阅读说明：本技术 用于指/趾甲矫正的套件 (Kit for nail correction ) 是由 D.霍伊贝格 于 2018-05-14 设计创作，主要内容包括：本发明涉及一种用于对人或动物的脚趾甲或手指甲实施指甲矫正方法的套件。(The present invention relates to a kit for applying a method of nail correction to a toenail or fingernail of a human or animal.)

1. A kit for correcting fingernails or toenails comprising

a) A primer (primer coating agent) comprising

40-60% hydroxyethyl methacrylate

40-60% of phosphate ester dimethacrylate,

0.1 to 1.0 percent of an initiator,

b) at least one composition for preparing a photo-curable nail support comprising

15-45% of bisphenol- (A) - (di) methacrylate, urethane-dimethacrylate in a ratio of 1:5 to 5:1,

85-55% of filler and pigment

0.1-1% camphorquinone, amino initiator.

2. The kit for correcting fingernails or toenails of claim 1, further comprising one or more spring supports.

3. The kit for correcting fingernails or toenails as defined in claim 1 or 2, comprising

Two compositions for preparing a photo-curable nail support, namely a first composition comprising

17-21% of bisphenol- (A) - (di) methacrylate, urethane-dimethacrylate in a ratio of 1:4 to 4:1,

79-83% of filler and pigment

0.1-1% camphorquinone, an amino initiator,

and a second composition comprising

36-40% bisphenol- (A) - (di) methacrylate, urethane-dimethacrylate in a ratio of 1:4 to 4:1,

60-64% of fillers and pigments

0.1-1% camphorquinone, amino initiator.

4. A kit for correcting fingernails or toenails as defined in claim 1, 2 or 3, wherein the mass ratio of bisphenol- (a) - (di) methacrylate to urethane-dimethacrylate in the composition for preparing the photo-curable nail support is in the range of 1:2-2:1, preferably 1: 1.

5. The kit for correcting fingernails or toenails as in claims 1-4, wherein the amino initiator is ethyl 4-dimethylaminobenzoate.

6. The kit for correcting fingernails or toenails as in claims 1-4, wherein the primer comprises 0.1-2% of at least one antifungal agent.

7. The kit for correcting fingernails or toenails as in claims 1 to 6, wherein the at least one antifungal agent is selected from the group consisting of econazole, bifonazole, clotrimazole, fenticonazole, ketoconazole, miconazole, oxiconazole.

Examples

The invention is further illustrated by the following exemplary compositions:

A) priming agent (priming agent)

	A1	A2	A3	A4
					Components	(wt%)	(wt%)	(wt%)	(wt%)
Hydroxyethyl methacrylate	49.7	39.7	35.7	45.7
					Phosphate dimethacrylate [ bis (glyceryl dimethacrylate) phosphate]	49.7	59.7	54.6	44.7
Camphorquinone	0.4	0.4	0.5	0.4
					Triethylamine	0.2		0.1	0.2
N, N-dimethyl-p-toluidine		0.2	0.1

B) Nail support (Soft)

	B1	B2	B3	B4	B5
						Components	(wt%)	(wt%)	(wt%)	(wt%)	(wt%)
Bisphenol A (di) methacrylate	16.0	15.0	14.0	30.0	22.0
						Urethane dimethacrylate	16.0	30.0	30.0	15.0	22.0
Silica filler (Aerosil 9200)	20.0	0.0	17.0	16.5	18.5
						Silica filler (Aerosil 7200)	5.0	10.3	15.0	12.5	4.5
Barium glass (median particle size: 13μm)	18.0	13.0	13.0	12.0	14.5.0
						Barium glass (median particle size: 5μm)	3.9	14.0	5.2	5.0	5.5
Polymer particles (median size: 10 μm)	20.0	12.0	4.0	4,5	8.0
						Polymer particles (median size: 6 μm)	0.0	5.0	1.0	3.5	4.0
Camphorquinone	0.6	0.4	0.5	0.6	0.0
						Triethylamine	0.5	0.0	0.1	0.4	0.0
N, N-dimethyl-p-toluidine	0.0	0.3	0.2	0.0	0.0
						2-Ethyl anthraquinone	0.0	0.0	0.0	0.0	0.6
N-phenylglycine	0.0	0.0	0.0	0.0	0.4

C) Nail support (hard)

	C1	C2	C3	C4	C5
						Components	(wt%)	(wt%)	(wt%)	(wt%)	(wt%)
Bisphenol A (di) methacrylate	20.0	25.0	18.0	19.0	15.0
						Urethane dimethacrylate	20.0	13.0	20.0	20.0	23.0
Silica filler (Aerosil 9200)	20.0	0.0	18.0	16.5	19.5
						Silica filler (Aerosil 7200)	5.0	13.3	16.0	15.5	5.5
Barium glass (median particle size: 13μm)	16.0	14.0	12.5	12.0	12.5
						Barium glass (median particle size: 5μm)	3.9	16.1	7.0	6.5	8.5
Polymer particles (median size: 10 μm)	14.0	12.0	6.2	6.0	11.0
						Polymer particles (median size: 6 μm)	0.0	5.0	1.0	3.5	4.0
Camphorquinone	0.6	0.8	0.7	0.6	0.0
						Triethylamine	0.5	0.0	0.2	0.4	0.0
N, N-dimethyl-p-toluidine	0.0	0.8	0.4	0.0	0.0
						2-Ethyl anthraquinone	0.0	0.0	0.0	0.0	0.6
N-phenylglycine	0.0	0.0	0.0	0.0	0.4

Drawings

Fig. 1 illustrates the application of a composition for preparing a photo-curable nail support on a nail.

Figure 2 shows the photocurable composition (after irradiation) on the nail near the nail sinus.

Figure 3 illustrates the application of the photocurable composition on the nail near the nail sinus.

Fig. 4 shows the installation of a spring bracket by fixing a first end (upper) and subsequently the other end of the spring bracket by means of a kit according to the invention.