阅读说明：本技术 一种新型柔光反射瓷砖及其制备方法 (A kind of novel sheen reflection ceramic tile and preparation method thereof ) 是由 于志强 于 2019-08-17 设计创作，主要内容包括：本发明公开了一种新型柔光反射瓷砖及其制备方法,它包括瓷砖本体和蜡层；瓷砖本体的表面带有蜡层；瓷砖本体包括的组分有：钾长石、钠长石、高岭土、白云石、硅灰石、氧化锌、碳酸钡、哑光熔块、白刚玉和重钙。本发明生成成本低且成品率较高,硬度好以及平整度好的优点。产品最终的光度为29-35度,视觉舒适度好。(The invention discloses a kind of novel sheen reflection ceramic tiles and preparation method thereof, it includes ceramic tile ontology and wax layer；The surface of ceramic tile ontology has wax layer；The component that ceramic tile ontology includes has: potassium feldspar, albite, kaolin, dolomite, wollastonite, zinc oxide, barium carbonate, Matt frit, white fused alumina and coarse whiting.Manufacturing cost of the present invention is low and yield rate is higher, the advantage that hardness is good and flatness is good.The final luminosity of product is 29-35 degree, and visual comfort is good.)

1. a kind of novel sheen reflects ceramic tile, it includes ceramic tile ontology (1) and wax layer (2)；The surface band of the ceramic tile ontology (1) There are wax layer (2)；Its feature exists:

The component that the ceramic tile ontology (1) includes has: potassium feldspar, albite, kaolin, dolomite, wollastonite, zinc oxide, carbon Sour barium, Matt frit, white fused alumina and coarse whiting；

The content of ceramic tile ontology (1) each component are as follows: 25 parts of potassium feldspar, 15 parts of albite, 10 parts of kaolin, 2 parts of dolomite, 10 parts of wollastonite, 5 parts of zinc oxide, 7 parts of barium carbonate, 20 parts of Matt frit, 5 parts of white fused alumina and 3 parts of coarse whiting.

2. a kind of preparation method of novel sheen reflection ceramic tile, is applied to a kind of novel sheen described in claim 1 and reflects porcelain Brick, which is characterized in that described method includes following steps:

The above-mentioned uniform puddling of each component obtains mixture after mixing, and water is added in mixture and stirs evenly, mixture and water are matched Than for 100:35, being milled to fineness through ball mill is 325 mesh, 0.6 gram of specific gravity, by shaping mechanism at adobe, on adobe surface On leaching glaze covering carried out with 400g/ ㎡, be sent into furnace after 1200 DEG C of firings condensation, be polished to 35 degree of light by 240 mesh abrading blocks Then degree is uniformly dripped on brick face using nanoscale wax water with dropper, then with hard plastic waxing piece 2kg/ ㎡ power polishing, hard plastic The revolving speed of waxing piece is that 70r/min quickly squeezes waxing, and the polishing time is 5min, and 85 DEG C are warming up to after polishing and is condensed rapidly more It closes, so that brick face luminosity is maintained 29 degree, natural cooling to obtain the final product.

Technical field

The invention belongs to ceramic tile technical fields, and in particular to a kind of novel sheen reflection ceramic tile and preparation method thereof.

Background technique

The floor tile and wall brick of architectural decoration are widely used already, and compared to other floor decorative materials, ceramic tile is being filled Adorn effect, health etc. has apparent advantage, the decorative pattern of ceramic tile, texture and pattern are more life-like, lively, greatly Meet pursuit of the consumer to decorative effect.

Currently, conventional sheen ceramic tile is to be passed through the techniques such as to spray, spread, get rid of by a kind of transparent crystal particle in the market, make Particle is attached to ceramic tile surface naturally, after high temperature is fired, makes to form 5-6 grades of hardness Mohs of protection on product surface Layer, makes that Wear Resistance is splendid, anti-pollution power is strong, and product facing is although glittering to blaze, but the reflection sense of light is strong, euphorosia It is poor to spend, especially very dazzling in the case where light reflection is strong.

Existing sheen ceramic tile, the also known as refined furring tile of sheen, manufacturing process is mainly the following, first is that passing through glaze spraying Cabinet is got rid of glaze cabinet transparent crystal uniform particle is laid on ceramic brick surface with wet-format, its advantage is that the knot with green body Conjunction property is good, the disadvantage is that dry granular poor fluidity, easily stifled spray gun eye, produce bad control, flatness is poor, and hardness is lower.Second is that logical It filters glaze cabinet to be laid on ceramic brick surface transparent crystal uniform particle with wet-format, advantage is that the ceramic tile being fired into is put down Preferably, the disadvantage is that hardness is lower, dry granular poor fluidity easily precipitates, produces bad control whole degree.Lead to third is that fancy glaze is made in dry granular Screen decorating machine is crossed to be imprinted in a manner of stamp on brick face, although hardness is high its advantage is that dry granular is evenly distributed, flatness compared with It is good, still, since fancy glaze is that glaze is mixed with crystal particle, determined by the property of fancy glaze itself, the disadvantage is that halftone Breakage rate is big, at high cost.

Summary of the invention

Present invention aim to address the prior arts there are high production cost and reflects the technical problem of strong sheen degree difference, mentions For a kind of novel sheen reflection ceramic tile and preparation method thereof, with overcome the deficiencies in the prior art.

In order to achieve the above object, the technical solution adopted by the present invention is that:

A kind of novel sheen reflection ceramic tile, it includes ceramic tile ontology and wax layer；The surface of the ceramic tile ontology has wax layer；It is wanted Point exists:

The component that the ceramic tile ontology includes has: potassium feldspar, albite, kaolin, dolomite, wollastonite, zinc oxide, carbonic acid Barium, Matt frit, white fused alumina and coarse whiting；

The content of the ceramic tile ontology each component are as follows: 25 parts of potassium feldspar, 15 parts of albite, 10 parts of kaolin, 2 parts of dolomite, silicon 10 parts of lime stone, 5 parts of zinc oxide, 7 parts of barium carbonate, 20 parts of Matt frit, 5 parts of white fused alumina and 3 parts of coarse whiting.

The invention also discloses a kind of preparation methods of novel sheen reflection ceramic tile, and described method includes following steps:

The above-mentioned uniform puddling of each component obtains mixture after mixing, and water is added in mixture and stirs evenly, mixture and water are matched Than for 100:35, being milled to fineness through ball mill is 325 mesh, 0.6-0.8 grams of specific gravity, by shaping mechanism at adobe, in adobe Leaching glaze covering is carried out with 400-420g/ ㎡ on surface, is sent into furnace after 1200 DEG C of firings condense, by 240-3000 mesh abrading block It is polished to 35-45 degree luminosity, is then uniformly dripped on brick face using nanoscale wax water with dropper, then with hard plastic waxing piece 2- The polishing of 3kg/ ㎡ strength, the revolving speed of hard plastic waxing piece are that 70-80r/min quickly squeezes waxing, and the polishing time is 5-8min, is beaten It is warming up to 85 DEG C after mill and condenses rapidly and make up, so that brick face luminosity is maintained 29-35 degree, natural cooling to obtain the final product.

The beneficial effects of the present invention are:

Manufacturing cost is low and yield rate is higher, the advantage that hardness is good and flatness is good.The final luminosity of product is 29-35 degree, Visual comfort is good.

Detailed description of the invention

To describe the technical solutions in the embodiments of the present invention more clearly, make required in being described below to embodiment Attached drawing is briefly described, it should be apparent that, drawings in the following description are only some embodiments of the invention, for For those of ordinary skill in the art, without creative efforts, it can also be obtained according to these attached drawings other Attached drawing, in which:

Attached drawing 1 is structural schematic diagram of the invention.

1- ceramic tile ontology 2- wax layer in figure.

Specific embodiment

Technical solution of the present invention is clearly and completely described below in conjunction with Fig. 1, it is clear that described implementation Example is a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, ordinary skill Personnel's every other embodiment obtained without making creative work, shall fall within the protection scope of the present invention.