阅读说明：本技术 一种泥土书法的制作方法 (Method for making clay calligraphy ) 是由 宋晨 于 2021-07-05 设计创作，主要内容包括：本发明公开了一种泥土书法的制作方法,选择泥土为原料,经晒干后超微粉碎,过筛；配制泥土颜料,包含以下重量份数的原料：泥土60-70份、砂石10-20份、胶粉5-10份、助剂2-5份,所述助剂包括增稠剂、成膜剂、抑菌剂、防腐剂,加水与泥土颜料进行调配,所述泥土颜料通过与1-5倍的清水混合,制成溶液；选择书写的工具,蘸取调制好的溶液,在画板进行涂布；自然晾干后,保存得到成品。利用泥土进行书写,在书法创作中的是一种材料的探索与创新,在画板上产生特殊的线条和肌理,表现空间大,艺术性更高；趣味性强,利于推广。(The invention discloses a method for manufacturing clay calligraphy, which comprises the steps of selecting clay as a raw material, drying the clay in the sun, carrying out superfine grinding on the clay, and sieving the clay; preparing a soil pigment, which comprises the following raw materials in parts by weight: 60-70 parts of soil, 10-20 parts of sandstone, 5-10 parts of rubber powder and 2-5 parts of auxiliary agents, wherein the auxiliary agents comprise thickening agents, film-forming agents, bacteriostatic agents and preservatives, water is added to the auxiliary agents and the soil pigments for blending, and the soil pigments are mixed with 1-5 times of clear water to prepare a solution; selecting a writing tool, dipping the prepared solution, and coating on a drawing board; naturally drying, and storing to obtain the final product. The calligraphy is characterized in that earth is used for writing, a material is explored and innovated in calligraphy creation, special lines and textures are generated on a drawing board, the expression space is large, and the artistry is higher; the interesting is strong, and the popularization is facilitated.)

1. The manufacturing method of the clay calligraphy is characterized by comprising the following steps:

step 1: firstly, natural soil is selected as a raw material, is subjected to superfine grinding after being dried in the sun, and is sieved by a sieve of 50-150 meshes;

step 2: the clay pigment for writing comprises the following raw materials in parts by weight:

60-70 parts of soil, 10-20 parts of sandstone, 5-10 parts of rubber powder and 2-5 parts of auxiliary agents, wherein the auxiliary agents comprise thickening agents, film-forming agents, bacteriostatic agents and preservatives;

and step 3: adding water and mixing with soil pigment, wherein the soil pigment is mixed with 1-5 times of clear water to prepare a solution;

and 4, step 4: selecting a writing tool, dipping the prepared solution, and coating on a drawing board;

and 5: naturally drying, and storing to obtain the final product.

2. The method for making clay calligraphy according to claim 1, characterized in that: and 2, weighing the raw materials in parts by weight, pulverizing and uniformly stirring.

3. The method for making clay calligraphy according to claim 1, characterized in that: the clay pigment also comprises a color stone.

4. The method for making clay calligraphy according to claim 1, characterized in that: further comprising the step 6: and spraying a coagulant to firmly adhere the soil pigment on the drawing board.

5. The method for making clay calligraphy according to claim 1, characterized in that: and the step 4 also comprises the step of adding coarse soil with a scattered particle structure on the writing surface and attaching the coarse soil on the drawing board.

6. The method for making clay calligraphy according to claim 1, characterized in that: the drawing board is made of paper, cloth, slate and wood.

7. The method for making clay calligraphy according to claim 1, characterized in that: the finished product on the drawing board produces a color change over time.

8. The method for making clay calligraphy according to claim 1, characterized in that: the preservative is nano-scale titanium dioxide.

Technical Field

The invention relates to the technical field of calligraphy art, in particular to a manufacturing method of clay calligraphy.

Background

Although the traditional Chinese calligraphy is listed as the end of "six skill", the traditional Chinese calligraphy has an unimportant effect in terms of department of ascending and department of keeping, so that the position of the traditional Chinese calligraphy, like the position depicted by Haben horse, is a "public field" at the level of knowledge and text in the traditional society. The calligraphy art is one of the essentials of the traditional art in China, and in the traditional calligraphy art, people usually use a writing brush to create, write by dipping ink, and the ink keeps the rule without change.

Disclosure of Invention

The invention aims to overcome the technical defects and provides a method for manufacturing a clay calligraphy.

In order to achieve the purpose of the invention, the invention adopts the technical scheme that:

a manufacturing method of clay calligraphy comprises the following steps:

step 1: selecting natural soil as raw material, sun drying, micronizing, and sieving with 50-150 mesh sieve;

step 2: the clay pigment for writing comprises the following raw materials in parts by weight:

60-70 parts of soil, 10-20 parts of sandstone, 5-10 parts of rubber powder and 2-5 parts of auxiliary agent, wherein the auxiliary agent comprises a thickening agent, a film-forming agent, a bacteriostatic agent and a preservative,

and step 3: adding water and mixing with soil pigment, wherein the soil pigment is mixed with 1-5 times of clear water to prepare a solution;

and 4, step 4: selecting a writing tool, dipping the prepared solution, and coating on a drawing board;

and 5: naturally drying, and storing to obtain the final product.

Further, the earth pigment in the step 2 is prepared by weighing raw materials in parts by weight, powdering and uniformly stirring.

Further, the clay pigment also comprises a color stone.

Further, the method also comprises the step 6: and spraying a coagulant to firmly adhere the soil pigment on the drawing board.

Further, the step 4 further comprises adding coarse soil with a scattered particle structure on the writing surface and attaching the coarse soil on the drawing board.

Furthermore, the drawing board is made of paper, stone slabs and wood boards.

Further, the finished product on the drawing board generates color change along with the time.

Further, the preservative is nano-scale titanium dioxide.

The invention has the beneficial effects that: the calligraphy is characterized in that earth is used for writing, a material is explored and innovated in calligraphy creation, special lines and textures are generated on a drawing board, the expression space is large, and the artistry is higher; after the rubber powder is added, the writing materials of the clay can be conveniently stuck on the drawing board and are not easy to fall off; the drying of the soil is convenient for sterilization and disinfection, the crushing and sieving ensure the fineness of the pigment, the mixing of the sand and the stone increases the granular feeling, the preservative prolongs the shelf life of the calligraphy finished product, and the nano-scale titanium dioxide also has the sun-proof effect; the bacteriostatic agent avoids bacteria from breeding on soil, and the thickening agent is convenient for improving the viscosity of the system, so that the system is kept in a uniform and stable suspension state or an emulsion state, and is convenient for writing and using.

Drawings

FIG. 1 is a first schematic diagram of a finished calligraphic article of the present invention;

FIG. 2 is a schematic diagram of a second embodiment of the present invention;

FIG. 3 is a schematic view of the condition of the earth pigment of the present invention;

FIG. 4 is a third schematic diagram of the finished calligraphy product of the present invention.

Detailed Description

In order to make the content of the present invention more clearly understood, the technical solutions in the embodiments of the present invention are clearly and completely described below.

Example one

A manufacturing method of clay calligraphy comprises the following steps:

step 1: selecting natural soil as a raw material, drying in the sun, carrying out superfine grinding, and sieving by a 50-mesh sieve;

step 2: the clay pigment for writing comprises the following raw materials in parts by weight:

60 parts of soil, 10 parts of sandstone, 5 parts of rubber powder and 2 parts of auxiliary agents, wherein the auxiliary agents comprise a thickening agent, a film-forming agent, a bacteriostatic agent and a preservative, the preservative is nano-scale titanium dioxide, and the soil pigment in the step 2 is prepared by weighing raw materials in parts by weight, pulverizing and uniformly stirring; the clay pigment also comprises a color stone;

and step 3: adding water and a soil pigment for blending, wherein the soil pigment is mixed with 1 time of clear water to prepare a solution;

and 4, step 4: selecting a writing tool, dipping the prepared solution, and coating on a drawing board; the drawing board is made of paper; adding coarse soil with a scattered particle structure on the writing surface and attaching the coarse soil on the drawing board;

and 5: and after naturally airing, storing to obtain a finished product, wherein the finished product on the drawing board generates color change along with the passage of time.

Step 6: and spraying a coagulant to firmly adhere the soil pigment on the drawing board.

Example two

A manufacturing method of clay calligraphy comprises the following steps:

step 1: selecting natural soil as a raw material, drying in the sun, carrying out superfine grinding, and sieving by a 150-mesh sieve;

step 2: the clay pigment for writing comprises the following raw materials in parts by weight:

70 parts of soil, 20 parts of sandstone, 10 parts of rubber powder and 5 parts of auxiliary agent, wherein the auxiliary agent comprises a thickening agent, a film-forming agent, a bacteriostatic agent and a preservative, the preservative is nano-scale titanium dioxide, and the soil pigment in the step 2 is prepared by weighing raw materials in parts by weight, pulverizing and uniformly stirring; the clay pigment also comprises a color stone;

and step 3: adding water and a soil pigment for blending, wherein the soil pigment is mixed with 5 times of clear water to prepare a solution;

and 4, step 4: selecting a writing tool, dipping the prepared solution, and coating on a drawing board; the drawing board is made of slate; adding coarse soil with a scattered particle structure on the writing surface and attaching the coarse soil on the drawing board;

and 5: and after naturally airing, storing to obtain a finished product, wherein the finished product on the drawing board generates color change along with the passage of time.

Step 6: and spraying a coagulant to firmly adhere the soil pigment on the drawing board.

EXAMPLE III

A manufacturing method of clay calligraphy comprises the following steps:

step 1: selecting natural soil as a raw material, drying in the sun, carrying out superfine grinding, and sieving by a 100-mesh sieve;

step 2: the clay pigment for writing comprises the following raw materials in parts by weight:

65 parts of soil, 15 parts of gravel, 8 parts of rubber powder and 3 parts of auxiliary agent, wherein the auxiliary agent comprises a thickening agent, a film forming agent, a bacteriostatic agent and a preservative, the preservative is nano-scale titanium dioxide, and the soil pigment in the step 2 is prepared by weighing raw materials in parts by weight, pulverizing and uniformly stirring; the clay pigment also comprises a color stone;

and step 3: adding water and an earth pigment for blending, wherein the earth pigment is mixed with 2 times of clear water to prepare a solution;

and 4, step 4: selecting a writing tool, dipping the prepared solution, and coating on a drawing board; the drawing board is made of a wood board; adding coarse soil with a scattered particle structure on the writing surface and attaching the coarse soil on the drawing board;

and 5: and after naturally airing, storing to obtain a finished product, wherein the finished product on the drawing board generates color change along with the passage of time.

Step 6: and spraying a coagulant to firmly adhere the soil pigment on the drawing board.

The calligraphy is characterized in that earth is used for writing, a material is explored and innovated in calligraphy creation, special lines and textures are generated on a drawing board, the expression space is large, and the artistry is higher; the paint can be used on drawing boards made of different materials, and the viscosity of the clay pigment is blended according to the requirement; after the rubber powder is added, the writing materials of the clay can be conveniently stuck on the drawing board and are not easy to fall off; the drying of the soil is convenient for sterilization and disinfection, the crushing and sieving ensure the fineness of the pigment, the mixing of the sand and the stone increases the granular feeling, the preservative prolongs the shelf life of the calligraphy finished product, and the nano-scale titanium dioxide also has the sun-proof effect; the bacteriostatic agent avoids bacteria from breeding on soil, and the thickening agent is convenient for improving the viscosity of the system, so that the system is kept in a uniform and stable suspension state or an emulsion state, and is convenient for writing and using.

The present invention and the embodiments thereof have been described above, but the description is not limited to the embodiments, but only one of the embodiments of the present invention, and the actual embodiments are not limited thereto. In conclusion, those skilled in the art should appreciate that they can readily use the disclosed conception and specific embodiments as a basis for designing or modifying other structures for carrying out the same purposes of the present invention without departing from the spirit and scope of the invention as defined by the appended claims.