Lubricating oil composition for internal combustion engine

文档序号:1676634 发布日期:2019-12-31 浏览:34次 中文

阅读说明:本技术 内燃机用润滑油组合物 (Lubricating oil composition for internal combustion engine ) 是由 松田裕充 星野耕治 于 2018-05-18 设计创作,主要内容包括:一种内燃机用润滑油组合物,其含有润滑油基油,该润滑油基油包含1种以上的矿物油系基油或1种以上的合成系基油或者它们的组合,100℃时的运动粘度为4.0~4.5mm<Sup>2</Sup>/s,250℃时的NOACK蒸发量为15质量%以下,内燃机用润滑油组合物还含有:(A)含有钙的金属系清洁剂,以组合物总量为基准,以钙量计,含量为1000质量ppm以上且低于2000质量ppm,和(B)含有镁的金属系清洁剂,以组合物总量为基准,以镁量计,含量为100~1000质量ppm,内燃机用润滑油组合物还含有或不含(C)粘度指数提高剂,在含有时,以组合物总量为基准,含量低于1质量%。(A lubricating oil composition for internal combustion engines, which comprises a lubricating base oil comprising 1 or more kinds of mineral base oils or 1 or more kinds of synthetic base oils or a combination thereof and having a kinematic viscosity at 100 ℃ of 4.0 to 4.5mm 2 (s) a NOACK evaporation amount at 250 ℃ of 15 mass% or less, and a lubricating oil composition for an internal combustion engine further comprising: (A) a calcium-containing metal-based detergent in an amount of 1000 ppm by mass or more and less than 2000 ppm by mass in terms of calcium based on the total composition, and (B) a magnesium-containing metal-based detergent in an amount of 100 to 1000 ppm by mass in terms of magnesium based on the total composition, the lubricating oil composition for an internal combustion engine further contains or does not contain (C) a viscosity index improver and, when contained, the content is less than 1% by mass in terms of the total composition.)

1. A lubricating oil composition for an internal combustion engine, characterized by comprising:

a lubricant base oil comprising 1 or more kinds of mineral base oils or 1 or more kinds of synthetic base oils, or a combination thereofAnd the kinematic viscosity of the lubricating base oil at 100 ℃ is 4.0 to 4.5mm2(ii)/s, wherein the NOACK evaporation amount at 250 ℃ is 15 mass% or less;

(A) a calcium-containing metal-based detergent in an amount of 1000 mass ppm or more and less than 2000 mass ppm in terms of calcium based on the total amount of the composition; and

(B) a magnesium-containing metal-based detergent in an amount of 100 to 1000 mass ppm in terms of magnesium based on the total amount of the composition,

the lubricating oil composition for an internal combustion engine may further contain or not contain (C) a viscosity index improver, and when contained, the content of the (C) viscosity index improver is less than 1% by mass based on the total amount of the composition.

2. The lubricating oil composition for an internal combustion engine according to claim 1, wherein:

the component (C) contains (C1) a poly (meth) acrylate viscosity index improver having a weight-average molecular weight of 100,000 or more,

the content of the component (C1) is 95 mass% or more of the total content of the component (C).

3. The lubricating oil composition for an internal combustion engine according to claim 1 or 2, wherein:

does not contain the component (C).

4. The lubricating oil composition for an internal combustion engine according to any one of claims 1 to 3, wherein:

also contains (D) a friction modifier.

5. The lubricating oil composition for an internal combustion engine according to claim 4, wherein:

the component (D) contains a molybdenum-based friction modifier.

6. The lubricating oil composition for an internal combustion engine according to any one of claims 1 to 5, wherein:

the lubricating base oil is 1 or more kinds of synthetic base oils.

7. The lubricating oil composition for an internal combustion engine according to any one of claims 1 to 6, wherein:

the HTHS viscosity at 150 ℃ is 1.7 to 2.0 mPas.

8. The lubricating oil composition for an internal combustion engine according to any one of claims 1 to 7, wherein:

the HTHS viscosity at 100 ℃ is 3.5 to 4.4 mPas.

9. The lubricating oil composition for an internal combustion engine according to any one of claims 1 to 8, wherein:

the NOACK evaporation amount at 250 ℃ is 15 mass% or less.

Technical Field

The present invention relates to a lubricating oil composition for an internal combustion engine.

Background

Conventionally, lubricating oil is used for smooth operation of mechanical devices such as internal combustion engines and transmissions. In particular, high performance is required for lubricating oil for internal combustion engines (engine oil) in accordance with the increase in performance and output of internal combustion engines and the increase in operating conditions. Therefore, in order to satisfy such required performance, conventional engine oils have been compounded with various additives such as antiwear agents, metal detergents, ashless dispersants, and antioxidants. In addition, recently, fuel economy required for lubricating oils has been increasing, and applications to high viscosity index base oils and various friction modifiers have been studied.

Disclosure of Invention

Technical problem to be solved by the invention

However, the conventional lubricating oil is insufficient in terms of fuel economy.

For example, as a general method for achieving fuel economy, a method of reducing the kinematic viscosity and increasing the viscosity index of a lubricating oil (multi-grade general-purpose lubricating oil (multi-grade oil) obtained by combining a low-viscosity base oil and a viscosity index improver) and a method of compounding a friction reducing agent are known. When the viscosity of the lubricating oil is lowered, the viscosity of the lubricating oil or the base oil constituting the lubricating oil is lowered, so that the lubricating performance under severe lubricating conditions (under high-temperature high-shear conditions) is lowered, and there is a concern that problems such as abrasion, seizure, and fatigue fracture may occur, and the evaporability may be deteriorated. Further, ashless and molybdenum-based friction modifiers are known as the friction reducers, but fuel saving and fuel consumption are required to be better than those of lubricating oils containing these friction reducers in general.

In order to prevent the problem due to the decrease in viscosity and maintain the durability, it is necessary to increase the viscosity of HTHS at 150 ℃ (HTHS viscosity is also referred to as high-temperature high-shear viscosity), and to prevent the decrease in viscosity due to shear, it is necessary to increase the shear stability. In order to further impart fuel economy while maintaining other practical properties, it is effective to reduce the kinematic viscosity at 40 ℃, the kinematic viscosity at 100 ℃ and the HTHS viscosity at 100 ℃ while maintaining the HTHS viscosity at 150 ℃ at a constant level, but it is very difficult for conventional lubricating oils to satisfy all of these conditions.

In recent years, in order to reduce the fuel consumption of an automobile internal combustion engine, particularly an automobile gasoline engine, it has been proposed to replace a conventional natural intake engine with an engine having a supercharger and a lower exhaust gas amount (supercharged small engine). The supercharged small engine has a supercharger, so that the output can be maintained and the exhaust gas amount can be reduced, thereby achieving fuel saving. On the other hand, in a supercharged small engine, when the torque is gradually increased in a Low rotation region, a phenomenon (LSPI: Low Speed Pre-Ignition) of igniting earlier than a predetermined timing in the cylinder may occur. When the LSPI occurs, the energy loss increases, which is a restriction on improvement of fuel efficiency and improvement of low-speed torque. With regard to the occurrence of LSPI, it is suspected to be due to the influence of engine oil.

For the purpose of suppressing LSPI, for example, it is conceivable to reduce the content of calcium-based detergent. In addition, as a measure for improving fuel economy, the content of the molybdenum-based friction modifier is generally increased. However, in the lubricating oil composition of such a formulation, there is a tendency that the cleaning performance is deteriorated.

In addition, in order to improve the fuel economy, it is effective to reduce the viscosity of the base oil as described above. However, since the base oil having a low viscosity is easily evaporated, the fuel consumption of the fuel-saving lubricating oil composition using the base oil having a low viscosity tends to increase.

The present invention addresses the problem of providing a lubricating oil composition for an internal combustion engine, which is capable of improving fuel economy, LSPI suppression capability, fuel consumption suppression capability, and cleaning performance in a well-balanced manner.

Technical solution for solving technical problem

The present invention includes the following embodiments [1] to [8 ].

[1] A lubricating oil composition for an internal combustion engine, characterized by comprising:

a lubricant base oil comprising 1 or more kinds of mineral base oils or 1 or more kinds of synthetic base oils or a combination thereof, wherein the lubricant base oil has a kinematic viscosity at 100 ℃ of 4.0 to 4.5mm2(s) a NOACK evaporation amount at 250 ℃ of 15 mass% or less,

(A) a metal-based detergent containing calcium in an amount of 1000 mass ppm or more and less than 2000 mass ppm in terms of calcium based on the total amount of the composition, and

(B) a magnesium-containing metal-based detergent in an amount of 100 to 1000 ppm by mass in terms of magnesium based on the total amount of the composition,

the lubricating oil composition for an internal combustion engine may further contain or not contain (C) a viscosity index improver, and when contained, the content is less than 1% by mass based on the total amount of the composition.

[2] The lubricating oil composition for an internal combustion engine according to [1], wherein the component (C) contains a poly (meth) acrylate viscosity index improver (C1) having a weight average molecular weight of 100,000 or more, and the content of the component (C1) is 95% by mass or more of the total content of the component (C).

[3] The lubricating oil composition for an internal combustion engine according to [1] or [2], which does not contain the component (C).

[4] The lubricating oil composition for an internal combustion engine according to any one of [1] to [3], further comprising (D) a friction modifier.

[5] The lubricating oil composition for an internal combustion engine according to [4], wherein the component (D) contains a molybdenum-based friction modifier.

[6] The lubricating oil composition for an internal combustion engine according to any one of [1] to [5], wherein the lubricating base oil is at least 1 synthetic base oil.

[7] The lubricating oil composition for an internal combustion engine according to any one of [1] to [6], wherein the HTHS viscosity at 150 ℃ is 1.7 to 2.0 mPas.

[8] The lubricating oil composition for an internal combustion engine according to any one of [1] to [7], wherein the HTHS viscosity at 100 ℃ is 3.5 to 4.4 mPas.

[9] The lubricating oil composition for an internal combustion engine according to any one of [1] to [8], wherein the NOACK evaporation amount at 250 ℃ is 15 mass% or less.

In the present specification, the "kinematic viscosity at 100 ℃" means the kinematic viscosity at 100 ℃ as defined in ASTM D-445. "HTHS viscosity at 150 ℃" means the high temperature high shear viscosity at 150 ℃ as defined in ASTM D4683. "HTHS viscosity at 100 ℃" means the high temperature high shear viscosity at 100 ℃ as defined in ASTM D4683. "NOACK evaporation at 250 ℃" refers to the evaporation of the lubricating oil at 250 ℃ as measured according to ASTM D5800.

ADVANTAGEOUS EFFECTS OF INVENTION

The lubricating oil composition for an internal combustion engine of the present invention can improve fuel economy, LSPI suppression capability, oil consumption suppression capability, and cleaning performance in a well-balanced manner.

Detailed Description

Hereinafter, the present invention will be described in detail. Unless otherwise specified, the numerical values a and B are "a to B" when they are expressed as "a to B". In this description, when a unit is marked for only the numerical value B, the unit is also applicable to the numerical value a. The words "or" and "or" mean logical or unless otherwise specified. In the present specification, the term "alkaline earth metal" also includes magnesium.

< lubricating oil base oil >

As the lubricant base oil, the following lubricant base oils (hereinafter, may be referred to as "lubricant base oils according to the present embodiment") may be used: comprising 1 or more kinds of mineral base oils or 1 or more kinds of synthetic base oils or a combination thereof, and having a kinematic viscosity at 100 ℃ of 4.0 to 4.5mm2(s) has a NOACK evaporation amount at 250 ℃ of 15 mass% or less. As the mineral base oil, 1 or more kinds of API group II base oils, 1 or more kinds of API group III base oils, or a combination thereof can be preferably used, and as the synthetic base oil, 1 or more kinds of API group IV base oils can be preferably used.

Examples of the mineral oil base oil include the following mineral oil base oils: a paraffinic mineral oil obtained by refining a lubricating oil fraction obtained by atmospheric distillation and/or vacuum distillation of a crude oil by a combination of 1 or 2 or more types selected from refining treatments such as solvent deasphalting, solvent extraction, hydrogenolysis, solvent dewaxing, catalytic dewaxing, hydrorefining, sulfuric acid washing, clay treatment and the like, and an n-paraffinic hydrocarbon base oil, an iso-paraffinic hydrocarbon base oil, a mixture thereof and the like, the kinematic viscosity at 100 ℃ being at least one selected from the group consisting of4.0~4.5mm2(ii)/s, wherein the NOACK evaporation amount at 250 ℃ is 15 mass% or less.

Preferred examples of the mineral oil base oil include: the base oils (1) to (8) shown below were used as the raw materials, and the feedstock and/or the lubricating oil fraction recovered from the feedstock were refined by a predetermined refining method, and the lubricating oil fraction was recovered to obtain the base oils.

(1) Distillate oil obtained by atmospheric distillation of paraffinic crude oil and/or mixed base crude oil

(2) Distillate oil (WVGO) obtained by vacuum distillation of atmospheric distillation residue of paraffinic crude oil and/or mixed base crude oil

(3) Waxes obtained in the dewaxing step of lubricating oils (slack wax, etc.) and/or synthetic waxes obtained in the Gas To Liquids (GTL) process (Fischer-Tropsch wax, GTL wax, etc.)

(4) 1 or 2 or more kinds of mixed oils selected from the base oils (1) to (3) and/or a light hydrocracking treated oil of the mixed oils

(5) 2 or more kinds of mixed oils selected from the base oils (1) to (4)

(6) Deasphalted oil (DAO) of base oil (1), (2), (3), (4) or (5)

(7) Light hydrocracking treated oil (MHC) of base oil (6)

(8) 2 or more kinds of mixed oils selected from the base oils (1) to (7).

Further, as the above-mentioned predetermined purification method, hydrorefining such as hydrogenolysis and hydrorefining; solvent refining such as furfural solvent extraction; dewaxing such as solvent dewaxing and catalytic dewaxing; clay purification using acid clay, activated clay, or the like; chemical (acid or alkali) cleaning such as sulfuric acid cleaning and sodium hydroxide cleaning. One of these purification methods may be carried out alone or in combination of 2 or more. In the case of combining 2 or more purification methods, the order is not particularly limited and can be selected as appropriate.

The mineral oil-based base oil is particularly preferably the base oil (9) or (10) described below obtained by subjecting a base oil selected from the base oils (1) to (8) described above or a lubricating oil fraction recovered from the base oil to a predetermined treatment.

(9) A base oil selected from the base oils (1) to (8) or a lubricating oil fraction recovered from the base oil is subjected to hydrogenolysis, and the product thereof or a lubricating oil fraction recovered from the product by distillation or the like is subjected to dewaxing treatment such as solvent dewaxing, catalytic dewaxing or the like, or is subjected to the dewaxing treatment and then subjected to distillation to obtain a hydrogenolyzed base oil

(10) A hydroisomerized base oil obtained by hydroisomerizing a base oil selected from the base oils (1) to (8) or a lubricating oil fraction recovered from the base oil, and subjecting the product thereof or the lubricating oil fraction recovered from the product by distillation or the like to a dewaxing treatment such as solvent dewaxing or catalytic dewaxing, or subjecting the product to the dewaxing treatment and then to distillation. The base oil obtained as a result of the dewaxing step is preferably subjected to a catalytic dewaxing step.

In addition, when the lubricating base oil of the above (9) or (10) is obtained, a solvent refining treatment and/or a hydrofinishing treatment may be further performed at an appropriate stage as necessary.

The catalyst used for the hydrogenolysis/hydroisomerization is not particularly limited, and the following catalysts are preferably used: a hydrogenolysis catalyst obtained by using, as a carrier, a composite oxide having decomposition activity (for example, silica-alumina, alumina-boria, silica-zirconia, or the like) or a combination of 1 or more of these composite oxides and bonded with a binder, and supporting a metal having hydrogenation ability (for example, 1 or more of metals of group VIB, group VIII, or the like in the periodic table of elements) on the carrier; or a hydroisomerization catalyst comprising a carrier comprising a zeolite (for example, ZSM-5, beta zeolite, SAPO-11, or the like) and at least 1 or more metals having hydrogenation ability among the group VIII metals supported on the carrier. The hydrogenolysis catalyst and the hydroisomerization catalyst may be used in combination by stacking, mixing, or the like.

The reaction conditions in the hydrogenolysis/hydroisomerization are not particularly limited, but are preferably 0.1 to 20MPa in hydrogen partial pressure, 150 to 450 ℃ in average reaction temperature, and 0.1 to 3.0hr LHSV-1And a hydrogen/oil ratio of 50 to 20000 scf/b.

At 100 ℃ of lube base oilThe kinematic viscosity is 4.0-4.5 mm2And s. By setting the kinematic viscosity of the lubricating base oil at 100 ℃ to 4.0mm2At least s, an oil film can be sufficiently formed at the lubricated part, the lubricity can be improved, and the evaporation loss of the lubricating oil composition can be reduced. And the kinematic viscosity at 100 ℃ of the lubricating base oil was adjusted to 4.5mm2The fuel economy can be improved by not more than s.

The kinematic viscosity of the lubricant base oil at 40 ℃ is preferably 40mm2Less than s, more preferably 30mm2A thickness of 25mm or less, more preferably2Less than s, particularly preferably 22mm2Less than s, most preferably 20mm2The ratio of the water to the water is less than s. On the other hand, the kinematic viscosity at 40 ℃ is preferably 10mm2More preferably 12 mm/s or more2At least s, more preferably 14mm2More than s, particularly preferably 16mm2More than s. When the kinematic viscosity at 40 ℃ of the lubricating base oil is not more than the upper limit value, the low-temperature viscosity characteristics and fuel economy of the lubricating oil composition can be further improved. Further, when the kinematic viscosity at 40 ℃ of the lubricating base oil is not less than the lower limit value, an oil film at the lubricated part can be sufficiently formed, the lubricity can be improved, and the evaporation loss of the lubricating oil composition can be reduced.

In the present specification, the "kinematic viscosity at 40 ℃" means the kinematic viscosity at 40 ℃ specified in ASTM D-445.

The viscosity index of the lubricant base oil is preferably 100 or more, more preferably 105 or more, further preferably 110 or more, particularly preferably 115 or more, and most preferably 120 or more. When the viscosity index is not less than the lower limit, the viscosity-temperature characteristics, thermal oxidation stability, and volatility prevention of the lubricating oil composition can be further improved, and the friction coefficient can be easily reduced and the wear resistance can be easily improved. In the present specification, the viscosity index refers to a viscosity index measured in accordance with JIS K2283-1993.

The NOACK evaporation amount at 250 ℃ of the lubricating base oil is 15% by mass or less. The NOACK evaporation amount herein is a value obtained by measuring the evaporation amount of the lubricating oil measured in accordance with ASTM D5800. The lower limit of the NOACK evaporation amount at 250 ℃ of the lubricant base oil is not particularly limited, but is usually 5% by mass or more.

The pour point of the lube base oil is preferably-10 ℃ or lower, more preferably-12.5 ℃ or lower, and still more preferably-15 ℃ or lower. When the pour point exceeds the above upper limit value, the low-temperature fluidity of the entire lubricating oil composition tends to decrease. In addition, in the present specification, the pour point refers to a pour point measured in accordance with JIS K2269-.

The sulfur content of a lube base oil depends on the sulfur content of its raw material. For example, when a raw material containing substantially no sulfur, such as a synthetic wax component obtained by a fischer-tropsch synthesis reaction or the like, is used, a lubricating base oil containing substantially no sulfur can be obtained. When a sulfur-containing raw material such as slack wax obtained in a refining process of a lubricating base oil or microcrystalline wax obtained in a refining process is used, the sulfur content in the lubricating base oil obtained is usually 100 mass ppm or more. From the viewpoint of further improving the thermal oxidation stability and low vulcanization of the lubricating oil composition, the sulfur content of the lubricating base oil is preferably 100 mass ppm or less, more preferably 50 mass ppm or less, still more preferably 10 mass ppm or less, and particularly preferably 5 mass ppm or less.

The content of nitrogen in the lubricant base oil is preferably 10 mass ppm or less, more preferably 5 mass ppm or less, and still more preferably 3 mass ppm or less. When the content of nitrogen exceeds 10 mass ppm, thermal and oxidation stability tends to be lowered. In the present specification, the nitrogen score refers to the nitrogen score measured in accordance with JIS K2609-.

% C of mineral oil base oilPPreferably 70 or more, more preferably 75 or more, and usually 99 or less, preferably 95 or less, more preferably 94 or less. By making% C of the base oilPWhen the amount of the additive is not less than the lower limit, the viscosity-temperature characteristics, thermal/oxidative stability and friction characteristics are easily improved, and when the additive is blended into the base oil, the efficacy of the additive is easily improved. In addition, by making the% C of the base oilpWhen the content is not more than the above upper limit, the solubility of the additive is easily improved.

% C of mineral oil base oilAPreferably 2 or less, more preferably 1 or less, still more preferably 0.8 or less, and particularly preferably 0.5 or less. By making% C of the base oilAWhen the amount is less than the upper limit, the viscosity-temperature characteristics, thermal/oxidative stability, and fuel economy are easily improved.

Mineral oil base oil% CNPreferably 30 or less, more preferably 25 or less, and preferably 1 or more, more preferably 4 or more. By making% C of the base oilNWhen the amount is less than the above upper limit, the viscosity-temperature characteristics, thermal/oxidative stability and friction characteristics are easily improved. In addition, by making% CNWhen the amount is more than the lower limit, the solubility of the additive is easily improved.

In the present specification,% CP、%CNAnd% CAThe percentages are the percentage of the number of paraffinic carbon atoms to the total number of carbon atoms, the percentage of the number of naphthenic carbon atoms to the total number of carbon atoms, and the percentage of the number of aromatic carbon atoms to the total number of carbon atoms, each determined by the method (n-D-M ring analysis) according to ASTM D3238-85. That is, the above-mentioned% CP、%CNAnd% CABased on the value determined by the above method, for example, the% C determined by the above method even in the case of a lubricating base oil containing no naphthenic componentNBut may also be displayed as a value exceeding 0.

The content of the saturated component in the mineral oil-based base oil is preferably 90 mass% or more, preferably 95 mass% or more, and more preferably 99 mass% or more, based on the total amount of the base oil. When the content of the saturated component is not less than the lower limit, the viscosity-temperature characteristics and the thermal/oxidative stability can be improved. In the present specification, the saturated component means a value measured according to ASTM D2007-93.

In addition, similar methods for separating saturated components can be used to obtain the same result. For example, in addition to the method described in ASTM D2007-93, a method described in ASTM D2425-93, a method described in ASTM D2549-91, a method using High Performance Liquid Chromatography (HPLC), a method in which these methods are modified, and the like can be cited.

The aromatic component in the mineral oil base oil is preferably 10% by mass or less, more preferably 5% by mass or less, further preferably 4% by mass or less, particularly preferably 3% by mass or less, most preferably 2% by mass or less, may be 0% by mass, and in one embodiment is 0.1% by mass or more, based on the total amount of the base oil. When the content of the aromatic component is not more than the above upper limit, the viscosity-temperature characteristics, the thermal oxidation stability, the friction characteristics, the volatility prevention and the low-temperature viscosity characteristics are easily improved, and the efficacy of the additive is easily improved when the additive is blended in the lubricating base oil. The lubricant base oil may not contain an aromatic component, but the solubility of the additive can be further improved by setting the content of the aromatic component to the lower limit value or more.

In the present specification, the aromatic component means a value measured according to ASTM D2007-93. The aromatic component generally includes, in addition to alkylbenzene and alkylnaphthalene, anthracene, phenanthrene, alkylated products thereof, a compound obtained by condensation of 4 or more benzene rings, pyridine-based, quinoline-based, phenol-based, naphthol-based, and other aromatic compounds having a hetero atom.

The synthetic base oil may have a kinematic viscosity at 100 ℃ of 4.0 to 4.5mm2Examples of the NOACK evaporation amount at 250 ℃ of 15 mass% or less include polyalphaolefins and hydrides thereof, isobutylene oligomers and hydrides thereof, isoparaffins, alkylbenzenes, alkylnaphthalenes, diesters (ditridecyl glutarate, di-2-ethylhexyl adipate, diisodecyl adipate, ditridecyl adipate, di-2-ethylhexyl sebacate, etc.), polyol esters (trimethylolpropane octanoate, trimethylolpropane nonanoate, pentaerythritol 2-ethylhexanoate, pentaerythritol nonanoate, etc.), polyoxyalkylene glycols, dialkyl diphenyl ethers, polyphenylene ethers, and mixtures thereof, and among them, polyalphaolefins are preferable. The polyalphaolefin typically includes oligomers or cooligomers (Co-oligomers) (1-octene oligomers, decene oligomers) of an alpha-olefin having 2 to 32 carbon atoms, preferably 6 to 16 carbon atomsA copolymer, an ethylene-propylene co-oligomer, etc.) and hydrogenated products of these.

The method for producing the polyalphaolefin is not particularly limited, and examples thereof include a method of polymerizing an alpha-olefin in the presence of a polymerization catalyst such as a catalyst comprising a complex compound of aluminum trichloride or boron trifluoride with water, an alcohol (ethanol, propanol, butanol, etc.), a carboxylic acid or an ester.

The lubricating base oil has a kinematic viscosity of 4.0 to 4.5mm at 100 ℃ based on the entire base oil2The NOACK evaporation amount at 250 ℃ may be 15 mass% or less, and may be constituted by a single base oil component or may contain a plurality of base oil components.

The content of the lubricant base oil in the lubricant composition is usually 75 to 95% by mass, preferably 85% by mass or more, based on the total amount of the composition.

< (A), (B): metal-based detergent

The lubricating oil composition of the present invention contains, as the metal-based detergent, (a) a metal-based detergent containing calcium (hereinafter, sometimes referred to as "component (a)" or "calcium-based detergent"), and (B) a metal-based detergent containing magnesium (hereinafter, sometimes referred to as "component (B)" or "magnesium-based detergent"). Examples of the metal-based detergent include a phenol-based detergent, a sulfonate-based detergent, and a salicylate-based detergent. These metal-based detergents can be used alone or in combination of 2 or more.

As the phenate-based detergent, an overbased salt of an alkaline earth metal salt of a compound having a structure represented by the following formula (1) can be preferably exemplified. As the alkaline earth metal, magnesium or calcium is preferable.

In the formula (1), R1Represents a linear or branched, saturated or unsaturated alkyl or alkenyl group having 6 to 21 carbon atoms, m is a polymerization degree and represents an integer of 1 to 10, A represents a thioether (-S-) group or a methylene (-CH)2-) group, x represents an integer of 1 to 3. Furthermore, R1Can be 2Combinations of the above different groups.

R in the formula (1)1The number of carbon atoms of (A) is preferably 9 to 18, more preferably 9 to 15. By reacting R1The carbon number of (2) is not less than the above lower limit, and the solubility in the base oil can be improved. On the other hand, by making R1The number of carbon atoms of (a) is not more than the above upper limit, and the detergent can be easily produced and also can have improved heat resistance.

The polymerization degree m in the formula (1) is preferably 1 to 4. When the polymerization degree m is within this range, the heat resistance can be improved.

As the sulfonate-based detergent, an alkaline earth metal salt of an alkyl aromatic sulfonic acid obtained by sulfonating an alkyl aromatic compound, or a basic salt or an overbased salt thereof can be preferably exemplified. The alkyl aromatic compound preferably has a weight average molecular weight of 400 to 1500, more preferably 700 to 1300.

As the alkaline earth metal, magnesium or calcium is preferable. Examples of the alkyl aromatic sulfonic acid include so-called petroleum sulfonic acid and synthetic sulfonic acid. Examples of the petroleum sulfonic acid include a product obtained by sulfonating an alkyl aromatic compound in a lubricating oil fraction of a mineral oil, and a so-called mahogany acid which is a by-product in the production of white oil. Examples of the synthetic sulfonic acid include products obtained by recovering a by-product from a plant for producing alkylbenzene as a raw material of a detergent, and products obtained by alkylating alkylbenzene having a linear or branched alkyl group, which is obtained by alkylating benzene with a polyolefin. Another example of the synthetic sulfonic acid is one obtained by sulfonating alkylnaphthalenes such as dinonylnaphthalene. The sulfonating agent used in sulfonating these alkyl aromatic compounds is not particularly limited, and fuming sulfuric acid or sulfuric anhydride, for example, can be used.

As the salicylate-based detergent, a metal salicylate, an alkali salt thereof, or an overbased salt thereof can be preferably exemplified. As the metal salicylate, a compound represented by the following formula (2) can be preferably exemplified.

In the above formula (2), R2Each independently represents an alkyl group or alkenyl group having 14 to 30 carbon atoms, M represents an alkaline earth metal, and n represents 1 or 2. As M, calcium or magnesium is preferred. N is preferably 1. When n is 2, R2Combinations of different groups are possible.

As a preferred embodiment of the salicylate-based detergent, an alkaline earth metal salicylate having n ═ 1 in the formula (2) above, or an alkaline salt or an overbased salt thereof can be cited.

The method for producing the alkaline earth metal salicylate is not particularly limited, and a known method for producing monoalkylsalicylate can be used. For example, the alkaline earth metal salicylate can be obtained by alkylating phenol as a starting material with an olefin and then carboxylating the alkylated product with carbon dioxide or the like to obtain monoalkylsalicylic acid, or by alkylating salicylic acid with an equivalent amount of the olefin to obtain monoalkylsalicylic acid, and then reacting the obtained monoalkylsalicylic acid with a metal base such as an oxide or hydroxide of an alkaline earth metal, or by once forming an alkali metal salt such as a sodium salt or a potassium salt with the monoalkylsalicylic acid or the like and then performing metal exchange with an alkaline earth metal salt.

The metal-based detergent may be overbased with a carbonate (e.g., an alkaline earth metal carbonate such as calcium carbonate or magnesium carbonate) or with a borate (e.g., an alkaline earth metal borate such as calcium borate or magnesium borate).

The method for obtaining the metal-based detergent overbased with the alkaline earth metal carbonate is not particularly limited, and for example, the metal-based detergent can be obtained by reacting a neutral salt of the metal-based detergent (for example, alkaline earth metal phenate, alkaline earth metal sulfonate, alkaline earth metal salicylate, etc.) with an alkaline earth metal base (for example, alkaline earth metal hydroxide, oxide, etc.) in the presence of carbon dioxide.

The method for obtaining the metal-based detergent highly alkalized with the alkaline earth metal borate is not particularly limited, and the metal-based detergent can be obtained by reacting a neutral salt of the metal-based detergent (for example, alkaline earth metal phenate, alkaline earth metal sulfonate, alkaline earth metal salicylate, etc.) with an alkaline earth metal base (for example, alkaline earth metal hydroxide, oxide, etc.) in the presence of boric acid, boric anhydride, or borate.

As the component (a), for example, a phenol calcium salt detergent, a calcium sulfonate detergent, a salicylic acid calcium salt detergent, or a combination thereof can be used. (A) The ingredient preferably contains at least an overbased calcium salicylate detergent. (A) The component (A) can be overbased by calcium carbonate or calcium borate.

As the component (B), for example, a phenol magnesium salt detergent, a sulfonic acid magnesium salt detergent, a salicylic acid magnesium salt detergent, or a combination thereof can be used. (B) The component (A) preferably contains an overbased magnesium sulfonate detergent. (B) The component (A) can be highly alkalized by magnesium carbonate or magnesium borate.

The metal-based detergent is generally commercially available in a state diluted with light lubricating oil base oil or the like, and a metal-based detergent having a metal content of 1.0 to 20 mass%, preferably 2.0 to 16 mass%, is generally used. The total base number of the metal-based detergent is arbitrary, and a metal-based detergent having a total base number of 500mgKOH/g or less, preferably 150 to 450mgKOH/g is usually used. The total base number is a total base number obtained by a perchloric acid method measured according to JIS K2501(1992) of "Petroleum products and lubricating oils-neutralization test method" 7.

The total base number of the calcium-based detergent (component (A)) is preferably 150mgKOH/g or more, and preferably 350mgKOH/g or less, more preferably 300mgKOH/g or less, and particularly preferably 250mgKOH/g or less.

The content of the component (a) in the lubricating oil composition is 1000 mass ppm or more and less than 2000 mass ppm, more preferably 1000 to 1500 mass ppm, in terms of calcium, based on the total amount of the lubricating oil composition. LSPI can be suppressed by making the content of LSPI less than 2000 mass ppm in terms of calcium. Further, by setting the content of calcium to the lower limit or more, the cleanliness of the engine interior can be maintained at a high level, and the base number maintenance performance can be improved.

The total base number of the magnesium-based detergent (component (B)) is preferably 200mgKOH/g or more, more preferably 250mgKOH/g or more, particularly preferably 300mgKOH/g or more, and preferably 600mgKOH/g or less, more preferably 550mgKOH/g or less, particularly preferably 500mgKOH/g or less.

The content of the component (B) in the lubricating oil composition is 100 to 1000 mass ppm, preferably 150 mass ppm or more, more preferably 200 mass ppm or more, and preferably 800 mass ppm or less, more preferably 500 mass ppm or less in terms of magnesium based on the total amount of the lubricating oil composition. When the content of magnesium is not less than the lower limit, engine cleanliness can be improved while suppressing LSPI. Further, by setting the content in terms of magnesium to the upper limit or less, an increase in the friction coefficient can be suppressed.

(C) viscosity index improver

The lubricating oil composition of the present invention preferably contains less than 1% by mass or does not contain (C) a viscosity index improver (hereinafter, sometimes referred to as "component (C)") based on the total amount of the lubricating oil composition. That is, the content of the viscosity index improver in the lubricating oil composition is preferably 0% by mass or more and less than 1% by mass based on the total amount of the composition. Examples of the component (C) include non-dispersible or dispersible poly (meth) acrylate viscosity index improvers, (meth) acrylate-olefin copolymers, non-dispersible or dispersible ethylene- α -olefin copolymers or hydrides thereof, polyisobutylene or hydrides thereof, styrene-diene hydrogenated copolymers, styrene-maleic anhydride ester copolymers, polyalkylstyrenes, and the like. When the content of the component (C) in the lubricating oil composition is less than 1 mass%, the detergency of the lubricating oil composition can be improved. (C) The content of the component (b) is more preferably 0.9% by mass or less, and particularly preferably 0.8% by mass or less.

When the lubricating oil composition contains component (C), a poly (meth) acrylate-based viscosity index improver (hereinafter, sometimes referred to as "component (C1)") having a weight average molecular weight of 100,000 or more can be preferably used as component (C) of component (C1). (C) The content of the component (C1) in the component (a) is preferably 95% by mass or more, and may be 100% by mass, based on the total content of the component (C).

(C1) The weight average molecular weight (Mw) of the component (a) is 100,000 or more, preferably 200,000 or more, and preferably 1,000,000 or less, more preferably 700,000 or less, and further preferably 500,000 or less. When the weight average molecular weight is not less than the lower limit, the effect of improving the viscosity index when the component (C1) is dissolved in the lubricating base oil can be improved, the fuel economy and the low-temperature viscosity characteristics can be further improved, and the cost can be easily reduced. Further, by setting the weight average molecular weight to be equal to or less than the upper limit value, the viscosity increase suppressing effect can be made excessively large, and therefore, the fuel economy and the low-temperature viscosity characteristics can be further improved, and the shear stability, the solubility in the lubricating base oil, and the storage stability can be improved.

(C1) The component (b) preferably contains a poly (meth) acrylate viscosity index improver (hereinafter, also referred to as "viscosity index improver according to the present embodiment") in which the proportion of the structural unit represented by the following general formula (3) to the total monomer units in the polymer is 10 to 90 mol%. In the present specification, "(meth) acrylate" means "acrylate and/or methacrylate".

(in the formula (3), R3Represents hydrogen or methyl, R4Represents a linear or branched hydrocarbon group having 1 to 18 carbon atoms. )

In one embodiment, R4Is a hydrocarbon group having 1 to 5 carbon atoms, or a hydrocarbon group having 6 to 18 carbon atoms, or a combination thereof.

In the viscosity index improver according to the present embodiment, the proportion of the (meth) acrylate structural unit represented by the general formula (3) in the polymer is preferably 10 to 90 mol%, more preferably 80 mol% or less, and still more preferably 70 mol% or less. Further, it is more preferably 20 mol% or more, still more preferably 30 mol% or more, and particularly preferably 40 mol% or more. By setting the ratio of the (meth) acrylate structural unit represented by the general formula (3) to the total monomer units in the polymer to the upper limit value or less, the solubility in the base oil, the effect of improving the viscosity-temperature characteristic, and the low-temperature viscosity characteristic are easily improved. Further, by setting the ratio of the (meth) acrylate structural unit represented by the general formula (3) to the total monomer units in the polymer to the lower limit value or more, the effect of improving the viscosity-temperature characteristics can be easily improved.

The viscosity index improver according to the present embodiment may be a copolymer having a (meth) acrylate structural unit other than the (meth) acrylate structural unit represented by the general formula (3). Such a copolymer can be obtained by copolymerizing 1 or 2 or more kinds of monomers represented by the following general formula (4) (hereinafter, referred to as "monomer (M-1)") with monomers other than the monomer (M-1).

(in the formula (4), R5Represents a hydrogen atom or a methyl group, R6Represents a linear or branched hydrocarbon group having 1 to 18 carbon atoms. )

In one embodiment, R6Is a hydrocarbon group having 1 to 5 carbon atoms, or a hydrocarbon group having 6 to 18 carbon atoms, or a combination thereof.

The monomer to be combined with the monomer (M-1) is optional, and for example, a monomer represented by the following general formula (5) (hereinafter, referred to as "monomer (M-2)") is suitable. The copolymer of the monomer (M-1) and the monomer (M-2) is a so-called non-dispersible poly (meth) acrylate viscosity index improver.

(in the formula (5), R7Represents a hydrogen atom or a methyl group, R8Represents a linear or branched hydrocarbon group having 19 or more carbon atoms. )

R in the monomer (M-2) represented by the formula (5)8As described above, the hydrocarbon group is a linear or branched hydrocarbon group having 19 or more carbon atoms, preferably a linear or branched hydrocarbon group having 20 or more carbon atoms, more preferably a linear or branched hydrocarbon group having 22 or more carbon atoms, and still more preferably a branched hydrocarbon group having 24 or more carbon atoms. In addition, R8Of the hydrocarbon radicals shownThe upper limit of the number of carbon atoms is not particularly limited, and a linear or branched hydrocarbon group having 50,000 or less carbon atoms is preferable. R8More preferably a linear or branched hydrocarbon group having not more than 500 carbon atoms, still more preferably a linear or branched hydrocarbon group having not more than 100 carbon atoms, particularly preferably a branched hydrocarbon group having not more than 50 carbon atoms, and most preferably a branched hydrocarbon group having not more than 40 carbon atoms.

In the viscosity index improver according to the present embodiment, the number of (meth) acrylate structural units corresponding to the monomer (M-2) in the polymer may be 1, or may be a combination of 2 or more. When the polymer contains a structural unit corresponding to the monomer (M-2), the proportion of the structural unit corresponding to the monomer (M-2) to the total monomer units in the polymer is preferably 0.5 to 70 mol%, more preferably 60 mol% or less, still more preferably 50 mol% or less, particularly preferably 40 mol% or less, and most preferably 30 mol% or less. In addition, it is preferably 1 mol% or more, more preferably 3 mol% or more, further preferably 5 mol% or more, and particularly preferably 10 mol% or more. By setting the ratio of the structural unit corresponding to the monomer (M-2) to the total monomer units in the polymer to the upper limit value or less, the effect of improving the viscosity-temperature characteristics and the low-temperature viscosity characteristics can be easily improved. Further, by setting the ratio of the structural unit corresponding to the monomer (M-2) to the total monomer units in the polymer to the lower limit value or more, the effect of improving the viscosity-temperature characteristics can be easily improved.

As the other monomer to be combined with the monomer (M-1), 1 or 2 or more selected from the group consisting of a monomer represented by the following general formula (6) (hereinafter, referred to as "monomer (M-3)") and a monomer represented by the following general formula (7) (hereinafter, referred to as "monomer (M-4)") is preferable. The copolymer of the monomer (M-1) and the monomer (M-3) and/or (M-4) is a so-called dispersion type poly (meth) acrylate viscosity index improver. The dispersion-type poly (meth) acrylate viscosity index improver may further contain a monomer (M-2) as a structural unit.

(in the formula (6), R9Represents a hydrogen atom or a methyl group, R10Represents an alkylene group having 1 to 18 carbon atoms, E1Represents an amine residue or a heterocyclic residue containing 1 to 2 nitrogen atoms and 0 to 2 oxygen atoms, and a represents 0 or 1. )

As R10Specific examples of the alkylene group having 1 to 18 carbon atoms include an ethylene group, a propylene group, a butylene group, a pentylene group, a hexylene group, a heptylene group, an octylene group, a nonylene group, a decylene group, an undecylene group, a dodecylene group, a tridecylene group, a tetradecylene group, a pentadecylene group, a hexadecylene group, a heptadecylene group, and an octadecylene group (these alkylene groups may be linear or branched).

As E1Specific examples of the group include dimethylamino, diethylamino, dipropylamino, dibutylamino, phenylamino, toluylamino, ditoluylamino, acetylamino, benzoylamino, morpholino, Pyrrolyl (Pyrrolyl), pyrrolinyl (pyrrolno), pyridyl, methylpyridinyl, pyridylalkyl, piperidyl (2-, 3-or 4-) (Piperidinyl), piperidin-1-yl (Piperidino), quinolyl, pyrrolidinonyl (pyrrolondonyl), pyrrolinyl, and pyrazinyl.

(in the formula (7), R11Represents a hydrogen atom or a methyl group, E2Represents an amine residue or a heterocyclic residue containing 1 to 2 nitrogen atoms and 0 to 2 oxygen atoms. )

As E2Specific examples of the group include dimethylamino, diethylamino, dipropylamino, dibutylamino, phenylamino, toluylamino, ditoluylamino, acetylamino, benzoylamino, morpholino, pyrrolyl, pyrrolinyl, pyridyl, methylpyridinyl, pyridylalkyl, piperidyl (2-, 3-or 4-), piperidin-1-yl, quinolyl, pyrrolidinonyl, and the like,Imidazolinyl and pyrazinyl and the like.

Specific examples of the monomers (M-3) and (M-4) include dimethylaminomethyl methacrylate, diethylaminomethyl methacrylate, dimethylaminoethyl methacrylate, diethylaminoethyl methacrylate, 2-methyl-5-vinylpyridine, morpholinomethyl methacrylate, morpholinoethyl methacrylate, N-vinylpyrrolidone, and mixtures thereof.

The copolymerization molar ratio of the monomer (M-1) to the copolymer of the monomers (M-2) to (M-4) is not particularly limited, and the monomer (M-1): monomers (M-2) to (M-4) ═ 20: 80-90: about 10, more preferably 30: 70-80: 20, more preferably 40: 60-70: 30.

the method for producing the viscosity index improver according to the present embodiment is arbitrary, and for example, a non-dispersible poly (meth) acrylate compound can be easily obtained by radical solution polymerization of the monomer (M-1) and the monomer (M-2) in the presence of a polymerization initiator (e.g., benzoyl peroxide). Further, for example, the dispersion type poly (meth) acrylate compound can be easily obtained by radical solution polymerization of the monomer (M-1) and 1 or more nitrogen-containing monomers selected from the monomers (M-3) and (M-4), optionally with the monomer (M-2), in the presence of a polymerization initiator.

(D) Friction modifier

The lubricating oil composition of the present invention preferably contains (D) a friction modifier (hereinafter, sometimes referred to as "component (D)"). As the friction modifier, a molybdenum-based friction modifier (oil-soluble organic molybdenum compound), an ashless friction modifier, or a combination thereof can be preferably used.

When the component (D) contains a molybdenum-based friction modifier, the content thereof is preferably 100 to 2000 mass ppm based on the total amount of the lubricating oil composition in terms of molybdenum. As the molybdenum-based friction modifier, molybdenum dithiocarbamate (molybdenum dithiocarbamate sulfide or molybdenum dithiocarbamate oxysulfide, hereinafter, sometimes referred to as "component D1") can be preferably used.

As the component (D1), for example, a compound represented by the following general formula (8) can be used.

In the above general formula (8), R12~R15The alkyl group may be the same or different and has 2 to 24 carbon atoms or an (alkyl) aryl group having 6 to 24 carbon atoms, preferably an alkyl group having 4 to 13 carbon atoms or an (alkyl) aryl group having 10 to 15 carbon atoms. The alkyl group may be any of a primary alkyl group, a secondary alkyl group, and a tertiary alkyl group, and may be linear or branched. Further, "(alkyl) aryl" means "aryl or alkylaryl". In the alkylaryl group, the substitution position of the alkyl group in the aromatic ring is arbitrary. Y is1~Y4Each independently being a sulfur atom or an oxygen atom, Y1~Y4At least 1 of them being a sulfur atom.

Examples of the oil-soluble organic molybdenum compound other than the component (D1) include molybdenum dithiophosphate; molybdenum compounds (for example, molybdenum oxides such as molybdenum dioxide and molybdenum trioxide, molybdic acids such as orthomolybdic acid, paramolybdic acid, (poly) molybdic sulfide acid, metal salts and ammonium salts of these molybdic acids, molybdenum sulfides such as molybdenum disulfide, molybdenum trisulfide, molybdenum pentasulfide and molybdenum polysulfide, molybdic sulfide acid, metal salts or amine salts of molybdic sulfide acid, molybdenum halides such as molybdenum chloride) and the like) and sulfur-containing organic compounds (for example, coordination compounds of alkyl (thio) xanthates, thiadiazoles, mercaptothiadiazoles, thiocarbonates, tetraalkylthiuram disulfides, bis (di (thio) hydrocarbyl dithiophosphonate) disulfides, organic (poly) sulfides, sulfurized esters and the like) or other organic compounds); and organic molybdenum compounds containing sulfur, such as a complex of a sulfur-containing molybdenum compound such as molybdenum sulfide or molybdic acid sulfide and alkenylsuccinimide. The organic molybdenum compound may be a mononuclear molybdenum compound, or a polynuclear molybdenum compound such as a dinuclear molybdenum compound or a trinuclear molybdenum compound.

Further, as the oil-soluble organomolybdenum compound other than the component (D1), an organomolybdenum compound containing no sulfur as a constituent element can also be used. Specific examples of the organic molybdenum compound containing no sulfur as a constituent element include a molybdenum-amine complex, a molybdenum-succinimide complex, a molybdenum salt of an organic acid, and a molybdenum salt of an alcohol, and among them, a molybdenum-amine complex, a molybdenum salt of an organic acid, and a molybdenum salt of an alcohol are preferable.

When the lubricating oil composition contains a molybdenum-based friction modifier, the content thereof is usually 100 to 2000 mass ppm, preferably 300 mass ppm or more, more preferably 500 mass ppm or more, further preferably 700 mass ppm or more, and preferably 1500 mass ppm or less, more preferably 1200 mass ppm or less, further preferably 1000 mass ppm or less, in terms of molybdenum amount based on the total amount of the lubricating oil composition. When the molybdenum content is not less than the lower limit, the fuel economy and LSPI suppression ability can be improved. Further, by setting the molybdenum content to the upper limit or less, the storage stability of the lubricating oil composition can be improved.

As the ashless friction modifier, a compound generally used as a friction modifier for lubricating oil can be used without particular limitation. Examples of the ashless friction modifier include compounds having 6 to 50 carbon atoms, which contain 1 or more hetero elements selected from an oxygen atom, a nitrogen atom, and a sulfur atom in the molecule. More specifically, examples thereof include ashless friction modifiers having an alkyl group or alkenyl group having at least 1 carbon atom number of 6 to 30, preferably a straight-chain alkyl group, straight-chain alkenyl group, branched-chain alkyl group or branched-chain alkenyl group having 6 to 30 carbon atoms in the molecule, amine compounds, fatty acid esters, fatty acid amides, fatty acids, fatty alcohols, fatty ethers, urea compounds, hydrazine compounds, and the like.

When the lubricating oil composition contains an ashless friction modifier, the content thereof is usually 1000 to 10000 ppm by mass, preferably 3000 ppm by mass or more, and preferably 8000 ppm by mass or less, based on the total amount of the lubricating oil composition. When the content of the ashless friction modifier is not less than the lower limit value, a sufficient friction reducing effect can be obtained by the addition thereof. When the content of the ashless friction modifier is not more than the upper limit value, the effect of inhibiting the wear resistance additive and the like can be easily suppressed, and the solubility of the additive can be easily improved.

< E) Nitrogen-containing ashless dispersant

The lubricating oil composition of the present invention may contain (E) a nitrogen-containing ashless dispersant (hereinafter, sometimes referred to as "component (E)").

As the component (E), for example, 1 or more compounds selected from the following (E-1) to (E-3) can be used.

(E-1) a succinimide having at least 1 alkyl group or alkenyl group in the molecule or a derivative thereof (hereinafter, sometimes referred to as "component (E-1)")

(E-2) benzylamine having at least 1 alkyl group or alkenyl group in the molecule or a derivative thereof (hereinafter, sometimes referred to as "(E-2)")

(E-3) a polyamine having at least 1 alkyl group or alkenyl group in the molecule or a derivative thereof (hereinafter, sometimes referred to as "component (E-3)").

As the component (E), the component (E-1) can be particularly preferably used.

Examples of the succinimide having at least 1 alkyl group or alkenyl group in the molecule in the component (E-1) include compounds represented by the following general formula (9) or (10).

In the formula (9), R16Represents an alkyl group or alkenyl group having 40 to 400 carbon atoms, and h represents an integer of 1 to 5, preferably 2 to 4. R16Is preferably 60 or more, and is preferably 350 or less.

In the formula (10), R17And R18Each independently represents an alkyl group or an alkenyl group having 40 to 400 carbon atoms, and may be a combination of different groups. R17And R18Particularly preferred is a polybutenyl group. In addition, i represents an integer of 0 to 4, preferably 1 to 4, and more preferably 1 to 3. R17And R18Is preferably 60 or more, and is preferably 350 or less.

By using R in the formula (9) and the formula (10)16~R18Has a carbon number of at least the above lower limit, and can provide good solubility in the lubricating base oil. On the other hand, by making R16~R18The number of carbon atoms of (b) is not more than the above upper limit, and the low temperature fluidity of the lubricating oil composition can be improved.

Alkyl or alkenyl (R) in the formula (9) and formula (10)16~R18) The polymer may be linear or branched, and examples thereof include oligomers derived from olefins such as propylene, 1-butene and isobutylene, and branched alkyl groups and branched alkenyl groups derived from copolymerized oligomers of ethylene and propylene. Among them, a branched alkyl group or alkenyl group derived from an oligomer of isobutylene conventionally called polyisobutylene, or a polybutenyl group is most preferable.

Alkyl or alkenyl (R) in the formula (9) and formula (10)16~R18) The appropriate number average molecular weight is 800-3500.

The succinimide having at least 1 alkyl group or alkenyl group in the molecule includes a so-called mono-type succinimide represented by formula (9) having succinic anhydride added to only one end of a polyamine chain, and a so-called bis-type succinimide represented by formula (10) having succinic anhydride added to both ends of a polyamine chain. The lubricating oil composition of the present invention may contain either a mono-type succinimide or a bis-type succinimide, or may contain both of them as a mixture.

The method for producing the succinimide having at least 1 alkyl group or alkenyl group in the molecule is not particularly limited, and for example, the succinimide can be produced by reacting a compound having an alkyl group or alkenyl group having 40 to 400 carbon atoms with maleic anhydride at 100 to 200 ℃ and reacting the obtained alkyl succinic acid or alkenyl succinic acid with a polyamine. Examples of the polyamine include diethylenetriamine, triethylenetetramine, tetraethylenepentamine, and pentaethylenehexamine.

As the benzylamine having at least 1 alkyl group or alkenyl group in the molecule among the component (E-2), a compound represented by the following formula (11) can be exemplified.

In the formula (11), R19Represents an alkyl group or alkenyl group having 40 to 400 carbon atoms, and j represents an integer of 1 to 5, preferably 2 to 4. R19Is preferably 60 or more, and is preferably 350 or less.

The method for producing the component (E-2) is not particularly limited. For example, there is a method in which a polyolefin such as a propylene oligomer, polybutene, or an ethylene- α -olefin copolymer is reacted with phenol to obtain an alkylphenol, and then the alkylphenol is reacted with formaldehyde and a polyamine such as diethylenetriamine, triethylenetetramine, tetraethylenepentamine, or pentaethylenehexamine by a mannich reaction.

As the polyamine having at least 1 alkyl group or alkenyl group in the molecule among the component (E-3), a compound represented by the following formula (12) can be exemplified.

R20-NH—(CH2CH2NH)k—H (12)

In the formula (12), R20Represents an alkyl group or alkenyl group having 40 to 400 carbon atoms or less, and k represents an integer of 1 to 5, preferably 2 to 4. R20Is preferably 60 or more, and is preferably 350 or less.

The method for producing the component (E-3) is not particularly limited. For example, a method of chlorinating a polyolefin such as a propylene oligomer, polybutene, or an ethylene- α -olefin copolymer, and then reacting the chlorinated polyolefin with ammonia or a polyamine such as ethylenediamine, diethylenetriamine, triethylenetetramine, tetraethylenepentamine, or pentaethylenehexamine is exemplified.

Examples of the derivatives of the components (E-1) to (E-3) include (i) modified compounds obtained from an oxygen-containing organic compound, wherein a monocarboxylic acid having 1 to 30 carbon atoms, such as a fatty acid, a polycarboxylic acid having 2 to 30 carbon atoms (such as oxalic acid, phthalic acid, trimellitic acid, pyromellitic acid, and the like), an acid anhydride or ester compound thereof, an alkylene oxide having 2 to 6 carbon atoms, or a hydroxy (poly) oxyalkylene carbonate is reacted with the above-mentioned succinimide, benzylamine, or polyamine having at least 1 alkyl group or alkenyl group in the molecule (hereinafter referred to as "the above-mentioned nitrogen-containing compound"), and thereby a part or all of the remaining amino groups and/or imino groups are neutralized or amidated; (ii) a boron-modified compound in which a part or all of the remaining amino groups and/or imino groups are neutralized or amidated by reacting the above nitrogen-containing compound with boric acid; (iii) a phosphoric acid-modified compound in which a part or all of the remaining amino groups and/or imino groups are neutralized or amidated by reacting phosphoric acid with the above nitrogen-containing compound; (iv) a sulfur-modified compound obtained by reacting a sulfur compound with the above-mentioned nitrogen-containing compound; and (v) a modified compound obtained by subjecting the above-mentioned nitrogen-containing compound to a modification selected from the group consisting of a modification with an oxygen-containing organic compound, a boron modification, a phosphoric acid modification, and a sulfur modification in combination of 2 or more. The use of a boric acid-modified compound of alkenylsuccinimide, particularly a boric acid-modified compound of bis-type alkenylsuccinimide, among the derivatives of (i) to (v) can further improve the heat resistance of the lubricating oil composition.

(E) The molecular weight of the component is not particularly limited, and a suitable weight average molecular weight is 1000 to 20000.

When the lubricating oil composition contains the component (E), the content thereof is preferably 100 ppm by mass or more, more preferably 300 ppm by mass or more, and preferably 1500 ppm by mass or less, more preferably 1000 ppm by mass or less as a nitrogen component, based on the total amount of the lubricating oil composition. By setting the content of the component (E) to the lower limit or more, the coking resistance (heat resistance) of the lubricating oil composition can be sufficiently improved. Further, by setting the content of the component (E) to the upper limit or less, the fuel economy can be maintained at a high level.

(E) When component (E) contains boron, the content of boron in the lubricating oil composition derived from component (E) is preferably 400 ppm by mass or less, more preferably 350 ppm by mass or less, and particularly preferably 300 ppm by mass or less, based on the total amount of the lubricating oil composition. When the boron content from the component (E) is not more than the above upper limit, the ash content of the lubricating oil composition can be suppressed to a low level while maintaining the fuel economy at a high level.

< other additives >

The lubricating oil composition of the present invention may contain other additives that are generally used in lubricating oils for the purpose of further improving the performance thereof. Examples of such additives include zinc dialkyldithiophosphate, an antioxidant, an antiwear agent, an extreme pressure agent, an anticorrosive agent, a rust preventive agent, a metal deactivator, an anti-emulsifier, and an antifoaming agent.

As the zinc dialkyldithiophosphate (ZnDTP), for example, a compound represented by the following general formula (13) can be used.

In the formula (13), R21~R24Each independently represents a linear or branched alkyl group having 1 to 24 carbon atoms, and may be a combination of different groups. In addition, R21~R24The number of carbon atoms of (a) is preferably 3 or more, and preferably 12 or less, and more preferably 8 or less. In addition, R21~R24Any of primary alkyl groups, secondary alkyl groups, and tertiary alkyl groups may be used, and primary alkyl groups or secondary alkyl groups or a combination thereof are preferable, and it is further preferable that the molar ratio of primary alkyl groups to secondary alkyl groups (primary alkyl groups: secondary alkyl groups) is 0: 100-30: 70. this ratio may be a combination ratio of alkyl chains within the molecule, or may be a mixing ratio of ZnDTP having only primary alkyl groups to ZnDTP having only secondary alkyl groups. The fuel economy can be further improved by making the secondary alkyl group dominant.

The method for producing the zinc dialkyldithiophosphate is not particularly limited. For example, by having a corresponding R21~R24The alcohol of (2) is reacted with phosphorus pentasulfide to synthesize dithiophosphoric acid, which is synthesized by neutralizing with zinc oxide.

When the lubricating oil composition contains ZnDTP, the content thereof is preferably 600 mass ppm or more and preferably 800 mass ppm or less as the amount of phosphorus based on the total amount of the composition. When the ZnDTP content is not less than the lower limit, not only oxidation stability but also LSPI inhibitory ability can be improved. Further, by setting the ZnDTP content to the upper limit or less, the catalyst poisoning of the exhaust gas treatment catalyst is easily reduced.

As the antioxidant, known antioxidants such as a phenol-based antioxidant and an amine-based antioxidant can be used. Examples thereof include amine antioxidants such as alkylated diphenylamine, phenyl- α -naphthylamine, and alkylated- α -naphthylamine, and phenol antioxidants such as 2, 6-di-t-butyl-4-methylphenol and 4, 4' -methylenebis (2, 6-di-t-butylphenol).

When the lubricating oil composition contains an antioxidant, the content thereof is usually 5.0% by mass or less, preferably 3.0% by mass or less, and preferably 0.1% by mass or more, more preferably 0.5% by mass or more, based on the total amount of the lubricating oil composition.

As the anti-wear agent or the extreme pressure agent, an anti-wear agent or an extreme pressure agent used in a lubricating oil can be used without particular limitation. For example, sulfur-based, phosphorus-based, sulfur-phosphorus-based extreme pressure agents and the like can be used, and specific examples thereof include phosphites, thiophosphites, dithiophosphates, trithiophosphites, phosphates, thiophosphates, dithiophosphates, trithiophosphates, amine salts thereof, metal salts thereof, derivatives thereof, dithiocarbamates, zinc dithiocarbamates, disulfide ethers, polysulfide ethers, sulfurized olefins, sulfurized oils and fats. Among these, a sulfur-based extreme pressure agent is preferably added, and particularly, sulfurized fats and oils are preferable.

When the lubricating oil composition contains an anti-wear agent or an extreme pressure agent, the content thereof is preferably 0.01 to 10% by mass based on the total amount of the lubricating oil composition.

As the preservative, for example, known preservatives such as benzotriazole-based compounds, methylbenzotriazole-based compounds, thiadiazole-based compounds, and imidazole-based compounds can be used. When the lubricant composition contains a preservative, the content thereof is usually 0.005 to 5% by mass based on the total amount of the lubricant composition.

Examples of the rust inhibitor include known rust inhibitors such as petroleum sulfonate, alkylbenzene sulfonate, dinonylnaphthalene sulfonate, alkylsulfonate, fatty acid, alkenylsuccinic acid half ester, fatty acid soap, polyol fatty acid ester, fatty amine, oxidized paraffin, and alkyl polyoxyethylene ether. When the lubricating oil composition contains a rust inhibitor, the content thereof is usually 0.005 to 5% by mass based on the total amount of the lubricating oil composition.

Examples of the metal deactivator include known metal deactivators such as imidazoline, pyrimidine derivatives, alkylthiadiazoles, mercaptobenzothiazole, benzotriazole and its derivatives, 1,3, 4-thiadiazole polythioether, 1,3, 4-thiadiazole-2, 5-dialkyldithiocarbamate, 2- (alkyldithio) benzimidazole, and β - (ortho-carboxybenzylthio) propionitrile. When the lubricating oil composition contains a metal deactivator, the content thereof is usually 0.005 to 1% by mass based on the total amount of the lubricating oil composition.

As the demulsifier, for example, a known demulsifier such as a polyalkylene glycol nonionic surfactant can be used. When the lubricating oil composition contains an anti-emulsifier, the content thereof is usually 0.005 to 5% by mass based on the total amount of the lubricating oil composition.

As the defoaming agent, for example, known defoaming agents such as silicone, fluorosilicone, fluoroalkyl ether and the like can be used. When the lubricating oil composition contains an antifoaming agent, the content thereof is usually 0.0001 to 0.1% by mass based on the total amount of the lubricating oil composition.

As the colorant, for example, a known colorant such as an azo compound can be used.

< lubricating oil composition >

The kinematic viscosity of the lubricating oil composition at 100 ℃ is preferably 4.0 to 6.1mm2S, more preferably 5.5mm2Less than s, and more preferably 4.5mm2More than s. By setting the kinematic viscosity at 100 ℃ of the lubricating oil composition to the upper limit value or less, the fuel economy can be further improved. Further, by setting the kinematic viscosity at 100 ℃ of the lubricating oil composition to the lower limit or more, it becomes easy to improve the lubricity.

The kinematic viscosity of the lubricating oil composition at 40 ℃ is preferably 4.0 to 50mm2S, more preferably 40mm2Less than s, particularly preferably 35mm2Less than s, and more preferablyIs selected to be 15mm2More preferably 18 mm/s or more2More than s, particularly preferably 20mm2More than s. By setting the kinematic viscosity of the lubricating oil composition at 40 ℃ to the lower limit or more, the lubricity can be easily improved. Further, when the kinematic viscosity at 40 ℃ of the lubricating oil composition is not more than the upper limit, it becomes easy to obtain a desired low-temperature viscosity, and fuel economy can be further improved.

The viscosity index of the lubricating oil composition is preferably 100 or more, more preferably 120 or more, and particularly preferably 130 or more. When the viscosity index of the lubricating oil composition is equal to or higher than the lower limit value, it becomes easy to increase the fuel economy while maintaining the HTHS viscosity at 150 ℃, and it becomes easy to decrease the viscosity at low temperatures (for example, -35 ℃ c., which is the measurement temperature of CCS viscosity defined by SAE viscosity grade 0W-X known as the fuel economy viscosity grade).

The HTHS viscosity of the lubricating oil composition at 150 ℃ is preferably 1.7 to 2.0 mPas, and more preferably 1.9 mPas or less. In the present specification, the HTHS viscosity at 150 ℃ means the high-temperature high-shear viscosity at 150 ℃ as defined in ASTM D4683. By setting the HTHS viscosity at 150 ℃ to the lower limit or more, the lubricity can be easily improved. Further, the fuel economy can be further improved by setting the HTHS viscosity at 150 ℃ to the upper limit or lower.

The HTHS viscosity of the lubricating oil composition at 100 ℃ is preferably 3.5 to 4.4 mPas, more preferably 4.2 mPas or less, even more preferably 3.7 mPas or more, and particularly preferably 3.8 mPas or more. In the present specification, the HTHS viscosity at 100 ℃ means the high-temperature high-shear viscosity at 100 ℃ as defined in ASTM D4683. By setting the viscosity of HTHS at 100 ℃ to the lower limit or more, the lubricity can be easily improved. Further, by setting the viscosity of the HTHS at 100 ℃ to the upper limit value or less, it becomes easy to obtain a desired low-temperature viscosity, and fuel economy can be further improved.

The evaporation loss of the lubricating oil composition is preferably 15% by mass or less based on NOACK evaporation at 250 ℃. By setting the NOACK evaporation amount of the lubricating oil composition to 15 mass% or less, the evaporation loss of the lubricating oil can be further reduced, and therefore, the increase in viscosity can be further suppressed. In the present specification, the NOACK evaporation amount refers to the evaporation amount of the lubricating oil measured according to ASTM D5800. The lower limit of the NOACK evaporation amount at 250 ℃ of the lubricating oil composition is not particularly limited, but is usually 5% by mass or more.

23页详细技术资料下载
上一篇:一种医用注射器针头装配设备
下一篇:切割油组合物

网友询问留言

已有0条留言

还没有人留言评论。精彩留言会获得点赞!

精彩留言,会给你点赞!