阅读说明：本技术 一种棉布的处理方法 (Cotton cloth treatment method ) 是由 李孝同 郝成生 于 2019-10-07 设计创作，主要内容包括：本发明提供了本发明提供了一种棉布的处理方法,包括处理液和处理方法,其特征在于,所述处理液包括：羟基聚磷酸酯1-2份、十八烷基咪唑啉2-3份、4-苯甲酰基-3-甲基-1-苯基-2吡唑啉-5-酮1-2份、聚丙稀酰胺0.5-1份、油酸聚氧乙烯酯1-1.5份、聚丙二醇0.5-1份、黄藤素1-1.5份、乙二醛0.5-1份、抗紫外线剂1-2份、水100-150份；按照上述比例准备处理液,温度加热至200-250度,将处理液充分搅拌,冷却后放入容器内；棉布放入盛有处理液的容器内进行浸轧,轧余率为60％-100％,在90度预烘2分钟,在150度焙烘3分钟,制得抗菌棉布；本发明设计合理,处理后的面料具有抗菌、抗紫外线、抗皱、阻燃以及防静电性能,值得推广。(The invention provides a cotton cloth treatment method, which comprises a treatment liquid and a treatment method, and is characterized in that the treatment liquid comprises: 1-2 parts of hydroxyl polyphosphate, 2-3 parts of octadecyl imidazoline, 1-2 parts of 4-benzoyl-3-methyl-1-phenyl-2 pyrazoline-5-ketone, 0.5-1 part of polyacrylamide, 1-1.5 parts of polyoxyethylene oleate, 0.5-1 part of polypropylene glycol, 1-1.5 parts of fibrauretine, 0.5-1 part of glyoxal, 1-2 parts of an ultraviolet resistant agent and 150 parts of 100-doped water; preparing the treatment fluid according to the proportion, heating the treatment fluid to the temperature of 200 ℃ and 250 ℃, fully stirring the treatment fluid, cooling the treatment fluid and then placing the treatment fluid into a container; padding the cotton cloth in a container containing the treatment solution with a padding rate of 60-100%, pre-drying at 90 ℃ for 2 minutes, and baking at 150 ℃ for 3 minutes to obtain antibacterial cotton cloth; the invention has reasonable design, and the treated fabric has the performances of antibiosis, ultraviolet resistance, crease resistance, flame retardance and antistatic property, and is worthy of popularization.)

1. A cotton cloth treatment method comprises a treatment liquid and a treatment method, and is characterized in that the treatment liquid comprises: 1-2 parts of hydroxyl polyphosphate, 2-3 parts of octadecyl imidazoline, 1-2 parts of 4-benzoyl-3-methyl-1-phenyl-2 pyrazoline-5-ketone, 0.5-1 part of polyacrylamide, 1-1.5 parts of polyoxyethylene oleate, 0.5-1 part of polypropylene glycol, 1-1.5 parts of fibrauretine, 0.5-1 part of glyoxal, 1-2 parts of an ultraviolet resistant agent and 150 parts of 100-doped water.

2. The method for treating cotton cloth according to claim 1, wherein the method comprises the following steps:

(1) preparing the treatment fluid according to the proportion, heating the treatment fluid to the temperature of 200 ℃ and 250 ℃, fully stirring the treatment fluid, cooling the treatment fluid and then placing the treatment fluid into a container;

(2) and (3) padding the cotton cloth in a container containing the treatment solution, wherein the padding rate is 60-100%, pre-drying at 90 ℃ for 2 minutes, and baking at 150 ℃ for 3 minutes to obtain the antibacterial cotton cloth.

3. The method for treating cotton cloth according to claim 1, wherein the number of padding is 2.

Technical Field

The invention relates to the field of cloth processing, in particular to a cotton cloth processing method.

Background

The cotton cloth is a cloth woven by cotton yarn. Is a general term for various cotton textiles. Cotton cloths are used to make fashion, casual wear, underwear and shirts. Its advantages are easy warm keeping, soft and close-fitting, and high hydroscopicity and air permeability. Its disadvantages are easy shrinkage and wrinkle, not very stiff and beautiful appearance, and need to be ironed frequently when wearing it. The existing cotton cloth has poor antibacterial and ultraviolet resistant effects. Therefore, a treatment method of cotton cloth with good antibacterial and ultraviolet-resistant effects becomes a problem to be solved urgently in the whole society.

Disclosure of Invention

In view of this, the present invention provides a cotton cloth treatment method including a treatment liquid and a treatment method, characterized in that the treatment liquid includes: 1-2 parts of hydroxyl polyphosphate, 2-3 parts of octadecyl imidazoline, 1-2 parts of 4-benzoyl-3-methyl-1-phenyl-2 pyrazoline-5-ketone, 0.5-1 part of polyacrylamide, 1-1.5 parts of polyoxyethylene oleate, 0.5-1 part of polypropylene glycol, 1-1.5 parts of fibrauretine, 0.5-1 part of glyoxal, 1-2 parts of an ultraviolet resistant agent and 150 parts of 100-doped water.

Further, the processing method is as follows:

(1) preparing the treatment fluid according to the proportion, heating the treatment fluid to the temperature of 200 ℃ and 250 ℃, fully stirring the treatment fluid, cooling the treatment fluid and then placing the treatment fluid into a container;

(2) and (3) padding the cotton cloth in a container containing the treatment solution, wherein the padding rate is 60-100%, pre-drying at 90 ℃ for 2 minutes, and baking at 150 ℃ for 3 minutes to obtain the antibacterial cotton cloth.

Further, the padding times are 2 times.

Compared with the prior art, the invention has the advantages that: the processing liquid adopted by the invention contains the antibacterial agent and the anti-ultraviolet agent, so that the antibacterial and anti-ultraviolet effects can be effectively realized, a user can use the processing liquid at ease, the design is reasonable, and the processed fabric has the antibacterial, anti-ultraviolet, anti-wrinkle, flame retardant and anti-static performances, and is worthy of popularization.

Detailed Description