阅读说明：本技术 实木颗粒板 (Solid wood particle board ) 是由 利博尔·库维克 于 2018-06-25 设计创作，主要内容包括：一种实木颗粒板(10),包括：芯层(2),该芯层(2)由树脂涂覆的具有大颗粒尺寸的实木颗粒形成；至少一个表面层(1,4),所述至少一个表面层(1,4)由树脂涂覆的实木颗粒形成,其中,所述至少一个表面层(1,4)包括颗粒尺寸小于芯层(2)的颗粒尺寸的实木颗粒；以及至少一个中间箔(3,5),所述至少一个中间箔(3,5)布置在表面层(1,4)与芯层(2)之间,其中,所述至少一个中间箔(3,5)的表面重量在5g/m<Sup>2</Sup>至600g/m<Sup>2</Sup>的范围内并且厚度在0.05mm至3mm的范围内。(A solid wood particle board (10) comprising: a core layer (2), the core layer (2) being formed of resin-coated solid wood particles having a large particle size; at least one surface layer (1, 4), the at least one surface layer (1, 4) being formed of resin-coated solid wood particles, wherein the at least one surface layer (1, 4) comprises solid wood particles having a particle size smaller than the particle size of the core layer (2); and at least one intermediate foil (3, 5), the at least one intermediate foil (3, 5) being arranged between the surface layer (1, 4) and the core layer (2), wherein the at least one intermediate foil (3, 5) has a surface weight of 5g/m 2 To 600g/m 2 And a thickness in the range of 0.05mm to 3 mm.)

1. A solid wood particle board (10; 11) comprising:

a core layer (2), the core layer (2) being formed of resin-coated solid wood particles having a large particle size;

at least one surface layer (1, 4), the at least one surface layer (1, 4) being formed of resin-coated solid wood particles, wherein the at least one surface layer (1, 4) comprises solid wood particles having a particle size smaller than the particle size of the core layer (2); and

at least one intermediate foil (3, 5), the at least one intermediate foil (3, 5) being arranged between a surface layer (1, 4) and the core layer (2), wherein the at least one intermediate foil (3, 5) has a surface weight of 5g/m²To 600g/m²And a thickness in the range of 0.05mm to 3 mm.

2. The solid wood particle board (10; 11) according to claim 1,

the at least one intermediate foil (3, 5) is vapour permeable.

3. The solid wood particle board (11) according to claim 1 or 2,

the solid wood particle board (11) comprises two surface layers (1, 4) and two intermediate foils (3, 5), the two intermediate foils (3, 5) being arranged on opposite surfaces of the core layer (2).

4. The solid wood particle board (10; 11) according to any one of claims 1 to 3,

the at least one intermediate foil (3, 5) is adhered to the core layer (2) and the surface layers (1, 4) by means of an adhesive provided in the core layer (2) and/or in the surface layers (1, 4).

5. The solid wood particle board (10; 11) according to any one of claims 1 to 4,

the at least one intermediate foil (3, 5) is formed of paper, perforated plastic sheet material, textile material or mesh.

6. The solid wood particle board (10; 11) according to any one of claims 1 to 5,

the density of the core layer (2) is 500kg/m³And the density of the at least one surface layer (1, 4) is 700kg/m³The above.

7. A method for producing a solid wood particle board (10; 11), the method comprising:

placing solid wood particles having a small particle size and a binder to form a first surface layer (1);

placing solid wood particles having a particle size larger than the particle size of the first surface layer and a binder to form a core layer (2);

arranging an intermediate foil (3) on top of the core layer (2), wherein the intermediate foil (3, 5) has a surface weight of 5g/m²To 600g/m²And a thickness in the range of 0.05mm to 3 mm;

placing solid wood particles having a particle size smaller than the particle size of the core layer (2) and a binder to form at least one second surface layer (4); and

the laid layers are compressed to form a solid wood particle board (10).

8. The method for producing a solid wood particle board (10; 11) according to claim 7, further comprising:

coating the solid wood particles with an adhesive prior to performing the step of placing the solid wood particles.

9. The method for producing a solid wood particle board (10; 11) according to claim 7 or 8,

-adhering the intermediate foil (3) to the core layer (2) and the surface layers (1, 4) by means of the adhesive provided in the core layer (2) and the surface layers (1, 4).

10. The method for producing a solid wood particle board (10; 11) according to any one of claims 7 to 9, further comprising:

-placing a first intermediate foil (5) on the first surface layer (1) before placing the solid wood particles and the binder of the core layer (2), wherein subsequently the core layer (2) is placed on top of the first intermediate foil (5);

-arranging a second intermediate foil (3) on top of the core layer (2); and

on top of the second intermediate foil (3) a second surface layer (4) is placed.

Technical Field

The invention relates to a solid wood particle board. An example of the solid wood particle board may include a core layer composed of solid wood particles having a large chip size, which is sandwiched between two surface layers composed of solid wood particles having a particle size smaller than the chip size of the core layer.

Background

Common solid wood particle boards, which are currently used in particular in the furniture-making industry, comprise a plurality of layers of solid wood particles, wherein different layers may consist of particles of different sizes. In particular, the surface layer may consist of solid wood particles of fine particle size, while the core layer may comprise solid wood particles having large particle size. However, the solid wood particle size in the respective layers of the board may be chosen in different ways depending on the intended use of the solid wood particle board. For example, for structural panels used in the flooring or in the wood building industry, the composition and number of layers may be selected as required for the respective intended use, although it is still desirable to provide a reasonably smooth surface. During the manufacturing process, the solid wood particles are typically mixed with or coated with a binder and then placed to form the desired layer. The layers are then compressed at high pressure and high temperature to form a particle board.

Large solid wood chips of a core layer, which usually has a rough surface texture, are pressed relatively loosely, with air pockets formed between the chips. Thus, a surface layer consisting of smaller particles is used to provide at least one smooth and flat outer surface. Solid wood particle boards are typically constructed in a symmetrical manner, comprising an odd number of layers having two respective outer surface layers and one or more core layers. The quality of the surface is particularly important to the furniture making industry.

In order to ensure a low total weight of the board, it is desirable to use a relatively thin surface layer. However, some of the smaller surface layer particles may fall into the gaps between the larger core layer particles, so that the surface roughness may increase in the case of a thin surface layer.

Disclosure of Invention

The object of the present invention is to provide a solid wood particle board having a flat surface. In the context of the present disclosure, the term "solid wood particle board" is used as a general term with respect to any panel product made at least partially of solid wood particles, such as for example particle board, OSB, chip board, particle board, wafer board, etc. Furthermore, the term "solid wood particle board" of the present disclosure may also cover boards having a fiber-based core layer and a particle board surface layer or boards which may for example comprise a core made of wood filaments covered by a fine particle board layer.

The solid wood particle board according to the present invention comprises: a core layer, which may for example consist of solid wood particles having a large particle size; and at least one surface layer, which may for example consist of solid wood particles having a particle size smaller than the particle size of the core layer. Thus, a lightweight solid wood particle board having a smooth surface is formed. However, the present disclosure is not limited to such chip boards, but may encompass other types of solid wood particle boards made of different types of solid wood particles or lignocellulosic materials.

Generally, a solid wood particle board is formed with two surface layers on the outer side and one or more core layers interposed between the two surface layers in a symmetrical manner. However, it is envisaged that for certain applications solid wood particle boards having an asymmetric configuration and having only one surface layer may be used, such that the core layer is covered by a separate surface layer on only one of the sides of the core layer.

At least one intermediate foil is arranged between the surface layer and the core layer. The intermediate foil layer may for example prevent solid wood particles from falling from the surface layer into the core layer. Thus, the thickness of the surface layer can be reduced compared to prior art particle boards, while ensuring a smooth and flat surface of the solid wood particle board.

During manufacturing, the solid wood particle board with the intermediate foil positioned between the core layer and the surface layer may be cured under pressure using, for example, hot pressing, cold pressing or high frequency current curing methods.

Thus, the solid wood particle board as defined above achieves a uniform coverage of the rough core (such as for example the core of a chip board, OSB or wafer board) by the surface layer even in case the surface layer is rather thin. Such a uniform coverage is extremely difficult to achieve by prior art methods, provided that the core layer is made of chips, such as OSB or wafer substrates. Thus, according to embodiments, a lightweight solid wood particle board may be provided, as the thickness of the heavy surface layer may be reduced due to the presence of the intermediate foil.

Furthermore, the presence of the intermediate foil allows to reduce the amount of surface layer used, while the manufactured solid wood particle board may still be in the density range of standard particle boards or even high density boards.

The intermediate foil has the following additional effects: the intermediate foil ensures that both surfaces of the solid wood particle board can be produced with the same quality. In typical prior art solid wood particle boards, the top surface tends to be of lower quality, and more material is typically used to form the top surface to achieve a given surface quality. Thus, the solid wood particle board according to embodiments allows for an improved surface quality for applications with high requirements, such as for example foil or direct printing.

It has also been found that providing an intermediate foil between the core layer and the top surface layer allows a faster manufacturing of the solid wood particle board and allows a manufacturing of the solid wood particle board with higher quality edges, when compared to the solid wood particle boards of the prior art. This may be caused by the balancing of the forces of the intermediate foil acting on the particle board blank in the hot pressing and thus allows a faster and better quality pressing step for forming the placed solid wood particle board blank into a finished solid wood particle board. Furthermore, the intermediate foil may influence the expansion of the particles during the hot pressing step and may improve the expansion characteristics compared to prior art solid wood particle boards without the intermediate foil.

According to an embodiment, the intermediate foil may be vapour permeable. If a cold pressing process is used, the intermediate foil does not have to be vapour permeable. However, if hot pressing is used, the vapour permeable intermediate foil allows moisture or steam to escape from the core layer during hot pressing and subsequent cooling. Alternatively, a thermoplastic intermediate foil without permeability may be used, as such an intermediate foil will crack or melt during hot pressing and will therefore not form a barrier to escape of vapour from any core or surface layer.

According to some embodiments, a solid wood particle board may be provided, wherein only one intermediate foil is provided between the core layer and one of the surface layers of the solid wood particle board. According to an alternative embodiment, the solid wood particle board may comprise two intermediate foils arranged on opposite surfaces of the core layer. Thus, for some applications, a solid wood particle board having two smooth surfaces may be provided. In addition, the overall stability and mechanical properties of the solid wood particle board can be improved by providing two intermediate foils on both sides of the core layer. Wherein the thickness, density and mechanical properties of the intermediate foil may be selected according to the desired mechanical properties of the finished solid wood particle board.

The intermediate foil of the invention may be adhered to the core layer and the surface layer by means of an adhesive provided in the core layer and the surface layer. Thus, it may not be necessary to provide an additional adhesive on the intermediate foil. Furthermore, the intermediate foil may be composed of various materials, such as paper, in particular, paper that is not resin-impregnated, perforated plastic sheets, fabric or mesh.

The surface weight of the intermediate foil according to the invention may be in the range of 5g/m²To 600g/m²Preferably at 5g/m²To 200g/m²Most preferably at 5g/m²To 60g/m²And the thickness may be in the range of 0.05mm to 3mm, preferably 0.05mm to 2.5mm, most preferably 0.05mm to 2.0 mm.

The density of the core layer may be 500kg/m³And the density of the surface layer may be 700kg/m³The above. Thus, a lightweight solid wood particle board can be provided. Due to the provision of the intermediate foil, a high surface quality can be ensured even in the case of a relatively thin surface layer.

The invention also relates to a method for producing a solid wood particle board. As a first step, solid wood particles sized to a small particle size and a binder are placed to form a first surface layer. Solid wood particles having a large particle size and a binder are placed on the first surface layer to form a core layer. Next, an intermediate foil is provided on top of the core layer, wherein the intermediate foil may be vapor permeable. The intermediate foil may be provided as a continuous sheet to allow a continuous manufacturing process. After the intermediate foil has been placed onto the core layer, solid wood particles having a particle size smaller than the particle size of the core layer and a binder are placed to form at least one surface layer. Finally, the laid layers are compressed to form a solid wood particle board.

Thus, small particles of the surface layer are prevented from entering the core layer by the provision of the intermediate foil. Additionally, since the intermediate foil may be vapor permeable, the solid wood particle board may be manufactured using a conventional continuous hot pressing process in which the intermediate foil allows steam and vapor to pass through the solid wood particle board during pressing and cooling. For other manufacturing methods, such as for example cold pressing or high frequency current curing, it may not be necessary to provide a vapour permeable intermediate foil.

Wherein the solid wood particles may be coated with an adhesive before performing the step of placing the solid wood particles.

According to an embodiment, the intermediate foil may be adhered to the core layer and the surface layer by an adhesive provided in the core layer and the surface layer. Thus, no additional adhesive has to be provided on the intermediate foil layer.

According to an embodiment, the first intermediate foil may be placed directly onto the first surface layer before placing the solid wood particles and the binder of the core layer, wherein the core layer may be placed on top of the first intermediate foil. Subsequently, a second intermediate foil may be provided on top of the core layer, and a second surface layer may be placed on top of the second intermediate foil.

In this way, a solid wood particle board comprising two surface layers on both sides of the core layer may be formed, wherein between each surface layer and the core layer a respective intermediate foil is positioned. Thus, a solid wood particle board for applications requiring a board with two high quality surfaces can be provided. In addition, with a suitable choice of the intermediate foil material, the mechanical properties of the solid wood particle board can be improved by adding two intermediate foil layers on both sides of the core layer.

Description of the drawings

Fig. 1 shows a schematic view of a particle board according to a first embodiment of the present invention.

Fig. 2 shows a schematic view of a particle board according to a second embodiment of the present invention.

Fig. 3 shows an example of a dual density solid wood particle board, wherein an intermediate foil as shown in fig. 1 or fig. 2 may be used.

Fig. 4 is a schematic illustration of the application of an adhesive to the middle foil layer during the manufacture of a solid wood particle board according to an embodiment of the invention.

Detailed Description

In order to manufacture a particle board according to one of the embodiments described in detail below, a layer of adhesive-coated solid wood particles is formed. Wherein the different layers usually comprise solid wood particles having different properties and the layers are placed on top of each other. In an embodiment as described below, at least one intermediate foil is arranged between two layers of placed solid wood particles. After forming the particle layers and arranging the intermediate foil between two particle layers, at least one curing or pressing process is performed, which may comprise simultaneous heating and pressing. The heat and pressure activate the adhesive and seek out any available moisture. The adhesive bonds throughout all the layers and then sets to provide a strong bond between the solid wood particles and the intermediate foil. Furthermore, pressing is applied to strengthen the layers and to evolve the internal structure of the solid wood particle board, which internal structure comprises the final density profile of the solid wood particle board. Pressing may be performed as a continuous process, wherein the layer of particles is placed continuously and transported continuously through the hot pressing device; or the pressing may be performed as a batch process, wherein the layered particle structure of predetermined size is placed in a hot pressing apparatus, in which the layered particle structure of predetermined size is kept stationary during pressing.

After pressing, the solid wood particle board may be cooled and trimmed to obtain the desired length and width. The solid wood particle board may be formed as a panel, but may also be formed as a moulded particle board product, such as a furniture component. In addition, the solid wood particle board may be sanded or shaved prior to further processing. Other layers such as, for example, decorative exterior layers or other support layers may be applied to the solid wood particle board after pressing and cooling.

Fig. 1 shows a schematic view of a first embodiment of the invention. The solid wood particle board 10 according to the present embodiment includes a plurality of layers arranged from bottom to top as follows: a bottom surface layer 1, a core layer 2, an intermediate foil 3 and a top surface layer 4.

In the depicted embodiment, the surface layers 1 and 4 are formed of small solid wood particles to provide a smooth high quality surface. Wherein both surface layers 1 and 4 may be composed of solid wood particles having substantially the same size and mechanical properties to ensure a balanced structure of the solid wood particle board and to prevent deformations and mechanical stresses within the board. The density of the surface layers 1 and 4 of the finished solid wood particle board can be 700kg/m³In order to ensure sufficient stability of the whole solid wood particle board.

In the depicted embodiment, the intermediate foil 3 is arranged between the core layer 2 and the top surface layer 4. Watch with intermediate foil 3The surface weight can be 5g/m²To 600g/m²Preferably at 5g/m²To 200g/m²Most preferably at 5g/m²To 60g/m²Within the range of (1). The thickness of the intermediate foil 3 may be in the range of 0.05 to 3mm, preferably 0.05 to 2.0mm, most preferably 0.05 to 2.0 mm. A key characteristic of the intermediate foil material may be that the intermediate foil material has a certain vapour permeability to ensure that heat and vapour are transferred during the hot pressing process. A Gurley resistance (Gurley resistance) may be used for determining the level of air resistance. For example, the air resistance of the intermediate foil may be between 1.1 and 12 gurley seconds. Preferably, the material can be mechanically stable up to about 240 ℃ to withstand the hot pressing process without being damaged. Alternatively, the intermediate foil may be designed to be destroyed or melted once the position of the solid wood particles in the respective layer of the solid wood particle board is fixed during pressing or curing.

Various materials may constitute the intermediate foil 3, such as paper, in particular paper not impregnated with resin, perforated plastic sheets, fabrics or meshes. In the first embodiment of fig. 1, no additional adhesive has to be provided on the intermediate foil 3. However, in another embodiment, the intermediate foil 3 may be treated with an adhesive to improve the bonding of the intermediate foil 3 to the core layer 2 and the surface layer 4, as for example shown in fig. 4 and described in detail below.

Due to the provision of the intermediate foil 3, the thickness of the surface layer 4 can be reduced compared to conventional solid wood particle board, such that the thickness of each surface layer on each side corresponds to about 8% of the overall board thickness, e.g. each surface layer may be 0.7mm thick for 11mm boards, or 2mm for 40mm boards. Thus, the overall density and weight of the solid wood particle board can be reduced while ensuring a high surface quality.

The intermediate foil 3 is arranged between the core layer 2 and the top surface layer 4 and thus prevents solid wood particles from moving from the top surface layer 4 into the core layer 2, thereby providing a smooth and flat surface of the surface layer 2. This embodiment may be used in various applications, for example to provide an unblemished appearance of furniture.

Due to the use of the intermediate foil 3, the core layer 2 does not need to serve as a carrier for fine surface particles. Thus, the core layer 2 may be produced with an even lower density than in conventional solid wood particle boards, thereby comprising even larger air pockets due to the use of larger solid wood particles in the core layer 2.

Fig. 2 shows a schematic view of a second embodiment of the invention. In contrast to the first preferred embodiment, the solid wood particle board 11 of the second embodiment comprises an additional intermediate foil 5 between the bottom surface layer 1 and the core layer 2.

The intermediate foils 3 and 5 are preferably provided with the same thickness, density and mechanical properties to ensure a balanced structure of the solid wood particle board 11, preventing deformation. Due to the symmetrical arrangement of all layers, it is possible to choose intermediate foils 3 and 5 that are thicker than the intermediate foil 3 in the first embodiment. Preferably, the thickness of each of the intermediate foils 3 and 5 is in the range of 0.05 to 3mm, preferably 0.05 to 2.5mm, most preferably 0.05 to 2.0 mm.

The arrangement of the two intermediate foils 3 and 5 provides two smooth and flat surfaces of the surface layers 1 and 4. This is only required if the top intermediate foil is too thick, to maintain the stability of the panel and to prevent the panel from bending due to the provision of a single thick intermediate foil.

The present invention is not limited to the above-described embodiments, but various modifications and/or additions may be incorporated into the described embodiments without departing from the scope of the invention.

For example, a veneer sheet or other material may also be applied on top of the surface layer 1 and/or the surface layer 4 to provide a decorative surface. The solid wood particle board may also be finished by painting or painting, or may be treated with fire resistant chemicals. Furthermore, other materials like agricultural waste may be incorporated into the layer of solid wood particle board.

The solid wood particle board according to the above embodiments may be produced in a continuous process or in a batch process. According to an embodiment of the continuous manufacturing method, the solid wood particles may be coated with a binder. Subsequently, the adhesive-coated solid wood particles may be placed on a conveyor belt or the like to form the first surface layer 1 and the core layer 2. The vapour permeable intermediate foil 3 may then be positioned in the top of the core layer, wherein the intermediate foil 3 is continuously supplied from a roll, for example. The top surface layer 4 of smaller adhesive coated solid wood particles may be placed on top of the intermediate foil 3. The final stack of adhesive coated solid wood particles and intermediate foils 3 arranged between the solid wood particles may then be transported to a continuous hot pressing apparatus for forming a finished solid wood particle board 10.

As a modification of the method described above, additional layers of solid wood particles, such as for example an additional surface layer 1, may be placed before or after the core particles are placed as described above. Wherein a second intermediate foil 5 may be provided after placing the additional bottom surface layer 1, and then the particles forming the core layer 2 are placed onto the second intermediate foil 5.

In summary, the embodiments described above provide a solid wood particle board, wherein the core layer may be formed of large solid wood particles to achieve a low density of the finished board, and wherein the at least one surface layer may be formed of smaller solid wood particles to achieve at least one smooth surface. The quality of the surface is ensured by arranging an intermediate foil between the core layer and the at least one surface layer, wherein the intermediate foil prevents any movement of the particles of the surface layer into the core layer and prevents any movement of the particles of the core layer into the surface layer. Since the intermediate foil may be vapour permeable, the intermediate foil may not influence the hot pressing process during the manufacture of the solid wood particle board. During hot pressing, the intermediate foil adheres to the particles of the core layer and the surface layer using an adhesive attached to the solid wood particles, so that it is usually not necessary to provide a further adhesive coating on the intermediate foil.

For some applications, it may be advantageous to provide a solid wood particle board having two high quality surfaces. In this case two intermediate foils may be provided on both sides of the core layer. In addition, an intermediate foil having the desired mechanical properties may be used for e.g. reinforcing solid wood particle boards while keeping the overall density of the board low. In this case, two intermediate foils may be used to obtain a balanced configuration of the reinforced solid wood particle board.

Fig. 3 shows an illustrative example of another type of solid wood particle board 12, wherein one or two intermediate foils as described above may be used. The dual density solid wood particle board 12 includes the core layer 2 sandwiched between the first surface layer 1 and the second surface layer 4 as described above. The dual density solid wood particle board 12 depicted in fig. 4 has, in addition to the features described above for the solid wood particle boards 10, 11, a plurality of different regions 6, 7, wherein the high density regions 6 and the low density regions 7 are arranged in an alternating manner, for example as alternating low density and high density longitudinal strips. Similar to that described above for the solid wood particle boards 10, 11 of fig. 1 and 2, one or two intermediate foil layers may be positioned between the core layer 2 and the respective surface layers 1, 4 of the dual density solid wood particle board 12 prior to hot pressing or curing. Thus, an intermediate foil as described above may be applied to various different types of solid wood particle board, while still achieving the technical effect of ensuring a high surface quality and a light weight configuration of the solid wood particle board.

Fig. 4 is a schematic view for illustrating how additional adhesive may be applied to the intermediate foil layers 3, 5 during placement of the solid wood particle layers 1, 2, 4 of the solid wood particle board 11 as shown in fig. 2.

Wherein the intermediate foils 3, 5 are supplied via respective rollers 21. A first intermediate foil layer 5 is provided on top of the laid adhesive-coated solid wood particles of the first surface layer 1 while the first surface layer 1 is being transported along the conveyor belt 22. Additional adhesive may be applied to the top of the first surface layer 1 and the top of the first intermediate foil layer 5 via respective spray nozzles 20 or the like. Thus, both surfaces of the first intermediate foil may be coated with a suitable adhesive to ensure a firm adhesion of the layers 1, 2 of solid wood particles to the intermediate foil 5, while the adhesion of the solid wood particles in each surface or core layer is ensured by the adhesive already applied to the respective solid wood particles before the layers are placed. Similarly, for the second intermediate foil layer 3, a spray nozzle 20 may be provided for coating the top of the placed core layer 2 and the second intermediate foil layer 3 with an adhesive before placing the solid wood particles of the second surface layer 4 on top of the second intermediate foil layer 3.

Examples of the invention

An exemplary embodiment of a solid wood particle board composition has 530kg/m³Has particles in the core layer having a thickness between 0.2mm and 0.8mm and a surface size from 2mm to 120mm in width and a length above 50mm, and has finer particles in the surface layer passing through a mesh of 1.6mm x 1.6 mm. For the core layer, standard polymeric MDI may be used as the binder, and the binder content may be 3.2%. For the surface layer, a conventional MUF resin having MR 0.95 and melamine in an amount of 2.5% may be used as a binder, and the binder content may be 14%. 17g/m with an air resistance of 2 Gurley seconds, for example, may be used²As an intermediate foil.