阅读说明：本技术 一种天鹅绒艺术涂料的施工工艺 (Construction process of velvet artistic paint ) 是由 姜年超 于 2019-10-29 设计创作，主要内容包括：本发明公开了一种天鹅绒艺术涂料的施工工艺,其包括如下步骤：S1.用除甲醛环保水漆调色打底,接近施工墙面的面色；S2.滚涂一道天鹅绒艺术涂料,用塑料打磨器按S型或者8字型将材料搓开；S3.待完全干燥后,再次均匀滚涂一道天鹅绒艺术涂料；然后再采用步骤S41-S43中的任一步骤：S41.滚涂完成后立即用塑料打磨器按S型或者8字型搓出阴阳面效果；S42.滚涂完成后立即用塑料打磨器上下均匀打磨,拉出竖条纹路；S43.滚涂完成后立即用塑料打磨器按S型或者8字型搓出阴阳面效果,待完全干燥后,用丝网印印花。本发明制得的墙面具有阴阳面效果或其他独特的效果。(The invention discloses a construction process of velvet art paint, which comprises the following steps: s1, painting a base by using formaldehyde-removing environment-friendly water paint to match colors, wherein the color is close to the surface color of a construction wall surface; s2, rolling and coating a velvet artistic paint, and rubbing the velvet artistic paint by using a plastic sander according to an S shape or an 8-shaped shape; s3, after the velvet is completely dried, uniformly rolling and coating a velvet artistic paint again; then any one of the steps S41-S43 is adopted: s41, rubbing the male and female surfaces with a plastic sander according to an S shape or an 8 shape immediately after the roller coating is finished; s42, immediately polishing uniformly up and down by using a plastic polisher after the roll coating is finished, and pulling out vertical bar lines; s43, immediately rubbing a shade and sun surface by using a plastic sander according to the S shape or the 8 shape after the roll coating is finished, and printing by using a screen after the shade and sun surface is completely dried. The wall surface prepared by the invention has a yin-yang surface effect or other unique effects.)

1. A construction process of velvet artistic paint is characterized by comprising the following steps:

s1, painting a base by using formaldehyde-removing environment-friendly water paint to match colors, wherein the color is close to the surface color of a construction wall surface;

s2, rolling and coating a velvet artistic paint, and rubbing the velvet artistic paint by using a plastic sander according to an S shape or an 8-shaped shape;

s3, after the velvet is completely dried, uniformly rolling and coating a velvet artistic paint again;

then any one of the following steps S41-S43 is adopted:

s41, rubbing the male and female surfaces with a plastic sander according to an S shape or an 8 shape immediately after the roller coating is finished;

s42, immediately polishing uniformly up and down by using a plastic polisher after the roll coating is finished, and pulling out vertical bar lines;

s43, immediately rubbing a shade and sun surface by using a plastic sander according to the S shape or the 8 shape after the roll coating is finished, and printing by using a screen after the shade and sun surface is completely dried.

2. The process of claim 1, wherein in S2 and S3, the velvet art paint comprises the following components by weight percent:

20% -30% of emulsion;

15% -20% of pearl powder;

10-14% of talcum powder;

5% -10% of an auxiliary agent;

the balance being water.

3. The process of claim 2, wherein the emulsion is one of an aqueous acrylic emulsion and an aqueous polyurethane emulsion from Tesmann corporation.

4. The process of claim 3, wherein the additive is one or more of a film forming additive, a thickening agent, a wetting agent, a dispersing agent, cellulose, a suspending agent, a defoaming agent, a pH regulator, a bactericide, an antifreeze, and a wax additive.

5. The process of claim 4, wherein the anti-freezing agent is propylene glycol.

6. The process of claim 5, wherein the suspending agent is bentonite.

7. The process of claim 6, wherein the wax adjuvant is a hand wax emulsion.

8. The process of claim 7, wherein the additives are film forming additives, thickeners, wetting agents, dispersants, cellulose, bentonite, defoamers, pH modifiers, biocides, propylene glycol, and feel wax emulsions.

9. The process for applying the velvet artistic paint according to claim 8, wherein the velvet artistic paint is prepared from the following components in percentage by weight:

20% -30% of emulsion;

15% -20% of pearl powder;

10-14% of talcum powder;

0.4 to 0.6 percent of wetting agent;

0.1 to 0.3 percent of dispersant

0.3 to 0.6 percent of cellulose;

0.1 to 0.3 percent of defoaming agent

0.1 to 0.3 percent of pH regulator;

0.1 to 0.3 percent of bactericide;

0.1 to 0.3 percent of bentonite;

0.6 to 1 percent of thickening agent;

1% -3% of handfeel wax emulsion;

the balance being deionized water.

Technical Field

The invention relates to the field of art coatings, in particular to a construction process of a velvet art coating.

Background

At present, China advocates environmental protection and energy conservation vigorously, and innovates greatly, promotes the continuous transformation and upgrading of building coating enterprises, and seeks more environment-friendly and novel coating products to meet the continuous pursuit of people on environment and wall decoration. Every kind of wall surface with every background is designed with unique artwork, and a great amount of new decorative materials are continuously introduced from abroad, impacting the domestic paint market.

Chinese patent document CN104761989B discloses a composite inorganic metal velvet coating and a preparation method thereof, wherein the composite inorganic metal velvet coating is prepared from the following raw materials in percentage by mass: 5-30% of water, 10-20% of inorganic silicon binder, 0.2-0.4% of cellulose, 0.2-0.4% of wetting agent, 0.3-0.5% of flatting agent, 0.2-0.8% of anti-freezing agent, 0.2-0.4% of organic silicon defoaming agent, 5-15% of fluff powder, 10-20% of pearl powder, 5-10% of sericite powder, 25-30% of glass sand, 0.1-0.4% of photocatalyst powder, 5-10% of suspension type thickening agent, 10-20% of emulsion, 1.7-3.3% of anti-settling agent, 2-4.4% of preservative, 0-0.2% of silver ion mildew inhibitor and 0-2% of coloring agent; the inorganic metal velvet coating prepared by the preparation method disclosed by the patent has a luxurious appearance with full pearly luster by taking the fineness, texture and high elasticity of fiber velvet powder as main raw materials and taking sericite powder and metal pearl powder as fillers, and the photocatalyst powder is added, so that the product has the function of decomposing indoor formaldehyde.

However, the patent document considers yin and yang as technical defects, and then simply coats or sprays the wall with metallic luster and elastic hand feeling, so that the wall is coated with a layer of heat-insulating wall clothing like a flannelette. The technical effect is to avoid the generation of yin and yang colors.

Disclosure of Invention

However, the invention aims to provide a construction process of the velvet art paint, so that the prepared wall surface has a cloudy-sunny surface effect or other unique effects.

The adopted technical scheme is as follows:

a construction process of velvet artistic paint comprises the following steps:

s1, painting a base by using formaldehyde-removing environment-friendly water paint to match colors, wherein the color is close to the surface color of a construction wall surface;

s2, rolling and coating a velvet artistic paint, and rubbing the velvet artistic paint by using a plastic sander according to an S shape or an 8-shaped shape;

s3, after the velvet is completely dried, uniformly rolling and coating a velvet artistic paint again;

then any one of the following steps S41-S43 is adopted:

s41, rubbing the male and female surfaces with a plastic sander according to an S shape or an 8 shape immediately after the roller coating is finished;

s42, immediately polishing uniformly up and down by using a plastic polisher after the roll coating is finished, and pulling out vertical bar lines;

s43, immediately rubbing a shade and sun surface by using a plastic sander according to the S shape or the 8 shape after the roll coating is finished, and printing by using a screen after the shade and sun surface is completely dried.

Through each step of this technical scheme construction process, can make the wall of cloudy positive surface effect, also can make the wall of vertical retort line effect, can also make not only have cloudy positive surface effect, further have the wall of stamp effect moreover.

Further, in S2 and S3, the velvet art paint is composed of the following components in percentage by weight:

20% -30% of emulsion;

15% -20% of pearl powder;

10-14% of talcum powder;

5% -10% of an auxiliary agent;

the balance being water.

In the formula of the velvet artistic paint, the pearl powder and the talcum powder are added into the emulsion, and the construction process is matched, so that the effect of the sun and the shade and other unique effects are easily generated.

Further, the emulsion is one of water-based acrylic emulsion and water-based polyurethane emulsion of Dismann company.

Further, the auxiliary agent is one or more of a film forming auxiliary agent, a thickening agent, a wetting agent, a dispersing agent, cellulose, a suspending agent, a defoaming agent, a pH regulator, a bactericide, an antifreezing agent and a wax auxiliary agent.

Further, the antifreeze is propylene glycol.

Further, the suspending agent is bentonite.

Further, the wax auxiliary agent is a hand feeling wax emulsion.

Further, the auxiliary agent comprises a film forming auxiliary agent, a thickening agent, a wetting agent, a dispersing agent, cellulose, bentonite, a defoaming agent, a pH regulator, a bactericide, propylene glycol and a handfeel wax emulsion.

Further, the velvet artistic paint comprises the following components in percentage by weight:

20% -30% of emulsion;

15% -20% of pearl powder;

10-14% of talcum powder;

0.4 to 0.6 percent of wetting agent;

0.1 to 0.3 percent of dispersant

0.3 to 0.6 percent of cellulose;

0.1 to 0.3 percent of defoaming agent

0.1 to 0.3 percent of pH regulator;

0.1 to 0.3 percent of bactericide;

0.1 to 0.3 percent of bentonite;

0.6 to 1 percent of thickening agent;

1% -3% of handfeel wax emulsion;

the balance being deionized water.

In the formula, the bentonite has good suspension property and dispersibility in an aqueous medium, and the bentonite ensures that the artistic coating is not easy to precipitate and delaminate and has uniform color, thereby improving the stability of the artistic coating. The hand feeling wax emulsion is used for improving the final wall surface hand feeling and improving the wear resistance.

The above-mentioned formulations of the respective raw materials are commercially available.

For example, as the humectant, a hamming FA115 humectant can be used; the dispersant can be SN5040 dispersant of Nopochaceae; the cellulose can adopt Asotblue HBR250 cellulose; the defoaming agent can be NXZ defoaming agent of Nopochaceae; the pH regulator can be Dow AMP-95pH regulator; the bactericide can be trojan K10N bactericide; the pulvis Talci can be flos Osmanthi Fragrantis 400 mesh pulvis Talci.

The bentonite can be Zhejiang Yuhong YH-D bentonite; the emulsion is NeoRezR aqueous polyurethane emulsion or Neocryl BT-26 aqueous acrylic emulsion of Imperial corporation. The pearl powder can be kuncai KC8500 400-mesh pearl powder; the film-forming assistant can be a sea horse OE500 odorless film-forming assistant; the propylene glycol can be Dow propylene glycol; the thickener can be polyurethane thickener of Dow RM2020 and/or alkali swelling thickener of Dow ASE-60; the hand feeling wax emulsion can adopt German KEIM E-012 hand feeling wax emulsion.

In the construction process of the velvet art coating, the formaldehyde-removing environment-friendly water paint can adopt the existing formaldehyde-removing environment-friendly water paint, or preferably adopts the following scheme:

the formaldehyde-removing environment-friendly water paint comprises the following components in percentage by weight:

30-35 parts of water-based acrylic emulsion, 15-20 parts of deionized water, 10-15 parts of coloring pigment, 0.2-0.6 part of thickening agent, 0.4-0.8 part of film-forming assistant, 0.3-1 part of wetting agent, 0.3-1 part of dispersing agent and 4-6 parts of rutile titanium dioxide; 0.3-1 part of bactericide.

The difference of the coloring pigment can be adjusted according to the requirement, so that a plurality of formaldehyde-removing environment-friendly water paints are formed, the formaldehyde-removing environment-friendly water paints are convenient to mix colors and prime, and the priming surface is close to the surface color of the construction wall surface.

In conclusion, the wall surface manufactured by the construction process of the invention has a sun-shade surface effect or other unique effects, which are not achieved by the prior art of CN 104761989B.

Drawings

FIG. 1 is a wall surface effect diagram after construction according to example 1.

FIG. 2 is a wall surface effect diagram after construction according to example 2.

FIG. 3 is a wall surface effect diagram after construction according to example 3.

Detailed Description

The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only preferred embodiments of the present invention, and not all embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.