阅读说明：本技术 一种在不锈钢表面制备金属基复合涂层的方法 (Method for preparing metal-based composite coating on surface of stainless steel ) 是由 李玉新 陈博文 刘思远 聂金浩 白培康 赵占勇 李忠华 魏守征 于 2021-01-08 设计创作，主要内容包括：本发明公开了一种在不锈钢表面制备金属基复合涂层的方法,该方法是在不锈钢表面以惰性气体的条件用同步送粉的方式采用激光熔覆技术制备TiBCN涂层,然后使用强流脉冲电子束技术均匀抛光激光熔覆层,最后利用微弧氧化技术制备厚度均匀的氧化铝陶瓷层,从而实现涂层的高硬度与良好的耐磨性。(The invention discloses a method for preparing a metal-based composite coating on a stainless steel surface, which comprises the steps of preparing a TiBCN coating on the stainless steel surface by a laser cladding technology in a synchronous powder feeding mode under the condition of inert gas, then uniformly polishing the laser cladding layer by using a high-current pulse electron beam technology, and finally preparing an alumina ceramic layer with uniform thickness by using a micro-arc oxidation technology, thereby realizing high hardness and good wear resistance of the coating.)

1. A method for preparing a metal composite coating on the surface of stainless steel is characterized by comprising the following steps: the high-hardness and high-wear-resistance coating is prepared on the surface of the 304 stainless steel substrate by combining a laser cladding technology with a high-current pulse electronic technology and a micro-arc oxidation technology.

2. The method for preparing a metal composite coating on the surface of stainless steel according to claim 1, wherein the method comprises the following steps: the preparation process comprises the following steps:

1) polishing a 304 stainless steel substrate, and preheating to 400-600 ℃;

2) carrying out vacuum drying treatment on the TiBCN powder to increase the fluidity;

3) preparing a TiBCN coating on the surface of 304 stainless steel by using a laser cladding technology:

the TiBCN coating is prepared on the surface of 304 stainless steel by the laser cladding technology, a synchronous powder feeding mode is adopted, argon is used as a carrier gas and a protective gas, and TiBCN powder in a powder feeding tank is carried to a nozzle for synchronous powder feeding by the aid of the argon; meanwhile, argon is introduced into a laser cladding workbench with five closed surfaces to serve as protective gas, so that the coating is prevented from being oxidized in the cladding process;

4) the surface of the TiBCN coating after laser cladding is subjected to surface purification treatment by adopting a high-current pulse electron beam technology, and the advantages of the high-current pulse electron beam technology are utilized to ensure that the elements on the surface of the TiBCN coating after laser cladding are uniformly distributed, so that the TiBCN coating is prepared for obtaining a more compact coating in the next step;

5) and preparing a high-hardness and high-wear-resistance coating on the TiBCN coating after laser cladding and pulse electron beam by adopting a micro-arc oxidation technology.

3. The method for preparing the metal composite coating on the surface of the stainless steel according to the claim 2, characterized in that: in the step 1), the polishing treatment of the 304 stainless steel is to polish the 304 stainless steel by using 180#, 500#, and 1000# sandpaper on a polishing machine respectively, so as to remove all dirt on the surface of the 304 stainless steel, and wipe the 304 stainless steel by using alcohol or acetone after polishing;

the 304 stainless steel block used was a 20mm by 10mm metal block.

4. The method for preparing the metal composite coating on the surface of the stainless steel according to the claim 2, characterized in that: and 2) drying for 1h at 80-120 ℃ in a vacuum drying oven, keeping for 12h, obtaining powder with better fluidity, making the powder more uniform in the process of laser cladding and powder feeding, and improving the cladding quality of the coating.

5. The method for preparing the metal composite coating on the surface of the stainless steel according to the claim 2, characterized in that: the laser cladding process parameters are that the laser power is 1000W-2000W, the scanning speed is 5-10 mm/s, the spot diameter is 4mm, the lap joint rate is 50%, the powder feeding flow under the influence of carrier gas is 200-400 mg/s, and the protective gas argon flow is 10-20L/min; the argon pressure is 0.5-1 MPa.

6. The method for preparing the metal composite coating on the surface of the stainless steel according to the claim 2, characterized in that: the TiBCN coating material comprises the following elements in percentage by mass: 50-60% of Ti, 10-12% of B, 4-6% of C, 15-25% of N and 0.5-1% of Si;

the thickness of the TiBCN coating obtained in the step 3) is between 0.5mm and 1 mm.

7. The method for preparing the metal composite coating on the surface of the stainless steel according to the claim 2, characterized in that: the high-current pulse electron beam technology comprises rapid melting-solidification or evaporation-condensation; before the high-current pulse electron beam is carried out, the TiBCN coating after laser cladding needs to be subjected to wire cutting, a sample block with the thickness of 10mm x 10mm is cut, and the surface of the sample block is subjected to polishing treatment.

8. The method for preparing the metal composite coating on the surface of the stainless steel according to the claim 2, characterized in that: experimental parameters of the high current pulsed electron beam: the accelerating voltage is 27kV, and the energy density is 2-6J/cm²Pulse time is 1-6 mus, target source distance is 150mm, vacuum degree is 5 x 10^-3Pa, and 5-30 times of irradiation.

9. The method for preparing the metal composite coating on the surface of the stainless steel according to the claim 2, characterized in that: before the micro-arc oxidation technology is used, the TiBCN coating after laser cladding needs to be polished, sand paper of 180#, 500#, and 1000# is used for polishing on a polishing machine respectively, a surface oxidation layer and unmelted particles are removed, so that a smooth surface is obtained, then an ultrasonic cleaning machine is used for cleaning in absolute ethyl alcohol for 10min, and finally a blower is used for drying a sample.

10. The method for preparing the metal composite coating on the surface of the stainless steel according to the claim 2, characterized in that: putting the polished sample into an electrolyte for micro-arc oxidation, treating the TiBCN coating by adopting a constant voltage mode of a pulse direct current micro-arc oxidation power supply, wherein the cathode is a stainless steel electrolytic tank, the anode is a TiBCN coating sample, and the sample is subjected to Na₂SiO₃Electrolyzing in the electrolyte of the system; the experimental parameters in the micro-arc oxidation process are that the working voltage of the electrolyte is 350-500V, the frequency is 500Hz, and the processing time is 5-15 min.

Technical Field

The invention relates to a preparation method of a metal-based composite coating, in particular to a method for preparing a metal composite coating on the surface of stainless steel, and belongs to the technical field of surface modification.

Background

304 stainless steel (304 ss) is currently considered one of the most important structural materials, and is widely used in a variety of high temperature environments due to its excellent mechanical properties and relatively high corrosion resistance. However, in order to extend its useful life while maintaining high structural integrity, the need for increased hardness, increased wear resistance and pitting resistance is becoming more apparent.

To date, the preparation of functional coatings on 304 stainless steel surfaces has been an effective way to increase its hardness, wear resistance and corrosion resistance. However, there are various materials and deposition methods for preparing the coating, and a wide range of coatings including nitride coatings, oxide coatings, etc. have been studied, and these coatings are the most promising methods for improving 304ss performance.

In the method for improving the surface performance of 304 stainless steel, the surface deposition technology is a method for researching comparative fire at present, and the surface deposition technology mainly comprises electroplating, thermal spraying, a PVD method, ion beam enhanced deposition, ion nitriding, liquid phase deposition, laser cladding and the like. The invention prepares the TiBCN coating on the surface of 304 stainless steel by adopting a laser cladding technology, thereby enhancing the hardness and improving the wear resistance and pitting resistance.

As one of the most promising additive manufacturing techniques, laser cladding enables near-net shape forming of complex metal products by high-energy laser deposition. Laser cladding has improved greatly over the past several decades and has been successfully used for machining a variety of metallic materials. However, laser cladding technology still faces some serious technical challenges, such as poor forming uniformity and stability, rough cladding layer surface, and the like. The laser cladding process is complex, involving coupling of the laser and powder, carrier gas and powder, and interaction between adjacent coatings. In addition, microcracks and voids inevitably occur, impairing the strength and compactness of the cladding layer structure. Thus, the wide application of laser cladding in the engineering industry is still limited. In order to solve these problems, in recent years, a great deal of research has been conducted to improve the mechanical properties of the laser-clad structure and to eliminate porosity. The adopted method is divided into two types, namely, the optimization of laser cladding process parameters (such as scanning speed, laser beam power, powder feeding speed and the like) and the use of other auxiliary processes, wherein the common laser cladding auxiliary processes comprise the steps of preheating powder and a matrix, adding a grain refiner into the powder, annealing, solution aging, tempering and other heat treatments. None of these methods is all that can partially improve the performance of the coating, and cannot improve the performance of the coating as a whole, so that the coating cannot well maintain its characteristics under some special environments (such as high temperature, hot corrosion, etc.).

High Current Pulsed Electron Beam (HCPEB) is an effective material surface modification technology developed in recent years, and during HCPEB irradiation, short-time high-density electron pulses can induce different physical processes on the surface layer, such as rapid melting-solidification, evaporation-condensation, and surface smoothing and annealing. These non-equilibrium processes can easily alter surface topography, microstructure, chemical composition, phase structure and surface stress states. Many previous studies show that the mechanical properties of the laser cladding coating surface can be effectively improved by HCPEB irradiation.

The micro-arc oxidation technology is a new technology which enables the coating oxide to grow in situ on the surface of a substrate and improves the coating performance. However, micro-arc oxidation technology is mainly applied to valve metals (aluminum, titanium, magnesium) and alloys thereof at present. In the actual test process, the micro-arc oxidation has no specific regulation and control effect on the surface of the laser cladding layer.

The micro-arc oxidation of the titanium alloy is mainly performed by Ti in electrolyte⁴⁺Ions and OH^-Ions react in situ on the surface of the substrate to form TiO₂Caused by the ceramic layer. The micro-arc oxidation film has good basement membrane interface adhesive force, excellent chemical corrosion resistance and high-temperature corrosion resistance. The structure, phase composition and mechanical properties of the oxide film can be adjusted by micro-arc oxidation parameters. The main regulating parameters of micro-arc oxidation are current density, discharge time, input voltage and electrolyte composition.

Disclosure of Invention

The invention aims to provide a preparation method for preparing a metal-based composite coating with high hardness and good wear resistance on the surface of stainless steel, which adopts the combined advantages of a micro-arc oxidation method and a laser cladding technology, reduces the cost, simultaneously reduces the micro-cracks and porosity of the coating, and greatly improves the hardness and frictional wear performance of the coating in a high-temperature environment.

The invention mainly relates to a method for preparing a coating with high hardness and high wear resistance on the surface of 304 stainless steel based on the combination of a laser cladding technology and a high-current pulse electron beam technology and a micro-arc oxidation technology. Because the defect of the laser cladding technology can not prepare a completely uniform coating, the combination of the laser cladding technology and the micro-arc oxidation technology can only prepare an uneven oxide layer, which can cause more damage to the coating and can lead the coating to be easily oxidized at high temperature, so that the oxide layer falls off, and the high-temperature friction and wear performance of the coating is greatly reduced. Cubic (face centered cubic) transition metal nitride based materials have high hardness, wear resistance, high chemical and thermal stability, and high melting points, and are very important hard protective coatings. To further improve the functional properties, other elements are incorporated into the crystal to form solid solutions or into the matrix around them to form nanocomposites. In the former case, alloying elements may be added to the sublattice, either by adding carbon to increase the shear modulus, thereby increasing hardness or improving tribological properties, and into the metal sublattice; the incorporation of boron into the nanocomposite improves the mechanical properties as well as thermal stability and oxidation resistance of the nitride. In this case, TiBCN films are beginning to be of interest because such materials can exhibit good performance by designing different systems with nanostructures.

The invention provides a method for preparing a metal composite coating on the surface of stainless steel, which combines a laser cladding technology with a high current pulse electronic technology and a micro-arc oxidation technology to prepare a high-hardness high-wear-resistance coating on the surface of a 304 stainless steel substrate, and comprises the following specific preparation processes:

1) polishing a 304 stainless steel substrate, and preheating to 400-600 ℃;

wherein, the polishing treatment of the 304 stainless steel is to polish the surface of the 304 stainless steel by 180#, 500#, 1000# sandpaper respectively, so as to remove all dirt on the surface of the 304 stainless steel, such as an oxide layer, grease and various impurities, and wipe the surface of the 304 stainless steel by alcohol or acetone after polishing;

the preheating treatment is carried out on the 304 stainless steel substrate, so that the internal stress generated in the casting process of the 304 stainless steel is released, and meanwhile, the influence of rapid temperature rise on the 304 stainless steel substrate in the laser cladding process is reduced, so that the coating is more compact, and the generation of cracks and pores is reduced;

2) the TiBCN powder is subjected to vacuum drying treatment to increase the fluidity

The drying treatment process is that the powder is dried in a vacuum drying oven at the temperature of 80-120 ℃ for 1 hour and kept for 12 hours, so that powder with better fluidity is obtained, the powder is more uniform in the process of laser cladding and powder feeding, and the cladding quality of the coating is improved; a more compact coating is obtained, and meanwhile, the powder is prevented from being accumulated and blocking a nozzle for synchronously feeding powder in the cladding process;

3) preparing TiBCN coating on 304 stainless steel surface by utilizing laser cladding technology

The TiBCN coating is prepared on the surface of 304 stainless steel by the laser cladding technology, a synchronous powder feeding mode is adopted, argon is used as a carrier gas and a protective gas, and TiBCN powder in a powder feeding tank is carried to a nozzle for synchronous powder feeding by the aid of the argon; meanwhile, argon is introduced into a laser cladding workbench with five closed surfaces to serve as protective gas, so that the coating is prevented from being oxidized in the cladding process;

the TiBCN coating material comprises the following elements in content: 50-60% of Ti, 10-12% of B, 4-6% of C, 15-25% of N and 0.5-1% of Si;

the thickness of the TiBCN coating obtained in the step 3) is between 0.5mm and 1 mm.

Specifically, the laser cladding process parameters include that the laser power (P) is 800W-2000W, the scanning speed (V) is 5-10 mm/s, the spot diameter is 4mm, the lap joint rate is 30% -50%, the powder feeding flow is 200-400 mg/s under the influence of carrier gas, and the protective gas argon flow is 10-20L/min;

more specifically, the argon pressure is 0.5-1 MPa;

more specifically, the 304 stainless steel block used was a 20mm by 10mm metal block.

4) The TiBCN coating after laser cladding is subjected to surface purification treatment by adopting a high-current pulse electron beam technology, and the advantages of the high-current pulse electron beam technology, such as rapid melting-solidification, evaporation-condensation and the like, are utilized, so that the elements on the surface of the TiBCN coating after laser cladding are uniformly distributed, and preparation is made for obtaining a more compact coating in the next step;

specifically, before the high-current pulsed electron beam is performed, the TiBCN coating after laser cladding needs to be wire-cut, cut into test blocks of 10mm × 10mm, and the surface thereof needs to be polished.

More specifically, experimental parameters of the high current pulsed electron beam: the accelerating voltage is 27kV, and the energy density is 2-6J/cm²Pulse time is 1-6 mus, target source distance is 150mm, vacuum degree is 5 x 10^-3Pa, and the irradiation times are 1-15.

6) And preparing a high-hardness and high-wear-resistance coating on the TiBCN coating after laser cladding and pulse electron beam by adopting a micro-arc oxidation technology.

In the preparation method, before the micro-arc oxidation technology is used, the TiBCN coating after laser cladding needs to be polished, the TiBCN coating is polished on a polishing machine by 180#, 500#, and 1000# abrasive paper respectively, a surface oxide layer and unmelted particles are removed, so that a smooth surface is obtained, then an ultrasonic cleaning machine is used for cleaning in absolute ethyl alcohol for 10min, and finally a blower is used for drying a sample;

putting the polished sample into an electrolyte for micro-arc oxidation, treating the TiBCN coating by adopting a constant voltage mode of a pulse direct current micro-arc oxidation power supply, wherein the cathode is a stainless steel electrolytic tank, the anode is a TiBCN coating sample, and the sample is subjected to Na₂SiO₃Electrolysis is carried out in the electrolyte of the system.

Specifically, the experimental parameters in the micro-arc oxidation process are as follows: the working voltage of the electrolyte is 350-500V, the frequency is 500Hz, and the processing time is 5-15 min.

After the electrolysis is finished, the surface of the sample around the coating is inlaid by using epoxy resin. The inlay does not affect the coating, and the part of the inlay is the peripheral part outside the prepared coating.

The invention has the beneficial effects that:

(1) the 304 stainless steel has good processing performance, toughness and high temperature resistance, and is widely applied to home decoration, food, medical treatment and various industries, and the TiBCN coating is prepared on the surface of the 304 stainless steel by utilizing a laser cladding technology, so that the wear resistance of the stainless steel can be effectively improved (the hardness of the 304 stainless steel prepared by a traditional casting method is only 180 HV);

(2) compared with the laser cladding technology, the surface of the coating after laser cladding is rough, the surface roughness of the coating after laser cladding can be greatly improved by adding the pulsed electron beam, and the surface of the coating can be quickly evaporated and solidified by the high-current pulsed electron beam technology, so that the surface purification effect is achieved; and finally, the mechanical property of the coating in a high-temperature environment is further enhanced by a micro-arc oxidation technology.

Drawings

FIG. 1: the coatings of example 1 and comparative example 1 rub wear curves.

FIG. 2: the coatings of example 2 and comparative example 2 rub wear curves.

FIG. 3: the coatings of example 3 and comparative example 3 rub wear curves.

Detailed Description

The present invention is further illustrated by, but is not limited to, the following examples.

Example 1:

the following examples are only preferred embodiments of the present invention and are not intended to limit the present invention in any way. Various modifications and alterations to this invention will become apparent to those skilled in the art. Any modification, equivalent replacement, or improvement made within the spirit and principle of the present invention should be included in the protection scope of the present invention.

Example 1

And sequentially polishing the 304 stainless steel substrate by using 180#, 500#, and 1000# sandpaper to obtain 304 stainless steel with a smooth surface, then placing the 304 stainless steel substrate in a muffle furnace to preheat to 600 ℃, and preserving heat for 1h to reduce coating cracking caused by stress caused by thermal expansion difference between the substrate and a coating material.

Drying TiBCN powder in vacuum drying oven at 80 deg.C for 1 hr, and maintaining for 12 hr to obtain

A powder with better flowability.

The TiBCN powder is filled into a powder feeding tank by adopting a laser cladding technology, argon is used as carrier gas, the TiBCN powder is carried to a laser nozzle, the laser power is 1500W by adopting a coaxial powder feeding mode, the scanning speed is 7mm/s, and the powder feeding rate is 300 mg/s.

And (3) polishing the prepared laser cladding coating on a polishing machine by using sand paper of 180#, 500#, and 1000# respectively, removing a surface oxide layer and unmelted particles to obtain a smooth surface, then cleaning the smooth surface in absolute ethyl alcohol for 10min by using an ultrasonic cleaning machine, and finally drying the sample by using a blower.

Then, by adopting a high-current pulse electron beam technology, carrying out irradiation treatment on the prepared laser cladding coating under a high-current pulse electron beam, wherein the specific process parameters are as follows: the accelerating voltage is 27kV, and the energy density is 5J/cm²Pulse time 4 mus, target source distance 150mm, vacuum 5 x 10^-3Pa, and the irradiation times are 10 times.

Finally, the coating is placed into an anode in micro-arc oxidation, a stainless steel electrolytic tank is selected as a cathode, the TiBCN coating is processed in a constant voltage mode of a pulse direct current micro-arc oxidation power supply, and the processed coating is placed in Na₂SiO₃Electrolysis is carried out in the electrolyte of the system. The experimental parameters in the micro-arc oxidation process are that the working voltage of the electrolyte is 350V, the frequency is 500Hz, and the processing time is 5 min. And inlaying the prepared sample by using epoxy resin, and analyzing an SEM image of the composite metal coating.

Comparative example 1

According to the method of the embodiment 1, a TiBCN coating is laser-cladded on the surface of a 304 stainless steel substrate, and the technological parameters of the laser cladding technology are changed into 1300W of laser power, 5mm/s of scanning speed and 260mg/s of powder feeding rate.

Then adopting a high-current pulse electron beam technology to coat the prepared laser cladding coating on high-current pulse electronsCarrying out irradiation treatment under beams, wherein the specific technological parameters are as follows: the accelerating voltage is 27kV, and the energy density is 5J/cm²Pulse time 4 mus, target source distance 150mm, vacuum 5 x 10^-3Pa, and the irradiation times are 5 times.

Finally, the coating is placed into an anode in micro-arc oxidation, a stainless steel electrolytic tank is selected as a cathode, the TiBCN coating is processed in a constant voltage mode of a pulse direct current micro-arc oxidation power supply, and the processed coating is placed in Na₂SiO₃Electrolysis is carried out in the electrolyte of the system. The experimental parameters in the micro-arc oxidation process are that the working voltage of the electrolyte is 350V, the frequency is 500Hz, and the processing time is 5 min.

The separately prepared samples of example 1 and comparative example 1 were taken, the cladding layer was polished, the surface of the sample was cleaned with an ultrasonic cleaner in an ethanol solution, the surface hardness of the sample was measured with a JMHVS-100AT precision automatic turret digital display microhardness tester with a test parameter of 200g and a holding time of 5 s. Selecting HT-1000 type high-temperature friction and wear testing machine to carry out, and selecting Si for experiment₃N₄The ceramic ball is used as a friction pair, the rotating speed of the motor is 500r/min, the abrasion time is 30min, the test load is 5N, the test temperature is 800 ℃, and the friction radius is 1 mm.

Fig. 1 shows the frictional wear curves of the coatings of example 1 and comparative example 1, and under the condition that the micro-arc oxidation experiment parameters are not changed, the frictional wear performance of the coating under the first 10 times of pulsed electron beams is found to be better by changing the laser cladding and pulsed electron beam test parameters, and the coating can be ensured to keep long-term stability during frictional wear by adjusting the laser cladding parameters.

Example 2

And sequentially polishing the 304 stainless steel substrate by using 180#, 500#, and 1000# sandpaper to obtain 304 stainless steel with a smooth surface, then placing the 304 stainless steel substrate in a muffle furnace to preheat to 600 ℃, and preserving heat for 1h to reduce coating cracking caused by stress caused by thermal expansion difference between the substrate and a coating material.

And (3) drying the TiBCN powder for 1h in a vacuum drying oven at the temperature of 100 ℃, and keeping for 12h to obtain powder with better fluidity.

The TiBCN powder is filled into a powder feeding tank by adopting a laser cladding technology, argon is used as carrier gas, the TiBCN powder is carried to a laser nozzle, the laser power is 1400W by adopting a coaxial powder feeding mode, the scanning speed is 5mm/s, and the powder feeding rate is 280 mg/s.

And (3) polishing the prepared laser cladding coating on a polishing machine by using sand paper of 180#, 500#, and 1000# respectively, removing a surface oxide layer and unmelted particles to obtain a smooth surface, then cleaning the smooth surface in absolute ethyl alcohol for 10min by using an ultrasonic cleaning machine, and finally drying the sample by using a blower. Then, by adopting a high-current pulse electron beam technology, carrying out irradiation treatment on the prepared laser cladding coating under a high-current pulse electron beam, wherein the specific process parameters are as follows: the accelerating voltage is 27kV, and the energy density is 5J/cm²Pulse time 4 mus, target source distance 150mm, vacuum 5 x 10^-3Pa, and the irradiation times are 10 times.

Finally placing the titanium substrate into an anode in micro-arc oxidation, selecting a stainless steel electrolytic tank as a cathode, and treating the TiBCN coating by adopting a constant voltage mode of a pulse direct current micro-arc oxidation power supply in Na₂SiO₃Electrolysis is carried out in the electrolyte of the system. The experimental parameters in the micro-arc oxidation process are that the working voltage of the electrolyte is 350V, the frequency is 500Hz, and the processing time is 5 min.

Comparative example 2

According to the method of the embodiment 2, laser power 1400W, scanning speed 5mm/s and powder feeding rate 280mg/s are selected by adjusting the parameters of the laser cladding coating.

And (3) polishing the prepared laser cladding coating on a polishing machine by using sand paper of 180#, 500#, and 1000# respectively, removing a surface oxide layer and unmelted particles to obtain a smooth surface, then cleaning the smooth surface in absolute ethyl alcohol for 10min by using an ultrasonic cleaning machine, and finally drying the sample by using a blower.

Then, by adopting a high-current pulse electron beam technology, carrying out irradiation treatment on the prepared laser cladding coating under a high-current pulse electron beam, wherein the specific process parameters are as follows: the accelerating voltage is 27kV, and the energy density is 5J/cm²Pulse time 4 mus, target source distance 150mm, vacuum 5 x 10^-3Pa, irradiation times 1 time.

Finally placing the anode in micro-arc oxidation, wherein the cathode is made of stainless steelThe steel electrolytic tank adopts a constant voltage mode of a pulse direct current micro-arc oxidation power supply to treat the TiBCN coating on Na₂SiO₃Electrolysis is carried out in the electrolyte of the system. The experimental parameters in the micro-arc oxidation process are that the working voltage of the electrolyte is 350V, the frequency is 500Hz, and the processing time is 5 min. And inlaying the prepared sample by using epoxy resin, and analyzing an SEM image of the composite metal coating.

FIG. 2: according to the friction and wear curves of the embodiment 2 and the comparative example 2, the same laser cladding experiment parameters and different times of the high current pulse electron beam experiment, the friction and wear performance of the embodiment 2 does not obviously fluctuate after the friction and wear experiment is carried out for 10min, and the friction and wear curve of the comparative example 2 obviously rises, namely the performance of the comparative example 2 obviously declines.

Example 3

And sequentially polishing the 304 stainless steel substrate by using 180#, 500#, and 1000# sandpaper to obtain 304 stainless steel with a smooth surface, then placing the 304 stainless steel substrate in a muffle furnace to preheat to 600 ℃, and preserving heat for 1h to reduce coating cracking caused by stress caused by thermal expansion difference between the substrate and a coating material.

Drying TiBCN powder in a vacuum drying oven at 120 deg.C for 1h, and maintaining for 12h to obtain

A powder with better flowability.

The TiBCN powder is filled into a powder feeding tank by adopting a laser cladding technology, argon is used as carrier gas, the TiBCN powder is carried to a laser nozzle, the laser power is 1300W, the scanning speed is 6mm/s, and the powder feeding rate is 250 mg/s.

And (3) polishing the prepared laser cladding coating on a polishing machine by using sand paper of 180#, 500#, and 1000# respectively, removing a surface oxide layer and unmelted particles to obtain a smooth surface, then cleaning the smooth surface in absolute ethyl alcohol for 10min by using an ultrasonic cleaning machine, and finally drying the sample by using a blower.

Then, by adopting a high-current pulse electron beam technology, carrying out irradiation treatment on the prepared laser cladding coating under a high-current pulse electron beam, wherein the specific process parameters are as follows: the accelerating voltage is 27kV, and the energy density is 5J/cm²When it is pulsedAt 4 mus, target source distance 150mm, vacuum degree 5 x 10^-3Pa, and the irradiation times are 10 times.

Finally placing the titanium substrate into an anode in micro-arc oxidation, selecting a stainless steel electrolytic tank as a cathode, and treating the TiBCN coating by adopting a constant voltage mode of a pulse direct current micro-arc oxidation power supply in Na₂SiO₃Electrolysis is carried out in the electrolyte of the system. The experimental parameters in the micro-arc oxidation process are that the working voltage of the electrolyte is 450V, the frequency is 500Hz, and the processing time is 5 min. And (3) inlaying the prepared sample by using epoxy resin, and testing hardness and wear resistance.

Comparative example 3

And (3) taking the laser cladding coating with the same parameters as those in the embodiment 3 and irradiating by a high-current pulse electron beam, wherein the test parameters in the micro-arc oxidation process specifically comprise that the working voltage of the electrolyte is 450V, the frequency is 500Hz, and the processing time is 15 min. And inlaying the prepared sample by using epoxy resin, and testing the wear resistance.

FIG. 3: the frictional wear curves of the coatings of comparative example 3 and comparative example 3 are obtained by changing the parameters of the micro-arc oxidation experiment, and the accompanying drawings show that the frictional wear performance of the coatings is greatly changed by changing the parameters of the micro-arc oxidation process, the friction coefficient of example 3 is only about 50% of that of comparative example 3, and the frictional wear curve of example 3 is smoother and more stable along with the frictional wear experiment, which proves that the components of the coatings are more uniform by adding the pulsed electron beam between the laser cladding and the micro-arc oxidation technology.