阅读说明：本技术 一种瓷砖填缝工艺 (Tile joint filling process ) 是由 姚水平 于 2021-07-13 设计创作，主要内容包括：本发明提供了室内装修技术领域的一种瓷砖填缝工艺,根据瓷砖的颜色调节水性环保固化剂中的颜色,进而将纯水性环氧树脂与调色后的水性环保固化剂按比例混合,进行搅拌,静置后,形成混合物料；使用铲刀以及压缝工具将混合物料填入瓷砖与相邻陶砖之间的间隙中,使用压实工具将间隙中的混合物料压实,待混合物料凝固,使用不伤害瓷砖的打磨工具将凝固后混合物料进行打磨；在打磨后的混合物料表面上涂抹地砖防污蜡；通过本工艺使得砖表面不会出现雾状,避免了后期缝隙容易渗污、下陷的现象,使得瓷砖整体表面更平整,实现缝隙的颜色与瓷砖的颜色一致,采用地砖防污蜡,在瓷砖缝隙表面形成保护膜,达到不渗污的效果。(The invention provides a tile joint filling process in the technical field of interior decoration, which adjusts the color of a water-based environment-friendly curing agent according to the color of a tile, further mixes a pure water-based epoxy resin and the water-based environment-friendly curing agent after color adjustment according to a proportion, stirs, and stands to form a mixed material; filling the mixed material into a gap between the ceramic tile and the adjacent ceramic tile by using a scraper knife and a seam pressing tool, compacting the mixed material in the gap by using a compacting tool, and polishing the solidified mixed material by using a polishing tool which does not damage the ceramic tile after the mixed material is solidified; coating floor tile antifouling wax on the surface of the polished mixed material; through this technology make the brick surface can not appear vaporific, avoided the phenomenon that the later stage gap oozes dirty, subsides easily for the whole surface of ceramic tile is more level and more smooth, realizes that the colour in gap is unanimous with the colour of ceramic tile, adopts the antifouling wax of ceramic tile, forms the protection film on ceramic tile gap surface, reaches the effect of not oozing dirty.)

1. The tile joint filling process is characterized by comprising the following steps:

s1: adjusting the color of the aqueous environment-friendly curing agent according to the color of the ceramic tile;

s2: mixing pure water epoxy resin and the water-based environment-friendly curing agent after color matching according to a ratio, stirring, and standing to form a mixed material;

s3: and filling the mixed material into the gap between the ceramic tile and the adjacent ceramic tile by using a scraper knife and a seam pressing tool, compacting the mixed material in the gap by using a compacting tool, and waiting for the mixed material to solidify.

S4: polishing the solidified mixed material by using a polishing tool which does not damage the ceramic tile;

s5: and (3) coating floor tile antifouling wax on the surface of the polished mixed material.

2. A tile caulking process according to claim 1, wherein: the width of the splicing seam between any two adjacent ceramic tiles is less than or equal to 1 mm.

3. A tile caulking process according to claim 1, wherein: in the step S4, the polishing tool is a hair pad or a foam pad.

4. A tile caulking process according to claim 1, wherein: before S1, the method further includes the following steps: clear up two arbitrary adjacent ceramic tile splice joints obvious water stain that appears, use the joint cleaning instrument, clean the interior remaining tiny sediment of brickwork joint, guarantee that there is not the tiny sediment in the brickwork joint.

5. A tile caulking process according to claim 1, wherein in the step S1, the process further comprises the steps of: the organic pigment with the formula amount is gradually added into the water-based environment-friendly curing agent, and is compared with the color of the ceramic tile after being uniformly mixed until the color is consistent with the color of the ceramic tile.

6. A tile caulking process according to claim 1, wherein in the step S4, the process further comprises the steps of:

s41, grinding the joint seams between any two adjacent tiles in the S3 in a reciprocating way through a grinding tool;

s42, cleaning the polished tile joint in the step S41 to and fro through a cleaning tool to remove fine slag or scraps on the surface;

and S43, carrying out tile gap surface inspection on the tile gap cleaned in the step S42 until the filling material in the tile gap is level with the surface of the tile.

7. The tile caulking process according to claim 5, further comprising an organic wear-resistant material, wherein the aqueous environment-friendly curing agent, the organic wear-resistant material and the organic pigment form a mixture, and the mixture and the pure aqueous epoxy resin are in a ratio of 1: 9.

8. The tile caulking process according to claim 1, wherein in the step S42, the cleaning tool is a brush or/and a blower for cleaning fine slag.

Technical Field

The invention relates to the technical field of interior decoration, in particular to a tile joint filling process.

Background

The ceramic tile is common finishing material, when the ceramic tile was spread and is pasted, certain gap had all to leave directly for every ceramic tile, leaves certain gap reason between the ceramic tile firstly because ceramic tile, ceramic tile adhesive material, joint filling material etc. all have expend with heat and contract with cold the problem, at the in-process of temperature change, ceramic tile and relevant material all can have certain flexible, if do not leave the seam, can lead to the ceramic tile appear bulging or fracture at the in-process that uses in the later stage. Secondly, in the mechanized production process of the ceramic tile, errors may exist in the size, and if no seam is left, the seam is not flat when the ceramic tile is paved, so that the appearance of the ceramic tile is affected.

However, for gaps left between the tiles to be filled, the traditional tile caulking process has two types: the first is a common joint filling process using epoxy color sand, which is to fill the epoxy color sand into the gap directly by using a scraper, flatten the gap and clean the gap. This process has drawbacks: the seam is easy to be concave and the dirt is easy to be hidden in the later period. The oleoresin is easy to remain on the brick surface, is not easy to clean, and the brick surface is easy to have fog, thus affecting the beauty. Oleoresin is easily yellowed and blacked. Problems are generated in the later period, the maintenance and the management cannot be carried out, and only gap filling is carried out again; the second process is a seam beautifying process, wherein epoxy resin materials are used in the seam beautifying process, a special glue gun is used for beating the materials into a seam, then a spherical or arc scraper is used for flattening, and after solidification, redundant materials are cleaned. The disadvantage of this process is that the seam is difficult to flatten and is prone to unevenness.

Disclosure of Invention

In order to overcome the defects of the prior art, the invention provides a ceramic tile joint filling process, which has the following specific technical scheme:

a tile joint filling process comprises the following steps:

s1: adjusting the color of the aqueous environment-friendly curing agent according to the color of the ceramic tile;

s2: mixing pure water epoxy resin and the water-based environment-friendly curing agent after color matching according to a ratio, stirring, and standing to form a mixed material;

s3: and filling the mixed material into the gap between the ceramic tile and the adjacent ceramic tile by using a scraper knife and a seam pressing tool, compacting the mixed material in the gap by using a compacting tool, and waiting for the mixed material to solidify.

S4: polishing the solidified mixed material by using a polishing tool which does not damage the ceramic tile;

s5: and (3) coating floor tile antifouling wax on the surface of the polished mixed material.

Furthermore, the width of the splicing seam between any two adjacent ceramic tiles is less than or equal to 1 mm.

Further, in the step S4, the polishing tool is a hair pad or a foam pad.

Further, before S1, the method further includes the following steps: clear up two arbitrary adjacent ceramic tile splice joints obvious water stain that appears, use the joint cleaning instrument, clean the interior remaining tiny sediment of brickwork joint, guarantee that there is not the tiny sediment in the brickwork joint.

Further, the step S1 further includes the following steps: gradually adding the organic pigment into the water-based environment-friendly curing agent according to the formula amount, uniformly mixing, and comparing with the color of the ceramic tile until the color is consistent with the color of the ceramic tile;

further, the step S4 further includes the following steps:

s41, grinding the joint seams between any two adjacent tiles in the S3 in a reciprocating way through a grinding tool;

s42, cleaning the polished tile joint in the step S41 to and fro through a cleaning tool to remove fine slag or scraps on the surface;

s43, carrying out tile gap surface inspection on the tile gap cleaned in the S42 until the filling material at the tile gap is level to the surface of the tile;

the paint further comprises an organic wear-resistant material, wherein the aqueous environment-friendly curing agent, the organic wear-resistant material and the organic pigment form a mixture, and the ratio of the mixture to the pure aqueous epoxy resin is 1: 9.

Further, in step S42, the cleaning tool is a brush or/and a blower for cleaning the fine slag.

The beneficial technical effects obtained by the invention comprise:

an operator adjusts the color of the water-based environment-friendly curing agent according to the color of the ceramic tile, and then the pure water-based epoxy resin and the water-based environment-friendly curing agent after color adjustment are mixed in proportion, stirred and stood to form a mixed material; and filling the mixed material into the gap between the ceramic tile and the adjacent ceramic tile by using a scraper knife and a seam pressing tool, compacting the mixed material in the gap by using a compacting tool, and waiting for the mixed material to solidify. Polishing the solidified mixed material by using a polishing tool which does not damage the ceramic tile; coating floor tile antifouling wax on the surface of the polished mixed material; the pure water epoxy resin and the water-based environment-friendly curing agent are matched for use, so that the defect that the oil resin is easy to turn yellow and black under the attack of ultraviolet rays is overcome, and the defect that the traditional oil resin is easy to turn yellow and black is overcome. Simultaneously this material dissolves with the water, can not be at ceramic tile surface film forming, the brick surface has vaporificly easily promptly, the polishing instrument that uses not hindering the ceramic tile polishes the gap, avoided the later stage gap to ooze dirty easily, the phenomenon of sinking for the whole surface of ceramic tile is more level and smooth, through several kinds of colours in the colour even a ceramic tile to the material that fills a crack matches the ceramic tile, the colour that realizes the gap is unanimous with the colour of ceramic tile, let the whole effect of paving the subsides of ceramic tile reach similar "seamless" whole pleasing to the eye atmospheric effect. Adopt ceramic tile antifouling wax, form the protection film on ceramic tile gap surface, reach the effect that does not ooze dirty, but later maintenance simultaneously.

Drawings

The invention will be further understood from the following description in conjunction with the accompanying drawings. The components in the figures are not necessarily to scale, emphasis instead being placed upon illustrating the principles of the embodiments. Like reference numerals designate corresponding parts throughout the different views.

FIG. 1 is a schematic process flow diagram according to an embodiment of the present invention;

fig. 2 is a schematic view of a polishing process according to an embodiment of the present invention.

Detailed Description

In order to make the objects, technical solutions and advantages of the present invention more apparent, the present invention is further described in detail below with reference to embodiments thereof; it should be understood that the specific embodiments described herein are merely illustrative of the invention and are not intended to limit the invention. Other systems, methods, and/or features of the present embodiments will become apparent to those skilled in the art upon review of the following detailed description. It is intended that all such additional systems, methods, features and advantages be included within this description, be within the scope of the invention, and be protected by the accompanying claims. Additional features of the disclosed embodiments are described in, and will be apparent from, the detailed description that follows.

The same or similar reference numerals in the drawings of the embodiments of the present invention correspond to the same or similar components; in the description of the present invention, it should be understood that if there is an orientation or positional relationship indicated by the terms "upper", "lower", "left", "right", etc. based on the orientation or positional relationship shown in the drawings, it is only for convenience of describing the present invention and simplifying the description, but it is not intended to indicate or imply that the device or component referred to must have a specific orientation, be constructed in a specific orientation, and be operated, and therefore, the terms describing the positional relationship in the drawings are only used for illustrative purposes and are not to be construed as limiting the present patent, and the specific meaning of the terms described above will be understood by those of ordinary skill in the art according to the specific circumstances.

A tile joint filling process comprises the following steps:

s1: adjusting the color of the aqueous environment-friendly curing agent according to the color of the ceramic tile;

s2: mixing pure water epoxy resin and the water-based environment-friendly curing agent after color matching according to a ratio, stirring, and standing to form a mixed material;

s3: and filling the mixed material into the gap between the ceramic tile and the adjacent ceramic tile by using a scraper knife and a seam pressing tool, compacting the mixed material in the gap by using a compacting tool, and waiting for the mixed material to solidify.

S4: polishing the solidified mixed material by using a polishing tool which does not damage the ceramic tile;

s5: and (3) coating floor tile antifouling wax on the surface of the polished mixed material.

Specifically, as shown in fig. 1, an operator adjusts the color of the waterborne environment-friendly curing agent according to the color of the tile, and then mixes the purely waterborne epoxy resin and the toned waterborne environment-friendly curing agent in proportion, stirs the mixture, and stands the mixture to form a mixed material; and filling the mixed material into the gap between the ceramic tile and the adjacent ceramic tile by using a scraper knife and a seam pressing tool, compacting the mixed material in the gap by using a compacting tool, and waiting for the mixed material to solidify. Polishing the solidified mixed material by using a polishing tool which does not damage the ceramic tile; coating floor tile antifouling wax on the surface of the polished mixed material; the pure water epoxy resin and the water-based environment-friendly curing agent are matched for use, so that the defect that the oil resin is easy to turn yellow and black under the attack of ultraviolet rays is overcome, and the defect that the traditional oil resin is easy to turn yellow and black is overcome. Simultaneously this material dissolves with the water, can not be at ceramic tile surface film forming, the brick surface has vaporific grinding tool who does not hinder the ceramic tile of use to polish the gap easily promptly, avoided the phenomenon that the later stage gap oozes dirty, subsides easily for ceramic tile overall surface is more level and smooth, through several kinds of colours in the colour even a ceramic tile to the material that fills a crack matching ceramic tile, realizes that the colour in gap is unanimous with the colour of ceramic tile, lets the whole effect of paving the subsides of ceramic tile reach similar "seamless" whole pleasing to the eye atmospheric effect. Adopt ceramic tile antifouling wax, form the protection film on ceramic tile gap surface, reach the effect that does not ooze dirty, but later maintenance simultaneously.

Further, operating personnel is spreading arbitrary adjacent two concatenation seam width between the ceramic tile is less than or equal to 1mm for reach approximate seamless concatenation effect between the two adjacent ceramic tiles, can effectively promote the wholeness effect of fitment simultaneously, and adjacent two concatenation seam width between the ceramic tile is little can reduce the use amount of mixing material, and the cost is lower, it is more convenient to spread.

Further, in step S4, the polishing tool is a bristle pad or a foam pad, the bristle pad is a cleaning, polishing and waxing pad, and the main component of the polishing pad is made of natural animal bristles and fibers, and the polishing pad is mixed with high content of natural animal bristles fibers, so that the polishing effect is good and the polishing pad is also suitable for polishing the smooth surface of the hard floor with high efficiency.

In one embodiment, before S1, the method further includes the following steps: clear up arbitrary adjacent two the obvious water mark that the ceramic tile splice joint appears, use the joint cleaning instrument, the interior remaining tiny sediment of clean brick joint guarantees not have the tiny sediment in the brick joint, avoids water mark and tiny sediment to influence the adhesive strength of pure water nature epoxy and the waterborne environmental protection curing agent after mixing colors.

Further, the step S1 further includes the following steps: the organic pigment with the formula amount is gradually added into the water-based environment-friendly curing agent, and is compared with the color of the ceramic tile after being uniformly mixed until the color is consistent with the color of the ceramic tile, and the blended color can be compared with the color of the ceramic tile gradually;

further, the step S4 further includes the following steps:

s41, grinding the joint seams between any two adjacent tiles in the S3 in a reciprocating way through a grinding tool;

s42, cleaning the polished tile joint in the step S41 to and fro through a cleaning tool to remove fine slag or scraps on the surface;

s43, carrying out tile gap surface inspection on the tile gap cleaned in the S42 until the filling material at the tile gap is level to the surface of the tile;

specifically, the joint seam between any two adjacent ceramic tiles in the step S3 is polished back and forth by a polishing tool; cleaning the polished tile splicing seams in a reciprocating manner by a cleaning tool to remove fine slag or scraps on the surfaces; after cleaning, carrying out tile gap surface inspection on the tile gap until the filling material at the tile gap is level to the tile surface; through the rotatory operation of polishing of reciprocating translation of circulation to the smooth effect in filler material surface cleans and the surface inspection to the ceramic tile clearance simultaneously, and the filler material of guarantee ceramic tile clearance department is flat mutually with the ceramic tile surface.

In one embodiment, the ceramic tile filler further comprises an organic wear-resistant material, the aqueous environment-friendly curing agent, the organic wear-resistant material and the organic pigment form a mixture, the mixture and the pure water epoxy resin are in a ratio of 1:9, the mixture is reasonable in ratio, the pure water epoxy resin is guaranteed, the cost is low, the organic wear-resistant material can greatly reduce wear in daily life, and the service life of the filler in the gaps of the ceramic tiles is further prolonged.

Furthermore, in step S42, the cleaning tool is a brush or/and a blower for cleaning the fine slag, the brush or/and the blower has good operability, flexibility, convenience and low cost, and the blower can be configured to blow the brick joints or the brush and the blower are used in cooperation.

Although the invention has been described above with reference to various embodiments, it should be understood that many changes and modifications may be made without departing from the scope of the invention. That is, the methods, systems, and devices discussed above are examples. Various configurations may omit, substitute, or add various procedures or components as appropriate. For example, in alternative configurations, the methods may be performed in an order different than that described, and/or various components may be added, omitted, and/or combined. Moreover, features described with respect to certain configurations may be combined in various other configurations, as different aspects and elements of the configurations may be combined in a similar manner. Further, elements therein may be updated as technology evolves, i.e., many elements are examples and do not limit the scope of the disclosure or claims.

Specific details are given in the description to provide a thorough understanding of the exemplary configurations including implementations. However, configurations may be practiced without these specific details, e.g., well-known circuits, processes, algorithms, structures, and techniques have been shown without unnecessary detail in order to avoid obscuring the configurations. This description provides example configurations only, and does not limit the scope, applicability, or configuration of the claims. Rather, the foregoing description of the configurations will provide those skilled in the art with an enabling description for implementing the described techniques. Various changes may be made in the function and arrangement of elements without departing from the spirit or scope of the disclosure.

In sum, it is intended that the foregoing detailed description be regarded as illustrative rather than limiting, and that it be understood that it defines the spirit and scope of the invention. The above examples are to be construed as merely illustrative and not limitative of the remainder of the disclosure. After reading the description of the invention, the skilled person can make various changes or modifications to the invention, and these equivalent changes and modifications also fall into the scope of the invention defined by the claims.