阅读说明：本技术 一种铁皮天沟锈蚀穿孔后防渗漏方法 (Antiseep method after a kind of corrosion perforation of iron sheet gutter ) 是由 纪华亭 刘兴才 封建刚 于 2019-08-22 设计创作，主要内容包括：本发明公开了一种铁皮天沟锈蚀穿孔后防渗漏方法,属于防渗漏技术领域。一种铁皮天沟锈蚀穿孔后防渗漏方法,包括：基层清理、天沟加固、天沟内外表面防渗和防腐处理,所述的基层清理包括清理污物、浮锈、焊疤等处理措施,所述的天沟加固处理分为单独细孔和大面积穿孔情况及其修补措施,所述的天沟内表面处理措施为冷粘施工法满铺SBS防水卷材；本发明通过使用SBS防水卷材材料,价格比防腐油漆价格低的多,且使用寿命长,而且施工工艺简便,有利于即时投入工作,成效快,节省工作时间,提高劳动效率,同时也更容易保证防腐质量,消除因防腐质量不合格而导致的工期延误,且可以避免更换天沟对屋面压型钢板可能造成的其他隐患,降低更换成本。(The invention discloses Antiseep methods after a kind of corrosion perforation of iron sheet gutter, belong to water seepage-proof tech field.Antiseep method after a kind of corrosion perforation of iron sheet gutter, it include: base cleaning, gutter is reinforced, gutter surfaces externally and internally is prevented blending preservative treatment, the base cleaning includes the treatment measures such as cleaning dirt, floating rust, crator, the gutter consolidation process is divided into independent pore and large area perforation situation and its repairing measures, and the gutter inner surface treatment measure is that cold bonding construction method completely spreads SBS waterproof roll；By the present invention in that with SBS water-proofing coiled material, price is more low-cost than antifouling paint more, and long service life, and construction technology is easy, be conducive to devote oneself to work immediately, effect is fast, saves the working time, improves labor efficiency, it is also easier to guarantee anticorrosive quality simultaneously, eliminate because anticorrosive quality it is unqualified caused by construction delay, and replacement cost can be reduced to avoid other hidden danger that may cause to roofing profiled sheet of replacement gutter.)

1. Antiseep method after a kind of iron sheet gutter corrosion perforation characterized by comprising base cleaning, gutter reinforcing, gutter Surfaces externally and internally is anti-to blend preservative treatment.

2. Antiseep method after a kind of iron sheet gutter corrosion perforation according to claim 1, which is characterized in that the base Layer cleaning includes the treatment measures such as cleaning dirt, floating rust, crator.

3. Antiseep method after a kind of iron sheet gutter corrosion perforation according to claim 2, which is characterized in that using following Step is operated

S1, broom is used to clear away the dirt in gutter first；

S2, rice washing water is sprinkled upon to gutter surface；

S3, the floating rust on surface, crator and paint slight crack are thoroughly polished completely using motor wire brush；

S4, the remaining dirt of gutter after step S3 operation is blown off using high-pressure airless spraying gun；

S5, it sprays water to the gutter after step S3 operation, gutter surface is made to keep clean.

4. Antiseep method after a kind of iron sheet gutter corrosion perforation according to claim 1, which is characterized in that the day Ditch consolidation process is divided into independent pore and large area perforation situation and its repairing measures.

5. Antiseep method after a kind of iron sheet gutter corrosion perforation according to claim 4, which is characterized in that using following Step is operated

S6, visual inspection gutter overlapping part weldquality, check whether there is the place of loosening comprehensively；

It is S7, the local electric drill loosened in step S6 is secured to steel construction by rivet；

S8, for gutter inside, individually dotted pore can be disregarded, and large area site of perforation in gutter can be covered Color steel plate is reinforced with rivet.

6. Antiseep method after a kind of iron sheet gutter corrosion perforation according to claim 1, which is characterized in that the day Ditch inner surface treatment measure is that cold bonding construction method completely spreads SBS waterproof roll.

7. Antiseep method after a kind of iron sheet gutter corrosion perforation according to claim 6, is grasped using following steps Make

S9: to gutter inner surface, base is cleared up, it is made to keep clean；

S10: in one layer of the uniform brushing petroleum series base treatment agent of base, a period of time is stood, is made it dry；

S11: to inorganic agent uniform brushing adhesive of the step S10 after dry；

S12: after the modified coiled material of SBS is put well by predetermined position, starting paving from low to high, makes coiled material by current direction paving, The overlapping the slot that 10cm should all vertically and horizontally be reserved, it is viscous flat with adhesive；

Roller compaction is used after S13: step S12 several minutes of drying.

8. Antiseep method after a kind of iron sheet gutter corrosion perforation according to claim 1, which is characterized in that the day The processing of ditch surface anticorrosion is operated using following steps

S14: gutter surface is cleared up；

S15: priming, intermediate coat and finishing coat are applied to cleaning position and carry out anti-corrosion protection.

9. Antiseep method after a kind of iron sheet gutter corrosion perforation according to claim 8, which is characterized in that the gutter The preservative treatment of surfaces externally and internally base should carry out simultaneously.

Technical field

The present invention relates to Antiseep methods behind water seepage-proof tech field more particularly to a kind of corrosion perforation of iron sheet gutter.

Background technique

Gutter refers to that the recessed portion between two hip of building roofing, roof drainage divide functional in organized water drainage and inorganization to drain, have Tissue draining is usually being arranged down again by rain pipe in rainwater collection to gutter, and the ditch for gathering rainwater is thus referred to as gutter, and gutter is more It is made of galvanized iron sheet or asbestos cement.

Steel-structure factory building rise in China's also has phase of history, and the exhaust gas and dust adhesion that some workshops discharge throughout the year are in iron It on skin gutter, accumulates over a long period, causes the corrosion of iron sheet gutter serious, different degrees of perforated phenomenon occur in individual places, to production It causes a hidden trouble with personal safety, it is existing the solution perforated occur to gutter, it is on the one hand to smear to prevent in gutter outer surface Corruption paint, but antifouling paint price is higher, and operating process is cumbersome, the duration is longer, is on the other hand the day for replacing roof Ditch, but gutter may cause other hidden danger to roofing profiled sheet in replacement process, cause property or personal security by To influence.

Summary of the invention

The purpose of the present invention is to solve problems of the prior art, and a kind of iron sheet gutter corrosion proposed is worn Antiseep method behind hole.

To achieve the goals above, present invention employs following technical solutions:

Antiseep method after a kind of corrosion perforation of iron sheet gutter, comprising: base cleaning, gutter reinforce, gutter surfaces externally and internally antiseepage And preservative treatment.

Preferably, the base cleaning includes the treatment measures such as cleaning dirt, floating rust, crator.

Preferably, it is operated using following steps

S1, broom is used to clear away the dirt in gutter first；

S2, rice washing water is sprinkled upon to gutter surface；

S3, the floating rust on surface, crator and paint slight crack are thoroughly polished completely using motor wire brush；

S4, the remaining dirt of gutter after step S3 operation is blown off using high-pressure airless spraying gun；

S5, it sprays water to the gutter after step S3 operation, gutter surface is made to keep clean.

Preferably, the gutter consolidation process is divided into independent pore and large area perforation situation and its repairing measures.

Preferably, it is operated using following steps

S6, visual inspection gutter overlapping part weldquality, check whether there is the place of loosening comprehensively；

It is S7, the local electric drill loosened in step S6 is secured to steel construction by rivet；

S8, for gutter inside, individually dotted pore can be disregarded, and large area site of perforation in gutter can be covered Color steel plate is reinforced with rivet.

Preferably, the gutter inner surface treatment measure is that cold bonding construction method completely spreads SBS waterproof roll.

Preferably, it is operated using following steps

S9: to gutter inner surface, base is cleared up, it is made to keep clean；

S10: in one layer of the uniform brushing petroleum series base treatment agent of base, a period of time is stood, is made it dry；

S11: to inorganic agent uniform brushing adhesive of the step S10 after dry；

S12: after the modified coiled material of SBS is put well by predetermined position, starting paving from low to high, makes coiled material by current direction paving, The overlapping the slot that 10cm should all vertically and horizontally be reserved, it is viscous flat with adhesive；

Roller compaction is used after S13: step S12 several minutes of drying.

Preferably, gutter surface anticorrosion processing is operated using following steps

S14: gutter surface is cleared up；

S15: priming, intermediate coat and finishing coat are applied to cleaning position and carry out anti-corrosion protection.

Preferably, gutter surfaces externally and internally base preservative treatment should carry out simultaneously.

Compared with prior art, the present invention provides Antiseep method after a kind of corrosion perforation of iron sheet gutter, have following The utility model has the advantages that

1, Antiseep method after iron sheet gutter corrosion perforation, when iron sheet gutter because the time causes corrosion serious too long, individually It when different degrees of perforated phenomenon occurs in side, needs to repair iron sheet gutter, uses broom by the dirt in gutter first Cleaning, is sprinkled with rice washing water in gutter, and rice washing water has certain rust removing function, after convenient in 5.5-6 in acidity, pH value Brush cleaning, then by motor wire brush by the floating rust on gutter surface, crator and paint slight crack thoroughly polish completely, The dirts such as rust stain after later being brushed motor wire brush using high-pressure airless spraying gun are blown off, then by hydraulic giant to gutter surface into Further cleaning of going is handled, and observes whether gutter overlapping part loosens later, passes through electric drill for rivet for the region of loosening It is fastened with steel construction, for gutter inside, individually dotted perforation can be disregarded, and for large area site of perforation in gutter Color steel plate can be covered and reinforced with rivet, repairing is carried out to site of perforation and then secondary to the progress of gutter inner surface base Cleaning makes it keep clean, and then in one layer of the uniform brushing petroleum series base treatment agent of base, which is cold bottom Seed oil, then after adhesive bitument primer is dry, chloroprene rubber adhesive agent or SBS adhesive is can be used in brushing adhesive, should once be brushed It is even, modified coiled material is put well by predetermined position then, starts paving from low to high, makes coiled material by current direction paving, vertically and horizontally The overlapping the slot that 10cm should all be reserved, it is viscous flat with adhesive, roller compaction is used after several minutes dry, gutter inner surface treatment is arranged It applies as cold bonding construction method, and expires paving SBS waterproof roll, which can be used SBS modified asphalt waterproof coiled material, interior table Outer surface is handled after the preservative treatment of face, and priming, intermediate coat and finishing coat are applied to cleaning position and carry out anti-corrosion guarantor Shield, priming paint mainly play the role of closing steel, increase adhesive force, fill and lead up these three, and intermediate coat, which primarily serves, increases coating General thickness, improves the antiseptic property of entire coating, the effect of finishing coat mainly or decoration and protective effect, in general finishing coat at Membrane substance comparision contents are high, and filler is less.

It is not directed to part in the device to be the same as those in the prior art or can be realized by using the prior art, the present invention uses Cold bonding construction method completely spreads SBS waterproof roll, reaches antiseep and to gutter corrosion-resistant double effects, by using SBS waterproof roll Material material, price is more low-cost than antifouling paint more, and long service life, and construction technology is easy, is conducive to put into immediately Work, effect is fast, and the floating rust on gutter surface, the paint of bark and dirt can only be needed to clean out when doing antiseepage purposes using SBS , it is not required to that silvery white must be exposed as painting painting anticorrosion, the labor intensity of worker is greatly reduced, when saving work Between, it improves labor efficiency, while being also easier to guarantee anticorrosive quality, eliminates because the duration prolongs caused by anticorrosive quality is unqualified Accidentally, and replacement cost can be reduced to avoid other hidden danger that gutter may cause roofing profiled sheet are replaced.

Specific embodiment

The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation Example is only a part of the embodiment of the present invention, instead of all the embodiments.

Antiseep method after a kind of corrosion perforation of iron sheet gutter, comprising: base cleaning, gutter reinforce, gutter surfaces externally and internally It is anti-to blend preservative treatment.

Base cleaning includes the treatment measures such as cleaning dirt, floating rust, crator,

It is operated using following steps

S1, broom is used to clear away the dirt in gutter first；

S2, rice washing water is sprinkled upon to gutter surface；

S3, the floating rust on surface, crator and paint slight crack are thoroughly polished completely using motor wire brush；

S4, the remaining dirt of gutter after step S3 operation is blown off using high-pressure airless spraying gun；

S5, it sprays water to the gutter after step S3 operation, gutter surface is made to keep clean.

Gutter consolidation process is divided into independent pore and large area perforation situation and its repairing measures,

It is operated using following steps

S6, visual inspection gutter overlapping part weldquality, check whether there is the place of loosening comprehensively；

It is S7, the local electric drill loosened in step S6 is secured to steel construction by rivet；

S8, for gutter inside, individually dotted pore can be disregarded, and large area site of perforation in gutter can be covered Color steel plate is reinforced with rivet.

Gutter inner surface treatment measure is that cold bonding construction method completely spreads SBS waterproof roll,

It is operated using following steps

S9: to gutter inner surface, base is cleared up, it is made to keep clean；

S10: in one layer of the uniform brushing petroleum series base treatment agent of base, a period of time is stood, is made it dry；

S11: to inorganic agent uniform brushing adhesive of the step S10 after dry；

S12: after the modified coiled material of SBS is put well by predetermined position, starting paving from low to high, makes coiled material by current direction paving, The overlapping the slot that 10cm should all vertically and horizontally be reserved, it is viscous flat with adhesive；

Roller compaction is used after S13: step S12 several minutes of drying.

The processing of gutter surface anticorrosion is operated using following steps

S14: gutter surface is cleared up；

S15: priming, intermediate coat and finishing coat are applied to cleaning position and carry out anti-corrosion protection.

The preservative treatment of gutter surfaces externally and internally base should carry out simultaneously.

In the present invention, when iron sheet gutter because the time causes corrosion serious too long, there is different degrees of perforation in individual places It when phenomenon, needs to repair iron sheet gutter, the dirt in gutter is cleared away using broom first, is sprinkled with rice washing water in gutter Interior, rice washing water has certain rust removing function in 5.5-6 in acidity, pH value, then the brush cleaning after convenience passes through Motor wire brush thoroughly polishes the floating rust on gutter surface, crator and paint slight crack completely, uses high-pressure airless spraying gun later The dirts such as the rust stain after motor wire brush is brushed are blown off, then carry out further clean processing to gutter surface by hydraulic giant, Whether observation gutter overlapping part loosens later, the region of loosening is fastened rivet and steel construction by electric drill, for day Individually dotted perforation can be disregarded inside ditch, and can cover color steel plate for large area site of perforation in gutter and use rivet Reinforced, to site of perforation carry out repairing and then it is secondary gutter inner surface base is cleared up, so that its is kept clean, so Afterwards in one layer of the uniform brushing petroleum series base treatment agent of base, which is adhesive bitument primer, then to adhesive bitument primer After drying, chloroprene rubber adhesive agent or SBS adhesive is can be used in brushing adhesive, should once be brushed uniformly, then presses modified coiled material Predetermined position is put well, is started paving from low to high, is made coiled material by current direction paving, should all vertically and horizontally reserve the overlap joint of 10cm Seam, it is viscous flat with adhesive, roller compaction is used after several minutes dry, the measure to gutter inner surface treatment is cold bonding construction method, and SBS waterproof roll is completely spread, which can be used SBS modified asphalt waterproof coiled material, right after inner surface preservative treatment Outer surface is handled, and is applied priming, intermediate coat and finishing coat to cleaning position and carried out anti-corrosion protection, and priming paint mainly plays envelope Steel are closed, increases adhesive force, fill and lead up these three effects, intermediate coat primarily serves the general thickness for increasing coating, improves entire apply The antiseptic property of layer, the effect of finishing coat is mainly still decorated and protective effect, and film forming matter comparision contents are high in general finishing coat, fills out Expect less.

The present invention completely spreads SBS waterproof roll using cold bonding construction method, reaches antiseep and to gutter corrosion-resistant double effects, By using SBS water-proofing coiled material, price is more low-cost than antifouling paint more, and long service life, and construction technology letter Just, be conducive to devote oneself to work immediately, effect is fast, and the floating rust on gutter surface, the oil of bark can be only needed when doing antiseepage purposes using SBS Paint and dirt are cleaned out, and are not required to that silvery white must be exposed as painting painting anticorrosion, are greatly reduced the labour of worker Intensity saves the working time, improves labor efficiency, while being also easier to guarantee anticorrosive quality, eliminates because anticorrosive quality is unqualified Caused by construction delay, and replacement can be reduced to avoid other hidden danger that may cause to roofing profiled sheet of replacement gutter Cost.

The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto, Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.