阅读说明：本技术 一种粉煤灰渣砂浆及其制备方法 (Fly ash mortar and preparation method thereof ) 是由 周美茹 赵庆新 田宇 杨泽政 刘学智 王力伟 张卉 于 2020-06-19 设计创作，主要内容包括：本发明公开了一种粉煤灰渣砂浆及其制备方法,涉及混凝土技术领域技术领域。所述粉煤灰渣砂浆包括：按照质量比计,10％～15％的水、20％～25％的水泥、25％～40％的粉煤灰渣以及25％～40％的河砂。本发明通过采用粉煤灰渣替代天然河砂,抗压强度基本不变,抗折强度提升,抗碳化性能改良,收缩性能基本不变。在利用固体废弃物的同时,节约了天然河砂资源,能带来较大的经济效益。(The invention discloses fly ash mortar and a preparation method thereof, and relates to the technical field of concrete. The fly ash mortar comprises: according to the mass ratio, 10-15% of water, 20-25% of cement, 25-40% of fly ash slag and 25-40% of river sand. The invention adopts fly ash slag to replace natural river sand, so that the compressive strength is basically unchanged, the breaking strength is improved, the carbonization resistance is improved, and the shrinkage performance is basically unchanged. The solid waste is utilized, and meanwhile, the natural river sand resource is saved, and great economic benefit can be brought.)

1. A fly ash mortar, characterized by comprising: according to the mass ratio, 10-15% of water, 20-25% of cement, 25-40% of fly ash slag and 25-40% of river sand.

2. The fly ash mortar of claim 1, wherein the fly ash mortar comprises: the cement mortar comprises, by mass, 12% of water, 24% of cement, 28% of fly ash and 36% of river sand.

3. The flyash mortar of claim 1, wherein said flyash particles have a diameter of less than 2.36 mm.

4. The flyash mortar of claim 1, wherein said flyash is pre-wetted flyash by mass ratio.

5. The fly ash mortar of claim 1, wherein the fly ash is pretreated with 24 hours or more of foaming water.

6. The fly ash mortar according to claim 4, wherein the moisture content of the wet fly ash is 30 to 45%.

7. The fly ash mortar of claim 5, wherein the water content of the pretreated fly ash is controlled to be 30-45% by water control treatment after the soaking pretreatment.

8. The method for preparing the fly ash mortar according to any one of claims 1 to 7, wherein the method comprises the following steps:

sieving the fly ash, and selecting the particle size of below 2.36 mm;

pre-wetting fly ash, and soaking in water for more than or equal to 24 hours;

controlling water of the wet fly ash to reach saturation surface dryness, wherein the water content is 30-45%;

adding cement, sand and dry powdered coal ash of saturated surface into a stirrer, stirring, adding water while stirring, stirring for 2 min after adding water, and molding.

Technical Field

The invention relates to the technical field of mortar, in particular to fly ash mortar and a preparation method thereof.

Background

With the advancement of urbanization process, the building level is continuously improved, and the requirement on mortar is increasingly strict. The natural river sand is in high demand because of its excellent physical properties. Nowadays, the total amount of natural river sand consumed in the infrastructure of China every year is greatly increased, and the phenomenon of illegal exploitation of river sand occurs occasionally, which leads to the problems that building materials are gradually deficient in the near future and the like in China, and the search for fine aggregate for replacing natural river sand is urgent. With the increasing awareness of the protection and rational utilization of natural resources, society has come to pay attention to the protection of non-renewable resources, and has begun to research industrial wastes, particularly harmless solid wastes, that can replace non-renewable resources. The storage of the fly ash is huge, the stacking is particularly wasted, and the environmental problem is also generated. If the method is applied to the building industry, the waste can be changed into valuable, the environmental pressure is relieved, and the building cost is reduced.

In addition, the green water mountain is the Jinshan Yinshan. The environmental problem is more and more concerned by people, and the great use of the fly ash can greatly relieve the environmental pressure and solve a part of environmental problems. Therefore, the fly ash replaces the natural river sand, thereby achieving two purposes.

At present, the utilization rate of fly ash is not high in China, and the utilization rate of fly ash residue is lower. A method is urgently needed to be developed, which uses a great amount of fly ash to improve the utilization rate of the fly ash.

Disclosure of Invention

The invention aims to provide fly ash mortar and a preparation method thereof, which aim to solve the problems in the background technology.

In order to achieve the purpose, the invention provides the following technical scheme:

in one aspect, there is provided a fly ash mortar comprising: according to the mass ratio, 10-15% of water, 20-25% of cement, 25-40% of fly ash slag and 25-40% of river sand.

Preferably, the fly ash mortar comprises: the cement mortar comprises, by mass, 12% of water, 24% of cement, 28% of fly ash and 36% of river sand.

Preferably, the particle diameter of the fly ash is less than 2.36 mm.

Preferably, the fly ash is wet fly ash by mass ratio.

Preferably, the fly ash is pretreated by using foaming water for more than 24 hours.

Preferably, the water control treatment of the fly ash slag after the water soaking pretreatment is carried out, and the water content is controlled to be 30-45%

Preferably, the moisture content of the wet pulverized coal ash is 30-45%.

On the other hand, the preparation method of the fly ash mortar comprises the following steps:

sieving the fly ash, and selecting the particle size of below 2.36 mm;

pre-wetting fly ash, and soaking in water for more than or equal to 24 hours;

controlling water of the wet fly ash to reach saturation surface dryness, wherein the water content is 30-45%;

adding cement, sand and dry powdered coal ash of saturated surface into a stirrer, stirring, adding water while stirring, stirring for 2 min after adding water, and molding.

Compared with the prior art, the invention has the beneficial effects that:

the invention adopts fly ash slag to replace natural river sand, improves the fluidity of the mortar, basically keeps the compressive strength unchanged, improves the breaking strength, improves the carbonization resistance and basically keeps the shrinkage performance unchanged. The solid waste is utilized, and meanwhile, the natural river sand resource is saved, and great economic benefit can be brought.

Drawings

FIG. 1 shows the concrete compressive strength of 28d under different replacement rates of fly ash;

FIG. 2 shows the flexural strength of concrete 28d under different replacement rates of fly ash;

FIG. 3 shows the concrete 28d carbonization depth under different replacement rates of fly ash;

FIG. 4 shows concrete shrinkage at different replacement rates of fly ash;

FIG. 5 is a comparison of intensity;

fig. 6 is a shrinkage comparison.

Detailed Description

In order to enhance the understanding of the present invention, the present invention will be further described with reference to the following examples, which are only for the purpose of illustrating the present invention and are not to be construed as limiting the scope of the present invention.

An embodiment of the present invention provides, in one aspect, a fly ash mortar, including: according to the mass ratio, 10-15% of water, 20-25% of cement, 25-40% of fly ash slag and 25-40% of river sand.

The above embodiment uses fly ash instead of fine aggregate; the utilization rate of the fly ash can be greatly improved; waste utilization and environmental improvement; the workability and mechanical property of the concrete are improved; greatly reduces the cost of the mortar and brings great economic benefit.

In one embodiment, the fly ash mortar comprises: the cement mortar comprises, by mass, 12% of water, 24% of cement, 28% of fly ash and 36% of river sand.

In one embodiment, the fly ash is less than 2.36mm in particle diameter.

In one embodiment, the fly ash is wet fly ash by mass.

In one embodiment, the fly ash is pretreated by using foaming water for more than 24 hours.

In one embodiment, the water content of the pulverized coal ash after the water soaking pretreatment is controlled to be 30-45%, and in one embodiment, the water content of the wet pulverized coal ash is 30-45%.

On the other hand, the preparation method of the fly ash mortar comprises the following steps: sieving the fly ash, and selecting the particle size of below 2.36 mm;

pre-wetting fly ash, and soaking in water for more than or equal to 24 hours;

controlling water of the wet fly ash to reach saturation surface dryness, wherein the water content is 30-45%;

adding cement, sand and dry powdered coal ash of saturated surface into a stirrer, stirring, adding water while stirring, stirring for 2 min after adding water, and molding.

The following is a detailed description of the specific examples: