阅读说明：本技术 一种天然抗菌护肤针织面料的制造方法 (A kind of manufacturing method of natural antibacterial skin care knitting fabric ) 是由 刘汉星 于 2018-09-13 设计创作，主要内容包括：本发明涉及一种天然抗菌护肤针织面料的制造方法,包括如下步骤：步骤一、将蚕蛹蛋白纤维、莫代尔纤维和腈纶纤维按比重20:40:40混纺织成纱线；步骤二、将纱线与氨纶放入织机内组合针织成面料；步骤三、对面料进行染色整理处理；步骤四、对步骤三的面料成品定型,将蚕蛹蛋白纤维、莫代尔纤维与腈纶纤维按照合理的配比混纺制成纱线并将纱线与氨纶组合织成天然抗菌护肤面料,无需再添加蛋白氨基酸等抗菌类助剂,不仅具有天然抗菌、护肤、保暖、防紫外线的功能,还具有弹性好、柔软性好和优良的吸湿性等特点。(The present invention relates to a kind of manufacturing methods of natural antibacterial skin care knitting fabric, include the following steps: Step 1: silkworm protein fiber, Modal fibre and acrylic fiber are made into yarn by specific gravity 20:40:40 is blended；Fabric is knitted into Step 2: yarn is put into combine in loom with spandex；Step 3: carrying out dyeing arrangement processing to fabric；Step 4: the fabric finished product to step 3 is formed, by silkworm protein fiber, Modal fibre and acrylic fiber according to reasonably match it is blended yarn is made and combines yarn with spandex be made into natural antibacterial skin-protecting fabric, no longer need to the antibacterials analog assistants such as addition Argine Monohydrochloride, not only have the function of natural antibacterial, skin care, warming, antiultraviolet, also has the characteristics that the hygroscopicity that elasticity is good, flexibility is good and excellent.)

1. a kind of manufacturing method of natural antibacterial skin care knitting fabric, characterized by the following steps:

Step 1: silkworm protein fiber, Modal fibre and acrylic fiber are made into yarn by specific gravity 20:40:40 is blended；

Fabric is knitted into Step 2: yarn is put into combine in loom with spandex；

Step 3: carrying out dyeing arrangement processing to fabric；

Step 4: the fabric finished product to step 3 is formed.

2. the manufacturing method of natural antibacterial skin care knitting fabric according to claim 1, it is characterised in that: in step 1, Yarn is formed by weaving using the match close spinning process of network.

3. the manufacturing method of natural antibacterial skin care according to claim 1 knitting fabric, it is characterised in that: the yarn is 40S/1 yarn.

4. the manufacturing method of natural antibacterial skin care according to claim 1 knitting fabric, it is characterised in that: the spandex is 20D spandex.

5. the manufacturing method of natural antibacterial skin care according to claim 1 knitting fabric, it is characterised in that: the loom is Good fortune source circular knitting machine, bore are 30 cun, needle gage 32G, and total needle amount is 3000 needles.

6. the manufacturing method of natural antibacterial skin care knitting fabric according to claim 1, it is characterised in that: in step 2, The a length of 265mm/100 needle of the coil yarn of the yarn, a length of 95mm/100 needle of the coil yarn of the spandex.

7. the manufacturing method of natural antibacterial skin care according to claim 1 knitting fabric, it is characterised in that: the fabric is Spandex plain fabric.

8. the manufacturing method of natural antibacterial skin care knitting fabric according to claim 1, it is characterised in that: the fabric Main component is 30%-50% acrylic fiber, 20%-40% Modal fibre, 20%-40% silkworm protein fiber and 5%-10% spandex.

9. the manufacturing method of natural antibacterial skin care knitting fabric according to claim 1, it is characterised in that: in step 3, It is 190 ± 5 DEG C that embryo, which determines temperature, in dyeing arranging process.

10. the manufacturing method of natural antibacterial skin care knitting fabric according to claim 1, it is characterised in that: in step 4, Setting temperature is 160 ± 5 DEG C.

Technical field

The present invention relates to fabric knitting technology field, espespecially a kind of manufacturing method of natural antibacterial skin care knitting fabric.

Background technique

Traditional antibiotic skin-care class fabric is usually that the antibacterials analog assistants such as silver ion are added when dyeing and arranging to reach The function of antibiotic skin-care, the antibiotic skin-care function of fabric can gradually disappear with prolonged dress and after repeatedly washing It moves back, and the feel of fabric is coarse rough, cloth cover gloss difference is not suitable for use in thermal fabric.

Summary of the invention

To solve the above problems, the present invention, which provides one kind, does not add Antibacterial accessory ingredient, the natural antibacterial shield of durable antibacterial effect The manufacturing method of skin knitting fabric.

To achieve the above object, the present invention, which adopts the following technical scheme that, is: a kind of natural antibacterial skin care knitting fabric Manufacturing method includes the following steps:

Step 1: silkworm protein fiber, Modal fibre and acrylic fiber are made into yarn by specific gravity 20:40:40 is blended；

Fabric is knitted into Step 2: yarn is put into combine in loom with spandex；

Step 3: carrying out dyeing arrangement processing to fabric；

Step 4: the fabric finished product to step 3 is formed.

Preferably, in step 1, yarn is formed by weaving using the match close spinning process of network, and single thread force is high, and close structure is resistance to Mill property is good, and filoplume is few, and 3mm or more nocuousness filoplume is few, and yarn is bright and clean, and fabric quality is high, and pilling resistance is good.

Preferably, the yarn is 40S/1 yarn.

Preferably, the spandex is 20D spandex.

Preferably, the loom is good fortune source circular knitting machine, and bore is 30 cun, needle gage 32G, total needle amount 3000 Needle.

Preferably, in step 2, a length of 265mm/100 needle of the coil yarn of the yarn, the coil yarn of the spandex is a length of 95mm/100 needle.

Preferably, the fabric is spandex plain fabric.

Preferably, the main component of the fabric is 30%-50% acrylic fiber, 20%-40% Modal fibre, 20%-40% Silkworm protein fiber and 5%-10% spandex.

Preferably, in step 3, it is 190 ± 5 DEG C that embryo, which determines temperature, in dyeing arranging process.

Preferably, in step 4, setting temperature is 160 ± 5 DEG C.

The beneficial effects of the present invention are: by silkworm protein fiber, Modal fibre and acrylic fiber according to reasonably matching Than it is blended yarn is made and combines yarn with spandex be made into natural antibacterial skin-protecting fabric, it is anti-to no longer need to addition Argine Monohydrochloride etc. Mushroom auxiliary agent not only has the function of natural antibacterial, skin care, warming, antiultraviolet, also with elasticity is good, flexibility is good and excellent The features such as good hygroscopicity.

Detailed description of the invention

Fig. 1 is silkworm chrysalis pictorial diagram.

Fig. 2 is the pictorial diagram of silkworm protein fiber.

Specific embodiment

Manufacturing method of the present invention about a kind of natural antibacterial skin care knitting fabric, includes the following steps:

Step 1: silkworm protein fiber, Lenzin super fine denier Modal fibre and acrylic fiber are pressed using match network close spinning process Specific gravity 20:40:40 is blended to be made into 40S/1 yarn；

High using single yarn strength made of the match close spinning process of network, close structure, wearability is good, and filoplume is few, and 3mm or more has Evil filoplume is few, and yarn is bright and clean, and fabric quality is high, and pilling resistance is good

The ammonia for being knitted into 190g/m2 grammes per square metre is combined in the circular knitting machine of good fortune source Step 2: 40S/1 yarn is put into 20D spandex Synthetic fibre plain fabric；

Step 3: carrying out dyeing arrangement processing to fabric；

Step 4: the fabric finished product to step 3 is formed.

Preferably, the bore of good fortune source circular knitting machine is 30 cun, needle gage 32G, and total needle amount is 3000 needles.

Preferably, in step 2, a length of 265mm/100 needle of the coil yarn of the yarn, the coil yarn of the spandex is a length of 95mm/100 needle.

Preferably, the main component of the fabric be 37% acrylic fiber, 56% Modal fibre and silkworm protein fiber (because Existing detection method can't separately measure Modal fibre and silkworm protein fiber, therefore the conjunction of the two composition is write on one Rise) and 7% spandex.

Preferably, in step 3, it is 190 ± 5 DEG C that embryo, which determines temperature, in dyeing arranging process.

Preferably, in step 4, setting temperature is 160 ± 5 DEG C.

Silkworm protein fiber is the extraction protein stoste out of silkworm chrysalis, utilizes Polymer Technology, synthetic fiber spinning technology and life Silkworm chrysalis protein stoste is blended object engineering technology with native cellulose, makes protein-enriched on the surface of natural fiber and shape At silkworm chrysalis protein is made of 16 kinds of different aminoacids, highly beneficial to human skin, is had and is resisted ultraviolet light and moisture absorption is ventilative The characteristics of.

Modal fibre is a kind of high wet modulus regenerated celulose fibre, and the raw material of the fiber uses beech, first made It at wood pulp, then is processed into the entire production process of fiber fiber by special spinning technique and there is no any pollution, done strong Close to terylene, wet to improve many, gloss, flexibility, hygroscopicity, dyeability, dyefastness than common viscose glue by force excellent In Pure cotton Product；The fabric being made into it illustrates a kind of face gloss, feels with pleasant soft touch and pendency is felt And the fabulous endurable performance of moisture absorption, it is generally used for the production of underwear.

Acrylic fiber has the title of artificial wool.With soft, bulk, easy dye, bright in colour, fast light, antibacterial, it is not afraid of and damages by worms The advantages that, rebound degree can still keep 65% when elongation 20%, fluffy curling and it is soft, warmth retention property is higher than wool by 15%.

Spandex is the abbreviation of polyurethane fibre, is a kind of elastomer, has excellent elasticity.

The present invention is reasonable in reasonable ratio by silkworm protein fiber, Lenzin super fine denier Modal fibre and acrylic fiber Match it is blended yarn is made and is combined with spandex by yarn and is made into natural antibacterial skin-protecting fabric, merged pupa protein fiber, not The characteristics of Dai Er fiber and acrylic fiber kind functional fiber, no longer needs to the antibacterials analog assistants such as addition Argine Monohydrochloride, not only has There are natural antibacterial, skin care, warming, antiultraviolet function, also has that elasticity is good, flexibility is good and excellent hygroscopicity etc. is special Point, suitable for make the personal clothing such as cold-proof underwear underpants, infant or just finish operation or with special disease at one section In the clothing of patient that cannot have a bath or often movable outdoors or the crowd that is engaged in outwork clothing.

The antibacterial detection of fabric is as shown in table 1:

Table 1

The amino acid content detection of fabric is as shown in table 2:

Table 2

As shown in Table 1 and Table 2, the fabric that this manufacturing method is made into is through authoritative institution according to national standard FZ/T73023-2006 (2012) Detection complies with standard AAA grades of requirements, i.e., still conforms to antibacterial standard washed 50 times, there is up to 96.88% or more bacteriostasis rate.

Embodiment of above be only preferred embodiments of the present invention will be described, not to the scope of the present invention into Row limits, and without departing from the spirit of the design of the present invention, this field ordinary engineering and technical personnel is to technical side of the invention The various changes and improvements that case is made, should fall within the scope of protection determined by the claims of the present invention.