阅读说明：本技术 具有改进的渗透性的双层多线股帘线 (Double-layer multi-strand cord with improved permeability ) 是由 M·舍瓦莱 S·洛朗 E·克莱芒 A·贾内蒂 R·皮诺 于 2019-06-04 设计创作，主要内容包括：帘线(50)包括：-K>1根内部线股(TI),其包括具有Q＝1根内部丝线(F1)的内层(C1)、具有围绕内层(C1)以捻距p2进行缠绕的M根中间丝线(F2)的中间层(C2)、具有围绕中间层(C2)以捻距p3进行缠绕的N根外部丝线(F3)的外层(C3),-L>1根外部线股(TE),其包括内层(C1’)、外层(C3’)；分隔两根相邻外部线股的平均线股间距E大于或等于30μm；每根内部线股(TI)的中间层(C2)为不完全的；每根内部线股(TI)的外层(C3)为不完全的；并且0.36≤(p3-p2)/p3≤0.57。(The cord (50) comprises: -K >1 internal strands (TI) comprising an inner layer (C1) with Q ═ 1 internal filaments (F1), an intermediate layer (C2) with M intermediate filaments (F2) wound around the inner layer (C1) with a lay length p2, an outer layer (C3) with N external filaments (F3) wound around the intermediate layer (C2) with a lay length p3, -L >1 external strands (TE) comprising an inner layer (C1 '), an outer layer (C3'); the average strand spacing E separating two adjacent outer strands is greater than or equal to 30 μm; the intermediate layer (C2) of each inner strand (TI) is incomplete; the outer layer (C3) of each inner strand (TI) is incomplete; and 0.36 ≦ (p3-p2)/p3 ≦ 0.57.)

1. Double-layer multi-strand cord (50; 50'; 50 "; 51; 52; 53; 54; 55; 56; 57; 58; 59), characterized in that it comprises:

-an inner cord layer (CI) constituted by K >1 inner strands (TI) wound in a spiral, each inner strand (TI) being a strand of three layers (C1, C2, C3) and comprising:

an inner layer (C1) composed of 1 inner filament (F1) Q,

an intermediate layer (C2) consisting of M intermediate filaments (F2) wound around the inner layer (C1) with a lay length p2, and

an outer layer (C3) of N outer filaments (F3) wound around the intermediate layer (C2) with a lay length p3,

-an outer cord layer (CE) consisting of L >1 outer strands (TE) wound around the inner cord layer (CI), each outer strand (TE) being a strand of at least a double layer (C1 ', C3') and comprising:

an inner layer (C1 ') of Q ' inner filaments (F1 '), and

an outer layer (C3 ') consisting of N' outer filaments (F3 ') wound around the inner layer (C1'),

wherein:

-the average strand spacing E separating two adjacent outer strands is greater than or equal to 30 μm;

-the intermediate layer (C2) of each inner strand (TI) is unsaturated;

-the outer layer (C3) of each inner strand (TI) is unsaturated; and is

Lay lengths p2 and p3 satisfy the relation:

0.36≤(p3-p2)/p3≤0.57。

2. cord (50; 50'; 50 "; 51; 52; 53; 54; 55; 56; 57; 58; 59) according to the preceding claim, wherein the average strand spacing E separating two adjacent outer strands is greater than or equal to 70 μm, more preferably greater than or equal to 100 μm, still more preferably greater than or equal to 150 μm, and highly preferably greater than or equal to 200 μm.

3. The cord (50; 50'; 50 "; 51; 52; 53; 54; 55; 56; 57; 58; 59) according to any of the preceding claims, wherein 0.38 ≦ (p3-p2)/p3, preferably 0.40 ≦ (p3-p2)/p3, more preferably 0.43 ≦ (p3-p2)/p3, still more preferably 0.45 ≦ (p3-p2)/p 3.

4. Cord (50; 50'; 50 "; 51; 52; 53; 54; 55; 56; 57; 58; 59) according to any one of the preceding claims, wherein (p3-p2)/p3 ≦ 0.55, preferably (p3-p2)/p3 ≦ 0.53.

5. Cord (50; 50'; 50 "; 51; 52; 53; 54; 55; 56; 57; 58; 59) according to any one of the preceding claims, wherein the lay length p2 satisfies 8mm ≦ p2 ≦ 16mm, preferably 8mm ≦ p2 ≦ 14mm, more preferably 8mm ≦ p2 ≦ 12 mm.

6. Cord (50; 50'; 50 "; 51; 52; 53; 54; 55; 56; 57; 58; 59) according to any one of the preceding claims, wherein the lay length p3 satisfies 10mm ≦ p3 ≦ 40mm, preferably 15mm ≦ p3 ≦ 35mm, more preferably 15mm ≦ p3 ≦ 25mm, still more preferably 17mm ≦ p3 ≦ 23 mm.

7. Cord (50; 50'; 50 "; 51; 52; 53; 54; 55; 56; 57; 58; 59) according to any one of the preceding claims, wherein K-2, 3 or 4, preferably K-3 or 4.

8. Cord (50; 50'; 50 "; 51; 52; 53; 54; 55; 56; 57; 58; 59) according to any one of the preceding claims, wherein L-7, 8, 9 or 10, preferably L-8, 9 or 10, more preferably L-8 or 9.

9. Cord (50; 50'; 50 "; 51; 52; 53; 54; 55; 56; 57; 58; 59) according to any one of the preceding claims, wherein the inner cord layer (CI) is wound in a spiral form and with a pitch pi in the direction of the inner cord layer, the outer cord layer (CE) is wound in a spiral form and with a pitch pe in the direction of the outer cord layer, and the cord satisfies one and/or another of the following characteristics:

the direction of the inner layer of the cord is different from the direction of the outer layer of the cord,

pi is different from pe.

10. Cord (50; 50'; 50 "; 51; 52; 53; 54; 55; 56; 57; 58; 59) according to any one of the preceding claims, wherein the sum SI2 of the inter-filament distances (I2) of the intermediate layers (C2) of each inner strand (TI) satisfies SI2< d3, preferably SI2 ≦ 0.8x d3, wherein d3 is the diameter of each outer filament (F3) of each inner strand (TI).

11. The cord (50; 50'; 50 "; 51; 52; 53; 54; 55; 56; 57; 58; 59) according to any one of the preceding claims, wherein the outer layer (C3) of each inner strand (TI) is fully unsaturated.

12. Cord (50; 50'; 50 "; 51; 52; 53; 54; 55; 56; 57; 58; 59) according to any one of the preceding claims, wherein:

-Q＝1，M＝6，N＝11，

-the inner filament (F1) of each inner strand (TI) has a diameter d1 greater than the diameter d2 of each intermediate filament (F2) of each inner strand (TI), and

-the inner wire (F1) of each inner strand (TI) has a diameter d1 greater than the diameter d3 of each outer wire (F3) of each inner strand (TI).

13. Cord (50; 50'; 50 "; 51; 53; 54; 55; 56; 57; 58; 59) according to any one of the preceding claims, wherein d2 ═ d3, with the diameter d2 of each intermediate filament (F2) of each inner strand (TI) and the diameter d3 of each outer filament (F3) of each inner strand (TI).

14. The cord (50; 50 '; 50 "; 51; 52; 53; 54; 55; 56; 57; 58; 59) according to any one of the preceding claims, wherein the outer layer (C3') of each outer strand (TE) is unsaturated, preferably fully unsaturated.

15. A tyre (10), characterized in that said tyre (10) comprises at least one cord (50; 50', 50 "; 51; 52; 53; 54; 55; 56; 57; 58; 59) according to any one of the preceding claims.

Technical Field

The present invention relates to a multistrand cord which can be used in particular for reinforcing tyres, in particular tyres for heavy industrial vehicles.

Background

A tire with a radial carcass reinforcement comprises a tread, two inextensible beads, two sidewalls connecting the beads to the tread, and a belt or crown reinforcement disposed circumferentially between the carcass reinforcement and the tread. The carcass reinforcement and the crown reinforcement comprise a plurality of plies made of elastomeric compound, which may be reinforced by reinforcing elements, such as cords or monofilaments, of the metal or textile type.

The carcass reinforcement is anchored in each bead and is radially surmounted by a crown reinforcement. The carcass reinforcement comprises a single carcass ply containing filiform metal carcass reinforcing elements. Each wire-shaped metal carcass reinforcing element forms an angle of between 80 ° and 90 ° with the circumferential direction of the tire.

The crown reinforcement may also comprise various other auxiliary plies or layers of elastomeric compound having a width that may vary according to the circumstances and may or may not contain reinforcing elements. By way of example, mention may be made of so-called protective plies having the function of protecting the rest of the belt from external attacks or perforations, or so-called hooping plies (called "zero-degree" plies) containing reinforcing elements oriented substantially in the circumferential direction, whether radially on the outside or on the inside with respect to the working ply. The protective plies generally comprise reinforcing elements exhibiting high elongation, so that they deform under the effect of the stresses exerted by the indentations (for example stones).

A working ply reinforcement element comprising a double layer of multi-strand metal cords is known in the art, as disclosed in the embodiment of WO 2015090920. The cord comprises an inner cord layer consisting of inner strands and an outer cord layer consisting of six outer strands wound in a spiral around the inner cord layer.

Each of the inner and outer strands includes: an inner layer of strands consisting of a single internal thread; an intermediate layer consisting of six filaments; and an outer layer of strands consisting of eleven external filaments. The middle and outer layers of inner strands are wrapped in the S direction around the inner and middle layers of inner strands, respectively. The middle and outer layers of each outer strand are wrapped in the Z-direction around the inner and middle layers of each outer strand, respectively. The outer strands are wound around the inner strands in a helical fashion in the winding direction of the cord, which is the S direction. The respective lay length p2, p2 'of the middle layer of each inner and outer strand is equal to 14mm, and the respective lay length p3, p 3' of the outer layer of each inner and outer strand is equal to 20 mm.

Tires for heavy industrial vehicles, in particular of the construction site type, are subject to a number of attacks. In particular, this type of tire usually runs on uneven road surfaces, sometimes causing perforation of the tread. These perforations allow the ingress of corrosive agents (for example air and water) which oxidize the metallic reinforcing elements of the crown reinforcement (in particular the crown plies), thus significantly reducing the life of the tire.

One solution to increase the life of the tire is to combat the diffusion of these corrosive agents. It is thus possible to make provision for each of the inner and intermediate layers to be covered with an elastomeric compound during the manufacture of the cord. During this process, the elastomeric compound present penetrates the capillaries present between each layer of each strand, thus preventing the corrosive agent from diffusing. Such cords are commonly referred to as in-situ rubberized cords, and are well known in the art.

Another solution to increase the life of the tire is to increase the breaking force of the cords. Generally, the breaking force is increased by increasing the diameter of the filaments constituting the cord and/or by increasing the number of filaments and/or the individual strength of each filament. However, still further increasing the diameter of the filaments, for example, more than 0.50mm, necessarily results in a decrease in the flexibility of the cord, which is not desirable. Increasing the number of filaments generally results in a decrease in the ability of the elastomeric compound to penetrate the strands. Finally, increasing the individual strength of each thread requires a large investment in the equipment used to manufacture the thread.

Disclosure of Invention

The object of the present invention is a cord which, compared with cords of the prior art, exhibits an improved permeability of the elastomeric compound to the internal strands of the cord, thus making it possible to reduce the intrusion of corrosive agents into the cord and the diffusion along the cord.

Cord according to the invention

To this end, one subject of the invention is a double-layer multi-strand cord comprising:

-an inner layer of cord constituted by K >1 inner strands wound in a spiral, each inner strand being a three-layer strand and comprising:

an inner layer consisting of Q ═ 1 inner filaments,

an intermediate layer consisting of M intermediate filaments wound around the inner layer with a lay length p2, and

an outer layer consisting of N outer filaments wound around the intermediate layer with a lay length p3,

-an outer layer of cord consisting of L >1 outer strands wound around the inner layer of cord, each outer strand being an at least double-layered strand and comprising:

an inner layer of Q' inner filaments, and

an outer layer consisting of N' outer filaments wound around the inner layer,

wherein:

-the average strand spacing E separating two adjacent outer strands is greater than or equal to 30 μm;

-the intermediate layer (C2) of each inner strand (TI) is unsaturated;

-the outer layer (C3) of each inner strand (TI) is unsaturated; and is

Lay lengths p2 and p3 satisfy the relation: the ratio of (p3-p2)/p3 is more than or equal to 0.36 and less than or equal to 0.57.

It should be recalled that, as is known, the lay length of a strand means the length of this strand, measured parallel to the axis of the cord, after which the strand with this lay length completes a full turn around said axis of the cord. Similarly, the lay length of a wire represents the length of the wire measured parallel to the axis of the strand on which the wire is located, the wire having this lay length completing one full turn around said axis of the strand after said length.

The winding direction of the layer with strands or with threads means the direction in which the strands or threads are formed with respect to the axis of the cord or strands. The winding direction is generally indicated by the letter Z or S.

The lay length, winding direction and diameter of the wire and strands were determined according to standard ASTM D2969-04 of 2014.

According to the invention, the outer layer of the cord is unsaturated.

By definition, an unsaturated layer having strands is a layer such that sufficient space is left between the strands to allow the elastomeric compound to pass through. An unsaturated outer layer with strands means that the outer strands do not touch and that there is sufficient space between two adjacent outer strands to allow the elastomeric compound to pass through to the inner strands. In contrast, a saturated layer with strands is such that there is not enough space between the strands of the layer to allow the elastomeric compound to pass, for example because the two strands of each pair in the layer are in contact with each other.

According to the invention, the outer layer with outer strands has a strand spacing greater than or equal to 30 μm, said strand spacing being defined as the shortest distance on average separating a circular envelope (into which two adjacent outer strands are inscribed) in a cross section of the cord perpendicular to the main axis of the cord.

Preferably, the average strand spacing E separating two adjacent outer strands is greater than or equal to 70 μm, more preferably greater than or equal to 100 μm, still more preferably greater than or equal to 150 μm, and the height is preferably greater than or equal to 200 μm.

By "at least two layers" is meant that in certain embodiments, each outer strand may comprise two layers, which is meant to include only two layers, and not only one or three of them; and in other embodiments, each outer strand may comprise three layers, which means that only three layers are included, and only two or four of them are not included.

In the present invention, the cord has two layers with strands, which means that it comprises an assembly of neither more nor less than two layers with strands, which means that the assembly has two layers with strands, not one layer, nor three layers, but only two layers. The outer layer of cord is wrapped around the inner layer of cord in contact with the inner layer of cord.

The permeability of the cord according to the invention can be improved by the invention compared to cords in which the ratio (p3-p2)/p3 is outside the range of the ratio according to the invention, as for example in the example of WO2015090920 the ratio (p3-p2)/p3 of the cord is equal to 0.30. The inventors of the present invention propose the following assumptions: this ratio makes it possible to obtain a relatively large window for the radial passage of the elastomeric compound within each inner strand. The radial through-window is defined as the intersection between the two spaces: said spaces being, on the one hand, the spaces projected onto a plane parallel to the main axis of the cord between two adjacent threads of the outer layer of each inner strand and, on the other hand, the spaces projected onto a plane parallel to the main axis of the cord between two adjacent threads of the intermediate layer of each inner strand. Such a radial through-window is shown in fig. 16.

Furthermore, the cord according to the invention has spaces between the outer strands that allow the passage of the elastomeric compound, due to the fact that the outer layer of the cord is unsaturated. Known from the prior art are cords having a relatively high breaking strength due to the outer layer of the cord being saturated (the outer strands being in contact with each other in pairs), forming an arch that absorbs the tensile forces exerted on the cord. In the cord according to the invention, the unsaturated nature of the outer layer of the cord allows the elastomeric compound to penetrate between the outer strands on the one hand and each inner strand on the other hand, despite the fact that the camber around the inner strands is broken. In this way, therefore, the camber is at least partially recovered while imparting excellent permeability to the cord, and the drop in breaking strength of the cord is limited. Furthermore, this feature allows the elastomeric compound to penetrate between the outer layers of the inner and outer strands, forming an elastomeric compound cushion body that at least partially absorbs the radial component of the force between the inner and outer strands.

In the cords of the prior art comprising an inner layer of cords, which layer is constituted by a single inner strand, the significant unsaturation of the outer layer of cords for the purpose of promoting the permeability of the cords leads to a significant reduction in the quality of the metal and therefore a relatively large reduction in the breaking strength of the cords. In contrast to the cords of the prior art, in which each outer strand contributes more to the breaking strength than the cords according to the invention, in the cords of the invention, the significant unsaturation of the outer layer of the cord for the purpose of promoting the permeability of the cord, due to the presence of K inner strands, makes the reduction in the quality of the metal less pronounced and therefore the reduction in the breaking strength controllable.

Thanks to the invention and to the relationship between p2 and p3, each inner strand is a strand with a cylindrical layer. Very advantageously, each outer strand is a strand having a cylindrical layer, whether it has two or three layers. Strands with cylindrical layers are extremely highly permeable, unlike strands with compact layers in which the lay length is the same for all layers and the winding direction is the same for all layers, so that they exhibit much lower permeability.

Alternatively and preferably, in one embodiment, the cord is free of any polymeric compound, in particular the cord is free of any jacket having any polymeric compound covering the inner layer of the cord and thus covering each inner strand. In another embodiment, the cord is free of any elastomeric compound, in particular the cord is free of any jacket having any elastomeric compound covering the inner layer of the cord and thus covering each inner strand.

Advantageously, the cords are made of metal. The term "metallic cord" is understood by definition to mean a cord formed by wires composed of a metallic material, mainly (i.e. more than 50% of the wires of these wires) or completely (100% of the wires). Such a metal cord is preferably implemented using a steel cord, more preferably a cord made of pearlitic (or ferritic-pearlitic) carbon steel (hereinafter referred to as "carbon steel"), or a cord made of stainless steel (according to the definition steel comprising at least 11% of chromium and at least 50% of iron). However, it is of course possible to use other steels or other alloys.

When carbon steel is advantageously used, its carbon content (% by weight of steel) is preferably between 0.4% and 1.2%, in particular between 0.5% and 1.1%; these contents represent a good compromise between the mechanical properties required for the tyre and the availability of the wires.

The metal or steel used, whether it be carbon steel or stainless steel in particular, may itself be coated with a metal layer which, for example, improves the processability of the metal cord and/or its constituent elements or improves the service properties of the cord and/or the tire itself, such as adhesion, corrosion resistance or ageing resistance. According to a preferred embodiment, the steel used is covered with a layer of brass (Zn-Cu alloy) or zinc.

Preferably, the wires of the same layer of predetermined (inner or outer) strands all have substantially the same diameter. Advantageously, the inner strands all have substantially the same diameter. Advantageously, the outer strands all have substantially the same diameter. By "substantially the same diameter" is meant that the wires or strands have the same diameter within industry tolerances.

Advantageously, each wire of each strand has a diameter in the range 0.15mm to 0.60mm, preferably 0.20mm to 0.50mm, more preferably 0.22mm to 0.40mm, still more preferably 0.24mm to 0.35 mm.

A polymer compound or a compound of polymers means that the compound contains at least one polymer. Preferably, such polymers may be thermoplastics such as polyesters or polyamides, thermosetting polymers, elastomers such as natural rubber, thermoplastic elastomers, or combinations of these polymers.

An elastomeric compound or a compound of elastomers means that the compound contains at least one elastomer or one rubber (these two terms are synonymous), and at least one other component. Preferably, the elastomeric compound also contains a vulcanization system and a filler. More preferably, the elastomer is a diene elastomer.

Advantageously, the lay lengths p2 and p3 satisfy the relationship 0.38 ≦ (p3-p2)/p3, preferably 0.40 ≦ (p3-p2)/p3, more preferably 0.43 ≦ (p3-p2)/p3, still more preferably 0.45 ≦ (p3-p2)/p 3. The higher the ratio (p3-p2)/p3, or in other words the greater the difference between p3 and p2, the better the structural stability of each inner strand. In particular, the greater the degree to which the lay lengths of the intermediate and outer layers of each inner strand differ, the greater the crossing of the intermediate and outer wires with respect to each other (the contact between the intermediate and outer wires then being a relatively punctiform contact), the better the outer wires will mechanically encase the intermediate wire, and the better the permeability of each inner strand, the wires of which will then be uniformly distributed within each of the intermediate and outer layers. This mechanical integrity makes it possible to avoid, on the one hand, that all the filaments of the intermediate layer are combined together in contact with each other under the action of the mechanical forces exerted by the assembly tools during the manufacture of the cord, and, on the other hand, that all the filaments of the intermediate layer are combined together in contact with each other under the action of the pressure of the elastomeric compound penetrating the cord during the manufacture of the ply comprising the cord or the tire comprising the cord.

Furthermore, for a given lay length p3, by increasing the ratio (p3-p2)/p3, the spacing of the wires in the middle layer of each inner strand decreases. One skilled in the art would expect to see a decrease in the permeability of the inner strands. However, completely unexpectedly, as shown by the comparative tests described below, by increasing the ratio (p3-p2)/p3, the interplay of the middle layer of each inner strand did decrease, but the size of the radial passage window for the elastomeric compound increased, which means that the permeability of each inner strand was significantly increased.

Advantageously, the lay lengths p2 and p3 satisfy the relation (p3-p2)/p3 ≦ 0.55, preferably (p3-p2)/p3 ≦ 0.53. Below these values, the size of the radial passage window for the elastomeric compound is at a maximum, making it possible to optimize the permeability of each internal strand.

Advantageously, the lay length p2 satisfies 8mm ≦ p2 ≦ 16mm, preferably 8mm ≦ p2 ≦ 14mm, more preferably 8mm ≦ p2 ≦ 12 mm.

Advantageously, the lay length p3 satisfies 10mm ≦ p3 ≦ 40mm, preferably 15mm ≦ p3 ≦ 35mm, more preferably 15mm ≦ p3 ≦ 25mm, and still more preferably 17mm ≦ p3 ≦ 23 mm.

The lay lengths p2 and p3 within these preferred ranges make it possible to obtain cords exhibiting mechanical properties matching the use of the tire, relatively low cost and relatively low linear cord weight.

By definition, the diameter of a strand is the diameter of the smallest circle within which the strand may circumscribe.

Advantageously, K is 2, 3 or 4, preferably K is 3 or 4.

In one embodiment, L is equal to 7, 8, 9 or 10, preferably L is 8, 9 or 10, more preferably L is 8 or 9.

In a first variant, K is 2 and L is 7 or 8.

In a second variant, K is 3 and L is 7, 8 or 9, preferably K is 3 and L is 8 or 9. The case of L ═ 8 favors the unsaturation of the outer layer of the cord and therefore the penetration of the cord between the outer strands. The case of L-9 maximizes the number of outer strands and thus the breaking strength of the cord.

In a third variant, K is 4 and L is 7, 8, 9 or 10, preferably K is 4 and L is 9 or 10.

In these embodiments, in particular in the K-3 or 4 embodiments, when the cord is not sufficiently penetrated, there is a risk that significant diffusion of the corrosive agent can be seen between the K-3 or 4 inner strands, which delimit a central capillary, which greatly facilitates the diffusion of the corrosive agent along the cord. This disadvantage can be overcome by making the cord permeable by the elastomeric compound which then prevents the corrosive agents from entering the central capillary and, in the extreme case of the central capillary itself being permeable, from diffusing along the cord.

As already mentioned above, since the cord according to the invention has a configuration with K >1, the strongest transverse load applied to the cord when tensioning the cord is the transverse load applied between the inner strands, unlike a cord in which K is 1 and the strongest transverse load is the transverse load applied to the inner strands by the outer strands. Known from the prior art are cords having a configuration of K >1 and comprising a plurality of external strands such that the outer layer of the cord is saturated, so as to maximize the breaking strength by adding a maximum number of external strands. Herein, since the outer layer of the cord is unsaturated, in one aspect, the cord has spaces between the outer strands that allow the elastomeric compound to pass through, making the cord less susceptible to corrosion. On the other hand, despite the reduced number of outer strands, the unsaturation of the outer layer of the cord allows the elastomeric compound to penetrate between the outer strands on the one hand and the inner strands on the other hand, forming a cushion body of elastomeric compound that at least partially absorbs the transverse loads exerted between the inner strands. Thus, a better compromise between breaking strength and corrosion resistance is achieved compared to a similar cord having a saturated outer layer of the cord.

In embodiments that promote the permeability of the cord, the outer layer of the cord is fully unsaturated.

By definition, a fully unsaturated layer with strands, as opposed to a layer that is not fully unsaturated, is such that there is sufficient space in the layer to add at least one (X +1) th strand having the same diameter as the X strands of the layer, so the strands may or may not touch each other. In this particular case, there is sufficient space in the outer layer of the cord to add at least one (L +1) th strand having the same diameter as the L outer strands of the outer layer of the cord.

Thus, advantageously, the sum SIE of the inter-strand spacings E of the outer layers of the cord satisfies SIE ≧ DE. The sum SIE is the sum of the spacing E of the strands of each pair of adjacent strands separated in a layer. In a cross-section of the cord perpendicular to the main axis of the cord, the pitch of the strands of the ply is defined as the shortest distance of two adjacent strands in the average split ply. The spacing E of the strands is thus calculated by dividing the sum SIE by the number of spaces in the spacer.

In another embodiment, which promotes a compromise between permeability and breaking strength, the outer layer of the cord is not fully unsaturated.

The not fully unsaturated layer with strands is such that there is not enough space in the layer to add at least one (X +1) th strand with the same diameter as the X strands of the layer. In this particular case, there is not enough space in the outer layer to add at least one (L +1) th outer strand having the same diameter as the L outer strands of the cord outer layer. Thus, the sum SIE of the inter-strand spacings E of the outer layers of the cord satisfies SIE < DE. The sum SIE is the sum of the spacing E of the strands of each pair of adjacent strands separated in a layer. In a cross-section of the cord perpendicular to the main axis of the cord, the pitch of the strands of the ply is defined as the shortest distance of two adjacent strands in the average split ply. The spacing E of the strands is thus calculated by dividing the sum SIE by the number of spaces in the spacer.

By definition, the diameter DI of the inner strand is the diameter of the smallest circle that can circumscribe the inner strand therein. The diameter DE of the outer strands is the diameter of the smallest circle within which the outer strands may circumscribe.

In a preferred embodiment, the inner layer of the cord is wound in a spiral and with a non-zero lay length pi and the outer layer of the cord is wound in a spiral and with a non-zero lay length pe around the inner layer of the cord.

In one embodiment which is particularly advantageous with regard to the permeability of the cord, the inner layer of the cord is wound in a spiral in the direction of the inner layer of the cord with a pitch pi, the outer layer of the cord is wound in a spiral in the direction of the outer layer of the cord with a pitch pe, and the cord satisfies one and/or the other of the following characteristics:

the direction of the inner layer of the cord is different from the direction of the outer layer of the cord,

pi is different from pe.

In this embodiment, the cord has a cylindrical layered structure (as opposed to a compact structure) to promote the permeability of the cord.

In another embodiment, the inner layer of the cord is wound in a spiral form and with a pitch pi in the direction of the inner layer of the cord, the outer layer of the cord is wound in a spiral form and with a pitch pe in the direction of the outer layer of the cord, and the cord satisfies the following characteristics:

the direction of the inner layer of the cord is the same as the direction of the outer layer of the cord,

-pi equals pe.

In this embodiment, the high permeability of the inner strands makes it possible to obtain a cord exhibiting a satisfactory permeability, despite the compact structure of the cord (which is difficult to penetrate).

Optionally, the inner wire of each inner strand has a diameter d1 greater than or equal to the diameter d1 'of each inner wire of each outer strand, preferably each inner wire of each inner strand has a diameter d1 equal to the diameter d1' of each inner wire of each outer strand. Thus, the same diameter of the wires is used in the inner layer of each inner and outer strand, thereby limiting the number of different wires that need to be managed in the process of manufacturing the cord.

Optionally, each inner wire of each inner strand has a diameter d1 greater than or equal to the diameter d3 'of each outer wire of each outer strand, preferably each inner wire of each inner strand has a diameter d1 greater than the diameter d3' of each outer wire of each outer strand.

Optionally, each outer wire of each inner strand has a diameter d3 greater than or equal to the diameter d3 'of each outer wire of each outer strand, preferably each outer wire of each inner strand has a diameter d3 greater than the diameter d3' of each outer wire of each outer strand. Preferably, by virtue of the features d3> d3', each outer filament of each inner strand may be able to withstand the radial component of the force exerted by the outer strand on each inner strand when the cord is under tension. This characteristic d3> d3 'makes it possible to restore or even improve the breaking strength of the cord compared with cords comprising arches formed by external strands or compared with cords in which d3 ≦ d 3'. Preferably, 1< d3/d 3'≦ 2, more preferably 1< d3/d 3' ≦ 1.5, still more preferably 1< d3/d 3'≦ 1.25 or 1.25< d3/d 3' ≦ 1.5.

In an advantageous embodiment, the outer layer of cord is wound around the inner layer of cord in the winding direction of the outer layer of cord, and the respective outer layer of each inner strand and outer strand is wound around the intermediate layer of each inner strand and the inner layer of each outer strand, respectively, in the same winding direction, which is opposite to the winding direction of the cord. In this embodiment, the winding direction of the cord opposite to the winding direction of the respective outer layer of each inner and outer strand gives the cord better permeability, in particular between the outer strands. The inventors propose the following assumptions: by means of these winding directions, the external threads of the external strands cross the external threads of each internal strand so as to form a contact area of relative punctiform shape different from the cords in which the winding direction of the cords is the same as the winding direction of the external layers of each internal and external strand and the external threads of the external strands cross the external threads of the internal strands, so as to form a contact area of less punctiform shape but more linear shape, which hinders the passage of the elastomeric compound up to the internal layer.

Inner strand of a cord according to the invention

Advantageously, the sum of the wire spacings of the intermediate layers of each inner strand, SI2, satisfies SI2< d3, preferably SI2 ≦ 0.8x d3, where d3 is the diameter of each outer wire of each inner strand. The sum SI2 is the sum of the filament spacing of each pair of adjacent filaments in the separator layer. In a cross-section of the cord perpendicular to the main axis of the cord, the filament spacing of a layer is defined as the shortest distance of two adjacent filaments in an average separation layer. Thus, the spacing of the wires is calculated by dividing the sum SI2 by the spatial number of wires in the separator.

Since the diameter d3 of the outer filaments in the outer layer of each inner strand is preferably greater than the sum SI2, the outer filaments are prevented from entering the middle layer. This ensures good structural stability, thereby reducing the risk of modifying the radial passage window for the elastomeric compound and thus reducing the risk of reducing the good permeability of each internal strand.

Advantageously, the middle layer of each inner strand is unsaturated.

By definition, an unsaturated layer with filaments is a layer such that sufficient space is left between the filaments to allow the passage of the elastomeric compound. An unsaturated layer thus means that the filaments in the layer do not touch and that there is sufficient space between two adjacent filaments in the layer to allow the elastomeric compound to pass through the layer. In contrast, a saturated layer with strands makes insufficient space between the filaments of the layer to allow the passage of the elastomeric compound, for example because the two filaments of each pair in the layer are in contact with each other.

Advantageously, the spacing between the wires of the intermediate layer of each inner strand is greater than or equal to 5 μm. Preferably, the spacing between the wires of the intermediate layer of each inner strand is greater than or equal to 15 μm, more preferably greater than or equal to 35 μm, still more preferably greater than or equal to 50 μm, and the height is preferably greater than or equal to 60 μm.

The fact that the intermediate layer of each internal strand is unsaturated advantageously makes it easier for the elastomeric compound to penetrate into each internal strand, thus making each internal strand less sensitive to corrosion.

In embodiments that promote a compromise between permeability and breaking strength of each inner strand, the middle layer of each inner strand is not fully unsaturated.

By definition, a layer that is not fully unsaturated makes insufficient space in the layer to add at least one (X +1) th filament having the same diameter as the X filaments of the layer. In this particular case, there is not enough space in the intermediate layer to add at least one (M +1) th intermediate wire having the same diameter as the M intermediate wires of the intermediate layer. In other words, the not completely unsaturated intermediate layer of each inner strand means that the sum SI2 of the filament spacings I2 of the intermediate layer is smaller than the diameter d2 of the intermediate filaments of the intermediate layer. Thus, advantageously, the sum SI2 of the wire spacing of the middle layers of each inner strand satisfies SI2< d 2.

The fact that the intermediate layer of each inner strand is not fully unsaturated makes it possible to ensure the structural stability of the intermediate layer. This then reduces the risk of the external threads entering the intermediate layer, which would modify the radial passage window for the elastomeric compound and therefore reduce the good permeability of each internal strand.

Furthermore, the fact that the intermediate layer of each inner strand is not completely unsaturated makes it possible to ensure that each inner strand comprises a relatively high number of intermediate filaments and therefore exhibits a relatively high breaking strength.

In another embodiment that promotes the permeability of each inner strand, the middle layer of each inner strand is fully unsaturated.

By definition, a layer with complete unsaturation of the filaments is such that there is enough space in the layer to add at least one (X +1) th filament with the same diameter as the X filaments of the layer, so that the plurality of filaments may or may not be in contact with each other. In this particular case, there is sufficient space in the middle layer of each inner strand to add at least one (M +1) th intermediate wire having the same diameter as the M intermediate wires of the middle layer. In other words, a fully unsaturated intermediate layer of the inner strands means that the sum SI2 of the filament spacing I2 of the intermediate layer is greater than or equal to the diameter d2 of the intermediate filaments of the intermediate layer. Thus, advantageously, the sum of the wire spacings of the intermediate layers of each inner strand, SI2, satisfies SI2 ≧ d 2.

Advantageously, the outer layer of each inner strand is unsaturated, preferably fully unsaturated. In a similar manner to the intermediate layer, the fact that the outer layer of each inner strand is unsaturated advantageously makes it easier for the elastomeric compound to penetrate into each inner strand, thus making each inner strand less sensitive to corrosion.

Advantageously, the spacing between the wires of the outer layer of each inner strand is greater than or equal to 5 μm. Preferably, the outer layer of each inner strand has a filament spacing greater than or equal to 15 μm, more preferably greater than or equal to 35 μm, still more preferably greater than or equal to 50 μm, and a height greater than or equal to 60 μm.

By definition, a fully unsaturated layer, as opposed to a layer that is not fully unsaturated, is such that there is sufficient space in the layer to add at least one (X +1) th filament having the same diameter as the X filaments of the layer, so that the plurality of filaments may or may not be in contact with each other. In this particular case, there is sufficient space in the outer layer of each inner strand to add at least one (N +1) th wire having the same diameter as the N outer wires of the outer layer. In other words, a fully unsaturated outer layer per inner strand means that the sum SI3 of the filament spacings I3 of the outer layers is greater than or equal to the diameter d3 of the outer filaments of the outer layers. Thus, advantageously, the sum of the wire spacings of the outer layers of each inner strand SI3 satisfies SI3 ≧ d 3. The sum SI3 is the sum of the filament spacing separating each pair of adjacent filaments in the outer layer. In a cross-section of the cord perpendicular to the main axis of the cord, the filament spacing of a layer is defined as the shortest distance of two adjacent filaments in an average separation layer. Thus, the filament spacing is calculated by dividing the sum SI3 by the number of spaces separating the filaments in the outer layer.

The fact that the outer layer of each inner strand is completely unsaturated makes it possible to maximize the penetration of the elastomeric compound into each inner strand, thus making each inner strand less sensitive to corrosion.

In a preferred embodiment, Q ═ 1. In the embodiment with Q ═ 1, when, unlike the present invention, the cord is not sufficiently penetrated, there is a risk that the inner filaments of each inner strand can be seen to leave each inner strand, and even the cord, radially under the effect of the repeated compression loads applied to the cord. By means of the invention, due to the excellent permeability of each inner strand, despite the fact that Q ═ 1, the elastomeric compound acts like a coating around each inner strand, in particular around the outer and intermediate layers of each inner strand, avoiding the inner wire to come loose even under repeated compression loads.

In a preferred embodiment, each inner wire of each inner strand has a diameter d1 greater than or equal to the diameter d3 of each outer wire of each inner strand, and a height preferably of 1. ltoreq. d1/d 3. ltoreq.1.30. The use of a diameter satisfying d1> d3 makes it possible to promote the permeability of the elastomeric compound through the outer layer. When d1> d3, then d1/d3 ≦ 1.30 is highly preferred, which makes it possible, on the one hand, to control the structural stability of the outer layer and, on the other hand, to make the invention more advantageous because of the relatively small amount of unsaturation produced by the difference between d1 and d 3. The use of a diameter satisfying d 1-d 3 makes it possible to limit the number of different filaments to be managed in the manufacture of the cord and also makes the invention more advantageous since the equivalence between d1 and d3 does not produce unsaturations.

In another advantageous embodiment, each inner wire of each inner strand has a diameter d1 greater than or equal to the diameter d2 of each intermediate wire of each inner strand, the height preferably being 1. ltoreq. d1/d 2. ltoreq.1.30. The use of diameters satisfying d1> d2 enables the permeability of the elastomeric compound through the intermediate layer to be promoted. When d1> d2, then d1/d2 ≦ 1.30 is highly preferred, which makes it possible, on the one hand, to control the structural stability of the intermediate layer and, on the other hand, to make the invention more advantageous because of the relatively small amount of unsaturation produced by the difference between d1 and d 2. The use of a diameter satisfying d 1-d 2 makes it possible to limit the number of different filaments to be managed in the manufacture of the cord and also makes the invention more advantageous since the equivalence between d1 and d2 does not produce unsaturations.

In a preferred embodiment, Q is 1, M is 5 or 6 and N is 10, 11 or 12, preferably Q is 1, M is 5 or 6, N is 10 or 11, more preferably Q is 1, M is 6 and N is 11.

More advantageously, Q is 1, M is 5 or 6, N is 10 or 11,

each inner wire of each inner strand has a diameter d1 greater than or equal to the diameter d2 of each intermediate wire of each inner strand, and

the inner wire of each inner strand has a diameter d1 greater than or equal to the diameter d3 of each outer wire of each inner strand.

Still more advantageously, Q-1, M-6, N-11,

the inner wire of each inner strand has a diameter d1 greater than the diameter d2 of each intermediate wire of each inner strand, and

the inner wire of each inner strand has a diameter d1 greater than the diameter d3 of each outer wire of each inner strand.

Such inner strands exhibit the structural stability and permeability advantages described above. In particular, by using wires of different diameters, the unsaturation of the intermediate layer and of the outer layer, the incomplete saturation of the intermediate layer and the complete unsaturation of the outer layer are obtained.

Highly advantageously, in the case where each intermediate wire of each inner strand has a diameter d2 and each outer wire of each outer strand has a diameter d3, d2 is d 3. Thus, the same diameter of the wires is used in the intermediate and outer layers of each inner strand, thereby limiting the number of different wires that need to be managed in the process of manufacturing the cord.

Advantageously, each internal strand is of the ex-situ rubberized type. By rubberizing ex situ is meant that each inner strand consists of the filaments of the respective layer without any polymeric compound, in particular without any elastomeric compound, before assembling the outer layer of the cord and before assembling the cord.

Outer strand of a cord according to the invention

Advantageously, the outer layer of each outer strand is unsaturated, preferably fully unsaturated. The fact that the outer layer of each external strand is unsaturated advantageously makes it easier for the elastomeric compound to pass into and through each external strand, thus making each external strand less sensitive to corrosion.

Advantageously, the spacing between the wires of the outer layer of each outer strand is greater than or equal to 5 μm. Preferably, the outer layer of each outer strand has a filament spacing greater than or equal to 15 μm, more preferably greater than or equal to 35 μm, still more preferably greater than or equal to 50 μm, and a height greater than or equal to 60 μm.

The outer layer of each outer strand is preferably fully unsaturated, i.e. there is sufficient space in the outer layer to add at least one (N '+ 1) th filament having the same diameter as the N' filaments of the outer layer. In other words, a fully unsaturated outer layer of each outer strand means that the sum SI 3' of the filament spacings I3 ' of the outer layers is greater than or equal to the diameter d3' of the outer filaments of the outer layers. Thus, advantageously, the sum of the filament spacings of the outer layers of each outer strand SI3 satisfies SI 3'≧ d 3'. The sum SI 3' is the sum of the filament spacing separating each pair of adjacent filaments in the outer layer. The thread spacing of a layer is defined as the shortest distance of two adjacent threads in the average separation layer, in a cross section of the cord perpendicular to the main axis of the cord. Thus, the filament spacing is calculated by dividing the sum SI 3' by the number of spaces separating the filaments in the outer layer.

The fact that the outer layer of each outer strand is completely unsaturated makes it possible to maximize the elastomeric compound that penetrates into and through each outer strand, thus making each outer strand less sensitive to corrosion.

The high permeability of the outer strands described above therefore allows the elastomeric compound to penetrate better between the outer strands on the one hand and each inner strand on the other hand. In this way, the camber is at least partially recovered even more, while imparting excellent permeability to the cord, and the drop in breaking strength of the cord is limited. Furthermore, this feature allows the elastomeric compound to penetrate between the outer layers of the inner and outer strands, forming a cushion body of elastomeric compound that at least partially absorbs the radial component of the force between the inner and outer strands.

In some preferred embodiments, each inner wire of each outer strand has a diameter d1 'that is greater than or equal to the diameter d3' of each outer wire of each outer inner strand, and preferably 1. ltoreq. d1'/d 3'. ltoreq.1.30 in height. The use of a diameter satisfying d1 '> d3' enables to promote the permeability of the elastomeric compound through the outer layer. When d1 '> d3', then d1'/d3' ≦ 1.30 is highly preferred, which makes it possible on the one hand to control the structural stability of the outer layer and on the other hand to make good permeability of each outer strand more beneficial due to the relatively small amount of unsaturation created by the difference between d1 'and d 3'. The use of a diameter satisfying d1'═ d3' makes it possible to limit the number of different filaments to be managed in the manufacture of the cord and also to make the invention more advantageous since the equivalence between d1 'and d3' does not produce unsaturations.

Double-layer outer strand

In one embodiment, which facilitates the compromise between the diameter of the cord and the breaking strength, each outer strand has two layers. In this embodiment, the outer layer of each outer strand is wrapped around the inner layer of each outer strand in contact with the inner layer of each outer strand. In this embodiment, each outer strand comprises a collection of wires that is composed of neither more nor less than two layers with wires, which means that the collection of wires has two layers with wires, not one layer, nor three layers, but only two layers.

In preferred embodiments, Q' is 1, 2, 3 or 4.

In embodiments that make it possible to reduce the diameter of the cord, Q '═ 1, N' ═ 5, or 6, preferably Q '═ 1 and N' ═ 6.

In a preferred embodiment capable of increasing the breaking strength of the cord relative to the embodiment of Q ' ═ 1, Q ' ═ 2, 3, or 4, preferably Q ' ═ 3 or 4. Unlike the embodiment in which Q '═ 1 and under the effect of the repeated compression loads applied to the cord there is a risk of seeing the inner filaments of the outer strands projecting radially from the outer strands and even from the cord, the presence of a plurality of filaments (Q' >1) in the inner layer of each outer strand makes it possible to reduce this risk, since the compression loads are then distributed over the plurality of filaments of the inner layer.

In these preferred embodiments of Q ' >1, in particular in the embodiments of Q ' ═ 3 or 4, when the strands are not sufficiently infiltrated, there is a risk that significant diffusion of corrosive agents can be seen between the Q ' ═ 3 or 4 internal wires, which define the central capillary, which greatly promotes the diffusion of corrosive agents along each strand. This disadvantage can be overcome by making the strands permeable to the elastomeric compound, which then prevents the corrosive agents from entering the central capillary and, in the extreme case of the central capillary itself being permeable, from diffusing along the strands.

In a preferred embodiment of Q '>1, N' ═ 7, 8, 9 or 10, preferably N '═ 8, 9 or 10, more preferably N' ═ 8 or 9.

In these embodiments of Q ' >1, advantageously each outer strand has a cylindrical layer, i.e. a strand in which Q ' inner filaments are wound with a lay length p1' in the inner layer direction of each outer strand, N ' outer filaments are wound around the intermediate layer with a lay length p 3' in the outer layer direction of each outer strand, p1' being different from p 3' and/or the inner layer direction of the outer strand being different from the outer layer direction of the outer strand.

In a first variant, Q '═ 2 and N' ═ 7 or 8, preferably Q '═ 2 and N' ═ 7.

In a second variant, Q '═ 3 and N' ═ 7, 8 or 9, preferably Q '═ 3 and N' ═ 8.

In a third variant, Q '═ 4 and N' ═ 7, 8, 9 or 10, preferably Q '═ 4 and N' ═ 9.

Advantageously, the inner layer of cord is wound in the direction of the inner layer of cord, and the intermediate layer and the outer layer of each inner strand are each wound in the same winding direction as the direction of the inner layer of cord.

Advantageously, the outer layer of the cord is wound in the direction of the outer layer of the cord, and the inner layer (when Q' >1), the intermediate layer and the outer layer of each outer strand are each wound in the same winding direction as the direction of the outer layer of the cord.

In one embodiment, the direction of the inner layer of cords is the same as the direction of the outer layer of cords. In this embodiment, manufacture is relatively easy because, unlike the previous embodiments, there is no need to distinguish between the winding directions of the inner and outer layers of the cord. However, the contact between the outer filaments of the outer layers of inner and outer strands is relatively long, which may give rise to the following assembly defects in the case of certain combinations of lay length, diameter and configuration of the cord: such as assembly defects caused by unwanted slipping of the outer strands in the grooves formed between the inner strands.

In another embodiment, the direction of the inner layer of cords and the direction of the outer layer of cords are opposite directions. In this embodiment, the risk that the outer strands may slip undesirably in the grooves formed between the inner strands is reduced due to the intersection between the inner and outer strands.

Three-layer external strand

In another particularly advantageous embodiment for improving the breaking strength of the cord, each outer strand has three layers and comprises:

an intermediate layer consisting of M' intermediate filaments wound around the inner layer, and

an outer layer consisting of N' outer filaments wound around the intermediate layer.

In this embodiment, the outer layer of each outer strand is wrapped around the intermediate layer of each outer strand in contact with the intermediate layer of each outer strand, and the intermediate layer of each outer strand is wrapped around the inner layer of each outer strand in contact with the inner layer of each outer strand. In this embodiment, each outer strand comprises a collection of wires that is composed of neither more nor less than three layers of wires, which means that the collection of wires has three layers of wires, not two layers, nor four layers, but only three layers.

Advantageously, the sum of the filament spacings of the intermediate layers, SI2', satisfies SI2' < d3', preferably SI2' ≦ 0.8x d3', where d3' is the diameter of each outer filament of each outer strand. In a similar manner to the inner strands, the outer wires are prevented from entering the intermediate layer, because the diameter d3 'of the outer wires of each outer strand is preferably greater than the sum SI 2'. This ensures good structural stability, thereby reducing the risk of modifying the radial passage window for the elastomeric compound and thus reducing the risk of reducing the good permeability of each external strand. The sum SI2' is the sum of the wire spacing separating each pair of adjacent wires in the middle layer. The thread spacing of a layer is defined as the shortest distance of two adjacent threads in the average separation layer, in a cross section of the cord perpendicular to the main axis of the cord. Thus, the wire spacing is calculated by dividing the sum SI2' by the number of spaces separating the wires in the middle layer.

Advantageously, the intermediate layer of each outer strand is unsaturated.

Preferably, the inter-filament spacing of the intermediate layer of each outer strand is greater than or equal to 5 μm. Preferably, the inter-filament spacing of the intermediate layer of each outer strand is greater than or equal to 15 μm, more preferably greater than or equal to 35 μm, still more preferably greater than or equal to 50 μm, and the height is preferably greater than or equal to 60 μm.

The fact that the intermediate layer of each external strand is unsaturated advantageously makes it easier for the elastomeric compound to pass up to the centre of each external strand, thus making each external strand less sensitive to corrosion.

In embodiments that promote a compromise between permeability and breaking strength of each inner strand, the middle layer of each outer strand is not fully unsaturated.

In this embodiment, the middle layer of each outer strand is preferably not fully unsaturated, i.e. there is not enough space in the middle layer to add at least one (M '+ 1) th filament having the same diameter as the M' filaments of the middle layer. In other words, the not completely unsaturated intermediate layer of each outer strand means that the sum SI2' of the inter-wire distances I2' of the intermediate layer is smaller than the diameter d2' of the intermediate wires of the intermediate layer. In other words, the not completely unsaturated intermediate layer of the outer strands means that the sum SI2' of the filament spacings I2' of the intermediate layer is smaller than the diameter d2' of the intermediate filaments of the intermediate layer. Thus, advantageously, the sum SI2' of the wire spacings of the intermediate layers of outer strands satisfies SI2' < d2 '.

The fact that the intermediate layer of each outer strand is not fully unsaturated makes it possible to ensure the structural stability of the intermediate layer. Furthermore, the fact that the intermediate layer of each outer strand is not completely unsaturated makes it possible to ensure that each outer strand comprises a relatively high number of intermediate filaments and therefore exhibits a relatively high breaking strength.

In another embodiment that promotes the permeability of each outer strand, the middle layer of each outer strand is fully unsaturated.

By definition, a layer with complete unsaturation of the filaments is such that there is enough space in the layer to add at least one (X +1) th filament with the same diameter as the X filaments of the layer, so that the plurality of filaments may or may not be in contact with each other. In this particular case, there is sufficient space in the middle layer of each outer strand to add at least one (M '+ 1) th middle filament having the same diameter as the M' middle filaments of the middle layer. In other words, a fully unsaturated intermediate layer of the outer strands means that the sum SI2' of the filament spacings I2' of the intermediate layer is greater than or equal to the diameter d2' of the intermediate filaments of the intermediate layer. Thus, advantageously, the sum of the wire spacing of the middle layers of outer strands SI2' satisfies SI2' ≧ d2 '.

In some preferred embodiments, each inner wire of each outer strand has a diameter d1 'that is greater than or equal to the diameter d2' of each intermediate wire of each outer strand, and preferably 1. ltoreq. d1'/d 2'. ltoreq.1.30 in height. The use of a diameter satisfying d1 '> d2' enables to promote the permeability of the elastomeric compound through the intermediate layer. When d1 '> d2', then d1'/d2' ≦ 1.30 is highly preferred, which makes it possible on the one hand to control the structural stability of the middle layer and on the other hand to make the good permeability of each outer strand more beneficial due to the relatively small amount of unsaturation created by the difference between d1 'and d 2'. The use of a diameter satisfying d1'═ d2' makes it possible to limit the number of different filaments to be managed in the manufacture of the cord and also to make the invention more advantageous since the equivalence between d1 'and d2' does not produce unsaturations. Highly advantageously, in the case where each intermediate wire of each outer strand has a diameter d2' and each outer wire of each outer strand has a diameter d3', d2 ═ d3 '. Thus, the same diameter of the wires is used in the intermediate and outer layers of each outer strand, thereby limiting the number of different wires that need to be managed in the process of manufacturing the cord.

In a preferred variant of this embodiment, Q ' ═ 1, 2, 3, or 4, preferably Q ' ═ 1, 2, or 3, more preferably Q ' ═ 1 or 3.

In a preferred embodiment, Q' is 1.

In this embodiment of Q ' ═ 1, it is advantageous for each outer strand to have a cylindrical layer, i.e. a strand in which M ' intermediate filaments are wound around the inner layer in the direction of the middle layer of the outer strand with a pitch p2', N ' outer filaments are wound around the middle layer in the direction of the outer layer of the outer strand with a pitch p 3', p2' being different from p 3' and/or the middle layer direction of the outer strand being different from the outer layer direction of the outer strand.

In the embodiment with Q '═ 1, M intermediate filaments are wound around the inner layer with a lay length p2', and N 'outer filaments are wound around the intermediate layer with a lay length p 3', the lay lengths p2 'and p 3' then advantageously satisfying: 0.36 is less than or equal to (p3 '-p 2')/p 3 is less than or equal to 0.57. This ratio (p 3' -p2 ')/p 3' makes it possible to obtain a relatively large radial passage window for the elastomeric compound within each external strand.

Advantageously, the lay lengths p2 'and p 3' satisfy the relationship 0.38 ≦ (p3 '-p 2')/p 3', preferably 0.40 ≦ (p 3' -p2 ')/p 3', more preferably 0.43 ≦ (p3 '-p 2')/p 3', still more preferably 0.45 ≦ (p 3' -p2 ')/p 3'. In a similar manner to the inner strands, the higher the ratio (p 3' -p2 ')/p 3', or in other words the greater the difference between p 3' and p2', the better the structural stability of each outer strand.

Advantageously, the lay lengths p2 'and p 3' satisfy the relation (p3 '-p 2')/p 3'≦ 0.55, preferably (p 3' -p2 ')/p 3' ≦ 0.53. Below these values, the size of the radial passage window for the elastomeric compound is at a maximum, making it possible to optimize the permeability of each external strand.

Moreover, the high permeability of the outer strands described above allows the elastomeric compound to penetrate better between the outer strands on the one hand and between the outer and inner strands on the other hand. In this way, the arch is at least partially restored or even more.

Advantageously, the lay length p2 'satisfies 8 mm. ltoreq. p 2'. ltoreq.16 mm, preferably 8 mm. ltoreq. p2 '. ltoreq.14 mm, more preferably 8 mm. ltoreq. p 2'. ltoreq.12 mm.

Advantageously, the lay length p 3' satisfies 10 mm. ltoreq. p3 '.ltoreq.40 mm, preferably 15 mm. ltoreq. p3 '.ltoreq.35 mm, more preferably 15 mm. ltoreq. p3 '.ltoreq.25 mm, still more preferably 17 mm. ltoreq. p 3' 23 mm.

The lay lengths p2 'and p 3' in these preferred ranges make it possible to obtain cords exhibiting mechanical properties matching the use of the tire, relatively low cost and relatively low linear cord weight.

In a preferred embodiment, Q ' ═ 1, M ' ═ 5 or 6 and N ' ═ 10, 11 or 12, preferably Q ' ═ 1, M ' ═ 5 or 6, N ' ═ 10 or 11, more preferably Q ' ═ 1, M ' ═ 6 and N ' ═ 11.

It is more advantageous that the first and second electrodes are formed of a metal,

-Q ' ═ 1, M ' ═ 5 or 6, N ' ═ 10 or 11,

each inner wire of each outer strand has a diameter d1 'greater than or equal to the diameter d2' of each intermediate wire of each outer strand, and

each inner wire of each outer strand has a diameter d1 'greater than or equal to the diameter d3' of each outer wire of each outer strand.

It is still more advantageous that,

-Q’＝1，M’＝6，N’＝11，

each inner wire of each outer strand has a diameter d1 'greater than the diameter d2' of each intermediate wire of each outer strand, and

each inner wire of each inner strand has a diameter d1 'greater than the diameter d3' of each outer wire of each outer strand.

Such outer strands exhibit the structural stability and permeability advantages described above. In particular, by using wires of different diameters, an unsaturation of the intermediate layer and of the outer layer, an incomplete saturation of the intermediate layer and a complete unsaturation of the outer layer are obtained.

In a preferred embodiment capable of increasing the breaking strength of the cord relative to the embodiment of Q ' ═ 1, Q ' ═ 2, 3, or 4, preferably Q ' ═ 3 or 4.

In these embodiments of Q '>1, each outer strand advantageously has a cylindrical layer, i.e. a strand in which Q' inner filaments are wound with a lay length p1 'in the direction of the inner layer of the outer strand, M' intermediate filaments are wound with a lay length p2 'around the inner layer in the direction of the middle layer of the outer strand, and N' outer filaments are wound with a lay length p3 'around the middle layer in the direction of the outer layer of the outer strand, p1', p2 'and p 3' each differing from each other in pairs and/or the direction of adjacent layers of the outer strand.

In another preferred embodiment, Q '═ 3, M' ═ 8 or 9 and N '═ 13, 14 or 15, preferably, Q' ═ 3, M '═ 8 or 9, N' ═ 14 or 15, more preferably, Q '═ 3, M' ═ 9, N '═ 14 or 15, still more preferably, Q' ═ 3, M '═ 9 and N' ═ 15. In the embodiment of Q ═ 3, when the cord is not sufficiently penetrated, there is a risk that significant diffusion of the corrosive agent can be seen between the Q' ═ 3 internal threads, which delimit the central capillary, which greatly promotes the diffusion of the corrosive agent along the cord. In the embodiment of Q' ═ 3, the elastomeric compound prevents the corrosive agents from entering the central capillary when the cord is very well penetrated, and in the extreme case of the central capillary itself being penetrated, from diffusing along the cord.

It is more advantageous that the first and second electrodes are formed of a metal,

-Q ' ═ 3, M ' ═ 8 or 9, N ' ═ 14 or 15,

the inner wire of each outer strand has a diameter d1 'greater than or equal to the diameter d2' of each intermediate wire of each outer strand, and

the inner wire of each outer strand has a diameter d1 'greater than or equal to the diameter d3' of each outer wire of each outer strand.

It is still more advantageous that,

-Q ' ═ 3, M ' ═ 9, N ' ═ 14 or 15,

the inner wire of each outer strand has a diameter d1 'greater than the diameter d2' of each intermediate wire of each outer strand, and

the inner wire of each outer strand has a diameter d1 'greater than the diameter d3' of each outer wire of each outer strand.

Such outer strands exhibit the structural stability and permeability advantages described above. In particular, by using wires of different diameters, an unsaturation of the intermediate layer and of the outer layer, an incomplete saturation of the intermediate layer and a complete unsaturation of the outer layer are obtained.

Optionally, the inner wire of each inner strand has a diameter d1 greater than or equal to the diameter d2 'of each intermediate wire of each outer strand, preferably the inner wire of each inner strand has a diameter d1 greater than the diameter d2' of each intermediate wire of each outer strand.

Very advantageously, each intermediate wire of each inner strand has a diameter d2 greater than or equal to the diameter d2 'of each intermediate wire of each outer strand, preferably each intermediate wire of each inner strand has a diameter d2 greater than the diameter d2' of each intermediate wire of each outer strand.

In one embodiment, each outer strand is of the in situ rubberized type. Such strands comprise, before assembling the cord, a layer of polymeric compound, in particular of elastomeric compound, which is arranged between at least two radially adjacent layers with filaments, possibly between each of the radially adjacent layers with filaments. Such strands rubberized in situ are described in particular in WO 2010054790.

In another embodiment, each outer strand is of the ex situ rubberized type. By ex-situ rubberization is meant that each external strand consists of the individual layers of filaments without any polymeric compound, in particular without any elastomeric compound, before the cord is assembled.

Tire according to the invention

Another subject of the invention is a tire comprising a cord as defined above.

The cord is most particularly intended for industrial vehicles selected from heavy vehicles (for example "heavy load vehicles", i.e. subways, buses, road transport vehicles (trucks, tractors, trailers), off-road vehicles), agricultural or construction site vehicles, or other transport or handling vehicles.

Preferably, the tyre is for a vehicle of the construction site type. The dimensions of the tire are of the type wr U, W representing, as known to the person skilled in the art:

a nominal aspect ratio H/B (in the case where it is in the form H/B) defined by ETRTO, H being the cross-sectional height of the tire, B being the cross-sectional width of the tire,

-H.00 or B.00 (in the case where it is in H.00 or B.00 form), wherein H ═ B, H and B are as defined above,

u denotes the diameter (in inches) of the rim seat on which the tire is intended to be mounted, and R denotes the type of carcass reinforcement of the tire, in this case the radial direction.

Examples of such dimensions are e.g. 40.00R 57 or 59/80R 63.

Preferably U.gtoreq.35, more preferably U.gtoreq.49, even more preferably U.gtoreq.57.

In one embodiment, the tire has a carcass reinforcement anchored in two beads and radially surmounted by a crown reinforcement, itself surmounted by a tread, the crown reinforcement being joined to the beads by two sidewalls, the carcass reinforcement comprising at least one cord as defined above.

In another embodiment, the tire has a carcass reinforcement anchored in two beads and surmounted radially by a crown reinforcement, itself surmounted by a tread, the crown reinforcement being joined to the beads by two sidewalls and comprising at least one cord as defined above.

Advantageously, the carcass reinforcement comprises at least one carcass ply comprising filiform metal carcass reinforcing elements, each forming an angle of between 80 ° and 90 ° with the circumferential direction of the tyre.

Advantageously, the crown reinforcement comprises a working reinforcement comprising at least one cord as defined above.

Advantageously, the working reinforcement comprises at least one working ply comprising filiform metallic working reinforcing elements arranged substantially parallel to each other, each forming an angle at most equal to 60 °, preferably ranging from 15 ° to 40 °, with the circumferential direction of the tyre and formed by a cord as defined above.

In an advantageous embodiment, the working reinforcement comprises at least a first and a second working ply, each comprising a first and a second filiform metallic working reinforcing element, respectively, disposed substantially parallel to each other in each of the first and second working plies, each forming an angle at most equal to 60 °, preferably ranging from 15 ° to 40 °, with the circumferential direction of the tyre, and formed by a cord as defined above.

Advantageously, the crown reinforcement comprises a protective reinforcement comprising at least one protective ply comprising filiform metallic protective reinforcing elements arranged substantially parallel to each other, each filiform metallic protective reinforcing element forming an angle at least equal to 10 °, preferably ranging from 10 ° to 35 °, preferably from 15 ° to 30 °, with the circumferential direction of the tire.

In an advantageous embodiment, the protective reinforcement comprises a first and a second protective ply, each comprising a first and a second filiform metal protective reinforcing element, respectively, arranged substantially parallel to each other in each of the first and second protective ply, each forming an angle at least equal to 10 °, preferably ranging from 10 ° to 35 °, preferably from 15 ° to 30 °, with the circumferential direction of the tyre.

In a preferred embodiment, the protective reinforcement is interposed radially between the tread and the working reinforcement.

Advantageously, the crown reinforcement comprises an additional reinforcement comprising at least one additional ply comprising additional filiform metal reinforcing elements arranged substantially parallel to one another in the additional ply, each additional filiform metal reinforcing element forming an angle with the circumferential direction of the tire at most equal to 10 °, preferably ranging from 5 ° to 10 °.

In an advantageous embodiment, the additional reinforcement comprises a first and a second additional ply, each of which comprises a first and a second additional filiform metal reinforcing element, respectively, arranged substantially parallel to each other in each of the first and second additional plies, each of the first and second additional filiform metal reinforcing elements forming an angle at most equal to 10 °, preferably ranging from 5 ° to 10 °, with the circumferential direction of the tyre.

Drawings

The invention will be better understood from reading the following description, given purely by way of non-limiting example with reference to the accompanying drawings, in which:

figure 1 is a view of a cross section perpendicular to the circumferential direction of a tyre according to the invention;

FIG. 2 is a detail view of region II of FIG. 1;

figures 3 and 6 are schematic views of a section perpendicular to the cord axis (assuming it is straight and stationary) of [3x (0.38+ (6+11) x0.35) +9x (0.38+ (6+11) x0.30) ] +0.28 cords according to the first and fourth embodiments of the invention, respectively;

figure 4 is a schematic view of a cross section perpendicular to the cord axis (assuming it is straight and stationary) of a [2x (0.38+ (6+11) x0.35) +8x (0.38+ (6+11) x0.30) ] +0.28 cord according to a second embodiment of the invention;

figure 5 is a schematic view of a cross section perpendicular to the cord axis (assuming it is straight and stationary) of a [4x (0.38+ (6+11) x0.35) +10x (0.38+ (6+11) x0.30) ] +0.28 cord according to a third embodiment of the invention;

figures 7 and 8 are views similar to figures 3 and 6, respectively, of [3x (0.38+ (6+12) x0.35) +9x (0.38+ (6+12) x0.30) ] +0.28 cord according to fifth and sixth embodiments of the invention;

fig. 9 is a view similar to fig. 3 of a [3x (0.38+ (6+11) x0.35) +9x ((2+7) x0.40) ] +0.28 cord according to a seventh embodiment of the invention;

fig. 10 is a view similar to fig. 3 of a [3x (0.38+ (6+11) x0.35) +9x ((3+8) x0.38) ] +0.28 cord according to an eighth embodiment of the invention;

fig. 11 is a view similar to fig. 3 of a [3x (0.38+ (6+11) x0.35) +9x ((4+9) x0.35) ] +0.28 cord according to a ninth embodiment of the invention;

fig. 12 is a view similar to fig. 3 of a [3x ((1+5) x0.35+11x0.30)) +9x (0.30+ (6+11) x0.28) ] +0.28 cord according to a tenth embodiment of the invention;

fig. 13 is a view similar to fig. 3 of a [3x (0.45+ (6+11x0.38)) +9x ((3+9+15) x0.28) ] +0.28 cord according to an eleventh embodiment of the invention;

fig. 14 is a view similar to fig. 3 of a [3x (0.38+ (6+11) x0.35) +9x ((2+7) x0.32) ] +0.28 cord according to a twelfth embodiment of the invention;

figure 15 is a schematic view projected onto a plane containing the axis of each inner strand before assembling the cord according to the first embodiment of the invention; and

figure 16 shows a detail view of the region XV of the radial through window delimited by the threads of the middle layer and the threads of the outer layer of the outer strands in figure 15.

Detailed Description

Any numerical range expressed by the expression "between a and b" represents a numerical range extending from more than a to less than b (i.e. excluding the endpoints a and b), whereas any numerical range expressed by the expression "from a to b" means a numerical range extending from the endpoint "a" up to the endpoint "b", i.e. including the strict endpoints "a" and "b".

Examples of tires according to the invention

The figures show a reference frame X, Y, Z, which corresponds to the general axial direction (X), radial direction (Y) and circumferential direction (Z) of the tyre, respectively.

The "circumferential median plane" M of the tyre is the plane perpendicular to the axis of rotation of the tyre, disposed equidistant from the annular reinforcing structures of each bead and passing through the middle of the crown reinforcement.

Figures 1 and 2 show a tyre according to the invention, indicated as a whole by 10.

The tyre 10 is intended for heavy vehicles of the construction-site type, for example of the "dump truck" type. Thus, tire 10 has a size of the 53/80R63 type.

The tire 10 has a crown 12 reinforced by a crown reinforcement 14, two sidewalls 16 and two beads 18, each of these beads 18 being reinforced by a toroidal structure, in this case by a bead wire 20. The crown reinforcement 14 is radially surmounted by a tread 22 and connected to the beads 18 by sidewalls 16. The carcass reinforcement 24 is anchored in the two beads 18, in this case wound around the two bead wires 20 and comprising a turn-up 26 disposed towards the outside of the tyre 20, said tyre 20 being shown here fitted on a wheel rim 28. The carcass reinforcement 24 is radially surmounted by the crown reinforcement 14.

The carcass reinforcement 24 comprises at least one carcass ply 30, said carcass ply 30 comprising filiform metal carcass reinforcing elements 31 and extending from one bead 18 to the other bead 18 so as to form an angle of between 80 ° and 90 ° with the circumferential direction Z of the tyre 10.

The tire 10 also includes a seal ply 32 (commonly referred to as an "innerliner") composed of an elastomer, the seal ply 32 defining a radially inner surface 34 of the tire 10 and being intended to protect the carcass ply 30 from the diffusion of air from the interior space of the tire 10.

The crown reinforcement 14 comprises, radially from the outside towards the inside of the tyre 10: a protective reinforcement 36 disposed radially inside the tread 22; a working reinforcement 38 disposed radially inside the protective reinforcement 36; and an additional reinforcement 80 disposed radially inward of the working reinforcement 38. The protective reinforcement 36 is therefore interposed radially between the tread 22 and the working reinforcement 38. The working reinforcement 38 is interposed radially between the protective reinforcement 36 and the additional reinforcement 80.

The protective reinforcement 36 includes first and second protective plies 42, 44, with the first ply 42 being disposed radially inward of the second ply 44. Each of the first and second protective plies 42, 44 comprises a first and a second protective reinforcing element 43, 45, respectively, of filiform metal, arranged substantially parallel to each other in each of the first and second protective plies 42, 44. The first and second filiform metal protective reinforcing elements 43, 45 each form an angle with the circumferential direction Z of the tyre at least equal to 10 °, preferably ranging from 10 ° to 35 °, more preferably from 15 ° to 30 °.

The working reinforcement 38 includes first and second working plies 46, 48, with the first ply 46 being disposed radially inward of the second ply 48. Each of the first and second working plies 46, 48 comprises a first and a second filiform metal working reinforcing element 47, 49, respectively, disposed substantially parallel to each other in each of the first and second working plies 46, 48. The first and second filiform metal working reinforcing elements 47, 49 each form an angle at most equal to 60 °, preferably in the range 15 ° to 40 °, with the circumferential direction Z of the tyre 10. Optionally, the first and second filiform metal working reinforcing elements 47, 49 cross from one working ply to the other.

The additional reinforcement 80, also called a constraining block, whose function is to partially oppose the mechanical stresses of inflation, comprises a first and a second additional ply 82, 84, each of the first and second additional plies 82, 84 comprising a first and a second additional filiform metal reinforcing element 83, 85, respectively, arranged substantially parallel to each other in each of the first and second additional plies 82, 84. The first and second additional filiform metal reinforcing elements 83, 85 each form an angle at most equal to 10 °, preferably in the range 5 ° to 10 °, with the circumferential direction Z of the tyre 10. The additional filiform metal reinforcing elements are for example those described in FR 2419181 or FR 2419182.

In one embodiment, the first and second filiform metal working reinforcing elements 47, 49 are each formed by a cord according to the invention, for example by a cord 50 described below.

In another embodiment, each filiform metal carcass reinforcing element 31 is formed by a cord according to the invention, for example by a cord 50 described hereinafter.

In a further embodiment, each of the first and second filiform metal working reinforcing elements 47, 49 and each filiform metal carcass reinforcing element 31 is formed by a cord according to the invention, which may be identical or different depending on whether they are filiform metal reinforcing elements 31, 47 or 49.

Cord according to a first embodiment of the invention

Fig. 3 shows a cord 50 according to a first embodiment of the invention.

The cord 50 is metal and is of the multi-strand type with two cylindrical layers. Thus, it will be understood that there are not so many two layers with strands making up the cord 50. The layers with strands are adjacent and concentric. When the cord 50 is not integrated into the tire, the cord 50 does not have a polymeric compound and an elastomeric compound.

The cord 50 includes an inner layer CI of the cord 50 and an outer layer CE of the cord 50. The inner layer CI consists of K >1 inner strands TI wound in a spiral. In this case, K is 2, 3 or 4, preferably K is 3 or 4, and K is 3 here. The outer layer CE is made up of L >1 outer strands TE wound around the inner layer CI of the cord. In this particular case, L is 7, 8, 9 or 10, preferably L is 8, 9 or 10, more preferably L is 8 or 9, and where L is 9.

The cord 50 also comprises a coating F consisting of a single coating thread.

The inner layer CI of the cord is wound in a spiral form and with a pitch pi (here pi ═ 80mm) in the cord inner layer direction (Z in this case), and the outer layer CE is wound in a spiral form and with a pitch pe (here pe ═ 100mm) in the cord outer layer direction (Z in this case). Since pi is different from pe, the cord has a cylindrical layer.

The wrapping F is wound around the outer layer CE in a wrapping direction of the wrapping, in this case in a winding direction (in this case the S direction) opposite to the winding direction of the outer layer of the cord. The wrapping thread is wound around the outer strand TE in a helical form and with a lay length pf satisfying 2mm pf 10mm, preferably 3mm pf 8 mm. Where pf is 5.1 mm.

The assembly consisting of the inner layer CI and the outer layer CE (which means that the cord 50 is free of the coating F) has a diameter D greater than or equal to 4 mm. Here, D is 7.0 mm.

The outer layer CE of the cord 50 is unsaturated. The average strand spacing E separating two adjacent outer strands TE is greater than or equal to 30 μm. Preferably, the average strand spacing E separating two adjacent outer strands TE is greater than or equal to 70 μm, more preferably greater than or equal to 100 μm, still more preferably greater than or equal to 150 μm, and the height is preferably greater than or equal to 200 μm. In this embodiment, the outer layer with outer strands has a strand spacing greater than or equal to 200 μm. Here, E is 255 μm.

Each inner strand TI has a diameter DI and each outer strand TE has a diameter DE. In this particular case, DI is 1.78mm and DE is 1.58 mm.

The outer layer CE of the cord 50 is unsaturated. Specifically, SIE ═ 9x0.255 ═ 2.3mm, which is a value higher than DE ═ 1.58 mm.

Inner strand TI of the cord 50

Each inner strand TI has three layers. Each inner strand TI therefore comprises not more than three layers, in this case three layers.

Each inner strand TI comprises: an inner layer C1 composed of Q ═ 1 inner filaments; an intermediate layer C2 of M intermediate filaments F2, said intermediate filaments F2 being wound in a spiral around the inner layer C1; and an outer layer C3 of N outer filaments F3, said outer filaments F3 being wound in a helical fashion around the inner layer C1 and around the intermediate layer C2 in contact with the intermediate layer C2.

Q is 1, M is 5 or 6 and N is 10, 11 or 12, where preferably Q is 1, M is 5 or 6 and N is 10 or 11, where Q is 1, M is 6 and N is 11.

The inner filament F1 has an infinite lay length.

The intermediate layer C2 of each inner strand TI is wound around the inner layer C1 of each inner strand TI in the winding direction Z. M intermediate filaments F2 are wound around the inner filament F1 in a helical form and with a lay length p2 satisfying 8 mm. ltoreq. p 2. ltoreq.16 mm, preferably 8 mm. ltoreq. p 2. ltoreq.14 mm, more preferably 8 mm. ltoreq. p 2. ltoreq.12 mm. Here, p2 is 10 mm.

The outer layer C3 of each inner strand TI is wound around the intermediate layer C2 of each inner strand TI in the winding direction Z. The N outer filaments F3 are wound in a helical form around the M intermediate filaments F2 with a lay length p3 satisfying 10 mm. ltoreq. p 3. ltoreq.40 mm, preferably 15 mm. ltoreq. p 3. ltoreq.35 mm, more preferably 15 mm. ltoreq. p 3. ltoreq.25 mm, still more preferably 17 mm. ltoreq. p 3. ltoreq.23 mm. Here, p3 is 20 mm.

Since p1 differs from p2 and p2 differs from p3, each inner strand TI is in a cylindrical layer.

The lay lengths p2 and p3 satisfy 0.36 ≦ (p3-p2)/p3 ≦ 0.57.

0.38. ltoreq. p3-p2)/p3, preferably 0.40. ltoreq. p3-p2)/p3, more preferably 0.43. ltoreq. p3-p2)/p3, still more preferably 0.45. ltoreq. p3-p2)/p 3.

(p3-p2)/p 3. ltoreq.0.55, preferably (p3-p2)/p 3. ltoreq.0.53.

In this case, (p3-p2)/p3 is 0.50.

The middle layer C2 of each inner strand TI is unsaturated and not fully unsaturated. The wire spacing I2 of the average separation M of the intermediate wires of the intermediate layer C2 is greater than or equal to 5 μ M, here equal to 8.2 μ M. Since interlayer C2 is not fully unsaturated, the sum SI2 of the filament spacings I2 of interlayer C2 is smaller than the diameter d2 of intermediate filaments F2 of interlayer C2. The sum SI 2-6 x 0.0082-0.05 mm, which is strictly less than d 2-0.35 mm.

The sum SI2 of the filament spacings I2 of the intermediate layer C2 is smaller than the diameter d3 of the outer filaments F3 of the outer layer C3, preferably smaller than or equal to 0.8x d 3. The sum SI 2-6 x 0.0082-0.05 mm, which is strictly less than d 3-0.35 mm.

The outer layer C3 of each inner strand TI is unsaturated and fully unsaturated. The filament spacing I3 of the outer layer C3, which evenly separates the N outer filaments, is greater than or equal to 5 μm. Preferably, the filament spacing I3 is greater than or equal to 15 μm, more preferably greater than or equal to 35 μm, in this embodiment equal to 45 μm here. The sum SI3 of the filament spacing I3 of the outer layer C3 is greater than the diameter d3 of the outer filaments F3 of the outer layer C3. Here, the sum SI3 is 11x0.045 is 0.50mm, which is a value strictly greater than d3 is 0.35 mm.

The inner, intermediate and outer wires of each inner strand TI have diameters d1, d2 and d3, respectively. The diameter d1 of each inner wire, the diameter d2 of each intermediate wire and the diameter d3 of each outer wire of each inner strand TI ranges from 0.15mm to 0.60mm, preferably from 0.20mm to 0.50mm, more preferably from 0.25mm to 0.45mm, still more preferably from 0.28mm to 0.42 mm.

The inner filament F1 of each inner strand TI has a diameter d1 which is greater than or equal to the diameter d2 of each intermediate filament F2 of each inner strand TI and a height preferably of 1. ltoreq. d1/d 2. ltoreq.1.30. The inner filament F1 of each inner strand TI has a diameter d1 which is greater than or equal to the diameter d3 of each outer filament F3 of each inner strand TI and a height preferably of 1. ltoreq. d1/d 3. ltoreq.1.30. The respective diameter d2 of each intermediate filament F2 of each inner strand TI and the respective diameter d3 of each outer filament F3 of each inner strand TI satisfy d2 ═ d 3.

In this case, d1> d2, d1> d3, d1/d2 ═ d1/d3 ═ 1.27, and d1 ═ 0.38mm, d2 ═ d3 ═ 0.35 mm.

Outer strand TE of cord 50

Each outer strand TE has at least two layers. In this case, each outer strand TE has three layers. Each outer strand TE comprises more or less than three layers, in this case three layers.

Each outer strand TE comprises: an inner layer C1 ' consisting of Q ' inner filaments F1 '; an intermediate layer C2 ' consisting of M ' intermediate filaments F2 ', said intermediate filaments F2 ' being wound in a spiral around the inner layer C1 '; and an outer layer C3 ' of N ' outer filaments F3 ', said outer filaments F3 ' being wound in a helical fashion around the inner layer C1 ' and around the intermediate layer C2 ' in contact with the intermediate layer C2 '.

Q ' ═ 1, 2, 3, or 4, preferably Q ' ═ 1, 2, or 3, and more preferably Q ' ═ 1 herein.

Where Q ' ═ 1, M ' ═ 5 or 6 and N ' ═ 10, 11 or 12, preferably Q ' ═ 1, M ' ═ 5 or 6 and N ' ═ 10 or 11, where Q ' ═ 1, M ' ═ 6 and N ' ═ 11.

The inner filament F1' has an infinite lay length.

The intermediate layer C2 'of each outer strand TE is wound around the inner layer C1' of each outer strand TE in the winding direction Z. M 'intermediate filaments F2' are wound in helical form around the inner filament F1 'with a lay length p2' such that 8mm p2 'is 16mm, preferably 8mm p2' is 14 mm. Here, p2' is 14 mm.

The outer layer C3 ' of each outer strand TE is wound around the inner layer C1 ' and the middle layer C2 ' of each outer strand TE in the winding direction Z. N ' outer filaments F3 ' are wound in helical form around M ' intermediate filaments F2 ' with a lay length p 3' satisfying 10mm < p 3' < 40mm, preferably 15mm < p 3' < 35mm, more preferably 15mm < p 3' < 25mm, still more preferably 17mm < p 3' < 23 mm. Here, p 3' is 20 mm.

Because p1 'is different from p2' and p2 'is different from p 3', each outer strand TE is in a cylindrical layer.

The middle layer C2' of each outer strand TE is unsaturated and not fully unsaturated. The average separation M ' of the intermediate layers C2 ' is greater than or equal to 5 μ M with a wire spacing I2 '. The filament spacing I2' is greater than or equal to 15 μm, more preferably greater than or equal to 35 μm, in this embodiment equal to 38 μm. Since intermediate layer C2 ' is not completely unsaturated, the sum SI2' of the filament spacings I2' of intermediate layer C2 ' is smaller than the diameter d2' of intermediate filaments F2 ' of intermediate layer C2 '. The sum SI2 'is 6 × 0.038 to 0.23mm, which is strictly less than d2' to 0.30 mm.

Furthermore, the sum SI2' of the filament spacings I2' of the intermediate layer C2 ' is smaller than the diameter d3' of the outer filaments F3 ' of the outer layer C3 ', preferably smaller than or equal to 0.8x d3 '. The sum SI2 'is 6 × 0.038 to 0.23mm, which is strictly less than d3' to 0.30 mm.

The outer layer C3' of each outer strand TE is unsaturated and fully unsaturated. The filament spacing I3 ' of the outer layer C3 ' that evenly separates the N ' outer filaments is greater than or equal to 5 μm. The filament spacing I3' is greater than or equal to 15 μm, more preferably greater than or equal to 35 μm, still more preferably greater than or equal to 50 μm, in this embodiment equal to 55.4 μm. The sum SI3 'of the wire spacing I3' of the outer layer C3 'is greater than the diameter d3' of the outer wires F3 'of the outer layer C3'. The sum SI 3' is equal to 11x0.0554 equal to 0.61mm, which is a value strictly greater than d3 equal to 0.30 mm.

Each inner wire, each intermediate wire and each outer wire of each outer strand TE has a diameter d1', d2' and d3', respectively. The diameter d1' of each inner wire, d2' of each intermediate wire and d3' of each outer wire of each outer strand TE ranges from 0.15mm to 0.60mm, preferably from 0.20mm to 0.50mm, more preferably from 0.25mm to 0.45mm, still more preferably from 0.28mm to 0.42 mm.

The inner wire F1 ' of each outer strand TE has a diameter d1' which is greater than or equal to the diameter d2' of each intermediate wire F2 of each outer strand TE, very preferably 1. ltoreq. d1'/d2 '. ltoreq.1.30. Each inner wire F1 'of each outer strand TE has a diameter d1' which is greater than or equal to the diameter d3 'of each outer wire F3' of each outer strand TE, very preferably 1. ltoreq. d1'/d 3'. ltoreq.1.30. The respective diameter d2' of each intermediate filament F2 ' of each outer strand TE and the respective diameter d3' of each outer filament F3 ' of each outer strand TE satisfy d2 ═ d3 '.

In this case, d1' > d2', d1' > d3', d1'/d2' ═ d1'/d3' ═ 1.27, and d1' ═ 0.38mm, d2' ═ d3' ═ 0.30 mm.

The inner filament F1 of each inner strand TI has a diameter d1 greater than or equal to the diameter d1 'of each inner filament F1' of each outer strand TE, and preferably the inner filament F1 of each inner strand TI has a diameter d1 equal to the diameter d1 'of each inner filament F1' of each outer strand TE. Here, d1 ═ d1 ═ 0.38 mm.

The inner filament F1 of each inner strand TI has a diameter d1 greater than or equal to the diameter d2 'of each intermediate filament F2' of each outer strand TE, and preferably the inner filament F1 of each inner strand TI has a diameter d1 greater than the diameter d2 'of each intermediate filament F2' of each outer strand TE. Here, d1 ═ 0.38mm > d2 ═ 0.30 mm.

The inner filament F1 of each inner strand TI has a diameter d1 greater than or equal to the diameter d3 'of each outer filament F3' of each outer strand TE, and preferably the inner filament F1 of each inner strand TI has a diameter d1 greater than the diameter d3 'of each outer filament F3' of each outer strand TE. Here, d1 ═ 0.38mm > d3 ═ 0.30 mm.

Each intermediate filament F2 of each inner strand TI has a diameter d2 greater than or equal to the diameter d2 'of each intermediate filament F2' of each outer strand TE. Preferably, d2 ═ 0.35mm > d2 ═ 0.30mm here.

Each outer filament F3 of each inner strand TI has a diameter d3 greater than or equal to the diameter d3' of each outer filament F3 of each outer strand TE. Preferably, d3 ═ 0.35mm > d3 ═ 0.30mm here.

Each of the filaments has a breaking strength expressed as Rm satisfying 2500. ltoreq. Rm.ltoreq.3100 MPa. The steel used for these wires is known as SHT ("Super High Tensile") grade. Other filaments can be used, for example secondary filaments, such as those of the NT ("Normal Tensile") or HT ("High Tensile") grade, but also higher filaments, such as those of the UT ("Ultra Tensile") or MT ("Mega Tensile") grade.

Method for preparing a cord according to the invention

The cord according to the present invention is produced by using a method comprising steps well known to those skilled in the art.

In the step of manufacturing the inner strands using the following steps, it is preferably carried out successively in succession:

first of all, a first step of assembly, forming an intermediate layer C2 at a first assembly point by twisting M intermediate wires F2 in the Z direction at a lay length p2 around Q ═ 1 inner wires F1 of the inner layer C1;

-following a second step of assembly, forming at a second assembly point an outer layer C3 and each inner strand TI by twisting N outer filaments F3 in the Z direction with a lay length p3 around the M intermediate filaments F2 of the intermediate layer C2;

preferably, a final twist balancing step is performed.

In the step of manufacturing the outer strands using the following steps, it is preferably carried out successively in succession:

first of all a first step of assembly, forming the inner layer C1 ' at a first assembly point by twisting Q ' inner filaments F1 ' of the inner layer C1 ' in the Z direction with a lay length p1 '; in embodiments where Q' ═ 1, the first assembly step is omitted;

-following a second step of assembly, forming an intermediate layer C2 ' at a second assembly point by twisting or twining M ' intermediate wires F2 ' in the Z direction with a lay length p2' around Q ' inner wires F1 ' of the inner layer C1 ';

-a third step, following assembly, of forming at a third assembly point an outer layer C3 'and each outer strand TE by twisting or twisting N' outer wires F3 'in the Z direction with a lay length p 3' around the M intermediate wires F2 'of the intermediate layer C2';

preferably, a final twist balancing step is performed.

As is known to the person skilled in the art, "twist balancing" means here the elimination of the residual torque (or elastic return of the twist) exerted on each wire of the strands in the middle layer, as in the outer layer.

After this final twist balancing step, the manufacture of the strand is completed. Each strand is wound onto one or more take-up reels for storage before the subsequent operation of assembling the elementary strands by stranding to obtain a multi-strand cord.

In the step of manufacturing the inner layer CI, the K inner strands TI are assembled by twisting in the Z direction with a lay length pi, forming the inner layer CI at a first assembly point.

Then, in a subsequent manufacturing step, the L outer strands TE are assembled by twisting around the inner layer CI in the Z direction with a lay length pe, thus forming an assembly of layers CI and CE.

It is feasible, in a final assembly step, to wind the covering F around the previously obtained assembly in the S direction with a lay length pf.

The cords are then incorporated by calendering into a composite fabric formed from a known compound based on natural rubber and carbon black (as reinforcing filler), which is generally used for making the crown reinforcement of a radial tire. In addition to the elastomer and the reinforcing filler (carbon black), the compound essentially contains an antioxidant, stearic acid, an extender oil, cobalt naphthenate as adhesion promoter, and finally a vulcanization system (sulphur, accelerator and ZnO).

The composite fabric reinforced by these cords has an elastomeric compound matrix formed by two thin layers of elastomeric compound, respectively superimposed on both sides of the cords and having a thickness comprised between 1 and 4mm, inclusive. The calendering coating lay length (the lay length of the cord laid in the elastomeric compound fabric) ranges from 4mm to 8 mm.

These composite fabrics are then used as working plies in the crown reinforcement during the process of manufacturing the tire, the steps of which are otherwise known to those skilled in the art.

Cord according to a second embodiment of the invention

Fig. 4 shows a cord 50' according to a second embodiment of the invention. Elements similar to those of the first embodiment are denoted by the same reference numerals. Unlike the first embodiment described above, the cord 50' according to the second embodiment satisfies K-2 and L-8.

Cord according to a third embodiment of the present invention

The figure shows a cord 50 "according to a third embodiment of the invention. Elements similar to those of the first embodiment are denoted by the same reference numerals. Unlike the first embodiment described above, the cord 50 "according to the third embodiment satisfies K-4 and L-10.

Table a below summarizes the characteristics of the various cords 50, 50', and 50 ".

TABLE A

Cord according to fourth to twelfth embodiments of the present invention

Fig. 6 to 14 show cords 51 to 59 according to fourth to twelfth embodiments of the present invention.

The characteristics of the various cords 51 to 59 according to the fourth to twelfth embodiments of the invention are summarized in the following tables B and C.

Comparative test

Indication of the permeability of an elastomeric compound to strands

The ability of the strands to penetrate by the elastomeric compound was determined in the following tests, by simulating the dimensions of the radial passage windows formed by the two adjacent filaments F2 of the intermediate layer C2 and the two adjacent filaments F3 of the outer layer C3. Such a window is shown in fig. 15 and 16, fig. 15 showing a schematic view of each internal strand along its main axis P, and fig. 16 showing the radial through window S defined above.

This strand permeability index depicts the impermeability of the strand to air. In particular, the larger the size of the window, the higher the permeability index, the easier the elastomeric compound is to penetrate the strands, and thus the greater the impermeability of the strands to air. Air permeability may also be determined using an air permeability test that allows the longitudinal permeability of the strand or cord being tested to air to be determined by measuring the volume of air that passes through the test specimen at a constant pressure over a given period of time. As is well known to those skilled in the art, the principle of this test is to prove the effectiveness of the treatment of the strands or cords to render the cords impermeable to air; it has been described, for example, in the standard ASTM D2692-98. This test was performed on the as-made, non-aged strand or cord. The untreated strands or cords are previously coated on the outside with an elastomeric compound called coating compound. For this purpose, a series of 10 strands or 10 cords laid in parallel (distance between cords: 20mm) is disposed between two layers or "skins" of diene elastomer compound in the untreated state (two rectangles of dimensions 80 × 200 mm), each skin having a thickness of 5 mm; all the mass is then fixed in a mould, each strand or each cord being kept under sufficient tension (for example 3daN) using a clamping mould to ensure that it lays straight when it is placed in the mould; then vulcanized (cured) at a temperature of about 120 ℃ and a pressure of 15 bar for about 10 to 12 hours (rectangular pistons with dimensions 80x200 mm). The whole was then removed from the mould and 10 test specimens of the thus coated strands or cords were cut in the shape of a parallelepiped with the dimensions 7x7x60mm for characterization. Compounds used as coating elastomeric compounds are diene elastomeric compounds conventionally used for tires, also containing the following usual additives, based on natural (peptized) rubber and carbon black N330(65 phr): sulfur (7phr), sulfenamide accelerator (1phr), ZnO (8phr), stearic acid (0.7phr), antioxidant (1.5phr), cobalt naphthenate (1.5phr) (phr means parts by weight per 100 parts of elastomer); the E10 modulus of the coated elastomeric compound was about 10 MPa. The test is carried out on 6cm long strands or cordsOf rows, around which the strands or cords are therefore coated with the elastomeric compound in the cured state (or with the elastomeric compound), the tests being carried out in the following manner: air is injected at a pressure of 1 bar into the inlet end of the strand or cord and a flow meter (calibrated, for example from 0 to 500 cm) is used³/min) the air volume at the outlet end was measured. During the measurement, a sample of the strand cord is fixed in a compressed airtight seal (for example a seal made of dense foam or rubber) so that only the amount of air passing through the strand or cord from one end to the other along its longitudinal axis is taken into account in the measurement; the airtightness of the airtight seal itself was checked beforehand using a test specimen of solid elastomeric compound (i.e. a test specimen without strands and cords). The higher the longitudinal air impermeability of the strand or cord, the lower the measured average air flow rate (average of 10 specimens). Because the measurement precision is +/-0.2 cm3/min, the measurement values less than or equal to 0.2cm3/min are considered as zero; they correspond to strands or cords that can be described as airtight (completely airtight) along the strand or cord axis (i.e. in the longitudinal direction of the strand or cord).

However, the inventors tended to simulate and calculate the window S in the breathability test for the speed at which the strand could be evaluated.

Evaluation of the Permeability index of each inner strand according to the lay length p3 of the cord 50

Various internal strands similar to those of the cord 50 according to the invention were simulated by varying the value of p2 for various values of p3, wherein all other structural features of the cord remain unchanged compared to the above description.

The results of these simulations are collated in the individual tables 1 to 3, in each case in terms of base 100 relative to a control strand satisfying (p3-p2)/p3 ═ 0.30. Thus, for the window size values St for the test strands and S0 for the control strands, the permeability index is equal to St 100/S0. Thus, a result higher than 100 means that the test strand shows a good permeability with respect to the corresponding control strand. It is estimated that the size of the window is significantly higher when the permeability index is greater than or equal to 120 (which means when the size of the window in the test strand is 20% higher than the size of the control strand).

Each of tables 1 to 3 corresponds to a lay length p3 equal to 20mm, 23mm, 25mm, respectively.

It should be noted that although the filament spacing I2 increases as p2 increases, the maximum value of the radial through-window is available for I2 values that are not necessarily the highest values. Therefore, prior to the present invention, it would be difficult for one skilled in the art to predict the maximum permeability for p2 values that result in relatively low I2 values, starting with the assumption that the lower the I2, the lower the permeability of the strand.

In the range of 0.36 to 0.57 of the ratio (p3-p2)/p3, the value of the permeability index is significantly higher for each tested p3 value than that obtained for the corresponding control strand.

Cord 50’、50”51 to 59 of the inner strands

In a similar manner to the cord 50 according to the first embodiment of the invention, the various outer strands of the cords 50', 50 ", 51 to 59 according to the various embodiments of the invention were simulated by varying the value of p2 while setting the value of p3 to the value described above, wherein all other structural features of the respective cords remain unchanged compared to the above description.

The results of these simulations are collated in each of tables 4 to 6, in each case in terms of base 100 relative to a control strand satisfying (p3-p2)/p3 ═ 0.30. Thus, for the window size values St for the test strands and S0 for the control strands, the permeability index is equal to St 100/S0. Thus, a result higher than 100 means that the test strand shows a good permeability with respect to the corresponding control strand. It is estimated that the size of the window is significantly higher when the permeability index is greater than or equal to 120 (which means when the size of the window in the test strand is 20% higher than the size of the control strand).

It should be noted that although the filament spacing I2 increases as p2 increases, a maximum value of the dimension of the radial through window is available for I2 values that are not necessarily the highest values. Therefore, prior to the present invention, it would be difficult for one skilled in the art to predict the maximum permeability for p2 values that result in relatively low I2 values, starting with the assumption that the lower the I2, the lower the permeability of the strand.

In the range of 0.36 to 0.57 of the ratio (p3-p2)/p3, the value of the permeability index is significantly higher for each tested p3 value than that obtained for the corresponding control strand.

Tables 4 to 6 show that for different cord constructions, the penetration of the elastomeric compound into each inner strand is significantly improved for the ratio (p3-p2)/p3 ranging from 0.36 to 0.57 compared to the control cord of (p3-p2)/p3 ═ 0.30.

Of course, the present invention is not limited to the exemplary embodiments described above.

For reasons of industrial feasibility, cost and overall performance, it is preferred to practice the invention using linear wires (i.e. straight wires) having a conventional circular cross-section.

Features of the various embodiments described or contemplated above may also be combined, provided that the features are compatible with each other.