阅读说明：本技术 一种防锈剂组合物 (Antirust agent composition ) 是由 李团乐 王俊明 周旭光 于 2019-02-19 设计创作，主要内容包括：本发明涉及一种防锈剂组合物,其特征在于,以总重量百分比计,由下列原料制成：基础油5％～30％、有机羧酸类防锈剂30％～90％、如式(I)所示的双子咪唑啉衍生物5％～40％,式(I)中R1、R2均为C10～C21的直连或支链烃基。本发明的防锈剂组合物油溶性好,加剂量小,防锈性能优异,酸值低,抗乳化性好,可用于调配各种类型的工业润滑油品和防锈油脂。<Image he="425" wi="700" file="DDA0001972386720000011.GIF" imgContent="drawing" imgFormat="GIF" orientation="portrait" inline="no"></Image>。(The invention relates to an antirust agent composition which is characterized by being prepared from the following raw materials in percentage by weight: 5-30% of base oil, 30-90% of organic carboxylic acid antirust agent and 5-40% of gemini imidazoline derivative shown as formula (I), wherein R1 and R2 in the formula (I) are both C10-C21 straight-chain or branched-chain alkyl. The antirust agent composition has the advantages of good oil solubility, small dosage, excellent antirust performance, low acid value and good anti-emulsifying property, and can be used for preparing various industrial lubricating oil products and antirust grease.)

一种防锈剂组合物

技术领域

本发明涉及一种防锈剂组合物，属于防锈剂技术领域。

背景技术

金属腐蚀不仅造成金属材料的损耗，而且由于金属构件的损坏造成的间接损失更大，是导致生产停运和环境污染的主要原因之一。在各种防护方法中，缓蚀剂技术具有良好的效果和较高的经济效益，已成为防腐蚀技术中最重要的方法之一。目前应用最为广泛的油溶性防锈剂为有机羧酸类防锈剂，但是此类防锈剂酸值高，不适用于要求低酸值的工况中。同时由于分子极性强，在用于有水的工况中时，水的抽提作用会使油品中的有机羧酸类防锈剂含量降低，导致润滑油的防锈能力下降甚至消失，进而引起设备锈蚀，缩短油品的换油周期。

近年来，以双子咪唑啉衍生物为组分的防锈剂组合物屡见报道。专利CN103289671A报道了一种在油气井开发过程中的酸化处理用的抗高温的缓蚀剂，其组成为双子咪唑啉基季铵盐型表面活性剂、双子吡啶季铵盐型表面活性剂、互溶剂、增效剂以及溶剂，该防锈剂组合物在高温下性能显著，主要用于油井酸化作业。

专利CN102020978A公开了一种油气井缓蚀剂及其制备方法，其组成为双子咪唑啉表面活性剂、脂肪醇聚氧乙烯醚磷酸酯、聚醚破乳剂、脂肪酸酰胺硼酸酯及溶剂。该油气井缓蚀剂能够在金属表面形成牢固的吸附膜和疏水保护膜，阻碍与电化学反应有关的电荷或物质的转移，具有良好的克服局部腐蚀、抑制点腐的能力，该防锈剂主要用于油气开采中材质的防锈。

从以上专利可以看出，目前已报道的防锈剂组合物中所涉及的双子咪唑啉均为双子咪唑啉季铵盐，此类双子咪唑啉季铵盐表面活性高，抗乳化能力差，因此所形成的防锈剂组合物主要用于含水的乳化液。而本发明的防锈剂组合物中的双子咪唑啉，其分子结构并非季铵盐形式，无阴阳离子存在，因此其抗乳化能力及油溶性优于双子咪唑啉季铵盐，所形成的防锈剂组合物可用于汽轮机油、无灰液压油等工业润滑油品以及防锈油脂中。此外本发明的防锈剂组合物组成与上述专利明显不同。综上所述，本专利与上述专利存在显著区别。