阅读说明：本技术 一种具有耐洗防污功能的墙布的生产工艺 (Production process of wall cloth with washing-resistant and antifouling functions ) 是由 王玉霞 王国民 于 2020-06-17 设计创作，主要内容包括：本发明公开了一种具有耐洗防污功能的墙布的生产工艺,包括以下步骤：步骤1：布层的选料,所述布层选用棉布、麻布、热轧布、无纺布的一种或者多种,步骤2：胶层的选取,所述胶层选用热熔胶涂层,所述具体为植物胶和PA胶的混合涂抹,步骤3：功能层的取用,所述功能层即通过对布料进行不同的处理来获得相应的效果,所述功能层包括杀菌层、耐洗层、防污层和防腐层,步骤4：杀菌层的制备,所述将布料放置调配好的杀菌溶液中浸轧处理,然后将布料取出恒温烘干,步骤5：耐洗层的制备,所述将布料放置调配好的耐洗溶液中浸轧处理,然后将布料取出恒温烘干。(The invention discloses a production process of wall cloth with washing and fouling resistant functions, which comprises the following steps: step 1: selecting materials for a cloth layer, wherein the cloth layer is selected from one or more of cotton cloth, linen, hot-rolled cloth and non-woven cloth, and the step 2: selecting a glue layer, wherein the glue layer is a hot melt adhesive coating, specifically, the mixture of the plant glue and the PA glue is smeared, and the step 3 is as follows: taking a functional layer, wherein the functional layer obtains corresponding effects by performing different treatments on cloth, the functional layer comprises a sterilization layer, a washable layer, an antifouling layer and an anticorrosive layer, and the step 4: preparing a sterilization layer, namely placing the cloth in a prepared sterilization solution for padding treatment, then taking out the cloth and drying at a constant temperature, and step 5: and (3) preparing the washable layer, namely placing the cloth in a prepared washable solution for padding treatment, and then taking out the cloth and drying at a constant temperature.)

1. A production process of wall cloth with washing resistance and antifouling functions is characterized by comprising the following steps: step 1: selecting materials for a cloth layer, wherein the cloth layer is selected from one or more of cotton cloth, linen, hot-rolled cloth and non-woven cloth.

Step 2: the method comprises the following steps of selecting an adhesive layer, selecting a hot melt adhesive coating for the adhesive layer, and specifically coating a mixture of plant glue and PA glue.

And step 3: and taking the functional layer, wherein the functional layer obtains corresponding effects by performing different treatments on the cloth, and the functional layer comprises a sterilizing layer, a washable layer, an antifouling layer and an anticorrosive layer.

And 4, step 4: and (3) preparing a sterilization layer, namely placing the cloth in the prepared sterilization solution for padding treatment, and then taking out the cloth and drying at a constant temperature.

And 5: and (3) preparing the washable layer, namely placing the cloth in a prepared washable solution for padding treatment, and then taking out the cloth and drying at a constant temperature.

Step 6: and preparing an antifouling layer, namely placing the cloth in a prepared antifouling solution for padding treatment, and then taking out the cloth and drying at a constant temperature.

And 7: and (3) preparing an anticorrosive layer, namely placing the cloth in a prepared anticorrosive solution for padding treatment, and then taking out the cloth and drying at a constant temperature.

And 8: preheating treatment, namely preheating the cloth layer at a low temperature by heating equipment such as a heating pipe and the like which are common in the known technology, wherein the temperature is controlled at 35-45 ℃, and the heating time is 15-25 seconds.

And step 9: and printing decoration, wherein patterns are edited through a computer and are transmitted to a printer, and then the printer prints the patterns on the corresponding cloth areas of the cloth layer.

Step 10: and (3) drying and fixing color, wherein the cloth layer is dried and fixed through heating pipes and other common heating equipment in the known technology, the temperature is controlled to be 55-65 ℃, and the heating time is 60-85 seconds.

Step 11: and (3) compounding the wall cloth, namely compounding the cloth layer, the adhesive layer and the functional layer together to finish the production and the manufacture of the wall cloth.

2. The production process of the wall cloth with the washing and stain resistant functions according to claim 1, wherein in the step 2, 2 parts of the plant glue and 5 parts to 8 parts of the PA glue are sprayed, and the plant glue is sprayed on the PA glue by a paint spray gun.

3. The process for producing wall cloth with washing and fouling resistant functions according to claim 1, wherein in the step 4, 32-52 parts of deionized water is mixed with 11-31 parts of zinc pyrithione, and the selected cloth is soaked for 1-3 hours.

4. The process for producing wall cloth with washing and dirt resisting functions as claimed in claim 1, wherein in the step 5, 32-52 parts of deionized water is mixed with 24-44 parts of acrylic resin, and the selected cloth is soaked for 1-3 hours.

5. The process for producing wall cloth with washing and fouling resistant functions as claimed in claim 1, wherein in the step 6, 32-52 parts of deionized water and 12-32 parts of polyacrylamide are mixed, and the selected cloth is soaked for 1-3 hours.

6. The production process of the wall cloth with the washing and stain resistant functions as claimed in claim 1, wherein in the step 7, 32-52 parts of deionized water and 15-35 parts of aluminum acetate are mixed, and the selected cloth is soaked for 1-3 hours.

7. The process for producing wall cloth with washing and dirt resistance functions as claimed in claim 1, wherein the step 11 is to place the cloth layer on the uppermost layer, the glue layer on the lowermost layer, and the functional layer between the cloth layer and the glue layer.

Technical Field

The invention relates to the technical field of wall cloth production, in particular to a production process of wall cloth with washing resistance and antifouling functions.

Background

When a room is decorated, people often use wallpaper to paste the wall surface, because the wallpaper has the characteristics of various colors, rich patterns, luxury and splendid style, safety, environmental protection, convenient construction, proper price and the like which are incomparable with various other interior decoration materials. However, as the living standard of people is improved and the people continuously pursue high-quality life, the defects of the wallpaper gradually appear. Wall paper is mostly used to replace wallpaper nowadays, and compared with the wallpaper, the wall paper is thicker and more solid, and various patterns and styles can be manufactured.

However, the wall cloth is inevitably collided with the wall in daily life, so that the wall cloth is easily polluted, is stained with a plurality of stains or is doodled by children, but the wall cloth is easily damaged in the process of cleaning or scrubbing by using wet rags, so that the wall cloth which is washable and antifouling is required to meet the requirement of daily life.

Disclosure of Invention

Technical problem to be solved

Aiming at the defects of the prior art, the invention provides a production process of wall cloth with washing resistance and antifouling functions, which has the functions of washing resistance and stain resistance, can keep the wall cloth clean and provides a warm and clean living environment for people.

(II) technical scheme

In order to realize the antibacterial aim, the invention provides the following technical scheme: a production process of wall cloth with washing-resistant and antifouling functions comprises the following steps: step 1: selecting materials for a cloth layer, wherein the cloth layer is selected from one or more of cotton cloth, linen, hot-rolled cloth and non-woven cloth.

Step 2: the method comprises the following steps of selecting an adhesive layer, selecting a hot melt adhesive coating for the adhesive layer, and specifically coating a mixture of plant glue and PA glue.

And step 3: and taking the functional layer, wherein the functional layer obtains corresponding effects by performing different treatments on the cloth, and the functional layer comprises a sterilizing layer, a washable layer, an antifouling layer and an anticorrosive layer.

And 4, step 4: and (3) preparing a sterilization layer, namely placing the cloth in the prepared sterilization solution for padding treatment, and then taking out the cloth and drying at a constant temperature.

And 5: and (3) preparing the washable layer, namely placing the cloth in a prepared washable solution for padding treatment, and then taking out the cloth and drying at a constant temperature.

Step 6: and preparing an antifouling layer, namely placing the cloth in a prepared antifouling solution for padding treatment, and then taking out the cloth and drying at a constant temperature.

And 7: and (3) preparing an anticorrosive layer, namely placing the cloth in a prepared anticorrosive solution for padding treatment, and then taking out the cloth and drying at a constant temperature.

And 8: preheating treatment, namely preheating the cloth layer at a low temperature by heating equipment such as a heating pipe and the like which are common in the known technology, wherein the temperature is controlled at 35-45 ℃, and the heating time is 15-25 seconds.

And step 9: and printing decoration, wherein patterns are edited through a computer and are transmitted to a printer, and then the printer prints the patterns on the corresponding cloth areas of the cloth layer.

Step 10: and (3) drying and fixing color, wherein the cloth layer is dried and fixed through heating pipes and other common heating equipment in the known technology, the temperature is controlled to be 55-65 ℃, and the heating time is 60-85 seconds.

Step 11: and (3) compounding the wall cloth, namely compounding the cloth layer, the adhesive layer and the functional layer together to finish the production and the manufacture of the wall cloth.

Preferably, in the step 2, 2-5 parts of the plant gum and 5-8 parts of the PA gum are sprayed, and then the plant gum is sprayed on the PA gum through a coating spray gun.

Preferably, in the step 4, 32-52 parts of deionized water and 11-31 parts of zinc pyrithione are mixed, and the selected cloth is soaked for 1-3 hours.

Preferably, in the step 5, 32-52 parts of deionized water and 24-44 parts of acrylic resin are mixed, and the selected cloth is soaked for 1-3 hours.

Preferably, in the step 6, 32-52 parts of deionized water and 12-32 parts of polyacrylamide are mixed, and the selected cloth is soaked for 1-3 hours.

Preferably, in the step 7, 32-52 parts of deionized water and 15-35 parts of aluminum acetate are mixed, and the selected cloth is soaked for 1-3 hours.

Preferably, step 11 is to place the cloth layer on the uppermost layer, the glue layer on the lowermost layer, and the functional layer between the cloth layer and the glue layer.

The invention has the beneficial effects that:

compared with the prior art, the invention provides a production process of wall cloth with washing resistance and antifouling functions, which has the following beneficial effects:

the production process of the wall cloth with the washing and dirt preventing functions can reduce the degree of pollution of the wall cloth by stains and doodles to a certain degree, reduce the labor intensity of cleaning of a user, meet various cleaning operations of the wall cloth, prevent the surface or the interior of the wall cloth from being damaged, and simultaneously prevent the service life of the wall cloth from being influenced; the wall cloth can absorb and eliminate bacteria in the air, improve the air quality and safety, meet the requirement of health of children in families, and simultaneously accompany and protect the growth of the health and safety of the children; the wall cloth also has stronger corrosion resistance, can resist corrosive substances generated by various products with lighter corrosivity in daily life, and prolongs the service life of the wall cloth; the wall cloth can also edit favorite patterns through a computer and print the favorite patterns on the wall cloth, so that a satisfied, comfortable and reassuring life environment is created for a user.

Detailed Description

The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.