阅读说明：本技术 热作模具用Ni基合金以及使用其的热锻用模具、锻造制品的制造方法 (Ni-based alloy for hot die, hot forging die using same, and method for producing forged product ) 是由 铃木翔悟 青木宙也 上野友典 于 2018-11-29 设计创作，主要内容包括：本申请提供具有高的高温压缩强度和良好的耐氧化性,可以抑制作业环境的劣化以及形状劣化的热作模具用Ni基合金以及使用其的热锻用模具和使用前述热锻用模具的锻造制品的制造方法。热锻用模具以质量％计为W：7.0～15.0％、Mo：2.5～11.0％、Al：5.0～7.5％、Cr：0.5～7.5％、余量：Ni以及不可避免的杂质的热作模具用Ni基合金的表面的80％以上被铝氧化物层覆盖,在上述组成的基础上,可以进一步含有7.0％以下的Ta,进而可以含有选自元素Zr：0.5％以下、Hf：0.5％以下、稀土元素：0.2％以下、Y：0.2％以下、Mg：0.03％以下中的1种或者2种以上。(The present invention provides a Ni-based alloy for hot-forging dies, which has high-temperature compressive strength and good oxidation resistance and can suppress deterioration of working environment and shape deterioration, a hot-forging die using the same, and a method for producing a forged product using the hot-forging die. The hot forging die comprises, in mass%, W: 7.0-15.0%, Mo: 2.5-11.0%, Al: 5.0-7.5%, Cr: 0.5-7.5%, and the balance: the Ni-based alloy for hot working mold containing Ni and inevitable impurities may have a surface covered with an aluminum oxide layer in an amount of 80% or more, may further contain 7.0% or less of Ta in addition to the above composition, and may further contain an element selected from Zr: 0.5% or less, Hf: 0.5% or less of rare earth elements: 0.2% or less, Y: 0.2% or less, Mg: 0.03% or less of 1 or 2 or more.)

1. A die for hot forging, characterized by comprising, in mass%: 7.0-15.0%, Mo: 2.5-11.0%, Al: 5.0-7.5%, Cr: 0.5-7.5%, and the balance: at least 80% of the surface of the Ni-based alloy for hot working mold containing Ni and unavoidable impurities is covered with an aluminum oxide layer.

2. The die for hot forging according to claim 1, wherein the Ni-based alloy for hot working further contains, in mass%, an element selected from the group consisting of Zr: 0.5% or less, Hf: 0.5% or less of rare earth elements: 0.2% or less, Y: 0.2% or less, Mg: 0.03% or less of 1 or 2 or more.

3. The hot forging die as recited in claim 1 or 2, wherein the Ni-based alloy for hot working further contains 7.0% by mass or less of Ta.

4. The die for hot forging according to claim 2 or 3, wherein the Ni-based alloy for hot working further contains 1 or 2 elements selected from Ti and Nb in a total amount of 3.5% by mass or less, and the total content of Ta, Ti and Nb is 1.0 to 7.0%.

5. The die for hot forging according to any one of claims 1 to 4, wherein the Ni-based alloy for hot working further contains 15.0% by mass or less of Co.

6. The die for hot forging according to any one of claims 1 to 5, wherein the Ni-based alloy for hot working further contains, in mass%, an element selected from the group consisting of C: 0.25% or less, B: 0.05% or less of 1 or 2.

7. The hot forging die as claimed in any one of claims 1 to 6, wherein a coating layer of an antioxidant agent is provided on at least one of a forming surface and a side surface of the hot forging die.

8. A Ni-based alloy for hot-working dies, which contains, in mass%: 7.0-15.0%, Mo: 2.5-11.0%, Al: 5.0-7.5%, Cr: 0.5 to 7.5%, Ta: 0-7.0%, Co: 0 to 15.0%, and the balance of Ni and unavoidable impurities.

9. The Ni-based alloy for hot-work dies according to claim 8, further containing, in mass%, an element selected from the group consisting of Zr: 0.5% or less, Hf: 0.5% or less of rare earth elements: 0.2% or less, Y: 0.2% or less, Mg: 0.03% or less of 1 or 2 or more.

10. The Ni-based alloy for hot-work dies according to claim 8 or 9, further containing 1 or 2 elements selected from Ti and Nb in a total amount of 3.5% or less by mass, and the total content of Ta, Ti and Nb is 1.0 to 7.0%.

11. The Ni-based alloy for hot-work dies according to any one of claims 8 to 10, which has a heat resistance at a test temperature of: 1000 ℃, strain rate: 10^-3The 0.2% compressive strength per second is 500MPa or more.

12. The Ni-based alloy for hot-work dies according to any one of claims 8 to 10, which has a heat resistance at a test temperature of: 1100 ℃, strain rate: 10^-3The 0.2% compressive strength per second is 300MPa or more.

13. A method for producing a forged product, comprising the steps of:

a first step of heating a forged material; and the number of the first and second groups,

a second step of hot-forging the forging material heated in the first step using the die for hot forging according to any one of claims 1 to 7.

14. The method of manufacturing a forged product according to claim 13, wherein the second step is performed by heating the die for hot forging to 1000 ℃ or higher.

15. The method of manufacturing a forged product according to claim 14, wherein, prior to the step of heating the hot forging die to 1000 ℃ or higher, the Ni-based alloy for the hot forging die is preheated in the atmosphere at 1000 ℃ or higher to form an aluminum oxide layer on 80% or more of the surface of the Ni-based alloy for the hot forging die.

Technical Field

The present invention relates to a Ni-based alloy for hot dies, a hot forging die using the same, and a method for producing a forged product.

Background

In forging a product made of a heat-resistant alloy, a forging material is heated to a predetermined temperature to reduce deformation resistance. Since a heat-resistant alloy has high strength even at high temperatures, a die for hot forging used for forging the alloy needs high mechanical strength at high temperatures. In addition, in the hot forging, when the temperature of the die for hot forging is lower than that of the forged material, the workability of the forged material is lowered due to heat dissipation, and therefore, for example, forging of a product made of a difficult-to-work material such as Alloy718 or Ti Alloy is performed by heating the die for hot forging together with the raw material. Therefore, the die for hot forging must have high mechanical strength at a high temperature equal to or close to the temperature at which the forged material is heated. As a die for hot forging that satisfies this requirement, a Ni-based superalloy that can be used for hot forging at a die temperature in the atmosphere of 1000 ℃ or higher has been proposed (see, for example, patent documents 1 to 5).

In the present application, hot forging includes: hot die forging in which the temperature of the hot forging die is brought close to the temperature of the forged material, and constant temperature forging in which the temperature is the same as that of the forged material.

Disclosure of Invention

Problems to be solved by the invention

The above-described Ni-based superalloy is advantageous in high-temperature compressive strength, but in terms of oxidation resistance, when it is cooled after being heated in the atmosphere, fine scale of nickel oxide is scattered from the mold surface, and therefore, there is a concern that the working environment and the shape may be deteriorated. The problem of oxidation of the mold surface and the accompanying scattering of scale is a big problem in terms of whether or not the effect that can be used in the atmosphere can be exhibited to the maximum.

An object of the present invention is to provide a Ni-based alloy for hot dies, which has high-temperature compressive strength and good oxidation resistance and can suppress deterioration of working environment and shape deterioration, a hot forging die using the same, and a method for producing a forged product using the hot forging die.

Means for solving the problems

The present applicant has studied the problems of deterioration of the working environment and shape deterioration due to oxidation of the mold surface and accompanying scattering of scale, and has found a composition having high-temperature compressive strength and good oxidation resistance, and arrived at the present application.

That is, the present application relates to a die for hot forging, comprising, in mass%, W: 7.0-15.0%, Mo: 2.5-11.0%, Al: 5.0-7.5%, Cr: 0.5-7.5%, and the balance: at least 80% of the surface of the Ni-based alloy for hot working mold containing Ni and unavoidable impurities is covered with an aluminum oxide layer.

In the present application, in addition to the above composition, the composition may further contain an element selected from the group consisting of Zr: 0.5% or less, Hf: 0.5% or less of rare earth elements: 0.2% or less, Y: 0.2% or less, Mg: 0.03% or less of 1 or 2 or more.

In the present application, Ta may be further contained by 7.0% or less in addition to the above composition.

In addition to the above composition, the present application may further contain 1 or 2 elements selected from Ti and Nb in a total amount of 3.5% or less in a range where the total content of Ta, Ti and Nb is 1.0 to 7.0%.

In the present application, Co may be further contained in an amount of 15.0% or less in addition to the above composition.

More preferably, in the hot forging die using the Ni-based alloy for hot forging, at least one of the forming surface and the side surface of the hot forging die has a coating layer of an antioxidant agent.

Further, the present application relates to a Ni-based alloy for hot-work dies, which contains, in mass%: 7.0-15.0%, Mo: 2.5-11.0%, Al: 5.0-7.5%, Cr: 0.5 to 7.5%, Ta: 0-7.0%, Co: 0 to 15.0%, and the balance of Ni and unavoidable impurities.

In the present application, in addition to the above composition, the composition may further contain, in mass%, an element selected from the group consisting of Zr: 0.5% or less, Hf: 0.5% or less of rare earth elements: 0.2% or less, Y: 0.2% or less, Mg: 0.03% or less of 1 or 2 or more.

In the present application, in addition to the above composition, 1 or 2 selected from the elements Ti and Nb may be further contained in a total amount of 3.5% or less in mass% within a range where the total content of Ta, Ti and Nb is 1.0 to 7.0%.

Further, in the present application, it is preferable that at the test temperature: 1000 ℃, strain rate: 10^-3The 0.2% compressive strength per second is 500MPa or more.

More preferably, at the test temperature: 1100 ℃, strain rate: 10^-3The 0.2% compressive strength per second is 300MPa or more.

Further, the present application relates to a die for hot forging using the aforementioned Ni-based alloy for hot work die.

The present application also relates to a method for producing a forged product, comprising the steps of: a first step of heating a forged material; and a second step of hot forging the forging material heated in the first step using the hot forging die.

More preferably, in the method for producing a forged product, the second step is performed by heating the die for hot forging to 1000 ℃ or higher.

In the present invention, before the step of heating the hot forging die to 1000 ℃ or higher, the Ni-based alloy for hot forging die is preheated to 1000 ℃ or higher in the atmosphere, so that an aluminum oxide layer is formed on 80% or more of the surface of the Ni-based alloy for hot forging die.

ADVANTAGEOUS EFFECTS OF INVENTION

According to the present application, a Ni-based alloy for hot-working dies having high-temperature compressive strength and good oxidation resistance can be obtained. This can suppress deterioration of the working environment and deterioration of the shape during hot forging.

Drawings

Fig. 1 is a graph showing oxidation resistance of the present application example and comparative example under test conditions simulating long-term use of a mold.

FIG. 2 is a view showing the surfaces of test pieces after being held at 1100 ℃ for 8 hours in the atmosphere in the examples of the present application and comparative examples.

Fig. 3 is a sectional photograph showing a reflection electron image and an elemental map of an oxide layer formed on the surface of a test piece after being held in the atmosphere at 1100 ℃ for 3 hours or 8 hours in the present application example and comparative example.

Fig. 4 is a graph showing the oxidation resistance of the present application example and the comparative example in the test conditions simulating heating and cooling caused by repeated use of the mold.

Fig. 5 is a graph showing the high-temperature compressive strength of the present application example and comparative example.

Fig. 6 is a photograph showing the antioxidant effect of the mold surface caused by the coating of the antioxidant.

Detailed Description

The Ni-based alloy for hot-working dies of the present invention will be described in detail below. The unit of the chemical composition is mass%. The aforementioned Ni-based alloy for hot dies serves as a base material of the hot forging die of the present application.

＜W＞

W is solid-dissolved in an austenite matrix and also in Ni as a precipitation-strengthened phase₃Al is a basic gamma prime phase (gamma prime phase) to improve the high-temperature strength of the alloy. On the other hand, W has an action of reducing oxidation resistance and an action of easily precipitating a harmful phase such as TCP (Topologically Close Packed). In the present application, the W content in the Ni-based alloy is 7.0 to 15.0% from the viewpoint of improving the high-temperature strength and further suppressing the reduction in oxidation resistance and the precipitation of harmful phases. The lower limit of W is preferably 10.0%, the upper limit of W is preferably 12.0%, and the upper limit of W is more preferably 11.0% in order to more reliably obtain the effect of W.

＜Mo＞

Mo is dissolved in an austenite matrix and also in Ni as a precipitation-strengthened phase₃Al is a basic gamma' phase, and the high-temperature strength of the alloy is improved. On the other hand, Mo has an effect of reducing oxidation resistance. The content of Mo in the Ni-based superalloy in the present application is 2.5 to 11.0% from the viewpoint of improving the high-temperature strength and further suppressing the reduction of the oxidation resistance. In order to suppress the precipitation of harmful phases such as TCP accompanying the addition of W and Ta, Ti, and Nb described later, a preferable lower limit of Mo is set in balance with the contents of W, Ta, Ti, and Nb, and a preferable lower limit is 4.0%, and a more preferable lower limit is 4.5% in order to more reliably obtain the Mo effect. The upper limit of Mo is preferably 10.5%, more preferably 9.0%, and still more preferably 6.0%.

＜Al＞

Al is bonded with Ni to precipitate Ni₃The γ' phase formed from Al increases the high-temperature strength of the alloy, and forms a coating film of aluminum oxide on the surface of the alloy, thereby imparting oxidation resistance to the alloy. Another one isOn the other hand, if the content of Al is too large, eutectic γ' phase is excessively generated, and the high-temperature strength of the alloy is reduced. In the present application, the Al content in the Ni-based superalloy is 5.0 to 7.5% from the viewpoint of improving oxidation resistance and high-temperature strength. The lower limit of the amount of Al is preferably 5.2%, more preferably 5.4% in order to more reliably obtain the effect of Al. The upper limit of Al is preferably 6.7%, more preferably 6.5%, and still more preferably 6.0%.

＜Cr＞

Cr has an effect of promoting the formation of an alumina continuous layer on the surface or inside of the alloy, and improving the oxidation resistance of the alloy. Therefore, 0.5% or more of Cr needs to be added. In addition, when Cr is added together with Al, W, and the like, 3.0 to 7.5% of Cr exhibits high compressive strength at 1000 ℃. Further, in the case of a Cr content of 3.0% or less, a high compressive strength is obtained at a temperature of 1000 ℃ to 1100 ℃. Among them, addition of Cr in an amount exceeding 7.5% is to be avoided because the compressive strength at 1000 ℃ or higher is lowered. The addition of Cr is not necessarily detrimental to the high-temperature strength, and it has been confirmed that when 0.5 to 7.5% of Cr is added together with Al, W, etc., the high-temperature strength is rather high, and the oxidation resistance can be improved while maintaining the high-temperature strength. The lower limit is preferably 1.0%, and more preferably 1.3% in order to more reliably obtain the effect of Cr. On the other hand, if the Cr content is too large, a harmful phase such as tcp (polarity Close packed) may be easily precipitated. In particular, when a large amount of elements that increase the high-temperature strength of the alloy, such as W, Mo, Ta, Ti, and Nb, is contained, harmful compatibility tends to precipitate. From the viewpoint of maintaining the content of elements that improve oxidation resistance and high-temperature strength at a high level and suppressing precipitation of harmful phases, a preferred upper limit of the Cr content in the present application is 3.0%. More preferably, the upper limit is 2.0%.

＜Ta＞

The Ni-based superalloy in the present application may contain Ta. Ta in Ni₃The gamma' phase formed by Al is solid-dissolved in the form of replacing Al sites, the high-temperature strength of the alloy is improved, and the high-temperature strength formed on the surface of the alloy is improvedThe oxide coating film of (2) has an effect of further improving the oxidation resistance of the alloy, particularly under thermal cycle conditions in which the cycle of heating and cooling of the mold is short. On the other hand, if the content of Ta is too large, it has an effect of easily precipitating a harmful phase such as TCP. In the present application, the upper limit of Ta in the case of Ta being contained is 7.0% from the viewpoints of improving oxidation resistance and high-temperature strength and suppressing precipitation of harmful phases. When Ta is contained, the lower limit is preferably 0.5%, more preferably 2.5%, and still more preferably 5.0% in order to more reliably obtain the effect. The upper limit of Ta is preferably 6.7%, more preferably 6.5%.

< Zr, Hf, rare earth element, Y and Mg >

The Ni-based superalloy in the present application may contain 1 or 2 or more elements selected from Zr, Hf, rare earth elements, Y, and Mg. The Zr, Hf, rare earth element and Y suppress the diffusion of metal ions and oxygen at the grain boundary due to segregation to the grain boundary of the oxide coating. This inhibition of grain boundary diffusion reduces the growth rate of the oxide coating and changes the growth mechanism that promotes the peeling of the oxide coating, thereby improving the adhesion between the coating and the alloy. That is, these elements have an effect of further improving the oxidation resistance of the alloy by reducing the aforementioned reduction in the growth rate and improving the film adhesion, particularly under thermal cycle conditions in which the cycle of heating and cooling of the mold is short. Further, the rare earth element, Y, and Mg form sulfides with S (sulfur) which segregates at the interface between the oxide film and the alloy and inhibits chemical bonding between them, thereby reducing the adhesion of the film, preventing the segregation of S, and improving the adhesion. S is an element that may be contained as an impurity.

Among the rare earth elements, L a is preferably used because L a has a large effect of improving oxidation resistance, and L a has an effect of preventing S-segregation in addition to the above-described diffusion suppression and is excellent in these effects, so that L a can be selected among the rare earth elements, and Y also achieves the same effect as L a, and therefore addition of Y is also preferable, and 2 or more kinds including L a and Y are particularly preferably used.

In addition to the oxidation resistance, in particular, cracks of the mold due to excessive thermal stress generated under a thermal cycle condition in which a cycle of heating and cooling of the mold is short are suppressed, and therefore, in the case where toughness is also required, it is preferable to use Hf or Zr having a lower effect of reducing the toughness than the rare earth element or Y. Among Zr and Hf, Hf is particularly preferably used because the effect of lowering toughness is low and the effect of preventing cracks during casting can be expected. When the rare earth element and Y are not contained and 1 or 2 of Zr and Hf are contained, Zr and Hf have a smaller effect of preventing S segregation than the rare earth element and Y, and therefore, the oxidation resistance is further improved by adding Mg at the same time. Therefore, in order to improve the oxidation resistance and the toughness in a well-balanced manner, it is particularly preferable to use Hf and Mg at the same time.

When the amounts of Zr, Hf, rare earth elements, Y, and Mg added are too large, intermetallic compounds with Ni and the like are excessively generated to lower the toughness of the alloy, and therefore, it is preferable to use the following contents when any of these elements is contained.

From the viewpoint of improving oxidation resistance and suppressing a decrease in toughness, the upper limit of the content of each of Zr and Hf in the case of containing Zr and Hf in the present application is 0.5%. The upper limit of the content of each of Zr and Hf is preferably 0.3%, and more preferably 0.2%. The lower limit of the case where Zr or Hf is contained may be set to 0.001%. The lower limit of the amount of Zr and Hf contained is preferably 0.01%, more preferably 0.05%, and still more preferably 0.1% or more.

Since the rare earth element and Y have a higher toughness-reducing effect than Zr and Hf as described above, the upper limit of the content of each of these elements in the case of containing the rare earth element and Y in the present application is 0.2%, preferably 0.02%, and more preferably 0.005%. The lower limit of the rare earth element and Y may be 0.001%. The lower limit of the content of the rare earth element and Y is preferably 0.002%, and more preferably 0.003% or more.

Since Mg is only required in an amount necessary to form sulfides with S contained as impurities in the alloy, the upper limit of the content in the case of Mg is 0.03%. The lower limit in the case of Mg being contained may be set to 0.001%. The upper limit of Mg is preferably 0.025%, more preferably 0.02%. On the other hand, 0.005% may be set as the lower limit in order to more reliably exert the effect by Mg addition.

< Ti and Nb >

The Ni-based alloy for hot-work dies in the present application may contain 1 or 2 selected from Ti and Nb in a range of 3.5% or less in total. Ti, Nb and Ta are composed of Ni₃The gamma' phase formed by Al is solid-dissolved in a mode of replacing Al sites, so that the high-temperature strength of the alloy is improved. Further, it is an inexpensive element compared to Ta, and therefore is advantageous in terms of mold cost. On the other hand, when the contents of Ti and Nb are too large, it is likely to precipitate a harmful phase such as TCP, like Ta; the eutectic γ' phase is excessively generated, and the high-temperature strength of the alloy is reduced. Ti and Nb have a weaker effect of improving high-temperature strength than Ta, and do not have an effect of improving oxidation resistance unlike Ta.

From the above, from the viewpoint of suppressing the decrease in high-temperature strength associated with the precipitation of harmful phases and the excessive formation of eutectic γ' phase, it is desirable to limit the total content of Ta, Ti and Nb, and to replace Ta with Ti or Nb, which is advantageous in terms of mold cost, while maintaining the high-temperature strength characteristics and oxidation resistance within the same levels as those in the case where only Ta is contained. In the present application, when Ti and/or Nb are contained, it is preferable that the upper limit of the total content of Ta, Ti, and Nb is 7.0%, and the upper limit of the content of 1 or 2 selected from the elements Ti and Nb is 3.5%. The preferable upper limit of the sum of the contents of Ta, Ti and Nb is 6.5%, and the preferable upper limit of the content of 1 or 2 selected from the elements Ti, Nb is 2.7%. The lower limit of the total content of Ta, Ti and Nb is set to 1.0% from the viewpoint of reliably obtaining the effect of improving the high-temperature strength, and the lower limit of the content of 1 or 2 selected from the elements Ti and Nb may be set to 0.5% from the viewpoint of reliably obtaining the effect of reducing the cost of the mold. The lower limit of the total content of Ta, Ti and Nb is preferably 3.0%, and more preferably 4.0%. The preferable lower limit of the content of 1 or 2 selected from the elements Ti, Nb is 1.0%.

Among the choices of Ti and Nb, Ti is preferably used from the economical viewpoint, and Nb is preferably used when high-temperature strength is particularly important. When importance is attached to both the cost of the mold and the high-temperature strength, it is particularly preferable to use Ti and Nb simultaneously.

＜Co＞

The Ni-based alloy for hot-work dies in the present application may contain Co. Co is dissolved in an austenite matrix to improve the high-temperature strength of the alloy. On the other hand, if the content of Co is too large, Co is an expensive element compared to Ni, and therefore, it increases the cost of the mold, and also has an effect of easily precipitating a harmful phase such as TCP. From the viewpoint of improving the high-temperature strength, suppressing the increase in the cost of the mold, and suppressing the precipitation of a harmful phase, Co may be contained in a range of 15.0% or less. When Co is contained, the lower limit is preferably 0.5%, more preferably 2.5% in order to obtain the effect reliably. Further, the upper limit is preferably 13.0%, more preferably 6.0%.

< C and B >

The Ni-based alloy for hot-work dies in the present application may contain 1 or 2 elements selected from 0.25% or less of C (carbon) and 0.05% or less of B (boron). C. B improves the strength of the grain boundary of the alloy, and improves the high-temperature strength and ductility. On the other hand, when the content of C, B is too large, coarse carbides and borides are formed, and the strength of the alloy is also reduced. In the present application, the C content is preferably 0.005 to 0.25% and the B content is preferably 0.005 to 0.05% in the case of containing C from the viewpoint of improving the strength of the grain boundary of the alloy and suppressing the formation of coarse carbides and borides. The lower limit is preferably 0.01%, and the upper limit is preferably 0.15% in order to reliably obtain the effect of C. In order to reliably obtain the effect of B, the lower limit is preferably 0.01%, the upper limit is preferably 0.03%, and the upper limit is more preferably 0.02%.

When importance is attached to economy and high-temperature strength, it is particularly preferable to use only C, and when importance is attached to ductility, it is particularly preferable to use only B. When importance is attached to both the high-temperature strength and the ductility, it is particularly preferable to use C and B at the same time.

Other than the above-described additive elements are Ni and inevitable impurities. In the Ni-based superalloy of the present application, Ni is a main element constituting the γ phase, and constitutes a γ' phase together with Al, Ta, Mo, W, and the like. Among the above-mentioned inevitable impurity elements, S is preferably 0.0030% or less. Further, it is preferably limited to 0.0010% or less, and it is preferable to prevent the segregation to the interface between the oxide coating and the alloy and the deterioration of the adhesion of the coating due to the inhibition of the chemical bonding between the oxide coating and the alloy.

As is clear from the examples described later, it is considered that the composition in the present application preferably contains W, Mo, Al, Cr, Ta, Hf and Mg, and particularly the following ranges are preferable.

A Ni-based alloy for hot-work dies having a composition containing, in mass%: 10.0 to 12.0%, Mo: 4.0-6.0%, Al: 5.0-6.5%, Cr: 1.0-3.0%, Ta: 2.5-6.7%, Hf: 0.01-0.3%, Mg: 0.001 to 0.025%, and the balance of Ni and unavoidable impurities.

< oxide coating >

In the present application, it is important that 80% or more of the surface is covered with an aluminum oxide layer when the surface is heated to 1000 to 1100 ℃ in the atmosphere. The Ni-based alloy for the hot-working die can be used for hot die forging and constant-temperature forging in the atmosphere. The aforementioned temperature of 1000 ℃ is a temperature assumed for hot die forging. Further, 1100 ℃ is a temperature of the hypothetical constant temperature forging. The surface referred to herein is the most important molding surface in the mold. Preferably, the molding surface and the side surface of the mold are covered with an aluminum oxide layer, and more preferably, the entire surface of the mold is covered.

In order to form an aluminum oxide layer in 80% or more of the surface of the Ni-based alloy for hot working mold in this temperature range, for example, the aluminum oxide layer may be formedThe formation of an oxide layer (oxide film) is promoted by performing a blasting process such as shot blasting. However, when excessive component segregation occurs in the Ni-based alloy for hot-working dies, the oxide film tends to become uneven. Therefore, it is preferable to prevent the formation of unevenness of aluminum oxide in advance by applying, for example, a homogenization heat treatment at 1100 to 1300 ℃ for about 10 to 100 hours, which is performed in an inert atmosphere or in the atmosphere to reduce the segregation of components, for example, by applying an antioxidant to the entire surface of the cast material. When the coverage of the aluminum oxide layer is less than 80% of the surface, there is a problem that the amount of scale scattering increases. Therefore, in the present application, the area ratio of the aluminum oxide formed on the surface of the Ni-based alloy for hot dies is 80% or more. Preferably 90% or more, most preferably 100%. In order to confirm the coverage (area ratio) of the aluminum oxide layer of the present invention, at least 25mm was observed with an optical microscope²The above range may be used.

In addition, in the mold which is degreased and cleaned after the machining, for example, by preheating the mold in the air at a temperature of 1000 ℃ or higher and covering 80% or more of the surface with the aluminum oxide layer, it is possible to suppress inhibition of formation of the aluminum oxide layer and adhesion between the mold and the member due to stains such as grease adhering to the surface during the assembling work of the mold. The aluminum oxide layer formed on the molding surface has an effect of improving the wettability of the glass lubricant used as the lubricant. The upper limit of the preheating temperature may be 1150 ℃. The preheating time depends on the size of the hot forging die, and is sufficient in the range of about 10 minutes to 3 hours.

< die for hot forging >

In the present application, a hot forging die using a Ni-based alloy for a hot die having the above alloy composition and covered with an aluminum oxide layer within the range specified in the present application can be configured. The hot forging die of the present application can be obtained by sintering or casting of alloy powder. Casting which is inexpensive in production cost as compared with sintering of alloy powder is preferable, and a sand mold or a ceramic mold is preferably used for the mold in order to suppress generation of cracks in the ingot due to stress at the time of solidification.

Further, at least one of the forming surface and the side surface of the hot forging die of the present invention may be a surface having a coating layer of an antioxidant agent. This prevents oxidation of the mold surface and accompanying scattering of scale due to contact between oxygen in the atmosphere at high temperatures and the mold base material, and thus can more reliably prevent deterioration of the working environment and shape. The antioxidant is preferably an inorganic material composed of 1 or more of nitride, oxide, and carbide. This is because a dense oxygen barrier film is formed by the coating layer of nitride, oxide, or carbide, and oxidation of the mold base material is prevented. The coating layer may be any single layer of nitride, oxide, or carbide, or may be a stacked structure of any combination of 2 or more of nitride, oxide, and carbide. Further, the coating layer may be a mixture of any 2 or more of nitrides, oxides, and carbides. In the present application, a conventional method such as coating or spraying may be applied to form the coating layer, but from the economical viewpoint, the formation of the coating layer is preferable. The thickness of the coating layer is preferably 100 to 200 μm because the thickness of the coating layer can be easily increased by coating, and thus the contact between oxygen in the atmosphere and the mold base material can be more reliably prevented, but the effect is saturated even if the thickness of the coating layer is excessively increased. The antioxidant before coating is preferably a paste which is easy to coat, and the coating method is preferably a coating method using a simple brush.

As described above, the hot forging die using the Ni-based alloy for hot-working dies of the present application has high-temperature compressive strength and good oxidation resistance, prevents oxidation of the die surface and accompanying scattering of scale due to contact between oxygen in the atmosphere at high temperatures and the die base material, and can more reliably prevent deterioration of the working environment and shape deterioration.

< method for producing forged article >

A typical process for producing a forged product using a hot forging die using the Ni-based alloy for a hot die according to the present invention will be described.

First, as a first step, a forging material is heated to a predetermined forging temperature. Since the forging temperature varies depending on the material, the temperature is appropriately adjusted. The hot forging die using the Ni-based alloy for a hot die according to the present invention has a characteristic that it can be subjected to constant temperature forging and hot die forging even in an atmosphere in the atmosphere at a high temperature, and is therefore suitable for hot forging of Ni-based super heat-resistant alloys, Ti alloys, and the like, which are known as difficult-to-work materials. The forging temperature is typically 1000 to 1150 ℃.

Then, the forging material heated in the first step is hot forged using the hot forging die (second step). Before the hot forging, the second step is preferably performed by heating the die for hot forging to 1000 ℃. In the case of the hot die forging or the isothermal forging, the hot forging in the second step is preferably die forging. In addition, as described above, the Ni-based alloy for hot-working dies of the present invention can be hot-forged at a high temperature of 1000 ℃.