阅读说明：本技术 一种磁性软镜子及其制作工艺 (Magnetic soft lens and manufacturing process thereof ) 是由 王文明 于 2021-11-25 设计创作，主要内容包括：本发明涉及一种磁性软镜子及其制作工艺,属于镜子技术领域。磁性软镜子包括镜面层、磁吸层以及固化层,镜面层与磁吸层粘接连接,磁吸层与固化层粘接连接；固化层包括靠近磁吸层的粘接封装片以及与粘接封装片相对的固化封装片,粘接封装片与固化封装片之间填充有光固化材料；固化封装片由透明材料组成,固化封装片外包覆有用于防止光线照射至光固化材料的阻光膜；粘接封装片与固化封装片的材质均为软质的PVC材质或胶质。磁性软镜子方便运输,在运输过程中不易损坏。镜子可以贴附在铁质的墙或门上,不需要粘贴,不会对其表面破坏。(The invention relates to a magnetic soft mirror and a manufacturing process thereof, belonging to the technical field of mirrors. The magnetic soft lens comprises a mirror surface layer, a magnetic attraction layer and a curing layer, wherein the mirror surface layer is connected with the magnetic attraction layer in an adhesive manner, and the magnetic attraction layer is connected with the curing layer in an adhesive manner; the solidified layer comprises an adhesive packaging sheet close to the magnetic absorption layer and a solidified packaging sheet opposite to the adhesive packaging sheet, and a light-cured material is filled between the adhesive packaging sheet and the solidified packaging sheet; the curing packaging sheet is made of transparent materials, and a light-blocking film for preventing light from irradiating the photocuring materials is coated outside the curing packaging sheet; the bonding packaging sheet and the curing packaging sheet are made of soft PVC materials or colloid. The magnetic soft lens is convenient to transport and is not easy to damage in the transportation process. The mirror can be attached to an iron wall or door without being adhered, and the surface of the mirror cannot be damaged.)

1. A magnetic soft mirror is characterized by comprising a mirror surface layer, a magnetic attraction layer and a curing layer, wherein the mirror surface layer is connected with the magnetic attraction layer in an adhesive manner; the solidified layer comprises an adhesive packaging sheet close to the magnetic absorption layer and a solidified packaging sheet opposite to the adhesive packaging sheet, and a light-cured material is filled between the adhesive packaging sheet and the solidified packaging sheet; the curing packaging sheet is made of transparent materials, and a light-blocking film for preventing light from irradiating the photocuring materials is coated outside the curing packaging sheet; the bonding packaging sheet and the curing packaging sheet are made of soft PVC materials or colloid.

2. The magnetic soft mirror according to claim 1, wherein the photo-curable material comprises the following components in parts by mass: 100 parts of epoxy resin, 3-5 parts of monomer, 0.5-1.2 parts of photoinitiator and 0.1-0.3 part of thickener.

3. The magnetic soft mirror according to claim 2, wherein the epoxy resin is bisphenol a type epoxy resin E-51 or bisphenol a type epoxy resin E-44; the monomer is acrylic acid; the photoinitiator is a photoinitiator 6992 or a photoinitiator 1173.

4. The magnetic soft mirror according to claim 2, wherein the thickener is one of xanthan gum, polyoxyethylene or sodium polyacrylate.

5. A magnetic soft mirror according to any one of claims 1 to 4, wherein a three-dimensional latticed skeleton for preventing the light-curable material from moving freely is arranged between the bonding encapsulating sheet and the curing encapsulating sheet, and the three-dimensional latticed skeleton is filled between the bonding encapsulating sheet and the curing encapsulating sheet in a saturated manner.

6. A magnetic soft mirror according to any one of claims 1 to 4, wherein the photo-setting material is viscous paste before curing, and the hardness of the photo-setting material after curing is 3 to 4H.

7. A magnetic soft mirror according to any of claims 1 to 4, wherein the magnetically attractive layer is comprised of magnetic rubber.

8. The magnetic soft mirror according to any one of claims 1 to 4, wherein the material of the mirror layer is a high brightness VMPET aluminized polyester film.

9. The magnetic soft mirror of claim 1, wherein the light blocking film is a black PVC coating.

10. A process for making a magnetic soft mirror as claimed in claim 1, comprising the steps of:

1) the mirror layer is connected with the magnetic attraction layer in an adhesive mode to obtain a magnetic soft mirror body;

2) the curing packaging sheet is provided with two opposite surfaces of an A surface and a B surface, and a light-blocking film, namely a black PVC (polyvinyl chloride) coating film is coated on the A surface of the curing packaging sheet through a coating machine to obtain the coated curing packaging sheet;

3) coating a light-curing material on the surface B of the curing packaging sheet, wherein the bonding packaging sheet is provided with two opposite surfaces, namely a surface C and a surface D, and the surface C of the bonding packaging sheet faces the light-curing material covering the curing packaging sheet and is adhered to the light-curing material; bonding the periphery of the bonding packaging sheet and the periphery of the curing packaging sheet by using a black sealing adhesive tape so as to package the light-curing material between the bonding packaging sheet and the curing packaging sheet;

4) and (3) bonding and connecting one surface of the magnetic layer of the magnetic soft mirror body with the bonding packaging sheet to obtain the magnetic soft mirror.

Technical Field

The invention belongs to the technical field of mirrors, and particularly relates to a magnetic soft mirror and a manufacturing process thereof.

Background

There are three main types of mirrors currently in use: glass mirrors, acrylic sheet mirrors, and aluminized soft mirrors.

The glass mirror is fragile, inconvenient to transport and easy to hurt people after being broken.

The aluminized soft mirror is soft and is easily stuck on the wall, so that the phenomenon of distorting mirror occurs. For example, the invention patent with application publication number CN104605606A discloses a soft mirror, which is prepared by the following method: mirror finishing: the mirror surface is formed by compounding a high-brightness VMPET aluminized polyester film and a POF film, the aluminized surface of the high-brightness VMPET aluminized polyester film is used as a gluing surface, after an adhesive is coated, the high-brightness VMPET aluminized polyester film is compounded with the POF film and wound to obtain a composite film semi-finished product, the composite film semi-finished product is placed into a curing chamber, and after curing, a composite film finished product is obtained; assembling: cutting the finished composite film product according to the size of the mirror frame, and fixing the cut finished composite film product on the mirror frame to obtain a semi-finished soft mirror; and (3) post-treatment: and carrying out heat treatment on the semi-finished product of the soft mirror to obtain a product. The soft lens is formed by compounding an aluminized polyester film and a POF film, has low hardness, and can be unsmooth when being stuck on a wall.

The back of an acrylic mirror is generally glued to a support surface, such as the back of a wall or door, which is irreversibly damaged.

Disclosure of Invention

The invention aims to provide a magnetic soft mirror which can be attracted on a plate made of an iron material through magnetic force.

Yet another object of the present invention is to provide a process for manufacturing a magnetic soft mirror.

In order to achieve the above purpose, the invention adopts the technical scheme that:

a magnetic soft mirror comprises a mirror surface layer, a magnetic absorption layer and a curing layer, wherein the mirror surface layer is connected with the magnetic absorption layer in an adhesive manner, and the magnetic absorption layer is connected with the curing layer in an adhesive manner; the solidified layer comprises an adhesive packaging sheet close to the magnetic absorption layer and a solidified packaging sheet opposite to the adhesive packaging sheet, and a light-cured material is filled between the adhesive packaging sheet and the solidified packaging sheet; the curing packaging sheet is made of transparent materials, and a light-blocking film for preventing light from irradiating the photocuring materials is coated outside the curing packaging sheet; the bonding packaging sheet and the curing packaging sheet are made of soft PVC materials or colloid.

The thickness of the bonding packaging sheet is 0.3-0.5 mm, and the thickness of the curing packaging sheet is 0.3-0.5 mm.

The thickness of the light curing material filled between the bonding packaging sheet and the curing packaging sheet is 2.5-3.5 mm.

The thickness of the magnetic absorption layer is 0.8-1.2 mm.

Further, the light-cured material comprises the following components in parts by mass: 100 parts of epoxy resin, 3-5 parts of monomer, 0.5-1.2 parts of photoinitiator and 0.1-0.3 part of thickener.

Further, the epoxy resin is bisphenol A type epoxy resin E-51 or bisphenol A type epoxy resin E-44; the monomer is acrylic acid; the photoinitiator is a photoinitiator 6992 or a photoinitiator 1173.

Further, the thickening agent is one of xanthan gum, polyoxyethylene or sodium polyacrylate.

Furthermore, a three-dimensional latticed framework for preventing the light curing material from moving randomly is arranged between the bonding packaging sheet and the curing packaging sheet, and the three-dimensional latticed framework is filled between the bonding packaging sheet and the curing packaging sheet in a saturated mode.

Further, the light-cured material is viscous paste before curing, and the hardness after curing is 3-4H.

Further, the magnetic attraction layer is composed of magnetic rubber, which is commercially available.

Furthermore, the material of mirror layer is high bright VMPET aluminized polyester film. High-gloss VMPET aluminized polyester film is commercially available.

Further, the light-blocking film is a black PVC coating.

The manufacturing process of the magnetic soft mirror comprises the following steps:

1) the mirror layer is connected with the magnetic attraction layer in an adhesive mode to obtain a magnetic soft mirror body;

2) the curing packaging sheet is provided with two opposite surfaces of an A surface and a B surface, and a light-blocking film, namely a black PVC (polyvinyl chloride) coating film is coated on the A surface of the curing packaging sheet through a coating machine to obtain the coated curing packaging sheet;

3) coating a light-curing material on the surface B of the curing packaging sheet, wherein the bonding packaging sheet is provided with two opposite surfaces, namely a surface C and a surface D, and the surface C of the bonding packaging sheet faces the light-curing material covering the curing packaging sheet and is adhered to the light-curing material; bonding the periphery of the bonding packaging sheet and the periphery of the curing packaging sheet by using a black sealing adhesive tape so as to package the light-curing material between the bonding packaging sheet and the curing packaging sheet;

4) and (3) bonding and connecting one surface of the magnetic layer of the magnetic soft mirror body with the bonding packaging sheet to obtain the magnetic soft mirror.

The invention has the beneficial effects that:

the material of the bonding packaging sheet and the material of the curing packaging sheet of the magnetic soft mirror are soft PVC material or colloid, the whole base material is soft before the light curing material is not cured, and the magnetic soft mirror can be rolled up for transportation. The light-cured material can form an even hard plate after being cured, the mirror surface layer is loaded on the hard plate, the mirror surface is even, and a bad mirror image of a distorting mirror cannot be generated. The magnetic layer can enable the mirror to be attached to an iron wall or door without being adhered, and the surface of the mirror cannot be damaged.

According to the magnetic soft mirror, the light curing material contains the thickening agent, and the thickening agent can increase the viscosity of the light curing material and prevent the light curing material from moving back and forth between the bonding packaging sheet and the curing packaging sheet. The arrangement of the three-dimensional grid-shaped framework can further prevent the movement of the light-cured material.

Drawings

Fig. 1 is a cross-sectional view of a magnetic soft mirror.

Detailed Description

The present invention will be further described with reference to the following examples and accompanying drawings.

Example 1

The soft mirror of magnetism of this embodiment, including mirror layer 1, magnetism inhale layer 2 and cured layer 3, mirror layer 1 and magnetism inhale 2 adhesive linkage in layer, magnetism inhale 2 and cured layer 3 adhesive linkage in layer.

The mirror layer 1 is a layer of high-brightness VMPET aluminized polyester film which has a mirror effect.

The magnetic absorption layer is a layer of magnetic rubber, and the magnetic rubber is purchased from the market.

The solidified layer 3 comprises an adhesive packaging sheet 31 close to the magnetic absorption layer and a solidified packaging sheet 32 opposite to the adhesive packaging sheet, and a light-cured material 33 is filled between the adhesive packaging sheet and the solidified packaging sheet.

The photocuring material comprises the following components in parts by mass: 100 parts of epoxy resin, 3 parts of monomer, 0.5 part of photoinitiator and 0.3 part of thickener. The epoxy resin is bisphenol A type epoxy resin E-51. The monomer is acrylic acid. The photoinitiator is photoinitiator 6992. The thickener is xanthan gum. The epoxy resin, the monomer and the photoinitiator are cured under the condition of illumination. The viscosity of the epoxy resin, the monomer and the initiator after mixing is low, the epoxy resin, the monomer and the initiator are easy to flow when being packaged in the bonding packaging sheet and the curing packaging sheet, and the viscosity of the epoxy resin is increased and is sticky after the thickening agent is added, so that the epoxy resin is difficult to flow after being packaged. The photo-curable material was viscous paste before curing, and the hardness after curing was 3H.

A three-dimensional latticed framework 4 for preventing the light curing material from moving randomly is arranged between the bonding packaging sheet 31 and the curing packaging sheet 32, and the three-dimensional latticed framework 4 is filled between the bonding packaging sheet and the curing packaging sheet in a saturated mode. The mixture of the viscous epoxy resin, the monomer, the initiator and the thickening agent is filled in the three-dimensional latticed framework, the fluidity of the mixture is further limited, so that the whole photocuring material is uniformly distributed, and a uniform hard structure is formed after curing.

The curing and encapsulating sheet 32 is made of a transparent material which can allow light to pass through, and is made of a PVC material. And the bonding packaging sheet is in sealing bonding with the curing packaging sheet so as to seal and package the light curing material.

The outer cladding of solidification encapsulation piece 32 has the membrane 5 that hinders that is used for preventing light irradiation to photocuring material, and it is black PVC tectorial membrane to hinder the membrane, hinders the membrane and can prevent the photocuring material solidification in the solidification encapsulation piece, and the back is detached to hindering the membrane, and photocuring material just can solidify.

According to the magnetic soft mirror, the light-blocking film tissue light shines into the transparent curing packaging sheet in the transportation process, the light-blocking film is torn off when the magnetic soft mirror is used, the light-blocking film can be cured by using a portable ultraviolet lamp, and the light-blocking film becomes a hard material after being cured, so that the magnetic soft mirror has a supporting effect.

The thickness of the bonding packaging sheet is 0.3mm, and the thickness of the curing packaging sheet is 0.3 mm.

The thickness of the light-cured material filled between the bonding packaging sheet and the curing packaging sheet is 3 mm.

The thickness of the magnetic absorption layer is 1 mm.

The manufacturing process of the magnetic soft mirror comprises the following steps:

1) and (3) bonding and connecting the high-brightness VMPET aluminized polyester film of the mirror layer with the magnetic rubber of the magnetic absorption layer to obtain the magnetic soft mirror body.

2) The curing packaging sheet is provided with two opposite surfaces of an A surface and a B surface, and the light-blocking film, namely the black PVC coating film is coated on the A surface of the curing packaging sheet through a coating machine to obtain the coated curing packaging sheet.

3) Uniformly mixing the epoxy resin, the monomer, the initiator and the thickening agent according to the formula ratio to obtain a viscous pasty photocuring material, and coating the viscous pasty photocuring material on the surface B of the cured packaging sheet, wherein the surface B of the cured packaging sheet is rough, so that the photocuring material can be conveniently adhered to and cured on the surface of the packaging sheet after being cured. The three-dimensional latticed framework is pressed on the light-cured material, is composed of a plurality of filaments, is soft but has strength, and can be pressed into the viscous pasty light-cured material for supporting. The bonding packaging sheet is provided with two opposite surfaces of a surface C and a surface D, the surface C of the bonding packaging sheet is rough, and the surface C of the bonding packaging sheet faces the light curing material covered on the curing packaging sheet and is adhered on the light curing material. The periphery of the adhesive encapsulating sheet and the cured encapsulating sheet is then bonded using a black sealing tape to encapsulate the light-curable material between the adhesive encapsulating sheet and the cured encapsulating sheet.

4) And (3) bonding and connecting one surface of the magnetic layer of the magnetic soft mirror body with the bonding packaging sheet to obtain the magnetic soft mirror.

Example 2

The soft mirror of magnetism of this embodiment, including mirror layer, magnetism inhale layer and cured layer, mirror layer and magnetism inhale layer adhesive bonding, magnetism inhale layer and cured layer adhesive bonding.

The mirror layer is a layer of high-brightness VMPET aluminized polyester film, and the high-brightness VMPET aluminized polyester film has a mirror effect.

The magnetic absorption layer is a layer of magnetic rubber, and the magnetic rubber is purchased from the market.

The solidified layer comprises an adhesive packaging sheet close to the magnetic absorption layer and a solidified packaging sheet opposite to the adhesive packaging sheet, and a light-cured material is filled between the adhesive packaging sheet and the solidified packaging sheet.

The photocuring material comprises the following components in parts by mass: 100 parts of epoxy resin, 5 parts of monomer, 0.8 part of photoinitiator and 0.1 part of thickener. The epoxy resin is bisphenol A type epoxy resin E-51. The monomer is acrylic acid. The photoinitiator is photoinitiator 6992. The thickener is xanthan gum. The epoxy resin, the monomer and the photoinitiator are cured under the condition of illumination. The viscosity of the epoxy resin, the monomer and the initiator after mixing is low, the epoxy resin, the monomer and the initiator are easy to flow when being packaged in the bonding packaging sheet and the curing packaging sheet, and the viscosity of the epoxy resin is increased and is sticky after the thickening agent is added, so that the epoxy resin is difficult to flow after being packaged. The photo-curable material was viscous paste before curing, and the hardness after curing was 3H.

The curing packaging sheet is made of transparent materials which can enable light to penetrate through, and is made of PVC materials. And the bonding packaging sheet is in sealing bonding with the curing packaging sheet so as to seal and package the light curing material.

A three-dimensional latticed framework for preventing the light curing material from moving randomly is arranged between the bonding packaging sheet and the curing packaging sheet, and the three-dimensional latticed framework is filled between the bonding packaging sheet and the curing packaging sheet in a saturated mode. The mixture of the viscous epoxy resin, the monomer, the initiator and the thickening agent is filled in the three-dimensional latticed framework, the fluidity of the mixture is further limited, so that the whole photocuring material is uniformly distributed, and a uniform hard structure is formed after curing.

The outer cladding of solidification encapsulation piece has the membrane of hindering light that is used for preventing that light from shining to photocuring material, hinders the membrane for black PVC tectorial membrane, hinders the membrane and can prevent the photocuring material solidification in the solidification encapsulation piece, will hinder the membrane and detach the back, photocuring material just can solidify.

The thickness of the bonding packaging sheet is 0.5mm, and the thickness of the curing packaging sheet is 0.5 mm.

The thickness of the light-cured material filled between the bonding packaging sheet and the curing packaging sheet is 2.5 mm.

The thickness of the magnetic absorption layer is 1.2 mm.

The manufacturing process of the magnetic soft mirror comprises the following steps:

1) and (3) bonding and connecting the high-brightness VMPET aluminized polyester film of the mirror layer with the magnetic rubber of the magnetic absorption layer to obtain the magnetic soft mirror body.

2) The curing packaging sheet is provided with two opposite surfaces of an A surface and a B surface, and the light-blocking film, namely the black PVC coating film is coated on the A surface of the curing packaging sheet through a coating machine to obtain the coated curing packaging sheet.

3) Uniformly mixing the epoxy resin, the monomer, the initiator and the thickening agent according to the formula ratio to obtain a viscous pasty photocuring material, and coating the viscous pasty photocuring material on the surface B of the cured packaging sheet, wherein the surface B of the cured packaging sheet is rough, so that the photocuring material can be conveniently adhered to and cured on the surface of the packaging sheet after being cured. The three-dimensional latticed framework is pressed on the light-cured material, is composed of a plurality of filaments, is soft but has strength, and can be pressed into the viscous pasty light-cured material for supporting. The bonding packaging sheet is provided with two opposite surfaces of a surface C and a surface D, the surface C of the bonding packaging sheet is rough, and the surface C of the bonding packaging sheet faces the light curing material covered on the curing packaging sheet and is adhered on the light curing material. The periphery of the adhesive encapsulating sheet and the cured encapsulating sheet is then bonded using a black sealing tape to encapsulate the light-curable material between the adhesive encapsulating sheet and the cured encapsulating sheet.

4) And (3) bonding and connecting one surface of the magnetic layer of the magnetic soft mirror body with the bonding packaging sheet to obtain the magnetic soft mirror.

Example 3

The soft mirror of magnetism of this embodiment, including mirror layer, magnetism inhale layer and cured layer, mirror layer and magnetism inhale layer adhesive bonding, magnetism inhale layer and cured layer adhesive bonding.

The mirror layer is a layer of high-brightness VMPET aluminized polyester film, and the high-brightness VMPET aluminized polyester film has a mirror effect.

The magnetic absorption layer is a layer of magnetic rubber, and the magnetic rubber is purchased from the market.

The solidified layer comprises an adhesive packaging sheet close to the magnetic absorption layer and a solidified packaging sheet opposite to the adhesive packaging sheet, and a light-cured material is filled between the adhesive packaging sheet and the solidified packaging sheet.

The photocuring material comprises the following components in parts by mass: 100 parts of epoxy resin, 4 parts of monomer, 1.2 parts of photoinitiator and 0.2 part of thickener. The epoxy resin is bisphenol A epoxy resin E-44. The monomer is acrylic acid. The photoinitiator is photoinitiator 1173. The thickening agent is polyoxyethylene. The epoxy resin, the monomer and the photoinitiator are cured under the condition of illumination. The viscosity of the epoxy resin, the monomer and the initiator after mixing is low, the epoxy resin, the monomer and the initiator are easy to flow when being packaged in the bonding packaging sheet and the curing packaging sheet, and the viscosity of the epoxy resin is increased and is sticky after the thickening agent is added, so that the epoxy resin is difficult to flow after being packaged. The photo-curable material was viscous paste before curing, and the hardness after curing was 3H.

A three-dimensional latticed framework for preventing the light curing material from moving randomly is arranged between the bonding packaging sheet and the curing packaging sheet, and the three-dimensional latticed framework is filled between the bonding packaging sheet and the curing packaging sheet in a saturated mode. The mixture of the viscous epoxy resin, the monomer, the initiator and the thickening agent is filled in the three-dimensional latticed framework, the fluidity of the mixture is further limited, so that the whole photocuring material is uniformly distributed, and a uniform hard structure is formed after curing.

The curing packaging sheet is made of transparent materials which can enable light to penetrate through, and is made of PVC materials. And the bonding packaging sheet is in sealing bonding with the curing packaging sheet so as to seal and package the light curing material.

The outer cladding of solidification encapsulation piece has the membrane of hindering light that is used for preventing that light from shining to photocuring material, hinders the membrane for black PVC tectorial membrane, hinders the membrane and can prevent the photocuring material solidification in the solidification encapsulation piece, will hinder the membrane and detach the back, photocuring material just can solidify.

The thickness of the bonding packaging sheet is 0.5mm, and the thickness of the curing packaging sheet is 0.5 mm.

The thickness of the light-cured material filled between the bonding packaging sheet and the curing packaging sheet is 2.8 mm.

The thickness of the magnetic absorption layer is 0.8 mm.

The manufacturing process of the magnetic soft mirror comprises the following steps:

1) and (3) bonding and connecting the high-brightness VMPET aluminized polyester film of the mirror layer with the magnetic rubber of the magnetic absorption layer to obtain the magnetic soft mirror body.

2) The curing packaging sheet is provided with two opposite surfaces of an A surface and a B surface, and the light-blocking film, namely the black PVC coating film is coated on the A surface of the curing packaging sheet through a coating machine to obtain the coated curing packaging sheet.

3) Uniformly mixing the epoxy resin, the monomer, the initiator and the thickening agent according to the formula ratio to obtain a viscous pasty photocuring material, and coating the viscous pasty photocuring material on the surface B of the cured packaging sheet, wherein the surface B of the cured packaging sheet is rough, so that the photocuring material can be conveniently adhered to and cured on the surface of the packaging sheet after being cured. The three-dimensional latticed framework is pressed on the light-cured material, is composed of a plurality of filaments, is soft but has strength, and can be pressed into the viscous pasty light-cured material for supporting. The bonding packaging sheet is provided with two opposite surfaces of a surface C and a surface D, the surface C of the bonding packaging sheet is rough, and the surface C of the bonding packaging sheet faces the light curing material covered on the curing packaging sheet and is adhered on the light curing material. The periphery of the adhesive encapsulating sheet and the cured encapsulating sheet is then bonded using a black sealing tape to encapsulate the light-curable material between the adhesive encapsulating sheet and the cured encapsulating sheet.

4) And (3) bonding and connecting one surface of the magnetic layer of the magnetic soft mirror body with the bonding packaging sheet to obtain the magnetic soft mirror.

Example 4

The soft mirror of magnetism of this embodiment, including mirror layer, magnetism inhale layer and cured layer, mirror layer and magnetism inhale layer adhesive bonding, magnetism inhale layer and cured layer adhesive bonding.

The mirror layer is a layer of high-brightness VMPET aluminized polyester film, and the high-brightness VMPET aluminized polyester film has a mirror effect.

The magnetic absorption layer is a layer of magnetic rubber, and the magnetic rubber is purchased from the market.

The solidified layer comprises an adhesive packaging sheet close to the magnetic absorption layer and a solidified packaging sheet opposite to the adhesive packaging sheet, and a light-cured material is filled between the adhesive packaging sheet and the solidified packaging sheet.

The photocuring material comprises the following components in parts by mass: 100 parts of epoxy resin, 4 parts of monomer, 1 part of photoinitiator and 0.1 part of thickener. The epoxy resin is bisphenol A epoxy resin E-44. The monomer is acrylic acid. The photoinitiator is photoinitiator 6992. The thickener is xanthan gum. The epoxy resin, the monomer and the photoinitiator are cured under the condition of illumination. The viscosity of the epoxy resin, the monomer and the initiator after mixing is low, the epoxy resin, the monomer and the initiator are easy to flow when being packaged in the bonding packaging sheet and the curing packaging sheet, and the viscosity of the epoxy resin is increased and is sticky after the thickening agent is added, so that the epoxy resin is difficult to flow after being packaged. The photo-curable material was viscous paste before curing, and the hardness after curing was 3H.

The curing packaging sheet is made of transparent materials which can enable light to penetrate through, and is made of PVC materials. And the bonding packaging sheet is in sealing bonding with the curing packaging sheet so as to seal and package the light curing material.

A three-dimensional latticed framework for preventing the light curing material from moving randomly is arranged between the bonding packaging sheet and the curing packaging sheet, and the three-dimensional latticed framework is filled between the bonding packaging sheet and the curing packaging sheet in a saturated mode. The mixture of the viscous epoxy resin, the monomer, the initiator and the thickening agent is filled in the three-dimensional latticed framework, the fluidity of the mixture is further limited, so that the whole photocuring material is uniformly distributed, and a uniform hard structure is formed after curing.

The outer cladding of solidification encapsulation piece has the membrane of hindering light that is used for preventing that light from shining to photocuring material, hinders the membrane for black PVC tectorial membrane, hinders the membrane and can prevent the photocuring material solidification in the solidification encapsulation piece, will hinder the membrane and detach the back, photocuring material just can solidify.

The thickness of the bonding packaging sheet is 0.4mm, and the thickness of the curing packaging sheet is 0.4 mm.

The thickness of the light-cured material filled between the bonding packaging sheet and the curing packaging sheet is 3.5 mm.

The thickness of the magnetic absorption layer is 0.9 mm.

The manufacturing process of the magnetic soft mirror comprises the following steps:

1) and (3) bonding and connecting the high-brightness VMPET aluminized polyester film of the mirror layer with the magnetic rubber of the magnetic absorption layer to obtain the magnetic soft mirror body.

2) The curing packaging sheet is provided with two opposite surfaces of an A surface and a B surface, and the light-blocking film, namely the black PVC coating film is coated on the A surface of the curing packaging sheet through a coating machine to obtain the coated curing packaging sheet.

3) Uniformly mixing the epoxy resin, the monomer, the initiator and the thickening agent according to the formula ratio to obtain a viscous pasty photocuring material, and coating the viscous pasty photocuring material on the surface B of the cured packaging sheet, wherein the surface B of the cured packaging sheet is rough, so that the photocuring material can be conveniently adhered to and cured on the surface of the packaging sheet after being cured. The three-dimensional latticed framework is pressed on the light-cured material, is composed of a plurality of filaments, is soft but has strength, and can be pressed into the viscous pasty light-cured material for supporting. The bonding packaging sheet is provided with two opposite surfaces of a surface C and a surface D, the surface C of the bonding packaging sheet is rough, and the surface C of the bonding packaging sheet faces the light curing material covered on the curing packaging sheet and is adhered on the light curing material. The periphery of the adhesive encapsulating sheet and the cured encapsulating sheet is then bonded using a black sealing tape to encapsulate the light-curable material between the adhesive encapsulating sheet and the cured encapsulating sheet.

4) And (3) bonding and connecting one surface of the magnetic layer of the magnetic soft mirror body with the bonding packaging sheet to obtain the magnetic soft mirror.

Example 5

The soft mirror of magnetism of this embodiment, including mirror layer, magnetism inhale layer and cured layer, mirror layer and magnetism inhale layer adhesive bonding, magnetism inhale layer and cured layer adhesive bonding.

The mirror layer is a layer of high-brightness VMPET aluminized polyester film, and the high-brightness VMPET aluminized polyester film has a mirror effect.

The magnetic absorption layer is a layer of magnetic rubber, and the magnetic rubber is purchased from the market.

The solidified layer comprises an adhesive packaging sheet close to the magnetic absorption layer and a solidified packaging sheet opposite to the adhesive packaging sheet, and a light-cured material is filled between the adhesive packaging sheet and the solidified packaging sheet.

The photocuring material comprises the following components in parts by mass: 100 parts of epoxy resin, 3 parts of monomer, 0.7 part of photoinitiator and 0.2 part of thickener. The epoxy resin is bisphenol A type epoxy resin E-51. The monomer is acrylic acid. The photoinitiator is photoinitiator 1173. The thickening agent is polyoxyethylene. The epoxy resin, the monomer and the photoinitiator are cured under the condition of illumination. The viscosity of the epoxy resin, the monomer and the initiator after mixing is low, the epoxy resin, the monomer and the initiator are easy to flow when being packaged in the bonding packaging sheet and the curing packaging sheet, and the viscosity of the epoxy resin is increased and is sticky after the thickening agent is added, so that the epoxy resin is difficult to flow after being packaged. The photo-curable material was viscous paste before curing, and the hardness after curing was 4H.

The curing packaging sheet is made of transparent materials which can enable light to penetrate through, and is made of PVC materials. And the bonding packaging sheet is in sealing bonding with the curing packaging sheet so as to seal and package the light curing material.

A three-dimensional latticed framework for preventing the light curing material from moving randomly is arranged between the bonding packaging sheet and the curing packaging sheet, and the three-dimensional latticed framework is filled between the bonding packaging sheet and the curing packaging sheet in a saturated mode. The mixture of the viscous epoxy resin, the monomer, the initiator and the thickening agent is filled in the three-dimensional latticed framework, the fluidity of the mixture is further limited, so that the whole photocuring material is uniformly distributed, and a uniform hard structure is formed after curing.

The outer cladding of solidification encapsulation piece has the membrane of hindering light that is used for preventing that light from shining to photocuring material, hinders the membrane for black PVC tectorial membrane, hinders the membrane and can prevent the photocuring material solidification in the solidification encapsulation piece, will hinder the membrane and detach the back, photocuring material just can solidify.

The thickness of the bonding packaging sheet is 0.3mm, and the thickness of the curing packaging sheet is 0.3 mm.

The thickness of the light-cured material filled between the bonding packaging sheet and the curing packaging sheet is 3.2 mm.

The thickness of the magnetic absorption layer is 1.1 mm.

The manufacturing process of the magnetic soft mirror comprises the following steps:

1) and (3) bonding and connecting the high-brightness VMPET aluminized polyester film of the mirror layer with the magnetic rubber of the magnetic absorption layer to obtain the magnetic soft mirror body.

2) The curing packaging sheet is provided with two opposite surfaces of an A surface and a B surface, and the light-blocking film, namely the black PVC coating film is coated on the A surface of the curing packaging sheet through a coating machine to obtain the coated curing packaging sheet.

3) Uniformly mixing the epoxy resin, the monomer, the initiator and the thickening agent according to the formula ratio to obtain a viscous pasty photocuring material, and coating the viscous pasty photocuring material on the surface B of the cured packaging sheet, wherein the surface B of the cured packaging sheet is rough, so that the photocuring material can be conveniently adhered to and cured on the surface of the packaging sheet after being cured. The three-dimensional latticed framework is pressed on the light-cured material, is composed of a plurality of filaments, is soft but has strength, and can be pressed into the viscous pasty light-cured material for supporting. The bonding packaging sheet is provided with two opposite surfaces of a surface C and a surface D, the surface C of the bonding packaging sheet is rough, and the surface C of the bonding packaging sheet faces the light curing material covered on the curing packaging sheet and is adhered on the light curing material. The periphery of the adhesive encapsulating sheet and the cured encapsulating sheet is then bonded using a black sealing tape to encapsulate the light-curable material between the adhesive encapsulating sheet and the cured encapsulating sheet.

4) And (3) bonding and connecting one surface of the magnetic layer of the magnetic soft mirror body with the bonding packaging sheet to obtain the magnetic soft mirror.

Comparative example 1

The magnetic soft mirror of this comparative example was substantially the same as example 1 except that no three-dimensional lattice-like skeleton was provided between the cured encapsulating sheet and the bonded encapsulating sheet. The soft magnetic mirror of comparative example 1 is liable to have uneven distribution of the photo-curable material after being rolled up, resulting in uneven thickness after curing and the possibility of mirror image of a half-mirror.

Comparative example 2

The magnetic soft mirror of this comparative example was substantially the same as example 1 except that no thickener was included in the photocurable material. In the magnetic soft mirror of comparative example 2, the viscosity of the photo-curing material is low, and the curing encapsulating sheet and the bonding encapsulating sheet are soft, so that the curing encapsulating sheet and the bonding encapsulating sheet can flow back and forth, and the situation that the photo-curing material is unevenly distributed is likely to occur after the magnetic soft mirror is rolled up, so that the thickness is uneven after curing, and a mirror image of a distorting mirror may occur.

Comparative example 3

The magnetic soft mirror of this comparative example is substantially the same as example 1 except that only a mirror layer and a magnetically attracting layer are included. When the magnetic soft lens of the comparison example is adsorbed on a flat iron plane, the mirror surface mirror image can not generate the distorting mirror phenomenon. When the magnetic soft mirror is adsorbed on an uneven iron plane, the mirror surface mirror image has a distorting mirror phenomenon.

Comparative example 4

The magnetic soft mirror of this comparative example was substantially the same as example 1 except that only the mirror layer and the cured layer were contained. The magnetic soft mirror of comparative example 4 was not magnetic and could not be adsorbed on an iron plane.