阅读说明：本技术 一种涤纶提花面料及其生产方法 (Terylene jacquard fabric and production method thereof ) 是由 范美忠 范建良 史一峰 陆忠涛 于 2020-12-30 设计创作，主要内容包括：本发明公开了一种涤纶提花面料及其生产方法,涤纶提花面料及其生产方法：第一步：原料选择,经纱选择100D/36F的涤纶白低弹丝,纬纱选择150D/48F的涤纶黑丝,50D/36F的双色竹纤维丝；第二步：检验原料的条干是否均匀,并检查色差情况；第三步：将双色竹纤维丝分别缠绕在经纱和纬纱上；第四步：通过扦经工艺、提花锻造工艺、预定型工艺、水洗染整工艺、定型工艺完成加工。通过经纬交错可实现提花工艺的加工,配合竹纤维丝与经纱和纬纱的结合,能够提高面料的吸湿效果,保证原有耐皱褶效果的同时,提高舒适性。(The invention discloses a terylene jacquard fabric and a production method thereof, wherein the terylene jacquard fabric and the production method thereof comprise the following steps: the first step is as follows: selecting raw materials, wherein warp yarns are 100D/36F polyester white low-stretch yarns, weft yarns are 150D/48F polyester black yarns, and 50D/36F bicolor bamboo fiber yarns; the second step is that: checking whether the evenness of the raw materials is uniform or not, and checking the color difference condition; the third step: winding the bicolor bamboo fiber yarns on the warp yarns and the weft yarns respectively; the fourth step: the processing is completed by a skewering process, a jacquard forging process, a pre-setting process, a washing dyeing and finishing process and a setting process. The processing of jacquard weave technology can be realized through warp and weft crisscross, and the moisture absorption effect of surface fabric can be improved to the combination of cooperation bamboo cellosilk and warp and woof, when guaranteeing original resistant wrinkle effect, improves the travelling comfort.)

1. A terylene jacquard fabric and a production method thereof are characterized in that: the terylene jacquard fabric and the production method thereof are as follows:

the first step is as follows: selecting raw materials, wherein warp yarns are 100D/36F polyester white low-stretch yarns, weft yarns are 150D/48F polyester black yarns, and 50D/36F bicolor bamboo fiber yarns;

the second step is that: checking whether the evenness of the raw materials is uniform or not, and checking the color difference condition;

the third step: winding the bicolor bamboo fiber yarns on the warp yarns and the weft yarns respectively;

the fourth step: the processing is completed by a skewering process, a jacquard forging process, a pre-setting process, a washing dyeing and finishing process and a setting process.

2. The terylene jacquard fabric and the production method thereof according to claim 1, wherein the terylene jacquard fabric is characterized in that: the double-color bamboo fiber yarns in the first step are respectively white yarns corresponding to warp yarns and black yarns corresponding to weft yarns.

3. The terylene jacquard fabric and the production method thereof according to claim 1, wherein the terylene jacquard fabric is characterized in that: and the bamboo fiber yarns, the warp yarns and the weft yarns in the third step are processed by a silk thread winding machine in a combined manner.

4. The terylene jacquard fabric and the production method thereof according to claim 1, wherein the terylene jacquard fabric is characterized in that: the jacquard forging process in said fourth step is carried out by means of a jacquard machine, operating at a tension of between 280 and 330 kg.

5. The terylene jacquard fabric and the production method thereof according to claim 4, wherein the terylene jacquard fabric is characterized in that: the jacquard machine processing rotation speed in the fourth step is 540-620 revolutions per minute.

6. The terylene jacquard fabric and the production method thereof according to claim 1, wherein the terylene jacquard fabric is characterized in that: the operation temperature of the pre-setting process in the fourth step is 140 to 160 degrees.

7. The terylene jacquard fabric and the production method thereof according to claim 1, wherein the terylene jacquard fabric is characterized in that: the operation temperature of the water washing dyeing and finishing process in the fourth step is 120-150 ℃.

8. The terylene jacquard fabric and the production method thereof according to claim 7, wherein the terylene jacquard fabric is characterized in that: and the water washing liquid of the water washing dyeing and finishing process in the fourth step is 3-5% of water solution of the transfer softening and fluffing agent.

9. The terylene jacquard fabric and the production method thereof according to claim 1, wherein the terylene jacquard fabric is characterized in that: the operation temperature of the sizing process in the fourth step is 160 to 180 ℃.

Technical Field

The invention belongs to the technical field of polyester jacquard fabrics, and particularly relates to a polyester jacquard fabric and a production method thereof.

Background

Terylene is an important variety in synthetic fibers and is the trade name of polyester fibers in China. The fiber is made from polyethylene terephthalate (PET), which is a fiber-forming high polymer prepared by esterification or ester exchange and polycondensation reaction of Poly Terephthalic Acid (PTA) or dimethyl terephthalate (DMT) and ethylene glycol (MEG), through spinning and post-treatment.

The terylene has wide application range, is widely used for manufacturing clothes and industrial products, and most clothes are made of terylene materials, have excellent crease resistance and good elasticity and are not easy to wash out.

The jacquard fabric is a home textile fabric and fashion fabric, and is characterized in that the jacquard fabric is a large variety of fabrics, namely, the fabric is a concave-convex pattern formed by interlacing warp and weft, and the jacquard fabric can be divided into a home textile fabric and a fashion fabric.

The terylene jacquard fabric can be produced by combining terylene with a jacquard process, but the prior terylene jacquard fabric has poor hygroscopicity, is easy to sweat and has low comfort level.

Disclosure of Invention

The invention aims to provide a polyester jacquard fabric and a production method thereof, and aims to solve the problems of poor moisture absorption, easiness in sweating and low comfort level of the polyester jacquard fabric.

In order to achieve the purpose, the invention provides the following technical scheme: a terylene jacquard fabric and a production method thereof are disclosed, wherein the terylene jacquard fabric and the production method thereof comprise the following steps:

the first step is as follows: selecting raw materials, wherein warp yarns are 100D/36F polyester white low-stretch yarns, weft yarns are 150D/48F polyester black yarns, and 50D/36F bicolor bamboo fiber yarns;

the second step is that: checking whether the evenness of the raw materials is uniform or not, and checking the color difference condition;

the third step: winding the bicolor bamboo fiber yarns on the warp yarns and the weft yarns respectively;

the fourth step: the processing is completed by a skewering process, a jacquard forging process, a pre-setting process, a washing dyeing and finishing process and a setting process.

Preferably, the bicolor bamboo fiber yarns in the first step are respectively white yarns corresponding to warp yarns and black yarns corresponding to weft yarns.

Preferably, the bamboo fiber yarn in the third step is combined with the warp yarn and the weft yarn by a yarn winding machine.

Preferably, the jacquard forging process in said fourth step is carried out by means of a jacquard machine, operating at a tension comprised between 280 and 330 kg.

Preferably, the jacquard machine processing rotation speed in the fourth step is 540 to 620 revolutions per minute.

Preferably, the operation temperature of the pre-setting process in the fourth step is 140 to 160 degrees.

Preferably, the operation temperature of the water washing dyeing and finishing process in the fourth step is between 120 and 150 ℃.

Preferably, the water washing liquid of the water washing dyeing and finishing process in the fourth step is 3-5% of water solution of the transfer softening and fluffing agent.

Preferably, the operation temperature of the sizing process in the fourth step is 160 to 180 degrees.

Compared with the prior art, the invention has the beneficial effects that: the processing of jacquard weave technology can be realized through warp and weft crisscross, and the moisture absorption effect of surface fabric can be improved to the combination of cooperation bamboo cellosilk and warp and woof, when guaranteeing original resistant wrinkle effect, improves the travelling comfort.

Detailed Description

Example 1

A terylene jacquard fabric and a production method thereof, the terylene jacquard fabric and the production method thereof are as follows:

the first step is as follows: selecting raw materials, wherein warp yarns are 100D/36F polyester white low-stretch yarns, weft yarns are 150D/48F polyester black yarns, and 50D/36F bicolor bamboo fiber yarns;

the second step is that: checking whether the evenness of the raw materials is uniform or not, and checking the color difference condition;

the third step: winding the bicolor bamboo fiber yarns on the warp yarns and the weft yarns respectively;

the fourth step: the processing is completed by a skewering process, a jacquard forging process, a pre-setting process, a washing dyeing and finishing process and a setting process.

The double-color bamboo fiber yarns in the first step are respectively white yarns corresponding to warp yarns and black yarns corresponding to weft yarns.

And the bamboo fiber yarns, the warp yarns and the weft yarns in the third step are processed by a silk thread winding machine in a combined manner.

The jacquard forging process in the fourth step is carried out by means of a jacquard machine, working at a tension of between 280 and 330 kg.

The jacquard machine processing rotation speed in the fourth step is 580 revolutions per minute.

The operation temperature of the pre-setting process in the fourth step was 140 degrees.

The operation temperature of the water washing dyeing and finishing process in the fourth step is 120 ℃.

The water washing liquid of the water washing dyeing and finishing process in the fourth step is 4 percent of water solution of the transfer softening and fluffing agent.

The operation temperature of the setting process in the fourth step is 160 ℃.

Example 2

A terylene jacquard fabric and a production method thereof, the terylene jacquard fabric and the production method thereof are as follows:

the first step is as follows: selecting raw materials, wherein warp yarns are 100D/36F polyester white low-stretch yarns, weft yarns are 150D/48F polyester black yarns, and 50D/36F bicolor bamboo fiber yarns;

the second step is that: checking whether the evenness of the raw materials is uniform or not, and checking the color difference condition;

the third step: winding the bicolor bamboo fiber yarns on the warp yarns and the weft yarns respectively;

the fourth step: the processing is completed by a skewering process, a jacquard forging process, a pre-setting process, a washing dyeing and finishing process and a setting process.

The double-color bamboo fiber yarns in the first step are respectively white yarns corresponding to warp yarns and black yarns corresponding to weft yarns.

And the bamboo fiber yarns, the warp yarns and the weft yarns in the third step are processed by a silk thread winding machine in a combined manner.

The jacquard forging process in the fourth step is carried out by means of a jacquard machine, working at a tension of between 280 and 330 kg.

The processing speed of the jacquard machine in the fourth step is 600 revolutions per minute.

The operation temperature of the pre-setting process in the fourth step is 150 degrees.

The operation temperature of the water washing dyeing and finishing process in the fourth step is 130 ℃.

The water washing liquid of the water washing dyeing and finishing process in the fourth step is 5 percent of water solution of the transfer softening and fluffing agent.

The operation temperature of the setting process in the fourth step is 170 ℃.

Example 3

A terylene jacquard fabric and a production method thereof, the terylene jacquard fabric and the production method thereof are as follows:

the first step is as follows: selecting raw materials, wherein warp yarns are 100D/36F polyester white low-stretch yarns, weft yarns are 150D/48F polyester black yarns, and 50D/36F bicolor bamboo fiber yarns;

the second step is that: checking whether the evenness of the raw materials is uniform or not, and checking the color difference condition;

the third step: winding the bicolor bamboo fiber yarns on the warp yarns and the weft yarns respectively;

the fourth step: the processing is completed by a skewering process, a jacquard forging process, a pre-setting process, a washing dyeing and finishing process and a setting process.

The double-color bamboo fiber yarns in the first step are respectively white yarns corresponding to warp yarns and black yarns corresponding to weft yarns.

And the bamboo fiber yarns, the warp yarns and the weft yarns in the third step are processed by a silk thread winding machine in a combined manner.

The jacquard forging process in the fourth step is carried out by means of a jacquard machine, working at a tension of between 280 and 330 kg.

The jacquard machine processing rotation speed in the fourth step is 570 revolutions per minute.

The operation temperature of the pre-setting process in the fourth step was 145 ℃.

The operation temperature of the water washing dyeing and finishing process in the fourth step is between 125 ℃.

The water washing liquid of the water washing dyeing and finishing process in the fourth step is 4.5 percent of water solution of the transfer softening and fluffing agent.

The operation temperature of the setting process in the fourth step was 165 ℃.