阅读说明：本技术 一种基于调控导电丝生长的选择器性能优化方法及应用 (Selector performance optimization method based on regulation and control of conductive wire growth and application ) 是由 杨蕊 张泽琛 缪向水 王昊伟 于 2021-08-20 设计创作，主要内容包括：本发明公开了一种基于调控导电丝生长的选择器性能优化方法及应用,包括：在选择器的阻变层和顶电极之间引入中间电极层；其中,顶电极中的活性电极材料为Ag或Cu；阻变层材料为薄层氧化物或经过氧处理的薄层二维材料；中间电极层材料为钛、钽、铝等活性电极材料；中间电极层与阻变层接触时,中间电极层中的活性电极材料会夺取阻变层中的氧发生氧化作用从而转变为非晶氧化层,以限制来源于顶电极中的活性阳离子迁移,从而限制导电丝的生长；且中间电极层为厚度不均的薄膜,与顶电极的接触面不平整,使得顶电极与阻变层之间形成点接触,导电丝生长倾向于在点接触处发生,进一步限制了导电丝生长的随机性；本发明工艺简单,大大改善了选择器的性能。(The invention discloses a selector performance optimization method based on regulation and control of conductive wire growth and application, comprising the following steps: introducing an intermediate electrode layer between the resistive layer and the top electrode of the selector; wherein the active electrode material in the top electrode is Ag or Cu; the resistance change layer material is a thin layer oxide or a thin layer two-dimensional material subjected to oxygen treatment; the middle electrode layer is made of active electrode materials such as titanium, tantalum, aluminum and the like; when the middle electrode layer is in contact with the resistance change layer, the active electrode material in the middle electrode layer can deprive oxygen in the resistance change layer to generate oxidation action so as to convert the oxygen into an amorphous oxide layer, so that the migration of active cations from the top electrode is limited, and the growth of the conductive wire is limited; the middle electrode layer is a thin film with uneven thickness, and the contact surface of the middle electrode layer and the top electrode is uneven, so that point contact is formed between the top electrode and the resistance change layer, the growth of the conductive wire tends to occur at the point contact position, and the growth randomness of the conductive wire is further limited; the invention has simple process and greatly improves the performance of the selector.)

1. A selector performance optimization method based on regulation and control of conductive wire growth is characterized by comprising the following steps:

introducing an intermediate electrode layer between the resistive layer and the top electrode of the selector; wherein the active electrode material in the top electrode is Ag or Cu; the resistance-change layer is an oxygen-containing resistance-change layer, and is made of a thin oxide layer or a thin two-dimensional material subjected to oxygen treatment; the middle electrode layer is made of active electrode materials, including titanium, tantalum or aluminum;

when the intermediate electrode layer is in contact with the resistance change layer, active electrode materials in the intermediate electrode layer and oxygen in the resistance change layer are oxidized, so that the intermediate electrode layer is converted into an amorphous oxide layer to limit migration of active cations from the top electrode, and growth of a conductive wire is limited; and at the moment, the middle electrode layer is a thin film with uneven thickness, and the contact surface of the middle electrode layer and the top electrode is uneven, so that point contact is formed between the top electrode and the resistance change layer, and the growth randomness of the conductive wire is further limited.

2. The selector performance optimization method of claim 1, wherein a maximum thickness of the intermediate electrode layer does not exceed 10 nm.

3. A selector performance optimization method according to claim 1 or 2, characterized in that the intermediate electrode layer is grown by electron beam evaporation.

4. A selector based on the growth of a conductive wire is characterized by comprising a substrate, a bottom electrode, a resistance change layer, a middle electrode layer and a top electrode which are arranged from bottom to top; the top electrode comprises an active electrode layer and an inert protective electrode which are arranged from bottom to top; wherein the active electrode material in the top electrode is Ag or Cu; the resistance-change layer is an oxygen-containing resistance-change layer, and is made of a thin oxide layer or a thin two-dimensional material subjected to oxygen treatment; the middle electrode layer is made of active electrode materials, including titanium, tantalum or aluminum;

when the intermediate electrode layer is in contact with the resistance change layer, active electrode materials in the intermediate electrode layer and oxygen in the resistance change layer are oxidized, so that the intermediate electrode layer is converted into an amorphous oxide layer to limit migration of active cations from the top electrode, and growth of a conductive wire is limited; and at the moment, the middle electrode layer is a thin film with uneven thickness, and the contact surface of the middle electrode layer and the top electrode is uneven, so that point contact is formed between the top electrode and the resistance change layer, and the growth randomness of the conductive wire is further limited.

5. A selector as claimed in claim 4 wherein the maximum thickness of the intermediate electrode layer is no more than 10 nm.

6. The selector of claim 4 or 5, wherein the thickness of the resistive layer is 3-15 nm.

7. The selector of claim 4 or 5, wherein the bottom electrode is a multilayer electrode formed by one or two of gold, titanium, platinum and chromium.

8. A method of manufacturing a selector as claimed in any one of claims 4 to 7, comprising:

s1, depositing a metal film on the substrate to obtain a bottom electrode;

s2, preparing a resistance change layer on the bottom electrode; the resistance-change layer is an oxygen-containing resistance-change layer, and is made of a thin oxide layer or a thin two-dimensional material subjected to oxygen treatment;

s3, depositing an active electrode on the resistance change layer; the active electrode deposited on the resistance change layer comprises titanium, tantalum or aluminum; at the moment, the active electrode on the resistance-change layer and oxygen in the resistance-change layer are oxidized to be converted into an amorphous oxide layer, and a thin film with uneven thickness, namely an intermediate electrode layer, is obtained;

s4, sequentially depositing an active electrode layer and an inert protective electrode on the middle electrode layer to obtain a top electrode; wherein the contact surface of the top electrode and the middle electrode layer is uneven; the active electrode layer in the top electrode is made of Ag or Cu.

9. The method of manufacturing a selector as claimed in claim 8, wherein the maximum thickness of the intermediate electrode layer is not more than 10 nm.

Technical Field

The invention belongs to the field of microelectronic devices, and particularly relates to a selector performance optimization method based on regulation and control of conductive wire growth and application.

Background

The memristor has great potential in the aspects of nonvolatile storage, logic operation, brain-like calculation and the like due to the advantages of high speed, low power consumption, simple structure, easy integration, compatibility with the cmos process and the like. However, when a target cell is subjected to a write and erase operation in a memristor crossbar array structure, a leakage current may exist in adjacent cells, so that the write and erase operations can be mistakenly performed. To avoid the effects of leakage currents in the array, a 1S1R structure is often constructed by connecting a selector in series with the memristor on each cross cell to improve the accuracy of the array operation.

To ensure proper read and write operations of the target cells of the array, the selector is generally required to have good threshold transition characteristics, such as a large ON-OFF ratio, a high ON-state current, a low OFF-state current, good stability between cycles and devices, and the like. Most of selectors which are most concerned at present work based on the formation and spontaneous fusing of metal conductive wires (usually Ag wires or Cu wires), but because the on-OFF of the conductive wires has great randomness and the excess injection of Ag or Cu in the resistive layer is easily caused along with the increase of the number of cycles, the performance is poor in the aspects of cycling stability, on-OFF ratio, OFF-state current and the like, and therefore, developing a method for regulating the on-OFF of the conductive wires to improve the randomness becomes a hotspot of current research work.

The existing selector performance optimization method based on the regulation and control of the growth of the conductive wire comprises the steps of inserting graphene with a nanopore defect into an electrode/resistance change layer interface or replacing an active electrode Ag with an Ag nanodot, and although the local growth of the conductive wire is controlled to a certain extent, the stability of the selector is improved, the requirement on process treatment parameters is still more complicated, so that the search for a simpler, more convenient and feasible selector optimization method still has certain research significance.

Disclosure of Invention

Aiming at the defects or improvement requirements of the prior art, the invention provides a selector performance optimization method based on the growth regulation of the conductive wire and application thereof, and aims to solve the technical problem that the prior art cannot reduce the randomness of the connection and disconnection of the conductive wire in the selector by a simple process so as to improve the performance of the selector.

In order to achieve the above object, in a first aspect, the present invention provides a method for optimizing the performance of a selector based on the regulation of the growth of a conductive wire, including:

introducing an intermediate electrode layer between the resistive layer and the top electrode of the selector; wherein the active electrode material in the top electrode is Ag or Cu; the resistance-change layer is an oxygen-containing resistance-change layer, and is made of a thin oxide layer or a thin two-dimensional material subjected to oxygen treatment; the material of the middle electrode layer is an active electrode material and comprises titanium, tantalum or aluminum;

when the middle electrode layer is contacted with the resistance change layer, the active electrode material in the middle electrode layer and oxygen in the resistance change layer are oxidized, so that the middle electrode layer is converted into an amorphous oxide layer to limit the migration of active cations from the top electrode, and the growth of the conductive wire is limited; and at the moment, the middle electrode layer is a thin film with uneven thickness, and the contact surface of the middle electrode layer and the top electrode is uneven, so that point contact is formed between the top electrode and the resistance change layer, and the growth randomness of the conductive wire is further limited.

Further preferably, the maximum thickness of the intermediate electrode layer does not exceed 10 nm.

Further preferably, the intermediate electrode layer is grown by electron beam evaporation.

In a second aspect, the invention provides a selector based on the growth of a conductive wire, which comprises a substrate, a bottom electrode, a resistance change layer, an intermediate electrode layer and a top electrode, wherein the substrate, the bottom electrode, the resistance change layer, the intermediate electrode layer and the top electrode are arranged from bottom to top; the top electrode comprises an active electrode layer and an inert protective electrode which are arranged from bottom to top; wherein the active electrode material in the top electrode is Ag or Cu; the resistance-change layer is an oxygen-containing resistance-change layer, and is made of a thin oxide layer or a thin two-dimensional material subjected to oxygen treatment; the material of the middle electrode layer is an active electrode material and comprises titanium, tantalum or aluminum;

when the middle electrode layer is contacted with the resistance change layer, the active electrode material in the middle electrode layer and oxygen in the resistance change layer are oxidized, so that the middle electrode layer is converted into an amorphous oxide layer to limit the migration of active cations from the top electrode, and the growth of the conductive wire is limited; and at the moment, the middle electrode layer is a thin film with uneven thickness, and the contact surface of the middle electrode layer and the top electrode is uneven, so that point contact is formed between the top electrode and the resistance change layer, and the growth randomness of the conductive wire is further limited.

Further preferably, the maximum thickness of the intermediate electrode layer does not exceed 10 nm.

Further preferably, the thickness of the resistance change layer is 3 to 15 nm.

Further preferably, the bottom electrode is a multilayer electrode formed by stacking one or two metals selected from gold, titanium, platinum and chromium.

In a third aspect, the present invention provides a method for preparing a selector based on conductive wire growth according to the second aspect, comprising:

s1, depositing a metal film on the substrate to obtain a bottom electrode;

s2, preparing a resistance change layer on the bottom electrode; the resistance-change layer is an oxygen-containing resistance-change layer, and is made of a thin oxide layer or a thin two-dimensional material subjected to oxygen treatment;

s3, depositing an active electrode on the resistance change layer; the active electrode deposited on the resistance change layer comprises titanium, tantalum or aluminum; at the moment, the active electrode on the resistance-change layer and oxygen in the resistance-change layer are oxidized and converted into an amorphous oxide layer, and a thin film with uneven thickness, namely an intermediate electrode layer, is obtained;

s4, sequentially depositing an active electrode layer and an inert protective electrode on the middle electrode layer to obtain a top electrode; wherein, the contact surface of the top electrode and the middle electrode layer is uneven; the material of the active electrode layer in the top electrode is Ag or Cu.

Further preferably, the maximum thickness of the intermediate electrode layer does not exceed 10 nm.

Generally, by the above technical solution conceived by the present invention, the following beneficial effects can be obtained:

1. the invention provides a selector performance optimization method based on regulation and control of conductive wire growth, wherein an intermediate electrode layer is introduced between a resistance change layer and a top electrode of a selector, wherein the resistance change layer is made of oxygen-containing thin-layer materials, the introduced intermediate electrode layer is made of titanium, tantalum, aluminum and other easily-oxidized active electrode materials, so that when an active electrode in the intermediate electrode layer is in contact with the oxygen-containing resistance change layer, oxygen atoms can migrate to the intermediate electrode layer to be oxidized into a continuous amorphous oxide layer, and the condition that external bias comes from external bias is limitedActive cation (Ag) obtained by oxidation of top electrode⁺Or Cu²⁺) Thereby limiting the growth of the conductive filaments; and at the moment, the middle electrode layer is a thin film with nonuniform thickness, so that an uneven and uneven interface is generated between the middle electrode layer and the top electrode, point contact of the top electrode and the resistance-change layer is easily formed at the position where the top electrode is close to the resistance-change layer, a strong local electric field is generated at the point contact position under the condition of external bias, the conducting wire is easily switched on and off between the point contact position and the bottom electrode at the corresponding position, and the non-point contact position is not easily switched on and off due to weak electric field and blockage of an amorphous oxide layer, so that the on-off of the conducting wire in certain fixed areas is controlled, and the growth randomness of the conducting wire is further limited. The invention has simple preparation process, reduces the on-OFF randomness of the conductive wire, solves the problems of poor circulation stability, unstable OFF-state current, non-centralized SET and RESET voltage distribution and the like of the traditional selector, and greatly improves the performance of the selector.

2. In the selector performance optimization method based on the regulation and control of the growth of the conductive wire, the intermediate electrode layer can be directly stacked on the resistance change layer together with the active electrode and the inert protective electrode in the top electrode through electron beam evaporation, and the preparation process is simple and rapid.

3. In the selector performance optimization method based on the regulation and control of the growth of the conductive wire, the ultrathin middle electrode layer can be made of one metal of titanium, tantalum, aluminum and the like, and the resistance change layer can be made of thin-layer oxide or oxygen-containing thin films of thin-layer two-dimensional materials and the like subjected to oxygen treatment.

Drawings

FIG. 1 is a schematic diagram of a selector based on conductive filament growth according to a second aspect of the present invention;

FIG. 2 is a schematic structural diagram of a selector based on conductive filament growth according to embodiment 1 of the present invention;

FIG. 3 is a DC cycle I-V characteristic curve for example 1 and comparative example 1 provided by the present invention; wherein (a) is the DC cycle I-V characteristic of example 1 and (b) is the DC cycle I-V characteristic of comparative example 1;

FIG. 4 is a graph of threshold transition I-V characteristics of example 1 provided by the present invention at different limiting currents;

FIG. 5 is a DC cycle I-V characteristic curve for example 2 and comparative example 2 provided by the present invention; wherein (a) is the DC cycle I-V characteristic of example 2, and (b) is the DC cycle I-V characteristic of comparative example 2.

Detailed Description

In order to make the objects, technical solutions and advantages of the present invention more apparent, the present invention is described in further detail below with reference to the accompanying drawings and embodiments. It should be understood that the specific embodiments described herein are merely illustrative of the invention and are not intended to limit the invention. In addition, the technical features involved in the embodiments of the present invention described below may be combined with each other as long as they do not conflict with each other.

In a first aspect, the invention provides a selector performance optimization method based on the regulation and control of the growth of a conductive wire, which comprises the following steps:

introducing an intermediate electrode layer between the resistive layer and the top electrode of the selector; wherein the active electrode material in the top electrode is Ag or Cu; the resistance-change layer is an oxygen-containing resistance-change layer, and is made of a thin oxide layer or a thin two-dimensional material subjected to oxygen treatment; the middle electrode layer is made of active electrode materials, including titanium, tantalum, aluminum and other active electrode materials which are easy to oxidize;

on one hand, the intermediate electrode layer is extremely thin (the maximum thickness is not more than 10nm) and is an active electrode easy to oxidize, and when the intermediate electrode layer is in contact with the oxygen-containing resistance change layer, oxygen atoms in the oxygen-containing resistance change layer can migrate into the intermediate electrode layer to be oxidized into an ultrathin amorphous oxide layer so as to limit the migration of active cations obtained by oxidation of the top electrode, thereby limiting the growth of the conductive wire.

On the other hand, at the moment, the middle electrode layer is a thin film with uneven thickness, and an uneven interface exists between the middle electrode layer and the top electrode, so that point contact of the top electrode and the resistive layer is formed at a position where the top electrode is close to the resistive layer, a stronger local electric field is generated at the point contact position under an external bias voltage, and the conducting wire is more prone to being switched on and off between the point contact position and the bottom electrode at a corresponding position, so that the switching-on and switching-off of the conducting wire in a fixed area are effectively regulated and controlled, and the key performance parameters of the selector, such as cycle stability, switching ratio and the like, are improved. In this embodiment, the thickness of the middle electrode layer is set to 3nm, and a thin film with non-uniform thickness is obtained after the preparation, so that an uneven and uneven interface is generated between the ultrathin active electrode layer and the top electrode.

Further, in an alternative embodiment, the intermediate electrode layer is grown by electron beam evaporation.

In a second aspect, the present invention provides a selector based on the growth of conductive wires, as shown in fig. 1, including a substrate, a bottom electrode, a resistance change layer, an intermediate electrode layer and a top electrode arranged from bottom to top; the top electrode is a multilayer structure top electrode and comprises an active electrode layer and an inert protective electrode which are arranged from bottom to top; wherein the active electrode material in the top electrode is Ag or Cu; the resistance-change layer is an oxygen-containing resistance-change layer, and is made of a thin oxide layer or a thin two-dimensional material subjected to oxygen treatment; the material of the middle electrode layer is an active electrode material and comprises titanium, tantalum or aluminum;

the middle electrode layer is extremely thin (the maximum thickness is not more than 10nm), and when the middle electrode layer is contacted with the resistance change layer, active electrode materials in the middle electrode layer can capture oxygen in the resistance change layer to generate oxidation, so that the middle electrode layer is converted into an amorphous oxide layer to limit the migration of active cations from the top electrode, and the growth of the conductive wire is limited; and at the moment, the middle electrode layer is a thin film with uneven thickness, and the contact surface of the middle electrode layer and the top electrode is uneven, so that point contact is formed between the top electrode and the resistance change layer, and the growth of the conductive wire tends to occur at the point contact position due to electric field concentration at the point contact position, so that the growth randomness of the conductive wire is limited.

Specifically, under the action of forward bias applied to the top electrode, Ag or Cu in the top electrode is oxidized at the point contact, and the obtained Ag⁺Or Cu²⁺Under the action of electric field, the electrons migrate to the bottom electrode and are gradually reduced near the bottom electrode, so that a conductive filament path is formed between the bottom electrode and the top electrodeAbrupt change from high resistance state to low resistance state; and spontaneous fusing of the conductive wire occurs in the process of gradually removing the voltage, and the device is volatilized from a low-resistance state to a high-resistance state, namely, the device has the characteristic of volatile threshold value transformation typical of a selector.

In the embodiment, the thickness of the resistance change layer is 3-15 nm; the bottom electrode is a multilayer electrode formed by one or two metals of gold, titanium, platinum and chromium.

In a third aspect, the present invention provides a method for preparing a selector based on conductive wire growth according to the second aspect, comprising:

s1, depositing a metal film on the substrate to obtain a bottom electrode;

s2, preparing a resistance change layer on the bottom electrode; the resistance-change layer is an oxygen-containing resistance-change layer, and is made of a thin oxide layer or a thin two-dimensional material subjected to oxygen treatment;

s3, depositing an active electrode on the resistance change layer; the active electrode deposited on the resistance change layer comprises titanium, tantalum or aluminum; at the moment, the active electrode on the resistance-change layer and oxygen in the resistance-change layer are oxidized and converted into an amorphous oxide layer, and a thin film with uneven thickness (the maximum thickness is not more than 10nm), namely an intermediate electrode layer, is obtained;

s4, sequentially depositing an active electrode layer and an inert protective electrode on the middle electrode layer to obtain a top electrode; wherein, the contact surface of the top electrode and the middle electrode layer is uneven; the material of the active electrode layer in the top electrode is Ag or Cu.

To further illustrate the selector provided by the present invention, taking the active electrode in the top electrode as Ag, and optimizing the performance of the selector by regulating the growth of Ag filament as an example, the following embodiments are described:

examples 1,

In this example, the optimization selector for improving the performance by controlling the growth of Ag filaments has a structure as shown in fig. 2. The substrate is a silicon substrate; the bottom electrode is of a double-layer structure consisting of titanium and platinum, the titanium is 10nm, the platinum is 30nm, the titanium is in contact with the silicon substrate to serve as an adhesion layer, and the platinum grows on the titanium; the resistance-change layer is made of a thin two-dimensional material HfSe₂Oxidized to HfSe containing oxygen by oxygen plasma treatment₂-xOx; the middle electrode layer is a Ti electrode, and the growth setting thickness is 3 nm; in the top electrode, an Ag electrode is grown on the middle electrode layer, and the thickness of the Ag electrode is 50 nm; the inert protective electrode is positioned on the Ag electrode, and an Au electrode is adopted, and the thickness is 10 nm.

In this embodiment, the optimized selector capable of improving performance by adjusting and controlling the growth of the Ag filament is prepared by photolithography, electron beam evaporation, two-dimensional material directional transfer, and oxygen plasma treatment, and specifically includes the following steps:

(1) and ultrasonically cleaning the silicon substrate for 10min by using acetone, ethanol and deionized water in sequence, repeatedly cleaning for 3 times, and drying the cleaned silicon substrate by using a nitrogen gun.

(2) After photoresist is homogenized on a silicon substrate, patterning is carried out by utilizing an ultraviolet lithography technology, and a bottom electrode pattern is obtained by developing, wherein the line width is 5 um; the 10/30nm titanium/platinum electrode was then electron beam evaporated and subjected to lift-off treatment with acetone to give a patterned titanium/platinum bottom electrode.

(3) Dry transfer is carried out by utilizing a two-dimensional material transfer platform, and HfSe obtained by mechanical stripping is obtained₂The flakes are transferred directionally to the bottom electrode; then to HfSe in the vacuum chamber of the reactive ion etcher₂Performing oxygen plasma treatment, setting the flow rate to be 50sccm, the power to be 50w, and the treatment time to be 5min to obtain the oxygen-containing HfSe₂-an xOx resistance change layer.

(4) Coating photoresist again and performing alignment treatment by using ultraviolet lithography to enable the top electrode pattern and the substrate to have two-dimensional HfSe₂The bottom electrode of the-xOx thin layer is in a cross structure and is developed to obtain a top electrode pattern; and then sequentially growing Ti/Ag/Au metal laminated structures by electron beam evaporation, wherein the thicknesses of the Ti/Ag/Au metal laminated structures are 3/50/10nm respectively, and cleaning and blow-drying the Ti/Ag/Au metal laminated structures after soaking in acetone to obtain the patterned top electrode laminated layer.

To further verify the reliability of the proposed method of the present invention, example 1, in which an optimized selector was prepared using the method provided by the present invention, was experimentally compared with comparative example 1, in which the method was not used.

Comparative example 1:

in the comparative example, except for the absence of the intermediate electrode layer, the remaining structure and the selected materials were kept the same as those in example 1; the remaining preparation of the selector was kept as in example 1, except that only 50/10nm of Ag/Au was grown as the electron beam evaporated top electrode of the multilayer structure.

The electrical performance test of the selectors corresponding to the embodiment 1 and the comparative example 1 is respectively carried out by utilizing a semiconductor analysis tester, and the specific steps are as follows:

a bias voltage was applied to the top electrode of example 1 and comparative example 1, and the bottom electrode was grounded, and DC I-V characteristic scans were performed, respectively.

In example 1, the voltage sweep range was set to 0-0.65V, the limiting current was set to 10ua, and 100 cycles of dc I-V characteristic sweeps were continuously performed to obtain I-V characteristic curves as shown in fig. 3 (a); in comparative example 1, the voltage sweep range was set to 0 to 1.2V and the limiting current was set to 10ua, and the I-V characteristic curve was obtained as shown in (b) of FIG. 3 by similarly conducting 100 cycles of the DC I-V characteristic sweep. It is noteworthy that for example 1 and comparative example 1, the curves of the first I-V scan and the subsequent 99 scans are not very different, i.e. both have a forming-free behavior.

Specifically, as can be seen from the graph (a) in fig. 3, in the example 1, in the process of the voltage increase from 0 to 0.65V, the current of the optimization selector sharply increases in the range of 0.4 to 0.65V, and the sudden change from the high resistance state to the low resistance state occurs, which is called the SET process; during the process of gradually withdrawing the voltage from 0.65-0V, the current sharply drops in the range of 0.05-0V, and the selector spontaneously returns to the initial high-resistance state from the low-resistance state, which is called a RESET process. As can be seen from the graph (b) of fig. 3, in comparative example 1, the selector has the SET process occurring in the range of 0.5-1.0V and the RESET process occurring in the range of 0.25-0V. As can be seen from comparing graph (a) in FIG. 3 with graph (b) in FIG. 3, the 100-cycle DC I-V curve results of example 1 compared to comparative example 1 show that example 1 has a larger on-off ratio, from 10 of comparative example 1³Optimized to be close to 10⁶(ii) a The SET voltage range of the embodiment 1 is obviously reduced, so that the energy consumption can be reduced in the gating process of the array; the SET and RESET voltage distributions of example 1 are more concentrated, and surface example 1 has better stability between cycles; the high resistance state of example 1 is more stable and does not gradually increase with increasing voltageAnd the phenomenon can effectively reduce the misoperation probability. I.e. the key performance parameters of the selector in example 1 are optimized.

Further, example 1 was subjected to dc I-V characteristic scanning at different limiting currents, and the results are shown in fig. 4. As can be seen from FIG. 4, under the condition of high ON-state current limited by 100ua, the excellent threshold transition characteristic can be still maintained in the embodiment 1, and the switching ratio is close to 10⁷。

Examples 2,

In the embodiment, the bottom electrode is of a double-layer structure consisting of 10nm of chromium and 30nm of gold, and the gold grows on the chromium; the resistance change layer is made of a thin two-dimensional material GaSe2, and is made into an oxygen-containing thin layer through oxygen plasma treatment, the flow is set to be 50sccm, the power is set to be 80w, and the treatment time is set to be 2 min. The remaining structure and manufacturing method of the selector in this example are the same as those in example 1.

To further verify the reliability of the proposed method of the present invention, example 2, in which an optimized selector was prepared using the method provided by the present invention, was experimentally compared with comparative example 2, in which the method was not used.

Comparative example 2:

in the comparative example, except for the absence of the intermediate electrode layer, the remaining structure and the selected materials were kept the same as those in example 2; the remaining preparation of the selector was kept as in example 2, except that only 50/10nm of Ag/Au was grown as the electron beam evaporated the top electrode of the multilayer structure.

Direct current cycle I-V scans were performed on the selectors corresponding to example 2 and comparative example 2, respectively, to obtain a direct current cycle I-V curve of example 2 as shown in (a) of fig. 5, and a direct current cycle I-V curve of comparative example 2 as shown in (b) of fig. 5.

As can be seen from comparing the graph (a) in fig. 5 with the graph (b) in fig. 5, compared with the comparative example 2, the example 2 has a larger switching ratio, the high-resistance state is more stable, and the transition slope is significantly increased, so that the malfunction of the gating process in the memristor array can be effectively reduced, while the comparative example 2 has the disadvantage of poor inter-device stability and inter-cycle stability, and is obviously not suitable for being used as a selector.

Based on the obvious performance optimization obtained by the embodiment, the feasibility of the method for adjusting the on-off of the Ag wire by introducing the ultrathin middle electrode layer so as to optimize the performance of the selector is verified.

It will be understood by those skilled in the art that the foregoing is only a preferred embodiment of the present invention, and is not intended to limit the invention, and that any modification, equivalent replacement, or improvement made within the spirit and principle of the present invention should be included in the scope of the present invention.