阅读说明：本技术 烯烃-烯烃醇共聚物及其制备方法 (Olefin-olefin alcohol copolymer and method for producing the same ) 是由 高榕 郭子芳 赖菁菁 李昕阳 张军辉 刘东兵 顾元宁 周俊领 安京燕 于 2019-10-31 设计创作，主要内容包括：本发明涉及一种烯烃-烯烃醇共聚物及其制备方法。该烯烃-烯烃醇共聚物的制备方法中使用的催化剂包括式I所示的二亚胺金属配合物。通过本发明的制备方法的优选实施方式可以获得球形和/或类球形聚合物,在工业应用中具有良好的前景。(The invention relates to an olefin-olefin alcohol copolymer and a preparation method thereof. The catalyst used in the preparation method of the olefin-olefin alcohol copolymer comprises a diimine metal complex shown in a formula I. Spherical and/or spheroidal polymers can be obtained by preferred embodiments of the preparation process of the invention, with good prospects in industrial applications.)

1. A process for preparing an olefin-olefin alcohol copolymer comprising polymerizing an olefin and an olefin alcohol in the presence of a catalyst and optionally a chain transfer agent to produce the olefin-olefin alcohol copolymer,

wherein the catalyst comprises a main catalyst and an optional cocatalyst, and the main catalyst comprises a diimine metal complex shown as a formula I:

in the formula I, R₁And R₂The same or different, independently selected from C1-C30 hydrocarbyl containing or not containing substituent; r₃And R₄The same or different, each independently selected from hydrogen, halogen, hydroxyl, C1-C20 alkyl with or without substituent; r₃-R₄Optionally forming a ring with each other; r₁₁Selected from C1-C20 substituted or unsubstituted hydrocarbon groups; y is selected from non-metal atoms of group VIA; m is a group VIII metal; x is selected from halogen, C1-C10 alkyl with or without substituent and C1-C10 alkoxy with or without substituent.

2. The method of claim 1, wherein R is₁And R₂Selected from substituted or unsubstituted C1-C20 alkyl and or substituted or unsubstituted C6-C20 aryl, preferably R₁And/or R₂Is a group of formula A:

in the formula A, R¹-R⁵The substituents are the same or different, and are respectively and independently selected from hydrogen, halogen, hydroxyl, C1-C20 alkyl with or without substituent, C2-C20 alkenyl with or without substituent, C2-C20 alkynyl with or without substituent, C3-C20 cycloalkyl with or without substituent, C1-C20 alkoxy with or without substituent, and C1-C20 alkyl with or without substituentOptionally substituted C2-C20 alkenyloxy, optionally substituted C2-C20 alkynyloxy, optionally substituted C3-C20 cycloalkoxy, optionally substituted C6-C20 aryl, optionally substituted C7-C20 aralkyl, and optionally substituted C7-C20 alkaryl; r¹-R⁵Optionally forming a ring with each other;

preferably, in formula A, R¹-R⁵The aryl group is the same or different and is independently selected from hydrogen, halogen, hydroxyl, C1-C10 alkyl with or without substituent, C2-C10 alkenyl with or without substituent, C2-C10 alkynyl with or without substituent, C3-C10 cycloalkyl with or without substituent, C1-C10 alkoxy with or without substituent, C2-C10 alkenyloxy with or without substituent, C2-C10 alkynyloxy with or without substituent, C3-C10 cycloalkoxy with or without substituent, C6-C15 aryl with or without substituent, C7-C15 aralkyl with or without substituent and C7-C15 alkaryl with or without substituent;

m is selected from nickel and palladium; y is selected from O and S; x is selected from halogen, C1-C10 alkyl with or without substituent and C1-C10 alkoxy with or without substituent, preferably selected from halogen, C1-C6 alkyl with or without substituent and C1-C6 alkoxy with or without substituent; r₁₁Is selected from C1-C20 alkyl with or without substituent, preferably C1-C10 alkyl with or without substituent, more preferably C1-C6 alkyl with or without substituent.

3. The method of claim 1 or 2, wherein R is₃And R₄The substituents are the same or different, and are respectively and independently selected from hydrogen, halogen, hydroxyl, C1-C20 alkyl with or without substituent, C2-C20 alkenyl with or without substituent, C2-C20 alkynyl with or without substituent, C3-C20 cycloalkyl with or without substituent, C1-C20 alkoxy with or without substituent, C2-C2 with or without substituent0 alkenyloxy group, substituted or unsubstituted C2-C20 alkynyloxy group, substituted or unsubstituted C3-C20 cycloalkoxy group, substituted or unsubstituted C6-C20 aryl group, substituted or unsubstituted C7-C20 aralkyl group, and substituted or unsubstituted C7-C20 alkaryl group.

4. The method of any one of claims 1-3, wherein R is₃And R₄The aryl group is the same or different and is independently selected from hydrogen, halogen, hydroxyl, C1-C10 alkyl with or without substituent, C2-C10 alkenyl with or without substituent, C2-C10 alkynyl with or without substituent, C3-C10 cycloalkyl with or without substituent, C1-C10 alkoxy with or without substituent, C2-C10 alkenyloxy with or without substituent, C2-C10 alkynyloxy with or without substituent, C3-C10 cycloalkoxy with or without substituent, C6-C15 aryl with or without substituent, C7-C15 aralkyl with or without substituent and C7-C15 alkaryl with or without substituent;

preferably, R₃And R₄Each independently selected from hydrogen, C1-C10 alkyl, halogenated C1-C10 alkyl, C1-C10 alkoxy, halogenated C1-C10 alkoxy and halogen, more preferably from hydrogen, C1-C6 alkyl, halogenated C1-C6 alkyl, C1-C6 alkoxy, halogenated C1-C6 alkoxy and halogen.

5. A process according to any one of claims 1 to 4, characterised in that the substituents are selected from halogen, hydroxy, C1-C10 alkyl, halogenated C1-C10 alkyl, C1-C10 alkoxy and halogenated C1-C10 alkoxy; the substituents are preferably selected from halogen, hydroxy, C1-C6 alkyl, halogenated C1-C6 alkyl, C1-C6 alkoxy and halogenated C1-C6 alkoxy;

preferably, the C1-C6 alkyl group is selected from methyl, ethyl, n-propyl, isopropyl, n-butyl and isobutyl, n-pentyl, isopentyl, n-hexyl, isohexyl, and 3, 3-dimethylbutyl;

preferably, the C1-C6 alkoxy group is selected from methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy and isobutoxy, n-pentoxy, isopentoxy, n-hexoxy, isohexoxy and 3, 3-dimethylbutoxy,

preferably, the halogen is selected from fluorine, chlorine, bromine and iodine.

6. A process according to any one of claims 1 to 5, wherein the diimine metal complex is of formula III:

in the formula III, R¹-R⁵The substituents are the same or different, and are respectively and independently selected from hydrogen, halogen, hydroxyl, C1-C10 alkyl with or without substituent, C3-C10 cycloalkyl with or without substituent, C1-C10 alkoxy with or without substituent, C3-C10 cycloalkoxy with or without substituent, C6-C15 aryl with or without substituent, C7-C15 aralkyl with or without substituent and C7-C15 alkaryl with or without substituent;

R₃and R₄Each independently selected from hydrogen, C1-C10 alkyl, halogenated C1-C10 alkyl, C1-C10 alkoxy, halogenated C1-C10 alkoxy and halogen, more preferably from hydrogen, C1-C6 alkyl, halogenated C1-C6 alkyl, C1-C6 alkoxy, halogenated C1-C6 alkoxy and halogen;

m is nickel;

y is O;

x is selected from fluorine, chlorine and bromine;

R₁₁is selected from C1-C20 alkyl with or without substituent, preferably C1-C10 alkyl with or without substituent, more preferably C1-C6 alkyl with or without substituent;

the substituent is selected from halogen, hydroxyl, C1-C6 alkyl, halogenated C1-C6 alkyl, C1-C6 alkoxy and halogenated C1-C6 alkoxy.

7. The process according to any one of claims 1 to 6, wherein the olefin comprises an olefin having 2 to 16 carbon atoms, preferably the olefin comprises ethylene or an alpha-olefin having 3 to 16 carbon atoms, and/or the olefinic alcohol is selected from one or more olefinic alcohols of formula G:

in the formula G, L₁-L₃Each independently selected from H and C with or without substituent₁-C₃₀Alkyl radical, L₄Is C having a pendant group₁-C₃₀An alkylene group;

preferably, the copolymer has a content of structural units derived from the olefin alcohol represented by the formula G of 0.4 to 10.0 mol%;

preferably, L₁And L₂Is H, L₃Is H or C₁-C₃₀Alkyl radical, L₄Is C having a pendant group₁-C₃₀An alkylene group;

more preferably, L₁And L₂Is H, L₃Is H or C₁-C₂₀Alkyl radical, L₄Is C having a pendant group₁-C₂₀An alkylene group;

still more preferably, L₁And L₂Is H, L₃Is H or C₁-C₁₀Alkyl radical, L₄Is C having a pendant group₁-C₁₀An alkylene group;

further preferably, L₁And L₂Is H, L₃Is H or C₁-C₁₀Alkyl radical, L₄Is C having a pendant group₁-C₆An alkylene group.

8. The method of claim 7, wherein L is₁-L₃Wherein said substituents are selected from halogen, C₁-C₁₀Alkyl radical, C₁-C₁₀Alkoxy radical, C₆-C₁₀In aryl, cyano and hydroxy groupsOne or more of (a); more preferably L₁-L₃Wherein the substituent is selected from one or more of C1-C6 alkyl, halogen and C1-C6 alkoxy;

the side group in L4 is selected from halogen and C₆-C₂₀Aryl radical, C₁-C₂₀Alkyl and C₁-C₂₀One or more of alkoxy, said C₆-C₂₀Aryl radical, C₁-C₂₀Alkyl and C₁-C₂₀Alkoxy is optionally substituted by a substituent, preferably selected from halogen, C₁-C₁₀Alkyl radical, C₁-C₁₀Alkoxy radical, C₆-C₁₀One or more of aryl and hydroxyl.

9. The process of any one of claims 1 to 8, wherein the cocatalyst is selected from organoaluminum compounds and/or organoboron compounds; the organic aluminum compound is selected from one or more of alkyl aluminoxane, alkyl aluminum and alkyl aluminum halide; the organoboron compound is selected from an aryl boron and/or a borate; the chain transfer agent is selected from one or more of alkyl aluminum, alkyl magnesium and alkyl zinc;

preferably, when the cocatalyst is an organoaluminum compound, the molar ratio of aluminum in the cocatalyst to M in the diimine metal complex is (10-10)⁷):1, preferably (10-100000) 1, more preferably (100-; when the cocatalyst is an organic boron compound, the molar ratio of boron in the cocatalyst to M in the diimine metal complex is (0.1-1000):1, preferably (0.1-500): 1; the molar ratio of the chain transfer agent to M in the diimine metal complex is (0.1-5000):1, preferably (1.0-1000): 1.

10. Process according to any one of claims 1 to 9, characterized in that the polymerization is carried out in an alkane solvent, preferably selected from C₃-C₂₀One or more alkanes, preferably selected from C₃-C₁₀Alkanes, more preferably selected from butane, isobutane, pentane, hexane, heptaneOne or more of an alkane, octane, and cyclohexane.

11. Olefin-olefin alcohol copolymer prepared according to the process of any one of claims 1-10, which is spherical and/or spheroidal, and/or which has a particle size of 0.1-50 mm.

12. Use of an olefin-olefin alcohol copolymer prepared according to the process of any one of claims 1 to 10 or of the olefin-olefin alcohol copolymer of claim 11 as a polyolefin material.

Technical Field

The invention belongs to the field of preparation of high molecular polymers, and particularly relates to an olefin-olefin alcohol copolymer and a preparation method thereof.

Background

The polyolefin product has low price, excellent performance and wide application range. Under the condition of keeping the original excellent physical and chemical properties of the polyolefin, polar groups are introduced into polyolefin molecular chains by a chemical synthesis method, so that the chemical inertness, the printing property, the wettability and the compatibility with other materials can be improved, and new characteristics which are not possessed by raw materials are endowed. High pressure free radical polymerization is currently used commercially to promote direct copolymerization of olefins with polar monomers, such as ethylene-vinyl acetate, ethylene-methyl methacrylate, and ethylene-acrylic acid copolymers. Although the polar comonomer can be directly introduced into the polyolefin chain by high-pressure radical copolymerization, the method requires high-temperature and high-pressure conditions, and is high in energy consumption and expensive in equipment cost.

Ethylene-vinyl alcohol (EVOH or EVAL) copolymer is a novel high molecular material integrating the processability of ethylene polymer and the gas barrier property of vinyl alcohol polymer, is one of three barrier resins industrially produced in the world at present, and is widely used for packaging food, medical solution and other products. Since vinyl alcohol cannot exist independently in the form of monomer, it is usually prepared by alcoholysis of ethylene-vinyl acetate copolymer by radical polymerization, but the alcoholysis process requires the use of a large amount of solvent, and the final saponification product contains a large amount of impurities such as acetic acid and alkali metal salt, and requires a large amount of water for washing.

As a preparation technology of polymers at normal temperature and normal pressure, coordination catalytic copolymerization has attracted extensive attention due to its remarkable effects in reducing energy consumption, improving reaction efficiency and the like. The catalyst participates in the reaction process, so that the activation energy of the copolymerization reaction of the olefin monomer and the polar monomer is greatly reduced, and the functional polymer with higher molecular weight can be obtained at lower temperature and pressure. Currently, only a few documents report the use of transition metal complexes to catalyze the copolymerization of olefins and unsaturated alcohols. However, in the prior art, the polymer obtained by any method is a viscous massive solid, so that the polymer is easily scaled in polymerization equipment, and the transportation, solvent removal, granulation and the like of the polymer are difficult.

Disclosure of Invention

It is an object of the present invention to overcome the disadvantages of the prior art and to provide a novel process for preparing olefin-olefin alcohol copolymers. Furthermore, the spherical and/or spheroidal polymer can be directly obtained by the method, the polymer has good appearance and good industrial application prospect.

In a first aspect, the present invention provides a process for the preparation of an olefin-olefin alcohol copolymer comprising polymerising an olefin and an olefin alcohol in the presence of a catalyst and optionally a chain transfer agent to produce the olefin-olefin alcohol copolymer,

wherein the catalyst comprises a main catalyst and an optional cocatalyst, and the main catalyst comprises a diimine metal complex shown as a formula I:

in the formula I, R₁And R₂The same or different, independently selected from C1-C30 hydrocarbyl containing or not containing substituent; r₃And R₄The same or different, each independently selected from hydrogen, halogen, hydroxyl, C1-C with or without substituent20 hydrocarbyl groups; r₃-R₄Optionally forming a ring with each other; r₁₁Selected from C1-C20 substituted or unsubstituted hydrocarbon groups; y is selected from non-metal atoms of group VIA; m is a group VIII metal; x is selected from halogen, C1-C10 alkyl with or without substituent and C1-C10 alkoxy with or without substituent.

According to some embodiments of the diimine metal complexes of this invention, R₁And R₂Is selected from C1-C20 alkyl with or without substituent and/or C6-C20 aryl with or without substituent.

According to some embodiments of the diimine metal complexes of this invention, R₁And/or R₂Is a group of formula A:

in the formula A, R¹-R⁵The aryl group is the same or different and is independently selected from hydrogen, halogen, hydroxyl, C1-C20 alkyl with or without substituent, C2-C20 alkenyl with or without substituent, C2-C20 alkynyl with or without substituent, C3-C20 cycloalkyl with or without substituent, C1-C20 alkoxy with or without substituent, C2-C20 alkenyloxy with or without substituent, C2-C20 alkynyloxy with or without substituent, C3-C20 cycloalkoxy with or without substituent, C6-C20 aryl with or without substituent, C7-C20 aralkyl with or without substituent and C7-C20 alkaryl with or without substituent; r¹-R⁵Optionally forming a ring with each other.

According to some embodiments of the diimine metal complexes of this invention, in formula A, R¹-R⁵The substituents are the same or different, and are respectively and independently selected from hydrogen, halogen, hydroxyl, C1-C10 alkyl with or without substituent, C2-C10 alkenyl with or without substituent, C2-C10 alkynyl with or without substituent, C3-C10 cycloalkyl with or without substituent, and C3-C10 cycloalkyl with or without substituentC1-C10 alkoxy, substituted or unsubstituted C2-C10 alkenyloxy, substituted or unsubstituted C2-C10 alkynyloxy, substituted or unsubstituted C3-C10 cycloalkoxy, substituted or unsubstituted C6-C15 aryl, substituted or unsubstituted C7-C15 aralkyl, and substituted or unsubstituted C7-C15 alkaryl.

According to some embodiments of the diimine metal complexes of this invention, M is selected from nickel and palladium.

According to some embodiments of the diimine metal complexes of this invention, Y is selected from O and S.

According to some embodiments of the diimine metal complexes of this invention, X is selected from the group consisting of halogen, substituted or unsubstituted C1-C10 alkyl, and substituted or unsubstituted C1-C10 alkoxy, preferably from the group consisting of halogen, substituted or unsubstituted C1-C6 alkyl, and substituted or unsubstituted C1-C6 alkoxy.

According to some embodiments of the diimine metal complexes of this invention, R₁₁Is selected from C1-C20 alkyl with or without substituent, preferably C1-C10 alkyl with or without substituent, more preferably C1-C6 alkyl with or without substituent.

According to some embodiments of the diimine metal complexes of this invention, R₃And R₄The aryl group is selected from hydrogen, halogen, hydroxyl, C1-C20 alkyl with or without substituent, C2-C20 alkenyl with or without substituent, C2-C20 alkynyl with or without substituent, C3-C20 cycloalkyl with or without substituent, C1-C20 alkoxy with or without substituent, C2-C20 alkenyloxy with or without substituent, C2-C20 alkynyloxy with or without substituent, C3-C20 cycloalkoxy with or without substituent, C6-C20 aryl with or without substituent, C7-C20 aralkyl with or without substituent and C7-C20 alkaryl with or without substituent.

According to some embodiments of the diimine metal complexes of this invention, R₃And R₄The aryl group is the same or different and is independently selected from hydrogen, halogen, hydroxyl, C1-C10 alkyl with or without substituent, C2-C10 alkenyl with or without substituent, C2-C10 alkynyl with or without substituent, C3-C10 cycloalkyl with or without substituent, C1-C10 alkoxy with or without substituent, C2-C10 alkenyloxy with or without substituent, C2-C10 alkynyloxy with or without substituent, C3-C10 cycloalkoxy with or without substituent, C6-C15 aryl with or without substituent, C7-C15 aralkyl with or without substituent and C7-C15 alkaryl with or without substituent;

according to some embodiments of the diimine metal complexes of this invention, R₃And R₄Each independently selected from hydrogen, C1-C10 alkyl, halogenated C1-C10 alkyl, C1-C10 alkoxy, halogenated C1-C10 alkoxy and halogen, more preferably from hydrogen, C1-C6 alkyl, halogenated C1-C6 alkyl, C1-C6 alkoxy, halogenated C1-C6 alkoxy and halogen.

According to some embodiments of the diimine metal complexes of this invention, the substituents are selected from the group consisting of halogen, hydroxy, C1-C10 alkyl, halogenated C1-C10 alkyl, C1-C10 alkoxy, and halogenated C1-C10 alkoxy; the substituents are preferably selected from halogen, hydroxy, C1-C6 alkyl, halogenated C1-C6 alkyl, C1-C6 alkoxy and halogenated C1-C6 alkoxy.

According to some embodiments of the diimine metal complexes of this invention, the C1-C6 alkyl group is selected from the group consisting of methyl, ethyl, n-propyl, isopropyl, n-butyl and isobutyl, n-pentyl, isopentyl, n-hexyl, isohexyl, and 3, 3-dimethylbutyl;

according to some embodiments of the diimine metal complexes of this invention, the C1-C6 alkoxy group is selected from methoxy, ethoxy, n-propoxy, isopropoxy, n-and isobutoxy, n-pentoxy, isopentoxy, n-hexoxy, isohexoxy, and 3, 3-dimethylbutoxy,

according to some embodiments of the diimine metal complexes of the invention, the halogen is selected from fluorine, chlorine, bromine and iodine.

According to some embodiments of the diimine metal complexes of this invention, the diimine metal complexes are represented by formula III:

in the formula III, R¹-R⁵The substituents are the same or different, and are respectively and independently selected from hydrogen, halogen, hydroxyl, C1-C10 alkyl with or without substituent, C3-C10 cycloalkyl with or without substituent, C1-C10 alkoxy with or without substituent, C3-C10 cycloalkoxy with or without substituent, C6-C15 aryl with or without substituent, C7-C15 aralkyl with or without substituent and C7-C15 alkaryl with or without substituent;

R₃and R₄Each independently selected from hydrogen, C1-C10 alkyl, halogenated C1-C10 alkyl, C1-C10 alkoxy, halogenated C1-C10 alkoxy and halogen, more preferably from hydrogen, C1-C6 alkyl, halogenated C1-C6 alkyl, C1-C6 alkoxy, halogenated C1-C6 alkoxy and halogen;

m is nickel;

y is O;

x is selected from fluorine, chlorine and bromine;

R₁₁is selected from C1-C20 alkyl with or without substituent, preferably C1-C10 alkyl with or without substituent, more preferably C1-C6 alkyl with or without substituent.

According to some embodiments of the invention, the alkene alcohol is selected from one or more of the alkene alcohols represented by formula G:

in the formula G, L₁-L₃Each independently selected from H and C with or without substituent₁-C₃₀Alkyl radical, L₄Is C having a pendant group₁-C₃₀An alkylene group.

According to some embodiments of the invention, the copolymer has a content of structural units derived from the alkene alcohol represented by formula G of 0.4 to 10.0 mol%.

According to some embodiments of the invention, in formula G, L₁And L₂Is H.

According to some embodiments of the invention, in formula G, L₃Is H or C₁-C₃₀An alkyl group.

According to some embodiments of the invention, in formula G, L₄Is C having a pendant group₁-C₃₀An alkylene group.

According to some embodiments of the invention, in formula G, L₃Is H or C₁-C₂₀An alkyl group.

According to some embodiments of the invention, in formula G, L₄Is C having a pendant group₁-C₂₀An alkylene group.

According to some embodiments of the invention, in formula G, L₃Is H or C₁-C₁₀An alkyl group.

According to some embodiments of the invention, in formula G, L₄Is C having a pendant group₁-C₁₀An alkylene group.

According to some embodiments of the invention, in formula G, L₄Is C having a pendant group₁-C₆An alkylene group.

According to some embodiments of the invention, L₁-L₃Wherein said substituents are selected from halogen, C₁-C₁₀Alkyl radical, C₁-C₁₀Alkoxy radical, C₆-C₁₀One or more of aryl, cyano and hydroxyl.

According to some embodiments of the invention, L₁-L₃Wherein the substituent is selected from one or more of C1-C6 alkyl, halogen and C1-C6 alkoxy.

According to some embodiments of the invention, the pendant group in L4 is selected from halogen, C₆-C₂₀Aryl radical, C₁-C₂₀Alkyl and C₁-C₂₀One or more of alkoxyA, the C₆-C₂₀Aryl radical, C₁-C₂₀Alkyl and C₁-C₂₀Alkoxy is optionally substituted by a substituent, preferably selected from halogen, C₁-C₁₀Alkyl radical, C₁-C₁₀Alkoxy radical, C₆-C₁₀One or more of aryl and hydroxyl.

According to a preferred embodiment of the invention, said L₄The side group in (A) is selected from halogen and C₆-C₂₀Aryl radical, C₁-C₂₀Alkyl, hydroxy substituted C₁-C₂₀Alkyl and alkoxy substituted C₁-C₂₀One or more of alkyl; preferably, the side group is selected from halogen, C₆-C₂₀Aryl radical, C₁-C₁₀Alkyl, hydroxy substituted C₁-C₁₀Alkyl and alkoxy substituted C_1-10One or more of alkyl; more preferably, the side group is selected from halogen, phenyl, C₁-C₆Alkyl and hydroxy substituted C₁-C₆One or more of alkyl, said C₁-C₆Alkyl groups include methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, pentyl and hexyl.

According to a preferred embodiment of the invention, in formula G, L₁And L₂Is H, L₃Is H or C₁-C₃₀Alkyl radical, L₄Is C having a pendant group₁-C₃₀An alkylene group; said C is₁-C₃₀Alkyl is optionally substituted by a substituent, preferably selected from halogen, C₁-C₁₀Alkyl radical, C₁-C₁₀Alkoxy radical, C₆-C₁₀One or more of aryl, cyano and hydroxyl.

According to a preferred embodiment of the invention, in formula G, L₁And L₂Is H, L₃Is H, C₁-C₁₀Alkyl or halogen substituted C₁-C₁₀Alkyl, preferably L₃Is H or C₁-C₁₀An alkyl group; l is₄Is C having a pendant group₁-C₂₀Alkylene radicals, e.g. L₄Is methylene with side group, ethylene with side group, propylene with side group, butylene with side group, C with side group₅Alkylene, C having pendant groups₆Alkylene, C having pendant groups₇Alkylene, C having pendant groups₈Alkylene, C having pendant groups₉Alkylene, C having pendant groups₁₀Alkylene, C having pendant groups₁₂Alkylene, C having pendant groups₁₄Alkylene, C having pendant groups₁₈Alkylene, C having pendant groups₂₀Alkylene, preferably C, having pendant groups₁-C₁₀An alkylene group.

According to a preferred embodiment of the invention, in formula G, L₁And L₂Is H, L₃Is H or C_1-6An alkyl group; l is₄Is C having a pendant group₁-C₁₀An alkylene group.

In the present invention, the carbon number n of the Cn alkylene group means the number of C's in the linear chain, excluding the number of C's in the pendant group, and is, for example, isopropylidene (-CH)₂-CH(CH₃) -) is referred to herein as C with a pendant group (methyl)₂An alkylene group.

According to a preferred embodiment of the present invention, specific examples of the alkene alcohol represented by formula G include, but are not limited to: -2-methyl-3-buten-1-ol, 2-ethyl-3-buten-1-ol, 1-diphenyl-3-buten-1-ol, 2-methyl-3-buten-2-ol, 2-dimethyl-3-buten-1-ol, 3-methyl-1-penten-3-ol, 2, 4-dimethyl-4-penten-2-ol, 4-alkenyl-2-pentanol, 4-methyl-4-penten-2-ol, 2-phenyl-4-penten-2-ol, 2-methyl-3-buten-2-ol, 2-methyl-4-penten-2-ol, 2-methyl-2-penten-ol, 2-methyl, 2-allylhexafluoroisopropanol, 2-hydroxy-5-hexene, 3-buten-2-ol, 3-methyl-5-hexen-3-ol, 2-methyl-2-hydroxy-5-hexene, 1-allylcyclohexanol, 2, 3-dimethyl-2-hydroxy-5-hexene, 1-hepten-4-ol, 4-methyl-1-hepten-4-ol, 4-n-propyl-1-hepten-4-ol, 6-hepten-3-ol, 2-methyl-2-hydroxy-6-heptene, 5-methyl-2-hydroxy-6-heptene, 2-hydroxy-3-methyl-6-heptene, 2-hydroxy-3-ethyl-6-heptene, 2-hydroxy-4-methyl-6-heptene, 2-hydroxy-5-methyl-6-heptene, 2, 5-dimethyl-1-hepten-4-ol, 2, 6-dimethyl-7-octen-2-ol, 2-hydroxy-2, 4, 5-trimethyl-6-heptene, 2-methyl-3-hydroxy-7-octene, 3-methyl-3-hydroxy-6-heptene, 2-methyl-2-hydroxy-7-octene, 2-methyl-6-heptene, 2-hydroxy, 3-methyl-3-hydroxy-7-octene, 4-methyl-2-hydroxy-7-octene, 4-methyl-3-hydroxy-7-octene, 5-methyl-3-hydroxy-7-octene, 6-methyl-3-hydroxy-7-octene, 3-ethyl-3-hydroxy-7-octene, 1, 2-dihydroxy-7-octene, 2, 6-dimethyl-2, 6-dihydroxy-7-octene, 2, 6-dimethyl-2, 3-dihydroxy-7-octene, 2-methyl-2-hydroxy-3-chloro-7-octene, mixtures thereof, and mixtures thereof, 2-methyl-2-hydroxy-3, 5-dichloro-7-octene, 3, 4-dimethyl-4-hydroxy-8-nonene, 4-methyl-4-hydroxy-8-nonene, 4-ethyl-4-hydroxy-8-nonene, 4-propyl-4-hydroxy-8-nonene, 7-octen-2-ol, 3, 5-dichloro-2-methyl-7-octen-2-ol, 3-chloro-2-methyl-7-octen-2, 3-diol, and 2, 6-dimethyl-7-octen-2, 6-diol.

According to a preferred embodiment of the invention, the cocatalyst is chosen from organoaluminum compounds and/or organoboron compounds.

According to a preferred embodiment of the invention, the organoaluminium compound is selected from alkylaluminoxanes or compounds of general formula AlR_nX¹ _3-nWith an organoaluminum compound (alkylaluminum or alkylaluminum halide) of the general formula AlR_nX¹ _3-nWherein R is H, C₁-C₂₀Saturated or unsaturated hydrocarbon radicals or C₁-C₂₀Saturated or unsaturated hydrocarbyloxy radicals, preferably C₁-C₂₀Alkyl radical, C₁-C₂₀Alkoxy radical, C₇-C₂₀Aralkyl or C₆-C₂₀An aryl group; x¹Is halogen, preferably chlorine or bromine; 0<n is less than or equal to 3. Specific examples of the organoaluminum compound include, but are not limited to: trimethylaluminum, triethylaluminum, triisobutylaluminum, tri-n-hexylaluminum, trioctylaluminum, diethylaluminum monohydrogen, diisobutylaluminum monohydrogen, diethylaluminum monochloride, diisobutylaluminum monochloride, ethylaluminum sesquichloride, ethylaluminum dichloride, Methylaluminoxane (MAO) and Modified Methylaluminoxane (MMAO). Preferably, the organoaluminum compound is Methylaluminoxane (MAO).

According to a preferred embodiment of the invention, the organoboron compound is selected from an aryl boron and/or a borate. The arylborole is preferably a substituted or unsubstituted phenylborone, more preferably tris (pentafluorophenyl) boron. The borate is preferably N, N-dimethylanilinium tetrakis (pentafluorophenyl) borate and/or triphenylmethyl tetrakis (pentafluorophenyl) borate.

According to a preferred embodiment of the present invention, the concentration of the main catalyst in the reaction system is 0.00001 to 100mmol/L, for example, 0.00001mmol/L, 0.00005mmol/L, 0.0001mmol/L, 0.0005mmol/L, 0.001mmol/L, 0.005mmol/L, 0.01mmol/L, 0.05mmol/L, 0.1mmol/L, 0.3mmol/L, 0.5mmol/L, 0.8mmol/L, 1mmol/L, 5mmol/L, 8mmol/L, 10mmol/L, 20mmol/L, 30mmol/L, 50mmol/L, 70mmol/L, 80mmol/L, 100mmol/L and any value therebetween, preferably 0.0001 to 1mmol/L, more preferably 0.001 to 0.5 mmol/L.

According to a preferred embodiment of the present invention, when the cocatalyst is an organoaluminum compound, the molar ratio of aluminum in the cocatalyst to M in the procatalyst is (10-10000000):1, for example, 10:1, 20:1, 50:1, 100:1, 200:1, 300:1, 500:1, 700:1, 800:1, 1000:1, 2000:1, 3000:1, 5000:1, 10000:1, 100000:1, 1000000:1, 10000000:1 and any value therebetween, preferably (10-100000):1, more preferably (100-10000): 1; when the cocatalyst is an organoboron compound, the molar ratio of boron in the cocatalyst to M in the procatalyst is (0.1-1000):1, e.g., 0.1:1, 0.2:1, 0.5:1, 0.8:1, 1:1, 1.2:1, 1.4:1, 1.6:1, 1.8:1, 2:1, 2.5:1, 3:1, 4:1, 5:1, 8:1, 10:1, 20:1, 50:1, 100:1, 200:1, 300:1, 500:1, 700:1, 800:1, 1000:1, and any value therebetween, preferably (0.1-500): 1.

According to a preferred embodiment of the invention, the olefin comprises an olefin having 2 to 16 carbon atoms, and in some embodiments of the invention, the olefin comprises ethylene or an alpha-olefin having 3 to 16 carbon atoms. In other embodiments of the present invention, the olefin is C₃-C₁₆A cyclic olefin, preferably a 5-or 6-membered ring. Preferably, the olefin is ethylene or an alpha-olefin having 3 to 16 carbon atoms, more preferably ethylene or C₂-C₁₀Alpha-olefins, e.g. ethylene, propylene, butylenePentene, hexene, heptene and octene.

According to a preferred embodiment of the present invention, the concentration of the olefin alcohol monomer represented by the formula G in the reaction system is 0.01 to 6000mmol/L, preferably 0.1 to 1000mmol/L, more preferably 1 to 500mmol/L, and may be, for example, 1mmol/L, 10mmol/L, 20mmol/L, 30mmol/L, 50mmol/L, 70mmol/L, 90mmol/L, 100mmol/L, 200mmol/L, 300mmol/L, 400mmol/L, 500mmol/L and any value therebetween.

According to a preferred embodiment of the present invention, the chain transfer agent is selected from one or more of aluminum alkyls, magnesium alkyls and zinc alkyls.

According to a preferred embodiment of the invention, the chain transfer agent is a trialkylaluminum and/or a dialkylzinc, preferably one or more selected from the group consisting of trimethylaluminum, triethylaluminum, triisopropylaluminum, triisobutylaluminum, tri-n-hexylaluminum, tri-n-octylaluminum, dimethylzinc and diethylzinc.

According to a preferred embodiment of the invention, the molar ratio of the chain transfer agent to M in the procatalyst is (0.1-2000: 1, e.g. 0.1:1, 0.2:1, 0.5:1, 1:1, 2:1, 3:1, 5:1, 8:1, 10:1, 20:1, 50:1, 100:1, 200:1, 300:1, 500:1, 600:1, 800:1, 1000:1, 2000:1 and any value in between, preferably (10-600: 1).

According to a preferred embodiment of the invention, the polymerization is carried out in an alkane solvent selected from C₃-C₂₀One or more alkanes, preferably selected from C₃-C₁₀The alkane, for example, may be selected from one or more of butane, isobutane, pentane, hexane, heptane, octane and cyclohexane, preferably one or more of hexane, heptane and cyclohexane.

According to a preferred embodiment of the present invention, the olefin alcohol is pre-treated with a dehydroactive hydrogen, preferably with a co-catalyst or chain transfer agent as described above, to remove hydroxyl active hydrogen from the olefin alcohol. Preferably, the molar ratio of hydroxyl groups in the alkene alcohol to co-catalyst or chain transfer agent during pretreatment is from 10:1 to 1: 10.

According to a preferred embodiment of the invention, the reaction is carried out in the absence of water and oxygen.

According to a preferred embodiment of the invention, the conditions of the reaction include: the temperature of the reaction is-50 ℃ to 50 ℃, preferably-20 ℃ to 50 ℃, more preferably 0 ℃ to 50 ℃, and can be, for example, 0 ℃, 10 ℃, 20 ℃, 30 ℃, 40 ℃, 50 ℃ and any value therebetween; and/or the reaction time is 10-200min, preferably 20-60 min. In the present invention, the reaction pressure is not particularly limited as long as the monomer can be subjected to coordination copolymerization. When the olefin is ethylene, the pressure of ethylene in the reactor is preferably 1 to 1000atm, more preferably 1 to 200atm, and still more preferably 1 to 50atm, from the viewpoint of cost reduction and simplification of the polymerization process. In the present invention, the "reaction system" is meant to include the totality of solvent, olefin alcohol monomer, catalyst, and optionally chain transfer agent.

The invention also provides an olefin-olefin alcohol copolymer prepared by the preparation method, which comprises spherical and/or spheroidal polymers. According to a preferred embodiment of the invention, the spherical and/or spheroidal polymers have an average particle size of 0.1 to 50.0mm, for example 0.1mm, 0.5mm, 1.0mm, 2.0mm, 3.0mm, 5.0mm, 8.0mm, 10.0mm, 15.0mm, 20.0mm, 25.0mm, 30.0mm, 35.0mm, 40.0mm, 45.0mm, 50.0mm and any value in between, preferably 0.5 to 20.0 mm.

According to a preferred embodiment of the present invention, in the olefin-olefin alcohol copolymer, the content of the structural unit derived from the olefin alcohol represented by the formula G is 0.4 to 30.0 mol%, and for example, may be 0.4 mol%, 0.5 mol%, 0.7 mol%, 0.8 mol%, 1.0 mol%, 1.5 mol%, 2.0 mol%, 5.0 mol%, 8.0 mol%, 10.0 mol%, 15.0 mol%, 20.0 mol%, 25.0 mol%, 30.0 mol% and any value therebetween, preferably 0.7 to 10.0 mol%.

According to a preferred embodiment of the present invention, the weight average molecular weight of the olefin-olefin alcohol copolymer is 30000-500000, preferably 50000-400000.

According to a preferred embodiment of the present invention, the olefin-olefin alcohol copolymer has a molecular weight distribution of 4.0 or less, and for example, may be 0.1, 0.5, 1.0, 1.5, 2.0, 2.5, 3.0, 3.5, 4.0 and any value therebetween, and preferably, the molecular weight distribution is 1.0 to 4.0.

In the present invention, the particle size of a spherical or spheroidal polymer is herein considered to be equal to the diameter of a sphere having a volume equal to the volume of the particle.

According to still another aspect of the present invention, there is provided a use of the olefin-olefin alcohol copolymer as a polyolefin material.

The process for preparing an olefin-olefin alcohol copolymer provided by the present invention uses a novel trinuclear metal complex-containing catalyst. The catalyst is not reported, therefore, the technical problem solved by the invention is to provide a novel preparation method of olefin-olefin alcohol copolymer.

Furthermore, in the preparation method of the olefin-olefin alcohol copolymer provided by the invention, the spherical and/or spheroidal polymers with good shapes are directly prepared by selecting the olefin alcohol monomer for reaction, the catalyst and a proper polymerization process without subsequent processing steps such as granulation and the like, and the obtained polymerization product is not easy to scale in a reactor and is convenient to transport.

Further, compared with the existing industrial process for preparing olefin-olefin alcohol copolymers, the method for preparing olefin-olefin alcohol copolymers provided by the invention omits the step of saponification reaction, and has simpler preparation process.

In the present invention, alkyl refers to straight chain alkyl, branched chain alkyl or cycloalkyl, including but not limited to: methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl, tert-butyl, n-pentyl, isopentyl, tert-pentyl, neopentyl, n-hexyl, n-heptyl, n-octyl, n-decyl, cyclopropyl, cyclopentyl, cyclohexyl, 4-methylcyclohexyl, 4-ethylcyclohexyl, 4-n-propylcyclohexyl and 4-n-butylcyclohexyl.

In the present invention, examples of aryl groups include, but are not limited to: phenyl, 4-methylphenyl, 4-ethylphenyl, dimethylphenyl, vinylphenyl.

In the present invention, alkenyl refers to straight chain alkenyl, branched chain alkenyl or cycloalkenyl including, but not limited to: vinyl, allyl, butenyl.

In the present invention, examples of the aralkyl group include, but are not limited to: phenylmethyl, phenylethyl, phenyl-n-propyl, phenyl-isopropyl, phenyl-n-butyl and phenyl-tert-butyl.

In the present invention, examples of alkylaryl groups include, but are not limited to: tolyl, ethylphenyl, n-propylphenyl, isopropylphenyl, n-butylphenyl and tert-butylphenyl groups.

Drawings

FIG. 1 is an electron micrograph of a spherical and/or spheroidal polymer obtained in example 2 of the present invention.

Detailed Description

The present invention will be described in detail with reference to examples, but the present invention is not limited to the examples.

The analytical characterization instrument used in the present invention was as follows:

¹HNMR nuclear magnetic resonance apparatus: bruker DMX 300(300MHz), Tetramethylsilicon (TMS) as internal standard, was used to test the structure of the complex ligands at 25 ℃.

Comonomer content of the polymer (content of structural units derived from the olefin alcohol represented by formula G): by using¹³C NMR spectroscopy was carried out by dissolving a polymer sample in 1,2, 4-trichlorobenzene at 120 ℃ on a 400MHz Bruker Avance 400 NMR spectrometer using a 10mm PASEX 13 probe.

Molecular weight and molecular weight distribution PDI (PDI ═ Mw/Mn) of the copolymer: measured at 150 ℃ using PL-GPC220 in trichlorobenzene (standard: PS, flow rate: 1.0mL/min, column: 3 XPlgel 10um M1 XED-B300X 7.5 nm).

The activity measurement method comprises the following steps: weight of polymer (g)/nickel (mol). times.2.

Example 1

Complex Ni₁Preparation of

Will contain 0.277g(0.9mmol)(DME)NiBr₂Was slowly added dropwise to a solution containing 0.175g (0.6mmol) of ligand L₁Was stirred at room temperature for 6 hours in a dichloromethane solution (10mL), and was precipitated by addition of anhydrous ether. Filtering to obtain a filter cake, washing the filter cake with anhydrous ether, and vacuum drying to obtain yellow powdery solid Ni₁. Yield: 70.2 percent. Elemental analysis (C)₄₄H₅₈Br₆N₄Ni₃O₂): c, 39.72; h, 4.39; n, 4.21; experimental values (%): c, 39.38; h, 4.60; and N, 3.96.

Continuously drying a 1L stainless steel polymerization kettle equipped with mechanical stirring at 130 deg.C for 6h, vacuumizing while hot, and adding N₂Replace qi for 3 times. 500mL of hexane was poured into the polymerization system, and 6.6mg (5. mu. mol) of complex Ni was added₁15mmol (2.5mL) of 2-methyl-2-hydroxy-7-octene, 15mL of AlEt₃(1.0mol/L hexane solution), 6.5mL of Methylaluminoxane (MAO) (1.53mol/L toluene solution), and the reaction was stirred at 30 ℃ under an ethylene pressure of 10atm for 30 min. Finally, the polymer was obtained by neutralizing the mixture with a 10 wt% ethanol solution acidified with hydrochloric acid. The polymerization activity and the polymer performance parameters are shown in Table 1.

Example 2

Continuously drying a 1L stainless steel polymerization kettle equipped with mechanical stirring at 130 deg.C for 6h, vacuumizing while hot, and adding N₂Replace qi for 3 times. 500mL of hexane was poured into the polymerization system, and 6.6mg (5. mu. mol) of complex Ni was added₁30mmol (5.1mL) of 2-methyl-2-hydroxy-7-octene, 30mL of AlEt₃(1.0mol/L hexane solution), 6.5mL of MAO (1.53mol/L toluene solution), and the reaction mixture was stirred at 30 ℃ under an ethylene pressure of 10atm for 30 min. Finally, the polymer was obtained by neutralizing the mixture with a 10 wt% ethanol solution acidified with hydrochloric acid. The polymerization activity and the polymer performance parameters are shown in Table 1.

Example 3

Continuously drying a 1L stainless steel polymerization kettle equipped with mechanical stirring at 130 deg.C for 6h, vacuumizing while hot, and adding N₂Replace qi for 3 times. 500mL of hexane was poured into the polymerization system, and 6.6mg (5. mu. mol) of complex Ni was added₁30mmol (5.1mL) of 2-methyl-2-hydroxy-7-octene, 30mL of AlEt₃(1.0mol/L ofHexane solution), 6.5mL of MAO (1.53mol/L in toluene), and the reaction was stirred at 60 ℃ for 30min while maintaining ethylene pressure of 10 atm. Finally, the polymer was obtained by neutralizing the mixture with a 10 wt% ethanol solution acidified with hydrochloric acid. The polymerization activity and the polymer performance parameters are shown in Table 1.

Example 4

Continuously drying a 1L stainless steel polymerization kettle equipped with mechanical stirring at 130 deg.C for 6h, vacuumizing while hot, and adding N₂Replace qi for 3 times. 500mL of hexane was poured into the polymerization system, and 6.6mg (5. mu. mol) of complex Ni was added₁30mmol (5.1mL) of 2-methyl-2-hydroxy-7-octene, 30mL of AlEt₃(1.0mol/L hexane solution), 0.5mL diethyl zinc (1mol/L hexane solution), 6.5mL MAO (1.53mol/L toluene solution), and the reaction mixture was stirred at 30 ℃ under 10atm of ethylene pressure for 30 min. Finally, the polymer was obtained by neutralizing the mixture with a 10 wt% ethanol solution acidified with hydrochloric acid. The polymerization activity and the polymer performance parameters are shown in Table 1.

Example 5

Continuously drying a 1L stainless steel polymerization kettle equipped with mechanical stirring at 130 deg.C for 6h, vacuumizing while hot, and adding N₂Replace qi for 3 times. 500mL of hexane was poured into the polymerization system, and 6.6mg (5. mu. mol) of complex Ni was added₁30mmol (5.1mL) of 2-methyl-2-hydroxy-7-octene, 30mL of AlEt₃(1.0mol/L hexane solution), 1.0mL diethyl zinc (1mol/L hexane solution), 6.5mL MAO (1.53mol/L toluene solution), and the reaction was stirred at 30 ℃ for 30min while maintaining an ethylene pressure of 10 atm. Finally, the polymer was obtained by neutralizing the mixture with a 10 wt% ethanol solution acidified with hydrochloric acid. The polymerization activity and the polymer performance parameters are shown in Table 1.

Example 6

Continuously drying a 1L stainless steel polymerization kettle equipped with mechanical stirring at 130 deg.C for 6h, vacuumizing while hot, and adding N₂Replace qi for 3 times. 500mL of hexane was poured into the polymerization system, and 6.6mg (5. mu. mol) of complex Ni was added₁50mmol (8.5mL) 2-methyl-2-hydroxy-7-octene, 50mL AlEt₃(1.0mol/L hexane solution), 6.5mL of MAO (1.53mol/L toluene solution), and the reaction mixture was stirred at 30 ℃ under an ethylene pressure of 10atm for 30 min. Finally using 10wNeutralizing with ethanol solution acidified by t% hydrochloric acid to obtain the polymer. The polymerization activity and the polymer performance parameters are shown in Table 1.

Example 7

Continuously drying a 1L stainless steel polymerization kettle equipped with mechanical stirring at 130 deg.C for 6h, vacuumizing while hot, and adding N₂Replace qi for 3 times. 500mL of hexane was poured into the polymerization system, and 6.6mg (5. mu. mol) of complex Ni was added₁100mmol (17.0mL) of 2-methyl-2-hydroxy-7-octene, 100mL of AlEt₃(1.0mol/L hexane solution), 6.5mL of MAO (1.53mol/L toluene solution), and the reaction mixture was stirred at 30 ℃ under an ethylene pressure of 10atm for 30 min. Finally, the polymer was obtained by neutralizing the mixture with a 10 wt% ethanol solution acidified with hydrochloric acid. The polymerization activity and the polymer performance parameters are shown in Table 1.

Example 8

Complex Ni₂Preparation of

Will contain 0.277g (0.9mmol) of (DME) NiBr₂Was slowly added dropwise to a solution containing 0.243g (0.6mmol) of ligand L (10mL)₂Was stirred at room temperature for 6 hours in a dichloromethane solution (10mL), and was precipitated by addition of anhydrous ether. Filtering to obtain a filter cake, washing the filter cake with anhydrous ether, and vacuum drying to obtain yellow powdery solid Ni₂. The yield was 74.0%. Elemental analysis (C)₆₀H₉₀Br₆N₄Ni₃O₂): c, 46.35; h, 5.83; n, 3.60; experimental values (%): c, 46.48; h, 6.12; and N, 3.50.

Continuously drying a 1L stainless steel polymerization kettle equipped with mechanical stirring at 130 deg.C for 6h, vacuumizing while hot, and adding N₂Replace qi for 3 times. 500mL of hexane was poured into the polymerization system, and 7.8mg (5. mu. mol) of complex Ni was added₂30mmol (5.1mL) of 2-methyl-2-hydroxy-7-octene, 30mL of AlEt₃(1.0mol/L hexane solution), 6.5mL of MAO (1.53mol/L toluene solution), and the reaction mixture was stirred at 30 ℃ under an ethylene pressure of 10atm for 30 min. Finally dissolving the mixture in 10 wt% ethanol acidified by hydrochloric acidAnd (4) neutralizing the solution to obtain a polymer. The polymerization activity and the polymer performance parameters are shown in Table 1.

Example 9

Continuously drying a 1L stainless steel polymerization kettle equipped with mechanical stirring at 130 deg.C for 6h, vacuumizing while hot, and adding N₂Replace qi for 3 times. 500mL of hexane was poured into the polymerization system, and 7.8mg (5. mu. mol) of complex Ni was added₂30mmol (8.5mL) of 2-methyl-2-hydroxy-7-octene, 30mL of AlEt₃(1.0mol/L hexane solution), 6.5mL MAO (1.53mol/L toluene solution), and the reaction was stirred at 60 ℃ under 10atm of ethylene pressure for 30 min. Finally, the polymer was obtained by neutralizing the mixture with a 10 wt% ethanol solution acidified with hydrochloric acid. The polymerization activity and the polymer performance parameters are shown in Table 1.

Example 10

Continuously drying a 1L stainless steel polymerization kettle equipped with mechanical stirring at 130 deg.C for 6h, vacuumizing while hot, and adding N₂Replace qi for 3 times. 500mL of hexane was poured into the polymerization system, and 7.8mg (5. mu. mol) of complex Ni was added₂30mmol (4.1mL) of 3-methyl-5-hexen-3-ol, 30mL of AlEt₃(1.0mol/L hexane solution), 6.5mL MAO (1.53mol/L toluene solution), and the reaction mixture was stirred at 30 ℃ under 10atm of ethylene pressure for 60 min. Finally, the polymer was obtained by neutralizing the mixture with a 10 wt% ethanol solution acidified with hydrochloric acid. The polymerization activity and the polymer performance parameters are shown in Table 1.

Example 11

Complex Ni₃Preparation of

Will contain 0.277g (0.9mmol) of (DME) NiBr₂To a solution of 2-methyl-1-propanol (10mL) containing 0.243g (0.6mmol) of ligand L₂Was stirred at room temperature for 6 hours in a dichloromethane solution (10mL), and was precipitated by addition of anhydrous ether. Filtering to obtain a filter cake, washing the filter cake with anhydrous ether, and vacuum drying to obtain yellow powdery solid Ni₃. The yield was 74.5%. Elemental analysis (C)₆₄H₉₈Br₆N₄Ni₃O₂): c, 47.71; h, 6.13; n, 3.48; experimental values (%): c, 47.48; h, 6.42; and N, 3.29.

Continuously drying a 1L stainless steel polymerization kettle equipped with mechanical stirring at 130 deg.C for 6h, vacuumizing while hot, and adding N₂Replace qi for 3 times. 500mL of hexane was poured into the polymerization system, and 8.0mg (5. mu. mol) of complex Ni was added₃30mmol (5.1mL) of 2-methyl-2-hydroxy-7-octene, 30mL of AlEt₃(1.0mol/L hexane solution), 6.5mL of MAO (1.53mol/L toluene solution), and the reaction mixture was stirred at 30 ℃ under an ethylene pressure of 10atm for 30 min. Finally, the polymer was obtained by neutralizing the mixture with a 10 wt% ethanol solution acidified with hydrochloric acid. The polymerization activity and the polymer performance parameters are shown in Table 1.

Example 12

Continuously drying a 1L stainless steel polymerization kettle equipped with mechanical stirring at 130 deg.C for 6h, vacuumizing while hot, and adding N₂Replace qi for 3 times. 500mL of hexane was poured into the polymerization system, and 8.0mg (5. mu. mol) of complex Ni was added₃30mmol (4.5mL) of 4-methyl-1-hepten-4-ol, 30mL of AlEt₃(1.0mol/L hexane solution), 6.5mL of MAO (1.53mol/L toluene solution), and the reaction mixture was stirred at 30 ℃ under an ethylene pressure of 10atm for 30 min. Finally, the polymer was obtained by neutralizing the mixture with a 10 wt% ethanol solution acidified with hydrochloric acid. The polymerization activity and the polymer performance parameters are shown in Table 1.

Example 13

Complex Ni₄Preparation of

Will contain 0.277g (0.9mmol) of (DME) NiBr₂Was slowly added dropwise to a solution containing 0.272g (0.6mmol) of ligand L₃In dichloromethane (10 mL). The color of the solution immediately turned deep red and a large amount of precipitate formed. Stirring at room temperature for 6h, and precipitating with anhydrous diethyl ether. Filtering to obtain a filter cake, washing the filter cake with anhydrous ether, and vacuum drying to obtain brownish red powdery solid Ni₄. The yield was 74.1%. Elemental analysis (C)₆₄H₆₂Br₆F₄N₄Ni₃O₂): c, 46.57; h, 3.79; n, 3.39; experimental values (%): c, 46.72; h, 3.97; and N, 3.48.

Continuously drying a 1L stainless steel polymerization kettle equipped with mechanical stirring at 130 deg.C for 6hrs, vacuumizing while it is hot, and adding N₂Replace qi for 3 times. 500mL of hexane, 30mmol (5.1mL) of 2-methyl-2-hydroxy-7-octene, 30mL of AlEt₃(1.0mol/L in hexane), 6.5ml of Methylaluminoxane (MAO) (1.53mol/L in toluene) were added, and 8.2mg (5. mu. mol) of Ni complex were added₄. The reaction was vigorously stirred at 30min with keeping the ethylene pressure at 10atm at 30 ℃. The polymer was obtained by neutralizing with a 10 wt% hydrochloric acid acidified ethanol solution, and the results are shown in Table 1.

Example 14

Continuously drying a 1L stainless steel polymerization kettle equipped with mechanical stirring at 130 deg.C for 6h, vacuumizing while hot, and adding N₂Replace qi for 3 times. 500mL of hexane was poured into the polymerization system, and 6.6mg (5. mu. mol) of complex Ni was added₁30mmol (5.1mL) of 2-methyl-2-hydroxy-7-octene, 30mL of AlEt₃(1.0mol/L hexane solution), 15mL of a toluene solution of N, N-dimethylanilinium tetrakis (pentafluorophenyl) borate (1mmol/L toluene solution) was added, and the reaction was stirred at 30 ℃ under an ethylene pressure of 10atm for 30 min. Finally, the polymer was obtained by neutralizing the mixture with a 10 wt% ethanol solution acidified with hydrochloric acid. The polymerization activity and the polymer performance parameters are shown in Table 1.

Example 15

Continuously drying a 1L stainless steel polymerization kettle equipped with mechanical stirring at 130 deg.C for 6h, vacuumizing while hot, and adding N₂Replace qi for 3 times. 500mL of hexane was poured into the polymerization system, and 6.6mg (5. mu. mol) of complex Ni was added₁30mmol (6.0mL) of 10-undecen-1-ol, 30mL of AlEt₃(1.0mol/L hexane solution), 6.5mL of MAO (1.53mol/L toluene solution), and the reaction mixture was stirred at 30 ℃ under an ethylene pressure of 10atm for 30 min. Finally, the polymer was obtained by neutralizing the mixture with a 10 wt% ethanol solution acidified with hydrochloric acid. The polymerization activity and the polymer performance parameters are shown in Table 1.

Example 16

Continuously drying a 1L stainless steel polymerization kettle equipped with mechanical stirring at 130 deg.C for 6h, vacuumizing while hot, and adding N₂Replace qi for 3 times. 500mL of toluene was injected into the polymerization system while adding 6.6mg (5. mu. mol) of complex Ni₁30mmol (5.1mL) of 2-methyl-2-hydroxy-7-octene, 30mL of AlEt₃(1.0mol/L hexane solution), 6.5mL of MAO (1.53mol/L toluene solution), and the reaction mixture was stirred at 30 ℃ under an ethylene pressure of 10atm for 30 min. Finally, the polymer was obtained by neutralizing the mixture with a 10 wt% ethanol solution acidified with hydrochloric acid. The polymerization activity and the polymer performance parameters are shown in Table 1.

TABLE 1

As can be seen from Table 1, the catalyst of the present invention exhibits higher polymerization activity when it catalyzes the copolymerization of ethylene and enol, and the obtained polymer has higher molecular weight. The copolymerization activity of the catalyst can reach 4.21 x 10 to the maximum⁶g·mol^-1(Ni)·h^-1. The molecular weight of the polymer can be controlled within a wide range according to the addition of the chain transfer agent. In addition, by regulating and controlling the polymerization conditions, a copolymerization product with good particle morphology can be prepared.

It should be noted that the above-mentioned embodiments are only for explaining the present invention, and do not set any limit to the present invention. The present invention has been described with reference to exemplary embodiments, but the words which have been used herein are words of description and illustration, rather than words of limitation. The invention can be modified, as prescribed, within the scope of the claims and without departing from the scope and spirit of the invention. Although the invention has been described herein with reference to particular means, materials and embodiments, the invention is not intended to be limited to the particulars disclosed herein, but rather extends to all other methods and applications having the same functionality.