阅读说明：本技术 金属泡沫的制备方法 (Method for producing metal foam ) 是由 金昭镇 柳东雨 李振圭 于 2018-07-06 设计创作，主要内容包括：本申请提供了用于制备金属泡沫的方法。本申请提供了一种方法，所述方法可以自由地控制金属泡沫的特性例如孔径和孔隙率，还可以制备常规难以生产的膜或片形式特别是薄膜或薄片形式的金属泡沫，以及可以制备具有优异的其他物理特性例如机械强度的金属泡沫。根据本申请的一个实例，还可以有效地形成其中如上所述的金属泡沫以良好的粘合力在金属基材上一体化的结构。(The present application provides a method for making a metal foam. The present application provides a method which can freely control characteristics of metal foam such as pore size and porosity, can also produce metal foam in the form of a film or sheet, particularly a thin film or sheet, which is conventionally difficult to produce, and can produce metal foam having excellent other physical characteristics such as mechanical strength. According to an example of the present application, it is also possible to effectively form a structure in which the metal foam as described above is integrated on the metal substrate with good adhesion.)

1. A method for preparing a metal foam comprising the steps of: forming a first metal foam precursor using a first slurry comprising a metal powder, a binder, and a dispersant; forming a second metal foam precursor on the first metal foam precursor using a second slurry comprising a metal powder, a binder and a dispersant and having a composition different from the composition of the first slurry; and sintering the metal foam precursor.

2. The method for producing a metal foam according to claim 1, wherein the first slurry and the second slurry each comprise 1 to 500 parts by weight of the binder relative to 100 parts by weight of the metal powder; and 10 to 3,000 parts by weight of the dispersant with respect to 100 parts by weight of the binder.

3. The method for preparing a metal foam according to claim 1, wherein the average particle size of the metal powder is in the range of 0.1 μ ι η to about 200 μ ι η.

4. The process for preparing a metal foam according to claim 1, wherein the binder is an alkyl cellulose, polyalkylene carbonate or polyvinyl alcohol-based binder.

5. The method for producing metal foam according to claim 1, wherein the dispersant is an alcohol.

6. The method for producing metal foam of claim 1, wherein the slurry does not comprise a solvent.

7. The method for preparing metal foam according to claim 1, wherein the metal foam precursor is formed in the form of a film or sheet.

8. The method for producing a metal foam according to claim 1, wherein the sintering is performed at a temperature in the range of 500 ℃ to 2000 ℃.

9. The method for producing a metal foam of claim 1, wherein the first metal foam precursor and the second metal foam precursor are formed in contact with each other.

10. The method for producing metal foam according to claim 1, wherein a ratio (a/B) of a weight ratio (a) of the metal powder in the first slurry to a weight ratio (B) of the metal powder in the second slurry is in a range of 0.1 to 20.

11. The method for preparing metal foam according to claim 1, wherein a ratio (C/D) of a weight part (C) of the binder in the first slurry to 100 weight parts of the metal powder to a weight part (D) of the binder in the second slurry to 100 weight parts of the metal powder is in a range of 0.01 to 20.

12. The method for producing a metal foam according to claim 1, wherein a ratio (E/F) of the weight part (E) of the dispersant in the first slurry to 100 weight parts of the metal powder to the weight part (F) of the dispersant in the second slurry to 100 weight parts of the metal powder is in a range of 0.01 to 20.

13. The method for producing a metal foam according to claim 1, wherein the first metal precursor is present in a gravitational direction of the second metal precursor based on the second metal precursor.

Technical Field

This application claims benefit based on priority of korean patent application No. 10-2017-.

The present application relates to a method for producing a metal foam.

Background

Metal foam can be applied to various fields including light structures, transportation machinery, building materials, or energy absorption devices, etc. due to having various and useful characteristics such as light weight characteristics, energy absorption characteristics, heat insulation characteristics, fire resistance, or environmental friendliness. In addition, the metal foam not only has a high specific surface area, but also can further improve the flow of fluid (e.g., liquid and gas) or electrons, and thus can also be usefully used by being applied to a substrate for a heat exchanger, a catalyst, a sensor, an actuator, a secondary battery, a Gas Diffusion Layer (GDL), a microfluidic flow controller, or the like.

Disclosure of Invention

Technical problem

It is an object of the present application to provide a method which can freely control characteristics of a metal foam such as pore size and porosity, can also produce a metal foam in the form of a film or sheet, particularly a thin film or sheet, which is conventionally difficult to produce, and can produce a metal foam having excellent other physical characteristics such as mechanical strength. Furthermore, it is another object of the present application to provide a manufacturing process that can be controlled such that the cell characteristics inside a single metal foam can be varied.

Technical scheme

In the present application, the term metal foam or metal skeleton means a porous structure comprising a metal as a main component. Here, the metal as a main component means that the proportion of the metal is 55 wt% or more, 60 wt% or more, 65 wt% or more, 70 wt% or more, 75 wt% or more, 80 wt% or more, 85 wt% or more, 90 wt% or more, or 95 wt% or more based on the total weight of the metal foam or the metal skeleton. The upper limit of the proportion of the metal contained as the main component is not particularly limited. For example, the proportion of metal may be 100 wt% or less, or less than about 100 wt%.

The term porous nature may mean a porosity of at least 30% or greater, 40% or greater, 50% or greater, 60% or greater, 70% or greater, 75% or greater, or 80% or greater. The upper limit of the porosity is not particularly limited, and may be, for example, less than about 100%, about 99% or less, or about 98% or less. The porosity can be calculated in a known manner by calculating the density of the metal foam or the like.

The method for preparing a metal foam of the present application may comprise the step of sintering a metal foam precursor comprising a metal component. In the present application, the term metal foam precursor means the structure prior to a process, such as a sintering process, performed for forming the metal foam, i.e. the structure prior to forming the metal foam. Further, even when the metal foam precursor is referred to as a porous metal foam precursor, it does not necessarily have to be porous by itself, and may be referred to as a porous metal foam precursor for convenience as long as it can be finally formed into a metal foam of a porous metal structure.

In the present application, the metal foam precursor may be formed using a slurry including at least a metal component, a dispersant, and a binder.

Here, as the metal component, metal powder may be applied. Examples of the applicable metal powder are determined according to purposes, which are not particularly limited, but may be exemplified by any one powder selected from copper powder, molybdenum powder, silver powder, platinum powder, gold powder, aluminum powder, chromium powder, indium powder, tin powder, magnesium powder, phosphorus powder, zinc powder, and manganese powder, metal powder mixed with two or more of the foregoing, or alloy powder of two or more of the foregoing, but are not limited thereto.

If necessary, the metal component may contain, as an optional component, a metal component having a relative magnetic permeability and an electric conductivity within predetermined ranges. Such metal components may assist in the selection of the induction heating method during sintering. However, since sintering does not necessarily have to be performed by an induction heating method, the metal component having the above-described magnetic permeability and electric conductivity is not an essential component.

In one example, as the metal powder that may be optionally added, a metal powder having a relative magnetic permeability of 90 or more may be used. The term relative permeability (μ)_r) Is the magnetic permeability (mu) of the relevant material and the magnetic permeability (mu) in vacuum₀) Ratio of (mu/. mu.₀). In another example, the relative permeability may be 95 or greater, 100 or greater, 110 or greater, 120 or greater, 130 or greater, 140 or greater, 150 or greater, 160 or greater, 170 or greater, 180 or greater, 190 or greater, 200 or greater, 210 or greater, 220 or greater, 230 or greater, 240 or greater, 250 or greater, 260 or greater, 270 or greater, 280 or greater, 290 or greater, 300 or greater, 310 or greater, 320 or greater, 330 or greater, 340 or greater, 350 or greater, 360 or greater, 370 or greater, 380 or greater, 390 or greater, 400 or greater, 410 or greater, 420 or greater, 430 or greater, 440 or greater, 450 or greater, 460 or greater, 470 or greater, 480 or greater, 490 or greater, 500 or greater, 520 or greater, 430 or greater, 440 or greater, 450 or greater, 460 or greater, 470 or greater, 480 or greater, 490 or greater, 500 or greater, 520 or greater, 550 or greater, 570 or greater, 530 or greater, 560 or greater, or a magnetic permeability may be greater than the magnetic permeability of the magnetic materials, 580 or greater, or 590 or greater. The upper limit of the relative permeability is not particularly limited, because the higher the value, the more advantageous in the case of applying induction heating. In one example, the upper limit of the relative permeability may be, for example, about 300,000 or less.

The metal powder that may be optionally added may also be a conductive metal powder. In the present application, the term conductive metal powder may mean a powder of a metal or an alloy thereof having an electrical conductivity of about 8MS/m or more, 9MS/m or more, 10MS/m or more, 11MS/m or more, 12MS/m or more, 13MS/m or more, or 14.5MS/m at 20 ℃. The upper limit of the conductivity is not particularly limited, and may be, for example, about 30MS/m or less, 25MS/m or less, or 20MS/m or less.

In the present application, the metal powder having the relative magnetic permeability and electric conductivity may also be simply referred to as conductive magnetic metal powder.

Specific examples of such conductive magnetic metal powder may be exemplified by powders of nickel, iron, cobalt, or the like, but are not limited thereto.

If used, the proportion of the electrically conductive magnetic metal powder in the total metal powder is not particularly limited. For example, the ratio may be adjusted so that the ratio can generate appropriate joule heat upon induction heating. For example, the metal powder may include 30 wt% or more of the conductive magnetic metal powder based on the weight of the total metal powder. In another example, the proportion of the electrically conductive, magnetic metal powder in the metal powder may be about 35 wt% or more, about 40 wt% or more, about 45 wt% or more, about 50 wt% or more, about 55 wt% or more, 60 wt% or more, 65 wt% or more, 70 wt% or more, 75 wt% or more, 80 wt% or more, 85 wt% or more, or 90 wt% or more. The upper limit of the proportion of the conductive magnetic metal powder is not particularly limited, and may be, for example, less than about 100% by weight, or 95% by weight or less. However, the above-described ratios are exemplary ratios.

The size of the metal powder is also selected in consideration of desired porosity or pore size, etc., but is not particularly limited, wherein the average particle diameter of the metal powder may be, for example, in the range of about 0.1 μm to about 200 μm. In another example, the average particle size can be about 0.5 μm or greater, about 1 μm or greater, about 2 μm or greater, about 3 μm or greater, about 4 μm or greater, about 5 μm or greater, about 6 μm or greater, about 7 μm or greater, or about 8 μm or greater. In another example, the average particle size can be about 150 μm or less, 100 μm or less, 90 μm or less, 80 μm or less, 70 μm or less, 60 μm or less, 50 μm or less, 40 μm or less, 30 μm or less, or 20 μm or less. As the metal in the metal particles, metals having different average particle diameters may also be applied. The average particle diameter may be selected from an appropriate range in consideration of a desired shape of the metal foam (for example, thickness, porosity, or the like of the metal foam).

Here, the average particle diameter of the metal powder may be obtained by a known particle size analysis method, and for example, the average particle diameter may be a so-called D50 particle diameter.

The ratio of the metal component (metal powder) in the slurry as described above is not particularly limited, and may be selected in consideration of desired viscosity and process efficiency. In one example, the proportion of the metal component in the slurry may be about 0.5% to 95% on a weight basis, but is not limited thereto. In another example, the ratio can be about 1% or more, about 1.5% or more, about 2% or more, about 2.5% or more, about 3% or more, about 5% or more, 10% or more, 15% or more, 20% or more, 25% or more, 30% or more, 35% or more, 40% or more, 45% or more, 50% or more, 55% or more, 60% or more, 65% or more, 70% or more, 75% or more, or 80% or more, or can be about 90% or less, about 85% or less, about 80% or less, about 75% or less, about 70% or less, about 65% or less, 60% or less, 55% or less, 50% or less, 45% or less, 40% or less, 35% or less, 30% or less, 15% or less, or 20% or less, or 30% or less, or 20% or less, or a combination thereof, Or 5% or less, but not limited thereto.

The metal foam precursor may be formed by using a slurry containing a dispersant and a binder, and a metal powder.

Here, as the dispersant, for example, alcohol may be used. As the alcohol, monohydric alcohols having 1 to 20 carbon atoms, such as methanol, ethanol, propanol, pentanol, octanol, ethylene glycol, propylene glycol, pentanol, 2-methoxyethanol, 2-ethoxyethanol, 2-butoxyethanol, glycerol, texanol, or terpineol; or a diol having 1 to 20 carbon atoms, such as ethylene glycol, propylene glycol, hexylene glycol, octylene glycol or pentylene glycol; or a polyol, but the kind is not limited to the above.

The slurry may also comprise a binder. The kind of the binder is not particularly limited and may be appropriately selected according to the kind of the metal component or the dispersant, etc. applied when producing the slurry. For example, the adhesive may be exemplified by: alkylcelluloses containing alkyl groups having 1 to 8 carbon atoms, such as methylcellulose or ethylcellulose; polyalkylene carbonates containing alkylene units having 1 to 8 carbon atoms, such as polypropylene carbonate or polyethylene carbonate; or a polyvinyl alcohol-based binder (hereinafter, may be referred to as a polyvinyl alcohol compound), such as polyvinyl alcohol or polyvinyl acetate, and the like, but is not limited thereto.

The ratio of the components in the slurry as described above is not particularly limited. The ratio may be adjusted in consideration of process efficiency such as coating characteristics and formability when a process using the slurry is used.

For example, in the slurry, the binder may be included in a proportion of about 1 part by weight to 500 parts by weight with respect to 100 parts by weight of the above metal component. In another example, the ratio may be about 2 parts by weight or greater, about 3 parts by weight or greater, about 4 parts by weight or greater, about 5 parts by weight or greater, about 6 parts by weight or greater, about 7 parts by weight or greater, about 8 parts by weight or greater, about 9 parts by weight or greater, about 10 parts by weight or greater, about 20 parts by weight or greater, about 30 parts by weight or greater, about 40 parts by weight or greater, about 50 parts by weight or greater, about 60 parts by weight or greater, about 70 parts by weight or greater, about 80 parts by weight or greater, or about 90 parts by weight or greater, about 100 parts by weight or greater, about 110 parts by weight or greater, about 120 parts by weight or greater, about 130 parts by weight or greater, about 140 parts by weight or greater, about 150 parts by weight or greater, about 200 parts by weight or greater, or about 250 parts by weight or greater, and may be about 450 parts by weight or less, about 400 parts by weight or greater, and may be about 450 parts by weight or less, About 350 parts by weight or less, about 300 parts by weight or less, about 250 parts by weight or less, about 200 parts by weight or less, about 150 parts by weight or less, about 100 parts by weight or less, about 50 parts by weight or less, about 40 parts by weight or less, about 30 parts by weight or less, about 20 parts by weight or less, or about 10 parts by weight or less.

In the slurry, the dispersant may be included in a proportion of about 10 parts by weight to 3,000 parts by weight with respect to 100 parts by weight of the binder. In another example, the ratio may be about 20 parts by weight or greater, about 30 parts by weight or greater, about 40 parts by weight or greater, about 50 parts by weight or greater, about 60 parts by weight or greater, about 70 parts by weight or greater, about 80 parts by weight or greater, about 90 parts by weight or greater, about 100 parts by weight or greater, about 200 parts by weight or greater, about 300 parts by weight or greater, about 400 parts by weight or greater, about 500 parts by weight or greater, about 550 parts by weight or greater, about 600 parts by weight or greater, or about 650 parts by weight, and may be about 2,800 parts by weight or less, about 2,600 parts by weight or less, about 2,400 parts by weight or less, about 2,200 parts by weight or less, about 2,000 parts by weight or less, about 1,800 parts by weight or less, about 1,600 parts by weight or less, about 1,400 parts by weight or less, about 1,200 parts by weight or less, about 1,000 parts by weight or less, or about 1,000 parts by weight or less.

In the present specification, the unit parts by weight means a weight ratio between the components unless otherwise specified.

The slurry may further contain a solvent, if necessary. However, according to an example of the present application, the slurry may not contain a solvent. That is, even if the dispersant is regarded as a solvent, solvent components other than the dispersant may not be included, whereby the method of the present application can be more effectively performed. As the solvent, an appropriate solvent can be used in consideration of the solubility of the slurry component (for example, the metal component, the binder, or the like). For example, as the solvent, those having a dielectric constant in the range of about 10 to 120 may be used. In another example, the dielectric constant can be about 20 or greater, about 30 or greater, about 40 or greater, about 50 or greater, about 60 or greater, or about 70 or greater, or can be about 110 or less, about 100 or less, or about 90 or less. Such a solvent may be exemplified by water, an alcohol having 1 to 8 carbon atoms (e.g., ethanol, butanol or methanol), DMSO (dimethyl sulfoxide), DMF (dimethylformamide), NMP (N-methylpyrrolidone), or the like, but is not limited thereto.

When the solvent is applied, it may be present in the slurry in a ratio of about 50 parts by weight to 400 parts by weight with respect to 100 parts by weight of the binder, but is not limited thereto. In another example, the proportion of the solvent may be about 60 parts by weight or more, about 70 parts by weight or more, about 80 parts by weight or more, about 90 parts by weight or more, about 100 parts by weight or more, about 110 parts by weight or more, about 120 parts by weight or more, about 130 parts by weight or more, about 140 parts by weight or more, about 150 parts by weight or more, about 160 parts by weight or more, about 170 parts by weight or more, about 180 parts by weight or more, or about 190 parts by weight or more, or may be about 350 parts by weight or less, 300 parts by weight or less, or 250 parts by weight or less, but is not limited thereto.

In addition to the above components, the slurry may contain further required known additives. However, the process of the present application can be carried out using a slurry that does not contain the blowing agent of known additives.

The method of forming the metal foam precursor using the slurry as described above is not particularly limited. In the art of producing metal foams, various methods for forming metal foam precursors are known, and all of these methods may be applied in the present application. For example, the metal foam precursor may be formed by holding the slurry in a suitable template, or by coating the slurry in a suitable manner.

In one example of the present application, when the metal foam precursor is formed using the slurry, a method using a slurry having at least two different compositions may be applied. Here, the fact that the slurries have different compositions means the following cases: a case where two slurries similarly contain at least a metal powder, a binder and a dispersant, but different components are used as at least one component of the metal powder, the binder and the dispersant; cases where the three components differ in their compounding ratio even when they are used in the same kind; or the case where the types and the mixing ratios are all different.

Thus, the preparation method of the present application may comprise the steps of: forming a first metal foam precursor using the first slurry; and forming a second metal foam precursor on the first metal foam precursor using a second slurry having a composition different from the composition of the first slurry.

Here, the first slurry and the second slurry may each include a metal powder, a binder, and a dispersant, but their compositions are different as described above.

In addition to the step of forming two metal foam precursors with two slurries, the production method of the present application can also produce three or more metal foam precursors using other slurries, wherein in the case of using three or more slurries in this manner, if at least two of them have different compositions, the compositions of the remaining slurries can also be the same as those of the other slurries.

As described above, the first paste and the second paste may each include 1 to 500 parts by weight of the binder with respect to 100 parts by weight of the metal powder; and 10 to 3,000 parts by weight of a dispersant with respect to 100 parts by weight of the binder, wherein detailed types of the metal powder, the binder and the dispersant are as described above, but compositions of the first slurry and the second slurry are different from each other.

When the metal foam precursors are formed through the above steps, the first metal foam precursor and the second metal foam precursor may also be formed in contact with each other, and if necessary, another element such as a metal sheet may also be present between the first metal foam precursor and the second metal foam precursor.

In one example, the first and second slurries may have at least different weight ratios of the metal powder contained therein. In this case, the ratio (a/B) of the weight ratio (a, wt%) of the metal powder in the first slurry to the weight ratio (B, wt%) of the metal powder in the second slurry may be in the range of about 0.1 to 20. In another example, the ratio (a/B) may be about 0.3 or greater, 0.5 or greater, 0.7 or greater, 0.9 or greater, or 1 or greater, or may be about 18 or less, 16 or less, 14 or less, 12 or less, 11 or less, 10 or less, 9 or less, 8 or less, 7 or less, 6 or less, 5 or less, 4 or less, 3 or less, or 2.5 or less.

In one example, the first and second pastes may have at least different proportions of binder contained therein. In this case, a ratio (C/D) of the weight part (C) of the binder in the first paste to 100 weight parts of the metal powder to the weight part (D) of the binder in the second paste to 100 weight parts of the metal powder may be in a range of 0.01 to 20. In another example, the ratio (C/D) may be about 0.05 or greater, 0.1 or greater, 0.2 or greater, or 0.3 or greater, or may be about 18 or less, 16 or less, 14 or less, 12 or less, 11 or less, 10 or less, 9 or less, 8 or less, 7 or less, 6 or less, 5 or less, 4 or less, 3 or less, 2 or less, or approximately 1.5 or less.

In one example, the first and second slurries may have at least different proportions of dispersant contained therein. In this case, a ratio (E/F) of the weight part (E) of the dispersant in the first slurry to 100 weight parts of the metal powder to the weight part (F) of the dispersant in the second slurry to 100 weight parts of the metal powder may be in the range of 0.01 to 20. In another example, the ratio (C/D) may be about 0.05 or greater, 0.1 or greater, 0.2 or greater, or 0.3 or greater, or may be about 18 or less, 16 or less, 14 or less, 12 or less, 11 or less, 10 or less, 9 or less, 8 or less, 7 or less, 6 or less, 5 or less, 4 or less, 3 or less, 2 or less, or 1.5 or less, or approximately about 1 or less.

For example, if three or more slurries are applied in the preparation of the metal foam precursor, at least two of them may satisfy the relationship.

In this case, it is advantageous for the disclosed method of the present application to be effectively applied that, in the first slurry and the second slurry satisfying the above-described relationship, the first slurry first forms a metal foam precursor by application or the like, and then the second slurry forms the metal foam precursor thereon.

Therefore, when the metal foam precursor is formed using the first slurry and the second slurry satisfying the above-described relationship, the first metal precursor may exist in the gravity direction of the second metal precursor based on the second metal precursor. That is, the second metal precursor may be present on top of the first metal precursor.

The application of a coating process may be advantageous when producing the metal foam in the form of a film or sheet according to an example of the present application, in particular when producing the metal foam in the form of a film or sheet. For example, the desired metal foam may be formed by coating the slurry on a suitable substrate to form a precursor, followed by a sintering process to be described below.

The shape of such a metal foam precursor is not particularly limited, since it is determined according to the desired metal foam. In one example, the metal foam precursor may be in the form of a film or sheet. For example, when the precursor is in the form of a film or sheet, the thickness can be 2,000 μm or less, 1,500 μm or less, 1,000 μm or less, 900 μm or less, 800 μm or less, 700 μm or less, 600 μm or less, 500 μm or less, 400 μm or less, 300 μm or less, 200 μm or less, 150 μm or less, about 100 μm or less, about 90 μm or less, about 80 μm or less, about 70 μm or less, about 60 μm or less, or about 55 μm or less. Metal foams, due to their porous structural characteristics, generally have brittle characteristics, which make it problematic: they are difficult to produce in the form of films or sheets (particularly films or sheets), and they are easily broken even at the time of production. However, according to the method of the present application, it is possible to form a metal foam having pores uniformly formed inside and excellent mechanical properties as well as a thin thickness.

Here, the lower limit of the precursor thickness is not particularly limited. For example, the film-like or sheet-like precursor can have a thickness of about 5 μm or more, 10 μm or more, or about 15 μm or more.

The precursor thickness is the total thickness comprising the first metal foam precursor and the second metal foam precursor, and if another metal foam precursor is present, the thickness of the precursors may also be the combined thickness. The thickness ratio of each sub-precursor in the total metal foam precursor may be appropriately adjusted according to the purpose without any particular limitation.

If necessary, a suitable drying process may also be performed during the process of forming the metal foam precursor. For example, the metal foam precursor may also be formed by shaping the slurry by the above-described coating method or the like, and then drying it for a constant time. When a plurality of metal foam precursors are formed, drying may also be performed after each precursor is formed, and may also be performed finally after all of the metal foam precursors are formed. The conditions of drying are not particularly limited, and may be controlled, for example, at a level at which the solvent contained in the slurry can be removed to a desired level. For example, drying may be performed by holding the formed slurry at a temperature in the range of about 50 ℃ to 250 ℃, about 70 ℃ to 180 ℃, or about 90 ℃ to 150 ℃ for an appropriate time. The drying time may also be selected within an appropriate range.

In one example, a metal foam precursor can be formed on a metal substrate. For example, a metal foam precursor may be formed by coating the above slurry on a metal substrate and, if necessary, by the above drying process. Depending on the application of the metal foam, it may be desirable to form the metal foam on a metal substrate (base). Therefore, conventionally, metal foams are attached to metal substrates to form the above-described structures. However, this method has difficulty in ensuring adhesion between the metal foam and the metal substrate, and in particular, it has difficulty in attaching the thin metal foam on the metal substrate. However, according to the method disclosed in the present application, even in the case of a metal foam having a thin thickness, it can be formed on a metal substrate with good adhesion. If necessary, a metal substrate may also be provided between the precursors.

The type of the metal base material is determined according to the purpose, which is not particularly limited, and for example, a base material of the same metal as the metal foam or a different metal may be applied.

For example, the metal substrate may be a substrate selected from any one of metals of copper, molybdenum, silver, platinum, gold, aluminum, chromium, indium, tin, magnesium, phosphorus, zinc, and manganese, or a mixture or alloy of two or more thereof, and if necessary, a substrate selected from any one of nickel, iron, and cobalt as the above-described conductive magnetic metal, or a mixture or alloy of two or more thereof; or a base material of a mixture or alloy of the conductive magnetic metal and the other metals mentioned above, and the like.

The thickness of such a metal base material is not particularly limited, and may be appropriately selected according to the purpose.

The metal foam may be prepared by sintering a metal foam precursor formed in the manner described above. In this case, the method of performing sintering for producing the metal foam is not particularly limited, and a known sintering method may be applied. That is, sintering may be performed by applying an appropriate amount of heat to the metal foam precursor in an appropriate manner.

In this case, the conditions of sintering may be controlled in consideration of the state of the metal precursor applied (for example, the kind and amount of the metal powder, or the kind and amount of the binder or the dispersant, etc.), so that the binder and the dispersant, etc. may be removed while the metal powder is connected to form the porous structure, wherein the specific conditions are not particularly limited.

For example, sintering may be performed by maintaining the precursor at a temperature in the range of about 500 ℃ to 2000 ℃, 700 ℃ to 1500 ℃, or 800 ℃ to 1200 ℃, and the holding time may also be optionally selected. In one example, the holding time may be in the range of about 1 minute to 10 hours, but is not limited thereto.

That is, as described above, the sintering may be controlled in consideration of the state of the metal precursor to be applied (for example, the kind and amount of the metal powder, or the kind and amount of the binder or the dispersant, etc.) so that the metal powder is connected to form the porous structure and the binder and the dispersant, etc. may be removed.

The application also relates to metal foams. The metal foam may be a metal foam produced by the above-described method. In one example, such metal foam may be in the form of an attachment to the metal substrate or base described above.

The porosity of the metal foam may be in the range of about 40% to 99%. As described above, according to the method of the present application, porosity and mechanical strength can be controlled while containing uniformly formed pores. The porosity may be 50% or greater, 60% or greater, 70% or greater, 75% or greater, or 80% or greater, or may be 95% or less, or 90% or less.

Further, since the unit using different kinds of slurry is included, the porosity may vary in a gradient along the thickness direction of the metal foam, or may vary irregularly.

The metal foam may also be present in the form of a film or sheet. In one example, the metal foam may be in the form of a film or sheet. The thickness of such metal foam in the form of a film or sheet may be 2,000 μm or less, 1,500 μm or less, 1,000 μm or less, 900 μm or less, 800 μm or less, 700 μm or less, 600 μm or less, 500 μm or less, 400 μm or less, 300 μm or less, 200 μm or less, 150 μm or less, about 100 μm or less, about 90 μm or less, about 80 μm or less, about 70 μm or less, about 60 μm or less, or about 55 μm or less. For example, the thickness of the film-like or sheet-like metal foam may be about 10 μm or more, about 20 μm or more, about 30 μm or more, about 40 μm or more, about 50 μm or more, about 100 μm or more, about 150 μm or more, about 200 μm or more, about 250 μm or more, about 300 μm or more, about 350 μm or more, about 400 μm or more, about 450 μm or more, or about 500 μm or more.

The metal foam may have excellent mechanical strength, and for example, the tensile strength thereof may be 2.5MPa or more, 3MPa or more, 3.5MPa or more, 4MPa or more, 4.5MPa or more, or 5MPa or more. Further, the tensile strength can be about 10MPa or less, about 9MPa or less, about 8MPa or less, about 7MPa or less, or about 6MPa or less. Such tensile strength can be measured, for example, by KS B5521 at room temperature.

Such metal foams may be used in a variety of applications requiring porous metal precursors. In particular, according to the method of the present application, as described above, a thin-film or flake-like metal foam having excellent mechanical strength and a desired level of porosity can be produced, thereby expanding the application of the metal foam as compared with conventional metal foams.

Examples of metal foam applications that may be employed include, but are not limited to, machine tool saddles, heat dissipating materials, sound absorbing materials, heat insulating materials, heat exchangers, heat sinks, dust proofing materials, battery materials such as electrodes, and the like.

Advantageous effects

The present application provides a method which can freely control characteristics of metal foam such as pore size and porosity, can also produce metal foam in the form of a film or sheet, particularly a thin film or sheet, which is conventionally difficult to produce, and can produce metal foam having excellent other physical characteristics such as mechanical strength. According to an example of the present application, a structure in which such metal foam is integrated on a metal substrate with good adhesion can be efficiently formed.

Drawings

Fig. 1 and 2 are SEM photographs of the metal foam formed in the example.

Detailed Description

Hereinafter, the present application will be described in detail by examples and comparative examples, but the scope of the present application is not limited to the following examples.