阅读说明：本技术 一种汽车用耐磨损材料涂层 (Wear-resistant material coating for automobile ) 是由 周峰 倪兰花 周宸昕 于 2018-05-30 设计创作，主要内容包括：本发明公开一种汽车用耐磨损材料涂层,其特征在于：汽车用耐磨损材料涂层由以下成分按照重量比组成：硅藻粉为1-10份、碳粉为10-20份、抗氧剂为20-30份、滑石粉为12-22份、云母粉为10-20份,钛白粉1-10份,去离子水2-15份。本发明所生成的汽车用耐磨损材料涂层具有更加健康,对人体无害的优点。(The invention discloses a wear-resistant material coating for an automobile, which is characterized in that: the wear-resistant material coating for the automobile comprises the following components in percentage by weight: 1-10 parts of diatom powder, 10-20 parts of carbon powder, 20-30 parts of antioxidant, 12-22 parts of talcum powder, 10-20 parts of mica powder, 1-10 parts of titanium dioxide and 2-15 parts of deionized water. The wear-resistant material coating for the automobile, which is generated by the invention, has the advantages of being healthier and harmless to human bodies.)

一种汽车用耐磨损材料涂层

技术领域

本发明涉及材料领域，特别涉及一种汽车用耐磨损材料涂层。

背景技术

汽车涂层(coating)是涂料一次施涂所得到的固态连续膜，是为了防护，绝缘，装饰等目的，涂布于金属，织物，塑料等基体上的塑料薄层。涂料可以为气态、液态、固态，通常根据需要喷涂的基质决定涂料的种类和状态。

现有的汽车用耐磨损材料涂层往往含有对人体健康有害的物质。

发明内容

发明目的：为了克服现有技术中存在的不足，本发明提供一种更加健康的汽车用耐磨损材料涂层。

技术方案：为解决上述技术问题，本发明提供了一种汽车用耐磨损材料涂层，汽车用耐磨损材料涂层由以下成分按照重量比组成：硅藻粉为1-10份、碳粉为10-20份、抗氧剂为20-30份、滑石粉为12-22份、云母粉为10-20份，钛白粉1-10份，去离子水2-15份。

优选的，所述各组分的含量为：硅藻粉为2-8份、碳粉为12-18份、抗氧剂为22-28份、滑石粉为13-20份、云母粉为12-18份，钛白粉2-8份，去离子水5-10份。

优选的，所述各组分的含量为：硅藻粉为4-6份、碳粉为14-16份、抗氧剂为24-26份、滑石粉为15-18份、云母粉为14-16份，钛白粉4-6份，去离子水6-8份。

具体实施方式

一种汽车用耐磨损材料涂层，汽车用耐磨损材料涂层由以下成分按照重量比组成：硅藻粉为1-10份、碳粉为10-20份、抗氧剂为20-30份、滑石粉为12-22份、云母粉为10-20份，钛白粉1-10份，去离子水2-15份。

优选的，所述各组分的含量为：硅藻粉为2-8份、碳粉为12-18份、抗氧剂为22-28份、滑石粉为13-20份、云母粉为12-18份，钛白粉2-8份，去离子水5-10份。

优选的，所述各组分的含量为：硅藻粉为4-6份、碳粉为14-16份、抗氧剂为24-26份、滑石粉为15-18份、云母粉为14-16份，钛白粉4-6份，去离子水6-8份。

以上所述仅是本发明的优选实施方式，应当指出：对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。