阅读说明：本技术 一种pvc透光革的制备方法 (Preparation method of PVC light-transmitting leather ) 是由 匡建武 张术根 蒋晓兵 于 2021-07-29 设计创作，主要内容包括：本发明属于人造革制备技术领域,尤其一种PVC透光革的制备方法,包括以下方法步骤：材料准备：配制透明PVC底层浆料；配制PVC接着层浆料；配制PVC面层浆料；选定基布和离型纸,在离型纸上用涂布法涂一层透明PVC底层,烘干温度为170-180℃,将透明PVC底层表面采用涂布法再涂一层PVC接着层,并贴上基布；本发明提供一种PVC透光革的制备方法,通过配制透明PVC底层浆料、PVC接着层浆料和PVC面层浆料生产出由下至上依次设置的基布、接着层、PVC底层、印花层、PVC面层的皮革,提升皮革的色泽,提升皮革韧性和耐磨性,可以重复弯曲折叠,不易变形,极大的提高皮革的使用寿命。(The invention belongs to the technical field of artificial leather preparation, and particularly relates to a preparation method of PVC light-transmitting leather, which comprises the following steps: preparing materials: preparing transparent PVC bottom layer slurry; preparing PVC adhesive layer slurry; preparing PVC surface layer slurry; selecting base cloth and release paper, coating a transparent PVC bottom layer on the release paper by a coating method, drying at the temperature of 170-180 ℃, coating a PVC adhesive layer on the surface of the transparent PVC bottom layer by the coating method, and attaching the base cloth; the invention provides a preparation method of PVC light-transmitting leather, which is characterized in that the leather of a base cloth, an adhesive layer, a PVC bottom layer, a printing layer and a PVC surface layer which are sequentially arranged from bottom to top is produced by preparing transparent PVC bottom layer slurry, PVC adhesive layer slurry and PVC surface layer slurry, the color of the leather is improved, the toughness and the wear resistance of the leather are improved, the leather can be repeatedly bent and folded and is not easy to deform, and the service life of the leather is greatly prolonged.)

1. A preparation method of PVC light-transmitting leather is characterized by comprising the following steps:

s1, material preparation: preparing transparent PVC bottom layer slurry; preparing PVC adhesive layer slurry; preparing PVC surface layer slurry; selecting base cloth and release paper;

s2, coating a transparent PVC bottom layer on release paper by a coating method, wherein the drying temperature is 170-180 ℃;

s3, coating a PVC adhesive layer on the surface of the transparent PVC bottom layer by a coating method, attaching base cloth, and drying to form the PVC adhesive layer and the base cloth layer at the drying temperature of 180-190 ℃ to obtain a first semi-finished product;

s4, peeling the first semi-finished product from the release paper to obtain a second semi-finished product;

s5, printing the second semi-finished product;

and S6, laminating the second semi-finished product printed with the pattern on a PVC surface layer through a calendaring process, and drying at the temperature of 160-170 ℃ to obtain the PVC light-transmitting leather.

2. The preparation method of the PVC light-transmitting leather according to claim 1, wherein the preparation of the transparent PVC bottom layer slurry comprises the following steps of: 100 parts of PVC powder, 55-75 parts of plasticizer, 4-6 parts of PVC stabilizer and 15-25 parts of transparent liquid flame retardant, stirring for 30-40 minutes after mixing, and controlling the viscosity to be 2000-2500CPS to prepare transparent PVC bottom layer slurry.

3. The preparation method of the PVC light-transmitting leather according to claim 2, wherein the preparation of the PVC subsequent layer slurry comprises the following raw materials in parts by weight: 100 parts of PVC powder, 55-75 parts of plasticizer, 2-4 parts of PVC stabilizer and 10-20 parts of transparent liquid flame retardant, stirring for 20-40 minutes, and preparing into PVC adhesive layer slurry with the viscosity of 2500-3000 CPS.

4. The preparation method of the PVC light-transmitting leather according to claim 1, wherein the preparation of the PVC surface layer slurry comprises the following steps of preparing raw materials in parts by weight: 100 parts of PVC powder, 75-95 parts of plasticizer, 3-5 parts of PVC transparent stabilizer and 4-6 parts of black pigment. Stirring for 20-25 min after mixing, and controlling the viscosity at 2000-3000CPS to prepare the PVC surface layer slurry, wherein the PVC transparent stabilizer is preferably organic tin.

5. The preparation method of the PVC light-transmitting leather according to claim 2, wherein the preparation of the transparent PVC bottom layer slurry comprises the following steps of: 100 parts of PVC powder, 65 parts of plasticizer, 5 parts of PVC stabilizer and 20 parts of transparent liquid flame retardant, mixing and stirring for 35 minutes, controlling the viscosity at 2300CPS, and preparing the transparent PVC bottom layer slurry.

6. The method for preparing PVC light-transmitting leather according to claim 1, wherein in step S5, the printing treatment is a treatment with a treating agent added with ink on the second semi-finished product, and various patterns can be engraved on the treating wheel.

7. The method for preparing PVC light-transmitting leather according to claim 1, wherein in step S5, the printing process is to attach a transfer film on the second semi-finished product, and the transfer film can be various patterns.

8. The preparation method of the PVC light-transmitting leather according to claim 1, wherein the preparation of the PVC subsequent layer slurry comprises the following raw materials in parts by weight: 100 parts of PVC powder, 55-75 parts of plasticizer, 2-4 parts of PVC stabilizer and 10-20 parts of transparent liquid flame retardant, stirring for 20-40 minutes, and preparing into PVC adhesive layer slurry with the viscosity of 2500-3000 CPS.

9. The preparation method of the PVC light-transmitting leather according to claim 1, wherein the preparation of the PVC surface layer slurry comprises the following steps of preparing raw materials in parts by weight: 100 parts of PVC powder, 75-95 parts of plasticizer, 3-5 parts of PVC transparent stabilizer and 4-6 parts of black pigment, stirring for 20-25 minutes after mixing, and controlling the viscosity to be 2000-3000CPS to prepare PVC surface layer slurry.

10. The method for preparing PVC light-transmitting leather according to claim 3, wherein the transparent liquid flame retardant is 2-ethylhexyl diphenyl phosphate.

Technical Field

The invention relates to the technical field of artificial leather preparation, in particular to a preparation method of PVC light-transmitting leather.

Background

The variety of leather is very wide. Classified according to tanning methods, into chrome-tanned leather, vegetable-tanned leather, oil-tanned leather, aldehyde-tanned leather, combination-tanned leather, and the like. In addition, it can be classified into light leather and heavy leather. Leathers commonly used for uppers, garments, gloves and the like, known as light leathers, measured by area; leathers used for leather shoes, inner and outer soles, industrial accessories, etc., which are tanned with relatively thick animal skins by a vegetable tanning agent or a combination thereof, are called heavy leathers, measured by weight. The animal species are classified into pig leather, cow leather, sheep leather, horse leather, donkey leather, kangaroo leather, etc. according to the folding, and a small amount of fish leather, reptile leather, amphibian leather, ostrich leather, etc. are added. Wherein the cattle leather is divided into yellow cattle leather, buffalo leather, yak leather and dzo leather; the sheepskin is classified into sheep leather and goat leather. Among the main leather types, the cattle leather and the sheep leather have flat and thin surfaces, small hair holes, compact and compact internal structure, better plump and elastic feeling of the leather body and good physical properties. Therefore, the superior cattle and sheep leathers are generally used as leather for high-grade products, and the price of the superior cattle and sheep leathers is higher in the bulk leathers.

The artificial leather and the synthetic leather are composite materials which simulate the tissue structure and the service performance of leather and can be used as leather substitutes. Usually, woven fabric and non-woven fabric are used to simulate the net layer of leather, and microporous high-molecular coating is used to simulate the grain layer of leather, so that the obtained artificial leather is similar to leather in both front and back sides, and can be widely used for making shoes, boots, bags, balls, etc. In a general classification method, the artificial leather is a leather-like material prepared by coating a textile fabric as a base fabric with a polymer slurry, and most of the artificial leathers are polyvinyl chloride (PVC) as a coating agent, which is commonly called as "PVC" artificial leather. The leather industry covers the main industries of leather making, shoes making, leather clothing, leather pieces, fur, products thereof and the like, and the matching industries of leather chemical industry, leather hardware, leather machinery, auxiliary materials and the like. The association degree of the upstream and the downstream is high, the product is very green depending on market pulling, and the characteristics of earning foreign exchange, enriching people and employment are integrated.

At present, leather on the market is mainly made of animal skin and PU artificial leather, such as crocodile skin, is lack of elasticity, and the production material selection is harsh; the first layer of cowhide is not resistant to bending, is easy to bend and deform in the middle of the leather when used, is easy to fade, and can be hardened and broken after being soaked or washed by water; the two layers of cowhide have insufficient toughness, and the PU artificial leather which is additionally provided with a smoothing treatment procedure after surface coating is generally formed by compounding two layers and three layers, so that the produced leather has extremely poor texture toughness and short service life; the light-reflecting property of the traditional leather fabric is poor, and the light-transmitting texture is difficult to present.

Disclosure of Invention

Objects of the invention

In order to solve the technical problems in the background technology, the invention provides a preparation method of PVC light-transmitting leather.

(II) technical scheme

In order to solve the problems, the invention provides a preparation method of PVC light-transmitting leather, which comprises the following steps:

s1, material preparation: preparing transparent PVC bottom layer slurry; preparing PVC adhesive layer slurry; preparing PVC surface layer slurry; selecting base cloth and release paper;

s2, coating a transparent PVC bottom layer on release paper by a coating method, wherein the drying temperature is 170-180 ℃;

s3, coating a PVC adhesive layer on the surface of the transparent PVC bottom layer by a coating method, attaching base cloth, and drying to form the PVC adhesive layer and the base cloth layer at the drying temperature of 180-190 ℃ to obtain a first semi-finished product;

s4, peeling the first semi-finished product from the release paper to obtain a second semi-finished product;

s5, printing the second semi-finished product;

and S6, laminating the second semi-finished product printed with the pattern on a PVC surface layer through a calendaring process, and drying at the temperature of 160-170 ℃ to obtain the PVC light-transmitting leather.

Preferably, the preparation of the transparent PVC bottom layer slurry comprises the following raw materials in parts by weight: 100 parts of PVC powder, 55-75 parts of plasticizer, 4-6 parts of PVC stabilizer and 15-25 parts of transparent liquid flame retardant, stirring for 30-40 minutes after mixing, and controlling the viscosity to be 2000-2500CPS to prepare transparent PVC bottom layer slurry.

Preferably, the preparation of the PVC subsequent layer slurry comprises the following raw materials in parts by weight: 100 parts of PVC powder, 55-75 parts of plasticizer, 2-4 parts of PVC stabilizer and 10-20 parts of transparent liquid flame retardant, stirring for 20-40 minutes, and preparing into PVC adhesive layer slurry with the viscosity of 2500-3000 CPS.

Preferably, the preparation of the PVC surface layer slurry comprises the following raw materials in parts by weight: 100 parts of PVC powder, 75-95 parts of plasticizer, 3-5 parts of PVC transparent stabilizer and 4-6 parts of black pigment. Stirring for 20-25 min after mixing, and controlling the viscosity at 2000-3000CPS to prepare the PVC surface layer slurry, wherein the PVC transparent stabilizer is organic tin.

Preferably, the preparation of the transparent PVC bottom layer slurry comprises the following raw materials in parts by weight: 100 parts of PVC powder, 65 parts of plasticizer, 5 parts of PVC stabilizer and 20 parts of transparent liquid flame retardant, mixing and stirring for 35 minutes, controlling the viscosity at 2300CPS, and preparing the transparent PVC bottom layer slurry.

Preferably, in step S5, the printing process is performed on the second semi-finished product by using a treating agent added with ink, and various patterns can be engraved on the treating wheel.

Preferably, in step S5, the printing process is to attach a transfer film to the second semi-finished product, and the transfer film may have various patterns.

Preferably, the preparation of the PVC subsequent layer slurry comprises the following raw materials in parts by weight: 100 parts of PVC powder, 55-75 parts of plasticizer, 2-4 parts of PVC stabilizer and 10-20 parts of transparent liquid flame retardant, stirring for 20-40 minutes, and preparing into PVC adhesive layer slurry with the viscosity of 2500-3000 CPS.

Preferably, the preparation of the PVC surface layer slurry comprises the following raw materials in parts by weight: 100 parts of PVC powder, 75-95 parts of plasticizer, 3-5 parts of PVC transparent stabilizer and 4-6 parts of black pigment, stirring for 20-25 minutes after mixing, and controlling the viscosity to be 2000-3000CPS to prepare PVC surface layer slurry.

Preferably, the transparent liquid flame retardant is 2-ethylhexyl diphenyl phosphate.

The technical scheme of the invention has the following beneficial technical effects:

the transparent PVC bottom layer slurry is prepared by mixing 100 parts of PVC powder, 55-75 parts of plasticizer, 4-6 parts of PVC stabilizer and 15-25 parts of transparent liquid flame retardant, stirring for 30-40 minutes, and controlling the viscosity to be 2000-2500CPS, and is used for manufacturing transparent leather and improving the color of the leather.

By adopting 100 parts of PVC powder, 55-75 parts of plasticizer, 2-4 parts of PVC stabilizer and 10-20 parts of transparent liquid flame retardant, stirring for 20-40 minutes, and preparing PVC adhesive layer slurry with the viscosity of 2500 plus 3000CPS, the produced leather has good texture toughness, can be repeatedly bent and folded, is not easy to deform, and greatly prolongs the service life of the leather.

100 parts of PVC powder, a plasticizer, a PVC transparent stabilizer and a black pigment are mixed and stirred to control viscosity to prepare PVC surface layer slurry which is used for manufacturing a surface layer of leather, so that the leather has good wear resistance.

The invention provides a preparation method of PVC light-transmitting leather, which is characterized in that the leather of a base cloth, an adhesive layer, a PVC bottom layer, a printing layer and a PVC surface layer which are sequentially arranged from bottom to top is produced by preparing transparent PVC bottom layer slurry, PVC adhesive layer slurry and PVC surface layer slurry, the color of the leather is improved, the toughness and the wear resistance of the leather are improved, the leather can be repeatedly bent and folded and is not easy to deform, and the service life of the leather is greatly prolonged.

Drawings

FIG. 1 is a flow chart of a preparation method of the PVC light-transmitting leather.

Fig. 2 is a schematic diagram of the material preparation of the PVC light-transmitting leather of the present invention.

FIG. 3 is a structural diagram of a PVC light-transmitting leather prepared by the invention.

Fig. 4 is a common PVC leather with no illumination on the back.

FIG. 5 is a diagram of PVC clear leather prepared according to the invention with no light on the back.

Fig. 6 is a general PVC leather with light on the back.

FIG. 7 is a diagram of PVC clear leather prepared according to the invention with light on the back.

Detailed Description

In order to make the objects, technical solutions and advantages of the present invention more apparent, the present invention will be described in further detail with reference to the accompanying drawings in conjunction with the following detailed description. It should be understood that the description is intended to be exemplary only, and is not intended to limit the scope of the present invention. Moreover, in the following description, descriptions of well-known structures and techniques are omitted so as to not unnecessarily obscure the concepts of the present invention.

Example one

Referring to fig. 1-3, the invention provides a preparation method of a PVC light-transmitting leather, which comprises the following steps:

s1, material preparation: preparing transparent PVC bottom layer slurry, which comprises the following raw materials in parts by weight: 100 parts of PVC powder, 55 parts of plasticizer, 4 parts of PVC stabilizer and 15 parts of transparent liquid flame retardant, mixing and stirring for 30 minutes, controlling the viscosity to be 2000CPS, and preparing transparent PVC bottom layer slurry, wherein the transparent liquid flame retardant is 2-ethylhexyl diphenyl phosphate;

preparing PVC adhesive layer slurry, which comprises the following raw materials in parts by weight: 100 parts of PVC powder, 55 parts of plasticizer, 2 parts of PVC stabilizer and 10 parts of transparent liquid flame retardant, stirring for 20 minutes, and preparing PVC adhesive layer slurry with the viscosity of 2500CPS, wherein the transparent liquid flame retardant is 2-ethylhexyl diphenyl phosphate;

preparing PVC surface layer slurry, which comprises the following raw materials in parts by weight: 100 parts of PVC powder, 75 parts of plasticizer, 3 parts of PVC transparent stabilizer and 4 parts of black pigment; mixing, stirring for 20 minutes, controlling the viscosity to be 2000CPS, and preparing PVC surface layer slurry, wherein the PVC transparent stabilizer is organic tin;

selecting base cloth and release paper;

s2, coating a transparent PVC bottom layer on release paper by a coating method, wherein the drying temperature is 170 ℃;

s3, coating a PVC adhesive layer on the surface of the transparent PVC bottom layer by a coating method, attaching base cloth, and drying to form the PVC adhesive layer and the base cloth layer at 180 ℃ to obtain a first semi-finished product;

s4, peeling the first semi-finished product from the release paper to obtain a second semi-finished product;

s5, printing is carried out on the second semi-finished product, the printing treatment is carried out on the second semi-finished product by using a treating agent added with ink, and various patterns can be engraved on the treating wheel;

and S6, laminating the second semi-finished product printed with the pattern with a PVC surface layer through a calendaring process, and drying at 160 ℃ to obtain the PVC light-transmitting leather.

Example two

Referring to fig. 1-3, the invention provides a preparation method of a PVC light-transmitting leather, which comprises the following steps:

s1, material preparation: preparing transparent PVC bottom layer slurry, which comprises the following raw materials in parts by weight: 100 parts of PVC powder, 60 parts of plasticizer, 5 parts of PVC stabilizer and 18 parts of transparent liquid flame retardant, mixing and stirring for 33 minutes, controlling the viscosity to be 2200CPS, and preparing transparent PVC bottom layer slurry, wherein the transparent liquid flame retardant is 2-ethylhexyl diphenyl phosphate;

preparing PVC adhesive layer slurry, which comprises the following raw materials in parts by weight: 100 parts of PVC powder, 60 parts of plasticizer, 3 parts of PVC stabilizer and 12 parts of transparent liquid flame retardant, stirring for 25 minutes, and preparing PVC adhesive layer slurry with the viscosity of 2600CPS, wherein the transparent liquid flame retardant is 2-ethylhexyl diphenyl phosphate;

preparing PVC surface layer slurry, which comprises the following raw materials in parts by weight: 100 parts of PVC powder, 80 parts of plasticizer, 4 parts of PVC transparent stabilizer and 5 parts of black pigment; mixing and stirring for 22 minutes, controlling the viscosity at 2300CPS, and preparing PVC surface layer slurry, wherein the PVC transparent stabilizer is organic tin;

selecting base cloth and release paper;

s2, coating a transparent PVC bottom layer on release paper by a coating method, wherein the drying temperature is 173 ℃;

s3, coating a PVC adhesive layer on the surface of the transparent PVC bottom layer by a coating method, attaching base cloth, and drying to form the PVC adhesive layer and the base cloth layer at 183 ℃ to obtain a first semi-finished product;

s4, peeling the first semi-finished product from the release paper to obtain a second semi-finished product;

s5, printing is carried out on the second semi-finished product, the printing treatment is carried out on the second semi-finished product by using a treating agent added with ink, and various patterns can be engraved on the treating wheel;

and S6, laminating the second semi-finished product printed with the pattern on a PVC surface layer through a calendaring process, and drying at the temperature of 160-170 ℃ to obtain the PVC light-transmitting leather.

EXAMPLE III

Referring to fig. 1-3, the invention provides a preparation method of a PVC light-transmitting leather, which comprises the following steps:

s1, material preparation: preparing transparent PVC bottom layer slurry, which comprises the following raw materials in parts by weight: 100 parts of PVC powder, 70 parts of plasticizer, 5 parts of PVC stabilizer and 22 parts of transparent liquid flame retardant, mixing and stirring for 36 minutes, controlling the viscosity to be 2400CPS, and preparing transparent PVC bottom layer slurry, wherein the transparent liquid flame retardant is 2-ethylhexyl diphenyl phosphate;

preparing PVC adhesive layer slurry, which comprises the following raw materials in parts by weight: 100 parts of PVC powder, 70 parts of plasticizer, 3 parts of PVC stabilizer and 18 parts of transparent liquid flame retardant, stirring for 30 minutes, and preparing PVC adhesive layer slurry with the viscosity of 2800CPS, wherein the transparent liquid flame retardant is 2-ethylhexyl diphenyl phosphate;

preparing PVC surface layer slurry, which comprises the following raw materials in parts by weight: 100 parts of PVC powder, 90 parts of plasticizer, 4 parts of PVC transparent stabilizer and 5 parts of black pigment; stirring for 23 minutes after mixing, controlling the viscosity to be 2700CPS, and preparing PVC surface layer slurry, wherein the PVC transparent stabilizer is organic tin;

selecting base cloth and release paper;

s2, coating a transparent PVC bottom layer on release paper by a coating method, wherein the drying temperature is 176 ℃;

s3, coating a PVC adhesive layer on the surface of the transparent PVC bottom layer by a coating method, attaching base cloth, and drying to form the PVC adhesive layer and the base cloth layer at 186 ℃ to obtain a first semi-finished product;

s4, peeling the first semi-finished product from the release paper to obtain a second semi-finished product;

s5, printing the second semi-finished product, wherein the printing process is to paste a transfer printing film on the second semi-finished product, and the transfer printing film can be various patterns;

and S6, laminating the second semi-finished product printed with the pattern with a PVC surface layer through a calendaring process, and drying at the drying temperature of 166 ℃ to obtain the PVC light-transmitting leather.

Example four

Referring to fig. 1-3, the invention provides a preparation method of a PVC light-transmitting leather, which comprises the following steps:

s1, material preparation: preparing transparent PVC bottom layer slurry, which comprises the following raw materials in parts by weight: 100 parts of PVC powder, 75 parts of plasticizer, 6 parts of PVC stabilizer and 25 parts of transparent liquid flame retardant, mixing and stirring for 40 minutes, controlling the viscosity to be 2500CPS, and preparing transparent PVC bottom layer slurry, wherein the transparent liquid flame retardant is 2-ethylhexyl diphenyl phosphate;

preparing PVC adhesive layer slurry, which comprises the following raw materials in parts by weight: 100 parts of PVC powder, 75 parts of plasticizer, 4 parts of PVC stabilizer and 20 parts of transparent liquid flame retardant, stirring for 40 minutes, and preparing PVC adhesive layer slurry with the viscosity of 3000CPS, wherein the transparent liquid flame retardant is 2-ethylhexyl diphenyl phosphate;

preparing PVC surface layer slurry, which comprises the following raw materials in parts by weight: 100 parts of PVC powder, 95 parts of plasticizer, 5 parts of PVC transparent stabilizer and 6 parts of black pigment; mixing, stirring for 25 minutes, controlling the viscosity at 3000CPS, and preparing PVC surface layer slurry, wherein the PVC transparent stabilizer is organic tin;

selecting base cloth and release paper;

s2, coating a transparent PVC bottom layer on release paper by a coating method, and drying at 180 ℃;

s3, coating a PVC adhesive layer on the surface of the transparent PVC bottom layer by a coating method, attaching base cloth, and drying to form the PVC adhesive layer and the base cloth layer at 190 ℃ to obtain a first semi-finished product;

s4, peeling the first semi-finished product from the release paper to obtain a second semi-finished product;

s5, printing the second semi-finished product, wherein the printing process is to paste a transfer printing film on the second semi-finished product, and the transfer printing film can be various patterns;

and S6, laminating the second semi-finished product printed with the pattern with a PVC surface layer through a calendaring process, and drying at 170 ℃ to obtain the PVC light-transmitting leather.

Referring to fig. 4-5, under the condition that no light irradiates on the back, the common PVC leather is not different from the PVC light-transmitting leather prepared by the invention, referring to fig. 6-7, when the light irradiates on the back, the common PVC leather is obviously different from the PVC light-transmitting leather prepared by the invention, and the PVC light-transmitting leather prepared by the invention shows hidden patterns, so the PVC light-transmitting leather prepared by the invention has better light-transmitting performance.

The transparent PVC bottom layer slurry is prepared by mixing 100 parts of PVC powder, 55-75 parts of plasticizer, 4-6 parts of PVC stabilizer and 15-25 parts of transparent liquid flame retardant, stirring for 30-40 minutes, and controlling the viscosity to be 2000-2500CPS, and is used for manufacturing transparent leather and improving the color of the leather. By adopting 100 parts of PVC powder, 55-75 parts of plasticizer, 2-4 parts of PVC stabilizer and 10-20 parts of transparent liquid flame retardant, stirring for 20-40 minutes, and preparing PVC adhesive layer slurry with the viscosity of 2500 plus 3000CPS, the produced leather has good texture toughness, can be repeatedly bent and folded, is not easy to deform, and greatly prolongs the service life of the leather. 100 parts of PVC powder, a plasticizer, a PVC transparent stabilizer and a black pigment are mixed and stirred to control viscosity to prepare PVC surface layer slurry which is used for manufacturing a surface layer of leather, so that the leather has good wear resistance. The invention provides a preparation method of PVC light-transmitting leather, which is characterized in that the leather of a base cloth, an adhesive layer, a PVC bottom layer, a printing layer and a PVC surface layer which are sequentially arranged from bottom to top is produced by preparing transparent PVC bottom layer slurry, PVC adhesive layer slurry and PVC surface layer slurry, the color of the leather is improved, the toughness and the wear resistance of the leather are improved, the leather can be repeatedly bent and folded and is not easy to deform, and the service life of the leather is greatly prolonged.

The foregoing shows and describes the general principles, essential features, and advantages of the invention. It will be understood by those skilled in the art that the present invention is not limited to the embodiments described above, and the preferred embodiments of the present invention are described in the above embodiments and the description, and are not intended to limit the present invention.