阅读说明：本技术 橡胶物品增强用钢丝帘线及其制造方法和轮胎 (Steel cord for reinforcing rubber article, method for producing same, and tire ) 是由 尾花直彦 近藤幹人 于 2018-04-11 设计创作，主要内容包括：提供一种橡胶物品增强用钢丝帘线,对于复捻的钢丝帘线,其相对于构成帘线的长丝的总强度的帘线强度不容易降低且具有高的橡胶浸透性。橡胶物品增强用钢丝帘线具有复捻结构,其中捻合多根股线,各股线通过以两层以上捻合多根长丝而得到。长丝中的至少一些的拉伸强度为3,000MPa以上。满足长丝占有率为48％以上且小于54％,帘线捻合角度为78°以上且小于84°,除了包边长丝之外的相邻长丝之间的交叉角的平均值为小于17°,并且构成股线的相邻鞘丝之间的间隙为0.065mm以上。(Provided is a steel cord for reinforcing rubber articles, which is hard to reduce the cord strength relative to the total strength of filaments constituting the cord and has high rubber permeability for a double-twisted steel cord. The steel cord for reinforcing rubber articles has a double-twisted structure in which a plurality of strands each obtained by twisting a plurality of filaments in two or more layers are twisted. At least some of the filaments have a tensile strength of 3,000MPa or greater. The filament occupancy is 48% or more and less than 54%, the cord twist angle is 78 DEG or more and less than 84 DEG, the average value of the crossing angle between adjacent filaments other than the covered filaments is less than 17 DEG, and the gap between adjacent sheath filaments constituting the strand is 0.065mm or more.)

1. a steel cord for reinforcing rubber articles, comprising:

A plurality of strands twisted in a double twist configuration, each strand comprising a plurality of filaments twisted into two or more layers, wherein at least some of the filaments have a tensile strength of 3,000MPa or greater;

Wherein the steel cord satisfies the following:

The filament occupancy is more than 48% and less than 54%;

The cord twisting angle is more than 78 degrees and less than 84 degrees;

The average value of the crossing angle between adjacent filaments other than the binding filaments is less than 17 °; and

The gap between adjacent sheath filaments constituting the strand is 0.065mm or more.

2. A steel cord for reinforcing rubber articles as claimed in claim 1, wherein the average value of the crossing angle between adjacent filaments is less than 14 °.

3. A steel cord for reinforcing rubber goods as claimed in claim 1 or 2, wherein the double-twisted structure is a 1+ n (n-6 or 7) structure comprising 1 core strand and 6 to 7 sheath strands twisted around the core strand.

4. The steel cord for rubber article reinforcement according to claim 3, wherein a twist direction of sheath filaments of the core strand is opposite to a twist direction of sheath filaments of the sheath strand.

5. The steel cord for reinforcing rubber articles according to claim 3, wherein the twist direction of the sheath filament of one of said sheath strands is opposite to the twist direction of the sheath filament of the other adjacent one of said sheath strands.

6. The steel cord for reinforcing rubber articles according to any one of claims 1 to 5, wherein the surface layer portion of at least some of the filaments has a sheet orientation angle of 0.0 ° or more and 6.0 ° or less, or 12.5 ° or more and 18.5 ° or less.

7. a tire using the steel cord for reinforcing a rubber article according to any one of claims 1 to 6 for reinforcement.

8. A method for manufacturing a steel cord for reinforcing a rubber article,

The steel cord for reinforcing a rubber article according to any one of claims 1 to 7, which comprises a plurality of strands twisted in a double-twisted structure, each strand comprising a plurality of filaments twisted into two or more layers;

the method includes stress relieving annealing at least some of the filaments comprising the strand after the final drawing process at 250 ℃ or above and below 300 ℃.

9. The method of manufacturing a steel cord for reinforcing a rubber article according to claim 8, wherein the stress relief annealing process is performed without performing a leveling process after the final drawing process.

10. a method for manufacturing a steel cord for reinforcing a rubber article,

The steel cord for reinforcing a rubber article according to any one of claims 1 to 7, which comprises a plurality of strands twisted in a double-twisted structure, each strand comprising a plurality of filaments twisted into two or more layers;

Wherein at least some of the filaments comprising the strand are not flattened after the final drawing process.

Technical Field

The present invention relates to a high-strength steel cord for reinforcing rubber articles, which has a double-twisted structure; a method for producing the same; and a tire.

background

Double-twisted steel cords are used for reinforcement of rubber articles including tires for construction and mining vehicles. In recent years, reduction in weight of rubber articles such as tires has been studied by reducing the thickness of a reinforcing layer including steel cords through simplification of a cord structure or reduction in cord diameter. In order to reduce the weight while securing the strength required for reinforcement, various studies and developments have been made to increase the strength of the double-twisted steel cord.

However, even when the strength of each filament constituting the double-twisted steel cord is increased, it is difficult to obtain a cord strength commensurate therewith. Thus, there is a need for a steel cord having a cord strength with a small loss compared to the total strength of the filaments constituting the cord.

cracks may be caused to reach the reinforcement layer as the tire passes over sharp obstacles, etc. The water entering from the crack causes rusting of the steel cord, thereby decreasing the strength. To prevent this, the steel cord is required to be rust-proof. For this reason, the double-twisted cord is required to have high rubber permeability by forming gaps between adjacent filaments, whereby rubber can be impregnated.

As for the double-twisted steel cord, a steel cord for reinforcing a rubber article has been disclosed in which the twist direction of the outermost sheath filaments constituting the cord and the twist direction of the sheath cord are the same (patent document 1).

Disclosure of Invention

Problems to be solved by the invention

The steel cord for reinforcing rubber articles disclosed in patent document 1 has improved cord strength obtained by specifying the twist direction of filaments and strands. However, there is a constant demand for steel cords having higher strength, and in particular, there is a demand for small loss in cord strength compared to the total strength of filaments constituting the cord. In addition, a steel cord having high rubber permeability is also demanded.

Accordingly, it is an object of the present invention to provide: a steel cord for reinforcing a rubber article, which is double-twisted, has a cord strength with a small loss compared with the total strength of filaments constituting the cord, and has a high rubber permeability; a method for producing the steel cord; and a tire using the steel cord.

Means for solving the problems

the present inventors intensively studied a double-twisted steel cord, and found that adjustment of a cord twist angle and a crossing angle between adjacent filaments to a predetermined range, and adjustment of a filament occupancy and a gap between specific filaments can provide a steel cord for reinforcing a rubber article having a cord strength with less loss compared to the total strength of filaments constituting the cord and having a high rubber permeability, thereby completing the present invention.

Thus, the steel cord for reinforcing rubber articles of the present invention comprises a plurality of strands twisted in a double-twisted structure, each strand having a plurality of filaments twisted into two or more layers, wherein at least some of the filaments have a tensile strength of 3,000MPa or more; and wherein the steel cord satisfies the following:

The filament occupancy is more than 48% and less than 54%;

The cord twisting angle is more than 78 degrees and less than 84 degrees;

The average value of the crossing angle between adjacent filaments other than the binding filaments is less than 17 °; and

The gap between adjacent sheath filaments constituting the strand is 0.065mm or more.

In the steel cord for reinforcing a rubber article of the present invention, the average value of the crossing angle between adjacent filaments is preferably less than 14 °.

Preferably, the double-twisted structure is a 1+ n (n-6 or 7) structure including 1 core strand and 6 to 7 sheath strands twisted around the core strand.

Preferably, the twist direction of the sheath filaments of the core strand is opposite to the twist direction of the sheath filaments of the sheath strand.

Preferably, the twisting direction of the sheath filaments of 1 said sheath strand is opposite to the twisting direction of the sheath filaments of another adjacent said sheath strand.

Preferably, the sheet orientation angle (lamellar orientation angle) of the surface layer portion of at least some of the filaments is 0.0 ° or more and 6.0 ° or less, or 12.5 ° or more and 18.5 ° or less.

The tire of the present invention is a tire in which the above-described steel cord for reinforcing a rubber article is used for the reinforcement thereof.

In order to manufacture the above-mentioned steel cord for reinforcing a rubber article having a plurality of strands twisted in a double twist structure, each strand having a plurality of filaments twisted in two or more layers, the method for manufacturing the steel cord for reinforcing a rubber article of the present invention includes subjecting at least some of the filaments constituting the strand to a stress relief annealing process at 250 ℃ or more and less than 300 ℃ after a final drawing process.

preferably, in the method for manufacturing a steel cord for reinforcing a rubber article of the present invention, after the final drawing process, the stress-relief annealing process is performed without performing the leveling process.

ADVANTAGEOUS EFFECTS OF INVENTION

According to the present invention, it is possible to provide a steel cord for reinforcing a rubber article, which is a double-twisted steel cord having a cord strength with a small loss compared to the total strength of filaments constituting the cord and a high rubber permeability; a method for producing the steel cord; and a tire using the steel cord.

Drawings

Fig. 1 is a sectional view of a steel cord for reinforcing a rubber article in one embodiment of the present invention.

Fig. 2 is a sectional view of a steel cord for reinforcing a rubber article in another embodiment of the present invention.

Fig. 3 illustrates the cord twist angle.

Fig. 4A illustrates the intersection angle between adjacent filaments.

Fig. 4B illustrates the crossing angle between sheath filaments of adjacent strands.

Fig. 5 illustrates a gap between adjacent sheath filaments.

Detailed Description

Hereinafter, the steel cord for reinforcing rubber articles, the manufacturing method of the steel cord, and the tire using the steel cord of the present invention will be described in more detail with reference to the accompanying drawings.

Fig. 1 is a sectional view of a steel cord for reinforcing a rubber article (hereinafter simply referred to as "steel cord") in a direction perpendicular to a longitudinal direction of the steel cord in one embodiment of the present invention. The steel cord 10 shown in fig. 1 is a cord having a double-twisted structure including 1 core strand 11 and 6 sheath strands 12 twisted together, and has a cord structure of (3+9) +6 × (3+9) + 1. The outermost layer of the sheath strand 12 is wound with a covered filament 13. The core strand 11 has a two-layer twisted structure including 3 core filaments 111 and 9 sheath filaments 112 around them twisted together, and the sheath strand 12 has a two-layer twisted structure including 3 core filaments 121 and 9 sheath filaments 122 around them twisted together.

Fig. 2 is a sectional view of a steel cord in a direction perpendicular to a lengthwise direction of the steel cord in another embodiment of the present invention. The steel cord 20 shown in fig. 2 is a cord having a double-twisted structure including 1 core strand 21 and 6 sheath strands 22 twisted together, and has a (3+7) +6 × (3+7) +1 cord structure. The outermost layer of the sheath strand 22 is wound with a covered filament 23. The core strand 21 has a two-layer twisted structure including 3 core filaments 211 twisted together with 7 sheath filaments 212 around them, and the sheath strand 22 has a two-layer twisted structure including 3 core filaments 221 twisted together with 7 sheath filaments 222 around them.

The steel cord of the present invention is not limited to the cord structure shown in fig. 1 and 2. Preferably, a 1+ n (n-6 or 7) cord construction is used.

The steel cord of the present invention described below is characterized by the same as the steel cord 10 in fig. 1 and the steel cord 20 in fig. 2, and the steel cord in other embodiments of the present invention. Thus, in the following description, an embodiment of the present invention in which the steel cord 10 shown in fig. 1 is used to reinforce a tire will be described as a main representative example.

in the present embodiment, at least some of the filaments of the steel cord 10 have a tensile strength of 3,000MPa or more. For example, the tensile strength of the core filaments 121 and the sheath filaments 122 of the sheath strands 12 forming the steel cord 10 is 3,000MPa or more. When the tensile strength of some filaments of the steel cord 10 is 3,000MPa or more, the steel cord 10 in the present embodiment may have an increased strength. From the viewpoint of enhancing the strength of the steel cord 10, the tensile strength of all filaments constituting the steel cord 10 is preferably 3,000MPa or more.

The filament occupancy of the steel cord 10 in the present embodiment is 48% or more and less than 54%. The filament occupancy is a value represented by a percentage obtained by dividing the total cross-sectional area of filaments constituting the steel cord by the area of a circumscribed circle of the steel cord and multiplying the obtained value by 100. Thus, the filament occupancy (%) is (total cross-sectional area of filaments constituting the steel cord)/(area of circumscribed circle of the steel cord) × 100.

When the filament occupancy is in the range of 48% or more and less than 54%, the steel cord may have improved strength at high filament filling efficiency and achieve high rubber permeability. When the filament occupancy is less than 48%, the diameter of the steel cord 10 to achieve the necessary strength of the steel cord 10 increases due to low filament filling efficiency. This results in thickening of the rubber reinforcing layer when the steel cord 10 is used to reinforce a tire. Therefore, such a filament occupancy is disadvantageous in terms of weight reduction of the tire. When the filament occupancy is 54% or more, gaps between adjacent filaments described later are reduced, which results in poor rubber permeability. The filament occupancy is preferably 48% or more and less than 50%.

The cord twist angle of the steel cord 10 of the present embodiment is 78 ° or more and less than 84 °. As shown in fig. 3, the cord twist angle α is an angle formed by a direction perpendicular to the longitudinal direction of the steel cord and a direction along the longitudinal direction of the strand (in the case of the steel cord 10 of fig. 1, it refers to the sheath strand 12). The cord twist angle may be measured from the steel cord, or may be calculated from the cord diameter, strand diameter, and strand twist pitch of the steel cord.

When the cord twist angle is in the range of 78 ° or more and less than 84 °, a steel cord having a small loss of strength due to twisting and a stable twist behavior can be obtained. When the cord twist angle is less than 78 °, the twist is strong and the loss of strength due to the twist becomes too large to obtain a predetermined strength of the steel cord. Here, the strength loss due to twisting means a value obtained by subtracting the cord strength exertion rate (%) from 100. Thus, the strength loss due to twisting is as follows:

Strength loss due to twisting (%) -100-percentage of exertion of cord strength

The cord strength exertion rate is a value represented by a percentage obtained by dividing the strength of the steel cord by the total strength of the filaments constituting the steel cord and multiplying the obtained value by 100. Thus, the cord strength exertion rate is as follows:

The cord strength exertion rate (%) (strength of steel cord)/(total strength of filaments constituting steel cord) × 100

Preferably, the cord strength exertion rate is 90% or more. When the cord strength exertion rate is large, or when the loss of strength due to twisting is small, the steel cord may have a cord strength with a small loss compared to the total strength of filaments constituting the cord. When the cord twist angle is 84 ° or more, the twist is weak and the twist behavior becomes unstable. Preferably, the cord twist angle is 80 ° or more and less than 84 °.

In the present embodiment, the steel cord 10 has an average value of the crossing angle between the adjacent filaments other than the covered filaments of less than 17 °. When the average value of the crossing angle between adjacent filaments is less than 17 °, the loss of strength due to twisting is reduced. To illustrate the crossing angle between adjacent filaments, fig. 4A shows an exemplary crossing angle β between the core filament 111 and the sheath filament 112 of the core strand 11. To illustrate the crossing angle between sheath filaments of adjacent strands, fig. 4B shows an embodiment of the sheath filaments 112 of the core strand 11 and the sheath filaments 122 of the sheath strand 12. As shown in fig. 4A and 4B, the crossing angle means an angle formed by the length direction of 1 filament and the length direction of another filament adjacent to the previous filament. The average value of the crossing angle of the steel cord 10 means an average value of all crossing angles between adjacent filaments, such as a crossing angle between adjacent core filaments 111, a crossing angle between adjacent sheath filaments 112, a crossing angle between the core filament 111 and the sheath filament 112 of the core strand 11, a crossing angle between adjacent core filaments 121, a crossing angle between adjacent sheath filaments 122, a crossing angle between the core filament 121 and the sheath filament 122 of the sheath strand 12, a crossing angle between the sheath filament 112 of the core strand 11 and the sheath filament 122 of the sheath strand 12, a crossing angle between the sheath filament 122 of the adjacent sheath strand 12, and the like. Note that: the crossing angle between the binding filament 13 and the other filaments is not included in the average value.

When the average value of the crossing angle between adjacent filaments is 17 ° or more, the contact pressure between adjacent filaments during drawing of the steel cord is high, so that the loss of strength due to twisting is large. Preferably, the crossing angle between adjacent filaments has an average value of less than 14 °. When the average value of the crossing angle is less than 14 °, the loss of strength due to twisting can be further reduced.

in the steel cord 10 of the present embodiment, the gap between the adjacent sheath filaments in the sheath filaments constituting the strand is 0.065mm or more. More specifically, as shown in the explanatory view of the gap between the adjacent sheath filaments of the steel cord 20 of the present embodiment in fig. 5, the gap g between the adjacent sheath filaments is 0.065mm or more for both between the sheath filaments 212 forming the core strand 21 and between the sheath filaments 222 forming the sheath strand 22. When the gap between the adjacent sheath filaments is 0.065mm or more, the rubber permeability of the steel cord may be improved. When the gap between adjacent sheath filaments is less than 0.065mm, rubber permeability is poor. Preferably, the gap is 0.065mm or more and 0.100mm or less.

In the steel cord 10 in the present embodiment, the twist direction of the sheath filaments 112 of the core strand 11 is preferably opposite to the twist direction of the sheath filaments 122 of the sheath strand 12. When the twist direction of the sheath filaments 112 of the core strand 11 is preferably opposite to the twist direction of the sheath filaments 122 of the sheath strand 12, the average value of the crossing angle between adjacent filaments decreases.

In the steel cord 10 in the present embodiment, the twist direction of the sheath filaments 122 of 1 sheath strand 12 is preferably opposite to the twist direction of the sheath filaments 122 of another sheath strand 12 adjacent thereto. When the twist directions of the sheath filaments 122 of the adjacent sheath strands 12 are opposite to each other, the average value of the crossing angle between the adjacent filaments decreases.

In the steel cord 10 in the present embodiment, at least some of the filaments have a sheet orientation angle of the surface layer portion of 0.0 ° or more and 6.0 ° or less, or 12.5 ° or more and 18.5 ° or less. The surface portion refers to a region of the filament in a range of from the outermost surface to 20% volume fraction. The orientation angle of the lamellae of the surface layer portion of all the filaments may satisfy the above range.

The orientation angle of the thin layer will be explained. When manufacturing a filament, a raw material of a steel wire is drawn, and then subjected to a heating treatment, a plating process, and a final drawing process, thereby obtaining a filament having a predetermined wire diameter. During the final drawing process, the crystal structure of ferrite and cementite is oriented so that the orientation of the thin layers of the crystal groups (colunes) constituting the block (block) is aligned with the drawing direction, i.e., the longitudinal direction of the filament. According to the studies conducted by the present inventors, it was found that the sheet orientation angle of the surface layer portion affects the resistance of the filament to the lateral pressure applied from the adjacent filament. When the sheet orientation angle of the surface layer portion is 0.0 ° or more and 6.0 ° or less, or 12.5 ° or more and 18.5 ° or less, the resistance to lateral pressure applied to the filament increases, the cord strength exertion rate improves, and the strength loss due to twisting decreases. The orientation angle of the thin layer of the surface layer portion can be adjusted within the above range by, for example, adjusting the die angle (die angle) during the final drawing process. The angle of orientation of the lamellae can be measured by observing the metallographic structure of the filaments.

Next, a method of manufacturing the steel cord 10 in the present embodiment will be explained. The material of the steel wire is drawn for the filaments constituting each strand, and then subjected to heating treatment, plating processing, and final drawing processing, thereby obtaining filaments having a predetermined wire diameter. After the final drawing process, a stress relief annealing process is performed. Preferably, the stress relief annealing process is performed at a temperature of 250 ℃ or more and less than 300 ℃. When the stress relief annealing process is performed at a temperature of 250 ℃ or more and less than 300 ℃, the steel cord has high strength and a small loss of strength due to twisting can be easily obtained. When the stress relief annealing process is performed at a temperature lower than 250 ℃, the effect obtained from the stress relief annealing process is small and the loss of strength due to twisting is large. When the stress relief annealing process is performed at a temperature of 300 ℃ or higher, the stress relief annealing process causes over-annealing, which decreases the strength of the filament.

The flattening process, i.e., the process of applying repeated bending, for example, by staggered rollers, improves the residual stress and straightness of the filaments. However, the repeated bending processing of the filaments by the flattening processing increases the processing strain inside the filaments and increases the loss of strength due to twisting. Therefore, in order to reduce the strength loss due to twisting, leveling processing is not performed. Therefore, it is preferable to perform stress relief annealing as a process immediately after the final drawing process.

Further, the drawing conditions are preferably adjusted in the final drawing process in consideration of the orientation angle of the thin layer of the surface layer portion of the filament.

The steel cord 10 in the present embodiment is suitable for use in reinforcement of a tire. However, the use of the steel cord 10 in the present embodiment is not limited to tires.