阅读说明：本技术 一种相变储能板及其制作方法 (A kind of phase-change energy storage plate and preparation method thereof ) 是由 彭庆付 孟玲琳 祁仁华 崔玉凤 于 2019-09-09 设计创作，主要内容包括：本发明涉及建筑板材技术领域,尤其为一种相变储能板及其制作方法,包括。本发明中,用木质纤维或玻璃纤维替代了石棉纤维,保障了操作人员的身体健康,该板材,复合水泥层包括下述重量份组成的原料：水泥、木质纤维、粉煤灰、改性剂、减水剂,所述相变储能层包括下述重量份组成的原料：水泥、相变储能胶囊、木质纤维、粉煤灰、改性剂、减水剂,其中,相变储能层内设置的相变储能胶囊和设置在板材之间的相变储能纤维网可有效提高板材的相变储能能力,适宜推广使用。(The present invention relates to building board technical field, in particular a kind of phase-change energy storage plate and preparation method thereof, including.In the present invention, with wood fibre or glass fibre instead of asbestos fibre, the health of operator is ensured, the plate, Compound Water mud layer includes the raw material of following weight parts composition: cement, wood fibre, flyash, modifying agent, water-reducing agent, the phase-change accumulation energy layer includes the raw material of following weight parts composition: cement, phase-change energy storage capsule, wood fibre, flyash, modifying agent, water-reducing agent, wherein, the phase-change energy storage capsule being arranged in phase-change accumulation energy layer and the phase-change energy-storage fibre net being arranged between plate can effectively improve the phase-change accumulation energy ability of plate, it is suitable for promoting the use of.)

1. a kind of phase-change energy storage plate, including Compound Water mud layer (1) and phase-change accumulation energy layer (2), it is characterised in that: the complex cement Layer (1) includes the raw material of following weight parts composition: 40-80 parts of cement, 7-15 parts of wood fibre, 12-16 parts of flyash, modifying agent 0.5-1 parts, 0.5-1 parts of water-reducing agent, the phase-change accumulation energy layer (2) they include the raw material of following weight parts composition: 40-80 parts of cement, 20-30 parts of phase-change energy storage capsule (4), 7-15 parts of wood fibre, 12-16 parts of flyash, 0.5-1 parts of modifying agent, water-reducing agent 0.5-1 Part, the Compound Water mud layer (1) is set to phase-change accumulation energy layer (2) two sides up and down, the Compound Water mud layer (1) and phase-change accumulation energy layer (2) internal and Compound Water mud layer (1) and phase-change accumulation energy layer (2) junction are provided with phase-change energy-storage fibre net (3).

2. a kind of its production method of phase-change energy storage plate according to claim 1, characterized by the following steps:

1) after the raw material for weighing corresponding mass according to needed for Compound Water mud layer (1) and phase-change accumulation energy layer (2), respectively by Compound Water The raw material of mud layer (1) and phase-change accumulation energy layer (2) is stirred；

2) according to Compound Water mud layer (1), phase-change energy-storage fibre net (3), complex cement after on the conveyor by the placement of plate template, Layer (1), phase-change energy-storage fibre net (3), phase-change accumulation energy layer (2), phase-change energy-storage fibre net (3), phase-change accumulation energy layer (2), phase transformation storage Can web (3), Compound Water mud layer (1), the sequence of phase-change energy-storage fibre net (3), Compound Water mud layer (1) is successively in template Laying is poured, plate prototype is obtained；

3) by plate prototype after sizing, maintenance, cutting, phase-change energy storage plate is obtained.

Technical field

The present invention relates to building board technical field, specially a kind of phase-change energy storage plate and preparation method thereof.

Background technique

Currently there are most of plate, cannot effectively realize that phase-change accumulation energy, phase-changing energy storage material are close A kind of new material of year exploitation is to utilize Cucumber at a certain temperature, is absorbed or released energy by phase transformation.This material Material can be made into threadiness, capsule shape or other cladding forms.Threadiness can directly carry out textile process, but accommodate phase-change material Less, energy storage effect is undesirable.The bulky receiving material of capsule shape is more, but processing difficulties in practical applications, small in size When, the few problem of container is equally existed, therefore, proposes a kind of phase-change energy storage plate and preparation method thereof regarding to the issue above.

Summary of the invention

The purpose of the present invention is to provide a kind of phase-change energy storage plates and preparation method thereof, are replaced with wood fibre or glass fibre For asbestos fibre, the health of operator has been ensured, the plate, Compound Water mud layer includes the original of following weight parts composition Material: cement, wood fibre, flyash, modifying agent, water-reducing agent, the phase-change accumulation energy layer include the raw material of following weight parts composition: Cement, phase-change energy storage capsule, wood fibre, flyash, modifying agent, water-reducing agent, wherein the phase transformation storage being arranged in phase-change accumulation energy layer Energy capsule and the phase-change energy-storage fibre net being arranged between plate can effectively improve the phase-change accumulation energy ability of plate, and suitable popularization makes With to solve the problems mentioned in the above background technology.

To achieve the above object, the invention provides the following technical scheme:

A kind of phase-change energy storage plate and preparation method thereof, including Compound Water mud layer and phase-change accumulation energy layer, the Compound Water mud layer Raw material including following weight parts composition: 40-80 parts of cement, 7-15 parts of wood fibre, 12-16 parts of flyash, modifying agent 0.5-1 Part, 0.5-1 parts of water-reducing agent, the phase-change accumulation energy layer include the raw material of following weight parts composition: 40-80 parts of cement, phase-change accumulation energy 420-30 parts of capsule, 7-15 parts of wood fibre, 12-16 parts of flyash, 0.5-1 parts of modifying agent, 0.5-1 parts of water-reducing agent, it is described multiple Heshui mud layer is set to phase-change accumulation energy layer two sides up and down, inside the Compound Water mud layer and phase-change accumulation energy layer and Compound Water mud layer and Phase-change accumulation energy layer junction is provided with phase-change energy-storage fibre net.

Preferably, include the following steps:

1) after the raw material for weighing corresponding mass according to needed for Compound Water mud layer and phase-change accumulation energy layer, respectively by complex cement The raw material of layer and phase-change accumulation energy layer is stirred；

2) according to Compound Water mud layer, phase-change energy-storage fibre net, complex cement after on the conveyor by the placement of plate template, Layer, phase-change energy-storage fibre net, phase-change accumulation energy layer, phase-change energy-storage fibre net, phase-change accumulation energy layer, phase-change energy-storage fibre net, Compound Water Mud layer, phase-change energy-storage fibre net, Compound Water mud layer sequence laying is successively poured in template, obtain plate prototype；

3) by plate prototype after sizing, maintenance, cutting, phase-change energy storage plate is obtained.

Compared with prior art, the beneficial effects of the present invention are: with wood fibre or glass fibre instead of asbestos fibre, The health of operator is ensured, the plate, Compound Water mud layer includes the raw material of following weight parts composition: cement, wooden Fiber, flyash, modifying agent, water-reducing agent, the phase-change accumulation energy layer include the raw material of following weight parts composition: cement, phase transformation storage It can capsule, wood fibre, flyash, modifying agent, water-reducing agent, wherein the phase-change energy storage capsule that is arranged in phase-change accumulation energy layer and set The phase-change accumulation energy ability of plate can be effectively improved by setting the phase-change energy-storage fibre net between plate, be suitable for promoting the use of.

Detailed description of the invention

Fig. 1 is a kind of phase-change energy storage plate of the present invention and preparation method thereof overall structure diagram.

In figure: 1, Compound Water mud layer；2, phase-change accumulation energy layer；3, phase-change energy-storage fibre net；4, phase-change energy storage capsule.

Specific embodiment

Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other Embodiment shall fall within the protection scope of the present invention.

Referring to Fig. 1, the present invention provides a kind of technical solution:

A kind of phase-change energy storage plate and preparation method thereof, including Compound Water mud layer 1 and phase-change accumulation energy layer 2, Compound Water mud layer 1 wrap Include the raw material of following weight parts composition: 40-80 parts of cement, 7-15 parts of wood fibre, 12-16 parts of flyash, modifying agent 0.5-1 Part, 0.5-1 parts of water-reducing agent, phase-change accumulation energy layer 2 include the raw material of following weight parts composition: 40-80 parts of cement, phase-change energy storage capsule 420-30 parts, 7-15 parts of wood fibre, 12-16 parts of flyash, 0.5-1 parts of modifying agent, 0.5-1 parts of water-reducing agent, Compound Water mud layer 1 It is set to about 2 two sides of phase-change accumulation energy layer, Compound Water mud layer 1 and 2 inside of phase-change accumulation energy layer and Compound Water mud layer 1 and phase-change accumulation energy 2 junction of layer are provided with phase-change energy-storage fibre net 3.

Wherein, include the following steps:

1) after the raw material for weighing corresponding mass according to needed for Compound Water mud layer 1 and phase-change accumulation energy layer 2, respectively by Compound Water The raw material of mud layer 1 and phase-change accumulation energy layer 2 is stirred；

2) according to Compound Water mud layer 1, phase-change energy-storage fibre net 3, complex cement after on the conveyor by the placement of plate template, Layer 1, phase-change energy-storage fibre net 3, phase-change accumulation energy layer 2, phase-change energy-storage fibre net 3, phase-change accumulation energy layer 2, phase-change energy-storage fibre net 3, Compound Water mud layer 1, phase-change energy-storage fibre net 3, Compound Water mud layer 1 sequence laying is successively poured in template, obtain plate original Type；

3) by plate prototype after sizing, maintenance, cutting, phase-change energy storage plate is obtained.

It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding And modification, the scope of the present invention is defined by the appended.