阅读说明：本技术 一种超低温高锰钢用电弧焊焊条 (Arc welding electrode for ultralow-temperature high-manganese steel ) 是由 汪涛 汪昌红 包润新 陈成 蔡大江 魏艳 于 2021-07-20 设计创作，主要内容包括：本发明涉及焊接材料技术领域,尤其涉及一种超低温高锰钢用电弧焊焊条；焊条包括焊条钢芯和包裹在焊条钢芯外的药皮,所述焊条钢芯的成分为：C：0.35-0.46％,Si：0.06-0.18％,Mn：22-30％,Cr：3.7-4.6％,Ni:1.8-2.5％,Mo：1.3-2.1％,S：≤0.015％,P：≤0.015％,余量为Fe和不可避免的杂质,用水玻璃作为粘结剂,药皮占焊条总重量的35-40％,采用现有焊条生产设备及生产方法制备,其中所述药皮的成分及各成分占药皮的质量百分比为：大理石20-30％,碳酸锶5-10％,萤石18-25％,锆英砂3-6％,金红石4-8％,钛铁3-5％,磁铁矿3-8％,金属锰4-8％,金属铬4-6％,金属镍6-10％,金属钼2-4％,铜粉2-3％,钒铁1-3％,氮化铬铁4-7％,石墨0.5-1％,纯碱0.3-1％,海藻0.3-1％。本发明焊条具有良好超低温冲击韧性,焊接工艺性能优异,全位置焊接操作性能优良。(The invention relates to the technical field of welding materials, in particular to an electric arc welding electrode for ultralow-temperature high-manganese steel; the welding rod includes the welding rod steel core and wraps up the coating outside the welding rod steel core, the composition of welding rod steel core is: c: 0.35-0.46%, Si: 0.06-0.18%, Mn: 22-30%, Cr: 3.7-4.6%, Ni 1.8-2.5%, Mo: 1.3-2.1%, S: less than or equal to 0.015 percent, P: less than or equal to 0.015 percent, the balance of Fe and inevitable impurities, water glass is used as a binder, a coating accounts for 35 to 40 percent of the total weight of the welding rod, the welding rod is prepared by adopting the existing welding rod production equipment and the production method, wherein the coating comprises the following components in percentage by mass: 20-30% of marble, 5-10% of strontium carbonate, 18-25% of fluorite, 3-6% of zircon sand, 4-8% of rutile, 3-5% of ferrotitanium, 3-8% of magnetite, 4-8% of manganese metal, 4-6% of chromium metal, 6-10% of nickel metal, 2-4% of molybdenum metal, 2-3% of copper powder, 1-3% of ferrovanadium, 4-7% of ferrochromium nitride, 0.5-1% of graphite, 0.3-1% of soda ash and 0.3-1% of seaweed. The welding rod has good ultralow-temperature impact toughness, excellent welding process performance and excellent all-position welding operation performance.)

1. The welding electrode for the arc welding of the ultralow-temperature high-manganese steel comprises a welding electrode steel core and a coating wrapped outside the welding electrode steel core, and is characterized in that the coating comprises the following components in percentage by mass: 20-30% of marble, 5-10% of strontium carbonate, 18-25% of fluorite, 3-6% of zircon sand, 4-8% of rutile, 3-5% of ferrotitanium, 3-8% of magnetite, 4-8% of manganese metal, 4-6% of chromium metal, 6-10% of nickel metal, 2-4% of molybdenum metal, 2-3% of copper powder, 1-3% of ferrovanadium, 4-7% of ferrochromium nitride, 0.5-1% of graphite, 0.3-1% of soda ash and 0.3-1% of seaweed.

2. The arc welding electrode for ultra-low temperature high manganese steel according to claim 1, characterized in that the ingredients of the coating and the mass percentages of the ingredients in the coating are as follows: 30% of marble, 8% of strontium carbonate, 20% of fluorite, 3% of zircon sand, 5% of rutile, 3% of ferrotitanium, 3.5% of magnetite, 5% of manganese metal, 4% of chromium metal, 7% of nickel metal, 2% of molybdenum, 2% of copper powder, 1% of ferrovanadium, 4% of ferrochromium nitride, 0.5% of graphite, 1% of soda ash and 1% of seaweed.

3. The arc welding electrode for ultra-low temperature high manganese steel according to claim 1, characterized in that the ingredients of the coating and the mass percentages of the ingredients in the coating are as follows: 25% of marble, 10% of strontium carbonate, 21% of fluorite, 4% of zircon sand, 4% of rutile, 3.5% of ferrotitanium, 5% of magnetite, 4% of manganese metal, 4% of chromium metal, 8% of nickel metal, 3% of molybdenum, 2% of copper powder, 1.5% of ferrovanadium, 5.5% of ferrochrome nitride, 0.5% of graphite, 0.3% of soda ash and 0.7% of seaweed.

4. The arc welding electrode for ultra-low temperature high manganese steel according to claim 1, characterized in that the ingredients of the coating and the mass percentages of the ingredients in the coating are as follows: 26% of marble, 5% of strontium carbonate, 18% of fluorite, 3% of zircon sand, 5% of rutile, 4% of ferrotitanium, 8% of magnetite, 2.5% of manganese metal, 5% of chromium metal, 6% of nickel metal, 2% of molybdenum metal, 2.5% of copper powder, 2% of ferrovanadium, 5% of ferrochrome nitride, 1% of graphite, 0.5% of soda ash and 0.5% of seaweed.

5. The ultra-low temperature high manganese steel arc welding electrode according to claim 1, wherein said coating comprises 35-40% of the total weight of the electrode.

6. The arc welding electrode for ultra-low temperature high manganese steel according to claim 1, characterized in that the steel core of the electrode comprises the following components: c: 0.35-0.46%, Si: 0.06-0.18%, Mn: 22-30%, Cr: 3.7-4.6%, Ni 1.8-2.5%, Mo: 1.3-2.1%, S: less than or equal to 0.015 percent, P: less than or equal to 0.015 percent, and the balance of Fe and inevitable impurities.

Technical Field

The invention relates to the technical field of welding materials, in particular to an electric arc welding electrode for ultralow-temperature high-manganese steel.

Background

With the development of modern industry, the world energy consumption is more and more concentrated on gaseous energy, especially natural gas, which is a convenient and efficient clean energy, and the world natural gas has abundant resources with the storage capacity of about 400-³. However, natural gas is typically stored at locations remote from the primary consumption area, making storage and long-distance transportation of large quantities of natural gas an urgent problem to be solved. If the natural gas is made into liquid, the volume can be reduced by 600 times, and the storage and transportation cost of the natural gas can be greatly reduced. The liquefaction temperature of natural gas is-162 ℃, and a large amount of ultra-low temperature steel is required for LNG ships transporting natural gas and storage tanks storing natural gas. The alloy steel for storing and transporting low-temperature liquid such as liquefied natural gas, liquefied methane, liquid nitrogen, liquid oxygen and the like is mainly ultra-low temperature nickel steel, wherein the largest usage amount is 9Ni steel, the ductile-brittle transition temperature of the 9Ni steel is lower than-196 ℃, the design strength requirement is met, the alloy steel has good weldability and processability, the structure is stable at-196 ℃, and the requirements of transporting and storing the liquefied natural gas and the like are completely met. However, the addition range of nickel element in 9Ni steel is 8.5-10%, and the nickel element is expensive, so that the smelting and use cost of 9Ni steel is greatly increased, and therefore, in order to reduce price, save energy and meet market demands, the development of a novel ultra-low temperature alloy steel capable of replacing 9Ni steel is urgently needed.

The ultralow-temperature high-manganese steel (22-26% of Mn content) and 9Ni steel have the same physical metallurgical characteristics, have the advantages of high performance (excellent crack resistance) and low cost (30-40% of cost is saved), are used as the first-choice competitive material of steel machines for LNG storage tanks instead of 9Ni steel, have immeasurable application prospects, and have become research hotspots in various countries in the world. High manganese steel for LNG tanks developed by Pupai iron and Steel company, Dayu shipbuilding ocean company, and five-Ship-level society worldwide (ABS, BV, DNV-GL, KR, LR) in 2015 has been mass-produced.

The research and development of domestic ultralow-temperature high-manganese steel (with the Mn content of 22-26%) are still in the initial stage, and the matched welding material is a key technology for the application of the ultralow-temperature high-manganese steel. At present, no proper welding material is used for welding the ultralow-temperature high manganese steel, so that the popularization and application of the ultralow-temperature high manganese steel are trapped in a bottleneck.

Disclosure of Invention

In order to solve the problems, the invention develops a welding material matched with ultralow temperature high manganese steel (22-26% of Mn content), and the invention provides an electric arc welding electrode for the ultralow temperature high manganese steel, which comprises an electrode steel core and a coating wrapped outside the electrode steel core, wherein the coating comprises the following components in percentage by mass: 20-30% of marble, 5-10% of strontium carbonate, 18-25% of fluorite, 3-6% of zircon sand, 4-8% of rutile, 3-5% of ferrotitanium, 3-8% of magnetite, 4-8% of manganese metal, 4-6% of chromium metal, 6-10% of nickel metal, 2-4% of molybdenum metal, 2-3% of copper powder, 1-3% of ferrovanadium, 4-7% of ferrochromium nitride, 0.5-1% of graphite, 0.3-1% of soda ash and 0.3-1% of seaweed.

Preferably, the components of the coating and the mass percentage of each component in the coating are as follows: 30% of marble, 8% of strontium carbonate, 20% of fluorite, 3% of zircon sand, 5% of rutile, 3% of ferrotitanium, 3.5% of magnetite, 5% of manganese metal, 4% of chromium metal, 7% of nickel metal, 2% of molybdenum, 2% of copper powder, 1% of ferrovanadium, 4% of ferrochromium nitride, 0.5% of graphite, 1% of soda ash and 1% of seaweed.

Preferably, the components of the coating and the mass percentage of each component in the coating are as follows: 25% of marble, 10% of strontium carbonate, 21% of fluorite, 4% of zircon sand, 4% of rutile, 3.5% of ferrotitanium, 5% of magnetite, 4% of manganese metal, 4% of chromium metal, 8% of nickel metal, 3% of molybdenum, 2% of copper powder, 1.5% of ferrovanadium, 5.5% of ferrochrome nitride, 0.5% of graphite, 0.3% of soda ash and 0.7% of seaweed.

Preferably, the components of the coating and the mass percentage of each component in the coating are as follows: 26% of marble, 5% of strontium carbonate, 18% of fluorite, 3% of zircon sand, 5% of rutile, 4% of ferrotitanium, 8% of magnetite, 2.5% of manganese metal, 5% of chromium metal, 6% of nickel metal, 2% of molybdenum metal, 2.5% of copper powder, 2% of ferrovanadium, 5% of ferrochrome nitride, 1% of graphite, 0.5% of soda ash and 0.5% of seaweed.

Preferably, the coating accounts for 35-40% of the total weight of the welding rod.

Preferably, the welding rod steel core comprises the following components: c: 0.35-0.46%, Si: 0.06-0.18%, Mn: 22-30%, Cr: 3.7-4.6%, Ni 1.8-2.5%, Mo: 1.3-2.1%, S: less than or equal to 0.015 percent, P: less than or equal to 0.015 percent, and the balance of Fe and inevitable impurities.

The design principle of the electric arc welding rod for the ultralow-temperature high manganese steel suitable for all-position welding is as follows: through the design of a low-cost C-Mn-Cr-Ni-N alloy system, the Mn content in the formed weld metal is 22-26%, and the mechanical property is excellent at the temperature of-196 ℃ and lower. The invention contains a proper amount of strontium carbonate, which can ensure the good applicability of the vertical welding process; the austenite structure is further stabilized by adding a proper amount of Ni and N, so that the strength and the low-temperature impact toughness of the weld metal are improved; cr and Mo can form carbide or nitride to improve the strength of welding seams, and Mo can also reduce a solid-liquid coexisting region and effectively inhibit the occurrence of thermal cracks; by adding trace alloying elements such as V, Cu, the grains of weld metal can be refined, so that the strength and toughness of weld metal can be improved, and the crack resistance of weld metal can be improved.

Fluorite is used for slag dilution and dehydrogenation, prevents pores from being generated during welding, and can improve slag removal performance, and the addition amount of fluorite is 18-25%, and the addition amount is too much, so that opposite welding is not favorable.

The main component of marble is CaCO₃Its main functions are slagging and gas making, when the addition of the coating is less than 20%, the slag and gas protecting action is reduced, and when the addition is more than 30%, the splash is increased.

The strontium carbonate also has the functions of slagging and gas making, and can obviously improve the operating performance of vertical upward welding, and 5-10% is preferably added.

The zircon sand is beneficial to slag removal of the molten slag, but when the addition amount is excessive, the welding seam is easy to oxidize, and the addition amount is generally controlled to be 3-6%.

The magnetite has the function of improving the melting point of the slag, so that a coating sleeve is formed after the welding rod is ignited, and molten drops are thinned, and 3-8% is preferably added generally.

Ferrotitanium is used as deoxidant and degasifier to protect the transition of Mn element and form Ti-C, Ti-N compound and raise the strength of welded seam, and 3-5% is added.

Rutile is used as a slag former, has the functions of stabilizing electric arc and adjusting physical properties of slag, can improve vertical upward welding by adding a proper amount, and is preferably added by 4-8 percent generally.

Mn in the metal manganese is an element for expanding an austenite region and stabilizing an austenite structure, when the content of Mn in the weld metal is more than 20 percent, a complete austenite structure can be formed, the low-temperature brittle transition temperature disappears, and the low-temperature impact toughness of the weld metal is improved; the manganese metal can also participate in deoxidation, and is used for reducing the oxygen content of the weld metal and increasing the strength and crack resistance of the weld metal.

Cr in the metal chromium can form carbide with C, the strength of the weld metal is improved through dispersion strengthening and solid solution strengthening, the addition amount of the chromium is preferably 4-6% of the content of the chromium in the weld metal, and when the content of the chromium in the weld metal is more than 6%, the carbide of the chromium in the weld metal is excessive, so that the low-temperature impact toughness is reduced.

The addition of the chromium iron nitride aims to add N into the weld metal, wherein N is an element for expanding an austenite region and stabilizing an austenite structure, and can improve the low-temperature impact toughness of the weld metal; meanwhile, the chromium iron nitride is used as a solid solution strengthening element and can form nitride with Cr, Mo and V, the strength of the weld metal can be improved without obviously damaging the plasticity and toughness of the weld metal, the addition amount of the chromium iron nitride is preferably 4-7%, and the content of N in the weld metal is controlled to be 0.1-0.2%.

Ni in the nickel powder is an element for forming and stabilizing an austenite structure, so that the brittle transition temperature can be reduced, the strength and the low-temperature impact toughness of weld metal can be improved, and the addition amount of the nickel is 6-10% in consideration of economic cost.

Mo in the molybdenum powder can form carbide or nitride, the strength of a welding line is improved, the Mo can also reduce a solid-liquid coexisting region, the occurrence of thermal cracks can be effectively inhibited, the addition amount is 2-4%, the addition amount is excessive, and the low-temperature impact energy can be remarkably reduced due to excessive carbide and nitride of Mo in welding line metal.

V is a strong carbide forming element, can form special carbide, refines austenite grains and improves the metal strength and toughness of a welding seam; the addition amount is 1-2%, and the addition amount is too much, so that the low-temperature impact energy is obviously reduced due to too much V carbide and nitride in weld metal.

Cu is a solid solution strengthening and precipitation strengthening element, can improve the strength of weld metal, is unfavorable for crack resistance when the addition amount is more than 3 percent, and is preferably 2 to 3 percent.

C is an austenitizing element, and simultaneously can form carbide with Cr, Mo and V so as to improve the strength of the austenitic weld metal; when the content of C in deposited metal is less than 0.3%, the strength of the welding seam cannot meet the requirement; when the content of C in the deposited metal is more than 0.45%, blowholes are generated during welding and the impact toughness is lowered.

The addition of soda ash and seaweed is mainly used for improving the viscosity and the fluidity of powder and improving the press coating performance of the welding rod.

Due to the adoption of the technical scheme, compared with the prior art, the invention has the following beneficial effects:

1) the invention adopts the design of a low-cost C-Mn-Cr-Ni-N alloy system, the Mn content in the formed weld metal is 22-26%, the mechanical property is excellent at minus 196 ℃ and lower temperature, the Ni content of the matched welding material is obviously reduced, and the use cost advantage is obvious;

2) the electric arc welding electrode for ultralow-temperature high-manganese steel provided by the invention has good comprehensive properties of deposited metal and a welding joint, and the tensile strength is more than or equal to 700 MPa; the yield strength is more than or equal to 500 MPa; the elongation is more than or equal to 30 percent; under the condition of-196 ℃, Akv is more than or equal to 80J;

3) the electric arc welding electrode for ultralow-temperature high-manganese steel provided by the invention has excellent welding process performance and is suitable for all-position welding.

Detailed Description

The present invention is further described with reference to specific examples to enable those skilled in the art to better understand the present invention and to practice the same, but the examples are not intended to limit the present invention.

The invention provides an arc welding electrode for ultralow-temperature high manganese steel, which comprises an electrode steel core and a coating wrapped outside the electrode steel core, wherein the electrode steel core comprises the following components: c: 0.35-0.46%, Si: 0.06-0.18%, Mn: 22-30%, Cr: 3.7-4.6%, Ni 1.8-2.5%, Mo: 1.3-2.1%, S: less than or equal to 0.015 percent, P: less than or equal to 0.015 percent, the balance of Fe and inevitable impurities, water glass is used as a binder, a coating accounts for 35 to 40 percent of the total weight of the welding rod, the welding rod is prepared by adopting the existing welding rod production equipment and the production method, wherein the coating comprises the following components in percentage by mass: 20-30% of marble, 5-10% of strontium carbonate, 18-25% of fluorite, 3-6% of zircon sand, 4-8% of rutile, 3-5% of ferrotitanium, 3-8% of magnetite, 4-8% of manganese metal, 4-6% of chromium metal, 6-10% of nickel metal, 2-4% of molybdenum metal, 2-3% of copper powder, 1-3% of ferrovanadium, 4-7% of ferrochromium nitride, 0.5-1% of graphite, 0.3-1% of soda ash and 0.3-1% of seaweed.

The present invention will be further described with reference to the following examples.

Examples 1 to 3 provide three arc welding electrodes, which are numbered 1#, 2#, and 3#, respectively, the formulations and welding process performance evaluations of the arc welding electrodes for ultra-low temperature high manganese steel are shown in table 1, the mechanical properties of deposited metal of each electrode are shown in table 2, and the chemical compositions of the deposited metal are shown in table 3, specifically as follows:

table 1: formulation (mass%) and weldability Process Properties of examples 1 to 3

Example numbering	1#	2#	3#
				Marble	30	25	26
Strontium carbonate	8	10	5
				Fluorite	20	21	18
Zircon sand	3	4	3
				Rutile type	5	4	5
Ferrotitanium	3	3.5	4
				Magnetite	3.5	5	8
Manganese metal	5	4	5.5
				MetalChromium (III)	4	4	5
Metallic nickel	7	8	6
				Metallic molybdenum	2	3	2
Copper powder	2	2	2.5
				Vanadium iron	1	1.5	2
Chromium iron nitride	4	5.5	5
				Graphite	0.5	0.5	1
Soda ash	1	0.3	0.5
				Seaweed (Sargassum)	1	0.7	0.5
Evaluation of welding Process Properties	Good effect	In general	Good effect

Table 2: mechanical properties of deposited metal

Table 3: chemical composition of deposited metal

As can be seen from tables 1, 2 and 3, the welding rod for the all-position welding ultralow-temperature high manganese steel has the comprehensive properties of deposited metal and welding joints: the tensile strength is more than or equal to 700 MPa; the yield strength is more than or equal to 500 MPa; the elongation is more than or equal to 30 percent; under the condition of 196 ℃ below zero, Akv is more than or equal to 80J, and impact energy (Akv) is tested for three times, so that the data show that the all-position welding process has excellent performance and can completely meet the mechanical property requirement of the ultralow-temperature high-manganese steel and the use requirement of the welding position.

The above-mentioned embodiments are merely preferred embodiments for fully illustrating the present invention, and the scope of the present invention is not limited thereto. The equivalent substitution or change made by the technical personnel in the technical field on the basis of the invention is all within the protection scope of the invention. The protection scope of the invention is subject to the claims.