阅读说明：本技术 一种适用于机械钻头的高性能材料 (High-performance material suitable for mechanical drill bit ) 是由 蒋友河 于 2019-11-08 设计创作，主要内容包括：本发明是一种适用于机械钻头的高性能材料,包含添加剂和载体,配方中的原料按重量百分比组成分别是：0.5～6%碳纤维,10～35%马来酸酐接枝聚丙烯,1～10%青铜粉,0～3%精铁粉,0～2.5%环氧树脂,5～20%纳米硫酸钙,10～20%氟橡胶,30～60%催化剂,通过本方法制备的产品,具有强度高、耐磨性好的特点；钻头材料在满足所有API标准的力学性能的基础上,抗疲劳性能得到提高,疲劳寿命得到延长。(The invention relates to a high-performance material suitable for a mechanical drill bit, which comprises an additive and a carrier, wherein the raw materials in the formula comprise the following components in percentage by weight: 0.5-6% of carbon fiber, 10-35% of maleic anhydride grafted polypropylene, 1-10% of bronze powder, 0-3% of fine iron powder, 0-2.5% of epoxy resin, 5-20% of nano calcium sulfate, 10-20% of fluororubber and 30-60% of catalyst, and the product prepared by the method has the characteristics of high strength and good wear resistance; on the basis of meeting the mechanical properties of all API standards, the fatigue resistance of the drill bit material is improved, and the fatigue life is prolonged.)

一种适用于机械钻头的高性能材料

技术领域

本发明公开了一种适用于机械钻头的高性能材料。

背景技术

钻头是一般钻子或钻挖机器所采用的切割工具，以切割出圆形的孔洞，钻头的基本原理是使钻头切边旋转、切削工件、再由钻槽进行排除钻屑，现有的技术中，钻头的使用寿命普遍较短，现有钻头的耐磨性能不足，经常会出现折断或磨损的现象。

发明内容

针对上述现有技术存在的问题，本发明提供一种适用于机械钻头的高性能材料，具有强度高、耐磨性好的特点；钻头材料在满足所有API标准的力学性能的基础上，抗疲劳性能得到提高，疲劳寿命得到延长。

为了实现上述目的，本发明通过以下技术方案实现：一种适用于机械钻头的高性能材料，配方中的原料按重量百分比组成分别是：0.5～6%碳纤维，10～35%马来酸酐接枝聚丙烯，1～10%青铜粉， 0～3%精铁粉，0～2.5%环氧树脂，5～20%纳米硫酸钙，10～20%氟橡胶，30～60%催化剂。

有益效果：通过本方法制备的产品，具有强度高、耐磨性好的特点；钻头材料在满足所有API标准的力学性能的基础上，抗疲劳性能得到提高，疲劳寿命得到延长。

具体实施方式

实施例1

一种适用于机械钻头的高性能材料，配方中的原料按重量百分比组成分别是：0.5%碳纤维，10%马来酸酐接枝聚丙烯，1%青铜粉，1%精铁粉，1%环氧树脂，5%纳米硫酸钙，10%氟橡胶，30%催化剂，此时钻头的强度不足，容易出现折断的现象。

实施例2

一种适用于机械钻头的高性能材料，配方中的原料按重量百分比组成分别是：6%碳纤维，35%马来酸酐接枝聚丙烯，10%青铜粉，3%精铁粉，2.5%环氧树脂，20%纳米硫酸钙，20%氟橡胶，60%催化剂，此时不能满足所有API标准的力学性能。

实施例3

一种适用于机械钻头的高性能材料，配方中的原料按重量百分比组成分别是：4%碳纤维，23%马来酸酐接枝聚丙烯，5%青铜粉， 1.5%精铁粉，1.25%环氧树脂，13%纳米硫酸钙，15%氟橡胶，45%催化剂，此时具有强度高、耐磨性好的特点；钻头材料在满足所有API标准的力学性能的基础上，抗疲劳性能得到提高，疲劳寿命得到延长。