阅读说明：本技术 墨脱石日用瓷的制备方法 (The preparation method of Motuo stone household china ) 是由 刘付明 吕学贵 于 2019-09-25 设计创作，主要内容包括：本发明提供了一种墨脱石日用瓷的制备方法,将墨脱石坯体泥料经球磨细碎,经过箩、滤泥、真空搅泥调制,再经滚压成型得到半成品坯,施釉后经高温烧制而成。本发明的有益效果是：坯体中墨脱石与釉形成牢固结合层,墨脱石与釉原料在高温作用下促进釉表面细腻,给人以稳重素雅的感觉,制成后的表面对油脂吸附性差,清水冲刷即可洗掉餐后瓷釉表面上的油脂,健康环保；墨脱石日用瓷在使用时可向水释放弱碱性,水的活性得以强化,达到活性化水养生的目的。(The present invention provides a kind of preparation methods of Motuo stone household china, and Motuo stone green body pug is fine crushing through ball milling, stir mud modulation by square-bottomed bamboo basket, filter mud, vacuum, then obtain semi-finished product base through roll forming, fire after glazing through high temperature.The beneficial effects of the present invention are: Motuo stone and glaze form firm connection layer in green body, Motuo stone and glaze raw material promote glaze surface fine and smooth under high temperature action, give steady plain feeling, surface after being made is poor to grease adsorptivity, scour without sediment motion can wash off the grease on postprandial enamel surface, health environment-friendly；Motuo stone household china can discharge alkalescent to water when in use, and the activity of water is strengthened, and achieve the purpose that activate water health.)

1. a kind of preparation method of Motuo stone household china, it is characterised in that: Motuo stone green body pug is fine crushing through ball milling, pass through Square-bottomed bamboo basket, filter mud, vacuum stir mud modulation, then obtain semi-finished product base through roll forming, fire after glazing through high temperature.

2. the preparation method of Motuo stone household china according to claim 1, it is characterised in that: burnt after glazing through 1300 DEG C of high temperature It makes.

3. the preparation method of Motuo stone household china according to claim 2, it is characterised in that: burnt after glazing through 1300 DEG C of high temperature System forms for 16 hours.

4. the preparation method of Motuo stone household china according to claim 1, it is characterised in that: the semi-finished product base is household china Semi-finished product blueness base.

5. the preparation method of Motuo stone household china according to claim 1, it is characterised in that: in the Motuo stone green body pug Motuo stone comprising 30-50%.

6. the preparation method of Motuo stone household china according to claim 5, it is characterised in that: the main ingredient of the Motuo stone It include: the SiO that content is 55%₂, content be 1% Fe₂O₃, content be 10% Al₂O₃, the MgO that content is 23%, content is 9% loss on ignition.

7. the preparation method of Motuo stone household china according to claim 1, it is characterised in that: the glaze composition of glazing includes: The SiO that content is 66.34%₂, content be 15.48% Al₂O₃, content be 0.08% Fe₂O₃, the CaO that content is 7.77%, The MgO that content is 1.30%, the K that content is 3.23%₂O, the Na that content is 0.48%₂O, the igloss that content is 5.07%.

Technical field

The present invention relates to ceramics more particularly to a kind of preparation methods of Motuo stone household china.

Background technique

Traditional household china is easy absorption grease, is unfavorable for cleaning, also, can not activate water.

Summary of the invention

In order to solve the problems in the prior art, the present invention provides a kind of preparation methods of Motuo stone household china.

The present invention provides a kind of preparation methods of Motuo stone household china, and Motuo stone green body pug is fine crushing through ball milling, warp It crosses square-bottomed bamboo basket, filter mud, vacuum and stirs mud modulation, then obtain semi-finished product base through roll forming, fired after glazing through high temperature.

As a further improvement of the present invention, it is fired after glazing through 1300 DEG C of high temperature.

As a further improvement of the present invention, it fires 16 hours and forms through 1300 DEG C of high temperature after glazing.

As a further improvement of the present invention, the semi-finished product base is household china semi-finished product blueness base.

It as a further improvement of the present invention, include the Motuo stone of 30-50% in the Motuo stone green body pug.

As a further improvement of the present invention, the main ingredient of the Motuo stone includes: the SiO that content is 55%₂, content For 1% Fe₂O₃, content be 10% Al₂O₃, the MgO that content is 23%, the loss on ignition that content is 9%.

As a further improvement of the present invention, the glaze composition of glazing includes: the SiO that content is 66.34%₂, content is 15.48% Al₂O₃, content be 0.08% Fe₂O₃, the CaO that content is 7.77%, the MgO that content is 1.30%, content is 3.23% K₂O, the Na that content is 0.48%₂O, the igloss that content is 5.07%.

The beneficial effects of the present invention are: through the above scheme, Motuo stone and glaze form firm connection layer, Motuo stone in green body Promote glaze surface fine and smooth under high temperature action with glaze raw material, give steady plain feeling, grease is inhaled on the surface after being made Attached property is poor, and scour without sediment motion can wash off the grease on postprandial enamel surface, health environment-friendly；Motuo stone household china when in use can be to Water discharges alkalescent, and the activity of water is strengthened, and achievees the purpose that activate water health.

Specific embodiment

The invention will be further described With reference to embodiment.

A kind of preparation method of Motuo stone household china, by Motuo stone green body pug through ball milling is fine crushing reach requirement after, pass through Square-bottomed bamboo basket, filter mud, vacuum stir mud and are modulated to qualified pug, then obtain semi-finished product base through roll forming, burn after glazing through 1300 DEG C of high temperature System forms for 16 hours.

The semi-finished product base is household china semi-finished product blueness base.

It include the Motuo stone of 30-50% in the Motuo stone green body pug.

The main ingredient of the Motuo stone includes: 55% SiO₂, 1% Fe₂O₃, 10% Al₂O₃, 23% MgO, 9% loss on ignition, Remaining is micro, adds up to 98%.

The glaze composition of glazing includes: 66.34%SiO₂, 15.48% Al₂O₃, 0.08% Fe₂O₃, 7.77% CaO, 1.30% MgO, 3.23% K₂O, 0.48% Na₂O, 5.07% igloss add up to 99.83%.

Using Motuo stone household china made of a kind of preparation method of Motuo stone household china provided by the invention, porcelain body at Part is as follows:

Composition: SiO₂ Al₂O₃ Fe₂O₃ TiO₂ CaO MgO

Content: 61.48% 17.43% 0.71% 0.19% 0.42% 9.12%

Composition: K₂O Na₂O igloss is total

Content: 1.63% 0.62% 7.82% 99.42%.

A kind of preparation method of Motuo stone household china provided by the invention, the food stewed according to often feeding Motuo stone pot is to height Blood pressure, heart disease, cardio-cerebrovascular diseases patient have apparent food therapy health effect, are main former with natural minerals Motuo stone Material is reasonably combined with traditional ceramics raw material, Motuo stone raw material is applied to household china blank formulation, again through 1300 DEG C of height after glazing Temperature is fired.Motuo stone and glaze form firm connection layer in green body, and Motuo stone and glaze raw material promote glaze table under high temperature action Face is fine and smooth, gives steady plain feeling, Motuo stone Glaze for chinaware is poor to grease adsorptivity, and scour without sediment motion can be washed off after the meal Grease on enamel surface, health environment-friendly.Motuo stone household china can discharge alkalescent, the activity of water to aqueous food when in use Strengthened, achievees the purpose that activate water health.

The above content is a further detailed description of the present invention in conjunction with specific preferred embodiments, and it cannot be said that Specific implementation of the invention is only limited to these instructions.For those of ordinary skill in the art to which the present invention belongs, In Under the premise of not departing from present inventive concept, a number of simple deductions or replacements can also be made, all shall be regarded as belonging to of the invention Protection scope.