阅读说明：本技术 一种利用气液两相等离子体技术制备荧光碳量子点的方法 (Method for preparing fluorescent carbon quantum dots by gas-liquid two-phase plasma technology ) 是由 李元 郜晶 朱光远 温嘉烨 李睿 高一冉 张冠军 于 2021-07-02 设计创作，主要内容包括：本发明公开了一种利用气液两相等离子体技术制备荧光碳量子点的方法,涉及荧光碳量子技术领域。本发明是在液相等离子体技术的基础上通入惰性气体,利用气液两相放电方式产生等离子体。本发明引入惰性气体有利于放电通道形成,降低产物合成难度,而且能够有效提升活性粒子传质速率,有助于提升碳纳米产物的合成速率,并且可有效增大放电接触面积,增强放电稳定性。本发明反应效率高,耗时较短,且采用脉冲电源进行放电,相较于直流放电所需能耗较低、工艺简单,原料简单易得,无需催化剂、强氧化剂或强腐蚀剂,制得产物纯度较高。(The invention discloses a method for preparing fluorescent carbon quantum dots by using a gas-liquid two-phase plasma technology, and relates to the technical field of fluorescent carbon quantum dots. The invention introduces inert gas on the basis of liquid phase plasma technology and utilizes a gas-liquid two-phase discharge mode to generate plasma. The introduction of the inert gas is beneficial to the formation of a discharge channel, reduces the synthesis difficulty of the product, can effectively improve the mass transfer rate of active particles, is beneficial to the improvement of the synthesis rate of the carbon nano product, can effectively increase the discharge contact area, and enhances the discharge stability. The method has the advantages of high reaction efficiency, short time consumption, low energy consumption, simple process, simple and easily obtained raw materials, no need of a catalyst, a strong oxidant or a strong corrosive agent and high purity of the prepared product compared with direct current discharge by adopting a pulse power supply for discharge.)

1. A method for preparing fluorescent carbon quantum dots by using a gas-liquid two-phase plasma technology is characterized by comprising the following steps:

s1, preparing a reaction solution, introducing inert gas into the reaction solution, inserting two electrodes into the reaction solution, applying voltage to two ends of the electrodes under an inert atmosphere to perform discharge reaction so as to generate plasma between the two electrodes until the color of the reaction solution turns yellow brown;

and S2, after the reaction is finished, carrying out centrifugal separation on the reaction solution, and removing precipitates to obtain the fluorescent carbon quantum dots.

2. The method for preparing fluorescent carbon quantum dots by using the gas-liquid two-phase plasma technology according to claim 1, wherein the reaction solution is at least one of absolute ethyl alcohol, hexane, cyclohexane, benzene and toluene.

3. The method for preparing fluorescent carbon quantum dots by using the gas-liquid two-phase plasma technology as claimed in claim 1, wherein the inert gas is argon, and the gas flow rate is 0.5-2L/min.

4. The method for preparing fluorescent carbon quantum dots by using the gas-liquid two-phase plasma technology according to claim 1, wherein the electrodes are hollow stainless steel tubes with the outer diameter of 4mm and the inner diameter of 3mm, and the distance between the two electrodes is 1-4 mm.

5. The method for preparing fluorescent carbon quantum dots by using the gas-liquid two-phase plasma technology as claimed in claim 1, wherein the voltage applied across the electrodes is a pulse voltage, the voltage is 2-4kV, the frequency is 1-3kHz, and the current is 60-90A.

6. The method for preparing fluorescent carbon quantum dots by using the gas-liquid two-phase plasma technology according to claim 1, wherein the discharge time is 5-30 min.

Technical Field

The invention belongs to the technical field of carbon quantum dots, and particularly relates to a method for preparing fluorescent carbon quantum dots by using a gas-liquid two-phase plasma technology.

Background

The carbon nano material shows excellent characteristics in the aspects of light, magnetism, electricity, heat, sound and the like due to the surface effect, the small-size effect, the quantum size effect and the macroscopic quantum tunneling effect, has outstanding advantages in various fields of energy, biology, medicine, measurement, manufacturing and the like, and becomes the leading edge and the hot spot of the current scientific research. The carbon quantum dots are spherical zero-dimensional carbon nano materials with the particle size of less than 10nm, have the advantages of low toxicity, stable fluorescence characteristic, good biocompatibility and the like, and are widely applied to the fields of biological imaging, fluorescence labeling, biosensors and the like.

The preparation method of the existing fluorescent carbon quantum mainly comprises the following steps: laser methods, microwave synthesis methods, arc discharge methods, chemical vapor deposition methods, hydrothermal/solvothermal methods, liquid-phase plasma methods, and the like. Wherein, the equipment required by the laser method is complex and expensive, the yield is not high, and the method is not suitable for large-scale production; the chemical vapor deposition method needs to add a catalyst, and the introduction of the catalyst leads to the fact that the product is easy to contain impurities, and the purity of the product is yet to be improved; the growth process of the microwave synthesis method and the arc discharge method is difficult to control, and the particle size is not uniform; the hydrothermal method/solvothermal method usually requires long-time heating, and has long preparation time and large energy consumption; the liquid phase plasma method has simple operation, rich raw materials and high preparation speed, but the liquid has unstable discharge, large randomness of the discharge process and larger applied discharge voltage. Therefore, it is important to reduce the discharge voltage and improve the discharge stability to improve the liquid phase plasma technology.

Disclosure of Invention

Aiming at the defects of the prior art, the invention provides a method for preparing fluorescent carbon quantum dots by using a gas-liquid two-phase plasma technology. The preparation method has the advantages of lower discharge voltage, stable discharge, simple operation and high preparation speed.

The invention discloses a method for preparing fluorescent carbon quantum dots by utilizing a gas-liquid two-phase plasma technology, which comprises the following steps:

s1, preparing a reaction solution, introducing inert gas into the reaction solution, inserting two electrodes into the reaction solution, applying voltage to two ends of the electrodes under an inert atmosphere to perform discharge reaction so as to generate plasma between the two electrodes until the color of the reaction solution turns yellow brown;

and S2, after the reaction is finished, carrying out centrifugal separation on the reaction solution, and removing precipitates to obtain the fluorescent carbon quantum dots.

Preferably, the reaction solution is at least one of absolute ethyl alcohol, hexane, cyclohexane, benzene and toluene.

Preferably, the inert gas is argon, and the gas flow rate is 0.5-2L/min.

Preferably, the electrodes are hollow stainless steel tubes with the outer diameter of 4mm and the inner diameter of 3mm, and the distance between the two electrodes is 1-4 mm.

Preferably, the voltage applied across the electrodes is a pulsed voltage of 2-4kV, frequency of 1-3kHz, and current of 60-90A.

Preferably, the discharge time is 5-30 min.

Compared with the prior art, the invention has the following beneficial effects:

1. according to the invention, a gas-liquid two-phase discharge mode is adopted to generate plasma, inert gas is introduced to facilitate the formation of a discharge channel, the difficulty in product synthesis is reduced, the mass transfer rate of active particles can be effectively improved, the synthesis rate of carbon nano products can be improved, the discharge contact area can be effectively increased, and the discharge stability is enhanced;

2. the method has the advantages of high reaction efficiency, short time consumption, low energy consumption, simple process, simple and easily obtained raw materials, no need of a catalyst, a strong oxidant or a strong corrosive agent and high purity of the prepared product compared with direct current discharge by adopting a pulse power supply for discharge.

Drawings

FIG. 1 is a Transmission Electron Microscope (TEM) image of a fluorescent carbon quantum dot prepared in example 1 of the present invention;

FIG. 2 is a High Resolution Transmission Electron Microscope (HRTEM) image of the fluorescent carbon quantum dots prepared in example 1 of the present invention;

FIG. 3 is a particle size distribution diagram of fluorescent carbon quantum dots prepared in example 1 of the present invention;

FIG. 4 is a fluorescence emission spectrum of the fluorescent carbon quantum dot prepared in example 1 of the present invention;

FIG. 5 is a High Resolution Transmission Electron Microscope (HRTEM) image of the fluorescent carbon quantum dots prepared in example 2 of the present invention;

fig. 6 is a High Resolution Transmission Electron Microscope (HRTEM) image of the fluorescent carbon quantum dots prepared in example 3 of the present invention.

Detailed Description

The present invention will be further described with reference to the following specific examples.

Example 1

Adding 80mL of absolute ethyl alcohol into a reaction device, introducing argon gas at the gas flow rate of 1L/min, inserting two electrodes into the reaction device, and completely soaking the electrodes in the absolute ethyl alcohol, wherein the electrodes are hollow stainless steel tubes, the specification is that the outer diameter is 4mm, the inner diameter is 3mm, and the distance between the two electrodes is 1 mm; applying pulse high voltage at two ends of the electrode under argon atmosphere, wherein the voltage is 2.5kV, the frequency is 2kHz, and the current is 80A; discharging for 15min, and changing the color of the solution into yellow brown; and (4) carrying out centrifugal separation on the solution, and removing bottom sediment to obtain the carbon quantum dot mixed solution.

As can be seen from FIG. 1, the fluorescent carbon quantum dots prepared by the method have uniform particles and good dispersion degree;

as can be seen from FIG. 2, the crystallinity of the carbon quantum dots prepared by the invention is higher;

as can be seen from FIG. 3, the diameter of the carbon quantum dot particles prepared by the method is 2-6 nm;

as can be seen from FIG. 4, the fluorescence emission peak of the carbon quantum dot prepared by the method is obvious, and the fluorescence intensity peak appears at 436nm, which indicates that the fluorescent carbon quantum dot has good fluorescence characteristics.

Example 2

Adding 80mL of absolute ethyl alcohol into a reaction device, introducing argon gas at the gas flow rate of 1L/min, inserting two electrodes into the reaction device, and completely soaking the electrodes in the absolute ethyl alcohol, wherein the electrodes are hollow stainless steel tubes, the specification is that the outer diameter is 4mm, the inner diameter is 3mm, and the distance between the two electrodes is 1 mm; applying pulse high voltage at two ends of the electrode under argon atmosphere, wherein the voltage is 3kV, the frequency is 1kHz, and the current is 80A; discharging for 15min, and changing the color of the solution into yellow brown; and (4) carrying out centrifugal separation on the solution, and removing bottom sediment to obtain the carbon quantum dot mixed solution.

As can be seen from FIG. 5, the fluorescent carbon quantum dots prepared by the present invention have a certain crystallinity.

Example 3

Adding 80mL of cyclohexane into a reaction device, introducing argon gas at the gas flow rate of 1.5L/min, inserting two electrodes into the reaction device, and completely soaking the electrodes in the cyclohexane, wherein the electrodes are hollow stainless steel tubes, the specification is that the outer diameter is 4mm, the inner diameter is 3mm, and the distance between the two electrodes is 1 mm; applying pulse high voltage at two ends of the electrode under argon atmosphere, wherein the voltage is 2.5kV, the frequency is 2kHz, and the current is 80A; discharging for 10min, and changing the color of the solution into yellow brown; and (4) carrying out centrifugal separation on the solution, and removing bottom sediment to obtain the carbon quantum dot mixed solution.

As can be seen from FIG. 6, the fluorescent carbon quantum dots prepared by the method of the present invention have good dispersibility and good crystallinity.

The above embodiments are merely examples of the present invention, and it is obvious that the present invention is not limited to the above embodiments, but may be modified. All modifications directly or indirectly derivable by a person skilled in the art from the present disclosure are to be considered within the scope of the present invention.