阅读说明：本技术 一种混凝土裂缝自愈合拌合胶囊 (Concrete crack self-healing mixing capsule ) 是由 王建山 于 2021-01-24 设计创作，主要内容包括：一种混凝土拌合胶囊,在裂缝产生的时候,随着裂缝的开展混凝土内的胶囊会自动撕开,胶囊内的粉剂遇到水之后会形成亲混凝土凝胶充满裂缝,凝胶硬化后把裂缝黏合掉,达到混凝土自愈合的目的。胶囊可以做成毛边的,混凝土裂缝开展后,裂缝面和毛边会形成一条相交线,自动把有毛边的胶囊撕开,也可以做成遇水缓慢释放的胶囊。(A concrete mixing capsule is characterized in that when cracks are generated, the capsules in concrete can be automatically torn along with the development of the cracks, powder in the capsules can form hydrophilic concrete gel to fill the cracks after meeting water, and the cracks are bonded after the gel is hardened, so that the purpose of self-healing of the concrete is achieved. The capsule can be made into rough edges, after a concrete crack develops, the crack surface and the rough edges can form an intersecting line, the capsule with the rough edges is automatically torn open, and the capsule can also be made into a capsule which is slowly released when meeting water.)

一种混凝土裂缝自愈合拌合胶囊

技术领域

本发明涉及建筑施工领域，如何实现混凝土裂缝自愈合。

背景技术

存在问题：建筑物的地下室和屋顶混凝土都会开裂，开裂之后就会发生渗漏，后期堵漏处理既麻烦又会对混凝土自身结构产生伤害影响主体结构的耐久性，能不能发明一种会自愈合的混凝土呢。基于以上问题，寻找解决的办法。

发明内容

目前混凝土开裂是不可避免的，或多或少都会有裂缝产生，有的裂缝是受力结构承载力储备不够，需要对结构进行补强加固，大部分裂缝属于非结构裂缝，一旦发生裂缝之后，雨水和地下水就会侵蚀结构，慢慢发展成通缝，一旦形成了通缝就会发生渗漏，后期堵漏处理既麻烦又会对混凝土自身结构产生伤害影响主体结构的耐久性，能不能发明一种会自愈合的混凝土呢，本发明采用一种拌合胶囊，在裂缝产生的时候，随着裂缝的开展混凝土内的胶囊会自动撕开，胶囊内的粉剂遇到水之后会形成亲混凝土凝胶充满裂缝，凝胶硬化后把裂缝黏合掉，达到混凝土自愈合的目的。胶囊中的粉剂可以是超细混凝土，也可以是硅酸钠（水玻璃的粉剂）等能够和水混合之后形成凝胶和混凝土粘合填充裂缝的材料。胶囊可以做成毛边的，混凝土裂缝开展后,裂缝面和毛边会形成一条相交线，自动把有毛边的胶囊撕开，也可以做成遇水缓慢释放的胶囊。胶囊可以包裹粉剂也可以包裹水剂，使用水剂在泵送和机械搅拌的时候较容易破包影响混凝土的质量。凝胶材料也可以是单组份也可以是双组份或者多组份的，可以是无机的也可以有机的。

附图说明

下面以一个拌合了具有毛边胶囊的地下混凝土墙为例，结合附图和实施方式，对本发明的

具体实施方式

等方面进行进一步地说明。拌合了本发明的混凝土自愈合拌合胶囊的地下混凝土墙如图1，自愈合拌合胶囊细节示意图如图2，混凝土墙发生了一条裂缝，胶囊毛边和裂缝面形成交线如图3，凝胶硬化后裂缝愈合如图4。

图1.拌合了自愈合拌合胶囊的地下混凝土墙示意图

图2.自愈合拌合胶囊细节示意图

图3.胶囊毛边和裂缝面形成交线示意图

图4.凝胶硬化后裂缝愈合示意图

具体实施方式

如图2所示，自愈合拌合胶囊在边缘有锯齿状的毛边，混凝土裂缝开展后,裂缝面和毛边会形成一条相交线，自动把有毛边的胶囊撕开，胶囊中的粉剂和地下水混合形成凝胶如图3，凝胶硬化后裂缝愈合如图4。