Glass thermal shrinkage rate measuring system, method, storage medium and electronic device

文档序号:807214 发布日期:2021-03-26 浏览:20次 中文

阅读说明:本技术 玻璃热收缩率测定系统、方法、存储介质和电子设备 (Glass thermal shrinkage rate measuring system, method, storage medium and electronic device ) 是由 李青 李赫然 郝艺 胡恒广 闫冬成 周波 王丽红 王世岚 李瑞佼 段亚伟 于 2020-12-08 设计创作,主要内容包括:本公开涉及热收缩检测技术领域,具体地,涉及一种玻璃热收缩率测定系统、方法、存储介质和电子设备,所述系统包括:待测玻璃,衍射装置,以及与所述衍射装置连接的处理器,所述待测玻璃上预先刻蚀有衍射光栅,所述待测玻璃包括进行热处理前的第一待测玻璃和对所述第一待测玻璃进行热处理后的第二待测玻璃;所述衍射装置,用于对所述第一待测玻璃和所述第二待测玻璃上的衍射光栅进行衍射,并获取所述第一待测玻璃对应的第一光栅衍射图像和所述第二待测玻璃对应的第二光栅衍射图像;所述处理器,用于根据所述第一光栅衍射图像和所述第二光栅衍射图像确定所述待测玻璃的热收缩率。(The disclosure relates to the technical field of thermal shrinkage detection, in particular to a system and a method for determining the thermal shrinkage rate of glass, a storage medium and an electronic device, wherein the system comprises: the glass to be detected comprises first glass to be detected before heat treatment and second glass to be detected after heat treatment of the first glass to be detected; the diffraction device is used for diffracting diffraction gratings on the first glass to be tested and the second glass to be tested, and acquiring a first grating diffraction image corresponding to the first glass to be tested and a second grating diffraction image corresponding to the second glass to be tested; and the processor is used for determining the thermal shrinkage rate of the glass to be detected according to the first grating diffraction image and the second grating diffraction image.)

1. A glass thermal shrinkage determination system, comprising:

the glass to be detected comprises first glass to be detected before heat treatment and second glass to be detected after heat treatment of the first glass to be detected;

the diffraction device is used for diffracting diffraction gratings on the first glass to be tested and the second glass to be tested, and acquiring a first grating diffraction image corresponding to the first glass to be tested and a second grating diffraction image corresponding to the second glass to be tested;

and the processor is used for determining the thermal shrinkage rate of the glass to be detected according to the first grating diffraction image and the second grating diffraction image.

2. The system of claim 1, wherein the diffraction device comprises a light source, a diffraction screen, and an image receiver;

the light source is used for respectively irradiating the diffraction grating on the first glass to be tested and the diffraction grating on the second glass to be tested;

the diffraction screen is used for receiving the light rays irradiated by the light source to the diffraction grating and superposing the light rays to the image receiver so as to respectively generate the first grating diffraction image and the second grating diffraction image on the image receiver.

3. The system according to claim 2, wherein the processor is configured to determine a first grating constant of the diffraction grating on the first glass to be tested according to the first grating diffraction image, determine a second grating constant of the diffraction grating on the second glass to be tested according to the second grating diffraction image, and use a difference between the first grating constant and the second grating constant as the thermal shrinkage of the glass to be tested.

4. The system of claim 3, wherein the processor is configured to calculate the grating constant by:

acquiring the wavelength of the light source, the diffraction angle when the diffraction grating is diffracted by the diffraction device and the diffraction coefficient;

calculating the grating constant according to the wavelength, the diffraction angle and the diffraction coefficient.

5. The method for measuring the thermal shrinkage rate of the glass is characterized by being applied to a system for measuring the thermal shrinkage rate of the glass, wherein the system comprises the following components: the glass to be detected comprises first glass to be detected before heat treatment and second glass to be detected after heat treatment of the first glass to be detected;

the method comprises the following steps:

diffracting the diffraction gratings on the first glass to be tested and the second glass to be tested through the diffraction device, and obtaining a first grating diffraction image corresponding to the first glass to be tested and a second grating diffraction image corresponding to the second glass to be tested;

and the processor determines the thermal shrinkage rate of the glass to be detected according to the first grating diffraction image and the second grating diffraction image.

6. The method of claim 5, wherein the diffraction device comprises a light source, a diffraction screen, and an image receiver; the diffraction device diffracts the diffraction gratings on the first glass to be tested and the second glass to be tested, and the first grating diffraction image corresponding to the first glass to be tested and the second grating diffraction image corresponding to the second glass to be tested are acquired, wherein the acquiring comprises the following steps:

respectively irradiating the diffraction grating on the first glass to be tested and the diffraction grating on the second glass to be tested by using the light source;

and receiving light rays after the light source irradiates the diffraction grating through the diffraction screen, and superposing the light rays to the image receiver so as to respectively generate the first grating diffraction image and the second grating diffraction image on the image receiver.

7. The method of claim 6, wherein the processor determining the thermal shrinkage of the glass to be tested from the first grating diffraction image and the second grating diffraction image comprises:

and the processor determines a first grating constant of the diffraction grating on the first glass to be tested according to the first grating diffraction image, determines a second grating constant of the diffraction grating on the second glass to be tested according to the second grating diffraction image, and takes the difference value between the first grating constant and the second grating constant as the heat shrinkage rate of the glass to be tested.

8. The method of claim 7, wherein the grating constant is calculated by:

acquiring the wavelength of the light source, the diffraction angle when the diffraction grating is diffracted by the diffraction device and the diffraction coefficient;

calculating the grating constant according to the wavelength, the diffraction angle and the diffraction coefficient.

9. A computer-readable storage medium, on which a computer program is stored which, when being executed by a processor, carries out the steps of the method according to any one of claims 5 to 8.

10. An electronic device comprising the glass thermal shrinkage rate measurement system according to any one of claims 1 to 4.

Technical Field

The disclosure relates to the technical field of thermal shrinkage detection, in particular to a system and a method for measuring thermal shrinkage of glass, a storage medium and electronic equipment.

Background

With the development of display technology, the requirements for display resolution and image quality have increased, and in order to increase the display resolution, it is necessary to use glass having high thermal stability and low deformation rate. When the quality of glass is controlled, the thermal shrinkage rate of glass is one of the core parameters, and the requirement for the measurement accuracy of the thermal shrinkage rate of glass is increased due to the improvement of the requirement for the quality of glass.

In the prior art, two marks are usually made on the surface of glass to be measured, the distance between the marks of the glass which is not subjected to heat treatment and the glass which is subjected to heat treatment is measured under an optical microscope, and the thermal shrinkage rate of the glass to be measured is calculated according to the distance between the marks before heat treatment and the distance between the marks after heat treatment.

Disclosure of Invention

To overcome the problems in the related art, the present disclosure provides a glass thermal shrinkage rate measurement system, method, storage medium, and electronic device.

According to a first aspect of embodiments of the present disclosure, there is provided a glass thermal shrinkage determination system, the system comprising: the glass to be detected comprises first glass to be detected before heat treatment and second glass to be detected after heat treatment of the first glass to be detected; the diffraction device is used for diffracting diffraction gratings on the first glass to be tested and the second glass to be tested, and acquiring a first grating diffraction image corresponding to the first glass to be tested and a second grating diffraction image corresponding to the second glass to be tested; and the processor is used for determining the thermal shrinkage rate of the glass to be detected according to the first grating diffraction image and the second grating diffraction image.

Optionally, the diffraction device comprises a light source, a diffraction screen and an image receiver; the light source is used for respectively irradiating the diffraction grating on the first glass to be tested and the diffraction grating on the second glass to be tested; the diffraction screen is used for receiving the light rays irradiated by the light source to the diffraction grating and superposing the light rays to the image receiver so as to respectively generate the first grating diffraction image and the second grating diffraction image on the image receiver.

Optionally, the processor is configured to determine a first grating constant of the diffraction grating on the first glass to be tested according to the first grating diffraction image, determine a second grating constant of the diffraction grating on the second glass to be tested according to the second grating diffraction image, and use a difference between the first grating constant and the second grating constant as the thermal shrinkage rate of the glass to be tested.

Optionally, the processor is configured to calculate the grating constant by: acquiring the wavelength of the light source, the diffraction angle when the diffraction grating is diffracted by the diffraction device and the diffraction coefficient; calculating the grating constant according to the wavelength, the diffraction angle and the diffraction coefficient.

According to a second aspect of the embodiments of the present disclosure, there is provided a method for determining a thermal shrinkage rate of glass, which is applied to a system for determining a thermal shrinkage rate of glass, the system including: the glass to be detected comprises first glass to be detected before heat treatment and second glass to be detected after heat treatment of the first glass to be detected;

the method comprises the following steps: diffracting the diffraction gratings on the first glass to be tested and the second glass to be tested through the diffraction device, and obtaining a first grating diffraction image corresponding to the first glass to be tested and a second grating diffraction image corresponding to the second glass to be tested; and the processor determines the thermal shrinkage rate of the glass to be detected according to the first grating diffraction image and the second grating diffraction image.

Optionally, the diffraction device comprises a light source, a diffraction screen and an image receiver; the diffraction device diffracts the diffraction gratings on the first glass to be tested and the second glass to be tested, and the first grating diffraction image corresponding to the first glass to be tested and the second grating diffraction image corresponding to the second glass to be tested are acquired, wherein the acquiring comprises the following steps: respectively irradiating the diffraction grating on the first glass to be tested and the diffraction grating on the second glass to be tested by using the light source; and receiving light rays after the light source irradiates the diffraction grating through the diffraction screen, and superposing the light rays to the image receiver so as to respectively generate the first grating diffraction image and the second grating diffraction image on the image receiver.

Optionally, the determining, by the processor, the heat shrinkage rate of the glass to be tested according to the first grating diffraction image and the second grating diffraction image includes: and the processor determines a first grating constant of the diffraction grating on the first glass to be tested according to the first grating diffraction image, determines a second grating constant of the diffraction grating on the second glass to be tested according to the second grating diffraction image, and takes the difference value between the first grating constant and the second grating constant as the heat shrinkage rate of the glass to be tested.

Optionally, the grating constant is calculated by: acquiring the wavelength of the light source, the diffraction angle when the diffraction grating is diffracted by the diffraction device and the diffraction coefficient; calculating the grating constant according to the wavelength, the diffraction angle and the diffraction coefficient.

According to a third aspect of embodiments of the present disclosure, there is provided a computer readable storage medium having stored thereon computer program instructions which, when executed by a processor, implement the steps of the method of glass thermal shrinkage determination provided by the second aspect of the present disclosure.

According to a fourth aspect of the embodiments of the present disclosure, there is provided an electronic device including the glass thermal shrinkage rate measurement system according to the first aspect of the present disclosure.

Through the technical scheme, the system comprises: the glass to be detected comprises first glass to be detected before heat treatment and second glass to be detected after heat treatment of the first glass to be detected; the diffraction device is used for diffracting diffraction gratings on the first glass to be tested and the second glass to be tested, and acquiring a first grating diffraction image corresponding to the first glass to be tested and a second grating diffraction image corresponding to the second glass to be tested; the processor is used for determining the heat shrinkage rate of the glass to be detected according to the first grating diffraction image and the second grating diffraction image; in this way, the diffraction device diffracts the glass to be measured on which the diffraction grating is etched in advance before and after heat treatment respectively, grating diffraction image information before and after heat treatment of the glass to be measured is obtained, and the thermal shrinkage rate of the glass to be measured is determined according to the grating diffraction image information before and after heat treatment of the glass to be measured; in addition, because the diffraction grating is a large number of parallel nicks with infinite spacing, equal width and equal spacing, the range of the thermal shrinkage rate measured by the system can usually reach 0.5PPM (Part Per Million, parts Per Million), the system obviously improves the precision of the measurement of the thermal shrinkage rate of the glass, meets the high precision requirement of the measurement of the thermal shrinkage rate of the glass, and is convenient for selecting the glass with small adaptive deformation rate and strong thermal stability and high thermal stability when the display is manufactured.

Additional features and advantages of the disclosure are set forth in the detailed description which follows, and it is understood that the foregoing general description and the following detailed description are exemplary and explanatory only and are not restrictive of the disclosure.

Drawings

The accompanying drawings, which are included to provide a further understanding of the disclosure and are incorporated in and constitute a part of this specification, illustrate embodiments of the disclosure and together with the description serve to explain the disclosure without limiting the disclosure. In the drawings:

FIG. 1 is a block diagram illustrating a first glass thermal shrinkage measurement system according to an exemplary embodiment;

FIG. 2 is a block diagram illustrating a second glass thermal shrinkage measurement system according to an exemplary embodiment;

FIG. 3 is a schematic diagram of a glass to be tested etched with a diffraction grating;

FIG. 4 is a flow chart illustrating a method for determining the thermal shrinkage of glass in accordance with an exemplary embodiment;

FIG. 5 is a block diagram illustrating an electronic device in accordance with an example embodiment.

Detailed Description

The following detailed description of specific embodiments of the present disclosure is provided in connection with the accompanying drawings. It should be understood that the detailed description and specific examples, while indicating and explaining the disclosure, are intended for purposes of illustration and not limitation

In order to further improve the resolution and image quality of a display, it is necessary to use glass having high thermal stability and a small deformation ratio, and thus the measurement accuracy of the degree of thermal shrinkage of the glass is required to be high. In the prior art, the thermal shrinkage rate of glass is usually measured by observing the offset of marks of glass which is not subjected to heat treatment and glass which is subjected to heat treatment under an optical microscope, however, the data floating range of the thermal shrinkage rate of the glass measured by the method is large, the precision of the data floating range cannot meet the requirement on the measurement precision of the thermal shrinkage rate, for example, the thermal shrinkage rate of the glass needs to be measured to be accurate to 1PPM level in order to reach the preset resolution rate during the manufacturing of some high-resolution display screens, the marking lines are manufactured on the surface of the glass by a marking device in the prior art, the distance between the two marking lines is too large, and when the offset of the marks is measured by an operator by naked eyes by using the optical microscope, errors possibly caused by artificial measurement exist, so the data floating range of the thermal shrinkage rate of the glass measured when the thermal shrinkage rate of the glass, table 1 shows the results of measuring the thermal shrinkage of glass by using the prior art test method and the test method of the present invention for 3 glass test samples 1#, 2#, and 3# made of different chemical materials, as shown in table 1, the range of the thermal shrinkage of glass 1#, 2#, and 3# measured by using the prior art is 3.08PPM, 2.57PPM, and 2.87PPM, respectively, the error of the thermal shrinkage of glass measured by using the prior art is large, the requirement of a display screen on the measurement accuracy of the thermal shrinkage of glass cannot be met, and the measurement operation by using an optical microscope is complicated, which brings inconvenience to an operator.

TABLE 1 data table for determining heat shrinkage of glass according to the prior art and the present invention

To solve the above existing problems, the present disclosure provides a glass thermal shrinkage rate measurement system, method, storage medium, and electronic device, the system including: the glass to be detected comprises first glass to be detected before heat treatment and second glass to be detected after heat treatment of the first glass to be detected; the diffraction device is used for diffracting diffraction gratings on the first glass to be tested and the second glass to be tested, and acquiring a first grating diffraction image corresponding to the first glass to be tested and a second grating diffraction image corresponding to the second glass to be tested; the processor is used for determining the thermal shrinkage rate of the glass to be detected according to the first grating diffraction image and the second grating diffraction image; therefore, the diffraction device diffracts the glass to be measured with the diffraction grating etched in advance before and after heat treatment respectively and obtains grating diffraction image information before and after the heat treatment of the glass to be measured, and the thermal shrinkage rate of the glass to be measured is determined according to the grating diffraction image information before and after the heat treatment of the glass to be measured; in addition, because the diffraction grating is a large number of parallel nicks with equal width and equal interval and infinitesimal interval, the range of the thermal shrinkage rate measured by the system can reach 0.5PPM, as shown in Table 1, the range of the thermal shrinkage rate measured by the prior art for the glass 1#, 2# and 3# is 3.08PPM, 2.57PPM and 2.87PPM respectively, and the range of the thermal shrinkage rate measured by the system for the glass 1#, 2# and 3# is 0.56PPM, 0.47PPM and 0.48PPM respectively.

Specific embodiments of the present disclosure will be described in detail below with reference to the accompanying drawings.

Fig. 1 is a block diagram illustrating a first glass thermal shrinkage rate measuring system according to an exemplary embodiment, and as shown in fig. 1, the glass thermal shrinkage rate measuring system 10 includes: the glass to be detected 101, the diffraction device 102 and the processor 103 are connected with the diffraction device, the diffraction grating 1011 is etched on the glass to be detected 101 in advance, and the glass to be detected 101 comprises first glass to be detected 101 before heat treatment and second glass to be detected 101 after heat treatment of the first glass to be detected 101; the diffraction device 102 is configured to diffract the diffraction gratings 1011 on the first glass to be tested 101 and the second glass to be tested 101, and obtain a first grating diffraction image corresponding to the first glass to be tested 101 and a second grating diffraction image corresponding to the second glass to be tested 101; the processor 103 is configured to determine a thermal shrinkage rate of the glass 101 to be measured according to the first grating diffraction image and the second grating diffraction image.

The glass 101 to be measured is glass for which thermal shrinkage determination is required, the material of the glass 101 to be measured is not limited in the present disclosure, and the glass 101 to be measured may be glass composed of any chemical material, the first glass 101 to be measured is the glass 101 to be measured before thermal treatment, and the second glass 101 to be measured is glass after the first glass 101 to be measured is placed in a thermal treatment device for thermal treatment; the diffraction device 102 is a device for diffracting the diffraction grating on the glass to be measured; the first grating diffraction image and the second grating diffraction image are diffraction gratings on the first glass to be measured 101 and the second glass to be measured 101, respectively, and are formed by diffraction through the diffraction device 102.

In this step, the heat treatment may be heating the first glass 101 to be measured to a first preset temperature at a preset temperature-rising rate, and in order to heat the glass filaments of the first glass 101 uniformly, the heated first glass 101 to be measured may be subjected to heat preservation within a preset time, and then annealing and cooling the first glass 101 to be measured to a second preset temperature at a preset cooling rate, and finally obtaining a second glass 101 to be measured after heat treatment of the first glass 101 to be measured.

Illustratively, the first glass to be detected is placed on a porcelain boat or a refractory material, and is put into an annealing furnace for heat treatment, the temperature is raised to 600 ℃ according to the heating rate of 10 ℃/min, then the temperature is kept for 1 hour, so that the glass filaments are heated uniformly, then the glass is annealed and cooled to 20 ℃ (room temperature) according to the cooling rate of 5/min, and the glass after heat treatment is taken out, so that the glass is the second glass to be detected.

Alternatively, fig. 2 is a schematic structural diagram illustrating a second glass heat shrinkage rate measuring system according to an exemplary embodiment, and as shown in fig. 2, the diffraction device 102 includes a light source 1021, a diffraction screen 1022, and an image receiver 1023; the light source 1021 is used for respectively irradiating the diffraction grating 1011 on the first glass to be measured 101 and the diffraction grating 1011 on the second glass to be measured 101; the diffraction screen 1022 is configured to receive the light irradiated by the light source to the diffraction grating 1011 and superimpose the light to the image receiver 1023, so as to generate the first grating diffraction image and the second grating diffraction image on the image receiver 1023 respectively.

The first grating diffraction image is an image formed by the first glass to be measured 101 which is not subjected to heat treatment and is diffracted by the diffraction device 102, and the second grating diffraction image is an image formed by the second glass to be measured 101 which is subjected to heat treatment and is diffracted by the diffraction device 102.

In an embodiment, the light source 1021 may be a he-ne laser, the diffraction screen 1022 may be a lens, the he-ne laser irradiates the portion of the diffraction grating 1011 on the first glass to be tested 101 before heat treatment, the first grating diffraction image is formed through the lens, and the image receiver 1023 receives and records the first grating diffraction image; the first glass 101 to be measured is subjected to heat treatment to obtain the second glass 101 to be measured, a he-ne laser is used for irradiating the diffraction grating 1011 part on the second glass 101 to be measured after the heat treatment, the second grating diffraction image is formed through a lens, and the image receiver 1023 receives and records the second grating diffraction image.

Optionally, the processor 103 is configured to determine a first grating constant of the diffraction grating 1011 on the first glass 101 to be measured according to the first grating diffraction image, determine a second grating constant of the diffraction grating 1011 on the second glass 101 to be measured according to the second grating diffraction image, and use a difference between the first grating constant and the second grating constant as the thermal shrinkage rate of the glass 101 to be measured.

Fig. 3 is a schematic diagram of glass to be measured with a diffraction grating etched, as shown in fig. 3, a smooth portion between two scores on the glass to be measured can transmit light, which is equivalent to a slit, and a sum d of a width a of the slit and a width b of the score is referred to as a + b and is referred to as a grating constant, the first grating constant is a first grating constant of the diffraction grating 1011 on the first glass to be measured 101 that is not subjected to heat treatment, and the second grating constant is a second grating constant of the diffraction grating 1011 on the second glass to be measured 101 that is subjected to heat treatment. In this step, the processor 103 is configured to calculate the grating constant by: acquiring the wavelength of the light source, the diffraction angle when the diffraction grating is diffracted by the diffraction device 102, and the diffraction coefficient; and calculating the grating constant according to the wavelength, the diffraction angle and the diffraction coefficient.

Further, when obtaining the diffraction angle when diffracting the diffraction grating through the diffraction device 102, the processor 103 determines any one of the orders and positions of the main maximum and the distance from the main maximum to the center point of the grating diffraction image by obtaining the first grating diffraction image, where the order of the main maximum is the diffraction coefficient, when the main maximum is located above the center line of the grating diffraction image, the order of the main maximum is a positive order, and when the main maximum is located below the center line of the grating diffraction image, the order of the main maximum is a negative order, further, obtains the focal length of the diffraction screen, and determines the size of the diffraction angle according to the ratio of the distance from the main maximum to the center point of the grating diffraction image and the focal length of the diffraction screen.

Specifically, the first grating constant and the second grating constant may be obtained according to a grating equation d · sin θ ═ K λ (K ═ 0, 1, 2 … …), where d is the grating constant, sin θ is the diffraction angle, λ is the wavelength of the light source, and ± K is the order of the principal maximum.

The wavelength of the light source 1021 and the focal length information of the diffraction screen 1022 are preset by a user, and the processor 103 can directly obtain the wavelength of the light source and the focal length information of the diffraction screen 1022 preset by the user.

In addition, the magnitude of the diffraction angle can be determined in the following manner.

For example, the processor 103 determines that the distance from the second principal maximum in the first grating diffraction image to the central point of the grating diffraction image is x by acquiring the first grating diffraction image information, and the second principal maximum is located above the central line of the grating diffraction image, and the computer further acquires that the wavelength of the light source 1021 preset by the user is λ, the focal length of the diffraction screen 1022 is f, and determines the diffraction angle θ of the second principal maximum according to formula 1:

then, the first grating parameter d of the second principal maximum in the first grating diffraction image without heat treatment can be determined according to the grating equation1:

Similarly, the second grating constant d of the second grating diffraction image after heat treatment can be obtained by the method shown in the above example2The first grating constant d1And the second grating constant d2The difference of (d) is used as the thermal shrinkage rate of the glass 101, i.e. the thermal shrinkage rate of the glass 101 is d1-d2

By adopting the glass heat shrinkage rate measuring system, the diffraction device is used for respectively diffracting the glass to be measured, on which the diffraction grating is etched in advance, before and after heat treatment and acquiring grating diffraction image information before and after heat treatment of the glass to be measured, and the heat shrinkage rate of the glass to be measured is determined according to the grating diffraction image information before and after heat treatment of the glass to be measured, so that the heat shrinkage rate of the glass to be measured can be calculated according to the acquired grating diffraction image, errors caused by artificial measurement are reduced, the operation of heat shrinkage rate measurement is simplified, and convenience is brought to the measurement of the heat shrinkage rate of the glass; in addition, because the diffraction grating is a large number of parallel nicks with infinite intervals, equal width and equal intervals, the range of the thermal shrinkage rate measured by the system can reach 0.5PPM generally, the system obviously improves the measurement precision of the thermal shrinkage rate of the glass, meets the high-precision requirement on the measurement of the thermal shrinkage rate of the glass, and is convenient for selecting the glass with small adaptive deformation rate, strong thermal stability and high thermal stability when the display is manufactured.

FIG. 4 is a flow chart illustrating a method for determining the thermal shrinkage of glass that may be applied to the system for determining the thermal shrinkage of glass shown in FIG. 1, according to an exemplary embodiment, the system for determining the thermal shrinkage of glass comprising: the glass to be detected comprises first glass to be detected before heat treatment and second glass to be detected after heat treatment of the first glass to be detected;

the glass to be detected is glass which needs to be subjected to heat shrinkage rate determination, the material of the glass to be detected is not limited in the disclosure, and the glass to be detected can be glass consisting of any chemical material, the first glass to be detected is the glass to be detected before heat treatment, and the second glass to be detected is the glass to be detected after the first glass to be detected is put into a heat treatment device for heat treatment; the diffraction device is used for diffracting the diffraction grating on the glass to be tested; the first grating diffraction image and the second grating diffraction image are diffraction gratings on the first glass to be detected and the second glass to be detected respectively, and are formed after diffraction is carried out through a diffraction device.

The heat treatment can be heating the first glass to be measured to a first preset temperature at a preset heating rate, in order to uniformly heat the glass filaments of the first glass to be measured, the heated first glass to be measured can be subjected to heat preservation within a preset time, then annealing and cooling the first glass to be measured to a second preset temperature according to a preset cooling rate, and finally obtaining the second glass to be measured after the heat treatment of the first glass to be measured.

As shown in fig. 4, the method comprises the steps of:

in step 401, the diffraction gratings on the first glass to be tested and the second glass to be tested are diffracted by the diffraction device.

Wherein the diffraction device may comprise a light source, a diffraction screen and an image receiver.

In this step, the light source is used to irradiate the diffraction grating on the first glass to be measured and the diffraction grating on the second glass to be measured respectively.

In step 402, a first grating diffraction image corresponding to the first glass to be measured and a second grating diffraction image corresponding to the second glass to be measured are obtained.

In this step, the light beam irradiated by the light source to the diffraction grating is received by the diffraction screen and is superimposed on the image receiver, so that the first grating diffraction image and the second grating diffraction image are respectively generated on the image receiver.

The first grating diffraction image is an image formed by the first glass to be detected which is not subjected to heat treatment after being diffracted by the diffraction device, and the second grating diffraction image is an image formed by the second glass to be detected which is subjected to heat treatment after being diffracted by the diffraction device.

In an implementation example, the light source may be a he-ne laser, the diffraction screen may be a lens, the he-ne laser is used to irradiate a diffraction grating portion on the first glass to be detected before heat treatment, the first grating diffraction image is formed through the lens, and the image receiver receives and records the first grating diffraction image; and carrying out heat treatment on the first glass to be detected to obtain the second glass to be detected, irradiating the diffraction grating part on the second glass to be detected after heat treatment by using a helium-neon laser, forming a second grating diffraction image through a lens, and receiving and recording the second grating diffraction image by using an image receiver.

In step 403, the processor determines the thermal shrinkage rate of the glass to be measured according to the first grating diffraction image and the second grating diffraction image.

In this step, the processor may determine a first grating constant of the diffraction grating on the first glass to be measured according to the first grating diffraction image, determine a second grating constant of the diffraction grating on the second glass to be measured according to the second grating diffraction image, and then use a difference between the first grating constant and the second grating constant as a thermal shrinkage rate of the glass to be measured.

As shown in fig. 3, the smooth portion between two notches on the glass to be measured can transmit light, which is equivalent to a slit, and the sum d of the width a of the slit and the width b of the notch is called a + b as a grating constant, the first grating constant is a first grating constant of a diffraction grating on the first glass to be measured which is not subjected to heat treatment, and the second grating constant is a second grating constant of a diffraction grating on the second glass to be measured which is subjected to heat treatment. In this step, the processor calculates the grating constant by: acquiring the wavelength of the light source, the diffraction angle when the diffraction grating is diffracted by the diffraction device and the diffraction coefficient; and calculating the grating constant according to the wavelength, the diffraction angle and the diffraction coefficient.

Further, when a diffraction angle of the diffraction grating is obtained through the diffraction device, the processor determines any one of the orders and positions of the main maximum and the distance from the main maximum to the central point of the grating diffraction image through obtaining the first grating diffraction image, wherein the orders of the main maximum are the diffraction coefficient, when the main maximum is positioned above the central line of the grating diffraction image, the orders of the main maximum are positive orders, when the main maximum is positioned below the central line of the grating diffraction image, the orders of the main maximum are negative orders, further, the focal length of the diffraction screen is obtained, and the size of the diffraction angle is determined according to the ratio of the distance from the main maximum to the central point of the grating diffraction image to the focal length of the diffraction screen.

Specifically, the first grating constant and the second grating constant may be obtained according to a grating equation d · sin θ ═ K λ (K ═ 0, 1, 2 … …), where d is the grating constant, sin θ is the diffraction angle, λ is the wavelength of the light source, and ± K is the order of the principal maximum.

The processor can directly acquire the wavelength of the light source preset by the user and the focal length information of the diffraction screen.

In addition, the magnitude of the diffraction angle can be determined in the following manner.

Exemplarily, the processor determines, by obtaining the first grating diffraction image information, that a distance from a second principal maximum in the first grating diffraction image to a central point of the grating diffraction image is x, and the second principal maximum is located above a central line of the grating diffraction image, the computer further obtains a light source wavelength preset by a user as λ, a focal length of the diffraction screen is f, and determines a diffraction angle θ of the second principal maximum according to formula 1:

then, the first grating parameter d of the second principal maximum in the first grating diffraction image without heat treatment can be determined according to the grating equation1:

Similarly, the second grating constant d of the second grating diffraction image after heat treatment can be obtained by the method shown in the above example2The first grating constant d1And the second grating constant d2The difference value of the difference values is used as the thermal shrinkage rate of the glass to be tested,i.e. the thermal shrinkage of the glass to be measured is d1-d2

By adopting the method for measuring the heat shrinkage rate of the glass, the diffraction device is used for respectively diffracting the glass to be measured with the diffraction grating etched in advance before and after heat treatment and acquiring grating diffraction image information before and after heat treatment of the glass to be measured, and the heat shrinkage rate of the glass to be measured is determined according to the grating diffraction image information before and after heat treatment of the glass to be measured, so that the heat shrinkage rate of the glass to be measured can be calculated according to the acquired grating diffraction image, errors caused by artificial measurement are reduced, the operation of measuring the heat shrinkage rate is simplified, and convenience is brought to the measurement of the heat shrinkage rate of the glass; in addition, because the diffraction grating is a large number of parallel nicks with infinite intervals, equal width and equal intervals, the range of the thermal shrinkage rate measured by the system can reach 0.5PPM generally, the system obviously improves the measurement precision of the thermal shrinkage rate of the glass, meets the high-precision requirement on the measurement of the thermal shrinkage rate of the glass, and is convenient for selecting the glass with small adaptive deformation rate, strong thermal stability and high thermal stability when the display is manufactured.

The present disclosure also provides a storage medium having a computer program stored thereon, which when executed by a processor, implements the steps of the glass heat shrinkage rate measurement method provided by the present disclosure.

Fig. 5 is a block diagram illustrating an electronic device 500 according to an exemplary embodiment, where the electronic device 500 includes the glass thermal shrinkage determination system described above, as shown in fig. 5.

In another exemplary embodiment, a computer readable storage medium comprising program instructions which, when executed by a processor, implement the steps of the glass heat shrinkage determination method described above is also provided.

In another exemplary embodiment, a computer program product is also provided, which comprises a computer program executable by a programmable apparatus, the computer program having code portions for performing the glass heat shrinkage determination method described above when executed by the programmable apparatus.

The preferred embodiments of the present disclosure are described in detail with reference to the accompanying drawings, however, the present disclosure is not limited to the specific details of the above embodiments, and various simple modifications may be made to the technical solution of the present disclosure within the technical idea of the present disclosure, and these simple modifications all belong to the protection scope of the present disclosure.

It should be noted that, in the foregoing embodiments, various features described in the above embodiments may be combined in any suitable manner, and in order to avoid unnecessary repetition, various combinations that are possible in the present disclosure are not described again.

In addition, any combination of various embodiments of the present disclosure may be made, and the same should be considered as the disclosure of the present disclosure, as long as it does not depart from the spirit of the present disclosure.

14页详细技术资料下载
上一篇:一种医用注射器针头装配设备
下一篇:模拟土体在复杂环境条件下胀缩和水分迁移的方法和装置

网友询问留言

已有0条留言

还没有人留言评论。精彩留言会获得点赞!

精彩留言,会给你点赞!

技术分类