container, and uniformly stirring with the uniformly stirred material in the container in the step 3;

and 5: adding a flame retardant, titanium dioxide and a proper amount of water into the container, and uniformly stirring the mixture and the materials uniformly stirred in the container in the step (4);

step 6: uniformly stirring polyvinyl alcohol solution, latex and hydrophobing agent solution, adding solution formed by adding paraffin, softening agent and proper amount of water into the container, and uniformly stirring the solution and the materials uniformly stirred in the container in the step 5 to form corrugated paper pulp.

Preferably, the water in step 3 is water at 25-35 ℃.

Most preferably, the water of step 3 is water at 30 ℃.

Advantageous effects

The corrugated paper pulp prepared by the method for preparing the corrugated paper pulp is placed in a mould for forming, and the obtained corrugated board can be baked on flame with the flame temperature of more than 1000 ℃ without burning, and has the characteristics of fire prevention, flame retardance and high temperature resistance; the corrugated board is not deformed when meeting water, is not corroded by water and has the characteristics of water resistance and moisture resistance; the corrugated paper pulp has the advantages of simple manufacturing method, good raw material beating performance, good quality of the obtained paper pulp, high pulping yield and high fiber binding force, and provides excellent paper pulp raw materials for manufacturing corrugated paper.

Detailed Description

To achieve the object of the present invention, we will further describe by examples.