阅读说明：本技术 一种带有荧光颗粒的大理石装饰板的制造方法 (Manufacturing method of marble decorative plate with fluorescent particles ) 是由 邱玉芳 于 2019-10-16 设计创作，主要内容包括：本发明属于装饰板制造技术领域,尤其为一种带有荧光颗粒的大理石装饰板的制造方法,包括以下重量份数的组分：底料：基板；面料：不饱和聚酯树脂30-50份、碳酸钙粉20-30份、固化剂3-7份、促进剂3-7份、荧光颗粒5-15份、阻燃纤维2-8份,所述基板为PVC板、PP板或者铝合金基板,所述固化剂为过氧化苯甲酰,所述促进剂为苯乙烯；通过设置一个由轻质基材制作的基板,将混有荧光颗粒的物料混合后,通过烘干固化的方式固定在基材表面,形成大理石纹路,完成整个大理石装饰板的制作,使得大理石在质量上更加轻质,方便安装与运输,且其面料中混有的荧光颗粒,可以使大理石装饰板在晚上无光的条件下能够发出荧光,更滑美观。(The invention belongs to the technical field of decorative plate manufacturing, and particularly relates to a manufacturing method of a marble decorative plate with fluorescent particles, which comprises the following components in parts by weight: bottom materials: a substrate; fabric: 30-50 parts of unsaturated polyester resin, 20-30 parts of calcium carbonate powder, 3-7 parts of curing agent, 3-7 parts of accelerator, 5-15 parts of fluorescent particles and 2-8 parts of flame-retardant fiber, wherein the substrate is a PVC (polyvinyl chloride) plate, a PP (polypropylene) plate or an aluminum alloy substrate, the curing agent is benzoyl peroxide, and the accelerator is styrene; through setting up a base plate by light substrate preparation, after the material that will thoughtlessly have fluorescent particle mixes, fix on the substrate surface through the mode of stoving solidification, form the marble line, accomplish the preparation of whole marble decorative board for the marble is lighter in the quality, and easy to assemble and transportation, and thoughtlessly have fluorescent particle in its surface fabric, can make the marble decorative board can send fluorescence, and is more smooth pleasing to the eye under the condition of evening no light.)

1. The marble decorative plate with the fluorescent particles is characterized by comprising the following components in parts by weight:

bottom materials: a substrate;

fabric: 30-50 parts of unsaturated polyester resin, 20-30 parts of calcium carbonate powder, 3-7 parts of curing agent, 3-7 parts of accelerator, 5-15 parts of fluorescent particles and 2-8 parts of flame-retardant fiber.

2. The marble decorative plate with fluorescent particles of claim 1, wherein: the substrate is a PVC plate, a PP plate or an aluminum alloy substrate.

3. The marble decorative plate with fluorescent particles of claim 1, wherein: the curing agent is benzoyl peroxide.

4. The marble decorative plate with fluorescent particles of claim 1, wherein: the accelerant is styrene.

5. The marble decorative plate with fluorescent particles of claim 1, wherein: the flame-retardant fiber is glass fiber or ceramic fiber.

6. The method of manufacturing marble decorating plate with fluorescent particles as claimed in claim 1, wherein: the method comprises the following steps:

s1, firstly blowing dust on the surface of the substrate, then spraying primer on the surface of the substrate, naturally leveling the primer on the surface of the substrate, then drying and curing at the temperature of 220-240 ℃ for 5-20 minutes, and then naturally cooling;

s2, injecting 30-50 parts of unsaturated polyester resin, 20-30 parts of calcium carbonate powder, 3-7 parts of curing agent, 3-7 parts of accelerant, 2-8 parts of flame-retardant fiber, 10-30 parts of pigment particles and 5-15 parts of fluorescent particles into a container, and uniformly stirring for 20-30 minutes;

s3, installing a mold around the substrate for shaping the fabric;

s4, injecting the uniformly stirred mixture in the container into a mold with a substrate until the mold is filled with the substrate;

s5, drying and curing at the temperature of 180-220 ℃ for 15-30 minutes, and then demoulding after drying and curing.

Technical Field

The invention belongs to the technical field of decorative plate manufacturing, and particularly relates to a manufacturing method of a marble decorative plate with fluorescent particles.

Background

The artificial marble is prepared by taking crushed stone of natural marble or granite as a filling material and cement, gypsum and unsaturated polyester resin as an adhesive through stirring, molding, grinding and polishing, so the artificial marble has the characteristics of a plurality of natural marbles, for example, the artificial marble can be manually adjusted, so the artificial marble has various colors, good flexibility, unobvious joining treatment, very strong sense of unity, gorgeous and colorful, has ceramic luster, high appearance hardness, difficult damage, corrosion resistance and high temperature resistance, is very easy to clean, has a great defect, has more obvious damage to human bodies, and the common artificial marbles in the market at present usually have the following four types: the cement type artificial marble, polyester type artificial marble, composite type artificial marble and sintered type artificial marble, along with the development of modern building industry, have proposed the light, high-strength, esthetic, many-variety requirements for ornamental material, the artificial facing stone appears under this situation, it is light in weight, high, corrosion-resistant, pollution-resistant, construction convenience, the pattern can be controlled artificially, it is the ideal ornamental material of modern building.

The existing marble has heavy weight, causes great troubles to the installation and transportation of the marble slab, does not have the fluorescent effect on the existing marble slab, and has poor ornamental effect under the condition of no light at night.

Disclosure of Invention

To solve the problems set forth in the background art described above. The invention provides a manufacturing method of a marble decorative plate with fluorescent particles, which has the characteristics of light weight, convenient transportation and installation and fluorescence at night under the condition of no light.

In order to achieve the purpose, the invention provides the following technical scheme: the marble decorative plate with the fluorescent particles comprises the following components in parts by weight:

bottom materials: a substrate;

fabric: 30-50 parts of unsaturated polyester resin, 20-30 parts of calcium carbonate powder, 3-7 parts of curing agent, 3-7 parts of accelerator, 5-15 parts of fluorescent particles and 2-8 parts of flame-retardant fiber.

Preferably, the substrate is a PVC plate, a PP plate or an aluminum alloy substrate.

Preferably, the curing agent is benzoyl peroxide.

Preferably, the promoter is styrene.

Preferably, the flame retardant fibers are glass fibers or ceramic fibers.

A manufacturing method of a marble decorative plate with fluorescent particles comprises the following steps:

s1, firstly blowing dust on the surface of the substrate, then spraying primer on the surface of the substrate, naturally leveling the primer on the surface of the substrate, then drying and curing at the temperature of 220-240 ℃ for 5-20 minutes, and then naturally cooling;

s2, injecting 30-50 parts of unsaturated polyester resin, 20-30 parts of calcium carbonate powder, 3-7 parts of curing agent, 3-7 parts of accelerant, 2-8 parts of flame-retardant fiber, 10-30 parts of pigment particles and 5-15 parts of fluorescent particles into a container, and uniformly stirring for 20-30 minutes;

s3, installing a mold around the substrate for shaping the fabric;

s4, injecting the uniformly stirred mixture in the container into a mold with a substrate until the mold is filled with the substrate;

s5, drying and curing at the temperature of 180-220 ℃ for 15-30 minutes, and then demoulding after drying and curing.

Compared with the prior art, the invention has the beneficial effects that:

according to the invention, the substrate made of the light base material is arranged, materials mixed with fluorescent particles are mixed and then fixed on the surface of the base material in a drying and curing mode to form marble grains, so that the whole marble decorative plate is manufactured, the marble is lighter in quality and convenient to mount and transport, and the fluorescent particles mixed in the fabric can enable the marble decorative plate to emit fluorescence at night without light, so that the marble decorative plate is smooth and attractive.

Detailed Description

The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.

Example 1

The invention provides the following technical scheme: the marble decorative plate with the fluorescent particles comprises the following components in parts by weight:

bottom materials: a substrate;

fabric: 30 parts of unsaturated polyester resin, 20 parts of calcium carbonate powder, 3 parts of curing agent, 3 parts of accelerator, 5 parts of fluorescent particles and 2 parts of flame-retardant fiber.

Specifically, the substrate is a PVC plate.

Specifically, the curing agent is benzoyl peroxide.

In particular, the accelerator is styrene.

Specifically, the flame-retardant fibers are glass fibers.

The manufacturing method of the marble decorative plate with the fluorescent particles comprises the following steps:

s1, firstly, blowing dust on the surface of the substrate, then spraying primer on the surface of the substrate, naturally leveling the primer on the surface of the substrate, then drying and curing at 220 ℃ for 5 minutes, and then naturally cooling;

s2, injecting 30 parts of unsaturated polyester resin, 20 parts of calcium carbonate powder, 3 parts of curing agent, 3 parts of accelerant, 2 parts of flame-retardant fiber, 10 parts of pigment particles and 5 parts of fluorescent particles into a container, and uniformly stirring for 20 minutes;

s3, installing a mold around the substrate for shaping the fabric;

s4, injecting the uniformly stirred mixture in the container into a mold with a substrate until the mold is filled with the substrate;

and S5, drying and curing for 15 minutes at the temperature of 180 ℃, and then demolding after drying and curing.

In this embodiment, through setting up a base plate by the preparation of PVC material, after the material that will thoughtlessly have fluorescent particle mixes, fix on the substrate surface through the mode of stoving solidification, form the marble line, accomplish the preparation of whole marble decorative board for the marble is lighter in the quality, and easy to assemble and transportation, and the fluorescent particle who thoughtlessly has in its surface fabric can make the marble decorative board can send fluorescence at night under the condition of no light, and is more smooth pleasing to the eye.

Example 2

The invention provides the following technical scheme: the marble decorative plate with the fluorescent particles comprises the following components in parts by weight:

bottom materials: a substrate;

fabric: 40 parts of unsaturated polyester resin, 25 parts of calcium carbonate powder, 5 parts of curing agent, 5 parts of accelerator, 10 parts of fluorescent particles and 5 parts of flame-retardant fiber.

Specifically, the substrate is a PP plate.

Specifically, the curing agent is benzoyl peroxide.

In particular, the accelerator is styrene.

Specifically, the flame-retardant fibers are glass fibers.

The manufacturing method of the marble decorative plate with the fluorescent particles comprises the following steps:

s1, firstly, blowing dust on the surface of the substrate, then spraying primer on the surface of the substrate, naturally leveling the primer on the surface of the substrate, then drying and curing at 230 ℃ for 10 minutes, and then naturally cooling;

s2, injecting 40 parts of unsaturated polyester resin, 25 parts of calcium carbonate powder, 5 parts of curing agent, 5 parts of accelerator, 5 parts of flame-retardant fiber, 20 parts of pigment particles and 10 parts of fluorescent particles into a container, and uniformly stirring for 25 minutes;

s3, installing a mold around the substrate for shaping the fabric;

s4, injecting the uniformly stirred mixture in the container into a mold with a substrate until the mold is filled with the substrate;

and S5, drying and curing at the temperature of 200 ℃ for 20 minutes, and then demolding after drying and curing.

In this embodiment, through setting up a base plate by the preparation of PP material, after the material that will thoughtlessly have fluorescent particle mixes, fix on the substrate surface through the mode of stoving solidification, form the marble line, accomplish the preparation of whole marble decorative board for the marble is lighter in the quality, and easy to assemble and transportation, and the fluorescent particle who thoughtlessly has in its surface fabric can make the marble decorative board can send fluorescence at night under the condition of no light, and is more smooth pleasing to the eye.

Example 3

The invention provides the following technical scheme: the marble decorative plate with the fluorescent particles comprises the following components in parts by weight:

bottom materials: a substrate;

fabric: 50 parts of unsaturated polyester resin, 30 parts of calcium carbonate powder, 7 parts of curing agent, 7 parts of accelerator, 15 parts of fluorescent particles and 8 parts of flame-retardant fiber.

Specifically, the substrate is an aluminum alloy substrate.

Specifically, the curing agent is benzoyl peroxide.

In particular, the accelerator is styrene.

Specifically, the flame-retardant fibers are ceramic fibers.

The manufacturing method of the marble decorative plate with the fluorescent particles comprises the following steps:

s1, firstly, blowing dust on the surface of the substrate, then spraying primer on the surface of the substrate, naturally leveling the primer on the surface of the substrate, then drying and curing at 240 ℃ for 20 minutes, and then naturally cooling;

s2, injecting 50 parts of unsaturated polyester resin, 30 parts of calcium carbonate powder, 7 parts of curing agent, 7 parts of accelerator, 8 parts of flame-retardant fiber, 30 parts of pigment particles and 15 parts of fluorescent particles into a container, and uniformly stirring for 30 minutes;

s3, installing a mold around the substrate for shaping the fabric;

s4, injecting the uniformly stirred mixture in the container into a mold with a substrate until the mold is filled with the substrate;

and S5, drying and curing at the temperature of 220 ℃ for 30 minutes, and then demolding after drying and curing.

In this embodiment, through setting up a base plate by the aluminum alloy preparation, after will thoughtlessly having fluorescent particle's material mixture, fix on the substrate surface through the mode of stoving solidification, form the marble line, accomplish the preparation of whole marble decorative board for the marble is lighter in the quality, easy to assemble and transportation, and thoughtlessly have fluorescent particle in its surface fabric, can make the marble decorative board can send fluorescence at night under the condition of no light, and is more smooth pleasing to the eye.

Finally, it should be noted that: although the present invention has been described in detail with reference to the foregoing embodiments, it will be apparent to those skilled in the art that changes may be made in the embodiments and/or equivalents thereof without departing from the spirit and scope of the invention. Any modification, equivalent replacement, or improvement made within the spirit and principle of the present invention should be included in the protection scope of the present invention.