阅读说明：本技术 一种轻质人防门的制造工艺 (Manufacturing process of light civil air defense door ) 是由 纪建华 陈春洋 赵继光 沈旭辉 周小兵 于 2019-08-29 设计创作，主要内容包括：本发明公开了一种轻质人防门的制造工艺,包括如下步骤：第一步,将设计好铺层的碳纤维预浸布依照排叠结构顺序卷制碳纤维加强管,烘干固化后脱模；第二步,将碳纤维加强管垂直于加强芯层并贯穿设置,碳纤维加强管贯穿加强芯层的两端长度一致。该轻质人防门的制造工艺可减轻重量的同时提高强度和使用寿命。(the invention discloses a manufacturing process of a light civil air defense door, which comprises the following steps: firstly, rolling the carbon fiber prepreg cloth with the designed spreading layer into a carbon fiber reinforced pipe according to a row-stacking structure sequence, drying, curing and demoulding; and secondly, arranging the carbon fiber reinforced pipe perpendicular to the reinforcing core layer in a penetrating manner, wherein the lengths of two ends of the carbon fiber reinforced pipe penetrating through the reinforcing core layer are consistent. The manufacturing process of the light civil air defense door can reduce the weight, improve the strength and prolong the service life.)

一种轻质人防门的制造工艺

技术领域：

本发明涉及人防门领域，具体讲是一种轻质人防门的制造工艺。

背景技术：

现有的人防门通常是混凝土或者钢结构以及两者的结合，这样的人防门不仅笨重，而且强度上差强人意，使用寿命短。

发明内容

：

本发明所要解决的技术问题是，提供一种可以生产机械强度高、使用寿命长的轻质人防门的制造工艺。

本发明的技术解决方案是，提供一种轻质人防门的制造工艺，包括如下步骤：

第一步，将设计好铺层的碳纤维预浸布依照排叠结构顺序卷制碳纤维加强管，烘干固化后脱模；

第二步，将碳纤维加强管垂直于加强芯层并贯穿设置，碳纤维加强管贯穿加强芯层的两端长度一致；

第三步，制作设计要求的人防门模板，将第二步中成型的加强结构放入模板中，将混凝土浇注其中，捣固混凝土使其密实，其中混凝土由以下质量份数原料配制，水泥200份、硅酸铁25份、膨胀粉60份、玻璃纤维15份，硅酸钠10份，二氧化钛纳米粉20份，水120份；

第四步，待混凝土固化后，再在人防门外表面喷涂搪瓷釉层并高温烧结，搪瓷釉层由锑白、高岭土、氧化锆、尿素和去离子水配置而成。

本发明的有益效果是：本方法制备的人防门可以在大幅减轻重量的前提下保持人防门的抗冲击力，并提高其使用寿命，相同厚度条件下，重量比原来的混凝土人防门轻45％以上，并且防潮防霉防氧化，强度比相同厚度混凝土人防门高3倍，大大提高了结构的疲劳寿命和抗冲击能力。

作为优选，加强芯层为发泡聚酯弹性体。

具体实施方式

：

下面结合具体实施方式对本发明作进一步说明：

一种轻质人防门的制造工艺，包括如下步骤：

第一步，将设计好铺层的碳纤维预浸布依照排叠结构顺序卷制碳纤维加强管，烘干固化后脱模；

第二步，将碳纤维加强管垂直于加强芯层并贯穿设置，碳纤维加强管贯穿加强芯层的两端长度一致；加强芯层为发泡聚酯弹性体，碳纤维加强管的长度为人防门厚度的三分之二；

第三步，制作设计要求的人防门模板，将第二步中成型的加强结构放入模板中，将混凝土浇注其中，捣固混凝土使其密实，其中混凝土由以下质量份数原料配制，水泥200份、硅酸铁25份、膨胀粉60份、玻璃纤维15份，硅酸钠10份，二氧化钛纳米粉20份，水120份；

第四步，待混凝土固化后，再在人防门外表面喷涂搪瓷釉层并高温烧结，搪瓷釉层由锑白、高岭土、氧化锆、尿素和去离子水配置而成。