阅读说明：本技术 含茶多酚或抑菌粉剂的干法造纸方法 (Dry method of paper-making method containing tea polyphenols or antibacterial pulvis ) 是由 李敬 于 2019-08-06 设计创作，主要内容包括：本发明公开了含茶多酚或抑菌粉剂的干法造纸方法,步骤如下：a.将木浆、开纤、ES纤维通过破碎机打碎得到粉末;b.在a步骤中得到的粉末中加入茶多酚或纳米银得到混合料;c.将步骤b中得到的混合料倒入混合机中,通过管道气流进行充分的混合;d.将步骤c中得到的混合料通过气流喷涂到网板上;e.对网板进行加热使网板上的混合料受热相互粘合成型;f.从网板上取下成型后的干法纸然后收卷即可。本制做方法工序简单、制作方便。(The invention discloses the dry method of paper-making methods containing tea polyphenols or antibacterial pulvis, and steps are as follows: a. smashes wood pulp, fibrillation, ES fiber to obtain powder by crusher;B. tea polyphenols are added in the powder obtained in a step or nano silver obtains mixture;C. mixture obtained in step b is poured into mixing machine, is adequately mixed by chimneying;D. mixture obtained in step c is sprayed on web plate by air-flow;E. carrying out heating to web plate keeps the mixture on web plate heated mutually adhesion-molded;F. dry-papermaking after molding is removed from web plate then to wind.This method for production process is simple, easy to make.)

1. the dry method of paper-making method containing tea polyphenols or antibacterial pulvis, which is characterized in that steps are as follows: a. is fine by wood pulp, fibrillation, ES Dimension is smashed to obtain powder by crusher;B. tea polyphenols are added in the powder obtained in a step or nano silver obtains mixture; C. mixture obtained in step b is poured into mixing machine, is adequately mixed by chimneying;D. it will be obtained in step c To mixture sprayed on web plate by air-flow;E. carrying out heating to web plate makes the mixture on web plate is heated to be mutually bonded into Type;F. dry-papermaking after molding is removed from web plate then to wind.

Technical field

The present invention relates to the dry method of paper-making methods containing tea polyphenols or antibacterial pulvis.

Background technique

Dust-free paper is a kind of important materials that can be used for making paper diaper.Traditional papermaking needs to use water, so making Paper be wet, it is necessary to carry out drying and processing again, more so as to cause manufacturing procedure, production is more inconvenient.

Summary of the invention

For overcome the deficiencies in the prior art, the present invention provides production process simple, easy to make dry method of paper-making method.

The technical solution adopted by the present invention to solve the technical problems is:

Dry method of paper-making method containing tea polyphenols or antibacterial pulvis, which is characterized in that steps are as follows: a. is by wood pulp, fibrillation, ES fiber It smashes to obtain powder by crusher;B. tea polyphenols are added in the powder obtained in a step or nano silver obtains mixture;c. Mixture obtained in step b is poured into mixing machine, is adequately mixed by chimneying;D. it will be obtained in step c Mixture sprayed on web plate by air-flow;E. carrying out heating to web plate makes the mixture on web plate is heated to be mutually bonded into Type;F. dry-papermaking after molding is removed from web plate then to wind.

The beneficial effects of the present invention are: this method for production is by a relatively simple rationally, use air as the carrier of fiber, In Form fibre thin layer on forming net, then the papermaking process special at one kind of paper with adhesive bonding, it and conventional papermaking processes The difference is that fiber is to form paper web in the absence of water.Paper after molding can be used directly, woth no need to as tradition Paper needs to do drying and processing, and it is antibacterial anti-in addition to joined tea polyphenols or nano silver, Nano-Zinc, chitosan etc. in process of production Bacterium raw material, to make paper more clean hygiene.

Specific embodiment

Dry method of paper-making method containing tea polyphenols or antibacterial pulvis, which is characterized in that steps are as follows: a. is by wood pulp, fibrillation, ES Fiber is smashed to obtain powder by crusher;B. tea polyphenols are added in the powder obtained in a step or nano silver is mixed Material;C. mixture obtained in step b is poured into mixing machine, is adequately mixed by chimneying;D. by step c Obtained in mixture sprayed on web plate by air-flow;E. carrying out heating to web plate keeps the mixture on web plate heated mutually viscous Synthesis type;F. dry-papermaking after molding is removed from web plate then to wind.