阅读说明：本技术 一种速溶香烟爆珠 (Instant cigarette blasting bead ) 是由 吴士斌 于 2019-09-20 设计创作，主要内容包括：本发明涉及烟草技术领域,具体是一种速溶香烟爆珠,包括以下步骤：S1、多糖亲水胶体制备：将浓度百分比为0.5-2%海藻酸钠、0.5-1.5%果胶、0.5-2.0%i-卡拉胶、1.5-2.0%麦芽糊精、1.0-5.0%香精香料混合加水调匀,通过胶体磨得到复合多糖亲水胶体,水温为50-70℃的水；S2、包液的制备：将浓度百分比为5-10%氯化钙、1-5%甘油、10-20%液体葡萄糖、1-3%三醋酸甘油酯用水溶解调匀,制成混溶液；S3、凝胶反应：将步骤S1得到的复合多糖亲水胶体滴入步骤S2制得的混溶液内。本发明的有益效果使得凝胶爆珠可以实现包埋各种性状的香料,突破了传统爆珠只能包埋油性香料的束缚,并且,当卷烟燃吸时凝胶爆珠被捏破后,凝胶中的水分可以转移到烟气中,使卷烟烟气更柔和湿润。(The invention relates to the technical field of tobacco, in particular to an instant cigarette bead, which comprises the following steps: s1, preparing polysaccharide hydrophilic colloid: mixing sodium alginate 0.5-2%, pectin 0.5-1.5%, I-carrageenan 0.5-2.0%, maltodextrin 1.5-2.0%, and essence 1.0-5.0%, adding water, and grinding to obtain hydrophilic colloid of complex polysaccharide with water temperature of 50-70 deg.C; s2, preparation of an envelope liquid: dissolving 5-10% calcium chloride, 1-5% glycerol, 10-20% liquid glucose, and 1-3% glycerol triacetate with water, and mixing to obtain mixed solution; s3, gel reaction: and (4) dripping the composite polysaccharide hydrophilic colloid obtained in the step (S1) into the mixed solution prepared in the step (S2). The gel bead can embed spices with various properties, breaks through the constraint that the traditional bead can only embed oily spices, and can transfer moisture in gel into smoke after the gel bead is pinched off when a cigarette is smoked, so that the cigarette smoke is softer and more moist.)

1. An instant cigarette blasting bead is characterized in that: including filter rod (1), the bottom bonding of filter rod (1) has cigarette (3), and the outer wall all around of filter rod (1) on the bonding have tipping paper (4), the inside axle center department of filter rod (1) is implanted and is exploded pearl (2), explode pearl (2) including diolame (5), the inside of diolame (5) is dripped into and is had package liquid (6).

2. The instant cigarette popping bead according to claim 1, comprising the steps of:

s1, preparing polysaccharide hydrophilic colloid: mixing sodium alginate 0.5-2%, pectin 0.5-1.5%, I-carrageenan 0.5-2.0%, maltodextrin 1.5-2.0%, and essence 1.0-5.0%, adding water, and grinding to obtain hydrophilic colloid of complex polysaccharide with water temperature of 50-70 deg.C;

s2, preparation of an envelope liquid: dissolving 5-10% calcium chloride, 1-5% glycerol, 10-20% liquid glucose, and 1-3% glycerol triacetate with water, and mixing to obtain mixed solution;

s3, gel reaction: dropping the composite polysaccharide hydrophilic colloid obtained in the step S1 into the mixed solution prepared in the step S2, controlling the flow rate to be 60-120 drops/min, and quickly generating a crosslinking effect under the action of Ca2+ by the polysaccharide hydrophilic colloid to react to generate a glue solution containing hydrogel sphere particles, wherein the reaction time is 5-10 min;

S4, washing gel particles: performing solid-liquid separation on the glue solution prepared in the step S3 to obtain gel ball particles, washing the gel particles with clear water until no glue solution remains on the ball body, and then soaking the prepared ball gel in clear water for 0.5-1 h;

s5, pretreatment of coating glue: dissolving 10-25% gelatin, 1-6% guar gum, 2.5-5.0% chitosan and 0.2-0.5% edible pigment with hot water to obtain coating gum solution with temperature of 70-90 deg.C and concentration of edible pigment solution of 0.2-0.3%;

s6, coating and forming: taking out the gel particles, airing, placing in a coating machine, spraying the coating glue solution prepared in the fifth step on the gel balls under the condition of soft rolling, wherein the application amount of the coating glue solution is 3-10% of the mass of the gel balls, and after the coating glue solution is applied, keeping the gel balls to be soft rolled in the coating machine until the coating film is cooled and solidified to obtain gel popping beads, wherein the application amount of the coating glue solution is 5-8% of the mass of the gel balls;

S7, screening finished products: sieving the gel blasting beads prepared in the step S6 according to the target particle size, and simultaneously removing unqualified beads to obtain qualified gel blasting beads;

S8, implanting a filter: and (5) carrying out food-grade talcum powder bath on the qualified gel popping beads obtained in the step (S7) to enable the surface of the gel popping beads to be stained with a layer of talcum powder, blowing off the redundant talcum powder, and implanting the gel popping beads into the specified position of the cigarette filter.

3. the instant cigarette popping bead as claimed in claim 1, wherein: firstly, sequentially adding selected gelatin, guar gum, chitosan and edible pigment oil into a mixing stirrer, stirring at the rotation speed of 500-600r/min and at the room temperature of 25-28 ℃ for 30-40min, then adding water with corresponding proportion into the stirrer, and stirring at the same temperature and the rotation speed of 600-700r/min for 1-2h to obtain the coating slurry.

4. the instant cigarette popping bead according to claim 3, wherein: and (4) pouring the coating slurry obtained in the step (S5) into a dryer to be dried for 20-30min at the temperature of 35-40 ℃ to obtain a coating solid block, and then fully crushing the coating solid block by using a crusher to obtain coating powder.

5. the instant cigarette popping bead as claimed in claim 1, wherein: drying the initial state of the cigarette exploded bead obtained in the step S4 for 10-15min at the temperature of 38-45 ℃ by a dryer to obtain a finished product of the cigarette exploded bead, and then implanting a cigarette filter into the finished product of the cigarette exploded bead for sale or warehousing for storage.

6. The instant cigarette beadlets of claim 5, wherein: the bead blasting stored in the warehouse is packaged by a sealed plastic bag and then packaged by a hard packaging barrel to prevent external force extrusion, and the packaging quantity of each barrel is controlled below 20 kilograms to avoid the damage to the beads caused by pressure accumulation.

Technical Field

the invention relates to the technical field of tobacco, in particular to an instant cigarette bead.

Background

as the demand of cigarette consumers for diversification of product styles increases, the bead-blasting cigarettes become a new favorite in the market. The bead-blasting cigarette is characterized in that oily beads capable of being blasted by pinching are added into a cigarette filter stick, the beads form a shell by taking a glue substance as a wall material, oily spices with characteristic aroma are wrapped in the shell, and the oily spices can be released by pinching when the cigarette is smoked, so that the aroma of the cigarette can be modified and compensated.

Such liquid blasting beads have a number of drawbacks: 1. because the limitation of the wrapping material only contains the oily perfume, other polar solvents can damage wall materials to cause liquid leakage, however, the oily perfume only accounts for less than 20 percent of the perfume family, and the fragrance type of the liquid popping beads is limited; 2. the flavor release of the liquid bead is very unstable, the flavor is too strong when the bead is crushed, but the characteristic flavor becomes very weak along with the burning and smoking of the cigarette; 3. the liquid blasting beads have very high cost due to the complex manufacturing process and high defective rate; 4. when the liquid explosion bead is pinched and exploded, oil stains can often seep out to pollute the filter stick and influence the appearance.

disclosure of Invention

the invention aims to provide an instant cigarette popping bead to solve the problems that the limitation of a wrapping material only can contain oil spices, other polar solvents can damage a wall material to cause liquid leakage, and the fragrance release of the liquid popping bead is very unstable in the background technology.

the technical scheme of the invention is as follows: the utility model provides an instant cigarette explodes pearl, includes the filter rod, the bottom of filter rod bonds there is the cigarette, and bonds on the outer wall all around of filter rod and have the tipping paper, the inside axle center department of filter rod plants and has exploded the pearl, it includes the diolame to explode the pearl, the inside of diolame is dripped into and is had the package liquid.

A preparation method of instant cigarette blasting beads comprises the following steps:

S1, preparing polysaccharide hydrophilic colloid: mixing sodium alginate 0.5-2%, pectin 0.5-1.5%, I-carrageenan 0.5-2.0%, maltodextrin 1.5-2.0%, and essence 1.0-5.0%, adding water, and grinding to obtain hydrophilic colloid of complex polysaccharide with water temperature of 50-70 deg.C;

S2, preparation of an envelope liquid: dissolving 5-10% calcium chloride, 1-5% glycerol, 10-20% liquid glucose, and 1-3% glycerol triacetate with water, and mixing to obtain mixed solution;

S3, gel reaction: dropping the composite polysaccharide hydrophilic colloid obtained in the step S1 into the mixed solution prepared in the step S2, controlling the flow rate to be 60-120 drops/min, and quickly generating a crosslinking effect under the action of Ca2+ by the polysaccharide hydrophilic colloid to react to generate a glue solution containing hydrogel sphere particles, wherein the reaction time is 5-10 min;

S4, washing gel particles: performing solid-liquid separation on the glue solution prepared in the step S3 to obtain gel ball particles, washing the gel particles with clear water until no glue solution remains on the ball body, and then soaking the prepared ball gel in clear water for 0.5-1 h;

s5, pretreatment of coating glue: dissolving 10-25% gelatin, 1-6% guar gum, 2.5-5.0% chitosan and 0.2-0.5% edible pigment with hot water to obtain coating gum solution with temperature of 70-90 deg.C and concentration of edible pigment solution of 0.2-0.3%;

s6, coating and forming: taking out the gel particles, airing, placing in a coating machine, spraying the coating glue solution prepared in the fifth step on the gel balls under the condition of soft rolling, wherein the application amount of the coating glue solution is 3-10% of the mass of the gel balls, and after the coating glue solution is applied, keeping the gel balls to be soft rolled in the coating machine until the coating film is cooled and solidified to obtain gel popping beads, wherein the application amount of the coating glue solution is 5-8% of the mass of the gel balls;

s7, screening finished products: sieving the gel blasting beads prepared in the step S6 according to the target particle size, and simultaneously removing unqualified beads to obtain qualified gel blasting beads;

S8, implanting a filter: and (5) carrying out food-grade talcum powder bath on the qualified gel popping beads obtained in the step (S7) to enable the surface of the gel popping beads to be stained with a layer of talcum powder, blowing off the redundant talcum powder, and implanting the gel popping beads into the specified position of the cigarette filter.

further, firstly, sequentially adding the selected gelatin, guar gum, chitosan and edible pigment oil into a mixing stirrer, stirring at the rotation speed of 500-600r/min at room temperature of 25-28 ℃ for 30-40min, then adding water with corresponding proportion into the stirrer, and stirring at the same temperature at the rotation speed of 600-700r/min for 1-2h to obtain the coating slurry.

Further, the coating slurry in the step S5 is poured into a drying machine to be dried for 20-30min at the temperature of 35-40 ℃ to obtain a coating solid block, and then the coating solid block is fully crushed by a crusher to obtain coating powder.

further, drying the initial state of the cigarette exploded bead obtained in the step S4 for 10-15min at the temperature of 38-45 ℃ by a dryer to obtain a finished product of the cigarette exploded bead, and then implanting a cigarette filter tip into the finished product of the cigarette exploded bead for sale or warehousing for storage.

Furthermore, the bead blasting stored in a warehouse is packaged by a sealed plastic bag and then packaged by a hard packaging barrel to prevent external force extrusion, and the packaging quantity of each barrel is controlled below 20 kilograms, so that the damage to the beads caused by pressure accumulation is avoided.

Compared with the prior art, the invention provides the instant cigarette popping bead through improvement, and the instant cigarette popping bead has the following improvements and advantages:

(1) The principle of the gel bead blasting of the invention is to embed fragrant substances by the gel, and the gel has hydrophilicity and contains a large amount of moisture, so that the gel bead blasting can embed various flavors, the constraint that the traditional bead blasting can only embed oily flavors is broken through, and when a cigarette is smoked, the moisture in the gel can be transferred to smoke, so that the cigarette smoke is softer and more moist.

drawings

the invention is further explained below with reference to the figures and examples:

FIG. 1 is a schematic structural view of the present invention;

FIG. 2 is a schematic view of the bead blasting configuration of the present invention;

Fig. 3 is a schematic view of the flow structure of the present invention.

Description of reference numerals:

1 filter tip rod, 2 blasting beads, 3 cigarettes, 4 tipping paper, 5 coating films and 6 liquid coatings.

Detailed Description

The present invention will be described in detail with reference to fig. 1 to 3, and the technical solutions in the embodiments of the present invention will be clearly and completely described, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.

It will be understood that when an element is referred to as being "secured to" another element, it can be directly on the other element or intervening elements may also be present. When a component is referred to as being "connected" to another component, it can be directly connected to the other component or intervening components may also be present. When a component is referred to as being "disposed on" another component, it can be directly on the other component or intervening components may also be present. The terms "vertical," "horizontal," "left," "right," and the like as used herein are for illustrative purposes only.

unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. The terminology used in the description of the invention herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. As used herein, the term "and/or" includes any and all combinations of one or more of the associated listed items.

The invention provides an instant cigarette blasting bead through improvement, as shown in figures 1-3, the instant cigarette blasting bead comprises a filter rod 1, a cigarette 3 is bonded at the bottom end of the filter rod 1, tipping paper 4 is bonded on the peripheral outer wall of the filter rod 1, a blasting bead 2 is implanted in the inner axis of the filter rod 1, the blasting bead 2 comprises a coating film 5, and a coating liquid 6 is dripped into the coating film 5.