阅读说明：本技术 一种天然乳胶纤维的制备方法 (Preparation method of natural latex fiber ) 是由 不公告发明人 于 2021-09-03 设计创作，主要内容包括：本发明公开了一种天然乳胶纤维的制备方法,一种天然乳胶纤维,包括以下份数,纤维100份,天然乳胶原液2-8份,亲水200-300份,抗菌剂0.5-1.5份。上述天然乳胶纤维的制备方法包括以下步骤：步骤1、将称取各原料备用。步骤2、将天然乳胶原液与抗菌剂混合搅拌均匀。步骤3、将混合原液与水混合搅拌均匀,得到液体。步骤4、将纤维分批放入容器中,同时分批注入混合液体。步骤5、将混合液体与纤维通过蒸汽升温至50-60度,保温30-45分钟。步骤6、将纤维取出,脱水、烘干,得到天然乳胶短纤维。本发明的有益效果是外面用乳胶包覆,使纤维在不失保暖的情况下可对人体睡眠安稳、抑制细菌、螨虫滋生。(The invention discloses a preparation method of natural latex fiber, which comprises the following components, by weight, 100 parts of fiber, 2-8 parts of natural latex stock solution, 300 parts of hydrophilic 200-chitosan and 0.5-1.5 parts of antibacterial agent. The preparation method of the natural latex fiber comprises the following steps: step 1, weighing all the raw materials for later use. And 2, mixing and stirring the natural latex stock solution and the antibacterial agent uniformly. And 3, mixing the mixed stock solution with water and uniformly stirring to obtain liquid. And 4, putting the fibers into the container in batches, and injecting the mixed liquid in batches at the same time. And 5, heating the mixed liquid and the fibers to 50-60 ℃ through steam, and preserving the heat for 30-45 minutes. And 6, taking out the fibers, dehydrating and drying to obtain the natural latex short fibers. The invention has the beneficial effects that the outside of the fabric is coated by latex, so that the fiber can be used for stabilizing the sleep of a human body and inhibiting the breeding of bacteria and mites without losing warmth.)

1. A method for preparing natural latex fiber is characterized in that natural latex coats short fiber.

2. The natural latex fiber as claimed in claim 1, wherein the ratio of the natural latex fiber is 100 parts of fiber, 2-8 parts of natural latex stock solution, 300 parts of hydrophilic 200-gel and 0.5-1.5 parts of antibacterial agent.

3. The natural latex fiber according to claims 1-2, wherein said natural latex fiber is a fiber of polyester, acrylic, nylon, down, silk, wool, modal, lyocell, cotton, bamboo fiber, polylactic acid, viscose.

4. A method of preparing a natural latex fiber according to claims 1-3, comprising the steps of:

step 1, weighing all the raw materials for later use.

And 2, mixing and stirring the natural latex stock solution and the antibacterial agent uniformly.

And 3, mixing the mixed stock solution with water and uniformly stirring to obtain liquid.

And 4, putting the fibers into the container in batches, and injecting the mixed liquid in batches at the same time.

And 5, heating the mixed liquid and the fibers to 50-60 ℃ through steam, and preserving the heat for 30-45 minutes.

And 6, taking out the fibers, dehydrating and drying to obtain the natural latex short fibers.

Technical Field

The invention relates to the field of textiles, in particular to fibers and a preparation method thereof.

Background

The natural latex product is popular with users due to the characteristics of air permeability, moisture absorption, soft touch, high elasticity and the like. The natural latex is the juice of rubber tree, the whole production process is a 'physical process', no chemical process is involved, the natural latex is nontoxic and harmless fundamentally, and the natural latex is safe for human beings and does not pollute the environment.

One third of the time in one lifetime is in sleep, while home textiles are essential for sleep. At present, home textiles are various in varieties, for example, quilts comprise cotton, down feather, silk, wool, polyester fibers, acrylic fibers, chinlon, modal, lyocell, bamboo fibers, polylactic acid viscose and the like, and the application of natural latex to short fibers and the application of the short fibers to home textile dormitories are not related in the prior art.

The latex is made of natural raw materials, can emit unique latex fragrance, and the fragrance not only can make people sleep stably, but also can inhibit breeding of mites. And because of the relation of materials, it does not produce the static electricity, this has reduced the invasion of dust greatly, it is very helpful to the improvement of the respiratory disease.

Disclosure of Invention

Aiming at the problem that the natural latex is applied to short fibers and used in home textile dormitories in the prior art, common fibers have no fragrance and cannot enable people to sleep stably and inhibit the breeding of bacteria and mites. The invention provides a preparation method of natural latex fiber, which is coated with latex. The fiber can make the human body sleep stably and inhibit the breeding of bacteria and mites without losing warmth.

Preferably, the natural latex fiber is latex coated with the polyester hollow short fiber.

The preferred short fiber is 1Dtex-22Dtex terylene, acrylic fiber, chinlon, down, silk, wool, modal, lyocell, cotton, bamboo fiber, polylactic acid and viscose fiber.

The preferable natural latex fiber comprises the following components, by weight, 100 parts of fiber, 2-8 parts of natural latex stock solution, 300 parts of hydrophilic 200-300 parts of antibacterial agent and 0.5-1.5 parts of antibacterial agent.

The preparation method of the natural latex fiber comprises the following steps:

step 1, weighing all the raw materials for later use.

And 2, mixing and stirring the natural latex stock solution and the antibacterial agent uniformly.

And 3, mixing the mixed stock solution with water and uniformly stirring to obtain liquid.

And 4, putting the fibers into the container in batches, and injecting the mixed liquid in batches at the same time.

And 5, heating the mixed liquid and the fibers to 50-60 ℃ through steam, and preserving the heat for 30-45 minutes.

And 6, taking out the fibers, dehydrating and drying to obtain the natural latex short fibers.

Detailed description of the invention

The technical solutions in the embodiments of the present invention will be fully described below with reference to the embodiments of the present invention. It is to be understood that the described embodiments are merely a few embodiments of the invention, and not all embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.

Example one

The natural latex fiber comprises 100 parts of polyester fiber, 5 parts of natural latex stock solution, 250 parts of hydrophilic fiber and 1 part of antibacterial agent.

The preparation method of the natural latex fiber comprises the following steps:

step 1, weighing all the raw materials for later use.

And 2, mixing and stirring the natural latex stock solution and the antibacterial agent uniformly.

And 3, mixing the mixed stock solution with water and uniformly stirring to obtain liquid.

And 4, putting the fibers into the container in batches, and injecting the mixed liquid in batches at the same time.

And 5, heating the mixed liquid and the fibers to 55 ℃ through steam, and preserving the heat for 40 minutes.

And 6, taking out the fibers, dehydrating and drying to obtain the natural latex polyester staple fibers.

Example two

A natural latex fiber comprises 100 parts of acrylic fiber, 2 parts of natural latex stock solution, 200 parts of hydrophilic fiber and 0.5 part of antibacterial agent.

The preparation method of the natural latex fiber comprises the following steps:

step 1, weighing all the raw materials for later use.

And 2, mixing and stirring the natural latex stock solution and the antibacterial agent uniformly.

And 3, mixing the mixed stock solution with water and uniformly stirring to obtain liquid.

And 4, putting the fibers into the container in batches, and injecting the mixed liquid in batches at the same time.

And 5, heating the mixed liquid and the fibers to 50 ℃ through steam, and preserving the heat for 30 minutes.

And 6, taking out the fibers, dehydrating and drying to obtain the natural latex acrylic staple fibers.

EXAMPLE III

A natural latex fiber comprises 100 parts of nylon fiber, 3 parts of natural latex stock solution, 210 parts of hydrophilic fiber and 0.5 part of antibacterial agent.

The preparation method of the natural latex fiber comprises the following steps:

step 1, weighing all the raw materials for later use.

And 2, mixing and stirring the natural latex stock solution and the antibacterial agent uniformly.

And 3, mixing the mixed stock solution with water and uniformly stirring to obtain liquid.

And 4, putting the fibers into the container in batches, and injecting the mixed liquid in batches at the same time.

And 5, heating the mixed liquid and the fibers to 55 ℃ through steam, and preserving the heat for 30 minutes.

And 6, taking out the fibers, dehydrating and drying to obtain the natural latex chinlon staple fibers.

Example four

A natural latex fiber comprises 100 parts of modal fiber, 4 parts of natural latex stock solution, 220 parts of hydrophilic fiber and 0.6 part of antibacterial agent.

The preparation method of the natural latex fiber comprises the following steps:

step 1, weighing all the raw materials for later use.

And 2, mixing and stirring the natural latex stock solution and the antibacterial agent uniformly.

And 3, mixing the mixed stock solution with water and uniformly stirring to obtain liquid.

And 4, putting the fibers into the container in batches, and injecting the mixed liquid in batches at the same time.

And 5, heating the mixed liquid and the fibers to 55 ℃ through steam, and preserving the heat for 30 minutes.

And 6, taking out the fibers, dehydrating and drying to obtain the natural latex modal staple fibers.

EXAMPLE five

A natural latex fiber comprises 100 parts of bamboo fiber, 6 parts of natural latex stock solution, 230 parts of hydrophilic fiber and 0.6 part of antibacterial agent.

The preparation method of the natural latex fiber comprises the following steps:

step 1, weighing all the raw materials for later use.

And 2, mixing and stirring the natural latex stock solution and the antibacterial agent uniformly.

And 3, mixing the mixed stock solution with water and uniformly stirring to obtain liquid.

And 4, putting the fibers into the container in batches, and injecting the mixed liquid in batches at the same time.

And 5, heating the mixed liquid and the fibers to 58 ℃ through steam, and preserving the heat for 35 minutes.

And 6, taking out the fibers, dehydrating and drying to obtain the natural latex bamboo short fibers.

EXAMPLE six

A natural latex fiber comprises 100 parts of polylactic acid fiber, 8 parts of natural latex stock solution, 240 parts of hydrophile and 0.7 part of antibacterial agent.

The preparation method of the natural latex fiber comprises the following steps:

step 1, weighing all the raw materials for later use.

And 2, mixing and stirring the natural latex stock solution and the antibacterial agent uniformly.

And 3, mixing the mixed stock solution with water and uniformly stirring to obtain liquid.

And 4, putting the fibers into the container in batches, and injecting the mixed liquid in batches at the same time.

And 5, heating the mixed liquid and the fibers to 58 ℃ through steam, and preserving the heat for 35 minutes.

And 6, taking out the fibers, dehydrating and drying to obtain the natural latex polylactic acid short fibers.

EXAMPLE seven

The natural latex fiber includes wool fiber 100 weight portions, natural latex liquid 5 weight portions, hydrophilic 260 weight portions and antiseptic 0.9 weight portions.

The preparation method of the natural latex fiber comprises the following steps:

step 1, weighing all the raw materials for later use.

And 2, mixing and stirring the natural latex stock solution and the antibacterial agent uniformly.

And 3, mixing the mixed stock solution with water and uniformly stirring to obtain liquid.

And 4, putting the fibers into the container in batches, and injecting the mixed liquid in batches at the same time.

And 5, heating the mixed liquid and the fibers to 58 ℃ through steam, and preserving the heat for 35 minutes.

And 6, taking out the fibers, dehydrating and drying to obtain the natural latex wool short fibers.

Example eight

A natural latex fibre is prepared from lyocell fibre (100 portions), natural latex stock solution (6 portions), hydrophilic fibre (280 portions) and antibacterial agent (1.1 portions).

The preparation method of the natural latex fiber comprises the following steps:

step 1, weighing all the raw materials for later use.

And 2, mixing and stirring the natural latex stock solution and the antibacterial agent uniformly.

And 3, mixing the mixed stock solution with water and uniformly stirring to obtain liquid.

And 4, putting the fibers into the container in batches, and injecting the mixed liquid in batches at the same time.

And 5, heating the mixed liquid and the fibers to 60 ℃ through steam, and preserving the heat for 40 minutes.

And 6, taking out the fibers, dehydrating and drying to obtain the natural latex lyocell short fibers.

Example nine

A natural latex fiber comprises 100 parts of cotton fiber, 4 parts of natural latex stock solution, 300 parts of hydrophile and 1.3 parts of antibacterial agent.

The preparation method of the natural latex fiber comprises the following steps:

step 1, weighing all the raw materials for later use.

And 2, mixing and stirring the natural latex stock solution and the antibacterial agent uniformly.

And 3, mixing the mixed stock solution with water and uniformly stirring to obtain liquid.

And 4, putting the fibers into the container in batches, and injecting the mixed liquid in batches at the same time.

And 5, heating the mixed liquid and the fibers to 60 ℃ through steam, and preserving the heat for 40 minutes.

And 6, taking out the fibers, dehydrating and drying to obtain the natural latex cotton staple fibers.

Example ten

The natural latex fiber includes viscose fiber 100 weight portions, natural latex liquid 8 weight portions, hydrophilic material 300 weight portions and antiseptic 1.3 weight portions.

The preparation method of the natural latex fiber comprises the following steps:

step 1, weighing all the raw materials for later use.

And 2, mixing and stirring the natural latex stock solution and the antibacterial agent uniformly.

And 3, mixing the mixed stock solution with water and uniformly stirring to obtain liquid.

And 4, putting the fibers into the container in batches, and injecting the mixed liquid in batches at the same time.

And 5, heating the mixed liquid and the fibers to 60 ℃ through steam, and preserving the heat for 40 minutes.

And 6, taking out the fibers, dehydrating and drying to obtain the natural latex viscose staple fibers.

The natural latex fiber has slight milk fragrance in the aspect of perception, and is softer and more elastic in hand feeling than common fibers.

The above description is only a preferred embodiment of the present invention, and is not intended to limit the present invention. Various modifications and changes may occur to those skilled in the art, and any modification, equivalent replacement, or improvement made without departing from the spirit and principle of the present invention is also encompassed in the present invention.