阅读说明：本技术 可弯折玻璃堆叠组件、制品及其制造方法 (Bendable glass stack assembly, article, and method of making same ) 是由 T·张 P·W·储 A·J·埃利森 T·M·格罗斯 胡广立 N·J·史密斯 于 2015-01-28 设计创作，主要内容包括：一种玻璃元件,其具有25μm至125μm的厚度,第一主表面,第二主表面,和从第一主表面延伸至第一深度的压缩应力区,该区由在第一主表面处至少约100MPa的压缩应力σI限定。此外,该玻璃元件具有应力分布,使得当经过200000次通过平行板方法弯折至1mm至20mm的目标弯折半径的循环时,其没有损坏。另外,当用具有1.5mm直径的碳化钨球加载玻璃元件的第一主表面时,玻璃元件有超过约1.5kgf的抗穿刺性。(A glass element having a thickness of 25 μ ι η to 125 μ ι η, a first major surface, a second major surface, and a compressive stress region extending from the first major surface to a first depth, the region defined by a compressive stress σ I of at least about 100MPa at the first major surface. Furthermore, the glass element has a stress distribution such that it is not damaged when it is subjected to 200000 cycles of bending by the parallel plate method to a target bending radius of 1mm to 20 mm. In addition, the glass element has a puncture resistance of greater than about 1.5kgf when the first major surface of the glass element is loaded with a tungsten carbide ball having a diameter of 1.5 mm.)