阅读说明：本技术 一种由改性和支座灌浆料及环氧料特定配比的灌浆料 (Grouting material prepared from modified support grouting material and epoxy material in specific ratio ) 是由 陈德林 于 2020-05-28 设计创作，主要内容包括：本发明公开了一种由改性和支座灌浆料及环氧料特定配比的灌浆料,其特征在于,包括如下质量份数的组份,改性灌浆料：600份～1000份；支座灌浆料：500份～800份；环氧树脂料：100份～200份；水：200份～300份；减水剂：5份～10份；早强剂：10份～30份；防离析剂：5份～15份；微膨胀剂：0.1份～0.5份；其他外加剂：10份～30份。本发明具有良好的施工性能,灌注后光滑平整。克服了传统砂浆不平整、易开裂起粉等缺点,并且具有流动性好、微膨胀、无泌水、不离析、开放操作时间长。施工润滑性好。(The invention discloses a grouting material prepared from a modified grouting material, a support and an epoxy material in a specific ratio, which is characterized by comprising the following components in parts by mass: 600 to 1000 portions; grouting material for the support: 500 to 800 portions; epoxy resin material: 100-200 parts; water: 200-300 parts; water reducing agent: 5-10 parts; early strength agent: 10-30 parts; anti-segregation agent: 5-15 parts; a micro-swelling agent: 0.1 to 0.5 portion; other additives: 10 to 30 portions. The invention has good construction performance and is smooth and flat after being poured. Overcomes the defects of unevenness, easy cracking and powder rising and the like of the traditional mortar, and has good fluidity, micro expansion, no bleeding, no segregation and long open operation time. The construction lubricity is good.)

1. The grouting material with specific mixture ratio of modified and support grouting material and epoxy material is characterized by comprising the following components in parts by mass,

modified grouting material: 600 to 1000 portions;

grouting material for the support: 500 to 800 portions;

epoxy resin material: 100-200 parts;

water: 200-300 parts;

water reducing agent: 5-10 parts;

early strength agent: 10-30 parts;

anti-segregation agent: 5-15 parts;

a micro-swelling agent: 0.1 to 0.5 portion;

other additives: 10 to 30 portions.

2. The grouting material prepared from the modified support grouting material and the epoxy material according to the specific ratio of the modified support grouting material to the epoxy material in claim 1, wherein: comprises the following components in parts by mass,

modified grouting material: 700 to 900 portions;

grouting material for the support: 600 to 700 portions;

epoxy resin material: 150 to 180 portions;

water: 220-250 parts of a solvent;

water reducing agent: 6-8 parts;

early strength agent: 14-20 parts of a solvent;

anti-segregation agent: 8-12 parts;

a micro-swelling agent: 0.2 to 0.4 portion;

other additives: 15 to 25 portions.

3. The grouting material prepared from the modified support grouting material and the epoxy material according to the specific ratio of the modified support grouting material to the epoxy material in claim 2, wherein: comprises the following components in parts by mass,

modified grouting material: 867.3 parts of a binder;

grouting material for the support: 680 parts of;

epoxy resin material: 169.7 parts;

water: 230 parts of (A);

water reducing agent: 6.3 parts of a mixture;

early strength agent: 16 parts of a mixture;

anti-segregation agent: 9.6 parts;

a micro-swelling agent: 0.3 part;

other additives: 20.8 parts.

4. The grouting material prepared from the modified support grouting material and the epoxy material according to any one of claims 1 to 3, wherein the grouting material comprises the following components in percentage by weight: the adhesive also comprises 25 parts by weight of a thickening agent, wherein the thickening agent is one or more of hydroxymethyl cellulose, hydroxyethyl cellulose and hydroxypropyl methyl cellulose.

5. The grouting material prepared from the modified support grouting material and the epoxy material according to any one of claims 1 to 3, wherein the grouting material comprises the following components in percentage by weight: the micro-swelling agent is UEA swelling agent or CSA swelling agent.

Technical Field

The invention relates to the technical field of grouting materials, in particular to a grouting material prepared from a modified grouting material, a support grouting material and an epoxy material in a specific ratio.

Background

In recent years, in the period of high-speed construction of infrastructure, in the process of bridge construction, a large number of basin-type rubber supports of prefabricated simply supported box girders and cast-in-place girders are installed, grouting is needed to be performed on connecting parts of the box girders and the supports to play a supporting and fixing role, and in the industries of heavy machinery and the like, grouting is needed to be performed on foundation bolts of an equipment foundation to enable the equipment to run quickly and continue production. Therefore how to quickly install and ensure a high quality of installation or repair of the support.

The traditional grouting material has the defects of easy loss of fluidity, slow strength development, new influence on construction progress and construction quality, and the automatic diagnosis alarm and remote monitoring system for the faults of the logistics equipment is provided aiming at the problems.

Disclosure of Invention

The invention aims to provide a grouting material prepared from a modified support grouting material and an epoxy material in a specific ratio, so as to solve the problems in the background technology.

In order to achieve the purpose, the invention provides the following technical scheme: a grouting material prepared from a modified support grouting material and an epoxy material in a specific ratio comprises the following components in parts by mass,

modified grouting material: 600 to 1000 portions;

grouting material for the support: 500 to 800 portions;

epoxy resin material: 100-200 parts;

water: 200-300 parts;

water reducing agent: 5-10 parts;

early strength agent: 10-30 parts;

anti-segregation agent: 5-15 parts;

a micro-swelling agent: 0.1 to 0.5 portion;

other additives: 10 to 30 portions.

Preferably, the grouting material prepared from the modified and support grouting material and the epoxy material in a specific ratio comprises the following components in parts by mass,

modified grouting material: 700 to 900 portions;

grouting material for the support: 600 to 700 portions;

epoxy resin material: 150 to 180 portions;

water: 220-250 parts of a solvent;

water reducing agent: 6-8 parts;

early strength agent: 14-20 parts of a solvent;

anti-segregation agent: 8-12 parts;

a micro-swelling agent: 0.2 to 0.4 portion;

other additives: 15 to 25 portions.

Preferably, the grouting material prepared from the modified and support grouting material and the epoxy material in a specific ratio comprises the following components in parts by mass,

modified grouting material: 867.3 parts of a binder;

grouting material for the support: 680 parts of;

epoxy resin material: 169.7 parts;

water: 230 parts of (A);

water reducing agent: 6.3 parts of a mixture;

early strength agent: 16 parts of a mixture;

anti-segregation agent: 9.6 parts;

a micro-swelling agent: 0.3 part;

other additives: 20.8 parts.

Preferably, the composite material further comprises 25 parts by weight of a thickening agent, and the thickening agent is one or more of hydroxymethyl cellulose, hydroxyethyl cellulose and hydroxypropyl methyl cellulose.

Preferably, the micro-swelling agent is a UEA swelling agent or a CSA swelling agent.

Compared with the prior art, the invention has the beneficial effects that: the grouting material prepared from the modified support grouting material and the epoxy material in a specific ratio has good construction performance, and is smooth and flat after being poured. Overcomes the defects of unevenness, easy cracking and powder rising and the like of the traditional mortar, and has good fluidity, micro expansion, no bleeding, no segregation and long open operation time. The construction lubricity is good.

Detailed Description

The technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.

The invention provides a technical scheme that: a grouting material prepared from a modified support grouting material and an epoxy material in a specific ratio comprises the following components in parts by mass,

modified grouting material: 600 to 1000 portions;

grouting material for the support: 500 to 800 portions;

epoxy resin material: 100-200 parts;

water: 200-300 parts;

water reducing agent: 5-10 parts;

early strength agent: 10-30 parts;

anti-segregation agent: 5-15 parts;

a micro-swelling agent: 0.1 to 0.5 portion;

other additives: 10 to 30 portions.

Preferably, the grouting material prepared from the modified and support grouting material and the epoxy material in a specific ratio comprises the following components in parts by mass,

modified grouting material: 700 to 900 portions;

grouting material for the support: 600 to 700 portions;

epoxy resin material: 150 to 180 portions;

water: 220-250 parts of a solvent;

water reducing agent: 6-8 parts;

early strength agent: 14-20 parts of a solvent;

anti-segregation agent: 8-12 parts;

a micro-swelling agent: 0.2 to 0.4 portion;

other additives: 15 to 25 portions.

Preferably, the grouting material prepared from the modified and support grouting material and the epoxy material in a specific ratio comprises the following components in parts by mass,

modified grouting material: 867.3 parts of a binder;

grouting material for the support: 680 parts of;

epoxy resin material: 169.7 parts;

water: 230 parts of (A);

water reducing agent: 6.3 parts of a mixture;

early strength agent: 16 parts of a mixture;

anti-segregation agent: 9.6 parts;

a micro-swelling agent: 0.3 part;

other additives: 20.8 parts.

Preferably, the composite material further comprises 25 parts by weight of a thickening agent, and the thickening agent is one or more of hydroxymethyl cellulose, hydroxyethyl cellulose and hydroxypropyl methyl cellulose.

Preferably, the micro-swelling agent is a UEA swelling agent or a CSA swelling agent.

Compared with the prior art, the invention has the beneficial effects that: the grouting material prepared from the modified support grouting material and the epoxy material in a specific ratio has good construction performance, and is smooth and flat after being poured. Overcomes the defects of unevenness, easy cracking and powder rising and the like of the traditional mortar, and has good fluidity, micro expansion, no bleeding, no segregation and long open operation time. The construction lubricity is good.

In the description of the present invention, it is to be understood that the terms "coaxial", "bottom", "one end", "top", "middle", "other end", "upper", "one side", "top", "inner", "front", "center", "two ends", and the like, indicate orientations or positional relationships based on the illustrated orientations or positional relationships for convenience in describing the present invention and simplifying the description, but do not indicate or imply that the device or element being referred to must have a particular orientation, be constructed and operated in a particular orientation, and thus, should not be construed as limiting the present invention.

In the present invention, unless otherwise expressly specified or limited, the terms "mounted," "disposed," "connected," "secured," "screwed" and the like are to be construed broadly, e.g., as meaning fixedly connected, detachably connected, or integrally formed; can be mechanically or electrically connected; the terms may be directly connected or indirectly connected through an intermediate, and may be communication between two elements or interaction relationship between two elements, unless otherwise specifically limited, and the specific meaning of the terms in the present invention will be understood by those skilled in the art according to specific situations.

Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.