阅读说明：本技术 一种漂染阻燃面料的染料配方 (Dye formula of bleaching and dyeing flame-retardant fabric ) 是由 郭宏兵 程春良 程永胜 郭澍 于 2020-11-20 设计创作，主要内容包括：本发明提出了一种漂染阻燃面料的染料配方,其特征在于：按照重量份数包括如下组份：活化剂9-12份；酸性染料固色剂2-8份；阻燃剂9-15份；阴离子渗透剂6-11份；催化剂8-13份；着色剂4-7份；匀染剂2-4份,填料3-8份,增稠剂7-12份,稳定剂2-4份,氧化铝和聚磷酸铵,所述氢氧化铝和聚磷酸铵的质量份数比例为2:1-3：1,本发明解决了现有技术中传统染料染色不是容易掉色就是上色不好,而且染料染色不均匀,且染料到了冬天容易冻结,阻燃效果较差的技术问题。(The invention provides a dye formula of a bleaching and dyeing flame-retardant fabric, which is characterized in that: the paint comprises the following components in parts by weight: 9-12 parts of an activating agent; 2-8 parts of an acid dye fixing agent; 9-15 parts of a flame retardant; 6-11 parts of an anion penetrating agent; 8-13 parts of a catalyst; 4-7 parts of a coloring agent; 2-4 parts of a leveling agent, 3-8 parts of a filler, 7-12 parts of a thickening agent, 2-4 parts of a stabilizer, aluminum oxide and ammonium polyphosphate, wherein the mass part ratio of the aluminum hydroxide to the ammonium polyphosphate is (2: 1-3): the invention solves the technical problems that the traditional dye is not easy to fade or not easy to color, the dye is not uniform in dyeing, the dye is easy to freeze in winter, and the flame retardant effect is poor in the prior art.)

1. The dye formula of the bleaching and dyeing flame-retardant fabric is characterized by comprising the following components in parts by weight: the paint comprises the following components in parts by weight: 9-12 parts of an activating agent; 2-8 parts of an acid dye fixing agent; 9-15 parts of a flame retardant; 6-11 parts of an anion penetrating agent; 8-13 parts of a catalyst; 4-7 parts of a coloring agent; 2-4 parts of a leveling agent, 3-8 parts of a filler, 7-12 parts of a thickening agent, 2-4 parts of a stabilizer, aluminum oxide and ammonium polyphosphate, wherein the mass part ratio of the aluminum hydroxide to the ammonium polyphosphate is (2: 1-3): 1.

2. the dye formula of the bleaching and dyeing flame-retardant fabric according to claim 1, which is characterized in that: 11 parts of an activating agent; 7 parts of an acid dye fixing agent; 13 parts of a flame retardant; 9 parts of an anion penetrating agent; 12 parts of a catalyst; 6 parts of a coloring agent; 3 parts of leveling agent, 5 parts of filler and 9 parts of thickening agent.

3. The dye formula of the bleaching and dyeing flame-retardant fabric according to claim 1, which is characterized in that: the activating agent is phosphoric acid propane diamine.

4. The dye formula of the bleaching and dyeing flame-retardant fabric according to claim 1, which is characterized in that: the thickening agent is sodium polyacrylate.

5. The dye formula of the bleaching and dyeing flame-retardant fabric according to claim 1, which is characterized in that: the acid dye color fixing agent is a sulfonate polycondensate.

6. The dye formula of the bleaching and dyeing flame-retardant fabric according to claim 1, which is characterized in that: the flame retardant is inorganic flame retardant magnesium hydroxide.

Technical Field

The invention particularly relates to a dye formula of a bleaching and dyeing flame-retardant fabric.

Background

The dyeing process has a history of over 2800 years, the variety is various, the dyeing process level is high, but the production cost is low by adopting a simple and convenient process, most of folk dye houses are operated in the open air, and main equipment comprises a cooking stove, a big vat, a stretcher board, a cloth grinding stone, a cloth rolling shaft, a cloth airing frame, a twist board, a vat roller, a vat bowl and the like.

Disclosure of Invention

The purpose of the invention is as follows: the invention aims to provide a dye formula of a bleaching and dyeing flame-retardant fabric aiming at the defects in the prior art, and is used for solving the technical problems that the traditional dye is not easy to fade or not easy to color, the dye is not uniform in dyeing, the dye is easy to freeze in winter, and the flame-retardant effect is poor in the traditional dye dyeing in the prior art.

The technical scheme is as follows: in order to achieve the aim, the invention provides a dye formula of a bleaching and dyeing flame-retardant fabric, which is characterized in that: the paint comprises the following components in parts by weight: 9-12 parts of an activating agent; 2-8 parts of an acid dye fixing agent; 9-15 parts of a flame retardant; 6-11 parts of an anion penetrating agent; 8-13 parts of a catalyst; 4-7 parts of a coloring agent; 2-4 parts of a leveling agent, 3-8 parts of a filler, 7-12 parts of a thickening agent, 2-4 parts of a stabilizer, aluminum oxide and ammonium polyphosphate, wherein the mass part ratio of the aluminum hydroxide to the ammonium polyphosphate is (2: 1-3): 1.

as a modification of this solution, 11 parts of the activating agent; 7 parts of an acid dye fixing agent; 13 parts of a flame retardant; 9 parts of an anion penetrating agent; 12 parts of a catalyst; 6 parts of a coloring agent; 3 parts of leveling agent, 5 parts of filler and 9 parts of thickening agent.

As a modification of this embodiment, the activator is propylenediamine phosphate.

As a modification of the scheme, the thickening agent is sodium polyacrylate.

As a refinement of this embodiment, the acid dye fixing agent is a sulfonate polycondensate.

As an improvement of the scheme, the fire retardant is an inorganic fire retardant magnesium hydroxide.

Compared with the prior art, the invention has the following beneficial effects:

the fabric dyed by the invention has uniform color, is not easy to fade, has good flame retardant effect, utilizes the anion penetrating agent to improve the surface activity of the flame retardant, thereby being beneficial to improving the flame retardance of the fabric after dyeing, and also increases the adhesive force and the curing force of the dye by arranging the acid dye fixing agent, thereby improving the dyeing efficiency of the dyeing agent.

Detailed Description

The present invention will be further illustrated below with reference to specific embodiments, which are to be understood as merely illustrative and not limitative of the scope of the present invention.

The dye formula of the bleaching and dyeing flame-retardant fabric comprises the following components in parts by weight: 9-12 parts of an activating agent; 2-8 parts of an acid dye fixing agent; 9-15 parts of a flame retardant; 6-11 parts of an anion penetrating agent; 8-13 parts of a catalyst; 4-7 parts of a coloring agent; 2-4 parts of a leveling agent, 3-8 parts of a filler, 7-12 parts of a thickening agent, 2-4 parts of a stabilizer, aluminum oxide and ammonium polyphosphate, wherein the mass part ratio of the aluminum hydroxide to the ammonium polyphosphate is (2: 1-3): 1.

in this embodiment: as a preferred said activator 11 parts; 7 parts of an acid dye fixing agent; 13 parts of a flame retardant; 9 parts of an anion penetrating agent; 12 parts of a catalyst; 6 parts of a coloring agent; 3 parts of leveling agent, 5 parts of filler and 9 parts of thickening agent.

Wherein: the activating agent is phosphoric acid propane diamine;

the thickening agent is sodium polyacrylate;

the acid dye color fixing agent is a sulfonate polycondensate;

the flame retardant is inorganic flame retardant magnesium hydroxide.

In the above structure: according to the invention, the surface activity of the flame retardant is improved by using the anion penetrant, so that the flame retardance of the fabric after dyeing is improved, the adhesive force and the curing force of the dye are increased by arranging the acid dye fixing agent, and the dyeing efficiency of the dyeing agent is improved.

The technical means disclosed in the invention scheme are not limited to the technical means disclosed in the above embodiments, but also include the technical scheme formed by any combination of the above technical features.