阅读说明：本技术 一种预铺自粘胶膜卷材复合防水片及其制备方法和应用 (Pre-laid self-adhesive film coiled material composite waterproof sheet and preparation method and application thereof ) 是由 胡全超 龚兴宇 于 2021-09-15 设计创作，主要内容包括：本发明涉及防水材料领域,具体涉及一种预铺自粘胶膜卷材复合防水片及其制备方法和应用,该复合防水片含有层叠设置的复合层和高密度聚乙烯层,形成所述复合层的材料为乙烯基极性共聚物,形成所述高密度聚乙烯层的材料为高密度聚乙烯。本发明提供的预铺自粘胶膜卷材复合防水片具有优异的耐老化性能、剥离强度和抗穿刺强度,同时,其制备方法简单、无污染,具有环保性。(The invention relates to the field of waterproof materials, in particular to a pre-laid self-adhesive film coiled material composite waterproof sheet, and a preparation method and application thereof. The pre-laid self-adhesive film coiled material composite waterproof sheet provided by the invention has excellent aging resistance, peeling strength and puncture resistance, and meanwhile, the preparation method is simple, pollution-free and environment-friendly.)

1. The pre-laid self-adhesive film coiled material composite waterproof sheet is characterized by comprising a composite layer and a high-density polyethylene layer which are arranged in a stacked mode, wherein the composite layer is made of vinyl polar copolymer, and the high-density polyethylene layer is made of high-density polyethylene;

the proportion relation between the thickness D1 of the composite layer and the thickness D2 of the high-density polyethylene layer is as follows: d1: d2 ═ 1: 1-20.

2. The composite waterproof sheet according to claim 1, wherein the high-density polyethylene has a weight average molecular weight of 10 to 30 ten thousand;

and/or the ratio of the thickness D1 of the composite layer to the thickness D2 of the high-density polyethylene layer is as follows: d1: d2 ═ 1: 2-10.

3. The composite waterproof sheet according to claim 1 or 2, wherein the vinyl polar copolymer is at least one of an ethylene-vinyl acetate copolymer, an ethylene-carbon monoxide copolymer, and an ethylene-vinyl acetate-carbon monoxide terpolymer.

4. The composite waterproof sheet according to claim 3, wherein the weight average molecular weight of the ethylene-vinyl acetate copolymer is 20 to 40 ten thousand, and the VA content is 18 to 26 mass%; and/or the presence of a gas in the gas,

the weight average molecular weight of the ethylene-carbon monoxide copolymer is 20-40 ten thousand; and/or the presence of a gas in the gas,

the weight average molecular weight of the ethylene-vinyl acetate-carbon monoxide terpolymer is 20-40 ten thousand.

5. A method for preparing a pre-laid self-adhesive film coiled material composite waterproof sheet is characterized by comprising the following steps: preparing a material for forming the composite layer and a material for forming the high-density polyethylene layer in a melt extrusion mode; the material for forming the composite layer is vinyl polar copolymer, and the material for forming the high-density polyethylene layer is high-density polyethylene;

controlling the conditions of melt extrusion so that the ratio between the thickness D1 of the composite layer and the thickness D2 of the high density polyethylene layer is: d1: d2 ═ 1: 1-20.

6. The method according to claim 5, wherein the method comprises preparing the pre-laid self-adhesive glue film coiled material composite waterproof sheet by adopting a one-step method;

the one-step method comprises the following steps: and carrying out in-mold melt co-extrusion on the material for forming the composite layer and the material for forming the high-density polyethylene layer by adopting a double extruder.

7. The method of claim 6, wherein the melt co-extrusion conditions are at least: the cylinder temperature is 190-240 ℃, the die head temperature is 190-240 ℃, the extrusion speed is 3-6m/min, and the calendering composite temperature is 50-70 ℃.

8. The method according to claim 5, wherein the method comprises preparing the pre-laid self-adhesive glue film coiled material composite waterproof sheet by adopting a two-step method; the two-step method comprises the following steps:

(I1) firstly, respectively applying a material for forming the composite layer and a material for forming the high-density polyethylene layer to prepare the high-density polyethylene layer and the composite layer in advance in a single extruder;

(I2) and compounding the high-density polyethylene layer and the composite layer through calendering and compounding.

9. The method according to claim 5, wherein the method comprises preparing the pre-laid self-adhesive glue film coiled material composite waterproof sheet by adopting a two-step method; the two-step method comprises the following steps:

(II1) extruding the high density polyethylene layer in a first extruder using the material forming the high density polyethylene layer and the composite layer in a second extruder using the material forming the composite layer using a twin extruder;

(II2) compounding the high density polyethylene layer with the composite layer by calendar compounding.

10. The method according to claim 8 or 9, wherein in each extruder, each of the extrusion conditions at least satisfy: the temperature of a cylinder is 190 ℃ and 240 ℃, the temperature of a die head is 190 ℃ and 240 ℃, and the extrusion speed is 3-6 m/min; and/or the presence of a gas in the gas,

each of the conditions of the calendering compounding at least satisfy: the calendering and compounding temperature is 50-70 ℃.

11. The pre-laid self-adhesive film roll composite waterproof sheet prepared by the method of any one of claims 5 to 10.

12. Use of the pre-laid self-adhesive film roll composite waterproofing sheet according to any one of claims 1 to 4 or 11 in waterproofing materials.

Technical Field

The invention relates to the field of waterproof materials, in particular to a pre-laid self-adhesive film coiled material composite waterproof sheet and a preparation method and application thereof.

Background

The high-density polyethylene is also called low-pressure polyethylene, is a thermoplastic resin with high crystallinity and a certain degree of translucency of a non-polar surface, has good heat resistance and cold resistance, good chemical stability, and has the excellent characteristics of higher rigidity, toughness, mechanical strength, dielectric property, environmental stress cracking resistance and the like.

The high-density polyethylene can be used for a non-asphalt-based high-molecular self-adhesive film main body layer, and provides the non-asphalt-based high-molecular self-adhesive film waterproof coiled material with the stretching, tearing and puncture resistance; it can also be used for high density polyethylene waterproof board and other high polymer waterproof products related to high density polyethylene.

At present, the construction convenience and reliability of waterproof materials are paid more and more attention, but some technical problems also exist: the high-density polyethylene waterproof sheet is mainly subjected to lap joint edge treatment by using a pressure-sensitive adhesive cold-bonding sheet, and is low in temperature and initial viscosity and not beneficial to construction; the deformation rate of the pressure-sensitive adhesive is different from that of the high-density polyethylene waterproof sheet under long-term cold and hot alternation, so that the long-term effectiveness of adhesion is not facilitated; the adhesive sheet is susceptible to aging, resulting in performance not being guaranteed.

For example, CN109130400A discloses a HDPE polymer self-adhesive film waterproof roll and a manufacturing process thereof, wherein the waterproof roll comprises a polymer sheet, a fabric and a separation film, and self-adhesive materials are filled between the polymer sheet and the fabric and between the fabric and the separation film. The prior art only considers the performance of the HDPE sheet layer, does not start from the whole, and still does not solve the problem of interface bonding between the HDPE sheet and the self-adhesive, and the problem of how to more reliably position the lap joint edge and the like.

Therefore, in order to solve the above-mentioned problems of the conventional art, it is necessary to develop a high density polyethylene waterproof sheet having better performance.

Disclosure of Invention

The invention aims to overcome the defects of poor aging resistance, low peel strength and low puncture strength of the existing high-density polyethylene waterproof material.

The inventor of the invention finds in research that the vinyl polar copolymer can provide better welding performance with a high-density polyethylene layer on one hand, and on the other hand, due to the existence of the polar functional group, the vinyl polar copolymer has better surface polarity, so that the adhesive can be favorably paved and infiltrated on the surface of the vinyl polar copolymer, and the bonding effect between the vinyl polar copolymer and the adhesive is greatly improved. Therefore, when the vinyl polar copolymer is adopted to form the composite layer, the high-density polyethylene layer is adopted to form the high-density polyethylene layer, and then the vinyl polar copolymer and the high-density polyethylene layer are stacked in a certain thickness proportion, the obtained pre-paved self-adhesive film coiled material composite waterproof sheet still has excellent ageing resistance, higher peel strength and puncture strength on the premise of simpler structure and material.

In order to achieve the above object, the first aspect of the present invention provides a pre-laid self-adhesive film coiled material composite waterproof sheet, which comprises a composite layer and a high density polyethylene layer, wherein the composite layer is formed by a vinyl polar copolymer, and the high density polyethylene layer is formed by a high density polyethylene;

the proportion relation between the thickness D1 of the composite layer and the thickness D2 of the high-density polyethylene layer is as follows: d1: d2 ═ 1: 1-20.

The invention provides a method for preparing a pre-laid self-adhesive film coiled material composite waterproof sheet, which comprises the following steps: preparing a material for forming the composite layer and a material for forming the high-density polyethylene layer in a melt extrusion mode; the material for forming the composite layer is vinyl polar copolymer, and the material for forming the high-density polyethylene layer is high-density polyethylene;

controlling the conditions of melt extrusion so that the ratio between the thickness D1 of the composite layer and the thickness D2 of the high density polyethylene layer is: d1: d2 ═ 1: 1-20.

The third aspect of the invention provides the pre-paved self-adhesive film coiled material composite waterproof sheet prepared by the method of the second aspect.

The fourth aspect of the present invention provides the use of the pre-laid self-adhesive film roll composite waterproof sheet according to the first or third aspect in a waterproof material.

Compared with the existing waterproof material technology, the pre-paved self-adhesive film coiled material composite waterproof sheet provided by the invention has at least the following advantages:

(1) the pre-laid self-adhesive film coiled material composite waterproof sheet provided by the invention has excellent aging resistance;

(2) the overlapping edge of the pre-paved self-adhesive film coiled material composite waterproof sheet provided by the invention can be welded for construction, and the peeling strength of the overlapping edge can not be reduced after the overlapping edge is used for a long time, so that the phenomenon of water channeling is avoided;

(3) the pre-laid self-adhesive film coiled material composite waterproof sheet provided by the invention has excellent puncture resistance and can provide better technical indexes;

(4) the preparation method of the pre-laid self-adhesive film coiled material composite waterproof sheet provided by the invention is simple, pollution-free and environment-friendly.

Additional features and advantages of the invention will be set forth in the detailed description which follows.

Detailed Description

The endpoints of the ranges and any values disclosed herein are not limited to the precise range or value, and such ranges or values should be understood to encompass values close to those ranges or values. For ranges of values, between the endpoints of each of the ranges and the individual points, and between the individual points may be combined with each other to give one or more new ranges of values, and these ranges of values should be considered as specifically disclosed herein.

It should be noted that, in various aspects of the present invention, the present invention is described only once in one aspect thereof without repeated description with respect to the same components in the aspects, and those skilled in the art should not be construed as limiting the present invention.

In the case where no explanation is given to the contrary, the room temperature in the present invention is 25. + -. 2 ℃.

As described above, the first aspect of the present invention provides a pre-laid self-adhesive film roll composite waterproof sheet, which comprises a composite layer and a high-density polyethylene layer, wherein the composite layer and the high-density polyethylene layer are stacked, the material forming the composite layer is a vinyl polar copolymer, and the material forming the high-density polyethylene layer is high-density polyethylene;

the proportion relation between the thickness D1 of the composite layer and the thickness D2 of the high-density polyethylene layer is as follows: d1: d2 ═ 1: 1-20.

Preferably, the high density polyethylene has a weight average molecular weight of 10 to 30 ten thousand.

Preferably, the ratio between the thickness D1 of the composite layer and the thickness D2 of the high density polyethylene layer is: d1: d2 ═ 1: 2-10. The inventor finds that under the preferred embodiment, the invention can obtain the pre-paved self-adhesive film coiled material composite waterproof sheet with higher aging resistance, peeling strength and puncture strength.

In the present invention, it is preferable that the width of the composite layer is 8 to 400cm, and when the width of the composite layer is 8cm, the composite layer is mainly used for welding together with the high density polyethylene layer, so that a more effective overlapping effect can be provided.

Preferably, the vinyl polar copolymer is at least one of ethylene-vinyl acetate copolymer, ethylene-carbon monoxide copolymer and ethylene-vinyl acetate-carbon monoxide terpolymer.

Preferably, the weight average molecular weight of the ethylene-vinyl acetate copolymer is 20 to 40 ten thousand, and the VA content is 18 to 26 mass%.

In the present invention, the VA content is the vinyl acetate content.

Preferably, the weight average molecular weight of the ethylene-carbon monoxide copolymer is 20 to 40 ten thousand.

Preferably, the ethylene-vinyl acetate-carbon monoxide terpolymer has a weight average molecular weight of 20 to 40 ten thousand.

In the invention, under the preferable embodiment, ethylene can endow the copolymer with certain strength, so that the copolymer has excellent physical properties, vinyl acetate can enable the copolymer to have soft characteristics, carbonyl formed by carbon monoxide can further improve the molecular polarity of the copolymer, and the compatibility with the adhesive resin is increased.

In order to obtain a pre-laid self-adhesive film roll composite waterproof sheet having higher aging resistance, peel strength and puncture strength, as described above, the second aspect of the present invention provides a method for preparing a pre-laid self-adhesive film roll composite waterproof sheet, the method comprising: preparing a material for forming the composite layer and a material for forming the high-density polyethylene layer in a melt extrusion mode; the material for forming the composite layer is vinyl polar copolymer, and the material for forming the high-density polyethylene layer is high-density polyethylene;

controlling the conditions of melt extrusion so that the ratio between the thickness D1 of the composite layer and the thickness D2 of the high density polyethylene layer is: d1: d2 ═ 1: 1-20, more preferably D1: d2 ═ 1: 2-10.

According to a preferred embodiment, the method comprises the steps of preparing the pre-paved self-adhesive film coiled material composite waterproof sheet by adopting a one-step method; the one-step method comprises the following steps: and carrying out in-mold melt co-extrusion on the material for forming the composite layer and the material for forming the high-density polyethylene layer by adopting a double extruder.

Preferably, the melt co-extrusion conditions at least satisfy: the cylinder temperature is 190-240 ℃, the die head temperature is 190-240 ℃, the extrusion speed is 3-6m/min, and the calendering composite temperature is 50-70 ℃. Under the preferred embodiment, the inventor finds that the pre-paved self-adhesive film coiled material composite waterproof sheet with higher aging resistance, peeling strength and puncture resistance can be obtained.

According to another preferred embodiment, the method comprises the steps of preparing the pre-paved self-adhesive film coiled material composite waterproof sheet by adopting a two-step method; the two-step method comprises the following steps:

(I1) firstly, respectively applying a material for forming the composite layer and a material for forming the high-density polyethylene layer to prepare the high-density polyethylene layer and the composite layer in advance in a single extruder;

(I2) and compounding the high-density polyethylene layer and the composite layer through calendering and compounding.

According to another preferred embodiment, the method comprises the steps of preparing the pre-paved self-adhesive film coiled material composite waterproof sheet by adopting a two-step method; the two-step method comprises the following steps:

(II1) extruding the high density polyethylene layer in a first extruder using the material forming the high density polyethylene layer and the composite layer in a second extruder using the material forming the composite layer using a twin extruder;

(II2) compounding the high density polyethylene layer with the composite layer by calendar compounding.

The following is a description of preferred conditions in the extruder in the aforementioned one-step and two-step processes.

Preferably, in each extruder, each of the extrusion conditions at least satisfies: the cylinder temperature is 190-240 ℃, the die head temperature is 190-240 ℃, and the extrusion speed is 3-6 m/min.

Preferably, each of the conditions of the calendering compounding at least satisfies: the calendering and compounding temperature is 50-70 ℃.

In the present invention, the operation of the extrusion may be performed in a single extruder or a twin extruder.

According to a particularly preferred embodiment, the method for preparing the pre-laid self-adhesive film roll composite waterproof sheet comprises the following steps:

respectively placing the material for forming the composite layer and the material for forming the high-density polyethylene layer into two extruders, enabling the two extruders to correspond to the same extrusion die head, and carrying out in-die melt co-extrusion in the same extrusion die head, wherein the barrel temperature is 190-240 ℃, the die head temperature is 190-240 ℃, the extrusion speed is 3-6m/min, and the calendering and compounding temperature is 50-70 ℃. The inventors have found that in this preferred embodiment, the upper and lower layers are both subjected to rolling compounding in a molten state, and that the compounding effect is further improved and the interlayer peel strength is further improved.

As mentioned above, the third aspect of the present invention provides the pre-laid self-adhesive glue film roll composite waterproof sheet prepared by the method of the second aspect.

As mentioned above, the fourth aspect of the present invention provides the use of the pre-laid self-adhesive film roll composite waterproof sheet according to the first or third aspect in a waterproof material.

The present invention will be described in detail below by way of examples.

In the following examples, unless otherwise specified, the laboratory instruments and raw materials are commercially available.

Laboratory apparatus

A single extruder: parallel twin screws, amstert, italy;

double extruder: single screw, suzhou jinyu corporation;

a tensile testing machine: c43, meits corporation.

Raw materials

Vinyl polar copolymer: ethylene-vinyl acetate-carbon monoxide terpolymer Elvaloy441 having a melt index of 8g/10min and a density of 0.98g/cm³Dow chemical company, USA;

vinyl polar copolymer: ethylene-vinyl acetate-carbon monoxide terpolymer Elvaloy741, melt index 35g/10min, density 1.0g/cm³Dow chemical company, USA;

vinyl polar copolymer: ethylene-vinyl acetate copolymer, EVA, melt index 2.5g/10min, density 0.938g/cm³Taiwan chemical fiber company, weight average molecular weight 20 ten thousand, VA content 18 mass%;

high density polyethylene I: melt index 0.18g/10min, density 0.946g/cm³Weight average molecular weight 25 ten thousand, TR-144, Saudi Chevrolet Phillips;

high density polyethylene II: melt index 0.2g/10min, density 0.946g/cm³Weight average molecular weight 25 ten thousand, TR-144, Guangzhou petrochemical company, China petrochemical;

polyethylene terephthalate film: PET-4C, great southeast Hippocampus Kogyo, Hangzhou;

SIS pressure sensitive adhesive: CKS-101, science and technology Water-proofing, Inc.;

asphalt-based pressure-sensitive adhesive: CKS-405, Koshu Water science and technology, Inc.

Example 1

The one-step method is adopted to prepare the pre-paved self-adhesive film coiled material composite waterproof sheet S1, and the method comprises the following steps:

respectively placing a vinyl polar copolymer Elvaloy441 and high-density polyethylene I into two extruders, enabling the two extruders to correspond to a same extrusion die head, and carrying out in-die melt co-extrusion in the same extrusion die head, wherein the cylinder temperature is 200 ℃, the die head temperature is 200 ℃, the calendering and compounding temperature is 60 ℃, and the speed ratio of the two rollers is 1: 1.05, the extrusion speed is 4 m/min; and in the process of extruding to rolling by a die head, inserting a polyethylene terephthalate film with the thickness of 0.04mm between a composite layer with the thickness of 0.5mm and a high-density polyethylene layer with the thickness of 1mm, cooling and shaping to obtain the pre-paved self-adhesive film coiled material composite waterproof sheet S1.

Example 2

The pre-paved self-adhesive film coiled material composite waterproof sheet S2 is prepared by adopting a two-step method and a single extruder, and the method comprises the following steps:

(I1) firstly, respectively using a vinyl polar copolymer Elvaloy441 and high-density polyethylene I to prepare a high-density polyethylene layer I with the thickness of 1mm and a composite layer I with the thickness of 0.5mm in advance in a single extruder, wherein the cylinder temperature is 200 ℃, the die head temperature is 200 ℃, and the extrusion speed is 4 m/min;

(I2) compounding the high-density polyethylene layer I and the composite layer I through calendering and compounding, wherein the calendering and compounding temperature is 60 ℃, and the speed ratio of two rollers is 1: 1.05; and in the calendering process, a polyethylene terephthalate film with the thickness of 0.04mm is inserted between the composite layer I and the high-density polyethylene layer I, and the composite waterproof sheet S2 of the pre-paved self-adhesive film coiled material is obtained after cooling and shaping.

Example 3

The pre-paved self-adhesive film coiled material composite waterproof sheet S3 is prepared by adopting a two-step method and a double extruder, and the method comprises the following steps:

(II1) extruding a high-density polyethylene layer II with the thickness of 1mm by using high-density polyethylene I in a first extruder and extruding a composite layer II with the thickness of 0.5mm by using a vinyl polar copolymer Elvaloy441 in a second extruder by using a double extruder, wherein the cylinder temperature is 200 ℃, the die head temperature is 200 ℃, and the extrusion speed is 4 m/min;

(II2) compounding the high-density polyethylene layer II and the composite layer II by calendering and compounding, wherein the calendering and compounding temperature is 60 ℃, and the speed ratio of two rollers is 1: 1.05; and in the calendering process, a polyethylene terephthalate film with the thickness of 0.04mm is inserted between the composite layer II and the high-density polyethylene layer II, and the composite waterproof sheet S3 of the pre-paved self-adhesive film coiled material is obtained after cooling and shaping.

Comparative example 1

This comparative example prepared a pre-applied self-adhesive film roll composite waterproof sheet DS1 using a procedure similar to that of example 1, except that: the thickness of the composite layer is 0.5mm, and the thickness of the high-density polyethylene layer is 0.25 mm.

Comparative example 2

This comparative example prepared a pre-applied self-adhesive film roll composite waterproof sheet DS2 using a procedure similar to that of example 1, except that: the thickness of the composite layer is 0.1mm, and the thickness of the high-density polyethylene layer is 3 mm.

Test example 1

The pre-paved self-adhesive film coiled material composite waterproof sheet S1-S3 and DS1-DS2 are respectively cut into sample blocks of 50mm multiplied by 200mm, the test is carried out according to GB/T328.21, the detection speed is 100mm/min, and the test results are shown in Table 1.

TABLE 1

As can be seen from Table 1, in S1-S3, the interlayer peeling force of the pre-paved self-adhesive film coiled material composite waterproof sheet S1 obtained by the processing mode of one-step in-mold melt co-extrusion is the highest; the interlayer peel force was lower for DS1-DS 2.

Example 4

The one-step method is adopted to prepare the pre-paved self-adhesive film coiled material composite waterproof sheet S4, and the method comprises the following steps:

respectively placing vinyl polar copolymer EVA and high-density polyethylene II into two extruders, enabling the two extruders to correspond to a same extrusion die head, carrying out in-die melt co-extrusion in the same extrusion die head, wherein the temperature of a machine barrel is 200 ℃, the temperature of the die head is 200 ℃, the calendering and compounding temperature is 60 ℃, and the speed ratio of two rollers is 1: 1.05, extrusion speed is 4.5m/min, obtains thickness to be 0.3mm the composite bed is 1mm with thickness high density polyethylene layer, then will the composite bed with high density polyethylene layer adopts hand-held type hot air welding machine to weld, places 24h at room temperature, obtains pre-paved self-adhesive film coiled material composite waterproof sheet S4.

Comparative example 3

This comparative example prepared a pre-applied self-adhesive film roll composite waterproof sheet DS3 using a procedure similar to that of example 4, except that: and carrying out adhesive lap joint on the composite layer and the high-density polyethylene layer by adopting SIS pressure-sensitive adhesive.

Comparative example 4

This comparative example prepared a pre-applied self-adhesive film roll composite waterproof sheet DS4 using a procedure similar to that of example 4, except that: and (3) carrying out adhesive lap joint on the composite layer and the high-density polyethylene layer by adopting asphalt-based pressure-sensitive adhesive.

Test example 2

Respectively cutting the pre-laid self-adhesive film coiled material composite waterproof sheet S4 and DS3-DS4 into sample blocks of 50mm multiplied by 200mm, and carrying out a non-treatment welding peel strength test according to GB/T328.21 at a detection speed of 100 mm/min; placing the sample in a 70 ℃ air-blast drying oven for 28 days, and then carrying out long-term thermal aging welding peel strength test according to GB/T328.21, wherein the detection speed is 100 mm/min; the test results are shown in Table 2.

TABLE 2

Examples of the invention	Example 4	Comparative example 3	Comparative example 4
				Thickness/mm of composite layer	0.3	0.3	0.3
High density polyethylene layer thickness/mm	1.0	1.0	1.0
				No treatment peel Strength/(N/mm)	6.2	1.8	2.0
Peeling strength by heat treatment/(N/mm)	5.8	0.8	0.5
				Heat treatment of failure form	Coil break	Interfacial destruction	Interfacial destruction

As can be seen from Table 2, S4 was lapped by welding, and the non-treatment peel strength was significantly higher than that of DS3-DS4 obtained by adhesive lapping, while the heat-aged peel strength was hardly attenuated, and the heat-aged peel strength of DS3-DS4 was greatly reduced from that of non-treatment peel strength.

Example 5

The one-step method is adopted to prepare the pre-paved self-adhesive film coiled material composite waterproof sheet S5, and the method comprises the following steps:

respectively placing a vinyl polar copolymer Elvaloy741 and high-density polyethylene I into two extruders, enabling the two extruders to correspond to a same extrusion die head, and carrying out in-die melt co-extrusion in the same extrusion die head, wherein the cylinder temperature is 200 ℃, the die head temperature is 200 ℃, the calendering composite temperature is 60 ℃, and the speed ratio of the two rollers is 1: 1.05, extrusion speed is 5m/min, obtain thickness be 0.1mm the composite bed with thickness be 1mm high density polyethylene layer, and will the composite bed with high density polyethylene layer carries out calendering complex, obtains pre-paved self-adhesive film coiled material composite waterproof sheet S5.

Example 6

This example uses a procedure similar to that of example 5 to prepare a pre-laid self-adhesive film roll composite waterproof sheet S6, except that: the thickness of the composite layer is 0.3 mm.

Example 7

This example uses a procedure similar to that of example 5 to prepare a pre-laid self-adhesive film roll composite waterproof sheet S7, except that: the thickness of the composite layer is 0.5 mm.

Example 8

This example uses a procedure similar to that of example 5 to prepare a pre-laid self-adhesive film roll composite waterproof sheet S8, except that: the thickness of the composite layer is 0.7 mm.

Example 9

This example uses a procedure similar to that of example 5 to prepare a pre-laid self-adhesive film roll composite waterproof sheet S9, except that: the thickness of the composite layer is 1 mm.

Comparative example 5

This comparative example prepared a pre-applied self-adhesive film roll composite waterproof sheet DS5 using a procedure similar to that of example 5, except that: without the composite layer.

Test example 3

Respectively coating SIS pressure-sensitive adhesive on the surfaces of pre-paved self-adhesive film coiled material composite waterproof sheets S5-S9 and DS5 at 140 ℃, wherein the coating weight is 350g/m²And covering the surface of the pressure-sensitive adhesive with the isolation sand to respectively obtain the non-asphalt-based macromolecular self-adhesive film waterproof coiled material A1-A6.

Respectively carrying out puncture resistance strength tests on the non-asphalt-based polymer self-adhesive film waterproof coiled material A1-A6 according to appendix B and ASTM E154 of CJ/T234-2006; performing a tear strength test according to GB/T328.18; the test results are shown in Table 3.

TABLE 3

Examples of the invention	Example 5	Example 6	Example 7	Example 8	Example 9	Comparative example 5
							Thickness/mm of composite layer	0.1	0.3	0.5	0.7	1.0	0
High density polyethylene layer thickness/mm	1.0	1.0	1.0	1.0	1.0	1.0
							CJ puncture resistance strength/N	378	402	435	442	450	356
ASTM puncture resistance strength/N	1120	1184	1275	1302	1356	1052
							Tear Strength/N	482	559	598	612	630	428

As can be seen from Table 3, the puncture strength and the tear strength of the composite layer increase the fastest when the thickness of the composite layer is 0.1 to 0.5mm, and the puncture strength and the tear strength of the composite layer increase less after the thickness of the composite layer exceeds 0.5 mm.

From the results, the pre-laid self-adhesive film coiled material composite waterproof sheet provided by the invention has excellent aging resistance, peeling strength and puncture strength, and meanwhile, the preparation method is simple, pollution-free and environment-friendly.

The preferred embodiments of the present invention have been described above in detail, but the present invention is not limited thereto. Within the scope of the technical idea of the invention, many simple modifications can be made to the technical solution of the invention, including combinations of various technical features in any other suitable way, and these simple modifications and combinations should also be regarded as the disclosure of the invention, and all fall within the scope of the invention.