阅读说明：本技术 一种提花桑波缎炼白工艺 (Jacquard mulberry satin whitening process ) 是由 陈跃会 杨晓东 朱建良 周建林 徐锦梅 于 2019-08-02 设计创作，主要内容包括：本发明公开了一种提花桑波缎炼白工艺,工艺流程如下,第一步,按照生产安排单的工艺卡要求的匹数、厂家进行发货；第二步,圈码→钉襻,用直径1米的圈码机圈成大卷,再用襻绳钩子钉好并挂在炼布架上；第三步,方练缸：每一缸做40-45匹,每匹长48米,用5吨的温水缸浸,时间40-60分钟,温度30-40℃,使绸缎完全浸润。该提花桑波缎炼白工艺炼白后白度均匀、无皱印、绸面干净。(The invention discloses a jacquard mulberry satin whitening process, which comprises the following steps of firstly, delivering goods according to the quantity required by a process card of a production arrangement list and a manufacturer; secondly, looping and stacking → stitching loop, looping the loop into a large roll by a loop stacking machine with the diameter of 1 meter, and then hooking and hanging the loop on a cloth refining frame by a loop rope; thirdly, square practice tank: each jar is used for soaking 40-45 pieces of silk fabric with the length of 48 meters in a warm water jar of 5 tons for 40-60 minutes at the temperature of 30-40 ℃ so that the silk fabric is completely soaked. The jacquard mulberry satin whitening process has the advantages of uniform whiteness, no wrinkle mark and clean silk surface after whitening.)

1. A jacquard mulberry satin whitening process is characterized in that: the process flow is as follows,

step one, delivering goods according to the number of the process cards required by the production arrangement list and manufacturers;

secondly, looping and stacking → stitching loop, looping the loop into a large roll by a loop stacking machine with the diameter of 1 meter, and then hooking and hanging the loop on a cloth refining frame by a loop rope;

thirdly, square practice tank: soaking 40-45 pieces of the silk fabric in a warm water jar of 5 tons for 40-60 minutes at 30-40 ℃ until the silk fabric is completely soaked, wherein each piece of the silk fabric is 48 meters long; then degumming by using a primary refining cylinder of 5 tons of hot water, and adding a dispersant: 15-20kg, soda: 6-8kg, sodium silicate: 4-6kg of sodium hydrosulfite: 1-1.5kg, controlling the temperature at 96-98 ℃, and refining for 90-100 minutes; then 5 tons of hot water are used for oxygen bleaching, and hydrogen peroxide: 20-22kg, sodium silicate: scouring at water temperature of 98 deg.C for 30-40 min at 5-8kg, and bleaching with oxygen for 115 min; remill jar with 5 tons of hot water: using a dispersing agent: 8-10kg, soda: 1-2kg, sodium silicate: 2-4kg, 0.5-1kg of sodium hydrosulfite, and is characterized in that: 1-2kg, controlling the temperature at 96-98 ℃, and refining for 50-60 minutes;

fourthly, rolling: using a tension-free loose rolling machine to roll the raw materials into large rolls according to the number of the process cards;

fifthly, finishing: drying by a woolen blanket machine, and shaping by a width weaving machine;

and sixthly, checking.

The technical field is as follows:

the invention relates to the technical field of textile printing and dyeing, in particular to a jacquard mulberry satin whitening process.

Background art:

the jacquard mulberry satin is formed by interweaving 100% of mulberry silk serving as a raw material on a rapier loom by adopting jacquard weave, and the jacquard weave needs to be white-scoured before dyeing, but the jacquard weave of the existing jacquard mulberry satin is easy to be light yellow, so that the overall whiteness of the fabric is uneven.

The invention content is as follows:

the technical problem to be solved by the invention is to provide a jacquard mulberry satin whitening process with good whiteness, and the whitening process enables the silk surface to be clean and free of wrinkle marks.

The technical scheme of the invention is to provide a jacquard mulberry satin whitening process, which comprises the following process flows,

step one, delivering goods according to the number of the process cards required by the production arrangement list and manufacturers;

secondly, looping and stacking → stitching loop, looping the loop into a large roll by a loop stacking machine with the diameter of 1 meter, and then hooking and hanging the loop on a cloth refining frame by a loop rope;

thirdly, square practice tank: soaking 40-45 pieces of the silk fabric in a warm water jar of 5 tons for 40-60 minutes at 30-40 ℃ until the silk fabric is completely soaked, wherein each piece of the silk fabric is 48 meters long; then degumming by using a primary refining cylinder of 5 tons of hot water, and adding a dispersant: 15-20kg, soda: 6-8kg, sodium silicate: 4-6kg of sodium hydrosulfite: 1-1.5kg, controlling the temperature at 96-98 ℃, and refining for 90-100 minutes; then 5 tons of hot water are used for oxygen bleaching, and hydrogen peroxide: 20-22kg, sodium silicate: scouring at water temperature of 98 deg.C for 30-40 min at 5-8kg, and bleaching with oxygen for 115 min; remill jar with 5 tons of hot water: using a dispersing agent: 8-10kg, soda: 1-2kg, sodium silicate: 2-4kg, 0.5-1kg of sodium hydrosulfite, and is characterized in that: 1-2kg, controlling the temperature at 96-98 ℃, and refining for 50-60 minutes; the operation of the oxygen bleaching cylinder can be used for bleaching oil stains and fancy yarns on the mulberry satin, and the re-scouring cylinder can be used for increasing the whiteness of the satin;

fourthly, rolling: using a tension-free loose rolling machine to roll the raw materials into large rolls according to the number of the process cards;

fifthly, finishing: drying by a woolen blanket machine, and shaping by a width weaving machine;

and sixthly, checking.

Compared with the prior art, the invention has the following advantages after the process is adopted: the finished product has good whiteness, clean silk surface and no wrinkle.

The specific implementation mode is as follows:

the invention is further illustrated with respect to specific embodiments below:

a jacquard mulberry satin whitening process, which comprises the following process flows,

step one, delivering goods according to the number of the process cards required by the production arrangement list and manufacturers;

secondly, looping and stacking → stitching loop, looping the loop into a large roll by a loop stacking machine with the diameter of 1 meter, and then hooking and hanging the loop on a cloth refining frame by a loop rope;

thirdly, square practice tank: soaking 40-45 pieces of the silk fabric in a warm water jar of 5 tons for 40-60 minutes at 30-40 ℃ until the silk fabric is completely soaked, wherein each piece of the silk fabric is 48 meters long; then degumming by using a primary refining cylinder of 5 tons of hot water, and adding a dispersant: 15-20kg, soda: 6-8kg, sodium silicate: 4-6kg of sodium hydrosulfite: 1-1.5kg, controlling the temperature at 96-98 ℃, and refining for 90-100 minutes; then 5 tons of hot water are used for oxygen bleaching, and hydrogen peroxide: 20-22kg, sodium silicate: scouring at water temperature of 98 deg.C for 30-40 min at 5-8kg, and bleaching with oxygen for 115 min; remill jar with 5 tons of hot water: using a dispersing agent: 8-10kg, soda: 1-2kg, sodium silicate: 2-4kg, 0.5-1kg of sodium hydrosulfite, and is characterized in that: 1-2kg, controlling the temperature at 96-98 ℃, and refining for 50-60 minutes; the operation of the oxygen bleaching cylinder can be used for bleaching oil stains and fancy yarns on the mulberry satin, and the re-scouring cylinder can be used for increasing the whiteness of the satin;

fourthly, rolling: using a tension-free loose rolling machine to roll the raw materials into large rolls according to the number of the process cards;

fifthly, finishing: drying by a woolen blanket machine, and shaping by a width weaving machine;

and sixthly, checking.

The invention has the following advantages: the invention has the following advantages: the finished product has good whiteness, clean silk surface and no wrinkle.

The foregoing is illustrative of the preferred embodiments of the present invention only and is not to be construed as limiting the claims.