阅读说明：本技术 一种烫金箔工艺画的制作方法及工艺画 (Manufacturing method of gilding foil craft picture and craft picture ) 是由 吕光迪 邹俊 万宇鹏 舒国锋 于 2020-06-17 设计创作，主要内容包括：本发明公开了一种烫金箔工艺画的制作方法,包括采用激光打印机在纸张上打印出所需内容,得到待烫金画坯；在热裱覆膜机的装载杆上装入金箔纸卷；开启热裱覆膜机,将热裱覆膜机的加热滚轴加热至设定温度,然后将所述画坯打印面与金箔纸反面相对,送入加热滚轴进行加热的同时金箔纸被压实粘贴在打印内容区域,烫制过程完成；所述设定温度满足将画坯打印内容区域的墨粉加热至具有粘性；待画坯整体烫制完成后,自然冷却,揭下未与纸张粘贴的金箔纸,纸张打印内容区域完全被金箔覆盖,烫金工艺完成,得到金箔画。本发明利用激光打印机打印出的内容区域高温加热后具有粘性的新用途,整个过程无需使用胶水,亦无需制模,实现定制化生产。(The invention discloses a method for manufacturing a gold stamping foil craft picture, which comprises the steps of printing required contents on paper by a laser printer to obtain a picture blank to be subjected to gold stamping; loading a gold foil paper roll on a loading rod of a hot mounting laminating machine; starting a hot mounting film laminating machine, heating a heating roller of the hot mounting film laminating machine to a set temperature, then enabling the printing surface of the picture blank to be opposite to the reverse side of the gold foil paper, feeding the picture blank into the heating roller for heating, compacting and sticking the gold foil paper to a printing content area, and finishing the ironing process; the set temperature is satisfied with the condition that the ink powder in the printing content area of the picture blank is heated to have viscosity; and after the whole painting blank is completely ironed, naturally cooling, removing the gold foil paper which is not adhered to the paper, completely covering the printing content area of the paper by the gold foil, and finishing the gold stamping process to obtain the gold foil painting. The invention has the new use of viscosity after high-temperature heating of the content area printed by the laser printer, does not need glue or mold making in the whole process, and realizes customized production.)

1. The manufacturing method of the gilt foil craft picture is characterized in that: the method comprises the following steps:

s01, printing required contents on paper by using a laser printer to obtain a blank of the picture to be gilded;

s02, heating the picture blank to be gilded until the printing content is molten to be colloidal, covering gold foil paper for compacting, and finishing the gilding process;

s03, after the whole blank to be drawn is completely ironed, naturally cooling, removing the gold foil paper which is not adhered to the paper, completely covering the printed content area of the paper with the gold foil, and finishing the gold stamping process to obtain the gold foil picture.

2. The manufacturing method of the bronzing foil craft picture according to claim 1, characterized in that: the step S02 specifically includes: loading a gold foil paper roll on a loading rod of a hot mounting laminating machine; then starting a hot mounting film laminating machine, heating a heating roller of the hot mounting film laminating machine to a set temperature, then enabling the printing surface of the picture blank to be opposite to the reverse side of the gold foil paper, feeding the picture blank into the heating roller for heating, compacting and sticking the gold foil paper to a printing content area, and finishing the ironing process; the set temperature is satisfied with the condition that the toner in the printing content area of the picture blank is heated to have viscosity.

3. The manufacturing method of the bronzing foil craft picture according to the claim 1 or 2, characterized in that: the paper in the step S01 is coated paper, paperboard, or ordinary office paper.

4. The manufacturing method of the bronzing foil craft picture according to the claim 1 or 2, characterized in that: further comprises a repairing process: when the gold foil paper which is not adhered to the paper is removed, the gold foil is found to be adhered in the printing content area and is not firmly adhered or adhered, and the steps S01-S03 are repeated.

5. The manufacturing method of the bronzing foil craft picture according to the claim 1 or 2, characterized in that: still include the mounting process: mounting the gold foil picture in the picture frame to form the complete craft picture.

6. The manufacturing method of the bronzing foil craft picture according to claim 2, characterized in that: in the step S02, the set temperature is 170 to 200 ℃.

7. The manufacturing method of the bronzing foil craft picture according to claim 6, characterized in that: in step S02, the set temperature is 180 ℃.

8. The manufacturing method of the bronzing foil craft picture according to the claim 1 or 2, characterized in that: in step S03, the cooling time is not less than 2 minutes.

Technical Field

The invention relates to the technical field of craft picture manufacturing, in particular to a manufacturing method of a gold stamping foil craft picture and the craft picture.

Background

The gold foil decorative picture is always a traditional decorative color element, and the existing gold foil picture has two main realization modes, one mode is to glue and paste gold foil manually, and the other mode is to use a copper plate to mold firstly, and then use special gold stamping equipment to fixedly stamp gold foil patterns. The above processes all have corresponding defects and shortcomings: the manual gluing and pasting forming efficiency is extremely low, and the requirement on the proficiency of an operator is high; the mold making and opening cost of the copper plate is high, and the hot stamping foil is only suitable for LOGO or patterns which are large in batch, have the same specification and are small in area under the same material, and is not suitable for individual requirements on family decoration.

With the development of society, people gradually form individual aesthetics on the basis of mass aesthetics. The traditional discordant style of the gilding art painting cannot meet the aesthetic requirements of users. How to rapidly manufacture a customized gold foil artistic picture which can be rapidly produced in small batch is an important factor occupying the market of the gold foil artistic picture.

Disclosure of Invention

The invention aims to solve the technical problem of how to quickly and efficiently manufacture personalized gold foil pictures in small batch.

The invention solves the technical problems through the following technical means:

the manufacturing method of the gold stamping foil craft picture comprises the following steps:

s01, printing required contents on paper by using a laser printer to obtain a blank of the picture to be gilded;

s02, heating the picture blank to be gilded until the printing content is molten to be colloidal, covering gold foil paper for compacting, and finishing the gilding process;

s03, after the whole blank to be drawn is completely ironed, naturally cooling, removing the gold foil paper which is not adhered to the paper, completely covering the printed content area of the paper with the gold foil, and finishing the gold stamping process to obtain the gold foil picture.

Preferably, the step S02 specifically includes: loading a gold foil paper roll on a loading rod of a hot mounting laminating machine; then starting a hot mounting film laminating machine, heating a heating roller of the hot mounting film laminating machine to a set temperature, then enabling the printing surface of the picture blank to be opposite to the reverse side of the gold foil paper, feeding the picture blank into the heating roller for heating, compacting and sticking the gold foil paper to a printing content area, and finishing the ironing process; the set temperature is satisfied with the condition that the toner in the printing content area of the picture blank is heated to have viscosity.

Preferably, the paper in step S01 is coated paper, cardboard, or general office paper.

Preferably, the method further comprises a repairing process: when the gold foil paper which is not adhered to the paper is removed, the gold foil is found to be adhered in the printing content area and is not firmly adhered or adhered, and the steps S01-S03 are repeated.

Preferably, the method also comprises a mounting process: mounting the gold foil picture in the picture frame to form the complete craft picture.

Preferably, in step S02, the set temperature is 170 to 200 ℃.

Preferably, in step S02, the set temperature is 180 ℃.

Preferably, in step S03, the cooling time is not less than 2 minutes.

The invention has the advantages that:

the invention provides a low-cost manufacturing method of a gold foil picture, which has the new sticky purpose after high-temperature heating of a content area printed by a laser printer, does not need glue or a mold in the whole process, can select gold foil paper with different colors according to the requirements of customers, and can produce the created gold foil picture by single step.

The components of the ink powder matched with the laser printer mainly comprise bonding resin, carbon black, a charge control agent, an external additive and the like. Wherein the function of the bonding resin is mainly used for a fixing link in the printing process. At high temperatures, the binder resin melts to become tacky, thereby adhering the other components of the toner to the paper, causing the image to solidify. This is a well known use of laser printers today. However, in the embodiment, after the content area printed by the laser printer is heated for the second time, the adhesive resin originally adhered to the paper is melted again to have the new purpose of adhering the gold foil, so that the production requirement of the current personalized customization is met, one-piece production is realized, the cost is low, and the method is a subversive revolution of the gold stamping process.

Detailed Description

In order to make the objects, technical solutions and advantages of the embodiments of the present invention clearer, the technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are some embodiments of the present invention, but not all embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.