阅读说明：本技术 一种具有高温软化定型功能的实木地板板材生产加工工艺 (Production and processing technology of solid wood floor board with high-temperature softening and shaping functions ) 是由 姜金法 于 2019-09-12 设计创作，主要内容包括：本发明涉及一种具有高温软化定型功能的实木地板板材生产加工工艺,其具体步骤如下：(1)将需要处理的实木地板板材整理平整,每块板材均放置在加热管道上；(2)加热管道上的板材利用升降机构升降后,挤压叠合在一起形成整体；(3)两端分别连接蒸汽管道,分别用于供给蒸汽和回收蒸汽；(4)蒸汽供给过程中,调节处理蒸汽供给量和升级机构挤压压强；(5)保持步骤(4)方式持续处理板材；(6)处理结束后,自然降温冷却到室温；(7)取下板材进行检测,完成实木地板板材的软化定型处理。该发明方法通过特殊的处理工艺,能同时针对若干板材一次性挤压处理定型,在处理过程中,能同时完成板材的软化、高压处理,且能获得定型和脱水效果。(The invention relates to a production and processing technology of a solid wood floor board with a high-temperature softening and shaping function, which comprises the following specific steps: (1) the method comprises the following steps of (1) finishing and flattening solid wood floor plates to be treated, wherein each plate is placed on a heating pipeline; (2) after the plates on the heating pipeline are lifted by the lifting mechanism, the plates are extruded and overlapped together to form a whole; (3) two ends of the steam pipe are respectively connected with a steam pipeline which is respectively used for supplying steam and recovering the steam; (4) in the steam supply process, adjusting the supply amount of the processing steam and the extrusion pressure of the upgrading mechanism; (5) continuously processing the plate in the mode of the step (4); (6) after the treatment is finished, naturally cooling to room temperature; (7) and taking down the board for detection to finish the softening and shaping treatment of the solid wood floor board. The method can simultaneously perform one-time extrusion treatment and shaping on a plurality of plates through a special treatment process, can simultaneously complete softening and high-pressure treatment of the plates in the treatment process, and can obtain shaping and dehydration effects.)

1. A production and processing technology of solid wood floor boards with high-temperature softening and shaping functions is characterized by comprising the following steps: the method comprises the following specific steps:

(1) the method comprises the following steps of (1) finishing and flattening solid wood floor plates to be treated, wherein each plate is placed on a heating pipeline;

(2) after the plates on the heating pipeline are lifted by the lifting mechanism, the plates are extruded and overlapped together to form a whole;

(3) the heating pipeline is hollow inside, and two ends of the heating pipeline are respectively externally connected with a steam pipeline and are respectively used for supplying steam and recovering the steam;

(4) in the steam supply process, adjusting the supply amount of the processing steam and the extrusion pressure of the upgrading mechanism;

(5) continuously processing the plate in the mode of the step (4);

(6) after the treatment is finished, closing steam supply, and naturally cooling to room temperature;

(7) and loosening the boards which are overlapped together by using the lifting mechanism, taking down the boards for detection, and finishing the softening and shaping treatment of the solid wood floor boards.

2. The production and processing technology of the solid wood floor board with the high-temperature softening and shaping functions as claimed in claim 1, which is characterized in that: the heating pipeline is a copper alloy pipe or an aluminum alloy pipe.

3. The production and processing technology of the solid wood floor board with the high-temperature softening and shaping functions as claimed in claim 1, which is characterized in that: the upgrading mechanism in the step (2) is a hydraulic mechanism, a plurality of upgrading mechanisms are arranged, and the upgrading mechanisms are distributed at the periphery of the lower part of the plate to be extruded.

4. The production and processing technology of the solid wood floor board with the high-temperature softening and shaping functions as claimed in claim 1, which is characterized in that: the external steam pipeline is used for supplying steam to the external pipeline, and the recovery pipeline is used for recycling after recovering the steam.

5. The production and processing technology of the solid wood floor board with the high-temperature softening and shaping functions as claimed in claim 1, which is characterized in that: in the step (5), the treatment temperature is 110-138 ℃, the treatment time is 60-120 minutes, and the extrusion pressure is kept at 160-200 MPa.

6. The production and processing technology of the solid wood floor board with the high-temperature softening and shaping functions as claimed in claim 1, which is characterized in that: in the process method, the thickness of the processed plate is 1-30 mm.

7. The production and processing technology of the solid wood floor board with the high-temperature softening and shaping functions as claimed in claim 1, which is characterized in that: the process method completes softening, high pressure, sizing and dehydration processes simultaneously to obtain the solid wood floor board meeting the requirements for subsequent processing treatment.

Technical Field

The invention belongs to the technical field of solid wood floor processing, and particularly relates to a production and processing technology of a solid wood floor board with a high-temperature softening and shaping function.

Background

In the production and manufacturing process of the solid wood floor, proper plates need to be provided, and the plates need to have proper performance, so that the condition that deformation occurs in the subsequent use of finished products is avoided, and the working performance of the finished products is prevented from being influenced. In particular, since the board for the floor is required to have special properties, a general processing method is not favorable for processing the board, and the subsequent production and processing method has high cost, for which, a proper method is necessary for processing so as to obtain a better board processing effect.

Disclosure of Invention

The invention aims to provide a production and processing technology of a solid wood floor board with a high-temperature softening and shaping function, so that the solid wood floor board can be better processed to obtain the solid wood floor board meeting the requirements.

In order to achieve the above object, the present invention has the following technical means.

A production and processing technology of a solid wood floor board with a high-temperature softening and shaping function comprises the following specific steps:

(1) the method comprises the following steps of (1) finishing and flattening solid wood floor plates to be treated, wherein each plate is placed on a heating pipeline;

(2) after the plates on the heating pipeline are lifted by the lifting mechanism, the plates are extruded and overlapped together to form a whole;

(3) the heating pipeline is hollow, and two ends of the heating pipeline are respectively connected with a steam pipeline which is used for supplying steam and recovering steam;

(4) in the steam supply process, adjusting the supply amount of the processing steam and the extrusion pressure of the upgrading mechanism;

(5) continuously processing the plate in the mode of the step (4);

(6) after the treatment is finished, closing steam supply, and naturally cooling to room temperature;

(7) and loosening the boards which are overlapped together by using the lifting mechanism, taking down the boards for detection, and finishing the softening and shaping treatment of the solid wood floor boards.

Further, the heating pipeline is a copper alloy pipe or an aluminum alloy pipe.

Furthermore, the upgrading mechanism in the step (2) is a hydraulic mechanism, and a plurality of upgrading mechanisms are arranged and distributed at the periphery of the lower part of the plate to be extruded.

Furthermore, the external steam pipeline is used for supplying steam to the external pipeline, and the recovery pipeline is used for recycling after recovering the steam.

Further, in the step (5), the treatment temperature is 110-138 ℃, the treatment time is 60-120 minutes, and the extrusion pressure is kept at 160-200 MPa.

Furthermore, in the process method, the thickness of the processed plate is 1-30 mm.

Furthermore, the process method completes the softening, high-pressure, sizing and dehydration processes at the same time to obtain the solid wood floor board meeting the requirements for subsequent processing treatment.

The invention has the beneficial effects that: the method can simultaneously carry out one-time extrusion treatment and shaping on a plurality of boards through a special treatment process, can simultaneously complete softening and high-pressure treatment of the boards in the treatment process, and can obtain shaping and dewatering effects, and the boards subjected to one-time treatment have stable performance, more compact product structure, stronger waterproofness and convenience in obtaining solid wood boards with better performance in subsequent use.

Detailed Description

The following description of specific embodiments of the present invention is provided in connection with examples to facilitate a better understanding of the present invention.