阅读说明：本技术 手工工艺品的制作方法 (The production method of hand-made ) 是由 王兆丰 于 2018-05-21 设计创作，主要内容包括：本发明公开了一种手工工艺品的制作方法,包括以下步骤：首先将水泥、沙、胶水按设计质量 比混合搅匀成水泥浆,然后将制得的水泥浆均匀 地涂抹在绷布的两面上,之后再将至少一块所述 的涂抹好水泥浆的绷布绷在模具上,之后保养3 天以上,每天浇水2次,上午和下午各一次,且在 保养过程中避免暖光照射,然后脱模制得手工工 艺品的半成品,最后再将手工工艺品的半成品晾 干并对其上色即可制得手工工艺品的成品。采用 本方法制作而成的手工工艺品具有制作简单、制 作成本低、易保存等特性。(The invention discloses a kind of production methods of hand-made, the following steps are included: first by cement, it is husky, glue stirs evenly into cement slurry than mixing by designing quality, then cement slurry obtained is equably applied on the two sides of taut cloth, the taut cloth that painting wipes cement slurry described at least one piece is stretched tight on mold again later, maintain 3 days later or more, watering 2 times daily, the morning and afternoon are each primary, and warm light is avoided to irradiate in servicing operations, then the semi-finished product that hand-made is made are demoulded, finally again drying the semi-finished product of hand-made and paint to it can be prepared by the finished product of hand-made.There are the characteristics such as simple production, low manufacture cost, easy to maintain using the hand-made that this method is made.)

1. a kind of production method of hand-made, it is characterised in that: stir evenly cement, sand, glue than mixing by designing quality At cement slurry, then cement slurry obtained is equably applied on the two sides of taut cloth, later again by painting described at least one piece The taut cloth for wiping cement slurry stretches tight on mold, maintain 3 days later or more, watering 2 times daily, the morning and afternoon are each primary, and It avoids warm light from irradiating in servicing operations, then demoulds the semi-finished product that hand-made is made, finally again by the half of hand-made Finished product, which is dried and painted to it, can be prepared by the finished product of hand-made.

2. a kind of production method of hand-made according to claim 1, it is characterised in that: the cement, sand, glue Mass ratio be the .2:1 of 1 .8~2.2:0.8~1 .1~1 .5.

3. a kind of production method of hand-made according to claim 1, it is characterised in that: the cement, sand, glue It is stirred 10~20 minutes after mixing with hand blender.

4. a kind of production method of hand-made according to claim 1, it is characterised in that: the mold is by waste and old drink Material bottle is formed by hand-made.

5. a kind of production method of hand-made according to claim 1, it is characterised in that: after demoulding, for craft The semi-finished product of craftwork carry out repairing moulding using cement slurry.

6. a kind of production method of hand-made according to claim 1, it is characterised in that: when the half of hand-made It after finished product bleaches, paints to it: the semi-finished product of hand-made being beaten using the mixture of glass glue and iron oxide red first The mass ratio of bottom, glass glue and iron oxide red is 6~8:2~4, is painted again using pigment after drying, after drying again, Yu Shougong Tone place lack of standardization on the semi-finished product of craftwork is repaired using pigment again, and dry can be prepared by hand-made later Finished product.

7. a kind of production method of hand-made, feature described in any one of -6 claims according to claim 1 Be: the cement is 425 cement, and husky granularity is 0.35mm, and glue is 106 glue.

Technical field

The present invention relates to the production of hand-made, especially a kind of production side for the hand-made for not needing to fire Method.

Background technique

Currently, the production raw material of craftwork generally uses minerals powder, ceramics and glass object etc., using these raw materials come Craft articles require first to be ground into powder using ball mill, and then powder, which is sent in mold, makes its molding, it It is demoulded afterwards using equipment, finally molding embryo material is sent into kiln and is fired into finished product, so being made of these raw materials Not only manufacturing process is complex for craftwork, but also cost of manufacture is high.

Summary of the invention

Technical problem to be solved by the invention is to provide a kind of production methods of hand-made, are made of this method Made of hand-made have and make the characteristics such as simple, at low cost, easy to maintain.

The technical solution adopted by the present invention to solve the technical problems is: a kind of production method of hand-made, by water Mud, sand, glue stir evenly into cement slurry than mixing by designing quality, and cement slurry obtained is equably then applied to the two of taut cloth On face, the taut cloth that painting wipes cement slurry described at least one piece is stretched tight on mold again later, maintain 3 days later or more, daily Watering 2 times, the morning and afternoon are each primary, and avoid warm light from irradiating in servicing operations, then demould and hand-made is made Semi-finished product, finally again drying the semi-finished product of hand-made and painting to it can be prepared by the finished product of hand-made.It is described Cement, sand, glue mass ratio according to the narrow difference in season and the original material performance of cement, sand, glue, generally require After a certain range examination is adjusted, optimal components ratio is determined, the foundation of allotment is to first have to guarantee the wellability for the cloth that stretches tight, cannot It is feeding-up, but certain viscosity must be kept, taut cloth bottom can be covered, adhesiveness moderately guarantees close between the taut cloth of multilayer Fitting reduces bubble and generates, is conducive to the mellow and full of moulding and avoids moulding defect.Not visible light in servicing operations, meanwhile, watering It is unsuitable excessive, to guarantee that surface wettability is advisable without droplet, to realize the gradually uniform desiccation and guarantee half of cement slurry from inside to outside The intensity of finished product prevents semi-finished product from the defects of delamination, crackle, gap occur.Entirety can start to paint after uniformly reaching dry Step.

According to the test of inventor, cement, sand, glue mass ratio be .1~1 the .2:0 of 1 .8~2 .2:1 of .8~1 .5 ratio, the connecting shaping significant effect of the cement slurry modulated and taut cloth, the ratio of defects of semi-finished product are lower.

Further, it is stirred 10~20 minutes after the cement, sand, glue mixing with hand blender.Relative to craft Stirring, can mix more uniform, and the stirring used time is shorter than the setting time of cement slurry, conveniently be applied on taut cloth.

Further, the mold is formed by waste and old beverage bottle by hand-made, with save the cost, is turned waste into wealth.

Further, after demoulding, for the semi-finished product of hand-made, repairing moulding is carried out using cement slurry, by repairing It is difficult to a small amount of, the local defect avoided again, obtains more beautiful moulding.The cement slurry of repairing, with the cement being applied on taut cloth Slurry is obtained by mixing in the same way.

Further, it after the semi-finished product of hand-made bleach, paints to it: first using glass glue and iron oxide red The mass ratio of semi-finished product progress bottoming of the mixture to hand-made, glass glue and iron oxide red is 6~8:2~4, dries it Afterwards, then using semi-finished product of the pigment to hand-made it paints, after drying again, not in tone on the semi-finished product of hand-made At specification, is repaired again using pigment, dry the finished product that can be prepared by hand-made later.Glass glue and iron oxide red The preferred range of mass ratio, depending on the background color depth as needed, it usually needs when deeper background color, selection increases the use of iron oxide red Amount, meanwhile, glass glue has the function of that repairing naked eyes is difficult to the defect observed.

Further, the cement is 425 cement, and husky granularity is 0.35mm, and glue is 106 glue.

When using the raw material of aforementioned model or specification, cement, sand, glue mass ratio be recommended as 2:1:1 .3, for invention People is through the resulting optimum proportioning of long term test.

The beneficial effects of the present invention are: hand-made of the invention using cement, sand and glue be used as raw material, and whole process Using hand-made, traditional culture of the Chinese nation can not only be shown, and its manufacturing process is very simple, low manufacture cost, The shape for the hand-made made is ever-changing, has originality.