Method for manufacturing cobalt-based alloy layered molded body
阅读说明：本技术 钴基合金层叠造型体的制造方法 (Method for manufacturing cobalt-based alloy layered molded body ) 是由 今野晋也 王玉艇 江口滋信 上村好古 本山宜彦 小牧孝直 于 2018-09-07 设计创作，主要内容包括：为了实现具有与析出增强Ni基合金材同等以上的机械特性的Co基合金材,本发明提供Co基合金层叠造型体的制造方法。本发明涉及的Co基合金层叠造型体的制造方法的特征在于,所述钴基合金具有如下化学组成：包含0.08～0.25质量％的C、0.1质量％以下的B、10～30质量％的Cr、Fe为5质量％以下且合计为30质量％以下的Fe和Ni、合计为5～12质量％的W和/或Mo、合计为0.5～2质量％的Ti、Zr、Nb和Ta、0.5质量％以下的Si、0.5质量％以下的Mn、以及0.003～0.04质量％的N,且余量由Co和杂质构成,所述制造方法具有：合金粉末准备工序、以及选择性激光熔融工序。(The invention provides a method for producing a Co-based alloy laminated molded body, in order to realize a Co-based alloy material having mechanical properties equal to or higher than those of a precipitation-strengthened Ni-based alloy material. The method for producing a Co-based alloy layered product according to the present invention is characterized in that the Co-based alloy has the following chemical composition: the manufacturing method comprises 0.08-0.25 mass% of C, 0.1 mass% or less of B, 10-30 mass% of Cr, 5 mass% or less of Fe and Ni, and 30 mass% or less of W and/or Mo, 5-12 mass% of Ti, Zr, Nb and Ta, 0.5 mass% or less of Si, 0.5 mass% or less of Mn, and 0.003-0.04 mass% of N, wherein the balance is Co and impurities, and the manufacturing method comprises: an alloy powder preparation step and a selective laser melting step.)
1. A method for producing a cobalt-based alloy layered molded article, which is a method for producing a cobalt-based alloy layered molded article,
the cobalt-based alloy has the following chemical composition: contains carbon of 0.08 to 0.25 mass%, boron of 0.1 mass% and chromium of 10 to 30 mass%, contains iron of 5 to 30 mass% and nickel of 30 mass% and the total of the iron and the nickel is 30 mass%, contains tungsten and/or molybdenum of 5 to 12 mass%, contains titanium, zirconium, niobium and tantalum of 0.5 to 2 mass%, contains silicon of 0.5 to 0.5 mass%, manganese of 0.5 to 0.003 to 0.04 mass%, and nitrogen of 0.003 to 0.04 mass%, with the balance consisting of cobalt and impurities,
the manufacturing method comprises the following steps:
an alloy powder preparation step of preparing a cobalt-based alloy powder having the chemical composition; and
a selective laser melting step of repeating an alloy powder bed preparation basic step of preparing an alloy powder bed having a predetermined thickness by laying the cobalt-based alloy powder and a laser melting/solidification basic step of partially melting/rapidly solidifying the cobalt-based alloy powder in a predetermined region of the alloy powder bed by irradiating the region with a laser,
in the selective laser melting step, the predetermined thickness h, the output power P, and the scanning speed S are controlled such that the relationship among the predetermined thickness h of the alloy powder bed, the output power P of the laser, and the scanning speed S of the laser satisfies "15 < h < 150" and "67 (P/S) -3.5 < h < 2222(P/S) + 13", where the unit of the thickness h is μm, the unit of the output power P is W, and the unit of the scanning speed S is mm/S.
2. The method for producing a cobalt-based alloy layered molded body according to claim 1,
the alloy powder preparation step includes an alloy powder classification basic step: the cobalt-based alloy powder is classified into a particle size range of 5 μm or more and 100 μm or less.
3. A method of manufacturing a cobalt-based alloy layered molded body according to claim 1 or 2,
in the chemical composition of the cobalt-based alloy,
0.01 to 1 mass% of titanium,
0.05 to 1.5 mass% of zirconium,
0.02 to 1 mass% of niobium,
The tantalum content is 0.05 mass% or more and 1.5 mass% or less.
4. A method of manufacturing a cobalt-based alloy layered molded body according to claim 1 or 2,
in the chemical composition of the cobalt-based alloy, 0.5 mass% or less of aluminum and 0.04 mass% or less of oxygen are contained as the impurities.
Technical Field
The present invention relates to a cobalt-based alloy material having excellent mechanical properties, and more particularly to a method for producing a layered molded article of a cobalt-based alloy.
Background
Cobalt (Co) based alloy materials, together with nickel (Ni) based alloy materials, are representative heat resistant alloy materials, also referred to as superalloys, and are widely used for high temperature components of steam turbines (e.g., gas turbines, steam turbines). Although the material cost is higher than that of the Ni-based alloy material, the Co-based alloy material is excellent in corrosion resistance and wear resistance and is easily subjected to solid solution strengthening, and thus has been used as turbine vanes and combustor members.
In the heat-resistant alloy material, byIn the conventional improvement of various alloy compositions and the improvement of the manufacturing process, a gamma' -phase (for example, Ni) is developed in the Ni-based alloy material3The (Al, Ti) phase) precipitation is now predominant. On the other hand, in the Co-based alloy material, an intermetallic compound phase that greatly contributes to improvement of mechanical properties, such as a γ' phase of the Ni-based alloy material, is hard to precipitate, and therefore precipitation strengthening by a carbide phase has been studied.
For example, Japanese patent application laid-open No. Sho 61(1986) -243143 discloses a Co-based superplastic alloy characterized by having a matrix of a cobalt-based alloy with a crystal grain size of 10 μm or less and by precipitating massive and granular carbides with a grain size of 0.5 to 10 μm. Further, it is disclosed that the above cobalt-based alloy is formed of, in terms of a weight ratio of C: 0.15-1%, Cr: 15-40%, W and or Mo: 3-15%, B: 1% or less, Ni: 0-20%, Nb: 0-1.0%, Zr: 0-1.0%, Ta: 0-1.0%, Ti: 0-3%, Al: 0 to 3%, and the balance Co. According to patent document 1, a Co-based superplastic alloy can be provided which exhibits superplasticity even in a low temperature region (for example, 950 ℃) and has an elongation of 70% or more, and which can be formed into a complex-shaped article by plastic working such as forging.
In Japanese patent laid-open No. Hei 7(1995) -179967, a Co-based alloy is disclosed which is composed of, in wt%: 21-29%, Mo: 15-24%, B: 0.5-2%, Si: 0.1% or more and less than 0.5%, C: more than 1% and 2% or less, Fe: 2% or less, Ni: 2% or less and the balance substantially consisting of Co, and is excellent in corrosion resistance, wear resistance and high-temperature strength. According to patent document 2, the Co-based alloy has a composite structure in which molybdenum boride and chromium carbide are relatively finely dispersed in a quaternary alloy phase of Co, Cr, Mo, and Si, and has good corrosion resistance, wear resistance, and high strength.
In recent years, as a technique for Manufacturing a final product having a complicated shape by a near net shape (near net shape), a three-dimensional molding technique (so-called 3D printing) such as an Additive Manufacturing (AM) method has been attracting attention, and the three-dimensional molding technique has been actively developed to be applied to a heat-resistant alloy member.
For example, Japanese patent laid-open No. 2016 (WO2015/073081A 1) discloses a method for forming a layer comprising a) a step of supplying a raw material for a particulate composite material in a powder or suspension state having a porosity of less than 20%; b) depositing a first portion of the composite material on a target surface; c) a step of forming a first layer by supplying energy to the composite material of the first portion and sintering, fusing, or melting the composite material of the first portion; d) depositing a second portion of said composite material over said first layer; e) a step of forming a second layer by supplying energy to the composite material of the second portion and sintering, fusing, or melting the composite material of the second portion; the energy is supplied by a laser.
According to Japanese patent laid-open No. 2016-535169, selective laser melting (SLM method) or direct metal laser melting (DMLM method) is generally useful for one material (pure titanium, a single alloy such as Ti-6 Al-4V). In contrast, in the case of a plurality of materials, alloys, or combinations of alloys with other materials such as plastics, ceramics, polymers, carbides, glass, etc., the selective laser sintering method (SLS method) or the direct metal laser sintering method (DMLS method) is generally applicable. It should be noted that sintering is a technical concept different from melting, and the sintering process is as follows: a process that does not completely melt the material powder, but heats it to such an extent that the powders can fuse together at the molecular level.
Disclosure of Invention
Problems to be solved by the invention
Since a high-temperature steam turbine component can be directly molded even in a component having a complicated shape in the production of the high-temperature steam turbine component by 3D printing, the production method is an attractive technique from the viewpoint of shortening the production time and improving the production yield (that is, from the viewpoint of reducing the production cost).
The Co-based alloy materials described in Japanese Kokai publication Sho-61 (1986) -243143 and Japanese Kokai publication Hei-7 (1995) -179967 are considered to have higher mechanical properties than those of conventional Co-based alloy materials, but unfortunately, they cannot be said to have sufficient mechanical properties than the precipitation-strengthened Ni-based alloy materials in recent years. Therefore, in the past, studies on laminated molded bodies (AM bodies) for high-temperature components of steam turbines have been conducted on precipitation-strengthened Ni-based alloy materials in many cases.
However, AM bodies of precipitation-strengthened Ni-based alloys are likely to have problems in that the formation of γ' phase, which is critical for mechanical properties, is inhibited, or internal defects are generated in the product, and as a result, the expected mechanical properties cannot be sufficiently obtained. This is considered to be because: since precipitation-strengthened Ni-based alloy materials currently used as high-temperature components of steam turbines are optimized on the premise of melting and casting processes in high vacuum, oxidation and nitridation of Al components and Ti components constituting γ' phases are likely to occur at the stage of preparing alloy powders for AM methods and at the stage of AM methods.
On the other hand, since the Co-based alloy materials described in jp 61(1986) -243143 and jp 7(1995) -179967 do not assume precipitation of an intermetallic compound phase such as a γ' phase of the Ni-based alloy material, they do not contain a large amount of Al and Ti which are easily oxidized, and thus a melting and casting process in the air can be used. Therefore, it is considered advantageous for the production of the alloy powder for AM method and the production of the AM body. In addition, the Co-based alloy material has the following advantages: has corrosion resistance and wear resistance equal to or higher than those of Ni-based alloy materials.
However, as described above, the conventional Co-based alloy material has a disadvantage of having lower mechanical properties than the γ' -phase precipitation-strengthened Ni-based alloy material. In other words, if mechanical properties equivalent to or higher than those of γ' phase precipitation-strengthened Ni-based alloy materials can be achieved (for example, the creep rupture temperature at 58MPa for 10 ten thousand hours is 875 ℃ or higher, and the tensile strength at room temperature is 500MPa or higher), the Co-based alloy AM body can be a very attractive high-temperature turbine component.
The present invention has been made in view of the above-mentioned problems, and an object thereof is to: a method for producing a Co-based alloy laminated molded body, in order to realize a Co-based alloy material having mechanical properties equal to or higher than those of a precipitation-strengthened Ni-based alloy material.
Means for solving the problems
(I) One aspect of the present invention provides a method for producing a Co-based alloy laminated molded article, the method comprising forming a Co-based alloy layer on a substrate,
the above-mentioned Co-based alloy has the following chemical composition: contains carbon (C) of 0.08 to 0.25 mass%, boron (B) of 0.1 mass%, chromium (Cr) of 10 to 30 mass%, iron (Fe) of 5 to 30 mass%, iron (Fe) and nickel (Ni) in total, tungsten (W) and/or molybdenum (Mo) of 5 to 12 mass%, titanium (Ti), zirconium (Zr), niobium (Nb) and tantalum (Ta) of 0.5 to 2 mass%, silicon (Si) of 0.5 mass%, manganese (Mn) of 0.5 mass%, and nitrogen (N) of 0.003 to 0.04 mass%, with the balance being Co and impurities,
the manufacturing method comprises the following steps:
an alloy powder preparation step of preparing a Co-based alloy powder having the above chemical composition; and
a Selective Laser Melting (SLM) step of repeating an alloy powder bed preparation basic step of preparing an alloy powder bed having a predetermined thickness by laying the Co-based alloy powder and a laser melting/solidification basic step of partially melting/rapidly solidifying the Co-based alloy powder in a predetermined region of the alloy powder bed by irradiating the Co-based alloy powder in the alloy powder bed with a laser,
in the SLM step, the predetermined thickness h, the output power P, and the scanning speed S of the alloy powder bed are controlled so that the relationship among the predetermined thickness h (unit: μm), the output power P (unit: W), and the scanning speed S (unit: mm/S) of the laser satisfies "15 < h < 150" and "67 (P/S) -3.5 < h < 2222(P/S) + 13".
The present invention can be modified or modified as described below in the above-mentioned method (I) for producing a Co-based alloy layered molded article.
(i) The alloy powder preparation step includes an alloy powder classification basic step: the Co-based alloy powder is classified into a particle size range of 5 μm or more and 100 μm or less.
(ii) In the chemical composition of the Co-based alloy, the Ti is 0.01 mass% or more and 1 mass% or less, the Zr is 0.05 mass% or more and 1.5 mass% or less, the Nb is 0.02 mass% or more and 1 mass% or less, and the Ta is 0.05 mass% or more and 1.5 mass% or less.
(iii) In the chemical composition of the Co-based alloy, the impurities include 0.5 mass% or less of aluminum (Al) and 0.04 mass% or less of oxygen (O).
Effects of the invention
According to the present invention, a method for producing a Co-based alloy laminated molded body can be provided for realizing a Co-based alloy material having mechanical properties equal to or higher than those of a precipitation-strengthened Ni-based alloy material.
Drawings
Fig. 1 is a flowchart showing a process example of a method for producing a Co-based alloy product according to the present invention.
Fig. 2 is a Scanning Electron Microscope (SEM) observation image showing an example of the microstructure of the Co-based alloy AM body according to the present invention.
Fig. 3 is a schematic perspective view showing a turbine stator blade as a high-temperature component of a turbine, which is an example of a Co-based alloy product according to the present invention.
FIG. 4 is a schematic cross-sectional view showing an example of a gas turbine equipped with a Co-based alloy product according to the present invention.
Fig. 5 is an SEM observation image showing an example of the microstructure of the Co-based alloy AM body formed by the laser metal deposition method (LMD method).
Fig. 6 is an SEM observation image showing an example of the microstructure of a Co-based alloy cast body formed by the precision casting method.
Fig. 7 is a graph showing an example of the relationship between the average size of segregation units in the AM body of the Co-based alloy and the 0.2% proof stress of the Co-based alloy product.
Fig. 8 is an SLM condition example for obtaining a Co-based alloy AM body according to the present invention, and is a graph showing a relationship between a thickness of an alloy powder bed and a local heat input amount.
Detailed Description
[ basic idea of the invention ]
As described above, various developments have been made on the enhancement of the Co-based alloy material by the precipitation of the carbide phase. Examples of the carbide phase contributing to precipitation strengthening include MC type carbide phases of Ti, Zr, Nb, and Ta, and composite carbide phases of these metal elements.
Each of Ti, Zr, Nb, and Ta and C, which is indispensable for forming a carbide phase, has a characteristic of being significantly segregated in a final solidification portion (for example, dendrite boundaries or crystal grain boundaries) when the Co-based alloy is melted and solidified. Therefore, in the conventional Co-based alloy material, the carbide phase particles are precipitated along the dendrite boundaries and the crystal grain boundaries of the matrix phase. For example, in a common casting material of a Co-based alloy, the average spacing of dendrite boundaries and the average crystal grain size are generally 101～102Of the order of μm, so that the mean spacing of the carbide phase particles is also 101～102In the order of μm. Even in a process such as laser welding in which the solidification rate is high, the average interval of carbide phase particles in the solidified portion is about 5 μm.
It is known that the precipitation strengthening in an alloy is generally inversely proportional to the average interval between precipitates, and it is said that the precipitation strengthening is effective when the average interval between precipitates is about 2 μm or less. However, in the above-mentioned conventional techniques, the average interval between precipitates does not reach this level, and a sufficient effect of enhancing the precipitates cannot be obtained. In other words, in the conventional technique, it is difficult to finely disperse and precipitate carbide phase particles contributing to the reinforcement of the alloy. This is a factor that is considered to cause insufficient mechanical properties of the Co-based alloy material as compared with the precipitation-strengthened Ni-based alloy material.
As another carbide phase that can be precipitated in the Co-based alloy, there is a Cr carbide phase. Since the Cr component has high solid solubility in the Co-based alloy matrix phase and is difficult to segregate, the Cr carbide phase can be dispersed and precipitated in the matrix phase grains. However, it is known that the lattice matching of the Cr carbide phase with the Co-based alloy matrix phase crystals is low and not as effective as the precipitation-strengthening phase.
The present inventors have considered that if carbide phase particles contributing to precipitation strengthening are dispersed and precipitated in the matrix phase grains in a Co-based alloy material, the mechanical properties of the Co-based alloy material can be dramatically improved. Further, it is considered that if the alloy material has both of the corrosion resistance and the wear resistance which are originally excellent in the Co-based alloy material, a heat-resistant alloy material superior to the precipitation-strengthened Ni-based alloy material can be provided.
Therefore, the present inventors have conducted extensive studies on an alloy composition and a production method for obtaining such a Co-based alloy material. As a result, it has been found that carbide phase particles contributing to alloy reinforcement are dispersed and precipitated in the matrix phase grains of a Co-based alloy material by optimizing the alloy composition and controlling the heat input for local melting/rapid solidification in the production by the AM method (particularly, the selective laser melting method) to be within a predetermined range. The present invention has been completed based on this finding.
Hereinafter, embodiments according to the present invention will be described in accordance with manufacturing steps with reference to the drawings. However, the present invention is not limited to the embodiments described herein, and may be appropriately combined with or modified based on a known technique without departing from the technical spirit of the present invention.
[ Co-based alloy laminated molded article/Co-based alloy product manufacturing method ]
Fig. 1 is a flowchart showing a process example of a method for producing a Co-based alloy product according to the present invention. As shown in fig. 1, the method for producing a Co-based alloy product according to the present invention roughly includes the steps of: an alloy powder preparation step (S1) for preparing a Co-based alloy powder; a selective laser melting step (S2) for forming an AM body of a desired shape using the prepared Co-based alloy powder; a melting heat treatment step (S3) for melting the formed AM body; and an aging heat treatment step (S4) for aging the AM body subjected to the melt treatment. The AM body obtained in the selective laser melting step S2 is a Co-based alloy layer multilayer molded body according to the present invention.
Hereinafter, each step will be described in more detail.
(preparation of alloy powder)
This step S1 is a step of preparing Co-based alloy powder having a predetermined chemical composition. The chemical composition preferably contains 0.08 to 0.25 mass% of C, 0.1 mass% of B, 10 to 30 mass% of Cr, 5 to 30 mass% of Fe and Ni in total, 5 to 12 mass% of W and/or Mo in total, 0.5 to 2 mass% of Ti, Zr, Nb, and Ta in total, 0.5 to 0.5 mass% of Si, 0.5 to 0.5 mass% of Mn, and 0.003 to 0.04 mass% of N, with the balance being made up of Co and impurities.
C: 0.08 to 0.25 mass%
The C component is an important component constituting an MC type carbide phase (sometimes referred to as a carbide phase containing at least one of Ti, Zr, Nb, and Ta, or a reinforced carbide phase) as a precipitation-strengthened phase. The content of the component C is preferably 0.08 to 0.25 mass%, more preferably 0.1 to 0.2 mass%, and still more preferably 0.12 to 0.18 mass%. If the content of C is less than 0.08% by mass, the amount of precipitated reinforcing carbide phase is insufficient, and the effect of improving mechanical properties cannot be sufficiently obtained. On the other hand, if the C content exceeds 0.25 mass%, the C is excessively cured, and the ductility and toughness of the alloy material are reduced.
B: 0.1% by mass or less
The component B is a component contributing to improvement of the bonding property at crystal grain boundaries (so-called grain boundary strengthening). The component B is not essential, but when contained, it is preferably 0.1% by mass or less, more preferably 0.005% by mass or more and 0.05% by mass or less. If the B content exceeds 0.1 mass%, cracks (for example, solidification cracks) are likely to occur at the time of formation of the AM body.
Cr: 10 to 30 mass% inclusive
The Cr component contributes to improvement of corrosion resistance and oxidation resistance. The content of the Cr component is preferably 10 mass% or more and 30 mass% or less, and more preferably 10 mass% or more and 25 mass% or less. When a corrosion-resistant coating layer is separately provided on the outermost surface of the Co-based alloy product, the content of the Cr component is more preferably 10 mass% or more and 18 mass% or less. If the Cr content is less than 10% by mass, the corrosion resistance and oxidation resistance become insufficient. On the other hand, if the Cr content exceeds 30 mass%, a brittle σ phase or Cr carbide phase is formed, and mechanical properties (toughness, ductility, strength) are degraded.
Ni: 30 mass% or less
Since the Ni component has characteristics similar to those of the Co component and is less expensive than Co, it is a component that can be contained in a form of replacing a part of the Co component. The Ni component is not an essential component, but when contained, it is preferably 30 mass% or less, more preferably 20 mass% or less, and further preferably 5 mass% or more and 15 mass% or less. If the Ni content exceeds 30 mass%, wear resistance and resistance to local stress, which are characteristics of the Co-based alloy, decrease. This is considered to be due to the difference between the lamination defect energy of Co and the lamination defect energy of Ni.
Fe: 5% by mass or less
Since the Fe component is much cheaper than Ni and has similar characteristics to the Ni component, it is a component that can be contained in a form of replacing a part of the Ni component. That is, the total content of Fe and Ni is preferably 30 mass% or less, more preferably 20 mass% or less, and further preferably 5 mass% or more and 15 mass% or less. The Fe component is not an essential component, but when contained, it is preferably 5 mass% or less, more preferably 3 mass% or less within a range smaller than the Ni content. If the Fe content exceeds 5 mass%, the corrosion resistance and mechanical properties deteriorate.
W and/or Mo: 5 to 12 mass% in total
The W component and the Mo component contribute to solid solution strengthening of the matrix phase. The total content of the W component and/or the Mo component is preferably 5 mass% or more and 12 mass% or less, and more preferably 7 mass% or more and 10 mass% or less. If the total content of the W component and the Mo component is less than 5% by mass, the solid solution strengthening of the matrix phase becomes insufficient. On the other hand, if the total content of the W component and the Mo component exceeds 12 mass%, a brittle σ phase is easily generated, and mechanical properties (toughness and ductility) are degraded.
Re: 2 mass% or less
The Re component is a component contributing to solid solution strengthening of the matrix phase and also contributing to improvement of corrosion resistance. The Re component is not essential, but when contained, it is preferably 2 mass% or less, more preferably 0.5 mass% or more and 1.5 mass% or less, in place of a part of the W component or the Mo component. If the Re content exceeds 2 mass%, the effects of the Re component are saturated, and the increase in material cost is also a disadvantage.
Ti, Zr, Nb, and Ta: 0.5 to 2 mass% in total
The Ti component, Zr component, Nb component, and Ta component are important components constituting the reinforced carbide phase (MC type carbide phase). The total content of the Ti, Zr, Nb, and Ta components is preferably 0.5 mass% or more and 2 mass% or less, and more preferably 0.5 mass% or more and 1.8 mass% or less. If the total content is less than 0.5% by mass, the amount of precipitated reinforcing carbide phase is insufficient, and the effect of improving mechanical properties cannot be sufficiently obtained. On the other hand, if the total content exceeds 2 mass%, the reinforcing carbide phase particles are coarsened, the generation of a brittle phase (for example, a σ phase) is promoted, or oxide phase particles that do not contribute to precipitation strengthening are generated, and the mechanical properties are degraded.
More specifically, the Ti content is preferably 0.01 mass% or more and 1 mass% or less, and more preferably 0.05 mass% or more and 0.8 mass% or less. The Zr content is preferably 0.05 mass% or more and 1.5 mass% or less, and more preferably 0.1 mass% or more and 1.2 mass% or less. The Nb content is preferably 0.02 mass% or more and 1 mass% or less, and more preferably 0.05 mass% or more and 0.8 mass% or less. The Ta content is preferably 0.05 mass% or more and 1.5 mass% or less, and more preferably 0.1 mass% or more and 1.2 mass% or less.
Si: 0.5% by mass or less
The Si component plays a role of deoxidation and contributes to improvement of mechanical characteristics. The Si component is not an essential component, but when contained, it is preferably 0.5 mass% or less, more preferably 0.01 mass% or more and 0.3 mass% or less. If the Si content exceeds 0.5 mass%, an oxide (e.g., SiO) is formed2) The coarse particles of (2) become a factor of lowering mechanical properties.
Mn: 0.5% by mass or less
The Mn component plays a role in deoxidation and desulfurization, and contributes to improvement of mechanical properties and improvement of corrosion resistance. The Mn component is not an essential component, but when contained, it is preferably 0.5% by mass or less, more preferably 0.01% by mass or more and 0.3% by mass or less. If the Mn content exceeds 0.5 mass%, coarse particles of sulfide (e.g., MnS) are formed, which causes a reduction in mechanical properties and corrosion resistance.
N: 0.003-0.04 mass%
The N component is a component contributing to enhancement of stable generation of the carbide phase. The content of the N component is preferably 0.003 mass% or more and 0.04 mass% or less, more preferably 0.005 mass% or more and 0.03 mass% or less, and further preferably 0.007 mass% or more and 0.025 mass% or less. If the N content is less than 0.003 mass%, the effect of the N component cannot be sufficiently obtained. On the other hand, if the N content exceeds 0.04 mass%, coarse particles of nitrides (e.g., Cr nitrides) are formed, which causes a reduction in mechanical properties.
And the balance: co component + impurities
The Co component is one of the main components of the present alloy, and is a component having the maximum content. As described above, the Co-based alloy material has the following advantages: has corrosion resistance and wear resistance equal to or higher than those of Ni-based alloy materials.
The Al component is one of impurities of the present alloy, and is not an intentionally contained component. However, if the Al content is 0.5 mass% or less, the mechanical properties of the Co-based alloy product will not be increasedAnd therefore allowable. If the Al content exceeds 0.5 mass%, an oxide or nitride (e.g., Al) is formed2O3AlN) becomes a factor of reducing mechanical properties.
The O component is also one of impurities of the present alloy, and is not an intentionally contained component. However, if the content of O is 0.04 mass% or less, it is allowable because it does not largely adversely affect the mechanical properties of the Co-based alloy product. If the O content exceeds 0.04 mass%, coarse particles of various oxides (for example, Ti oxide, Zr oxide, Al oxide, Fe oxide, Si oxide) are formed, which causes a reduction in mechanical properties.
In step S1, the method and technique for preparing the Co-based alloy powder are not particularly limited, and conventional methods and techniques can be used. For example, the following steps may be performed: a master alloy block production basic step (S1a) of mixing, melting, and casting raw materials so as to have a desired chemical composition to produce a master alloy block (master ingot); and an atomization step (S1b) for forming an alloy powder from the master alloy ingot. The atomization method is also not particularly limited, and conventional methods and methods can be used. For example, an air atomization method or a centrifugal atomization method which can obtain high-purity, homogeneous composition, and spherical particles can be preferably used.
From the viewpoint of operability in the selective laser melting step S2 in the next step and the packing property of the alloy powder bed, the particle size of the alloy powder is preferably 5 μm or more and 100 μm or less, more preferably 10 μm or more and 70 μm or less, and still more preferably 10 μm or more and 50 μm or less. If the particle diameter of the alloy powder is less than 5 μm, the fluidity of the alloy powder is lowered (the formability of the alloy powder bed is lowered) in the next step S2, which causes a reduction in the shape accuracy of the AM body. On the other hand, if the particle diameter of the alloy powder exceeds 100 μm, it becomes difficult to control local melting and rapid solidification of the alloy powder bed, insufficient melting of the alloy powder, or increase in surface roughness of the AM body in the next step S2.
As described above, the alloy powder classification basic step (S1c) is preferably performed: the alloy powder is classified into a particle size of 5 μm or more and 100 μm or less. In the present invention, when the particle size distribution of the alloy powder produced in the atomization basic step S1b was measured and it was confirmed that the particle size distribution was within a desired range, the basic step S1c was considered to have been performed.
(Selective laser melting Process)
This step S2 is a step of forming an AM body of a desired shape by a Selective Laser Melting (SLM) method using the prepared Co-based alloy powder. Specifically, in order to form an AM body by repeating an alloy powder bed preparation basic process (S2a) and a laser melting solidification basic process (S2b), a Co-based alloy powder is laid to prepare an alloy powder bed having a predetermined thickness in the alloy powder bed preparation basic process (S2a), and a laser is irradiated to a predetermined region of the alloy powder bed to partially melt and rapidly solidify the Co-based alloy powder in the region in the laser melting solidification basic process (S2 b).
In step S2, the microstructure of the AM body, which is a precursor of the final product of the Co-based alloy, is controlled so as to obtain a desired microstructure (a microstructure in which reinforcing carbide phase particles are dispersed and precipitated in the mother phase grains). In order to control the microstructure of the AM body, local melting and rapid solidification of the alloy powder bed are controlled.
More specifically, it is preferable to control the thickness h of the alloy powder bed, the laser output power P and the laser scanning speed S so as to satisfy "15 < h < 150" and "67 (P/S) -3.5 < h < 2222(P/S) + 13" in relation to the thickness h (unit: μm), the laser output power P (unit: W) and the scanning speed S (unit: mm/S) of the laser. If the control conditions are deviated from the above-described control conditions, an AM body having a desired microstructure cannot be obtained. In step S2, the Co-based alloy AM body according to the present invention can be obtained.
The output power P of the laser and the scanning speed S of the laser basically depend on the configuration of the laser device, and may be selected from the range of "10 ≦ P ≦ 1000" and "10 ≦ S ≦ 7000", for example.
(Co-based alloy layered molding)
Fig. 2 is a Scanning Electron Microscope (SEM) observation image showing an example of the microstructure of the Co-based alloy AM body according to the present invention. As shown in fig. 2, the Co-based alloy AM body of the present invention has a very excellent microstructure which has not been found so far.
The AM body is a polycrystalline body having an average crystal grain diameter of 10 to 100 [ mu ] m, and segregation units having an average size of 0.15 to 1.5 [ mu ] m are formed in the grains of the polycrystalline body. Further, particles in which the reinforcing carbide phase is precipitated at an average interval of 0.15 μm or more and 1.5 μm or less. In the present invention, the size of the segregation unit is defined as the average of the major axis and the minor axis.
As a result of further detailed observation of the microstructure using transmission electron microscopy-energy dispersive X-ray spectrometry (TEM-EDX), it was confirmed that in the segregation cells, the components (Ti, Zr, Nb, Ta, C) forming the reinforced carbide phase segregated in the boundary regions between the microcells (the outer peripheral regions of the microcells, the regions such as cell walls). Further, it was confirmed that particles of the reinforced carbide phase were precipitated in a part of the triple point/quadruple point in the boundary region of the segregation cell.
(melting Heat treatment Process)
This step S3 is a step of melting the formed Co-based alloy AM body. The conditions for the melting treatment are preferably heat treatment in which the temperature range of 1100 ℃ to 1200 ℃ is 0.5 hour to 10 hours inclusive. The cooling method after the heat treatment is not particularly limited, and may be any of water cooling, oil cooling, air cooling, and furnace cooling.
By performing the melting treatment, recrystallization of the mother phase crystal grains can be generated in the AM body, and the internal strain of the AM body generated at the time of rapid solidification can be alleviated. It is preferable that the average crystal grain size of the mother phase crystal grains is coarsened by recrystallization to be in a range of 20 μm to 145 μm. If the average crystal grain size is less than 20 μm or exceeds 145 μm, sufficient creep characteristics are not obtained in the final Co-based alloy fabricated product.
Furthermore, it is known that, when the mother phase crystal grains are recrystallized, components segregated in the boundary regions of the former segregation units aggregate to start forming a reinforced carbide phase, and as a result, the segregation units disappear (more precisely, the segregation units are not confirmed by SEM observation). The aggregation point at which the reinforced carbide phase starts to form is considered to be the position of triple point/quadruple point of the primary segregation unit boundary, and is considered to be in a state of being finely distributed in the entire matrix crystal grains (in-grain and on the crystal grain boundary).
By appropriately controlling the temperature conditions and the holding time conditions of the heat treatment for melting, the reinforcing carbide phase that has started to be formed can be grown in the form of particles without being aggregated and coarsened. In this case, the Co-based alloy product may be completed in step S3. However, from the viewpoint of controlling coarsening of the mother phase crystal grains (in other words, from the viewpoint of production stability and production yield), the following aging heat treatment step S4 is more preferably performed.
(aging Heat treatment Process)
In step S4, aging treatment is performed on the Co-based alloy AM body subjected to the melting treatment. The aging treatment conditions are preferably heat treatment in which the temperature range of 750 ℃ to 1000 ℃ is 0.5 to 10 hours. The cooling method after the heat treatment is not particularly limited, and may be any of water cooling, oil cooling, air cooling, and furnace cooling.
By performing the aging treatment, the reinforcing carbide phase formed at the start of the heat treatment step S3 for melting can be grown in the form of particles while suppressing excessive coarsening of the mother phase crystal grains. As a result, a Co-based alloy product can be obtained in which the average crystal grain size of the matrix crystal grains is 20 to 145 μm, the reinforcing carbide phase particles are finely dispersed and precipitated in each crystal grain, and the average inter-particle distance of the reinforcing carbide phase particles is 0.15 to 1.5 μm. In the Co-based alloy product of the present invention, it is needless to say that the reinforcing carbide phase particles are dispersed and precipitated also in the grain boundaries of the matrix crystal grains.
(finishing Process)
Although not shown in fig. 1, the Co-based alloy product obtained in the melting heat treatment step S3 and the aging heat treatment step S4 may be further subjected to a step of forming a corrosion-resistant coating layer and a step of surface finishing, as necessary.
[ Co-based alloy product ]
Fig. 3 is a schematic perspective view of a turbine stator blade as a high-temperature component of a turbine, which is an example of a Co-based alloy product according to the present invention. As shown in fig. 3, the turbine vane 100 is roughly composed of an inner ring-side end wall 101, a blade section 102, and an outer ring-side end wall 103. A cooling structure is often formed inside the blade portion. As described above, since the turbine stator blade 100 has a very complicated shape and structure, the technical significance of the AM body formed by the near-net shape and the alloy product based on the AM body is significant.
For example, in a power generation gas turbine having an output of 30MW, the length of the blade portion (distance between both end walls) of the turbine stator blade is about 170 mm.
FIG. 4 is a schematic cross-sectional view showing an example of a gas turbine equipped with a Co-based alloy product according to the present invention. As shown in fig. 4, the gas turbine 200 is roughly composed of a compressor section 210 that compresses intake air and a turbine section 220 that blows combustion gas of fuel to turbine blades to obtain rotational power. The high-temperature turbine component of the present invention can be suitably used as the turbine nozzle 221 and the turbine stator blade 100 in the turbine portion 220. Of course, the high-temperature turbine member of the present invention is not limited to the use in a gas turbine, and may be used in other turbine applications (for example, steam turbine applications).
Examples
The present invention will be described in more detail below with reference to examples and comparative examples. It should be noted that the present invention is not limited to these examples.
[ experiment 1]
(preparation of alloy powders IA-1 to IA-5 and CA-1 to CA-5)
Co-based alloy powders having chemical compositions shown in table 1 were prepared (alloy powder preparation step S1). More specifically, first, a master alloy block production basic step S1a is performed: after mixing the raw materials, the mixture was melted and cast by vacuum high-frequency induction melting to prepare a master alloy ingot (mass: about 2 kg). Next, the atomization basic process S1b is performed: the master alloy ingot was remelted and an alloy powder was formed by a gas atomization method in an argon atmosphere.
Next, the obtained alloy powders are subjected to an alloy powder classification basic step S1c for controlling the particle diameter. In this case, an alloy powder (particle size S) having a powder particle size in the range of 10 to 25 μm and an alloy powder (particle size L) having a powder particle size in the range of 100 to 150 μm are prepared.
TABLE 1 chemical compositions of inventive alloy powders IA-1 to IA-5 and comparative alloy powders CA-1 to CA-5
Means not intentionally containing, or not detecting
Bal containing impurities other than Al and O
As shown in Table 1, alloy powders IA-1 to IA-5 are alloy powders having chemical compositions satisfying the requirements of the present invention. On the other hand, with respect to the alloy powder CA-1, the C content and the Cr content deviate from the specification of the present invention. In the alloy powder CA-2, the C content, Ni content, and the total content of "Ti + Zr + Nb + Ta" deviate from the definition of the present invention. In the alloy powder CA-3, the N content and the total content of "Ti + Zr + Nb + Ta" deviate from the definition of the present invention. The total content of "Ti + Zr + Nb + Ta" in the alloy powder CA-4 deviates from the specification of the present invention. In the alloy powder CA-5, the W content and the total content of "Ti + Zr + Nb + Ta" deviate from the definition of the present invention.
[ experiment 2]
(production of SLM alloy product Using IA-2 powder and SLM alloy product Using CA-5 powder)
AM bodies (8 mm in diameter. times.10 mm in height) were formed by the SLM method using alloy powders of IA-2 and CA-5 having a particle size S prepared in experiment 1 (selective laser melting step S2). The SLM conditions were controlled by variously changing the scanning speed S (mm/S) of the laser beam with the thickness h of the alloy powder bed set to 100 μm and the output power P of the laser beam set to 100W (unit: W · S/mm ═ J/mm). The control of the local heat input amount corresponds to the control of the cooling rate.
Each AM body produced as described above was subjected to heat treatment for 4 hours at 1150 ℃ (melt heat treatment step S3). Subsequently, each AM body subjected to the melting treatment was subjected to a heat treatment of holding at 900 ℃ for 4 hours (aging heat treatment step S4), and an SLM alloy product using IA-2 powder and an SLM alloy product using CA-5 powder were produced.
(preparation of LMD alloy product Using IA-2 powder and LMD alloy product Using CA-5 powder)
Using alloy powders of IA-2 and CA-5 having a particle size L prepared in experiment 1, AM bodies were formed by a laser metal deposition method (LMD method), and the same melting heat treatment step S3 and aging heat treatment step S4 were performed to prepare LMD alloy products using IA-2 powder and LMD alloy products using CA-5 powder. For the LMD conditions, the output power P of the laser beam was set to 800W, and the scanning speed S of the laser beam was set to 15 mm/S.
The LMD method is one of the AM methods, and is a method of performing lamination molding by simultaneously performing alloy powder introduction and laser irradiation. The local heat input of the LMD method is generally greater than the local heat input of the SLM method. In other words, the cooling rate in the LMD method is slower than that of the SLM method.
(production of cast alloy product Using IA-2 powder and cast alloy product Using CA-5 powder)
A cast body (diameter: 8 mm. times. height: 10mm) was formed by precision casting using alloy powders of IA-2 and CA-5 having a particle size L prepared in experiment 1, and the same melting heat treatment step S3 and aging heat treatment step S4 were performed to produce a cast alloy product using the IA-2 powder and a cast alloy product using the CA-5 powder.
(microstructure observation and mechanical Property test)
From the AM body, the cast body, and the product produced as described above, a test piece for microstructure observation and a test piece for mechanical property test were taken, and microstructure observation and mechanical property test were performed.
The microstructure observation was performed by SEM. The obtained SEM observation image was subjected to image analysis using image processing software (public software developed by ImageJ, National Institutes of Health (NIH)), so as to measure the average size of the segregation units, the average interval of the microsegregation, and the average grain spacing of the carbide phase grains.
As the mechanical property test, a tensile test was conducted in a room temperature environment (about 23 ℃ C.) to measure a 0.2% proof stress.
Fig. 5 is an SEM observation image showing an example of the microstructure of an AM body of a Co-based alloy formed by the LMD method, and fig. 6 is an SEM observation image showing an example of the microstructure of a cast body of a Co-based alloy formed by the precision casting method. Fig. 2 shown above is an SEM observation image showing an example of the microstructure of the AM body of the Co-based alloy formed by the SLM method. In the samples shown in FIGS. 2 and 5 to 6, IA-2 was used as the alloy powder.
As described above, regarding the AM body formed by the SLM method (see fig. 2), segregation units having a size of about 1 μm are formed in the grains of the polycrystalline body. In contrast, in the AM body formed by the LMD method (see fig. 5), each crystal grain of the polycrystalline body is composed of segregation units having a size of about 5 to 20 μm. In the case of a cast product formed by the precision casting method (see fig. 6), micro segregation is observed along the dendrite boundaries, and the intervals of the micro segregation are about 100 to 300 μm.
As a result of observing the microstructure of the product produced by subjecting the AM body and the cast body to the solution treatment and the aging treatment, and measuring the average grain spacing of the carbide phase grains, it was found that the average grain spacing substantially coincides with the average size of the segregation cell and the average interval of the micro segregation (the microstructure is not shown). It is also known that when the average size of the segregation units is extremely small (for example, when the average size is about 0.1 μm or less), adjacent carbide phases are bonded to each other by the melt-aging treatment to form large particles (as a result, the average inter-particle distance of the carbide phase particles is enlarged).
Since products having greatly different microstructures were obtained, the relationship between the average size of the segregation cell and the mechanical properties was examined. Fig. 7 is a graph showing an example of the relationship between the average size of segregation units in the AM body of the Co-based alloy and the 0.2% proof stress of the Co-based alloy product. Fig. 7 also shows data of the cast body and the cast alloy manufacture for comparison. In the cast body, the average size of the segregation units is replaced with the average interval of the micro-segregation.
As shown in fig. 7, the Co-based alloy product produced using the CA-5 powder showed an almost constant 0.2% proof stress without being affected by the average size of the segregation units. On the other hand, in the Co-based alloy product produced using the IA-2 powder, the 0.2% proof stress greatly changes depending on the average size of the segregation units.
The CA-5 powder contained too little (almost no) of the total content of "Ti + Zr + Nb + Ta". Therefore, the product using the CA-5 powder had a microstructure in which the reinforcing carbide phase was not precipitated but Cr carbide particles were precipitated. From the results, it was confirmed that Cr carbide particles are not as effective as precipitation-strengthened particles. On the other hand, the product using the IA-2 powder had a fine structure that enhanced the precipitation of carbide phase particles. Therefore, it is considered that the 0.2% proof stress largely varies depending on the average size of the segregation units (as a result, the average inter-particle distance of carbide phase particles).
In addition, if the required characteristics of the present invention for the target high-temperature steam turbine member are taken into consideration, the 0.2% proof stress must be 500MPa or more. Therefore, if the 0.2% proof stress of 500MPa or more is determined as "pass" and if the proof stress of less than 500MPa is determined as "fail", the following are confirmed: the mechanical properties of the product are "acceptable" when the average size of the segregation units (the average inter-particle distance of carbide phase particles as a result) is in the range of 0.15 to 1.5 μm. In other words, one of the factors that do not provide sufficient mechanical properties in conventional carbide-phase-precipitated Co-based alloy materials is thought to be because the average interparticle distance of the reinforcing carbide-phase particles cannot be controlled within a desired range.
[ experiment 3]
(production of SLM alloy products IP-1-1 to IP-5-1 using IA-1 to IA-5 powders and SLM alloy products CP-1-1 to CP-5-1 using CA-1 to CA-5 powders)
AM bodies (8 mm in diameter. times.10 mm in height) were formed by the SLM method using alloy powders of IA-1 to IA-5 and CA-1 to CA-5 having a particle size S prepared in experiment 1 (selective laser melting step S2). As the SLM conditions, control was performed so that the average inter-particle distance of the carbide phase particles was in the range of 0.15 to 1.5 μm according to the result of experiment 2.
Each AM body produced as described above was subjected to heat treatment for 4 hours at 1150 ℃ (melt heat treatment step S3). Subsequently, the AM elements subjected to the melting treatment are subjected to a heat treatment (aging heat treatment step S4) in which the AM elements are kept at 750 to 1000 ℃ for 0.5 to 10 hours, thereby producing SLM alloy products IP-1-1 to IP-5-1 using IA-1 to IA-5 powders and SLM alloy products CP-1-1 to CP-5-1 using CA-1 to CA-5 powders.
(microstructure observation and mechanical Property test)
From the SLM alloy products IP-1-1 to IP-5-1 and CP-1-1 to CP-5-1 prepared as described above, a test piece for microstructure observation and a test piece for mechanical property test were taken, and microstructure observation and mechanical property test were performed.
For the observation of the microstructure, the same image analysis of the SEM observation image as in experiment 2 was performed, and the average particle diameter of the matrix crystal grains and the average particle pitch of the carbide phase particles were measured.
As the mechanical property test, a creep test was conducted under the conditions of a temperature of 900 ℃ and a stress of 98MPa, and a creep rupture time was measured. According to the required characteristics of the target high-temperature steam turbine component, the creep rupture time of 1100 hours or more is determined as "pass", and the time of less than 1100 hours is determined as "fail". The acceptable creep characteristic means that the temperature at which the creep rupture time becomes 10 ten thousand hours under a stress of 58MPa is 875 ℃ or more. This creep characteristic can be said to be equivalent to that of the Ni-based alloy material.
The results of experiment 3 are shown in table 2.
TABLE 2 measurement test results of SLM alloy manufactures IP-1-1 to IP-5-1 and CP1-1 to CP-5-1
As shown in Table 2, the creep tests were acceptable in all the samples for the SLM alloy manufactures IP-1-1 to IP-5-1. This is considered to be because the average particle diameter of the matrix crystal grains is in an appropriate range, and the average inter-particle distance of the reinforcing carbide phase particles (MC type carbide phase particles of Ti, Zr, Nb, and/or Ta) is sufficiently small (that is, the reinforcing carbide phase particles are finely dispersed and precipitated).
On the other hand, the SLM alloy products CP-1-1 to CP-5-1 were found to have a suitable range of the average grain size of the mother phase grains, but the creep test was not satisfactory in all samples. If viewed separately, for CP-1-1, it is believed that: since the content of C and the content of Cr are too high, Cr carbide particles are preferentially precipitated. For CP-2-1, it is believed that: since the C content and the total content of "Ti + Zr + Nb + Ta" are too high, the reinforced carbide phase particles become coarse, and as a result, the average inter-particle distance increases. For CP-3-1, it is thought that: since the content of C is too high and the total content of "Ti + Zr + Nb + Ta" is too low, Cr carbide particles are preferentially precipitated. From the results of CP-1-1 and CP-3-1, it was confirmed that Cr carbide particles were not as effective as precipitation-strengthened particles. For CP-4-1 and CP-5-1, it is thought that this is because: since the total content of "Ti + Zr + Nb + Ta" is too small (almost none), the reinforced carbide phase itself is not precipitated.
From the results of experiment 3, it was confirmed that IA-1 to IA-5 having the chemical compositions defined in the present invention are preferable as the starting powder of the SLM alloy product. It was also confirmed that the creep characteristics can be improved by controlling the average interparticle distance of the reinforced carbide phase particles to be in the range of 0.15 to 1.5 μm.
[ experiment 4]
(production of SLM alloy products IP-1-2 to IP-1-7 and IP-2-2 to IP-2-7)
AM bodies (8 mm diameter. times.10 mm height) were produced by the SLM method using alloy powders of IA-1 and IA-2 having a particle size S prepared in experiment 1 (selective laser melting step S2). As the SLM conditions, control was performed so that the average inter-particle distance of the carbide phase particles was in the range of 0.15 to 1.5 μm according to the result of experiment 2.
The AM bodies prepared as described above were subjected to a melting treatment and an aging treatment. In this case, SLM alloys products IP-1-2 to IP-1-7 and IP-2-2 to IP-2-7 having different average grain sizes of mother phase grains were produced by changing the temperature range (1000 to 1300 ℃) and the holding time range (0.5 to 10 hours) of the melt processing. The aging treatment conditions were the same as in experiment 3.
(microstructure observation and mechanical Property test)
From the SLM alloy products IP-1-2 to IP-1-7 and IP-2-2 to IP-2-7 prepared as described above, a test piece for microstructure observation and a test piece for mechanical property test were taken, and microstructure observation and mechanical property test were performed.
For observation of the microstructure, image analysis of SEM observation images was performed in the same manner as in experiment 2, and the average particle size of the matrix crystal grains was measured. As the mechanical property test, the creep test similar to experiment 2 was performed, and "pass/fail" was determined by the same determination criterion as experiment 2. The results of experiment 4 are shown in table 3.
TABLE 3 measurement and test results of SM alloy products IP-1-2 to IP-1-7 and IP-2-2 to IP-2-7
As shown in Table 3, it was confirmed that the average grain size of the mother phase crystal grains is preferably 20 to 145. mu.m. In addition, from the results of experiment 4, it was confirmed that the melt-forming treatment is preferably a heat treatment which is maintained at a temperature of 1100 to 1200 ℃ for 0.5 to 10 hours.
[ experiment 5]
(study of SLM conditions in Selective laser melting Process)
An AM body (8 mm in diameter × 10mm in height) was formed by the SLM method using the alloy powder of IA-4 particle size S prepared in experiment 1 (selective laser melting step S2). The SLM condition was controlled by variously changing the thickness h of the alloy powder bed and the scanning speed S (mm/S) of the laser with the output power P of the laser set to 85W (unit: W · S/mm ═ J/mm).
The fine structure of each AM body prepared as described above was observed, and the average size of the segregation units was measured. The microstructure observation and measurement method used SEM and image processing software (ImageJ) in the same manner as in experiment 2.
Fig. 8 is an SLM condition example for obtaining a Co-based alloy AM body according to the present invention, and is a graph showing a relationship between a thickness of an alloy powder bed and a local heat input amount. In fig. 8, as a result of observation of the microstructure of the AM body, the case where the average size of the segregation cell is in the range of 0.15 to 1.5 μm was judged as "pass" and indicated by "o" in the figure, and the cases other than this were judged as "fail" and indicated by "x" in the figure.
From the results of experiment 5, it was confirmed that the SLM conditions in the selective laser melting step S2 are preferably controlled so that the relationship between the thickness h (unit: μm) of the alloy powder bed, the output power P (unit: W) of the laser beam, and the scanning speed S (unit: mm/S) of the laser beam satisfies "15 < h < 150" and "67 (P/S) -3.5 < h < 2222(P/S) + 13". That is, the shaded area is an area that is qualified.
The above embodiments and experimental examples are described to help understand the present invention, and the present invention is not limited to the specific configurations described. For example, a part of the configuration of the embodiment may be replaced with a configuration of technical common knowledge of a person skilled in the art, or a configuration of technical common knowledge of a person skilled in the art may be added to the configuration of the embodiment. That is, in the present invention, a part of the configurations of the embodiments and experimental examples in the present specification may be deleted, replaced with another configuration, or added to another configuration without departing from the technical spirit of the invention.